Patent Grant
8001758
1. Field of the Invention
The present invention relates to a rubber-product-reinforcing steel cord (hereinafter, this may be simply referred to as a “cord”) used as a rubber-product-reinforcing material for an automotive tire, a conveyer belt, or the like, and a method for manufacturing the same.
2. Description of Related Art
As a single-layered rubber-product-reinforcing steel cord used as a rubber-product-reinforcing material for an automotive tire, a conveyer belt, or the like, conventionally, a cord is typically used that has a single-layered twist structure such as a 1×3 or a 1×5 structure, and that has a so-called closed-twist structure in which a plurality of wires are tightly intertwined in close contact with each other. However, in a cord having such a closed-twist structure, a closed space is formed at the center of the cord. When the cord is held between two rubber sheets and subjected to heat compression to form a composite sheet, rubber material does not penetrate the hollow portion at the center of the cord, and the composite has a structure in which the cord is merely enclosed by the rubber sheets. Thus, a so-called complete composite is not obtained in which the rubber material completely penetrates the hollow portion at the center of the cord and the rubber and the cord are integrated. Accordingly, when a composite sheet in which a conventional cord having such a closed-twist structure is held between rubber sheets and subjected to heat compression is combined into, for example, a tire of an automobile, adhesion between the rubber material and the cord is insufficient, and, thus, a so-called separation phenomenon is likely to occur in which the rubber material is separated from the cord during travel of the automobile. Furthermore, when water that has penetrated the rubber material reaches the hollow portion at the center of the cord, the water immediately spreads through the hollow portion in the longitudinal direction of the cord, and causes corrosion of the cord. As a result, a problem occurs in which the mechanical strength of the cord is significantly lowered.
Furthermore, a cord having an open-twist structure is known in which, as shown in
Furthermore, a configuration is proposed in which, as shown in
However, when a tension load acts on a cord having such a single-layered twist structure in which only parts of the wires are provided with spiral curls in this manner, the tension load tends to be concentrated on the non-spiral wires.
Thus, it is also conceivable that, as shown in
It is an object of the present invention to provide a rubber-product-reinforcing steel cord having a single-layered twist structure with good rubber penetration properties, excellent fatigue resistance, and small low-load stretch.
The present invention is directed to a rubber-reinforcing steel cord having a 1×n single-layered twist structure obtained by intertwining n wires, where n=3 to 6, with a same wire diameter, wherein all of the wires are provided with substantially elliptical spiral curls having a substantially elliptical cross-section and a pitch smaller than that of curls for intertwining, formed by providing the wires with spiral curls and then pressing the wires, and the substantially elliptical spiral curls have a curl pitch P of 0.32 Pc to 0.55 Pc, where Pc is a twist pitch in mm of a cord, and have a substantially elliptical cross-sectional shape with a minor axis D1/major axis D2 of 0.35 to 0.66.
Furthermore, the present invention is directed to a method for manufacturing a rubber-reinforcing steel cord having a 1×n single-layered twist structure obtained by intertwining n wires, where n=3 to 6, with a same wire diameter, comprising: providing all of the wires with spiral curls and then pressing the wires to provide the wires with substantially elliptical spiral curls having a substantially elliptical cross-section and a pitch smaller than that of curls for intertwining; wherein the substantially elliptical spiral curls have a curl pitch P of 0.32 Pc to 0.55 Pc, where Pc is a twist pitch in mm of a cord, and have a substantially elliptical cross-sectional shape with a minor axis D1/major axis D2 of 0.35 to 0.66; and intertwining the wires having the substantially elliptical spiral curls into each other to form a steel cord having a single-layered twist structure.
This cord is a cord obtained by intertwining wires in which all of the wires are provided with further substantially elliptical spiral curls having a pitch smaller than that of curls for intertwining. Accordingly, a cord after intertwining also has further curls having a pitch smaller than that of curls for intertwining, and, thus, a hollow portion at the center of the cord is in communication with the outside via a gap between the wires, and rubber material easily penetrates the interior portion.
Furthermore, in this cord, all of the wires have curls having a pitch smaller than that of curls for intertwining, and, when a tension load acts on the cord, the load acts equally on all of the wires, and, thus, the fatigue resistance is not lowered by concentration of the load on part of the wires, and excellent fatigue resistance is obtained. Furthermore, in this cord, at least any one pair of adjacent wires are substantially in contact with each other at any point in the longitudinal direction of the cord. Accordingly, the cord stretch is reduced, and the low-load stretch can be suppressed.
In the above-described configuration, the curl pitch P is 0.32 Pc to 0.55 Pc, where Pc is a twist pitch in mm of a cord. The reason for this is that, if the curl pitch P is less than 0.32 Pc, unnatural plastic deformation occurs where excessive stress acts during a curling process, and, thus, the wires are easily broken, and the productivity is lowered, and, if the curl pitch P is more than 0.55 Pc, the cord obtained by intertwining these wires has a reduced gap between the wires clue to a tensile force generated by the flow of the rubber material while molding a rubber product or by a frictional force applied to the surface of the cord, and, thus, the rubber material cannot sufficiently penetrate the interior portion. Furthermore, minor axis D1/major axis D2 of a cross-sectional shape of the substantially elliptical spiral curl is 0.35 to 0.66. The reason for this is that, if a cord is obtained by intertwining wires with a D1/D2 of less than 0.35, a gap between the wires is too small, and rubber material cannot sufficiently penetrate the interior portion during pressing and vulcanizing operations even when a rubber material with good flowability is used, and, if a cord is obtained by intertwining wires with a D1/D2 of more than 0.66, the twist stability becomes poor, and the fatigue resistance deteriorates.
In the above-described manufacturing method, wires may be processed such that, after the wires are provided with substantially elliptical spiral curls formed by providing the wires with spiral curls and then pressing the wires, the wires are once wound about a reel or the like, and a predetermined number of such wires are set at a supply apparatus of a twisting machine and intertwined into each other, or such that the wires are subjected to a curling process between from the supply apparatus to a twist port of the twisting machine.
According to the present invention, a rubber-product-reinforcing steel cord having a single-layered twist structure with good rubber penetration properties, excellent fatigue resistance, and small low-load stretch can be obtained. When this cord is used, for example, as a reinforcing material for an automotive tire, a tire that has excellent fatigue resistance and excellent rubber penetration properties can be produced without lowering handling work efficiency during tire manufacture. Moreover, the life of the tire can be significantly prolonged.
Furthermore, in this cord, wires before intertwining have a curl pitch P of 0.32 Pc to 0.55 Pc, where Pc is a twist pitch in mm of a cord. Thus, the occurrence of unnatural plastic deformation where excessive stress acts can be prevented during a curling process and the productivity can be increased. In the cord obtained by intertwining these wires, a gap between the wires can be prevented from being reduced by a tensile force generated by the flow of the rubber material while molding a rubber product or by a frictional force applied to the surface of the cord, and, thus, the rubber material sufficiently penetrates the interior portion. Furthermore, minor axis D1/major axis D2 of the substantially elliptical curl is 0.35 to 0.66, and, thus, in the cord obtained by intertwining these wires, the rubber material can sufficiently penetrate the interior portion during pressing and vulcanizing operations, twisting is stabilized, and deterioration in the fatigue resistance can be prevented.
Hereinafter, a rubber-product-reinforcing steel cord according to an embodiment of the present invention will be described with reference to the drawings.
A steel cord 10 shown in
In the cord 10, all of the wires 11 have not only curls for intertwining, but also substantially elliptical spiral curls having a pitch smaller than that of the curls for intertwining. The substantially elliptical spiral curls having a pitch smaller than that of the curls for intertwining are curls obtained by providing the wires with spiral curls, and then pressing the wires.
The pitch of the substantially elliptical spiral curls of a wire before intertwining is as shown in the plan view in
In the cord 10, all of the wires 11 have not only curls for intertwining, but also curls having a pitch smaller than that of the curls for intertwining, and, thus, a hollow portion at the center of the cord is in communication with the outside via a gap 12 between the wires 11. Accordingly, rubber material easily penetrates the interior portion.
Furthermore, in the cord 10, all of the wires 11 have curls having a pitch smaller than that of the curls for intertwining, and, when a tension load acts on the cord, the load acts equally on all of the wires 11, and, thus, the fatigue resistance is not lowered by concentration of the load on part of the wires 11, and excellent fatigue resistance is obtained.
Furthermore, in the cord 10, at least any one pair of adjacent wires 11 are substantially in contact with each other at any point in the longitudinal direction of the cord. Accordingly, the cord stretch is reduced, and the low-load stretch can be suppressed.
A cord (steel cord) 20 shown in
In the cord 20, all of the wires 21 have not only curls for intertwining, but also substantially elliptical spiral curls having a pitch smaller than that of the curls for intertwining. The substantially elliptical spiral curls having a pitch smaller than that of the curls for intertwining are curls obtained by providing the wires with spiral curls, and then pressing the wires. The curl pitch P (mm) of the substantially elliptical curls before intertwining is 0.32 Pc to 0.55 Pc, where Pc is a twist pitch in mm of a cord, and minor axis D1/major axis D2 is 0.35 to 0.66. Here, the wire diameter d is preferably 0.15 to 0.40 mm. The reason for this is that, if the wire diameter d is less than 0.15 mm, the strength of the steel cord decreases, and, if the wire diameter d is more than 0.40 mm, the flexibility is lowered. The twist pitch Pc is typically 8.0 to 18.0 mm.
In the cord 20, all of the wires 21 have not only curls for intertwining, but also curls having a pitch smaller than that of the curls for intertwining, and, thus, a hollow portion at the center of the cord is in communication with the outside via a gap 22 between the wires 21. Accordingly, rubber material easily penetrates the interior portion.
Furthermore, in the cord 20, all of the wires 21 have curls having a pitch smaller than that of the curls for intertwining, and, when a tension load acts on the cord, the load acts equally on all of the wires 21, and, thus, the fatigue resistance is not lowered by concentration of the load on part of the wires 21, and excellent fatigue resistance is obtained.
Furthermore, in the cord 20, at least any one pair of adjacent the wires 21 are substantially in contact with each other at any point in the longitudinal direction of the cord. Accordingly, the cord stretch is reduced, and the low-load stretch can be suppressed.
As examples, cords were produced as follows. A steel wire material having a diameter of 5.5 mm was repeatedly subjected to patenting and drawing, the surface was plated with brass, and, thus, wires having a wire diameter of 0.25 mm were obtained. These wires were used to manufacture steel cords having a 1×3 and a 1×5 single-layered twist structure.
Each of the cords having a 1×3 and a 1×5 single-layered twist structure of these examples was obtained by intertwining wires provided with small curls having a substantially elliptical cross-section formed by providing the wires with substantially spiral curls and then pressing the wires.
In all cases, the spiral curls were provided using a curling apparatus (a curling apparatus described in JP S63-63293B) that rotates about supplied wires. The shape of the curls was adjusted with the spacing between curling pins, the size of the curling pins, and the number of times of rotation about the wires.
Furthermore, the pressing step of processing spiral curls into spiral curls having a substantially elliptical cross-section was performed using a known pressing apparatus in which a plurality of freely rotating rollers were arranged in zigzag lines. Note that the pressing means is not limited to this.
The rubber penetration properties, the low-load stretch, the fatigue resistance, the shape stability (twist stability), and the productivity of the thus manufactured cords of the examples were evaluated in comparison with cords of conventional examples.
Evaluation of the rubber penetration properties was performed as follows: each cord was embedded in rubber material under a tension load of 49 N, the resultant was pressed and vulcanized, the cord was taken out of the rubber, the cord was dissembled, a predetermined length was observed, and the ratio of the length in which there was a trace of contact with the rubber with respect to the length subjected to the observation was displayed as a percentage.
Evaluation of the low-load stretch was performed, and stretch under a load of 49 N was displayed as a percentage.
Evaluation of the fatigue resistance was performed as follows: a plurality of cords were embedded in rubber material to form a composite sheet, this sheet was tested using a double-layered belt fatigue testing machine to obtain the number of times the operation was repeated until the cords broke due to fretting wear, buckling, and the like, and the number was displayed as an index number taking cords having a closed-twist structure of the conventional examples as 100.
Evaluation of the handling work efficiency was performed, and a cord having inferior performance was indicated as “Inferior”, that having slightly inferior performance as “Slightly Inferior”, and that having equivalent performance as “Equivalent”, in comparison with the performance of cords having a closed-twist structure of the conventional examples.
Evaluation of the shape stability was performed, and a cord having similar performance was indicated as “Uniform”, and that having non-similar performance as “Non-Uniform”, using cords having a closed-twist structure of the conventional examples as a reference (Uniform).
Evaluation of the productivity was performed by judging whether or not a wire was broken when subjected to a curling process, and a cord that was not broken was indicated as “Good”, and a cord that was broken was indicated as “Bad”.
As conventional examples, cords were produced as follows. A steel wire material having a diameter of 5.5 mm was repeatedly subjected to patenting and drawing, the surface was plated with brass, and, thus, wires having a wire diameter of 0.25 mm were obtained. These wires were used to manufacture three types of conventional cords having 1×3 structures consisting of a 1×3 closed-twist structure, a 1×3 open-twist structure, and a 1×3 structure in which part (one) of the wires was provided with spiral curls, and three types of conventional cords having 1×5 structures consisting of a 1×5 closed-twist structure, a 1×5 open-twist structure, and a 1×5 structure in which part (three) of the wires was provided with spiral curls.
Tables 1 and 2 show the evaluation results.
Tables 1 and 2 clearly show that the cords of the examples are superior to the conventional cords in all evaluations.
Thus, the present invention can be applied to a rubber-product-reinforcing material for an automotive tire, a conveyer belt, or the like.
The invention may be embodied in other forms without departing from the spirit or essential characteristics thereof. The embodiments disclosed in this application are to be considered in all respects as illustrative and not limiting. The scope of the invention is indicated by the appended claims rather than by the foregoing description, and all changes which come within the meaning and range of equivalency of the claims are intended to be embraced therein.
| Number | Date | Country | Kind |
|---|---|---|---|
| 2009-066156 | Mar 2009 | JP | national |
| 2009-218319 | Sep 2009 | JP | national |
| Number | Name | Date | Kind |
|---|---|---|---|
| 5162067 | Miyawaki | Nov 1992 | A |
| 5293737 | Kobayashi et al. | Mar 1994 | A |
| 5319915 | Kobayashi et al. | Jun 1994 | A |
| 5337549 | Kobayashi et al. | Aug 1994 | A |
| 5687557 | De Vos et al. | Nov 1997 | A |
| 5878564 | De Vos et al. | Mar 1999 | A |
| Number | Date | Country |
|---|---|---|
| 363893 | Apr 1990 | EP |
| 05140882 | Jun 1993 | JP |
| Number | Date | Country | |
|---|---|---|---|
| 20100236211 A1 | Sep 2010 | US |