Patent Grant
10611681
The disclosure relates to strengthened glass. More particularly, the disclosure relates to strengthened glass having a deep compressive layer.
Glasses strengthened by ion exchange tend to exhibit stress profiles that resemble a complementary error function or a parabolic function. While such stress profiles provide adequate protection for certain types of damage, such as sharp impacts, they do not provide sufficient protection for other types of insult, such as a drop from a height onto an abrasive surface.
The present disclosure provides a strengthened glass having a stress profile that differs from error-function and parabolic profiles that have previously been observed for such glasses. Stress relaxation and thermal annealing/diffusion effects, which occur at longer ion exchange and/or anneal times, increase the depth of compression (DOC) of the surface layer. A method of achieving these effects is also provided.
Accordingly, one aspect of the disclosure provides a glass article having a thickness (t) and a center at t/2. The glass has a first compressive layer under a first compressive stress (CS1), the compressive layer extending from a first surface of the glass to a first depth of compression (DOC1). The stress in the glass varies as a function of the thickness (t) to form a stress profile comprising: a first region extending from the first surface to a depth (d1) into the glass, wherein d1>0.06t and wherein at least a portion of the first region has a first slope (m1); and a second region extending from a depth of at least d1 to the first depth of compression (DOC1) and having a second slope (m2), wherein |m1|≤|m2|.
Another aspect of the disclosure provides a glass article strengthened by ion exchange, the glass article having a thickness (t) and a center at t/2. The glass article comprises: a compressive region on either side of the center, wherein the compressive region extends from a surface of the glass article to a depth of compression (DOC) and is under a compressive stress; and a tensile region extending from the depth of compression (DOC) to the center of the glass article, wherein the tensile region is under a physical center tension (CT). The stress in the glass varies as a function of the thickness (t) to form a stress profile comprising a sub-region within the compressive region in which the stress profile has a negative curvature, wherein the maximum absolute value of the negative curvature is between 20 MPa/(t (mm))2 and 4,000 MPa/(t (mm))2.
Yet another aspect of the disclosure provides a glass article strengthened by an ion exchange process followed by a thermal diffusion/annealing step. The glass article has a thickness (t) and a center at t/2, and a first compressive layer under a first compressive stress (CS1) that extends from a first surface of the glass to a first depth of compression (DOC1). The glass also comprises a tensile region extending from the first depth of compression (DOC1) to the center of the glass that is under a physical center tension (CT). The stress in the glass varies as a function of the thickness (t) to form a stress profile. The stress profile comprises: a first region extending from the first surface to a depth (d1) into the glass, wherein d1>0.06t and wherein at least a portion of the first region has a first slope (m1); and a second region extending from a depth of at least d1 to the first depth of compression (DOC1) and having a second slope (m2), wherein |m1|≤|m2|.
Still another aspect of the disclosure provides a method of strengthening a glass comprising first alkali cations. The glass has a first surface, a second surface opposite the first surface, a thickness (t), and a center at t/2. The method comprises: immersing the glass in an ion exchange bath comprising second alkali cations, wherein the second alkali cations are different from the first alkali cations, and replacing the first alkali cations within the glass with the second alkali cations from the ion exchange bath to form a compressive layer extending from the first surface and second surface of the glass to a first depth of compression (DOC1), where the compressive layer is under a first compressive stress (CS1) at the surface; and diffusing the second alkali cations from the first surface and the second surface to the center of the glass. The stress in the glass varies as a function of the thickness (t) to form a stress profile. The stress profile comprises: a first compressive region extending from each of the first surface and the second surface to a depth (d1) into the glass, wherein d1>0.06t and wherein at least a portion of the first region has a first slope (m1), and a second compressive stress (CS2) at each of the first surface and the second surface, wherein CS2≤CS1; and a second compressive region extending from a depth of at least d1 to a second depth of compression (DOC2) and having a second slope (m2), wherein |m1|≤|m2|, and wherein DOC2>DOC1.
In a first aspect a glass article is provided. The glass article comprises: a thickness t, a center located at t/2, a first compressive layer extending from a first surface of the glass article to a first depth of compression DOC1, and a first maximum compressive stress CS1 within the first compressive layer. The first compressive layer has a stress profile. The stress profile comprises a first region extending from the first surface to a depth d1 into the glass article, wherein d1>0.06t, and at least a portion of the first region has a first slope m1, and a second region extending from a depth of at least d1 to the first depth of compression DOC1 and having a second slope m2, wherein |m1|≤|m2|.
In a second aspect, the glass article of the first aspect is provided wherein the stress profile comprises a sub-region within the compressive region with a negative curvature, wherein the maximum absolute value of the negative curvature is at d1.
In a third aspect, the glass article of any of the preceding aspects is provided wherein the maximum absolute value of the negative curvature is between 20 MPa/(t (mm))2 and 4,000 MPa/(t (mm))2.
In a fourth aspect, the glass article of any of the preceding aspects is provided wherein a slope of the stress profile at d1 is zero.
In a fifth aspect, the glass article of any of the preceding aspects is provided wherein DOC1≥0.2t.
In a sixth aspect, the glass article of any of the preceding aspects is provided wherein CS1>0, m1>0 and m2<0.
In a seventh aspect, the glass article of any of the preceding aspects is provided wherein t is in a range from about 0.1 mm to about 2 mm.
In an eighth aspect, the glass article of any of the preceding aspects is provided wherein DOC1 is in a range from about 0.14t to about 0.35t.
In a ninth aspect, the glass article of any of the preceding aspects is provided wherein; the first maximum compressive stress CS1 is at the first surface and is in a range from about 500 MPa to about 2,000 MPa, and the stress profile further comprises a second sub-region having a positive curvature.
In a tenth aspect, the glass article of any of the preceding aspects is provided wherein the negative curvature of the first sub-region has an absolute value exceeding 10 MPa/(t (mm))2 over a spatial extent ranging from about 2% to about 25% oft.
In an eleventh aspect, the glass article of any of the preceding aspects is provided wherein: the first maximum compressive stress CS1 is at the first surface, and the compressive stress decreases to less than 50% of the first maximum compressive stress CS1 at a depth of less than about 8 μm below the first surface.
In a twelfth aspect, the glass article of any of the preceding aspects is provided further comprising a physical center tension in a range from about 40 MPa/(t (mm))½ to about 150 MPa/(t (mm))½.
In a thirteenth aspect, the glass article of any of the preceding aspects is provided wherein the second region of the stress profile comprises an inflection point.
In a fourteenth aspect, the glass article of any of the preceding aspects is provided wherein: the first region of the stress profile further comprises a sub-region extending from the first surface to a depth d2, d2<d1, the sub-region comprising at least a portion with a third slope m3, |m1|<|m3|, and 30 MPa/μm≤|m3|≤200 MPa/μm.
In a fifteenth aspect, the glass article of any of the preceding aspects is provided wherein 50 MPa/μm≤|m3|≤200 MPa/μm.
In a sixteenth aspect, the glass article of any of the preceding aspects is provided wherein the glass article comprises an alkali aluminosilicate glass.
In a seventeenth aspect, the glass article of the sixteenth aspect is provided wherein the alkali aluminosilicate glass comprises at least about 4 mol % P2O5, wherein (M2O3 (mol %)/RxO (mol %))<1, where M2O3═Al2O3+B2O3, and where RxO is the sum of monovalent and divalent cation oxides present in the alkali aluminosilicate glass.
In an eighteenth aspect, the glass article of the sixteenth aspect is provided wherein the alkali aluminosilicate glass comprises:
about 40 mol % to about 70 mol % SiO2;
about 11 mol % to about 25 mol % Al2O3;
about 2 mol % to about 15 mol % P2O5;
about 10 mol % to about 25 mol % Na2O;
about 10 to about 30 mol % RxO, where RxO is the sum of the alkali metal oxides, alkaline earth metal oxides, and transition metal monoxides present in the glass.
In a ninetieth aspect, the glass article of any of the preceding aspects is provided further comprising: a second compressive layer extending from a second surface of the glass article opposite the first surface to a second depth of compression DOC2, a second maximum compressive stress CS2 within the second compressive layer, and a tensile region extending from DOC1 to DOC2.
In a twentieth aspect, the glass article of the nineteenth aspect is provided wherein DOC1=DOC2.
In a twenty-first aspect a glass article is provided. The glass article comprises: a thickness t, a center located at t/2, a compressive region located between a surface of the glass article and the center, wherein the compressive region is under a compressive stress and extends from the surface to a depth of compression DOC; a sub-region within the compressive region in which a stress profile has a negative curvature, wherein the maximum absolute value of the negative curvature is between 20 MPa/(t (mm))2 and 4000 MPa/(t (mm))2; and a tensile region extending from the depth of compression DOC to at least the center of the glass article, wherein the tensile region is under a physical center tension CT.
In a twenty-second aspect, the glass article of the twenty-first aspect is provided wherein t is in a range from about 0.1 mm to about 2 mm.
In a twenty-third aspect, the glass article of the twenty-first or twenty-second aspect is provided wherein DOC is in a range from about 0.14t to about 0.35t.
In a twenty-fourth aspect, the glass article of any of the twenty-first through twenty-third aspects is provided wherein: a maximum compressive stress CS1 is at the first surface and is in a range from about 500 MPa to about 2,000 MPa, and the compressive region further comprises a sub-region in which the stress profile has a sub-region of positive curvature.
In a twenty-fifth aspect, the glass article of any of the twenty-first through twenty-fourth aspects is provided wherein: the glass article has a maximum compressive stress CS1 at the surface, and the compressive stress decreases to less than 50% of the maximum compressive stress at a depth of less than about 8 μm below the surface.
In a twenty-sixth aspect, the glass article of any of the twenty-first through twenty-fifth aspects is provided wherein the negative curvature has an absolute value exceeding 10 MPa/t2 over a sub-region, the sub-region having a spatial extent ranging from about 2% to about 25% oft.
In a twenty-seventh aspect, the glass article of any of the twenty-first through twenty-sixth aspects is provided wherein CT is in a range from about 40 MPa/(t (mm))1/2 to about 150 MPa/(t (mm))1/2.
In a twenty-eighth aspect, the glass article of any of the twenty-first through twenty-seventh aspects is provided wherein the glass article comprises an alkali aluminosilicate glass.
In a twenty-ninth aspect, the glass article of the twenty-eighth aspect is provided wherein the alkali aluminosilicate glass comprises at least about 4 mol % P2O5, wherein (M2O3 (mol %)/RxO (mol %))<1, wherein M2O3═Al2O3+B2O3, and wherein RxO is the sum of monovalent and divalent cation oxides present in the alkali aluminosilicate glass.
In a thirtieth aspect, the glass article of the twenty-eighth aspect is provided wherein the alkali aluminosilicate glass comprises: about 40 mol % to about 70 mol % SiO2; about 11 mol % to about 25 mol % Al2O3; about 2 mol % to about 15 mol % P2O5; about 10 mol % to about 25 mol % Na2O; about 13 to about 30 mol % RxO, where RxO is the sum of the alkali metal oxides, alkaline earth metal oxides, and transition metal monoxides present in the glass.
In a thirty-first aspect a method of strengthening a glass is provided. The method comprising: immersing a glass comprising first alkali cations in an ion exchange bath comprising second alkali cations to replace the first alkali cations within the glass with the second alkali cations from the ion exchange bath and form a first compressive layer extending from a first surface of the glass, wherein the glass has a thickness t, the second alkali cations are different from the first alkali cations, the first surface is opposite a second surface, the first compressive layer extends from the first surface to a first depth of compression DOC1, and the first compressive layer has a first compressive stress CS1; and diffusing the second alkali cations from the first surface to a center of the glass located at t/2, wherein stress in the glass varies as a function of the depth in the glass to form a stress profile. The stress profile comprises a first compressive region extending from the first surface to a depth d1 in the glass, wherein d1>0.06t, and at least a portion of the first region has a first slope m1, and a second compressive stress CS2 at the first surface, wherein CS2≤CS1; and a second compressive region extending from a depth of at least d1 to a second depth of compression DOC2 and having a second slope m2, wherein |m1|≤|m2|, and DOC2>DOC1.
In a thirty-second aspect, the method of the thirty-first aspect is provided wherein immersing the glass in the ion exchange bath comprising the second alkali cations also replaces the first alkali cations within the glass with the second alkali cations from the ion exchange bath to form a second compressive layer extending from the second surface of the glass.
In a thirty-third aspect, the method of the thirty-second aspect is provided wherein the first compressive layer and the second compressive layer are formed simultaneously.
In a thirty-fourth aspect, the method of any of the thirty-first through thirty-third aspects is provided wherein a slope of the stress profile at d1 is zero.
In a thirty-fifth aspect, the method of any of the thirty-first through thirty-fourth aspects is provided wherein the diffusing comprises a thermal diffusion step comprising heating the glass to a temperature in a range from about 400° C. to about 500° C.
In a thirty-sixth aspect, the method of the thirty-fifth aspect is provided wherein the thermal diffusion step comprises heating the glass for at least about 16 hours at the temperature.
In a thirty-seventh aspect, the method of any of the thirty-first through thirty-sixth aspects is provided wherein the ion exchange bath comprises at least 30 wt % of a salt comprising the first alkali cations.
In a thirty-eighth aspect, the method of any of the thirty-first through thirty-seventh aspects is provided further comprising immersing the glass in a second ion exchange bath following the step of immersing the glass in the ion exchange bath to form a surface compressive region comprising a third compressive stress CS3 at the first surface, wherein CS3>CS1.
In a thirty-ninth aspect, the method of the thirty-eighth aspect is provided wherein the second ion exchange bath comprises at least about 90 wt % of a salt comprising the second alkali cations.
In a fortieth aspect, the method of any of the thirty-first through thirty-ninth aspects is provided wherein the glass comprises an alkali aluminosilicate glass.
In a forty-first aspect, the method of the fortieth aspect is provided wherein the alkali aluminosilicate glass comprises at least about 4 mol % P2O5, wherein (M2O3 (mol %)/RxO (mol %))<1, M2O3═Al2O3+B2O3, and RxO is the sum of monovalent and divalent cation oxides present in the alkali aluminosilicate glass.
In a forty-second aspect, the method of the fortieth aspect is provided wherein the alkali aluminosilicate glass comprises: about 40 mol % to about 70 mol % SiO2; about 11 mol % to about 25 mol % Al2O3; about 2 mol % to about 15 mol % P2O5; about 10 mol % to about 25 mol % Na2O; about 10 to about 30 mol % RxO, where RxO is the sum of the alkali metal oxides, alkaline earth metal oxides, and transition metal monoxides present in the glass.
In a forty-third aspect, the method of any of the thirty-first through forty-second aspects is provided wherein the stress profile comprises a sub-region within the compressive region with a negative curvature, wherein the maximum absolute value of the negative curvature is at d1.
In a forty-fourth aspect, the method of forty-third aspect is provided wherein the maximum absolute value of the negative curvature is between 20 MPa/(t (mm))2 and 4,000 MPa/(t (mm))2.
In a forty-fifth aspect a consumer electronic product is provided. The consumer electronic product comprising: a housing having a front surface, a back surface and side surfaces; electrical components provided at least partially within the housing, the electrical components including at least a controller, a memory, and a display, the display being provided at or adjacent the front surface of the housing; and the glass article of any of the first through thirtieth aspects disposed over the display.
These and other aspects, advantages, and salient features will become apparent from the following detailed description, the accompanying drawings, and the appended claims.
In the following description, like reference characters designate like or corresponding parts throughout the several views shown in the figures. It is also understood that, unless otherwise specified, terms such as “top,” “bottom,” “outward,” “inward,” and the like are words of convenience and are not to be construed as limiting terms. In addition, whenever a group is described as comprising at least one of a group of elements and combinations thereof, it is understood that the group may comprise, consist essentially of, or consist of any number of those elements recited, either individually or in combination with each other. Similarly, whenever a group is described as consisting of at least one of a group of elements or combinations thereof, it is understood that the group may consist of any number of those elements recited, either individually or in combination with each other. Unless otherwise specified, a range of values, when recited, includes both the upper and lower limits of the range as well as any ranges therebetween. As used herein, the indefinite articles “a,” “an,” and the corresponding definite article “the” mean “at least one” or “one or more,” unless otherwise specified. It also is understood that the various features disclosed in the specification and the drawings can be used in any and all combinations.
As used herein, the terms “glass article” and “glass articles” are used in their broadest sense to include any object made wholly or partly of glass. Unless otherwise specified, all compositions are expressed in terms of mole percent (mol %).
As described herein, compressive stress (CS) and central tension or physical center tension (CT) are expressed in terms of megaPascals (MPa), depth of layer (DOL) and depth of compression (DOC) may be used interchangeably and are expressed in terms of microns (μm), where 1 μm=0.001 mm, and, unless otherwise specified, thickness (t) is expressed herein in terms of millimeters, where 1 mm=1,000 μm. Compressive stress (CS) is expressed herein as a positive value and central tension and physical center tension (CT) are expressed as negative values.
Compressive stress (including surface CS) is measured by surface stress meter (FSM) using commercially available instruments such as the FSM-6000, manufactured by Orihara Industrial Co., Ltd. (Japan). Surface stress measurements rely upon the accurate measurement of the stress optical coefficient (SOC), which is related to the birefringence of the glass. SOC in turn is measured according to Procedure C (Glass Disc Method) described in ASTM standard C770-16, entitled “Standard Test Method for Measurement of Glass Stress-Optical Coefficient,” the contents of which are incorporated herein by reference in their entirety.
As used herein, DOC means the depth at which the stress in the chemically strengthened alkali aluminosilicate glass article described herein changes from compressive to tensile. DOC may be measured by FSM or a scattered light polariscope (SCALP) depending on the ion exchange treatment. Where the stress in the glass article is generated by exchanging potassium ions into the glass article, FSM is used to measure DOC. Where the stress is generated by exchanging sodium ions into the glass article, SCALP is used to measure DOC. Where the stress in the glass article is generated by exchanging both potassium and sodium ions into the glass, the DOC is measured by SCALP, since it is believed the exchange depth of sodium indicates the DOC and the exchange depth of potassium ions indicates a change in the magnitude of the compressive stress (but not the change in stress from compressive to tensile); the exchange depth of potassium ions in such glass articles is measured by FSM.
Refracted near-field (RNF) method or SCALP may be used to measure the stress profile. When the RNF method is utilized to measure the stress profile, the maximum CT value provided by SCALP is utilized in the RNF method. In particular, the stress profile measured by RNF is force balanced and calibrated to the maximum CT value provided by a SCALP measurement. The RNF method is described in U.S. Pat. No. 8,854,623, entitled “Systems and methods for measuring a profile characteristic of a glass sample”, which is incorporated herein by reference in its entirety. In particular, the RNF method includes placing the glass article adjacent to a reference block, generating a polarization-switched light beam that is switched between orthogonal polarizations at a rate of between 1 Hz and 50 Hz, measuring an amount of power in the polarization-switched light beam and generating a polarization-switched reference signal, wherein the measured amounts of power in each of the orthogonal polarizations are within 50% of each other. The method further includes transmitting the polarization-switched light beam through the glass sample and reference block for different depths into the glass sample, then relaying the transmitted polarization-switched light beam to a signal photodetector using a relay optical system, with the signal photodetector generating a polarization-switched detector signal. The method also includes dividing the detector signal by the reference signal to form a normalized detector signal and determining the profile characteristic of the glass sample from the normalized detector signal.
The stress profiles may also be determined from the spectra of bound optical modes for TM and TE polarization by using the inverse Wentzel-Kramers-Brillouin (IWKB) method as taught in U.S. Pat. No. 9,140,543, the contents of which are hereby incorporated by reference in its entirety.
Described herein are strengthened glass articles having a stress profile (σ) that varies as a function (σ(x)) of position (x) within the glass article. The position (x) may refer to the depth into the glass article from a surface thereof. The stress profile has a slope (S) at any point that is a first derivative of the stress (σ) with position (x); i.e., S=(dσ/dx). The slope of a segment or portion of the stress profile that closely approximates a straight line is defined as the average slope for regions that are well approximated as straight segments. The slope rate (SR) or stress curvature of the stress profile is the second derivative of the stress (σ) with position (x); i.e., SR=(d2σ/dx2).
A schematic cross-sectional view of the strengthened glass article is shown in
In one aspect, the stress in the strengthened glass article varies as a function of the depth, and has a compressive layer extending from a first surface of the glass to a depth of compression (DOC) or depth of layer (DOL). The compressive layer is under a compressive stress (CS). The stress profile of the glass article is schematically shown in
The cations from the ion exchange bath may then be diffused from the surface of the glass to the center of the glass at a depth of t/2 in a thermal diffusion step. In some embodiments, this is achieved by allowing the ion exchange to proceed for longer time periods (e.g., 16 hours or more at 460° C.), and/or, in some embodiments, by a subsequent thermal diffusion (heating) step. The cations are allowed to diffuse from opposite surfaces of the glass until the diffused cations meet at the center of the glass 330. The thermal diffusion step in some embodiments results in a decrease in the compressive stress at the surface to a second compressive stress (CS2) and an increase in the depth of compression to a second depth of compression (DOC2) such that CS2≤CS1 and DOC2>DOC1.
The thermal diffusion step, in some embodiments, includes heating the glass to a temperature in a range from about 400° C. to about 500° C. for times ranging from at least about 0.5 hour to about 40 hours.
The slope (S1) following the first ion exchange step, expressed as CS1/DOC where CS1 is the compressive stress at the surface of the glass after the first ion exchange step, the absolute value of slope S1 (|S1|) is in a range from about 0.5 MPa/um to about 30 MPa/μm. In some embodiments, the slope (S1) has an absolute value (|S1|), where 1.2 MPa/μm≤|S1|≤20 MPa/μm, 1.5 MPa/μm≤|S1|≤15 MPa/μm, and all ranges and subranges therebetween. In still other embodiments, slope (S1) has an absolute value |S1| in a range from about 0.6 MPa/μm to about 15 MPa/um, 0.8 MPa/μm≤|S1|≤10 MPa/μm, 1.5 MPa/μm≤|S1|≤10 MPa/μm, and all ranges and subranges therebetween.
Following the thermal diffusion step, the glass has a stress profile 300, schematically shown in
In some embodiments, the glass article is strengthened by a two-step ion exchange process. Here the glass article is ion exchanged a second time following the thermal diffusion step. The second ion exchange is carried out in an ion exchange bath that differs in composition from the first ion exchange bath. The stress profile 350 obtained following the second ion exchange step is schematically shown in
Stress profiles observed for samples that were subjected to a first ion exchange followed by thermal treatment and second ion exchange as described herein are plotted in
In those embodiments in which the glass article is strengthened by a single-step ion exchange process, the slope S, which is expressed as CS/DOC, has an absolute value |S| in a range from about 0.5 MPa/μm (or 88 MPa/(88 μm/2)) to about 200 MPa/μm (or 1,000 MPa/5 μm). In other embodiments, the slope (S), has an absolute value (|S|) in a range from about 0.6 MPa/μm (or 88 MPa/140 μm) to about 200 MPa/μm (or 1,000 MPa/5 μm).
The slope rate (SR) of the stress profile in the compressive layer between the surface and the depth of compression (DOC) includes at least one region where the SR value changes sign, indicating that the slope (S) of the stress profile is not a monotonically increasing or decreasing function. Instead, the slope (S) changes from a decreasing to an increasing pattern or vice-versa, thus defining a S-shaped region of the stress profile.
In some embodiments, the depth of compression is at least 20% of the thickness; i.e., DOC≥0.2t. The depth of compression (DOC), in some embodiments, is in a range from about 0.05t to about 0.35t, and all ranges and subranges therebetween, for example, in some embodiments from about 0.14t to about 0.35t, in other embodiments from about 0.15t to about 0.25t, and in still other embodiments, from about 0.20t to about 0.25t. The thickness (t) of the strengthened glass article is in a range from about 0.1 mm to about 2 mm, such as about 0.4 mm or less.
The compressive layer, in some embodiments, may further comprise a near-surface region having a compressive stress (CS) at the surface in a range from about 50 MPa to about 1,000 MPa or, in other embodiments, from about 500 MPa to about 2,000 MPa, and all ranges and subranges therebetween. The stress profile in the compressive stress layer may further include a first sub-region having a negative curvature and a second sub-region having a positive curvature. As used herein, the term “negative curvature” means that the stress profile in that region is concaved downward and “positive curvature” means that the stress profile in that region is concaved upward. In some embodiments, the absolute value of the negative curvature exceeds 10 MPa/(t (mm))2 over a sub-region whose spatial extent ranges from about 2% to about 25% of the thickness (t). In some embodiments, the maximum absolute value of the negative curvature is between about 20 MPa/(t (mm))2 and about 4,000 MPa/(t (mm))2, and all ranges and subranges therebetween, for example, in some embodiments, from about 40 MPa/(t (mm))2 to about 2000 MPa/(t (mm))2, and, in still other embodiments, from about 80 MPa/(t (mm))2 to about 1,000 MPa/(t (mm))2. The stress profile in the second sub-region may, in some embodiments, include an inflection point. The physical center tension (CT) is in a range from about 40 MPa/(t (mm))1/2 to about 150 MPa/(t (mm))1/2 and all ranges and subranges therebetween, for example, in some embodiments, from about 42 MPa/(t (mm))1/2 to about 100 MPa/(t (mm))1/2.
The curvature of the stress profile is measured by identifying a portion of a stress profile that is of interest. A quadratic polynomial fit is applied to the portion of interest, with the resulting coefficient of the highest order term being the curvature of the portion of interest. The curvature will have units of MPa/mm2 when the y-axis of the stress profile is measured in MPa and the x-axis of the stress profile is measured in mm. Additionally, when the x-axis of the stress profile is measured in μm, the curvature may be converted to units of MPa/mm2 by the appropriate conversion factor.
In some cases the measured stress profile may include artifacts, or noise, as a result of the measurement process. In such cases, the artifacts are removed before determining the curvature of the stress profile to increase the accuracy of the calculated curvature. The artifacts may be removed by any appropriate processing method known in the art. For example, the artifacts may be removed by applying a low-pass filter to the stress profile or to the TE and TM index profiles (for example, when the IWKB method is used to determine the stress profile) from which the stress profile is extracted.
In some embodiments, the compressive stress within the compressive layer may decrease from a maximum compressive stress (CS) at the surface of the glass article to less than 50% of the maximum compressive stress within a depth of less than about 8 μm below the surface.
In some embodiments, the glass article is ion exchanged and annealed (i.e., subjected to a thermal diffusion step). In particular embodiments, the glass is ion exchanged in a single-step ion exchange (SIOX) process followed by an annealing process. In other embodiments, the ion exchange process is a two-step or dual ion exchange (DIOX) process comprising a first ion exchange step followed by an optional thermal anneal or diffusion step, which is then followed by a second ion exchange step in which the first ion exchange bath has a composition that is different from that of the second ion exchange bath. In some embodiments, the second ion exchange bath comprises at least 90% KNO3 by weight and less than 10% NaNO3 by weight. In other embodiments, the second ion exchange bath comprises at least 95 wt % KNO3 with NaNO3 accounting for the balance of the bath. In still other embodiments, the second ion exchange bath contains essentially 100% KNO3 by weight. The second ion exchange step adds a compressive stress “spike”—i.e., a sharp increase in compressive stress—in the region immediately adjacent to the surface of the glass.
In those embodiments in which a single-step ion exchange process is used to strengthen the glass article, the article is ion exchanged at a temperature ranging from about 300° C. to about 500° C. in an ion exchange bath containing from about 25% to about 100% KNO3 and 0% to about 75% NaNO3 by weight. The ion exchange bath may include other materials, such as silicic acid or the like, to improve bath performance.
The glasses described herein are ion exchangeable alkali aluminosilicate glasses, which, in some embodiments, are formable by down-draw processes, such as slot-draw, or fusion-draw processes that are known in the art. In particular embodiments, such glasses may have a liquidus viscosity of at least about 100 kiloPoise (kP), or at least about 130 kP. In one embodiment, the alkali aluminosilicate glass comprises SiO2, Al2O3, P2O5, and at least one alkali metal oxide (R2O), wherein 0.75≤[(P2O5 (mol %)+R2O (mol %))/M2O3 (mol %)]≤1.2, where M2O3═Al2O3+B2O3. In some embodiments, the alkali aluminosilicate glass comprises or consists essentially of: from about 40 mol % to about 70 mol % SiO2; from 0 mol % to about 28 mol % B2O3; from 0 mol % to about 28 mol % Al2O3; from about 1 mol % to about 14 mol % P2O5; and from about 12 mol % to about 16 mol % R2O and, in certain embodiments, from about 40 to about 64 mol % SiO2; from 0 mol % to about 8 mol % B2O3; from about 16 mol % to about 28 mol % Al2O3; from about 2 mol % to about 12 mol % P2O5; and from about 10 to about 16 mol % R2O, or from about 12 mol % to about 16 mol % R2O, where R2O includes Na2O. In some embodiments, 11 mol %≤M2O3≤30 mol %; in some embodiments, 13 mol %≤RxO≤30 mol %, where RxO is the sum of alkali metal oxides, alkaline earth metal oxides, and transition metal monoxides present in the glass. In some embodiments, the glass is lithium-free. In other embodiments, the glass may comprise up to about 10 mol % Li2O, or up to about 7 mol % Li2O. These glasses are described in U.S. patent application Ser. No. 13/305,271, granted as U.S. Pat. No. 9,346,703, entitled “Ion Exchangeable Glass with Deep Compressive Layer and High Damage Threshold,” filed Nov. 28, 2011, by Dana Craig Bookbinder et al. and claiming priority from U.S. Provisional Patent Application No. 61/417,941, filed on Nov. 30, 2010, and having the same title, the contents of which are incorporated herein by reference in their entirety.
In certain embodiments, the alkali aluminosilicate glass comprises at least about 2 mol % P2O5, or at least about 4 mol % P2O5, wherein (M2O3 (mol %)/RxO (mol %))<1, wherein M2O3═Al2O3+B2O3, and wherein RxO is the sum of monovalent and divalent cation oxides present in the alkali aluminosilicate glass. In some embodiments, the monovalent and divalent cation oxides are selected from the group consisting of Li2O, Na2O, K2O, Rb2O, Cs2O, MgO, CaO, SrO, BaO, and ZnO. In some embodiments, the glass is lithium-free and comprises or consists essentially of from about 40 mol % to about 70 mol % SiO2; from about 11 mol % to about 25 mol % Al2O3; from about 2 mol % P2O5, or from about 4 mol % to about 15 mol % P2O5; from about 10 mol % Na2O, or from about 13 mol % to about 25 mol % Na2O; from about 13 to about 30 mol % RxO, where RxO is the sum of the alkali metal oxides, alkaline earth metal oxides, and transition metal monoxides present in the glass; from about 11 mol % to about 30 mol % M2O3, where M2O3═Al2O3+B2O3; from 0 mol % to about 1 mol % K2O; from 0 mol % to about 4 mol % B2O3, and 3 mol % or less of one or more of TiO2, MnO, Nb2O5, MoO3, Ta2O5, WO3, ZrO2, Y2O3, La2O3, HfO2, CdO, SnO2, Fe2O3, CeO2, As2O3, Sb2O3, Cl, and Br; wherein 1.3≤[(P2O5+R2O)/M2O3]≤2.3, where R2O is the sum of monovalent cation oxides present in the glass. In some embodiments, the glass is lithium-free. In other embodiments, the glass may comprise up to about 10 mol % Li2O, or up to about 7 mol % Li2O. The glass is described in U.S. Pat. No. 9,156,724 by Timothy M. Gross, entitled “Ion Exchangeable Glass with High Crack Initiation Threshold,” filed Nov. 15, 2012, and U.S. Pat. No. 8,756,262 by Timothy M. Gross, entitled “Ion Exchangeable Glass with High Crack Initiation Threshold,” filed Nov. 15, 2012, both claiming priority to U.S. Provisional Patent Application No. 61/560,434 filed Nov. 16, 2011. The contents of the above patent and applications are incorporated herein by reference in their entirety.
In other embodiments, the alkali aluminosilicate glass comprises SiO2, Al2O3, P2O5, and greater than about 1 mol % K2O, wherein the glass has a coefficient of thermal expansion (CTE) of at least about 90×10−7° C.−1. In some embodiments, the glass comprises or consists essentially of: from about 57 mol % to about 75 mol % SiO2 (i.e., 57 mol %≤SiO2≤75 mol %); from about 6 mol % to about 17 mol % Al2O3 (i.e., 6 mol %≤Al2O3≤17 mol %); from about 2 mol % to about 7 mol % P2O5 (i.e., 2 mol %≤P2O5≤7 mol %); from about 14 mol % to about 17 mol % Na2O (i.e., 14 mol %≤Na2O≤17 mol %); and greater than about 1 mol % to about 5 mol % K2O (i.e., 1 mol %<K2O≤5 mol %). In some embodiments, the glass comprises or consists essentially of or comprises: from about 57 mol % to about 59 mol % SiO2 (i.e., 57 mol %≤SiO2≤59 mol %); from about 14 mol % to about 17 mol % Al2O3 (i.e., 14 mol %≤Al2O3≤17 mol %); from about 6 mol % to about 7 mol % P2O5 (i.e., 6 mol %≤P2O5≤7 mol %); from about 16 mol % to about 17 mol % Na2O (i.e., 16 mol %≤Na2O≤17 mol %); and greater than about 1 mol % to about 5 mol % K2O (i.e., 1 mol %<K2O≤5 mol %). In certain embodiments, the glass further comprises up to about 2 mol % MgO (i.e., 0 mol %≤MgO≤2 mol %) and/or up to about 1 mol % CaO (i.e., 0 mol %≤CaO≤1 mol %). In some embodiments, the glass is substantially free of MgO. In some embodiments, the glass is substantially free of B2O3 and/or lithium or Li2O. These glasses are described in U.S. patent application Ser. No. 14/465,888, published as U.S. Patent Application Publication No. 2015/0064472, entitled “Damage Resistant Glass with High Coefficient of Thermal Expansion,” filed Aug. 22, 2014, by Timothy M. Gross et al. and claiming priority from U.S. Provisional Patent Application No. 61/870,301, filed on Aug. 27, 2013, and having the same title, the contents of which are incorporated herein by reference in their entirety.
In another aspect, a method of strengthening a glass having a thickness (t) and achieving the stress profiles described herein is provided. The method comprises immersing the glass in an ion exchange bath comprising alkali cations (e.g., K+) that are different from alkali cations (e.g., Na+, Li+) that are present in the glass, and replacing alkali cations within the glass with the alkali cations from the ion exchange bath. The ion exchange forms a compressive layer extending from the surface of the glass to a first depth of compression (DOC1), where the compressive layer is under a first compressive stress (CS1).
The cations from the ion exchange bath are then diffused from the surface of the glass to the center of the glass at a depth of t/2. In some embodiments, this is achieved by allowing the ion exchange to continue for longer periods (e.g., 16 hours or more at 460° C.), and/or, in some embodiments, by a subsequent thermal diffusion (heating) step. The cations are allowed to diffuse from opposite surfaces of the glass until the diffused cations meet at the center of the glass. The diffusion step in some embodiments results in a decrease in the compressive stress at the surface to a second compressive stress (CS2) and an increase in the depth of compression to a second depth of compression (DOC2) such that CS2≤CS1 and DOC2>DOC1.
The thermal diffusion step, in some embodiments, includes heating the glass to a temperature in a range from about 400° C. to about 500° C. for times ranging from 0.5 hour to 40 hours.
In some embodiments, the method may further include a second ion exchange following either the first ion exchange or the thermal diffusion step. As previously described hereinabove, the second ion exchange bath has a composition that is different from that of the first ion exchange bath. In some embodiments, the second ion exchange bath comprises at least 90% KNO3 by weight and less than 10% NaNO3 by weight. In other embodiments, the second ion exchange bath comprises at least 95 wt % KNO3 with NaNO3 accounting for the balance of the bath. In still other embodiments, the second ion exchange bath contains essentially 100% KNO3 by weight. The second ion exchange step adds a compressive stress “spike”—i.e., a sharp increase in compressive stress—in the region immediately adjacent to the surface of the glass, creating a third compressive stress (CS3) at the surface, where CS3>CS1.
Under ideal conditions, the shape and values of the stress profile in an ion exchanged glass should obey a classic diffusion equation. The solution for this equation indicates that, in the case of a single boundary through which the ions diffuse without limit, the stress profile should be a complementary error function (erfc(x)). As used herein, the terms “error function” and “erf” refer to the function that is twice the integral of a normalized Gaussian function between 0 and x/σ√2. The terms “complementary error function” and “erfc” are equal to one minus the error function; i.e., erfc(x)=1−erf(x). For a bounded case—e.g., where ions diffuse from opposite surfaces to the center of the glass—diffusion of strengthening cations follows a complementary error function until the ions meet at the center of the glass, after which the whole diffusion profile may be better approximated by a parabolic shape profile for the ionic distribution. The stress profile is directly related to the ionic distribution inside the glass. The stress profile should therefore be similar to the ionic distribution, regardless of whether the distribution of ions according to a complementary error function or a parabolic function.
A significant divergence between expected and observed stress profiles may occur for certain glasses. This is likely due to stress relaxation present in the glass and additional annealing effects. Modeled and measured stress profiles of ion exchanged glass having a nominal composition of about 57 mol % SiO2, 0 mol % B2O3, about 17 mol % Al2O3, about 7% P2O5, about 17 mol % Na2O, about 0.02 mol % K2O, and about 3 mol % MgO and a thickness of 800 μm are plotted over a wide range of diffusion times in
A more detailed view of the stress profile in
Further details of modeled (dashed line) and experimentally determined (solid line) stress profiles for the case of 40 hour diffusion/ion exchange at 460° C. are shown in
The S-shaped stress profile may occur in instances when glass is ion exchanged in a bath that is “poisoned” to a particular level (e.g., comprising greater than 30 wt % NaNO3). Modeled (dashed lines) and measured (solid lines) stress profiles for 800 μm thick glass having a nominal composition of about 57 mol % SiO2, 0 mol % B2O3, about 17 mol % Al2O3, about 7% P2O5, about 17 mol % Na2O, about 0.02 mol % K2O, and about 3 mol % MgO are shown in
The modeled stress profiles directly overlap each other, and thus show that the expected diffusion profile based on a diffusion length of 2 (D×Time)1/2, where D is the diffusion coefficient at a certain temperature, is basically the same for the different cases investigated. Therefore, one would expect that the diffusion at 460° C. for 60 hours (line a in
Energy (surface, stored, total), physical center tension (CT), surface compressive stress (CS), depth of compression (DOC), and results of mechanical testing (4-point bend testing, abraded ring-on-ring (AROR), and drop onto 30 grit sandpaper) for the samples shown in
The strengthened glass articles described herein also demonstrate improved surface strength when subjected to abraded ring-on-ring (AROR) testing. The strength of a material is defined as the stress at which fracture occurs. The abraded ring-on-ring test is a surface strength measurement for testing flat glass specimens, and ASTM C1499-09(2013), entitled “Standard Test Method for Monotonic Equibiaxial Flexural Strength of Advanced Ceramics at Ambient Temperature,” serves as the basis for the ring-on-ring abraded ROR test methodology described herein. The contents of ASTM C1499-09 are incorporated herein by reference in their entirety. The glass specimen was abraded prior to ring-on-ring testing with 90 grit silicon carbide (SiC) particles that are delivered to the glass sample using the method and apparatus described in Annex A2, entitled “abrasion Procedures,” of ASTM C158-02(2012), entitled “Standard Test Methods for Strength of Glass by Flexure (Determination of Modulus of Rupture). The contents of ASTM C158-02 and the contents of Annex 2 in particular are incorporated herein by reference in their entirety.
Prior to ring-on-ring testing a surface of the glass sample was abraded as described in ASTM C158-02, Annex 2, to normalize and/or control the surface defect condition of the sample using the apparatus shown in Figure A2.1 of ASTM C158-02. The abrasive material is sandblasted onto the sample surface at a load of 15 psi using an air pressure of 45 psi. After air flow was established, 5 cm3 of abrasive material was dumped into a funnel and the sample was sandblasted for 5 seconds after introduction of the abrasive material.
Stress profiles measured for a different ion exchangeable alkali aluminosilicate glass, which is described in U.S. patent application Ser. No. 14/465,888, published as U.S. Patent Application Publication No. 2015/0064472, which was ion exchanged at 460° C. for 28 hours, are shown in
Other examples of S-shape stress profiles are shown in
Modeled stress profiles for glass having thicknesses of 0.8 mm and 0.5 mm produced by a combination of ion exchange and thermal diffusion are shown in
Strengthened glasses having S-shaped stress profiles appear to have a higher frangibility limit (i.e., the physical center tension (CT) above which explosive fragmentation and ejection of small fragment occurs upon insult or impact) than glasses having other profiles having a comparable depth of compression (DOC). An example of an S-shaped profile obtained for 0.4 mm thick non-frangible glass having a nominal composition of about 57 mol % SiO2, 0 mol % B2O3, about 17 mol % Al2O3, about 7% P2O5, about 17 mol % Na2O, about 0.02 mol % K2O, and about 3 mol % MgO is shown in
A glass article with a thickness of 0.4 mm was subjected to a first ion exchange, a thermal treatment, and a second ion exchange to form a S-shaped stress profile in the glass article. The glass article included a glass containing about 57 wt % SiO2, about 16 wt % Al2O3, about 17 wt % Na2O, about 3 wt % MgO, and about 7 wt % P2O5. The first ion exchange was carried out by immersing the glass article for 11 hours in a bath containing 38 wt % NaNO3 and 62 wt % KNO3 at a temperature of 450° C. The ion exchanged glass article was then subjected to thermal treatment for 6.5 hours at 420° C. The subsequent ion exchange was carried out by immersing the thermally treated glass article for 11 minutes in a bath containing 0.5 wt % NaNO3 and 99.5 wt % KNO3 at a temperature of 390° C.
The index profiles for transverse magnetic (TM) and transverse electric (TE) guided light were extracted by the IWKB procedure and are shown in
The fabrication process that produces the stress profile shown in
The strengthened articles disclosed herein may be incorporated into another article such as an article with a display (or display articles) (e.g., consumer electronics, including mobile phones, tablets, computers, navigation systems, and the like), architectural articles, transportation articles (e.g., automotive, trains, aircraft, sea craft, etc.), appliance articles, or any article that requires some transparency, scratch-resistance, abrasion resistance or a combination thereof. An exemplary article incorporating any of the strengthened articles disclosed herein is shown in
While typical embodiments have been set forth for the purpose of illustration, the foregoing description should not be deemed to be a limitation on the scope of the disclosure or appended claims. Accordingly, various modifications, adaptations, and alternatives may occur to one skilled in the art without departing from the spirit and scope of the present disclosure or appended claims.
This application claims the benefit of priority under 35 U.S.C. § 119 of U.S. Provisional Application Ser. No. 62/264,495, filed Dec. 8, 2015, and U.S. Provisional Application Ser. No. 62/280,376, filed Jan. 19, 2016, the contents of which are relied upon and incorporated herein by reference in their entirety.
| Number | Name | Date | Kind |
|---|---|---|---|
| 3798013 | Inoue et al. | Mar 1974 | A |
| 8756262 | Zhang | Jun 2014 | B2 |
| 8854623 | Fontaine et al. | Oct 2014 | B2 |
| 9140543 | Allan et al. | Sep 2015 | B1 |
| 9156724 | Gross | Oct 2015 | B2 |
| 9346703 | Bookbinder et al. | May 2016 | B2 |
| 9359251 | Bookbinder et al. | Jun 2016 | B2 |
| 9487434 | Amin et al. | Nov 2016 | B2 |
| 9593042 | Hu et al. | Mar 2017 | B2 |
| 9828282 | Beall | Nov 2017 | B2 |
| 10150698 | Amin | Dec 2018 | B2 |
| 10271442 | Gross | Apr 2019 | B2 |
| 20120194974 | Weber | Aug 2012 | A1 |
| 20130224492 | Bookbinder | Aug 2013 | A1 |
| 20140087193 | Cites et al. | Mar 2014 | A1 |
| 20150030834 | Morey et al. | Jan 2015 | A1 |
| 20150064472 | Gross et al. | Mar 2015 | A1 |
| 20150239775 | Amin et al. | Aug 2015 | A1 |
| 20150239776 | Amin et al. | Aug 2015 | A1 |
| 20150259244 | Amin et al. | Sep 2015 | A1 |
| 20150368148 | Duffy et al. | Dec 2015 | A1 |
| 20150368153 | Pesansky et al. | Dec 2015 | A1 |
| 20160083292 | Tabe et al. | Mar 2016 | A1 |
| 20160122239 | Amin et al. | May 2016 | A1 |
| 20160122240 | Oram et al. | May 2016 | A1 |
| 20160257605 | Amin et al. | Sep 2016 | A1 |
| 20160264452 | Amin et al. | Sep 2016 | A1 |
| Number | Date | Country |
|---|---|---|
| 201310569877 | May 2015 | CN |
| 1291631 | Mar 2003 | EP |
| 2014084588 | Jul 2014 | KR |
| 2011097314 | Aug 2011 | WO |
| 2015031148 | Mar 2015 | WO |
| 2015127483 | Aug 2015 | WO |
| 2015127583 | Sep 2015 | WO |
| 2015195419 | Dec 2015 | WO |
| 2015195465 | Dec 2015 | WO |
| 2016007910 | Jan 2016 | WO |
| 2016014937 | Jan 2016 | WO |
| 2016057590 | Apr 2016 | WO |
| Entry |
|---|
| International Search Report and Written Opinion PCT/US2016/065518 dated Mar. 31, 2017. |
| Green, D. J. “Critical parameters in the processing of engineered stress profile glasses”, Journal of Non-Crystalline Solids (2003), 316(1), 35-41. |
| Number | Date | Country | |
|---|---|---|---|
| 20170158556 A1 | Jun 2017 | US |
| Number | Date | Country | |
|---|---|---|---|
| 62280376 | Jan 2016 | US | |
| 62264495 | Dec 2015 | US |