The invention relates to a sampling device for molten metals, especially for iron or steel melts, having a carrier tube and a sample chamber fixed in the carrier tube with an inlet piece for the molten metal flowing into the sample chamber.
Such sampling devices are known from Japanese Utility Model Application No. 24340/1971 (Public Disclosure No. 24187/1972). Here, a sampling device is described having a thick-walled inlet piece, in whose wall a pre-chamber is incorporated. In Japanese Utility Model Application Public Disclosure No. 83217/1985 a sampling device is described having a sample chamber, which forms a structural unit with the material of a pre-chamber. In German Patent DE 2714636 C2 a sample chamber is described having an inlet tube, whose cross section is reduced multiple times in the central part of the tube by crimping on one side.
Further sampling devices are known from Japanese Published Patent Application (Kokai) JP 07306196A. The sampling device described here has an inlet tube that is tapered on its inlet end into the sample chamber. At this tapered section, the sample can be separated from the inlet end.
The invention is based on the object of improving the known sampling devices in order to guarantee reliable sampling.
The object is achieved by a sampling device for molten metals having a carrier and a sample chamber fixed in the carrier tube, having an inlet piece for the molten metal flowing into the sample chamber, with the inlet piece expediently formed on the sample chamber, having an inlet tube arranged in the inlet piece, and the inlet tube having an outlet into the sample chamber and an inlet opening on its other end. The outlet as well as the inlet opening of the inlet tube has a reduced cross section relative to the central part of the inlet tube. The inlet tube is formed of quartz glass, and the wall of the inlet tube is crimped toward the axis of the inlet tube at its two ends.
The in-flowing molten metal is thereby slowed so that destruction of the sample chamber during the sampling is prevented to the greatest extent. By the practical double-walled inlet, the heat transfer at this position is minimal, so that molten metal does not solidify on the wall of the inlet tube. Thus, the arrangement of the quartz tube, which exhibits a relatively low heat expansion, in an inlet piece formed on the sample chamber is therefore also advantageous, because the separation of the sample from the metal located in the inlet tube is thereby reliably guaranteed.
A deoxidation means for the in-flowing molten metal can be arranged in the sample chamber. The sample chamber can be formed from two, preferably metallic, half shells. By the arrangement according to the invention, a melting off of the sample chamber or an adhesion of the half shells is prevented. The inlet tube forms a sort of pre-chamber, which is used as a mixing chamber. In addition, it can be expedient if the inlet tube has a cross-sectional change in at least one position between the outlet and the inlet opening, compared with the adjacent regions of the inlet tube, because this condition additionally favors the separation of the solidified sample from the solidified material inside the inlet tube.
The foregoing summary, as well as the following detailed description of the invention, will be better understood when read in conjunction with the appended drawings. For the purpose of illustrating the invention, there is shown in the drawings an embodiment which is presently preferred. It should be understood, however, that the invention is not limited to the precise arrangements and instrumentalities shown. In the drawings:
A sample chamber 2 is arranged within or on a carrier tube 1 (
An inlet piece 7 made of the same material attaches directly to the sample chamber 2, in which an inlet tube 8 made of quartz glass is arranged (
The size of the cross-sectional reduction of the outlet 9 can be adapted to the appropriate application. The lower the over-heating of the melt, the smaller the diameter of the outlet 9 should be relative to the inner diameter of the inlet tube 8. For example, for sampling from the converter with an over-heating of approximately 60° C., a functional sampling device is constructed with a reduction of the inner diameter of the tube from 8 mm to 5.5 mm for an outer tube diameter of 10 mm.
With the use of inlet tubes 8 having a wall thickness of at least 2 mm, it can be useful to provide a further change in diameter of the inlet tube 8. However, smaller wall thicknesses of the inlet tube 8 are generally more advantageous.
After the molten metal flows into the sample chamber 2, the melt begins to solidify. At the reduced cross section of the outlet 9 of the inlet tube 8, the solidified molten metal cracks, so that the sample can be removed from the sampling device without the solidified metal located in the inlet tube 8.
It will be appreciated by those skilled in the art that changes could be made to the embodiments described above without departing from the broad inventive concept thereof. It is understood, therefore, that this invention is not limited to the particular embodiments disclosed, but it is intended to cover modifications within the spirit and scope of the present invention as defined by the appended claims.