SANDWICH COMPOSITE BOARD AND PREPARATION METHOD THEREOF

Description

TECHNICAL FIELD

The present disclosure belongs to the technical field of composite board preparation, and specifically relates to a sandwich composite board and a preparation method thereof.

BACKGROUND

With the gradual improvement of people’s living standards, the requirements for interior decoration are getting higher. Composite boards of various materials are becoming more and more popular in the application of interior decoration, and are widely used in doors and interior walls. However, at present, the overall cost of the composite boards meeting the application requirements is relatively high, and the composite boards are not fully mature in terms of their comprehensive properties such as fastness, compression resistance, impact resistance, thermal insulation and noise reduction. At present, composite boards are generally formed by sandwich boards, in which outer panels and a core material are bonded by glue, hot-pressed and dried, then cut and polished, and finally painted and formed. However, such composite boards are prone to cracking and delamination after being used for a period of time, and their properties of sound insulation, noise reduction and thermal insulation could not meet the actual application requirements. Therefore, the use of the composite boards in the architecture industry or decoration industry is limited to some extent.

It has been well recognized that noise pollution is the third major public hazard in today’s society, and there are more and more noise sources. Noise would have an impact on human nervous system, cardiovascular system, digestive system, immune system, and even fetal development. Indoor noise pollution has become one of the widely concerned noise problems at present. Some relevant noise standards for residential, commercial, industrial or other areas have been made by the authority, which has put forward higher requirements for architecture and decorative materials of buildings. It has become a hot spot of current research and development that how to realize noise reduction in the architecture industry or decoration industry via updating or upgrading of new materials. It is desirable to design composite boards with good integrity and good thermal insulation, sound insulation and noise reduction, which would achieve application development in architecture industry, decoration industry or the like.

SUMMARY

The present disclosure aims to provide a sandwich composite board and a preparation method thereof.

To achieve the above purposes, the present disclosure provides technical solutions as follows.

A sandwich composite board, includes an upper panel layer, a core material layer, and a lower panel layer in sequence from top to bottom, wherein the upper panel layer and the core material layer are integrally formed, and the lower panel layer and the core material layer are integrally formed, the upper panel layer and the lower panel layer are glass or fiber-reinforced resin-based composite sheets; and the core material layer consists of 30-70 parts by mass of aerogel, 10-35 parts by mass of a resin, and 2-4 parts by mass of an expandable microsphere foaming agent.

In an embodiment, the glass is tempered glass, semi-tempered glass, ultra-white glass, float glass, coated glass, or film covered glass.

In an embodiment, fibers of the fiber-reinforced resin-based composite sheets are selected from the group consisting of glass fibers, carbon fibers, boron fibers, and aramid fibers; and the resin of the fiber-reinforced resin-based composite sheet is selected from the group consisting of a unsaturated polyester resin, a vinyl resin, a polyurethane resin, an epoxy resin, a polycarbonate resin, a polyamide resin, and a phenolic resin. The “fiber-reinforced resin-based composite sheet” in the present disclosure is commercially available or can be prepared according to prior art.

In an embodiment, the aerogel is selected from the group consisting of silicon dioxide aerogel, aluminum oxide aerogel, titanium dioxide aerogel, and zirconium dioxide aerogel.

In an embodiment, the resin of the core material layer is a thermosetting resin or a thermoplastic resin.

In an embodiment, the thermosetting resin is one of a phenolic resin, an ureaformaldehyde resin, a melamine-formaldehyde resin, an epoxy resin, a unsaturated resin, a polyurethane, or a polyimide; and the thermoplastic resin is one of a polyethylene resin, a polypropylene resin, a polycarbonate resin, a polyvinyl chloride resin, a polystyrene resin, a polyamide resin, a polyformaldehyde resin, a polyphenyl ether resin, or a polysulphone resin.

In an embodiment the expandable microsphere foaming agent has a particle size of 10-50 µm.

The present disclosure also provides two methods for preparing the sandwich composite board.

Specifically, the first method includes the following steps of:

(1) adding the resin of the core material layer in a container and heating at 110- 160° C. to allow the resin to melt and obtain slurry A, then cooling the slurry A to 25-70° C. by standing;
(2) adding the aerogel and the expandable microsphere foaming agent to the slurry A obtained in step (1), and mixing uniformly to obtain slurry B;
(3) flatly placing the lower panel layer, spreading the slurry B obtained in step (2) uniformly on the lower panel layer, and then placing the upper panel layer on the slurry B to obtain a sandwich composite layer; and
(4) hot-press molding the sandwich composite layer obtained in step (3) to obtain the sandwich composite board.

The second method includes the following steps of:

(1) adding the aerogel, the resin, and the expandable microsphere foaming agent according to the compositions of the core material layer in a container and mixing uniformly to obtain a mixture A;
(2) placing the mixture A obtained in step (1) into a nonwoven bag and sealing the bag to obtain a core material B;
(3) flatly placing the lower panel layer, spreading the core material B obtained in step (2) on the lower panel layer, and then placing the upper panel layer on the core material B to obtain a sandwich composite layer;
(4) hot-press molding the sandwich composite layer obtained in step (3) to obtain the sandwich composite board.

In an embodiment, in the hot-press molding of step (4) in the above first method and second method, the temperature is 100 to 180° C., the pressure is 2 to 5 MPa, and the time is 30 minutes to 8 hours.

The embodiments of the present disclosure would achieve the following benefits.

(1) The thickness of the sandwich composite board prepared according to the present disclosure is controllable. The sandwich composite boards with different thicknesses can be prepared by adjusting the spreading thickness of the slurry B or adjusting the amount of the mixture A in the nonwoven bag.

(2) The density of the sandwich composite board prepared according to the present disclosure is controllable. The density of the sandwich composite board can be significantly reduced by adding the expandable microsphere foaming agent. The density of the sandwich composite board can be controlled by adjusting the amount of the expandable microsphere foaming agent.

(3) The integrity of the sandwich composite board prepared according to the present disclosure is good. The sandwich composite board is integrated by hot-press molding. If the upper panel layer and the lower panel layer are the fiber-reinforced resin-based composite sheets, they can be integrally solidified and formed with the core material layer under the condition of hot-pressing, and the interlayer bonding is good. If the upper panel layer and the lower panel layer are glass layers, since glass is partially softened and fused with the resin in the core material layer under the condition of hot-pressing, it would ensure good integrity between the layers, and avoid separation or peeling of the layers during use. In addition, the mixture A is placed in a nonwoven bag and then subject to hot-press molding, which would avoid dropping of powder or damaging of corner, and ensure the integrity of the product. When the mixture A is directly placed between the upper panel layer and the lower panel layer for hot-press molding, dropping of powder or damaging of corner would occur.

(4) The sandwich composite board prepared according to the present disclosure has good effects of thermal insulation, sound insulation and noise reduction. Aerogel and an expandable microsphere foaming agent are used as a sandwich structure in the present disclosure. The expandable microsphere foaming agent would possess porosity after foaming, so that the resulting foam would have certain thermal insulation and sound insulation properties, which would be maintained after being combined with the aerogel.

(5) The sandwich composite board prepared according to the present disclosure has good properties of thermal insulation, sound insulation and noise reduction, which would meet the growing social requirements, and could be widely used in architecture or decoration industry or the like.

DETAILED DESCRIPTION

The present disclosure will now be described in detail with reference to the specific examples. It should be understood that examples described herein are only for explaining the present disclosure, and not intended to limit the present disclosure.

Example 1

A sandwich composite board includes an upper panel layer, a core material layer and a lower panel layer in sequence from top to bottom. The upper panel layer and the core material layer are integrally formed, and the lower panel layer and the core material layer are integrally formed. The upper panel layer and the lower panel layer are carbon fiber-reinforced phenolic resin-based composite sheets. The core material layer consists of 60 parts by mass of silicon dioxide aerogel, 35 parts by mass of a polyethylene resin, and 4 parts by mass of an expandable microsphere foaming agent, i.e., EM406 (with average diameter of 20 µm, which is commercially available from NOF CORPORATION).