1. Field of the Invention
The present invention relates to a scented wafer and, more particularly, to a wafer that is impregnated with a scented material that emits a scent when heated that can be used for any suitable purpose, for example, aromatherapy, insect repellant, wild life attractant, medicinal uses, deodorants and odor control, perfume release and other desired or suitable purposes.
2. Description of the Prior Art
Various devices are currently used to emit scents in a surrounding area. For example, scented candles may be burned or candle tarts may be heated and melted to emit a scent. In the case of a candle, there is a safety hazard resulting from an open flame.
In the case of a candle tart, it turns to liquid when heated and forms a pool that emits a fragrance. The pool is in the form of a hot liquid and thus may spill and result in a burn to the user or damage to a supporting surface.
A need has arisen, therefore, for a new and improved device for emitting a scent when heated that is not subject to the disadvantages of a candle or candle tart. The scented wafer of the present invention meets this need.
The wafer of the present invention may be of any suitable size or shape and comprises a heat resistant body formed of any suitable material that is constructed for holding, flow, capillary effect and release of fragrant scents or other scents to be used for any desired or suitable purpose, such as aromatherapy, insect repellant, wild life attractant, medicinal uses, deodorants and odor control, perfume release. The term “scent” as used herein is intended to cover any material that will release a detected or undetected vapor when heated for any useful or desired purpose.
The body of the wafer is impregnated in any suitable manner with a suitable or desired scented wax or other liquid scent that will melt or vaporize when exposed to heat to emit the scent in the surrounding area. The rate of release of the scent is controlled by the porosity and capillary function of the body material as well as the temperature of the applied heat, and can be varied by the use of fiber denier and length blends in the body material. For example, finer fibers will create tighter structures to obtain a slow release of the scented material when heated and a greater surface area for pickup and holding of the scented material. Larger fibers will create more coarse and open structures for a quicker release of the scented material when heated and will have less surface for initial pickup and holding of the scented material
The body of the wafer is formed of a heat-resistant material that does not melt when the scented material impregnated therein is heated and melted. The body material may soften during heating of the scented material but retains its structural integrity and will thereafter harden when cooled so that the wafer can be reused. When depleted of scented material, the wafer may in some circumstances be impregnated again with a scented material so that it can be reused.
If the wafer is to be used with an open flame, the body material and fibers will be of a flame retardant material. If a conventional plate warmer or similar heater is to be used, the body material and fibers can be of a material that does not melt at the temperature of the plate warmer or heater.
The body 12 of the wafer is impregnated in any suitable manner with a suitable scented wax or other liquid scent that will melt or vaporize when exposed to heat to emit the scent in a surrounding area. The rate of release of the scent is controlled by the porosity and capillary function of the body material, as well as the temperature of the applied heat, and can be varied by the use of fiber denier and length blends in the body material. For example, finer fibers will create tighter structures to obtain a slow release of the scented material when heated and a greater surface area for pick up and holding of the scented material. Larger fibers will create more coarse and open structures for a quicker release of the scented material when heated and will have less surface for initial pick up and holding of the scented material. As an illustrative example, fibers may range from 0.5 micron to 25 denier and from lengths of 1/16 inch to 10 inches.
The body 12 of the wafer is formed of a suitable material that does not melt when the scented material impregnated therein is heated and melted. The body material may soften during heating of the scented material but retains its structural integrity and will thereafter harden when cooled so that the wafer can be reused. In some cases, when the wafer is depleted of scented material, it may be impregnated again with a desired scented material so that it can be reused.
If the wafer 10 is to be used with an open flame, the body material and fibers will be of a flame retardant material. Fibers such as but not limited to meta and para aramids, modacrylics, flame retardant polyesters, as well as oxidized polyacrylonitrile carbonized fibers may be used because they are inherently flame retardant. Glass fibers and blends of glass fibers can also be used in higher temperature applications. In general, the wafer may be comprised of flame retardant fibers such as modacrylics, flame retardant polyesters, Nomex, Kevlar, PBO, PBI, Meta Aramids and Para Aramids, glasses, silicas, polyacrylonitrile or carbon, blends of these materials or any other suitable materials.
If conventional plate warmers or similar heaters are to be used, the body material may be formed of any suitable material such as synthetics or blends of suitable materials that will resist melting at temperatures ranging from about 130-140° F., or any other desired temperature range.
As illustrative examples, the body 12 may be formed of any nonwoven, woven, meltblown, spunbond, thermo bonded, extruded or resin bonded material comprised of any natural or synthetic blend and varied deniers of fibers, or of any suitable capillary wicking material. The density can be adjusted so that its porosity will be suitable for holding and release of any desired or suitable scent or scents.
The body 12 may have any suitable or desired shape, such as flat form, two dimensional, three dimensional or multi-dimensional. Also, the body 12 may be formed in any suitable or desired manner, such as pressed and cut, pressed cavity formed and cut or extruded formed and cut.
Any suitable scented wax or other fragrance or scented material may be used. Specific illustrative examples of suitable waxes and fragrances or scents are as follows:
Waxes
Animal and plant based waxes
(all natural waxes)
Petroleum based wax
Synthetic based wax
Fragrances or Scents
Oil based, water based and alcohol based which can be derived from natural and/or synthetic ingredients.
The amount of fragrance or scent can range, e.g., from 1% to 100% but typically falls in the 10%-30% range by weight
As shown in
A general comparison of the amount of wax and fragrance used by a conventional wax tart and different illustrative embodiments of the scented wafer of the present invention is as follows:
Conventional Wax Tart
Scented Wafer (single large fiber wafer)
Scented Wafer (6 mini fiber wafers)
6 wafers at 8 grams=48 grams total
Fragrance or scent (15% load)—6 wafers at 1.2 grams=7.2 grams total
Wax—6 wafers at 6.8 grams=40.8 grams total
It is apparent, therefore, that different embodiments of the scented wafer of the present invention can use less fragrance or scent and wax than a conventional wax tart.
The scented wafer 10 of the present invention possesses many advantages over conventional scented candles, wax tarts or other known scent releasing devices, some of which are as follows:
1. A significantly longer life span;
2. Can be easily reused after a heating cycle;
3. Very safe to use since there is no open flame or exposed hot melted wax;
4. Can be constructed with various fibrous structures to control the rate of release of the scented material impregnated therein;
5. Uses less wax and fragrance to create a desired scent;
6. Can be easily and safely stored;
7. Is inexpensive to manufacture;
8. Can be created with numerous surfaces to present a large surface area for emission of scent;
9. Can be constructed of different fibrous materials depending on the scented material and on the heat source used to melt or vaporize the scented material impregnated therein; and
10. Can be used to release a scent for any suitable or desired purpose.
While the invention has been described in connection with what is presently considered to be the most practical and preferred embodiments, it is to be understood that the invention is not to be limited to the disclosed embodiments, but on the contrary, is intended to cover various modifications and equivalent arrangements included within the spirit and scope of the appended claims.
The present application claims the priority of Provisional Application No. 61/869,234 filed on Aug. 23, 2013, Provisional Application No. 61/969,305 filed on Mar. 24, 2014 and Provisional Application No. 62/000,029 filed on May 19, 2014.
Number | Date | Country | |
---|---|---|---|
20160022859 A1 | Jan 2016 | US |
Number | Date | Country | |
---|---|---|---|
61869234 | Aug 2013 | US | |
61969305 | Mar 2014 | US | |
62000029 | May 2014 | US |