Patent Grant
9663643
The invention relates to a PVC-free polymer compound for producing scavenger-containing seals or liners for screw caps, in particular twist crown corks.
Oxygen-sensitive foods and beverages around the world have a great brand significance. In this context, beer, fruit juices and tea-based beverages have to be mentioned in the first place. To keep these filling goods unchanged in terms of taste and composition for as long as possible, the packaging industry has developed a range of technologies.
In traditional bottles with metal closures, for example, barrier technologies as described in EP-0503124 A1 are preferably used. In addition, also oxygen-depleting compounds as described in EP-0328337 B1 are utilized. Both technologies are used for sealants of crown caps, but are restricted to use in so-called pry-off crown caps so far.
In the case of bottles made of PET and similar plastics, however, mono- or multilayer composites which should increase the oxygen barrier of the PET are applied. Common polymers in these cases are special polyamides or ethylene vinyl alcohol polymers (EVOH). In addition, also here oxygen-scavenging compounds can be introduced in one of the layers. As an alternative with a passive barrier, extremely thin coatings of carbon or silicon oxides can be applied in the bottle interior.
Twist crown caps are advantageous compared to the conventional crown caps for the consumer because they can be opened without tools. Usually, twist crown caps are produced from PVC-containing compounds in industry, because only then the strict requirements on the tightness on the one hand and the opening forces on the other hand are ensured. The tightness of the twist crown cap must avoid leakage of the fill content and contamination of the filling good. However, it must be guaranteed that the container can be opened without too much effort by a rotary movement of the twist crown cork, but does not open undesired. As an additional requirement for the seal, it must also be ensured that the opening and closing may be repeated as often as desired without a loss of the tightness and/or the opening forces.
It is advantageous to use compounds for seals of container closures which do not contain PVC components, neither in the form of PVC in general nor in the form of flexible PVC in particular. In the conventional incineration of household waste, halogen-containing plastics generate acidic gases whose escape into the atmosphere is harmful. In addition, even small amounts of PVC impede the mechanical recycling of plastic waste. Moreover, such PVC-based sealing elements require the use of plasticizers, which are also undesirable for health reasons.
There is therefore a need for twist-crown closures, which have a polymer-based sealing insert and comprise an oxygen-depleting component, which insert is not based on PVC.
With all these characteristics, the seals must also comply with the above-mentioned requirements concerning the possible migration of their chemical constituents.
Thus, it is one major objective of the invention to provide a sealing insert or liner for the manufacture of twist-crown closures, which allows equipping of the container closure with a polymer-based sealing element which has an oxygen-scavenging component, does not contain PVC, complies with legal regulations concerning the migration and meets the directives in regard to testing for extraneous flavors (off-flavors).
The formulation according to the invention allows the production of twist crown caps that on the one hand meet the requirements in regard to the tightness and the opening force and on the other hand comprise an oxygen-depleting component, but do not consist of PVC.
To achieve this and other objects, a sealing insert for twist crown corks according to the invention is provided with the features as defined in claim 1. Advantageous embodiments are defined in the dependent claims.
We have surprisingly found that certain compounds with a suitable Shore A hardness, and preferably based on TPE, polyolefin, and white oil, meet these mentioned requirements particularly well.
We have further found that substances such as ascorbic acid and other compounds known in the art are suitable to be used as an acceptable additive to create an oxygen barrier for twist crowns and the oxygen-scavenging functionality can thus be optimized. We have also found that sulfites, especially metal sulfites, and in particular sodium sulfite, are a suitable additive to create the above-mentioned oxygen barrier for twist crown caps.
A compound for a seal for a twist crown cap, to which sulfite was added as an oxygen-scavenging component, must of course also comply with the corresponding standards e.g. regarding a off-flavor test according to DIN 10950, as described in the “Leitfaden Verschlüsse” (guideline for closures) of the Packaging Technology Department of the TWA (Technical Scientific Committee) of the VLB Berlin (Berlin, March 2009).
We have found that it is possible to control the functionality of the oxygen-scavenging component (especially of the sulfite) via the average particle size. By reduction of the particle size and accompanying enlargement of the inner surface, the availability of active agent (e.g. sodium sulfite) is increased, since the sodium sulfate resulting from the reaction at the outer side of the scavenger particle forms a diffusion barrier for further oxygen and thus increases the barrier effect. So, the necessary amount of additive can be minimized. The activity of the scavenger particles can be modified using various additives, as also described in patent EP-1050556 B1.
The polymer compounds for seals for twist crown caps according to the invention also achieve the reduction of oxygen ingress in comparison with a scavenger-free reference material. The oxygen ingress into the filling good was determined by the “Total Package Oxygen” method (Orbisphere technology). For this, bottles are filled with a beer simulant (in terms of pH and CO2 content) in a glove box and the total oxygen content is measured non-destructively. Even after 150 days, ingress of less than 0.4 ppm oxygen can be achieved. An oxygen-induced taste effect is usually assumed at concentrations above 1 ppm. So, in comparison with the scavenger-free reference material, a reduction of oxygen ingress by a factor of 3 can at least be achieved.
In the herein-described twist crown caps, the sealing element is formed as a deposit on the inner surface of the container closure, similarly as it is the case for the known PVC-containing twist crowns.
The formulation according to the invention permits the production of PVC-free sealing compositions for twist crowns, which are equipped with at least one oxygen-depleting component.
Moreover, the formulation according to the invention permits the production of a sealing compound for twist crowns which can be foamed by chemical or physical blowing agents.
In preferred embodiments, the compound comprises between 2% to 20% copolymer consisting of polypropylene (PP) and polyethylene (PE), more preferably the material comprises between 5% to 15% copolymer.
In special preferred embodiments, the compound comprises between 5% to 25% polyethylene (low-density polyethylene, LDPE), more preferably the material comprises between 10% to 20% LDPE.
In other preferred embodiments, the compound comprises not more than 10%, preferably not more than 7%, more preferably not more than 4% and even more preferably not more than 1% of lubricants.
In further preferred embodiments, the compound comprises between 10% to 40% thermoplastic elastomers based on styrene-ethylene-butylene-styrene (SEBS), and more preferably the material comprises between 20% to 30% of TPE based on SEBS.
Preferably, the compound comprises between 20% to 45% medicinal white oil, and particularly preferably, the material comprises between 30% to 40% medicinal white oil.
In additionally preferred embodiments, the compound comprises between 10% to 30% polyethylene (linear low-density polyethylene, LLDPE), preferably the material comprises between 15% to 25% LLDPE.
In preferred embodiments, the compound comprises between 1% to 10% sodium sulfite, preferably the material comprises between 4% to 8% sodium sulfite.
In other preferred embodiments, the compound comprises between 20% to 100% of at least one block copolymer, wherein the block copolymer preferably is an interpolymer of ethylene and at least one C3-C20 alpha-olefin, or a copolymer of ethylene and one C3-C20 alpha-olefin or of ethylene and one C3-C20 alpha-olefin in case in combination with other unsaturated monomers.
Furthermore, it is preferred that the material of the sealing insert comprises no plasticizers.
According to the invention, said material has a Shore A hardness of 50-90, preferably a Shore A hardness of 60-80 and more preferably of 65-76.
It is also preferred that the polymer compounds exhibit a compression set between 20% to 90%, preferably between 30 to 60%, and more preferably between 40% to 50% in the compressive deformation test analogous to ASTM D395-97 Method B after 22 hours of storage at 70° C. and a compression of 25%.
According to the invention, the average particle size of the sodium sulfite is adjusted to smaller than 20 μm, preferably smaller than 12 μm and particularly preferably smaller than 7 μm.
According to the invention, the selection of the polymer compounds for the twist crowns should be carried out in such a way that constant, low opening values in the range of 0.678 Nm (6 lbf·in) to 1.130 Nm (10 lbf·in) with a target value of 0.791 Nm (7 lbf·in), according to the Packaging Technology Department of the TWA of the VLB, can be reached.
The polymer compounds for seals for twist crowns according to the invention can maintain a pressure of more than 8 bar after pasteurization (determined on Secure Seal Tester from the company Secure Pak).
It should be noted that the parameters of the opening forces, as well as of the pressure maintenance and the oxygen entry, are dependent on the width of the bottle opening and the sealing profile which might be provided.
Optionally, pigments can be added to the formulations of the compounds.
It has also been shown that other additives such as waxes and silicones may be added to the polymer compound, for example to improve processing and performance characteristics.
An exemplary formulation comprises:
The oxygen uptake was determined by the “Total Oxygen” method (Orbisphere technology). For this, bottles are filled with a beer simulant (in terms of pH and CO2 content) in a glove box and the total oxygen content is measured non-destructively. “Total package Oxygen (ppm)” in this context is the total concentration of oxygen in the filling container (bottle).
“Pasteurized” means that the beer simulans has been pasteurized before closing.
| Filing Document | Filing Date | Country | Kind | 371c Date |
|---|---|---|---|---|
| PCT/EP2009/008766 | 12/8/2009 | WO | 00 | 10/18/2012 |
| Publishing Document | Publishing Date | Country | Kind |
|---|---|---|---|
| WO2011/069520 | 6/16/2011 | WO | A |
| Number | Name | Date | Kind |
|---|---|---|---|
| 5060818 | Doi et al. | Oct 1991 | A |
| Number | Date | Country |
|---|---|---|
| 0250057 | Dec 1987 | EP |
| 0503124 | Sep 1992 | EP |
| 0328337 | Jan 1994 | EP |
| 1116747 | Jul 2001 | EP |
| 1050556 | Jun 2006 | EP |
| 1816086 | Aug 2007 | EP |
| 1894974 | Mar 2008 | EP |
| 2058379 | May 2009 | EP |
| Entry |
|---|
| International Search Report and Written Opinion for International Application No. PCT/EP2009/008766, European Patent Office, Netherlands, mailed on Mar. 16, 2010, 11 Pages. |
| Number | Date | Country | |
|---|---|---|---|
| 20130041087 A1 | Feb 2013 | US |