The invention relates to the field of seals, particularly seals made of thermoplastic vulcanisates.
A seal is a device for closing (sealing) a gap, or making a joint fluid-tight (the fluid being either gas or liquid). A seal is commonly a resilient (usually elastomeric) form that can conform tightly to two surfaces to form a fluid-tight joint. Seals can be divided into static and dynamic seals. A static seal is a seal designed for a use where there is no relative movement between the seal and the surfaces with which the seal interacts. A dynamic seal is a seal designed for use where there is relative movement between the seal and at least one of the surfaces with which it interacts, e.g. rotary movement of a shaft relative to a housing, or reciprocating movement of a rod or piston in a cylinder.
Seals at joints, particularly in the automotive industry, are conventionally made from vulcanised material (thermosets), such as rubber and high performance elastomers (Silicones, Vamac®, Viton®, etc.). Vulcanised materials must be moulded and then vulcanised to form cross-links. Use of a seal made of a vulcanisate in cooperation with a thermoplastic part or parts therefore requires several steps, including shaping the seal, vulcanisation and finally a step of assembly, whereby the seal must be assembled to the thermoplastic part or parts with which it will form a seal.
Thermoplastic vulcanisates (TPV's) are blends consisting of a continuous thermoplastic phase with a phase of vulcanised elastomer dispersed therein. TPVs combine many desirable characteristics of cross-linked rubbers with some characteristics of thermoplastic elastomers. An example of a TPV is disclosed in WO 2004/029155 (E.I. DuPont de Nemours), which discloses a curable thermoplastic blend comprising (a) from 15 to 60 wt % of a polyalkylene phthalate polyester polymer or copolymer and; (b) from 40 to 85 wt % of a cross-linkable poly(meth)acrylate or polyethylene/(meth)acrylate vulcanisate rubber in combination with an effective amount of peroxide free-radical initiator and an organic diene co-agent to cross-link the rubber during extrusion or injection moulding of the curable thermoplastic elastomeric blend. When the curable blend is melt extruded, the result is a TPV that can be processed in many ways like a thermoplastic, but which has the characteristics of a cross-linked rubber.
In contrast to conventional vulcanisates (thermosets), TPV's can be injection moulded, without further curing. This greatly facilitates the production of seals from TPV's. It also means that a seal formed from a TPV can be “overmoulded” with a thermoplastic part, using a two-step injection process. The thermoplastic is injected into the mould, with a partition preventing it from filling the part of the mould into which the TPV will be injected. The partition is then removed, and the TPV is injected into the remaining part of the mould. This forms a single part of two components: a structural thermoplastic part and a sealing part of TPV, in which the sealing part is integral with the structural thermoplastic part, thus eliminating an assembly step, and making a single piece.
However, TPV's suffer other drawbacks that limit their use in seals. Conventional seals in automotive uses are compression seals, such as so-called “O-ring” seals. The sealing force with a compression seal results exclusively from compression of the elastomeric material. TPV's suffer from poor compression set (in the order of or greater than 30%), meaning that a compression seal made of a TPV does not fully return to its original shape after compression, resulting in poor seal performance. The problem of poor compression set is worsened at high temperature.
A need remains for seals made of materials that can be processed with the ease of a thermoplastic, and yet which can maintain seal performance over a prolonged period.
In a first aspect, the invention provides a static seal made from polymer material comprising or consisting essentially of a TPV, wherein the TPV is selected from:
(1) a TPV comprising:
(A) from at or about 15 to 60 weight percent of a polyalkylene phthalate polyester polymer or copolymer continuous phase; and
(B) from at or about 40 to 85 weight percent of a polyethylene/(meth)acrylate rubber dispersed phase, wherein the rubber is dynamically cross-linked with a peroxide free radical initiator and an organic diene co-agent;
(2) a TPV comprising:
25 to 60% by weight of a polyamide resin and 75 to 40% by weight of a rubber component; said rubber component comprising 20 to 80% by weight of a hydrogenated nitrile group-containing rubber and 80 to 20% by weight of an acrylic rubber, said rubber component being dispersed in the form of cross-linked particles in said polyamide resin; said hydrogenated nitrile group-containing rubber being a hydrogenated copolymer containing 10 to 60% by weight of a vinyl nitrile, 15 to 90% by weight of a conjugated diene and 0 to 75% by weight of a monomer copolymerizable with vinyl nitrile and said conjugated diene, said hydrogenated nitrile-group containing rubber having an iodine value of 120 or less; said acrylic rubber being a copolymer of at least one acrylate selected from the group consisting of an alkyl acetate and an alkoxy-substituted alkyl acrylate with at least one compound selected from the group consisting of a nonconjugated diene, a conjugated diene, a dihydrodicyclopentadienyl group-containing (meth)acrylate, an epoxy group-containing ethylenically unsaturated compound, an active halogen-containing ethylenically unsaturated compound and a carboxyl group-containing ethylenically unsaturated compound;
(3) A TPV made by a method comprising:
(I) mixing:
(C) a rheologically stable polyamide resin having a melting point or glass transition temperature of 25° C. to 275° C.;
(D) a silicone base comprising (D′) 100 parts by weight of a diorganopolysiloxane gum having a plasticity of at least 30 and having an average of at least 2 alkenyl groups in its molecule and (D″) 5 to 200 parts by weight of a reinforcing filler, the weight ratio of said silicone base to said polyamide resin being greater than 35:65 to 85:15;
(E) for each 100 parts by weight of said polyamide resin, a compatibilizer selected from (i) from 0.1 to 5 parts by weight of a coupling agent having a molecular weight of less than 800 which contains at least two groups independently selected from ethylenically unsaturated group, epoxy, anhydride, silanol, carboxyl, hydroxyl, alkoxy, having 1 to 20 carbon atoms or oxazoline in its molecule, (ii) from 0.1 to 10 parts by weight of a functional diorganopolysiloxane having at least one group selected from epoxy, anhydride, silanol, carboxyl, amine, alkoxy having 1 to 20 carbon atoms or oxazoline in its molecule, or (iii) from 0.1 to 10 parts by weight of a copolymer comprising at least one diorganopolysiloxane block and at least one block selected from polyamide, polyether, polyurethane, polyurea, polycarbonate and polyacrylate;
(F) an organohydrido silicon compound which contains an average of at least 2 silicon-bonded hydrogen groups in its molecule; and
(G) a hydrosilation catalyst;
components (F) and (G) being present in an amount sufficient to cure said diorganopolysiloxane (D′); and
(II) dynamically curing said diorganopolysiloxane (D′);
(4) A TPV made by a method comprising:
(I) mixing:
(H) a thermoplastic resin comprising more than 50 percent by volume of a polyester resin said thermoplastic resin having a softening point of 23° C. to 300° C.;
(I) a silicone elastomer comprising (I′) 100 parts by weight of a diorganopolysiloxane gum having a plasticity of at least 30 and having an average of at least 2 alkenyl groups in its molecule and, optionally, (I″) up to 200 parts by weight of a reinforcing filler, the weight ratio of said silicone elastomer to said thermoplastic resin is from 35:65 to 85:15;
(J) a glycidyl ester compatibilizer;
(K) an organohydrido silicon compound which contains an average of at least 2 silicon-bonded hydrogen groups in its molecule; and
(L) a hydrosilation catalyst;
components (K) and (L) being present in an amount sufficient to cure said diorganopolysiloxane (I′); and
(II) dynamically vulcanizing said diorganopolysiloxane (I′);
(5) a TPV comprising:
In a second aspect, the invention provides a process for making a static flexion seal, comprising moulding, extruding or shaping a TPV to form a flexion seal, wherein the TPV is selected from:
(1) a TPV comprising:
(A) from at or about 15 to 60 weight percent of a polyalkylene phthalate polyester polymer or copolymer continuous phase; and
(B) from at or about 40 to 85 weight percent of a polyethylene/(meth)acrylate rubber dispersed phase, wherein the rubber is dynamically cross-linked with a peroxide free radical initiator and an organic diene co-agent;
(2) a TPV comprising:
25 to 60% by weight of a polyamide resin and 75 to 40% by weight of a rubber component; said rubber component comprising 20 to 80% by weight of a hydrogenated nitrile group-containing rubber and 80 to 20% by weight of an acrylic rubber, said rubber component being dispersed in the form of cross-linked particles in said polyamide resin; said hydrogenated nitrile group-containing rubber being a hydrogenated copolymer containing 10 to 60% by weight of a vinyl nitrile, 15 to 90% by weight of a conjugated diene and 0 to 75% by weight of a monomer copolymerizable with vinyl nitrile and said conjugated diene, said hydrogenated nitrile-group containing rubber having an iodine value of 120 or less; said acrylic rubber being a copolymer of at least one acrylate selected from the group consisting of an alkyl acetate and an alkoxy-substituted alkyl acrylate with at least one compound selected from the group consisting of a nonconjugated diene, a conjugated diene, a dihydrodicyclopentadienyl group-containing (meth)acrylate, an epoxy group-containing ethylenically unsaturated compound, an active halogen-containing ethylenically unsaturated compound and a carboxyl group-containing ethylenically unsaturated compound;
(3) A TPV made by a method comprising:
(I) mixing:
(C) a rheologically stable polyamide resin having a melting point or glass transition temperature of 25° C. to 275° C.;
(D) a silicone base comprising (D′) 100 parts by weight of a diorganopolysiloxane gum having a plasticity of at least 30 and having an average of at least 2 alkenyl groups in its molecule and (D″) 5 to 200 parts by weight of a reinforcing filler, the weight ratio of said silicone base to said polyamide resin being greater than 35:65 to 85:15;
(E) for each 100 parts by weight of said polyamide resin, a compatibilizer selected from (i) from 0.1 to 5 parts by weight of a coupling agent having a molecular weight of less than 800 which contains at least two groups independently selected from ethylenically unsaturated group, epoxy, anhydride, silanol, carboxyl, hydroxyl, alkoxy, having 1 to 20 carbon atoms or oxazoline in its molecule, (ii) from 0.1 to 10 parts by weight of a functional diorganopolysiloxane having at least one group selected from epoxy, anhydride, silanol, carboxyl, amine, alkoxy having 1 to 20 carbon atoms or oxazoline in its molecule, or (iii) from 0.1 to 10 parts by weight of a copolymer comprising at least one diorganopolysiloxane block and at least one block selected from polyamide, polyether, polyurethane, polyurea, polycarbonate and polyacrylate;
(F) an organohydrido silicon compound which contains an average of at least 2 silicon-bonded hydrogen groups in its molecule; and
(G) a hydrosilation catalyst;
components (F) and (G) being present in an amount sufficient to cure said diorganopolysiloxane (D′); and
(II) dynamically curing said diorganopolysiloxane (D′);
(4) A TPV made by a method comprising:
(I) mixing:
(H) a thermoplastic resin comprising more than 50 percent by volume of a polyester resin said thermoplastic resin having a softening point of 23° C. to 300° C.;
(I) a silicone elastomer comprising (I′) 100 parts by weight of a diorganopolysiloxane gum having a plasticity of at least 30 and having an average of at least 2 alkenyl groups in its molecule and, optionally, (I″) up to 200 parts by weight of a reinforcing filler, the weight ratio of said silicone elastomer to said thermoplastic resin is from 35:65 to 85:15;
(J) a glycidyl ester compatibilizer;
(K) an organohydrido silicon compound which contains an average of at least 2 silicon-bonded hydrogen groups in its molecule; and
(L) a hydrosilation catalyst;
components (K) and (L) being present in an amount sufficient to cure said diorganopolysiloxane (I′); and
(II) dynamically vulcanizing said diorganopolysiloxane (I′);
(5) a TPV comprising:
In a third aspect, the invention provides a dual component moulded article, comprising:
a first component made of a first polymer material; and
a sealing component comprising a static flexion seal made from polymer material comprising or consisting essentially of a TPV selected from:
(1) a TPV comprising:
(A) from at or about 15 to 60 weight percent of a polyalkylene phthalate polyester polymer or copolymer continuous phase; and
(B) from at or about 40 to 85 weight percent of a polyethylene/(meth)acrylate rubber dispersed phase, wherein the rubber is dynamically cross-linked with a peroxide free radical initiator and an organic diene co-agent;
(2) a TPV comprising:
25 to 60% by weight of a polyamide resin and 75 to 40% by weight of a rubber component; said rubber component comprising 20 to 80% by weight of a hydrogenated nitrile group-containing rubber and 80 to 20% by weight of an acrylic rubber, said rubber component being dispersed in the form of cross-linked particles in said polyamide resin; said hydrogenated nitrile group-containing rubber being a hydrogenated copolymer containing 10 to 60% by weight of a vinyl nitrile, 15 to 90% by weight of a conjugated diene and 0 to 75% by weight of a monomer copolymerizable with vinyl nitrile and said conjugated diene, said hydrogenated nitrile-group containing rubber having an iodine value of 120 or less; said acrylic rubber being a copolymer of at least one acrylate selected from the group consisting of an alkyl acetate and an alkoxy-substituted alkyl acrylate with at least one compound selected from the group consisting of a nonconjugated diene, a conjugated diene, a dihydrodicyclopentadienyl group-containing (meth)acrylate, an epoxy group-containing ethylenically unsaturated compound, an active halogen-containing ethylenically unsaturated compound and a carboxyl group-containing ethylenically unsaturated compound;
(3) A TPV made by a method comprising:
(I) mixing:
(C) a rheologically stable polyamide resin having a melting point or glass transition temperature of 25° C. to 275° C.;
(D) a silicone base comprising (D′) 100 parts by weight of a diorganopolysiloxane gum having a plasticity of at least 30 and having an average of at least 2 alkenyl groups in its molecule and (D″) 5 to 200 parts by weight of a reinforcing filler, the weight ratio of said silicone base to said polyamide resin being greater than 35:65 to 85:15;
(E) for each 100 parts by weight of said polyamide resin, a compatibilizer selected from (i) from 0.1 to 5 parts by weight of a coupling agent having a molecular weight of less than 800 which contains at least two groups independently selected from ethylenically unsaturated group, epoxy, anhydride, silanol, carboxyl, hydroxyl, alkoxy, having 1 to 20 carbon atoms or oxazoline in its molecule, (ii) from 0.1 to 10 parts by weight of a functional diorganopolysiloxane having at least one group selected from epoxy, anhydride, silanol, carboxyl, amine, alkoxy having 1 to 20 carbon atoms or oxazoline in its molecule, or (iii) from 0.1 to 10 parts by weight of a copolymer comprising at least one diorganopolysiloxane block and at least one block selected from polyamide, polyether, polyurethane, polyurea, polycarbonate and polyacrylate;
(F) an organohydrido silicon compound which contains an average of at least 2 silicon-bonded hydrogen groups in its molecule; and
(G) a hydrosilation catalyst;
components (F) and (G) being present in an amount sufficient to cure said diorganopolysiloxane (D′); and
(II) dynamically curing said diorganopolysiloxane (D′);
(4) A TPV made by a method comprising:
(I) mixing:
(H) a thermoplastic resin comprising more than 50 percent by volume of a polyester resin said thermoplastic resin having a softening point of 23° C. to 300° C.;
(I) a silicone elastomer comprising (I′) 100 parts by weight of a diorganopolysiloxane gum having a plasticity of at least 30 and having an average of at least 2 alkenyl groups in its molecule and, optionally, (I″) up to 200 parts by weight of a reinforcing filler, the weight ratio of said silicone elastomer to said thermoplastic resin is from 35:65 to 85:15;
(J) a glycidyl ester compatibilizer;
(K) an organohydrido silicon compound which contains an average of at least 2 silicon-bonded hydrogen groups in its molecule; and
(L) a hydrosilation catalyst;
components (K) and (L) being present in an amount sufficient to cure said diorganopolysiloxane (I′); and
(II) dynamically vulcanizing said diorganopolysiloxane (I′);
(5) a TPV comprising:
In a fourth aspect, the invention provides a process for making a dual component moulded article, comprising the steps of:
injection moulding into a mould a first polymer material, to form a first component; and
injection moulding into the mould a TPV to form a sealing component, wherein the TPV is selected from:
(1) a TPV comprising:
(A) from at or about 15 to 60 weight percent of a polyalkylene phthalate polyester polymer or copolymer continuous phase; and
(B) from at or about 40 to 85 weight percent of a polyethylene/(meth)acrylate rubber dispersed phase, wherein the rubber is dynamically cross-linked with a peroxide free radical initiator and an organic diene co-agent;
(2) a TPV comprising:
25 to 60% by weight of a polyamide resin and 75 to 40% by weight of a rubber component; said rubber component comprising 20 to 80% by weight of a hydrogenated nitrile group-containing rubber and 80 to 20% by weight of an acrylic rubber, said rubber component being dispersed in the form of cross-linked particles in said polyamide resin; said hydrogenated nitrile group-containing rubber being a hydrogenated copolymer containing 10 to 60% by weight of a vinyl nitrile, 15 to 90% by weight of a conjugated diene and 0 to 75% by weight of a monomer copolymerizable with vinyl nitrile and said conjugated diene, said hydrogenated nitrile-group containing rubber having an iodine value of 120 or less; said acrylic rubber being a copolymer of at least one acrylate selected from the group consisting of an alkyl acetate and an alkoxy-substituted alkyl acrylate with at least one compound selected from the group consisting of a nonconjugated diene, a conjugated diene, a dihydrodicyclopentadienyl group-containing (meth)acrylate, an epoxy group-containing ethylenically unsaturated compound, an active halogen-containing ethylenically unsaturated compound and a carboxyl group-containing ethylenically unsaturated compound;
(3) A TPV made by a method comprising:
(I) mixing:
(C) a rheologically stable polyamide resin having a melting point or glass transition temperature of 25° C. to 275° C.;
(D) a silicone base comprising (D′) 100 parts by weight of a diorganopolysiloxane gum having a plasticity of at least 30 and having an average of at least 2 alkenyl groups in its molecule and (D″) 5 to 200 parts by weight of a reinforcing filler, the weight ratio of said silicone base to said polyamide resin being greater than 35:65 to 85:15;
(E) for each 100 parts by weight of said polyamide resin, a compatibilizer selected from (i) from 0.1 to 5 parts by weight of a coupling agent having a molecular weight of less than 800 which contains at least two groups independently selected from ethylenically unsaturated group, epoxy, anhydride, silanol, carboxyl, hydroxyl, alkoxy, having 1 to 20 carbon atoms or oxazoline in its molecule, (ii) from 0.1 to 10 parts by weight of a functional diorganopolysiloxane having at least one group selected from epoxy, anhydride, silanol, carboxyl, amine, alkoxy having 1 to 20 carbon atoms or oxazoline in its molecule, or (iii) from 0.1 to 10 parts by weight of a copolymer comprising at least one diorganopolysiloxane block and at least one block selected from polyamide, polyether, polyurethane, polyurea, polycarbonate and polyacrylate;
(F) an organohydrido silicon compound which contains an average of at least 2 silicon-bonded hydrogen groups in its molecule; and
(G) a hydrosilation catalyst;
components (F) and (G) being present in an amount sufficient to cure said diorganopolysiloxane (D′); and
(II) dynamically curing said diorganopolysiloxane (D′);
(4) A TPV made by a method comprising:
(I) mixing:
(H) a thermoplastic resin comprising more than 50 percent by volume of a polyester resin said thermoplastic resin having a softening point of 23° C. to 300° C.;
(I) a silicone elastomer comprising (I′) 100 parts by weight of a diorganopolysiloxane gum having a plasticity of at least 30 and having an average of at least 2 alkenyl groups in its molecule and, optionally, (I″) up to 200 parts by weight of a reinforcing filler, the weight ratio of said silicone elastomer to said thermoplastic resin is from 35:65 to 85:15;
(J) a glycidyl ester compatibilizer;
(K) an organohydrido silicon compound which contains an average of at least 2 silicon-bonded hydrogen groups in its molecule; and
(L) a hydrosilation catalyst;
components (K) and (L) being present in an amount sufficient to cure said diorganopolysiloxane (I′); and
(II) dynamically vulcanizing said diorganopolysiloxane (I′);
(5) a TPV comprising:
Copolymer refers to polymers containing two or more monomers. In the case of a polymer derived from alternating essential co-monomers, such as polyalkylene terephthalate polyester and the like, the term “copolymer” is used to refer to the presence of at least one additional monomer other than the essential co-monomers.
Terpolymer means that the copolymer has at least three different comonomers.
Vulcanisate and the phrase “vulcanisate rubber” as used herein are intended to be generic to the cured or partially cured, cross-linked or cross-linkable rubber as well as curable precursors of cross-linked rubber and as such include elastomers, gum rubbers and so-called soft vulcanisates as commonly recognized in the art.
Thermoplastic vulcanisate (TPV) means blends of polymers consisting of a continuous thermoplastic phase with a phase of vulcanised elastomer dispersed therein. TPV's can be processed like thermoplastics (e.g. by moulding, extrusion and shaping).
Organic diene co-agent is intended to mean organic co-agents that contain two or more unsaturated double bonds.
Acrylate means an ester of acrylic acid with an alkyl group. Preferred in the invention are acrylates with alkyl groups having 1 to 4 carbon atoms.
The term “(meth)acrylic acid” refers to methacrylic acid and/or acrylic acid, inclusively. Likewise, the term “(meth)acrylate” means methacrylate and/or acrylate and “poly(meth)acrylate” means polymers derived from the polymerisation of either or a mixture of both corresponding type of monomers.
The expressions “rubber phase” and “thermoplastic phase” as used herein refer to and mean the polymeric morphological phases present in the resulting thermoplastic elastomeric blends derived from mixing and dynamic cross-linking of the cross-linkable acrylate rubber and the polyalkylene phthalate polyester starting materials, according to the method of the present invention.
Compression set: Compression set is a measurement of the ratio of elastic to viscous components of an elastomer's response to a given deformation. The cross-section is measured after the load is removed. Compression set is the percentage of the original thickness in the direction of the deformation that is not recovered, after a fixed time, under a specified load and at a specified temperature. This test may be conducted on cylindrical disks or O-rings. After compression by a standard load for a given period of time, the samples are removed and allowed to cool at room temperature for 30 minutes before measuring. After a load is released from an elastomer, the difference between the final thickness in the direction of deformation and the original thickness in the direction of deformation is considered the compression set. Compression set is expressed a percentage, as follows:
The lower the compression set, the more elastic the elastomer (i.e. an ideal elastomer returns to exactly its original volume after compression, and therefore has a compression set of 0%). Vulcanised rubbers typically have a compression set of 20%, thermoplastic vulcanisates are in the order of 30% or higher.
TPV: thermoplastic vulcanisate
LCP: liquid crystalline polymer
PET: polyethylene terephthalate
PBT: polybutylene terephthalate
ABS: a copolymer of acrylonitrile, butadiene, and styrene
PVC: polyvinyl chloride
All documents referred to herein are incorporated by reference.
The inventors have surprisingly found that the problem of poor compression set of TPV, particularly at elevated temperatures (i.e. greater than at or about 150° C., particularly above at or about 175° C.) can be overcome in making seals of TPV, by making flexion seals rather than compression seals. This permits the use of TPV's in making static seals in high temperature and oil exposed uses, such as the automotive industry, thereby allowing the reaping of the advantages of TPV's, such as the possibility of injection moulding without subsequent curing, in particular overmoulding. By using overmoulding, two different polymer materials can be made into a single piece. For example, a thermoplastic “hard” piece can be moulded as a single piece with a TPV sealing element, using a two-step injection process.
The expression “flexion seal” is meant to encompass any seal wherein the sealing surface is in the form of a flexible lip. The expression is equivalent with the expression “lip seal”. Flexion seals (10) employ a “hollow” section (13) with a flexible lip (1) or lips, as shown in
The TPV to be used in the flexion seal of the invention is selected from:
In a preferred embodiment, the flexion seal of the invention comprises, or is made from TPV (1), which comprises:
(A) from at or about 15 to 60 weight percent of a polyalkylene phthalate polyester polymer or copolymer continuous phase and; (B) from at or about 40 to 85 weight percent of a polyethylene/(meth)acrylate rubber dispersed phase, wherein the rubber is dynamically cross-linked with a peroxide free radical initiator and an organic diene co-agent. Such TPV's are described in WO 2004/029155 (E.I. DuPont de Nemours).
In a preferred embodiment, the polyalkylene phthalate polyester polymer or copolymer (A) of the continuous phase of TPV (1) is selected from the group consisting of polyalkylene terephthalate, polyalkylene terephthalate copolymer, and a block copolyester elastomer, such as a copolyether-ester block copolymer elastomer or a copolyester-ester block copolymer elastomer.
In a further preferred embodiment, the organic diene co-agent in TPV (1) is selected from the group consisting of diethylene glycol diacrylate, ethylene glycol dimethacrylate, diethylene glycol dimethacrylate, N,N′-m-phenylene dimaleimide, triallylisocyanurate, trimethylolpropane trimethacrylate, tetraallyloxyethane, triallyl cyanurate, tetramethylene diacrylate, polyethylene glycol dimethacrylate, and the like. Preferably the organic diene co-agent is selected from diethylene glycol diacrylate, diethylene glycol dimethacrylate, N,N′-m-phenylene dimaleimide, and triallylisocyanurate.
The free-radical initiator used in TPV (1) is preferably selected from the group consisting of 2,5-dimethyl-2,5-di-(t-butylperoxy)hexyne-3, t-butyl peroxybenzoate, 2,5-dimethyl-2,5-di-(t-butylperoxy)-2,5-dimethylhexane, dicumyl peroxide, α,α-bis(t-butylperoxy) 2,5-dimethylhexane, and the like. Preferred free-radical initiators are 2,5 dimethyl-2,5-di-(t-butylperoxy)hexyne-3; 2,5-dimethyl-2,5-di-(t-butylperoxy)hexane; or t-butyl peroxybenzoate.
In a particularly preferred embodiment, TPV (1) is as follows:
the polyalkylene phthalate polyester polymer or copolymer (A) is a block copolymer of segments of poly(butylene terephthalate) and segments of poly(tetramethylene glycol), the rubber (B) is an ethylene/methylacrylate copolymer elastomer, the peroxide free-radical initiator is 2,5-dimethyl-2,5-di-(t-butylperoxy)hexyne-3 and the organic diene co-agent is diethylene glycol dimethacrylate.
The specific combination of a block copolymer of segments of poly(butylene terephthalate) and segments of poly(tetramethylene glycol) along with an ethylene/methylacrylate copolymer elastomer, 2,5-dimethyl 2,5-di-(t-butylperoxy)hexyne-3 or 2,5-dimethyl-2,5-di-(t-butylperoxy)hexane free-radical initiator and diethylene glycol dimethacrylate co-agent produces a highly dispersed rubber phase with excellent properties.
In a particularly preferred embodiment, TPV (1) has the following composition:
25 wt % of a polyalkylene phthalate polyester polymer or copolymer which is a block copolymer of segments of poly(butylene terephthalate) and segments of poly(tetramethylene glycol);
75 wt % of a rubber which is an ethylene/methylacrylate copolymer elastomer;
wherein the rubber is dynamically cross-linked with a peroxide free-radical initiator which is 2,5-dimethyl-2,5-di-(t-butylperoxy)hexyne-3 and an organic diene co-agent which is diethylene glycol dimethacrylate.
In another particularly preferred embodiment, TPV (1) has the following composition:
50 wt % of a polyalkylene phthalate polyester polymer or copolymer which is a block copolymer of segments of poly(butylene terephthalate) and segments of poly(tetramethylene glycol);
50 wt % of a rubber which is an ethylene/methylacrylate copolymer elastomer;
wherein the rubber is dynamically cross-linked with a peroxide free-radical initiator which is 2,5-dimethyl-2,5-di-(t-butylperoxy)hexyne-3 and an organic diene co-agent which is diethylene glycol dimethacrylate.
The TPV may be compounded using processes such as those described in WO 2004/029155. An example is a process comprising the steps of:
(a) adding and admixing a cross-linkable polyethylene/(meth)acrylate vulcanisate rubber, a peroxide free-radical initiator and an organic diene co-agent in a melt extruder or melt blender at a temperature insufficient to promote significant cross-linking;
(b) adding a polyalkylene terephthalate polyester polymer or copolymer to the melt extruder or melt blender and admixing the polyalkylene terephthalate polyester polymer with the cross-linkable polyethylene/(meth)acrylate vulcanisate rubber prior to cross-linking;
(c) further mixing the cross-linkable polyethylene/(meth)acrylate vulcanisate rubber with peroxide free-radical initiator and an organic diene co-agent with the polyalkylene terephthalate polyester polymer or copolymer at conditions and temperature sufficient to cross-link the cross-linkable polyethylene/(meth)acrylate vulcanisate rubber; and
(d) recovering the TPV comprising from 15 to 60 weight percent of the polyalkylene terephthalate polyester polymer or copolymer as a continuous phase and from 40 to 85 weight percent of the polyethylene/(meth)acrylate vulcanisate rubber cross-linked with the peroxide free radical initiator and the organic diene co-agent as a disperse phase.
In a preferred embodiment, the flexion seal of the invention comprises, or is made from TPV (2), which comprises:
25 to 60% by weight of a polyamide resin and 75 to 40% by weight of a rubber component; said rubber component comprising 20 to 80% by weight of a hydrogenated nitrile group-containing rubber and 80 to 20% by weight of an acrylic rubber, said rubber component being dispersed in the form of cross-linked particles in said polyamide resin; said hydrogenated nitrile group-containing rubber being a hydrogenated copolymer containing 10 to 60% by weight of a vinyl nitrile, 15 to 90% by weight of a conjugated diene and 0 to 75% by weight of a monomer copolymerizable with vinyl nitrile and said conjugated diene, said hydrogenated nitrile-group containing rubber having an iodine value of 120 or less; said acrylic rubber being a copolymer of at least one acrylate selected from the group consisting of an alkyl acetate and an alkoxy-substituted alkyl acrylate with at least one compound selected from the group consisting of a nonconjugated diene, a conjugated diene, a dihydrodicyclopentadienyl group-containing (meth)acrylate, an epoxy group-containing ethylenically unsaturated compound, an active halogen-containing ethylenically unsaturated compound and a carboxyl group-containing ethylenically unsaturated compound.
The polyamide resin in TPV (2) is preferably selected from polyamide resins polyamide resin having a melting point of at or about 160° C. to at or about 250° C.
Preferably, the hydrogenated nitrile group-containing rubber of TPV (2) contains at least one functional group selected from the class consisting of a carboxyl group, an epoxy group, and a primary, secondary or tertiary amino group, in an amount of at least 5×10−3 molar equivalents per 100 g of the rubber.
Preferably, the acrylic rubber of TPV (2) contains at least one functional group selected from the class consisting of a carboxyl group and an epoxy group, in an amount of at least 1×10−2 molar equivalents per 100 g of the rubber.
Preferably, the cross-linked rubber particles of TPV (2) have a diameter of 5 μm or less.
Preferably, the cross-linked rubber particles of TPV (2) have a methyl ethyl ketone insoluble content of 80% by weight based on the amount of the whole rubber component.
Such TPV's are described in U.S. Pat. No. 4,996,264.
In a preferred embodiment, the flexion seal of the invention comprises, or is made from TPV (3), which is made by a method comprising:
(I) mixing:
(C) a rheologically stable polyamide resin having a melting point or glass transition temperature of 25° C. to 275° C.;
(D) a silicone base comprising (D′) 100 parts by weight of a diorganopolysiloxane gum having a plasticity of at least 30 and having an average of at least 2 alkenyl groups in its molecule and (D″) 5 to 200 parts by weight of a reinforcing filler, the weight ratio of said silicone base to said polyamide resin being greater than 35:65 to 85:15;
(E) for each 100 parts by weight of said polyamide resin, a compatibilizer selected from (i) from 0.1 to 5 parts by weight of a coupling agent having a molecular weight of less than 800 which contains at least two groups independently selected from ethylenically unsaturated group, epoxy, anhydride, silanol, carboxyl, hydroxyl, alkoxy, having 1 to 20 carbon atoms or oxazoline in its molecule, (ii) from 0.1 to 10 parts by weight of a functional diorganopolysiloxane having at least one group selected from epoxy, anhydride, silanol, carboxyl, amine, alkoxy having 1 to 20 carbon atoms or oxazoline in its molecule, or (iii) from 0.1 to 10 parts by weight of a copolymer comprising at least one diorganopolysiloxane block and at least one block selected from polyamide, polyether, polyurethane, polyurea, polycarbonate and polyacrylate;
(F) an organohydrido silicon compound which contains an average of at least 2 silicon-bonded hydrogen groups in its molecule; and
(G) a hydrosilation catalyst;
components (F) and (G) being present in an amount sufficient to cure said diorganopolysiloxane (D′); and
(II) dynamically curing said diorganopolysiloxane (D′);
In a preferred embodiment the weight ratio of said silicone base (D) to said polyamide resin (C) in TPV (3) is greater than at or about 35:65 to at or about 75:25. Preferably, the ratio is at or about 40:60 to at or about 70:30.
Preferably, the polyamide (C) in TPV (3) is selected from the group consisting of nylon 6, nylon 6/6, nylon 6/12 and nylon 12.
Preferably, the diorganopolysiloxane (D′) is a gum selected from the group consisting of a copolymer consisting essentially of dimethylsiloxane units and methylvinylsiloxane units and a copolymer consisting essentially of dimethylsiloxane units and methylhexenylsiloxane units and said reinforcing filler (D″) is a fumed silica.
Preferably, the organohydrido silicon component (F) is selected from the group consisting of a polymer consisting essentially of methylhydridosiloxane units and a copolymer consisting essentially of dimethylsiloxane units and methylhydridosiloxane units, having 0.5 to 1.7 weight percent hydrogen bonded to silicon and having a viscosity of 2 to 500 mPa-s at 25° C. and said catalyst (G) is a neutralized complex of platinous chloride and divinyltetramethyldisiloxane.
Preferably, the hindered phenol (E) has a molecular weight of less than 1,200 and contains 2 to 4 groups of the formula:
in which R and R′ are tert-butyl groups. More preferably, the hindered phenol (E) is selected from the group consisting of triethyleneglycol bis(3-(3′-tert-butyl-4′-hydroxy-5′-methylphenyl)propionate), N,N′-hexamethylenebis(3,5-di-tert-butyl-4-hydroxyhydrocinnamamide) and tetrakis(methylene(3,5-di-tert-butyl-4-hydroxy-hydrocinnamate))methane.
Examples of TPV's suitable as TPV (3) are described in U.S. Pat. No. 6,362,287.
In a preferred embodiment, the flexion seal of the invention comprises, or is made from TPV (4), which is made by a method comprising:
(I) mixing:
(H) a thermoplastic resin comprising more than 50 percent by volume of a polyester resin said thermoplastic resin having a softening point of 23° C. to 300° C.;
(I) a silicone elastomer comprising (I′) 100 parts by weight of a diorganopolysiloxane gum having a plasticity of at least 30 and having an average of at least 2 alkenyl groups in its molecule and, optionally, (I″) up to 200 parts by weight of a reinforcing filler, the weight ratio of said silicone elastomer to said thermoplastic resin is from 35:65 to 85:15;
(J) a glycidyl ester compatibilizer;
(K) an organohydrido silicon compound which contains an average of at least 2 silicon-bonded hydrogen groups in its molecule; and
(L) a hydrosilation catalyst;
components (K) and (L) being present in an amount sufficient to cure said diorganopolysiloxane (I′); and
(II) dynamically vulcanizing said diorganopolysiloxane (I′).
In a preferred embodiment, the polyester resin in TPV (4) is selected from poly(butylene terephthalate), poly(ethylene terephthalate), poly(trimethylene terephthalate), poly(ethylene naphthalate), poly(butylene naphthalate) or poly(cyclohexylenedimethylene terephthalate).
Preferably, in TPV (4), the diorganopolysiloxane (I′) is a gum selected from a copolymer consisting essentially of dimethylsiloxane units and methylvinylsiloxane units or a copolymer consisting essentially of dimethylsiloxane units and methylhexenylsiloxane units, and said reinforcing filler (I″) is a fumed silica.
Preferably, in TPV (4), the glycidyl ester compatibilizer (J) is a glycidyl ester polymer comprising repeating units of one or more glycidyl ester monomers. Particularly preferably, the glycidyl ester polymer comprises first repeating units derived from one or more glycidyl ester monomers and second repeating units derived from one or more alpha-olefin monomers. More preferably the glycidyl ester polymer is selected from olefin-glycidyl (meth)acrylate polymers, olefin-vinyl acetate-glycidyl (meth)acrylate polymers and olefin-glycidyl (meth)acrylate-alkyl (meth)acrylate polymers.
Preferably, in TPV (4), the organohydrido silicon component (K) is selected from the group consisting of a polymer consisting essentially of methylhydridosiloxane units and a copolymer consisting essentially of dimethylsiloxane units and methylhydridosiloxane units, having 0.5 to 1.7 weight percent hydrogen bonded to silicon and having a viscosity of 2 to 500 mPa·s at 25° C., and the catalyst (L) is a neutralized complex of platinous chloride and divinyltetramethyldisiloxane.
Preferably, in TPV (4), the weight ratio of said silicone elastomer (I) to said resin (H) is at or about 40:60 to at or about 70:30.
Examples of TPV's suitable as TPV (4) are described in U.S. Pat. No. 6,569,985.
In a preferred embodiment, the flexion seal of the invention comprises, or is made from TPV (5), which comprises:
Preferably, in TPV (5), The mixture (M) may be a mixture of two components (M1) and (M2).
(M1) is a block copolyester elastomer, such as a copolyether-ester block copolymer elastomer or a copolyester-ester block copolymer elastomer. Copolyether-ester elastomers and copolyester-ester elastomers are described for example in U.S. Pat. Nos. 4,981,908, 5,824,421 and 5,731,380, the descriptions of which are incorporated herein by reference. Preferably (M1) is selected from block copolymers of poly(butylene terephthalate) and poly(tetramethylene glycol), block copolymers of poly(butylene terephthalate) and ethylene-oxide-capped poly(propylene glycol), and mixtures of such block copolymers. Most preferably (M1) is a block copolymer of segments of poly(butylene terephthalate) and segments of poly(tetramethylene glycol). Suitable block copolyester elastomers are sold under the tradenames Hytrel® (DuPont, Wilmington, USA) and Arnitel® (DSM, Netherlands). The block copolyester elastomer (A1) is preferably present at or about 5 to at or about 60 wt % with respect to the overall polymer blend.
(M2) is a poly(butylene terephthalate) (PBT). Preferably the PBT has a number average molecular weight of at least at or about 7500, most preferably greater than at or about 15000, but preferably less than at or about 150000. It is particularly preferred to use a PBT of number average molecular weight of at or about 25000. Suitable PBT component is sold under the tradenames Crastin® (DuPont, Wilmington, USA), Pocan® (Lanxess, Germany) and Arnite® (DSM, Netherlands). The PBT is preferably present at or about 2 to at or about 60 wt % with respect to the overall polymer blend.
Preferably the rubber in TPV (5) is selected from poly(meth)acrylate and a mixed polymer of ethylene and methyl acrylate, most preferably it is a mixed polymer of ethylene and methyl acrylate. The rubber is cross-linked with a free-radical initiator (such as an organic peroxide) and an organic diene coagent. Preferably the rubber is a mixed polymer of ethylene and methyl acrylate, derived from the copolymerisation of ethylene and 63 wt % methyl acrylate. Suitable rubber is sold under the trade name Vamac® (DuPont, Wilmington, USA).
The organic diene co-agent in TPV (5) is preferably selected from the group consisting of diethylene glycol diacrylate, ethylene glycol dimethacrylate, diethylene glycol dimethacrylate, N,N′-m-phenylene dimaleimide, triallylisocyanurate, trimethylolpropane trimethacrylate, tetraallyloxyethane, triallyl cyanurate, tetramethylene diacrylate, polyethylene glycol dimethacrylate, and the like. Preferably the organic diene co-agent is selected from diethylene glycol diacrylate, diethylene glycol dimethacrylate, N,N′-m-phenylene dimaleimide, and triallylisocyanurate. The organic diene co-agent is preferably present at or about 0.5-6 wt %, more preferably at or about 1.5-4 wt %, based on the rubber.
The free radical initiator in TPV (5) is preferably an organic peroxide. More preferably the peroxide is selected from the group consisting of 2,5-dimethyl-2,5-di-(t-butylperoxy)hexyne-3, t-butyl peroxybenzoate, 2,5-dimethyl-2,5-di-(t-butylperoxy)-2,5-dimethylhexane, dicumyl peroxide, α,α-bis(t-butylperoxy) 2,5-dimethylhexane, and the like. Preferred free-radical initiators are 2,5 dimethyl-2,5-di-(t-butylperoxy)hexyne-3; 2,5-dimethyl-2,5-di-(t-butylperoxy)hexane; and t-butyl peroxybenzoate. The free-radical initiator is preferably present at or about 0.5-3 wt %, more preferably at or about 0.75-2.5 wt %, based on the rubber.
In another preferred embodiment of the flexion seal made of TPV (5), the cross-linked or cross-linkable rubber comprises copolymers of ethylene and methyl acrylate together with at least one other monomer with a reactive chemical group which can be cross-linked. Particularly preferred are monomers with carboxylate groups, which can be cross-linked with a diamine cross-linking agent.
The ionomer in TPV (5) is preferably selected from random copolymers of ethylene and methacrylic acid [poly(ethylene-co-methacrylic acid)]. The acid moieties may be protonated, but are preferably neutralised from at or about 10 to 100 mol %, more preferably from at or about 25-80 mol %, particularly preferably at or about 30-70 mol %, with a counterion selected from Na+ and Zn++, with Na+ preferred. A particularly preferred ionomer comprises 50-95% by weight of ethylene, 5-15% by weight of acrylic acid or methacrylic acid, and 0-35% by weight of a moiety selected from at least one of methyl acrylate, iso-butyl acrylate and n-butyl acrylate, and the acid groups are neutralized from 30-70% with a counterion of at least one metal ion selected from sodium and zinc, preferably sodium. Suitable ionomer may be purchased under the trade name Surlyn® (DuPont, Wilmington, USA).
The terpolymer in TPV (5) is preferably selected from terpolymers of ethylene, butylacrylate (BA) and glycidylmethacrylate (GMA), wherein the three components are present in at or about the following weight percentages: ethylene 50-98 wt %, BA 1-40 wt %, and GMA 1-15 wt %. Particularly preferred is a terpolymer having the following composition: ethylene 55-88 wt %, BA 10-35 wt %, and GMA 2-10 wt %. Suitable terpolymer may be purchased under the trade name Elvaloy® (DuPont, Wilmington, USA).
Particularly preferably, the flexion seal of the invention is made from a TPV (5) having the following composition:
In a preferred embodiment, the flexion seal of the invention comprises, or is made from TPV (6), which comprises:
Preferred constituents for TPV (6) are as described above for TPV (5).
The TPV's listed above as (1) to (6) may be mixed in any proportion. Particularly preferred mixtures are TPV's (1) and (5), TPV's (1) and (6), TPV's (1), (5) and (6), and TPV's (2) and (3).
The flexion seal of the invention may be made with any moulding, extruding or shaping technique that can be used with a TPV. Particularly preferred is injection moulding.
In a preferred embodiment, the flexion seal of the invention is “overmoulded” with another thermoplastic part made from a polymer different from the TPV of the sealing part. In this way a dual component moulded article is made. For example, a structural component of a non-elastomeric or less-elastomeric polymer can be integrally moulded (“overmoulded”) with a sealing component made of a static flexion seal of the TPV. In such an overmoulded part, if the other thermoplastic component is to serve a structural function, it is preferred that it have an elastic modulus greater than that of the TPV flexion seal component. The non-elastomeric or less elastomeric thermoplastic may comprise or be selected from, for example, nylon, polyacetal, LCP, PET, PBT, PCT, copolyetherester block copolymer elastomers, polycarbonate, ABS, polyvinyl chloride, polyolefins (such as polypropylene and polyethylene), and mixtures of these. The non-elastomeric or less elastomeric thermoplastic is injected into a mould, so as to partially fill the mould, i.e. by placing gates in the mould. Immediately thereafter, the TPV is injected to fill the unfilled part of the mould (these steps can also be reversed, although it is preferable to inject the TPV second). In this way an integral part is formed, in which the flexion sealing member is integrally moulded with the less elastomeric structural polymer.
In such overmoulded dual component parts, it is preferable that the first polymer material and the TPV component be chemically compatible so that bonding between the two components is maximised. For example, TPV (1) pairs well with polyesters, such as PET, PBT, PCT and LCP, and copolyetheresters. TPV (2) and TPV (3) pair well with polyamides. TPV (4), TPV (5) and TPV (6) pair well with polyesters, such as PET, PBT, PCT and LCP, and copolyetheresters.
Examples of flexion seals are disclosed, for example, in US2004/0056427A1, U.S. Pat. No. 6,559,633 and WO 03/089772.
In a preferred embodiment, the flexion seal of the invention is used in any environment where heat and/or oil resistance are required, particularly internal combustion engines, more particularly in the automotive industry, particularly under the hood and in and around the engine of a motor vehicle.
Examples of where such seals can be used include in air intake systems, engine cooling systems, power steering systems, exhaust systems, fuel systems, air conditioning systems, oil systems, brake systems, compressed air systems, electrical systems (e.g. automotive system sensors), vacuum systems and hydraulic systems.
A schematic of a lip seal is shown in
In a preferred embodiment, a boss (3) is added to the seal (10). One example of this is shown in
In an additional preferred embodiment, shown in
In another preferred embodiment, shown in
Test pieces were made of TPV and subjected to the following tests to demonstrate the improved behaviour of TPV when subjected to flexure forces as in a flexion seal, as compared to compression forces, as in a compression seal.
Compression testing was according to ASTM D 395-B-2. The general principle is shown in
Flexion testing was done as follows: The general principle of the assay is shown in
These results are shown graphically as a bar chart in
Number | Date | Country | Kind |
---|---|---|---|
05290759.9 | Apr 2005 | EP | regional |
Filing Document | Filing Date | Country | Kind | 371c Date |
---|---|---|---|---|
PCT/US2006/012396 | 4/4/2006 | WO | 00 | 9/13/2007 |