Patent Application
20120180866
The present invention relates to a sealing material sheet used in the process of manufacturing a solar cell module.
Solar cells have attracted attention as a clean power generation source using solar light. In a general solar cell module, as shown in
To manufacture a solar cell module, as shown in
Regarding the materials of the sealing material sheets 22 and 24, EVA (Ethylene-Vinyl Acetate copolymer) is often used as a main resin thereof For the purpose of providing various functions such as close adhesion, weather resistance, and light resistance, additives such as a cross-linking agent, an auxiliary cross-linking agent, a silane-coupling agent, a stabilizer, an ultraviolet absorber, an anti-aging agent, and a discoloration-preventing agent are often included therein at a constant ratio.
The method of producing the sealing material sheet employs a “T-die method of extruding a molten resin from a die having a linear slit and rapidly cooling and solidifying the resultant with a cooling roll or a water tank” or a “calender method”. A seal sheet with a thickness of about 500 μm is formed through the use of these film-forming processes. In the film-forming processes, the surface of the sealing material sheet may be subjected to an embossing process to provide unevenness thereto.
Methods of manufacturing a solar cell module are disclosed in Patent Documents 1 and 2.
Patent Document 1: Japanese Patent No. 3473605
Patent Document 2: Japanese Patent No. 3174531
In manufacturing a solar cell module hitherto, since the sealing material sheet is pressed by solar cells during heating and pressing in the sealing process, there is a problem in that the solar cells may be destroyed from the pressing force. There is also a problem in that air infiltrates due to degassing failure during the sealing and bubbles remain in the module, thereby lowering the production yield. To solve these problems, cushioning properties and degassing properties in the heating and pressing processes have been improved through the use of an embossing process to provide unevenness to the surface of the sealing material sheet or techniques of forming through-holes in the sealing material sheet (see Patent Documents 1 and 2).
Particularly, regarding the embossing process, when the embossing is performed so that the percentage VH/VA×100% (hereinafter, referred to as porosity P) of the total volume VH of the concave portions per, unit area of the sealing material sheet and the apparent volume VA of the sealing material sheet obtained by multiplying the unit area by the maximum thickness is in the range of 5% to 80% (preferably in the range of 20% to 50%), it is considered that the cushioning properties and the degassing properties are improved (see Patent Document 1).
However, in the sealing material sheet having been subjected to the deep embossing process with a porosity P of 5% to 80% or the EVA resin sheet having through-holes formed therein, there is a problem in that a predetermined amount of air is already included in the laminate in the step of laminating the constituent members of the solar cell module in the order of the front-side protective member, the sealing material sheet, the solar cells, the sealing material sheet, and the back-side protective member, and thus it takes time to perform the heating and degassing processes in a vacuum.
The invention is made to solve the above-mentioned problems.
According to a first aspect of the invention, there is provided a sealing material sheet which is used as a member of a solar cell module formed by heating and pressing a laminate in which a first protective member, a first sealing material sheet, a photoelectric conversion cell, a second sealing material sheet, and a second protective member are laminated in this order, wherein an uneven pattern is formed on one surface or both surfaces of the first sealing material sheet and the second sealing material sheet through an embossing process, and the embossing process is performed so that the percentage VH/VA×100% of the total volume VH of concave portions per unit area of the first sealing material sheet and the second sealing material sheet and the apparent volume VA of the sealing material sheets obtained by multiplying the unit area by the maximum thickness is in the range of 1% to 4%.
According to a second aspect of the invention, in the sealing material sheet according to the first aspect, the minimum value of a storage elastic modulus is equal to or less than 104 Pa when the sealing material sheet with a thickness of 1 mm is interposed between two φ25 mm Al plates and dynamic viscoelasticity of the sealing material sheet is measured at intervals of 1° C. in the course of raising the temperature from a measurement start temperature of 40° C. to a measurement end temperature of 150° C. with a deformation ratio of 5% and at a frequency of 1 Hz.
According to the invention, by employing a sealing material sheet with a porosity of 1% to 4%, it is possible to reduce an amount of air infiltrated into a laminate in the step of laminating the constituent members of the solar cell module and to shorten the time necessary for the heating and degassing process in a vacuum in the solar cell module manufacturing process.
The cushioning properties in the heating and pressing process in manufacturing a solar cell module are lowered in comparison with a sealing material sheet with a porosity of 5% to 80% by setting the porosity of the sealing material sheet to the range of 1% to 4%; however, it is possible to compensate for the lowering in cushioning properties and to prevent the solar cell from cracking in the heating and pressing process, by selecting a resin with a low elastic modulus as a resin which is a main material of the sealing material sheet. Since the fluidity of the resin in the heating and degassing process in a vacuum increases, it is possible to improve the degassing efficiency.
Accordingly, it is possible to shorten the time necessary for the heating and degassing process and to improve the manufacturing efficiency of the solar cell module.
Hereinafter, embodiments of the invention will be described in detail. In the embodiments, like elements are referenced by like reference signs and description thereof will not be repeated.
In
Examples of the main material of the first sealing material sheet 6 and the second sealing material sheet 8 include polyolefins such as polyethylene and polypropylene; ionomers; ethylene-vinyl acetate copolymers; polyfluorovinyl; polyvinyl chloride; or copolymers thereof.
A resin having high transparency may be used as the main material of the first sealing material sheet 6 and the second sealing material sheet 8 and ethylene-vinyl acetate or the like can be preferably used.
A cross-linking agent may be added to the first sealing material sheet 6 and the second sealing material sheet 8 without damaging the transparency for the purpose of enhancing the strength. Examples of the cross-linking agent include such as 1,1-di(t-butylperoxy)cyclohexane, 1,1-di(t-hexylperoxy)cyclohexane, n-butyl 4,4-di(t-butylperoxy)valerate, t-butylperoxy-3,5,5-trimethylhexanoate, 2,5-dimethyl-2,5-di(t-butylperoxy)hexane, t-butylcumylperoxide, and 2,2-di(t-butylperoxy)butane.
An additive for promoting a cross-linking reaction in addition to the cross-linking agent may be added to the first sealing material sheet 6 and the second sealing material sheet 8. Examples of the additive include such as triallyl isocyanurate, diallyl phthalate, and triallyl cyanurate.
Other than the above-mentioned, a silane-coupling agent, an ultraviolet absorber, and an anti-oxidant may be also added thereto.
Examples of the silane-coupling agent used to improve the close adhesion include such as γ-methacryloxy propyltrimethoxysilane, trimethoxypropylsilane, trimethoxymethylsilane, vinyltrimethoxysilane, vinyltriethoxysilane, trichloropropylsilane, and triethoxyphenylsilane.
Examples of the ultraviolet absorber used to improve the light resistance include such as 2-(5-methyl-2-hydroxyphenyl)benzotriazole, 2-(3-t-butyl-5-methyl-2-hydroxyphenyl)-5-chlorobenzotriazole, 2-(4,6-diphenyl-1,3,5-triazine 2-yl)-5-[(hexyl)oxy]-phenol, 2,4-dihydroxybenzophenone, and 2-hydroxy-4-n-octyloxybenzophenone.
Examples of the anti-oxidant used to improve the thermal stability include such as 1,6-hexanediol-bis[3-(3,5-di-t-butyl-4-hydroxyphenyl)propionate, pentaerythritol tetrakis[3-(3,5-di-t-butyl-4-hydroxyphenyl)propionate], tris(2,4-di-t-butylphenyl)phosphite, and 2,4-bis-(n-octylthio)-6-(4-hydroxy-3,5-di-t-butylanilino)-1,3,5-triazine.
A film is formed of the resin in which the main material and the additives are mixed, heated, and melted through the use of a T-die method or a calender method to produce a sealing material sheet. By suspending the resin sheet in the thermally-melted state on a roll (formed of metal or rubber) having an uneven pattern formed on the surface thereof in the course of forming the film, the uneven pattern of the roll can be transferred to one surface or both surface of the first sealing material sheet 6 and the second sealing material sheet 8 to form embossing on one surface or both surfaces of the first sealing material sheet 6 and the second sealing material sheet 8.
The uneven pattern of the roll in the course of forming a film is selected to perform the embossing process on the sealing material sheets, so that the porosity P defined as the percentage VH/VA×100% of the total volume VH of the concave portions per unit area of the first sealing material sheet 6 and the second sealing material sheet 7 and the apparent volume VA of the sealing material sheets obtained by multiplying the unit area by the maximum thickness is in the range of 1% to 4%.
The porosity P defined as the percentage VH/VA×100% can be calculated as follows. That is, in the sealing material sheet having been subjected to the embossing process, the apparent volume VA (mm3) of the sealing material sheet is the product of the maximum thickness tmax (mm) of the sealing material sheet and the unit area (for example, 1 m2=1000×1000=106 mm2) and is calculated as follows.
V
A (mm3)=tmax×106
On the other hand, the actual volume V0 (mm3) of the sealing material sheet per unit area is calculated from the specific gravity ρ (g/mm3) of the resin constituting the sealing material sheet and the actual weight W (g) of the sealing material sheet per unit area (1 m2) as follows.
V
0 (mm3)=W/ρ
The total volume VH (mm3) of the concave portions per unit area of the sealing material sheet is a value obtained by subtracting the actual volume V0 from the apparent volume VA of the sealing material sheet and is calculated as follows.
V
H (mm3)=VA−V0=VA−(W/ρ)
Therefore, the porosity (%) can be calculated as follows.
The porosity (%) cannot only be calculated by the use of the above-mentioned expression but can also be obtained by imaging a section or a surface subjected to the embossing process in the actual sealing material sheet through the use of a microscope and performing an image processing.
The maximum thickness tmax of the sealing material sheet represents the distance between the tip of the convex portions and the back surface when the embossing process is performed on one surface of the sealing material sheet, and represents the distance (the distance in the film thickness direction) between the tips of the convex portions on both surfaces when the embossing process is performed on both surfaces of the film. The maximum thickness tmax is preferably in the range of 50 to 2000 μm.
As described above, the cushioning properties in the heating and pressing process in manufacturing a solar cell module are lowered in comparison with a sealing material sheet with a porosity of 5% to 80% by setting the porosity of the sealing material sheet to the range of 1% to 4%; however, it is possible to solve such a problem by selecting a resin with a low elastic modulus as the resin which is the main material of the sealing material sheet. In addition, since the fluidity of the resin in the heating and degassing process increases, it is possible to improve the degassing efficiency.
The resin with a low elastic modulus is defined as follows.
The minimum value of the storage elastic modulus is equal to or less than 104 Pa when the sealing material sheet with a thickness of 1 mm is interposed between two φ25 mm Al plates and the dynamic viscoelasticity of the sealing material sheet is measured at intervals of 1° C. in the course of raising the temperature from a measurement start temperature of 40° C. to a measurement end temperature of 150° C. with a deformation ratio of 5% and at a frequency of 1 Hz. The dynamic viscoelasticity can be measured, for example, by the use of Rheometer AR-2000CX made by TA Instruments Ltd.
The resin with a low elastic modulus can be obtained by appropriately selecting the resin or appropriately adjusting the kinds and amounts of the additives.
Hereinafter, the invention will be described in more detail with reference to examples and comparative examples, but the invention is not limited to the examples.
An EVA resin of which the minimum value of the storage elastic modulus is 9200 Pa was prepared by adjusting the resin composition and the mixing ratio of the additives. That is, in this EVA resin, the minimum value of a storage elastic modulus is equal to or less than 9200 Pa when the sealing material sheet with a thickness of 1 mm is interposed between two φ25 mm Al plates and dynamic viscoelasticity of the sealing material sheet is measured at intervals of 1° C. in the course of raising the temperature from a measurement start temperature of 40° C. to a measurement end temperature of 150° C. with a deformation ratio of 5% and at a frequency of 1 Hz. An EVA resin roll of which both surfaces have been subjected to the embossing process so that the porosity is in the range of 3% to 4% was produced using the EVA resin.
A pseudo solar cell module was manufactured by way of a trial using a sealing material sheet cut out from the EVA resin roll and the degassing performance of the sealing material sheet was checked. The trial manufacturing process of the pseudo solar cell module and the method of checking the degassing performance will be described below.
The trial manufacturing conditions of the pseudo solar cell module will be described below with reference to
After the temporary pressing process, the temperature of the laminating chamber was set to 150° C., the vacuum of the laminating upper cover was released, and the laminate was thermally pressed under atmospheric pressure for 10 minutes (Part B of
Regarding the appearance of the pseudo solar cell module having been subjected to the main pressing process, it was checked with visual observation whether bubbles of 1 mm2 or more remained therein.
In this example, the manufacture of the pseudo module and the checking of bubbles with visual observation were repeated 30 times, respectively, when the time of the vacuum degassing and temporary pressing process was set to 60 seconds and when the time is set to 90 seconds. The results for the checking of the bubbles with visual observation in this example are shown in Table 1.
As shown in
The film weight per 1 m2 necessary for calculating the porosity P was calculated by weighing a film 20 of 10 cm×10 cm by the use of an electronic balance and converting the measured weight into a weight per 1 m2. The maximum thickness was measured by cutting out a sample piece 19 of 1 cm×2 cm from five points of the film 20 shown in
In this example, the porosity P of three points (both ends and the center) in the roll width direction, which were calculated by substituting three maximum thicknesses obtained in this way and one weight value of the film per 1 m2 for the expression of the porosity defined above, was used as the porosity of the EVA resin roll.
The bubbles of 1 mm2 or more in the pseudo solar cell module were checked by using two sealing material sheets with a porosity of 7% to 9% of which both surfaces had been subjected to the embossing process as the members of the laminate and setting the other conditions to be the same as in Example 1. The results are shown in Table 1.
The bubbles of 1 mm2 or more in the pseudo solar cell module were checked by using two sealing material sheets with a porosity of 20% to 22% of which both surfaces had been subjected to the embossing process as the members of the laminate and setting the other conditions to be the same as in Example 1. The results are shown in Table 1.
The bubbles of 1 mm2 or more in the pseudo solar cell module were checked by using two sealing material sheets with a porosity of 50% to 55% of which both surfaces had been subjected to the embossing process as the members of the laminate and setting the other conditions to be the same as in Example 1. The results are shown in Table 1.
In the pseudo solar cell module produced through the “vacuum degassing and temporary pressing process” for 60 seconds and the “main pressing process” for 10 minutes using two sealing material sheets formed by using the resin of which the minimum value of the storage elastic modulus based on the dynamic viscoelasticity measurement was 3300 Pa and performing the embossing process on both surfaces thereof so that the porosity was in the range of 3% to 4%, the bubbles of 1 mm2 or more and the cell cracks were checked with visual observation.
In this example, the manufacture of the pseudo module and the checking of the bubbles and the cell cracks with visual observation were repeated 30 times. The results for the checking of the bubbles and the cell cracks visual observation are shown in Table 2.
Under the same conditions as in Example 2, except that two sealing material sheets formed by using the resin of which the minimum value of the storage elastic modulus based on the dynamic viscoelasticity measurement was 9200 Pa and performing the embossing process on both surfaces thereof so that the porosity was in the range of 1% to 2%, the bubbles of 1 mm2 or more and the cell cracks in the pseudo solar cell module were checked. The results are shown in Table 2. The results of Example 1 are also shown in Table 2.
From the results of the tables, it can be seen that it is possible to reduce the amount of air infiltrated into the laminate in the step of laminating the constituent members of the solar cell module and to shorten the time necessary for the heating and degassing in a vacuum in the process of manufacturing the solar cell, by performing the embossing process on the first sealing material sheet and the second sealing material sheet so that the porosity P is in the range of 1% to 4%.
According to the invention, since the degassing failure in the module can be prevented and the time of the laminating process can be shortened in the solar cell module manufacturing process, it is possible to improve the production yield of the solar cell module.
1: FRONT-SIDE PROTECTIVE MEMBER
2: SEALING LAYER
3: SOLAR CELL
4: BACK-SIDE PROTECTIVE MEMBER
5: FRONT-SIDE PROTECTIVE MEMBER
6: SEALING MATERIAL SHEET
7: SOLAR CELL
8: SEALING MATERIAL SHEET
9: BACK-SIDE PROTECTIVE MEMBER
10: LAMINATING UPPER COVER
11: BACK-SIDE PROTECTIVE MEMBER
12: SEALING MATERIAL SHEET
13: SOLAR CELL
14: SEALING MATERIAL SHEET
15: FRONT-SIDE PROTECTIVE MEMBER
16: LAMINATING BOTTOM
17: 10 cm×10 cm EVA RESIN FILM
18: EVA RESIN ROLL
19: 1 cm×2 cm SAMPLE PIECE FOR MEASUREMENT OF MAXIMUM THICKNESS
20: 10 cm×10 cm EVA RESIN FILM
| Number | Date | Country | Kind |
|---|---|---|---|
| 2009-223906 | Sep 2009 | JP | national |
This application claims the benefit under 35 U.S.C. Section 371, of PCT International Application No. PCT/JP2010/066300, filed Sep. 21, 2010, which claimed priority to Japanese Application No. 2009-223906, filed Sep. 29, 2009 in the Japanese Patent Office, the disclosures of which are hereby incorporated by reference.
| Filing Document | Filing Date | Country | Kind | 371c Date |
|---|---|---|---|---|
| PCT/JP2010/066300 | 9/21/2010 | WO | 00 | 3/27/2012 |