The invention relates to a sealing material, to a gas seal made of this sealing material, and to a method for the production of such a gas seal made of this sealing material.
Sealing materials are used to seal a volume vis-à-vis another volume. Here, the seals can serve, for example, to keep out noxious gases or else as a vacuum seal in order to create or maintain a vacuum. Depending on the application, very different and, at times, high demands are made of such sealing materials, for example, when it comes to achieving good resistance to aggressive gases or a low permeation rate, for instance, for water, helium, nitrogen or oxygen (e.g. electric switching elements). Other important properties of seals are their resistance to the operating temperatures, resistance to oils, ultimate tensile strength, rupture strength, compression set resistance, outgassing behavior in a vacuum or their vacuum leakage rate.
Nowadays, no inexpensive sealing material is available that can satisfy all of the above-mentioned applications equally well. Different seals made of different sealing materials are used for the individual applications, depending on the requirements in question. Sometimes, metal seals in the form of disposable seals have to be used for this purpose. Consequently, different seals have to be kept on hand for various technical systems. It would be desirable if one single sealing material were available with which seals could be made that would meet a wide array of different requirements equally well. It would also be desirable if seals made of this sealing material were reusable in order to reduce material consumption.
It is one objective of the present invention to put forward a sealing material that is capable of meeting a wide array of requirements that have to be met by seals made of this material, especially a gas seal. Another objective of the invention is the production and provision of such a (gas) seal.
This objective is achieved by a sealing material for the production of a gas seal, preferably a vacuum seal, whereby the constituents of the sealing material include a bromobutyl elastomer in an amount of 100 parts by weight, a filler material in an amount between 10 and 100 parts by weight for setting the volume of the sealing material, a curing agent in an amount between 0.5 and 3.0 parts by weight for curing the sealing material, and a cross-linking component in an amount between 0.1 and 2.0 parts by weight for bringing about a peroxidic cross-linking of the sealing material in order to attain the desired gas-tightness.
In this context, the term “amount” refers to the relative volume ratios of the individual constituents with respect to each other, in relation to the appertaining weight of the individual constituents as such. The absolute total weight of a sealing material produced in this way depends on the application case in question. For example, within the scope of the present invention, a sealing material could contain 100 g of bromobutyl rubber as the bromobutyl elastomer, 45 g of filler material, 2 g of curing agent and 1 g of cross-linking component.
The main component of seals, especially gas seals, is an elastomer for achieving the sealing effect on the basis of the pressure exerted on the seal between the individual sealing surfaces. The bromobutyl rubber according to the invention, as the elastomer (bromobutyl elastomer) employed, permits a particularly high vacuum-tightness (that is to say, a low leakage rate) in comparison to sealing materials according to the state of the art, and accounts for resistance, on the one hand, to aggressive gases and, on the other hand, to pump oils such as, for instance, perfluoropolyethene oil or silicon oil. The filler material, for example, black carbon, does not itself bring about these properties, but in an advantageous manner, as a filling material, it creates processable a volume of the sealing material. The curing agent, for example, an organic peroxide, in combination with a suitable cross-linking component, permits a uniform and well-shaped curing of the sealing material, whereby this cross-linking component can bring about a sulfurous cross-linking or a peroxidic cross-linking. The cross-linking component, for example, a dimaleimide, serves as a multi-functional reagent for peroxidically cross-linked elastomers. The above-mentioned material properties of the sealing material according to the invention are attained through the interaction of the elastomer, the filler material, the curing agent and the cross-linking component.
The sealing material according to the invention is capable of meeting a wide array of different requirements that have to be met by seals made of this material such as, for example, a good resistance to aggressive gases, a low permeation rate, for example, for water, helium, nitrogen or oxygen (e.g. electric switching elements), a good resistance to the operating temperatures or to oils (pump oils), good ultimate tensile strength, rupture strength, compression set resistance, a slight to negligible outgassing behavior in a vacuum, and a very low vacuum leakage rate.
In one embodiment, the sealing material contains a plasticizer in an amount of less than 3 parts by weight, preferably between 0.3 and 1.5 parts by weight, which serves to improve the processing properties of the sealing material. The more plasticizer there is in the sealing material within the scope of the present invention, the softer the finished sealing material after it has been made into the desired shape and cured. However, the plasticizer amount should not be greater than necessary since the plasticizer can dissolve out during the later use of the sealing material in a gas seal. This is especially disadvantageous in the case of vacuum seals since, in this way, molecules evaporate out of the sealing material into the vacuum and the achieved final vacuum deteriorates, at least for a time period that is dependent on the pump capacity. Furthermore, the plasticizer can react chemically or can precipitate in an undesired manner inside the evacuated area. Plasticizers are preferably saturated carboxylic acids or fatty acids. An example of a suitable plasticizer is stearic acid.
In one embodiment, the sealing material contains, as an additional constituent, a material for acid neutralization in an amount of less than 5.0 parts by weight, preferably between 0.5 and 3.0 parts by weight. The material used for acid neutralization is an acid receptor for halogenated polymers. In this material, the neutralization effect is brought about, for example, by activated MgO that is embedded in an organic binder. The binder protects the MgO from absorbing moisture and thus from prematurely being converted into Mg(OH)2. An example of a suitable material for acid neutralization is Maglite DE.
In one embodiment, the sealing material contains, as an additional constituent, an antioxidant material in an amount of less than 5.0 parts by weight, preferably between 0.5 and 3.0 parts by weight. This antioxidant material can be used to chemically passivate reactive constituents of the sealing material or of compounds that reach the sealing material from the environment of the gas seal, so that the cross-linking of the sealing material is not detrimentally affected. This is particularly advantageous as protection against harmful oxidation reactions. An example of a suitable antioxidant material is Vulkanox MB2/MG.
In one embodiment, the filling material is chemically inert, so that the material properties of the sealing material that were previously set by the other constituents cannot be negatively affected. In one embodiment, the filler material is Statex N550. In a preferred embodiment, the filler material is black carbon. In another preferred embodiment, the amount of filler material in the sealing material is between 70 and 100 parts by weight. At this amount of filler material, the degree of hardness of the sealing material is higher and so is the hardness of the gas seal that is later made of this sealing material. If there is a smaller amount of filler material, softer gas seals can be made of the sealing material.
The invention also relates to a gas seal made of a sealing material according to the invention. The gas seal according to the invention is capable of meeting a wide array of requirements such as, for example, a good resistance to aggressive gases, a low permeation rate, for instance, for water, helium, nitrogen or oxygen (e.g. electric switching elements), a good resistance to the operating temperatures or to oils (pump oils), a good ultimate tensile strength, rupture strength, compression set resistance, a slight to negligible outgassing behavior in a vacuum, and a very low vacuum leakage rate.
In one embodiment, the gas seal is configured as an O-ring seal. O-rings are ring-shaped sealing elements, whereby the shape can also differ from a circular shape. For instance, O-rings can also be elliptical. Thanks to the relatively simple shape of O-rings, they are easy to manufacture on an industrial scale. Preferably, injection molding is used, but compression molding can also be employed to manufacture O-rings in case of small production runs. Due to its circular cross section, an O-ring can seal axially and/or radially. The initial tightness is effectuated by the compression of the rubber element during the installation (in the radial and/or in the axial direction). The sealing compression is a function of the superimposition of the pre-compression (owing to the installation) and of the system pressure that is to be sealed. Therefore, the sealing pressure that prevails in the sealing joint is higher by the magnitude of the pre-compression than the pressure that is to be sealed. Consequently, very high pressures can be sealed. O-rings are normally made in various standard sizes.
In one embodiment, the gas seal is configured as a metal-elastomer composite seal with a suitably shaped metal core encapsulated by the sealing material. An example of the metal that can be used here is copper. In this context, the term composite seal refers to a seal where the metal core is encapsulated by the sealing compound, but it does not mean a mixed material made of sealing material with metal fractions. Such a composite seal can withstand greater flange pressures (pressure of the sealing surfaces onto the seal) than a seal without a metal core. Here, the shape of the metal core is adapted to the shape of the later gas seal. For example, the metal core can be shaped as a flat ring or, in the case of an O-ring seal, as a metal ring whose cross section is smaller than the cross section of the later gas seal, for example, the later O-ring. Such composite seals have a lower leakage rate than gas seals made only of the sealing material according to the invention and, in contrast to pure metal seals, they can be reused.
In one embodiment, the gas seal according to the invention can be used as a vacuum seal. In a preferred embodiment, the constituents of the sealing material are selected in such a way that the gas seal has a leakage rate of less than 10−9 mbar*L/s. In one embodiment of the sealing compound according to the invention for a gas seal having a leakage rate of less than 10−9 mbar*L/s, the sealing compound contains bromobutyl rubber at 100 parts by weight as the elastomer, the filler material at 45±4.0 parts by weight (for example, Statex N550 as the filler material), the material for acid neutralization (acid neutralizer) at 1.0±0.2 parts by weight (for example, Maglite DE as the acid neutralizer), the plasticizer at 1.0±0.2 parts by weight (for example, stearic acid as the plasticizer), the antioxidant material at 1.0±0.2 parts by weight (for example, Vulkanox MB2/MG as the antioxidant material), the curing agent at 2.0±0.3 parts by weight (for example, Perkadox BC-40B-PD as the curing agent), the cross-linking component at 1.0±0.2 parts by weight (for example, N,N′-m-phenylene dimaleimide as the cross-linking component) and optionally, polyethylene glycol at 1.5±0.3 parts by weight (for example, PEG 4000). In one embodiment, this sealing material is used in a metal-elastomer composite seal.
Thus, the gas seal made of the sealing material according to the invention for rubber seals has excellent sealing properties that could otherwise only be achieved with expensive metal seals (copper seals) that can only be used one time. In comparison to metal seals, the gas seal according to the invention is an inexpensive and reliable alternative that, in addition, is reusable, so that the vacuum system can be quickly opened and closed again without a need to replace the gas seal.
The invention also relates to a method for the production of a gas seal according to the invention, comprising the following steps:
The gas seal (gas-tight seal) can be shaped, for example, by means of a compression procedure in an appropriate machine. Here, known and commercially available machines and methods can be used to produce gas seals, for example, sealing rings. The terms “suitable curing temperature” and “suitable curing time” are interrelated. The higher the curing temperature is, the shorter the curing time can be. Conversely, a gas seal made of the sealing material according to the invention requires a longer curing time at a lower curing temperature. For example, the curing temperature for a curing time between 4 and 7 minutes could be between 90° C. and 110° C. In another embodiment, for example, the curing temperature for a curing time between 1 and 2 minutes could be between 170° C. and 200° C.
In one embodiment, the method also comprises the step of setting the available time interval for processing the sealing material to form a gas seal, which is done by adjusting the amount of plasticizer.
In one embodiment, the step of shaping the gas seal comprises the step of encapsulating a suitably shaped metal core with the sealing material in order to produce a metal-elastomer composite seal. Here, the core is preferably completely encapsulated.
These and other aspects of the invention are shown in detail in the figures as follows:
The embodiments shown here are only examples of the present invention and therefore must not be construed in a limiting manner. Alternative embodiments taken into consideration by the person skilled in the art are likewise encompassed by the scope of protection of the present invention.