The present invention relates to a sealing material, and more particularly, to a sealing material suitable for sealing a hermetic terminal of a refrigerant compressor to be used in a refrigerator and the like.
A hermetic terminal of a refrigerant compressor is produced by sealing a metal stem and a metal pin to each other with a sealing material in order to maintain hermetic reliability.
The sealing material is produced and used as described below. First, a glass raw material is melted and formed, and the resultant formed body is pulverized in a ball mill and then allowed to pass through a predetermined sieve to provide fine powder. Next, granules are produced by mixing the fine powder with a binder and granulating the mixture. In some cases, the granules are obtained by adding and mixing ceramic powder to glass powder and granulating the resultant composite powder. After that, the resultant granules are subjected to tablet molding to produce a green compact having a through-hole, and the green compact is increased in temperature from normal temperature, to thereby decompose and remove the binder and sinter the green compact. Next, a metal pin is inserted in the through-hole of the resultant sintered compact, and the sintered compact is in turn housed in a circular metal stem, followed by being loaded into a firing furnace, and fired at a temperature higher than a glass transition point under an inert atmosphere or a nitrogen atmosphere, to thereby seal the metal pin and the metal stem to each other. As a result, the sealing material is in a state of being compressed by the metal stem. The metal stem generally has a linear thermal expansion coefficient of 140×10−7/° C. The metal, pin generally has a linear thermal expansion coefficient of from 100×10−7/° C. The sealing material generally has a linear thermal expansion coefficient of from 89×10−7/° C. to 95×10−7/° C.
Patent literature 1: JP 2014-175069 A
Patent Literature 2; JP 2015-064928A
Patent Literature 3: JP 2015-069732 A
In recent years, there has been an attempt to increase the capacity of a refrigerator and the like by increasing the current capacity of the hermetic terminal. In order to increase the current capacity of the hermetic terminal, it is effective to use a highly conductive metal as a core material of the metal pin.
However, when a metal pin comprising such highly conductive metal is sealed with a related-art sealing material, the sealing material is subjected to a large tensile stress by being pulled by the shrinking metal pin in the course of cooling to room temperature after a sealing step. With this, cracks are liable to occur in the sealing material, which may cause hermetic leakage of a refrigerant at the time of incorporation in the refrigerator and the like. Probable causes for this are that glass for sealing shows relatively low expansion and the highly conductive metal shows relatively high expansion, and that a difference in thermal expansion between the two is large.
The present invention has been made in view of the above-mentioned circumstances, and a technical object of the present invention is to devise a sealing material which hardly causes cracks when a metal pin comprising a highly conductive metal is sealed therewith, to thereby increase the current capacity and the hermetic reliability of a hermetic terminal.
The inventors of the present invention have repeated various experiments, and as a result, have found that the above-mentioned technical object can be achieved by restricting the linear thermal expansion coefficient of a sealing material within a predetermined range. Thus, the finding is proposed as the present invention. That is, according to one embodiment of the present invention, there is provided a sealing material for sealing a metal material, comprising 70 mass % to 100 mass % of glass powder comprising alkali silicate glass and 0 mass % to 30 mass % of ceramic powder, and having a linear thermal expansion coefficient in a temperature range of from 30° C. to 380° C. of more than 100×10−7/° C. and 170×10−7/° C. or less. Herein, the “alkali silicate glass” refers to glass which comprises SiO2 and an alkali metal oxide (Li2O, Na2O, and K2O) in a glass composition and in which the total amount of these components is 60 mol % or more. The “linear thermal expansion coefficient in a temperature range of from 30° C. to 380° C.” refers to an average value obtained through measurement using a sintered compact processed into a predetermined shape as a measurement sample with a push-rod-type thermal expansion coefficient measurement apparatus (THA).
The sealing material according to the embodiment of the present invention comprises 70 mass % to 100 mass % of the glass powder comprising alkali silicate glass. When the glass powder comprising alkali silicate glass is used, a bonding temperature can be reduced while an increase in expansion of the sealing material is achieved.
In addition, the sealing material according to the embodiment of the present invention has a linear thermal expansion coefficient in a temperature range of from 30° C. to 380° C. of more than 100×10−7/° C. With this, when a metal pin comprising a highly conductive metal is sealed with the sealing material, the sealing material is hardly subjected to a large tensile stress from the metal pin in the course of cooling to room temperature after a sealing step, and cracks hardly occur in the sealing material. As a result, a situation in which hermetic leakage of a refrigerant occurs at the time of incorporation in a refrigerator and the like can be prevented.
Further, the sealing material according to the embodiment of the present invention has a linear thermal expansion coefficient in a temperature range of from 30° C. to 380° C. of 170×10−7/° C. or less. With this, the sealing material is easily subjected to a compression stress from a metal stem after the sealing step, and the hermetic reliability of a hermetic terminal can be increased.
Secondly, in the sealing material according to the embodiment of the present invention, it is preferred that the glass powder comprise high-expansion glass powder, and that the high-expansion glass powder comprise as a glass composition, in terms of mol %, 55% to 75% of SiO2, 0% to 10% of B2O3, 1% to 12% of Al2O3, 17% to 28% of Li2O+K2O, and 0% to 15% of MgO+CaO+SrO+BaO. With this, the linear thermal expansion coefficient of the sealing material can be property increased. Herein, the “high-expansion glass powder” to glass powder having a linear thermal expansion coefficient in a temperature range of from 30° C. to 380° C. of more than 100×10−7/° C. The content of “Li2O+Na2O+K2O” refers to the total content of Li2O, Na2O, and K2O. The content of “MgO+CaO+SrO+BaO” refers to the total content of MgO, CaO, SrO, and BaO.
Thirdly, in the sealing material according to the embodiment of the present invention, it is preferred that the glass powder comprise the high-expansion glass powder and low-expansion glass powder. Herein, the “low-expansion glass powder” refers to glass powder having a linear thermal expansion coefficient in a temperature range of from 30° C. to 380° C. of 100×10−7/° C. or less.
Fourthly, in the sealing material according to the embodiment of the present invention, it is preferred that the sealing material comprise 70 mass % to 99 mass % of the glass powder and 1 mass % to 30 mass % of the ceramic powder, that the glass powder comprise low-expansion glass powder, and that the ceramic powder comprise high-expansion ceramic powder. Herein, the “high-expansion ceramic powder” refers to ceramic powder having a linear thermal expansion coefficient in a temperature range of from 30° C. to 380° C. of more than 100×10−7/° C.
Fifthly, in the sealing material according to the embodiment of the present invention, it is preferred that the high-expansion ceramic powder comprise any one of cristobalite, tridymite, and calcium fluoride.
Sixthly, in the sealing material according to the embodiment of the present invention, it is preferred that the sealing material have a granular form.
Seventhly, in the sealing material according to the embodiment of the present invention, it is preferred that the sealing material comprise a sintered compact.
Eighthly, in the sealing material according to the embodiment of the present invention, it is preferred that the sealing material be used for sealing a hermetic terminal.
In a sealing material of the present invention, the content of glass powder is from 70 mass % to 100 mass %, preferably from 80 mass % to 100 mass %, more preferably from 90 mass % to 100 mass %, still more preferably from 95 mass % to 100 mass %, particularly preferably from more than 97 mass % to 100 mass %. In addition, the content of ceramic powder is from 0 mass % to 30 mass %, preferably from 0 mass % to 20 mass %, more preferably from 0 mass % to 10 mass %, still more preferably from 0 mass % to 5 mass %, particularly preferably from 0 mass % to less than 3 mass %. When the content of the glass powder is too small (when the content of the ceramic powder is too large), the amount of a melting accelerate component is reduced, and hence sufficient fluidity is not obtained in a sealing step, and hermetic reliability is liable to be reduced.
The sealing material of the present invention has a linear thermal expansion coefficient in a temperature range of from 30° C. to 380° C. of more than 100×10−7/° C., preferably 103×10−7/° C. or more, more preferably 106×10−7/° C. or more, still more preferably 108×10−7/° C. or more. When the linear thermal expansion coefficient in a temperature range of from 30° C. to 380° C. is too low, in the case in which a metal pin comprising a highly conductive metal is sealed with the sealing material, the sealing material is liable to be subjected to a large tensile stress from the metal pin in the course of cooling to room temperature after the sealing step, and cracks are liable to occur in the sealing material. As a result, there is a risk in that hermetic leakage of a refrigerant occurs at the time of incorporation in a refrigerator and the like. Meanwhile, the sealing material of the present invention has a linear thermal expansion coefficient in a temperature range of from 30° C. to 380° C. of 170×10−7/° C. or less, preferably 150×10−7/° C. or less, more preferably 130×10−7/° C. or less, still more preferably 120×10−7/° C. or less. When the linear thermal expansion coefficient in a temperature range of from 30° C. to 380° C. is too high, it becomes difficult for the sealing material to be subjected to a compression stress from a metal stem after the sealing step, and the hermetic reliability of a hermetic terminal is liable to be reduced.
In the sealing material of the present invention, it is preferred that the glass powder comprise at least high-expansion glass powder, and that the high-expansion glass powder comprise as a glass composition, in terms of mol %, 55% to 75% of SiO2, 0% to 10% of B2O3, 1% to 12% of Al2O3, 17% to 28% of Li2O+Na2O+K2O, and 0% to 15% of MgO+CaO+SrO+BaO. The reasons why the contents of the components of the high-expansion glass powder are limited as described above are described below. In the description of the contents of the components, the expression “%” means “mol %”.
SiO2 is a main component for forming a glass skeleton, and the content of SiO2 is preferably from 55% to 75%, more preferably from 60% to 70%. When the content of SiO2 is too small, there is a risk in that the linear thermal expansion coefficient is increased improperly. In addition, water resistance and weather resistance are liable to be reduced. Meanwhile, when the content of SiO2 is too large, there is a risk in that the linear thermal expansion coefficient is reduced improperly. In addition, a bonding temperature is liable to be increased. When the water resistance and the weather resistance are reduced, glass has restriction in its handling in a granulation step, and further, there is a risk in that the long-term reliability of the hermetic terminal is reduced.
B2O3 is a component which increases meltability and reduces the bonding temperature. The content of B2O is preferably from 0% to 10%, more preferably from 0% to 5%, still more preferably from 0% to 3%. When the content of B2O3 is too large, abnormal shrinkage is liable to occur in a temperature range around a glass transition point in the course of cooling to room temperature after the sealing step.
Al2O3 is a component which increases the water resistance and the weather resistance. The content of Al2O3 is preferably from 1% to 12%, more preferably from 2% to 10%, still more preferably from 5% to 8%. When the content of Al2O3 is too small, the water resistance and the weather resistance are liable to be reduced. Meanwhile, when the content of Al2O3 is too large, there is a risk in that the linear thermal expansion coefficient is reduced improperly. In addition, the bonding temperature is liable to be increased.
An alkali metal oxide (Li2O, Na2O, and K2O) is a component which increases the linear thermal expansion coefficient, and is also a component which reduces the bonding temperature, but is a component which reduces the water resistance and the weather resistance. The content of Li2O+Na2O+K2O is preferably from 17% to 28%, more preferably from 19% to 25%, still more preferably from more than 20% to 23%. The content of Li2O is preferably from 0% to 12%, more preferably from 0% to 8%, still more preferably from 0% to 5%. The content of Na2O is preferably from 10% to 23%, more preferably from 12% to 20%, still more preferably from 15% to 18%. The content of K2O is preferably from 1% to 12%, more preferably from 3% to 10%, still more preferably from 5% to 7%. When the content of the alkali metal oxide is too small, there is a risk in that the linear thermal expansion coefficient is reduced improperly. In addition, the bonding temperature is liable to be increased. Meanwhile, when the content of the alkali metal oxide is too large, the water resistance and the weather resistance are liable to be reduced.
An alkaline earth metal oxide (MgO, CaO, SrO, and BaO) is a component which reduces the bonding temperature. The content of MgO+CaO+SrO+BaO is preferably from 0% to 15%, more preferably from 2% to 12%, still more preferably from 4% to 9%. The content of MgO is preferably from 0% to 7%, more preferably from 1% to 5%. The content of CaO is preferably from 0% to 7%, more preferably from 1% to 5%. The content of SrO is preferably from 0% to 5%, more preferably from 0% to 3%, still more preferably from 0% to 1%. The content of BaO is preferably from 0% to 5%, more preferably from 0% to 3%, still more preferably from 0% to 1%. When the content of the alkaline earth metal oxide is too small, the bonding temperature is liable to be increased. Meanwhile, when the content of the alkaline earth metal oxide is too large, the glass skeleton is liable to be unstable.
Other than the above-mentioned components, for example, TiO2, ZrO2, F2, Cl2, La2O3, MnO2, Cr2O3, Fe2O3, Co2O3, and the like may be introduced at respective contents of from 0.1% to 5% unless the effects of the present invention are impaired improperly.
In the sealing material of the present invention, the glass powder preferably comprises the high-expansion glass powder and low-expansion glass powder. In general, when the linear thermal expansion coefficient of the glass powder is to be increased, the content of the alkali metal oxide in a glass composition needs to be increased. In this case, however, the water resistance and the weather resistance of the glass powder are liable to be reduced. Therefore, the high-expansion glass powder tends to have low water resistance and low weather resistance, and the low-expansion glass powder tends to have high water resistance and high weather resistance. In view of the foregoing, the high-expansion glass powder and the low-expansion glass powder are mixed to be used as the glass powder, and thus the drawbacks of both the powders can be compensated for by each other. That is, the water resistance and the weather resistance can be increased while the linear thermal expansion coefficient is increased.
Various alkali silicate glasses may be used as the low-expansion glass powder. Of those, low-expansion glass powder comprising as a glass composition, in terms of mol %, 65% to 82% of SiO2, 0% to 10% of B2O3, 0% to of Al2O3, 10% to 20% of Li2O+Na2O+K2O, and to 1% to 15% of MgO+CaO+SrO+BaO is preferred. With this, the water resistance and the weather resistance can be increased while the bonding temperature is reduced.
Other than the above-mentioned case in which the sealing material of the present invention is formed only of the glass powder, it is also preferred that the sealing material of the present invention comprise 70 mass % to 99 mass % of the glass powder and 1 mass % to 30 mass % of the ceramic powder, the glass powder contain the low-expansion glass powder, and the ceramic powder contain high-expansion ceramic powder. When the low-expansion glass powder and the high-expansion ceramic powder are introduced in the sealing material, the water resistance and the weather resistance can be increased while the linear thermal expansion coefficient of the sealing material is increased. In this case, the content of the high-expansion ceramic powder is preferably from 1 mass % to 30 mass %, more preferably from 2 mass % to 15 mass %, still, more preferably from 3 mass % to 6 mass %. When the content of the high-expansion ceramic powder is too small, it becomes difficult to increase the linear thermal expansion coefficient of the sealing material. Meanwhile, when the content of the high-expansion ceramic powder is too large, the amount of the melting accelerate component is reduced, and hence bonding strength is reduced, and the hermetic reliability is liable to be reduced.
Various ceramic powders may be used as the high-expansion ceramic powder, but from the viewpoint of compatibility with the alkali silicate glass, any one of cristobalite, tridymite, and calcium fluoride is preferred.
The sealing material of the present invention preferably has a granular form. With this, a green compact having a predetermined shape, particularly a green compact having a through-hole for inserting a metal pin can be easily produced through tablet molding.
The sealing material of the present invention preferably comprises a sintered compact. With this, when the sealing material having inserted therein a metal pin is housed in a metal stem, chipping of the sealing material can be suppressed.
Now, the present invention is described by way of Examples. The following Examples are merely illustrative. The present invention is by no means limited to the following Examples.
Sample Nos. 1 and 2 are shown in Table 1.
First, a glass batch obtained by blending glass raw materials so as to give the glass composition shown in Table 1 was loaded in a platinum crucible, and melted at 1,500° C. for 4 hours. At the time of the melting, the glass batch was stirred with a platinum stirrer to be homogenized. Next, the resultant molten glass was formed into a film shape with a double roller, pulverized with a ball mill, and then classified with a test sieve. Thus, Sample Nos. 1 and 2 each having an average particle diameter D50 of about 30 μm were obtained, Sample Nos. 1 and 2 were each measured for a linear thermal expansion coefficient in a temperature range of from 30° C. to 380° C. The linear thermal expansion coefficients of Sample Nos. 1 and 2 are each an average value obtained through measurement using glass bulk processed into a predetermined shape as a measurement sample with a push-rod-type thermal expansion coefficient measurement apparatus (TMA).
A sealing material was obtained by mixing Sample No. 1 and Sample No. 2 at a mass ratio of 1:1, followed by granulation. The sealing material had a linear thermal expansion coefficient in a temperature range of from 30° C. to 380° C. of 110×10−7/° C. The linear thermal expansion coefficient of the sealing material is an average value obtained through measurement with TMA using, as a measurement sample, a sintered compact processed into a predetermined shape after having been sintered at a temperature higher than the softening point of the sealing material by 30° C. (the same applies to Experiment 2).
A sealing material, was obtained by mixing Sample No. 1 and cristobalite powder (average particle diameter D50: about 10 μm) at a mass ratio of 96:4, followed by granulation. The sealing material had a linear thermal expansion coefficient in a temperature range of from 30° C. to 380° C. of 110×10−7/° C.
The linear thermal expansion coefficients in a temperature range of from 30° C. to 380° C. of the sealing materials obtained in Experiments 1 and 2 are restricted within a predetermined range. Therefore, it is considered that cracks hardly occur in each of the sealing materials obtained in Experiments 1 and 2 when a metal pin comprising a highly conductive metal is sealed with the sealing material. As a result, it is considered that the current capacity and the hermetic reliability of a hermetic terminal can be increased through use of each of the sealing materials obtained in Experiments 1 and 2.
1 hermetic terminal
11 metal stem
12 metal pin
13 sealing material
| Number | Date | Country | Kind |
|---|---|---|---|
| 2016-003221 | Jan 2016 | JP | national |
| Filing Document | Filing Date | Country | Kind |
|---|---|---|---|
| PCT/JP2017/000165 | 1/5/2017 | WO | 00 |
| Publishing Document | Publishing Date | Country | Kind |
|---|---|---|---|
| WO2017/122578 | 7/20/2017 | WO | A |
| Number | Name | Date | Kind |
|---|---|---|---|
| 3723790 | Dumbaugh, Jr. | Mar 1973 | A |
| 3776764 | Takagi et al. | Dec 1973 | A |
| 4417913 | Davis | Nov 1983 | A |
| 4556613 | Taylor | Dec 1985 | A |
| 4752521 | Smith, III | Jun 1988 | A |
| 4814298 | Nelson et al. | Mar 1989 | A |
| 4952531 | Cherukuri | Aug 1990 | A |
| 6291092 | Kohli | Sep 2001 | B1 |
| 7189470 | Cortright | Mar 2007 | B2 |
| 10390427 | Kanbara | Aug 2019 | B2 |
| 20050277541 | Yoshii | Dec 2005 | A1 |
| 20060160690 | Cortright et al. | Jul 2006 | A1 |
| 20120171810 | Park | Jul 2012 | A1 |
| 20190023605 | Hirose | Jan 2019 | A1 |
| Number | Date | Country |
|---|---|---|
| 49-35044 | Sep 1974 | JP |
| 1-153554 | Jun 1989 | JP |
| 2004123496 | Apr 2004 | JP |
| 2008-527680 | Jul 2008 | JP |
| 2012074268 | Apr 2012 | JP |
| 2014-175069 | Sep 2014 | JP |
| 2015-64928 | Apr 2015 | JP |
| 2015-69732 | Apr 2015 | JP |
| 2004031088 | Apr 2004 | WO |
| Entry |
|---|
| International Preliminary Report on Patentability dated Jul. 17, 2018 in International Application No. PCT/JP2017/000165. |
| International Search Report dated Apr. 11, 2017 in International Application No. PCT/JP2017/000165. |
| Number | Date | Country | |
|---|---|---|---|
| 20190010082 A1 | Jan 2019 | US |