This application is a national stage entry, filed under 35 U.S.C. § 371, of International Application No. PCT/GB2015/051591, filed on Jun. 1, 2015, and claims the benefit of and priority to UK Patent Application No. GB1409799.2, filed Jun. 2, 2014, and UK Patent Application No. GB1410115.8, filed Jun. 6, 2014, the entire contents of each are hereby incorporated herein by reference in their entireties and for all purposes.
This invention relates to the preparation of seeds.
It is known to treat seeds and/or seedbeds in order to improve the seeds' germination and/or growth. The preparations used for these purposes may include fertilisers, biostimulants, pesticides, fungicides and bacteria. For example, U.S. Pat. No. 6,582,637 discloses encapsulating seeds with a composition that can include blends of various sulphates, soda ash, sulphur and potash as part of a compost coating. GB 983,920 discloses coating seeds with hydrophobic compounds which could include metal salts. An example composition disclosed in GB 983,920 includes potash waterglass (i.e. potassium silicate).
Whilst coating seeds with fertiliser might intuitively seem an attractive approach, in practice it has considerable difficulties. In particular, many fertiliser compositions that are effective when applied to a seedbed have been found to be unsuitable for coating seeds due the fact that they impair germination. (See, e.g., GB 983,920 at page 1, lines 11 to 15). There may be various reasons for this effect, but one is believed to be the creation of an excessively saline environment adjacent to the seed. Excessive salinity can desiccate the seed and the environment around it. It is generally considered that many fertiliser compositions should be applied no closer than, e.g. 5 to 10 cm from newly sown seeds. On account of these effects the fertiliser compositions that are used for coating seeds on a commercial basis are in general formulated specially for that purpose.
It would be desirable to have a material that could be readily manufactured, and that could improve the germination and/or growth of seeds when applied to the seeds as a coating.
According to one aspect of the present invention there is provided a coated seed product, the product comprising: at least one plant seed; and a coating adhered to the exterior of the plant seed, the coating comprising one or more evaporite minerals.
According to a second aspect of the present invention there is provided a method of forming a coated seed product comprising: forming a slurry comprising an evaporite mineral powder and a binder; applying the slurry to plant seeds so as to coat the seeds with the slurry; and drying the seeds to stabilise the coating.
The coating may comprise more than 50%, 60%, 70%, 80%, 90% or 95% by weight of the evaporite mineral(s).
The one or more evaporite minerals may comprise polyhalite. The one or more evaporite minerals may principally comprise polyhalite. The evaporite mineral content of the coating may be essentially solely of polyhalite.
The coating may comprises more than 50%, 60%, 70%, 80%, 90% or 95% polyhalite by weight.
The one or more evaporite minerals may be in the form of a powder. The number average grain size of the powder may be less than 500 μm.
The average thickness of the coating may be in the range from 0.1 mm to 2.0 mm. The average thickness of the coating may be in the range from 0.1 mm to 1.0 mm.
The mass of the coating may be in the range from 1 to 500 g per kg of seed. The mass of the coating may be in the range from 1 to 20 g per kg of seed. The mass of the coating may be in the range from 1 to 10 g per kg of seed. The mass of the coating averaged over a representative sample of the product may be in the range from 1 to 20 g per kg of seed or 1 to 10 g per kg of seed. That sample may contain more than 1000 or more than 10,000 seeds. The mass of the sample may be greater than 10 kg.
An aspect of the invention may be a coated seed product comprising a certain amount of content, the product comprising: at least one plant seed; and a coating adhered to the exterior of the plant seed, the coating comprising one or more evaporite minerals; wherein the mass of the coating is (a) above any of 1, 2, 3, 4 or 5 g per kg of seed and/or (b) less than any of 10, 12, 15, 18 or 20 g per kg of seed. The content may be more than any of 10 kg, 25 kg, 100 kg or 1000 kg and/or above 1000, 10,000 or 100,000 seeds.
The seed product may be a bulk seed product.
The seeds may be unsown seeds.
The seed may be a seed of a crop species. The seed may be a seed of a non-crop species.
The coating may comprise a binder whereby the one or more evaporite minerals is/are adhered to the exterior of the seed. The coating may comprise a matrix of binder in which particles of the one or more evaporite minerals are embedded. The coating may fully or partially enclose the seed. The binder may be susceptible to degradation on exposure to moisture. The binder may be such as to release at least 50% of the mineral particles embedded therein on exposure to an atmosphere having a relative humidity of 90% for two weeks.
The coating may be adhered directly to the exterior of the plant seed. The product may comprise an intermediate layer adhered directly to the exterior of the plant seed, and wherein the coating may be adhered to the intermediate layer. The intermediate layer may form a barrier layer between the exterior of the plant seed and the coating.
The seed may be a seed of beet, lettuce, oil seed rape, pea, rice or wheat, or of another plant.
The method may comprise mining the evaporite mineral(s). The method may comprise crushing the as-mined evaporite mineral(s) to form powder.
The present invention will now be described by way of example with reference to the accompanying drawings.
In the drawings:
Polyhalite is a complex hydrated sulphate of potassium, calcium and magnesium of general formula K2Ca2Mg(SO4)4.2H2O. Polyhalite has a Moh's hardness of around 2.5 to 3.5.
Once mined, polyhalite may be broken into blocks or chips of suitable size for transport and processing. For example, referring to
The raw or chipped polyhalite is processed to form a polyhalite powder. This may suitably be done by milling, for exampling in a ball mill (e.g. a continuous “Hardinge” ball mill) and more preferably an attritor mill 13. In an attritor mill the feedstock is agitated together with freely moving grinding elements such as steel balls. Air-swept suction may be applied in order to draw the milled material out of the mill. This allows the milling to be performed as a continuous process if desired, with chipped feedstock being added to the mill and powder being swept out of the mill by gas flow whilst the grinding elements continue to be agitated. The average grain size of the powder is dependent on various process parameters including the dwell time of the feedstock in the mill. Conveniently, the mill may be arranged to produce polyhalite powder grain size in the range from 50 to 400 μm, more preferably from 100 to 250 μm. Conveniently at least 50% or more preferably at least 70% of the mass of the polyhalite powder is composed of grains having a grain size, or a largest or average diameter, in the range from 50 to 400 μm, more preferably from 100 to 250 μm. Conveniently 90% by number of the grains of the powder are smaller than 500 μm in diameter. The grain size may be as measured by means of a Malvern Mastersizer 2000 or as measured by means of a sieve shaker.
In the next processing step a binder is added to the polyhalite powder, along with a liquid such as water, in a mixer 14. The binder helps the polyhalite powder to adhere to seeds and increases the strength of the eventual seed coating. That is important because the pellets should preferably be capable of resisting mechanical breakdown when spread through conventional agricultural drilling machinery. Any suitable binder may be used. Examples include starch, lignosulphates, sugars, milled grain, synthetic polymers such as polyvinyl acetate and dedicated seed coating binders such as Sepiret which is available from Agrichem (International) Limited. The optimal amount of binder may be determined by balancing the strength of the final coating with its ability to break down once spread on a growing medium. If too little binder is added then the resulting coated seeds may have insufficient strength and the coating may fall off the seeds during transport or drilling. If excess binder is added then the seed coating can be too resistant to breakdown in the field, impairing germination and/or growth of the seeds. One or more solid or liquid adjuvants may also be added. When it is added to the polyhalite powder the binder may be in dry form, e.g. as a powder, or in liquid form, e.g. as a suspension or solution in a liquid carrier.
In
The slurry is introduced to a rotating drum 15, along with seeds. The drum tumbles or rolls the seeds together with the slurry in order to coat the seeds with the slurry. The slurry may be sprayed into the drum.
Then the coated seeds pass to a dryer 16 which drives off excess moisture and stabilises (e.g. hardens) the coating, forming a supply of coated seeds as illustrated at 17. The seeds can then be packaged and transported to the growing site for planting or spreading.
The coated seeds may form a coated seed product, which may comprise many such seeds.
Once the seeds have been sown on or in a growing medium, the coating breaks down in the presence of moisture. That permits the moisture to reach the seed, assisting in inducing it to germinate.
The seeds could be coated using other processes. For example, the seeds could be coated in binder and then tumbled in the polyhalite powder; or the seeds could be tumbled in polyhalite powder without binder, to cause a dusting of polyhalite powder to adhere to the seeds.
Additional components could be included in the coating. Such components may be any one or more of the following, in any combination:
Such a component may be added at various stages in the process, for example it could be combined with the polyhalite powder before or after the formation of a slurry as described above, or with the binder prior to the mixing stage as described above, or it could be sprayed or otherwise coated on to the seeds before or after drying. The component could be sprayed or otherwise coated on to the seeds before the seeds are coated with the slurry, for example one or more components could be applied to the seed prior to the seeds being coated by the slurry.
As shown in
In practice, the mean thickness of the coating could be in the range from 0.1 to 1.0 mm, the mean thickness of the coating could also be in the range from 0.1 to 2.0 mm, but the range can be chosen to suit the seed in question and the desired mass of polyhalite per seed.
The coating could, for example, contain above 50%, above 60%, above 70% above 80%, above 90% or above 95% polyhalite by weight.
The mass of polyhalite with which each seed is coated can be controlled through the choice of binder, the relative proportions of binder and polyhalite in the slurry, the viscosity of the slurry, the dwell time of the seeds in the drum 5 and the spraying rate of slurry into the drum 5.
The response of seeds to a polyhalite coating has been found to vary depending on factors including the species of the seed and the medium in which the seed was grown. In trials conducted on a range of crop seeds including rice, wheat, peas, lettuce, oil seed rape and beet no phytotoxic effects of the coating were observed at doses of polyhalite up to at least 50 g per kg of seed. However, the same trials suggested that good benefits could be had from polyhalite at significantly lower dose rates, with a correspondingly lower cost of polyhalite. In general, the preferred dosage rate of polyhalite is in a range from 1 to 20 grams per kg of seed, more preferably from 1 to 10 grams per kg of seed.
The seed may be a seed of an angiosperm and/or of a crop species. The seed may be a seed of a cereal species such as wheat, maize, rice, millet, barley, oats or rye. The seed may be a seed of a root vegetable species such as beet. The seed may be a seed of a pulse such as peas. Other examples include lettuce and oil seed rape. The seed may be a seed of a non-crop species.
In trials it has been found that the polyhalite coating can have a particularly strong effect in promoting initial growth of the seed, especially initial aerial growth. This can be especially valuable in enabling the seedling to survive damage from parasites, pests, pathogenic disease and adverse environmental conditions. For example, a seed that puts on strong early aerial growth may be more resistant to attack by ground-based pests such as slugs. A plant that has improved root development may be more robust to rain storm events in early growth.
Trials were conducted to assess the effectiveness of the polyhalite coating on the germination and early growth of seeds.
Rice seeds were coated with polyhalite at ranges from 2 to 52 grams of polyhalite per kg of seed. The seeds were grown under semi-controlled conditions alongside uncoated rice seeds using sand and compost as the growing media. The heights of the plants were measured 11 days after application of the seeds (11 DAA). The average height of the untreated seeds was around 5.3 cm in compost and 7.4 cm in sand. A significant increase in plant height was recorded for the seeds coated with around 2 to 25 grams of polyhalite per kg of seed. For example, the average plant height for seeds coated with 2 g of polyhalite per kg of seed grown in compost was around 10.5 cm and the average plant height for seeds coated with 8 g of polyhalite per kg of seed grown in sand was around 12.0 cm.
These results are illustrated in
Wheat seeds were coated with polyhalite at ranges from 2 to 47 grams of polyhalite per kg of seed. The seeds were grown under semi-controlled conditions alongside uncoated wheat seeds using sand and compost as the growing media. The heights of the plants were measured 15 days after application of the seeds. The average height of the untreated seeds was around 24.9 cm in sand. A significant increase in plant height was recorded for the seeds coated with around 2 to 10 grams of polyhalite per kg of seed. For example, the average plant height for seeds coated with 2 g of polyhalite per kg of seed grown in sand was around 26.2 cm and the average plant height for seeds coated with 8 g of polyhalite per kg of seed grown in sand was around 26.9 cm.
These results are illustrated in
In this example a similar response was not observed for the seeds grown in compost. This may be due to the compost providing a greater level of nutrients than the sand.
Pea seeds were coated with polyhalite at ranges from 2 to 28 grams of polyhalite per kg of seed. The seeds were grown under semi-controlled conditions alongside uncoated pea seeds using sand and compost as the growing media. The heights of the plants were measured 15 days after application of the seeds. The average height of the untreated seeds was around 6.9 cm in sand. A significant increase in plant height was recorded for the seeds coated with around 2 to 10 grams of polyhalite per kg of seed. For example, the average plant height for seeds coated with 2 g of polyhalite per kg of seed grown in sand was around 7.6 cm and the average plant height for seeds coated with 5 g of polyhalite per kg of seed grown in sand was around 7.8 cm.
These results are illustrated in
Similar trials were conducted using seeds of lettuce, beet and oil seed rape. These also showed benefits from the use of polyhalite coatings, particularly at levels below 20 g of polyhalite per kg of seed.
One potential mechanism for the observed improvement in initial growth is that the polyhalite may bring about an improvement in the microfungal environment adjacent to the seeds.
The process as described above may be used for coating seeds with minerals other than polyhalite, and in particular for coating seeds with one or more evaporite minerals, especially sulphite or chloride minerals. These may include any one or more of anyhdrite, carnalite, gypsum, halite, kainite, kieserite, langbeinite, polyhalite and/or sylvite. The loadings and dosages of such minerals may be as discussed above for polyhalite. The mineral incorporated in the coating may contain one or more of potassium, calcium or magnesium. The mineral incorporated in the coating may be a hydrated sulphate, particularly a hydrated sulphate of one or more alkali metals or alkali earth metals.
Where numeric values are specified above, they may be average values over the seeds in a coated seed product.
The applicant hereby discloses in isolation each individual feature described herein and any combination of two or more such features, to the extent that such features or combinations are capable of being carried out based on the present specification as a whole in the light of the common general knowledge of a person skilled in the art, irrespective of whether such features or combinations of features solve any problems disclosed herein, and without limitation to the scope of the claims. The applicant indicates that aspects of the present invention may consist of any such individual feature or combination of features. In view of the foregoing description it will be evident to a person skilled in the art that various modifications may be made within the scope of the invention.
Number | Date | Country | Kind |
---|---|---|---|
1409799.2 | Jun 2014 | GB | national |
1410115.8 | Jun 2014 | GB | national |
Filing Document | Filing Date | Country | Kind |
---|---|---|---|
PCT/GB2015/051591 | 6/1/2015 | WO | 00 |
Publishing Document | Publishing Date | Country | Kind |
---|---|---|---|
WO2015/185906 | 12/10/2015 | WO | A |
Number | Name | Date | Kind |
---|---|---|---|
4251952 | Porter | Feb 1981 | A |
5188654 | Manalastas | Feb 1993 | A |
5435821 | Duvdevani et al. | Jul 1995 | A |
5623781 | Legro | Apr 1997 | A |
5994265 | Barclay et al. | Nov 1999 | A |
6156699 | Johnson et al. | Dec 2000 | A |
6582637 | Phinney | Jun 2003 | B1 |
20010042494 | Welshimer et al. | Nov 2001 | A1 |
20030022790 | Hero | Jan 2003 | A1 |
20030135957 | Phinney | Jul 2003 | A1 |
20040152596 | Peltonen | Aug 2004 | A1 |
20060010946 | Mayhew et al. | Jan 2006 | A1 |
20120220454 | Chen | Aug 2012 | A1 |
Number | Date | Country |
---|---|---|
1246283 | Mar 2000 | CN |
1437852 | Aug 2003 | CN |
101503322 | Mar 2012 | CN |
3618058 | Feb 1987 | DE |
102006034621 | Jan 2008 | DE |
2392204 | Dec 2011 | EP |
2612812 | Sep 1988 | FR |
983920 | Feb 1965 | GB |
1465979 | Mar 1977 | GB |
S5269711 | Jun 1977 | JP |
S54130311 | Oct 1979 | JP |
S6170906 | Apr 1986 | JP |
H0458805 | Feb 1992 | JP |
925869 | May 1982 | SU |
1456395 | Feb 1989 | SU |
WO-2004046064 | Jun 2004 | WO |
WO-2014026048 | Feb 2014 | WO |
Entry |
---|
Database Biosis (Online) Biosciences Information Service, Philadelphia, PA, US; 1991, Barbarick K A: “Polyhalite Application to Sorghum-Sudangrass and Leaching in Soil Columns”, Soil Science, vol. 151, No. 2, 1991, pp. 159-166. |
International Search Report Issued in PCT/GB2015/051592 dated Sep. 16, 2015. |
Search Report Issued in GB1409799.2 dated Dec. 19, 2014. |
Search Report Issued in GB1410115.8 dated Oct. 4, 2014. |
International Search Report issued in International Patent Application No. PCT/GB2015/051591, dated Sep. 16, 2015 (Sep. 16, 2015). 5 pages. |
Number | Date | Country | |
---|---|---|---|
20170121233 A1 | May 2017 | US |