Self-assembled calixarene-based guest-host assemblies for guest storage by van der waals confinement

Abstract

A guest-host assembly having a generally spheroidal host assembly formed of trimers of calixarene molecules in a hexagonal close-packed assembly and its preparation. The calixarene trimers are associated together predominantly by van der Waals forces to provide dilated channels having void volumes within the range of 100-200 Å3. A guest component, such as hydrogen, methane, or another hydrocarbon or halocarbon, is encapsulated within the dilated channels of the spheroidal host assembly and retained within the channels primarily by van der Waals forces. The guest-host assembly is stable at a temperature of 150° C. or higher. The temperature at which the onset of the release of the guest component occurs is within the range of 150-300° C.

Description

FIELD OF THE INVENTION

[0001] This invention relates to generally spheroidal host assemblies formed of trimers of calixarene molecules and the preparation of such assemblies and their use in confining guest components through van der Waals forces.

BACKGROUND OF THE INVENTION

[0002] Various calixarene-type compounds and self-assembled and spherical hexamers of calixarene derivatives have been proposed for various applications. For example, MacGillivray and Atwood in a paper entitled “A Chiral Spherical Molecular Assembly Held Together by 60 Hydrogen Bonds,” Nature, Vol. 389, pp. 469-472, October 1997, disclose a self-assembly mechanism for methylcalix[4]resorcinarenes self-assembled as a spherical hexamer along with adventitious water molecules. MacGillivray et al disclose the use of methylene-bridged resorcinarenes to form hexameric superstructures. MacGillivray makes reference to exploring various applications including a chiral catalyst for chemical transformations, a micro-vesicle for drug delivery, and an intermediate for separation problems.

[0003] Subsequent to the MacGillivray/Atwood paper, Gerkensmeier et al in a paper entitled “Self-Assembly of 2,8,14,20-Tetraisobutyl-5,11,17,23-tetrahydroxyresorc[4]arene,” European Journal of Organic Chemistry, 1999, pp. 2257-2262, discuss self-assembling systems based upon hydroxyresorcinarenes generated by the acid catalyzed condensation of 2-hydroxyresorcinol (pyrogallol) with aldehydes in polar media. Here, the self-assembly products were characterized as two-dimensional polymeric structures held together by hydrogen bonds. The Gerkensmeier et al paper does, however, report on the preparation of a spherical hexamer having an enclosed interior space populated by ten solvent molecules. However, attempts to replicate this hexamer structure were unsuccessful, and the structure was characterized by Gerkensmeier et al as being very fragile due to its being stabilized by weak hydrogen bonds.

[0004] The self-assembled host structures arrived-at through procedures, such as described in MacGillivray/Atwood and Gerkensmeier et al papers, are in the form of molecular structures which are maintained through chemical bonding such as covalent bonding or hydrogen bonding. Thus, as described in the MacGillivray/Atwood paper, the calixarene-based hexamers are sustained through intermolecular bonding formed predominantly through hydrogen bonds involving the adventitious water molecules.

SUMMARY OF THE INVENTION

[0005] In accordance with the present invention, there is provided a composition of matter comprising a guest-host assembly having a generally spheroidal host assembly formed of trimers of calixarene molecules in a hexagonal close-packed assembly. The calixarene trimers are associated together predominantly by van der Waals forces to provide dilated channels having void volumes within the range of 100-200 Å3. A guest component is encapsulated within the restricted channels of the spheroidal host assembly and retained within the channels primarily by van der Waals forces. The guest-host assembly is stable at a temperature of 150° C. (or higher). Preferably, the guest-host assembly is stable under conditions to provide a temperature at which the onset of the release of the guest component occurs within the range of 150-300° C.

[0006] In a preferred embodiment of the invention, the guest component is selected from the group consisting of hydrogen, methane, and hydrocarbons having molecular weight within the range of 2-520.

[0007] In a further embodiment of the invention, there is provided a method of forming a guest-host assembly which can be employed to release a guest component for a suitable use, such as for a fuel and a utilization process. In carrying out this embodiment of the invention, there is provided a generally spheroidal assembly formed of trimers of calixarene molecules in a hexagonal close-packed assembly of the trimers associated together predominantly by van der Waals forces. The assembly provides dilated channels having void volumes within the range of 100-200 Å3. A guest component is infused into the dilated channels of the host assembly to provide a guest-host assembly in which the guest component is retained in the assembly predominantly by van der Waals forces. Preferably, the guest-host assembly of the infused guest component is stable at a temperature of at least 150° C. When it is desired to utilize the guest component, the guest-host assembly is heated to a temperature sufficient to destabilize the guest-host assembly and release the guest molecules. Preferably, the onset temperature of the release of the guest component is at least 150° C. and preferably within the range of 150-300° C.

[0008] The host assembly of molecules can then be reutilized by cooling the host assembly molecules and reassembling them to form a generally spheroidal assembly formed of trimers of the calixarene molecules in a hexagonal close-packed assembly associated predominantly by van der Waals forces to provide dilated channels having void volumes within the range of 100-200 Å3. A guest component can then again be infused into the dilated channels of the guest-host assembly to provide a guest-host assembly in which the guest component is retained in the assembly predominantly by van der Waals forces and is stable to a temperature of at least 150° C.

BRIEF DESCRIPTION OF THE DRAWINGS

[0009] FIG. 1 is a schematic illustration of three calixarene molecules in a trimer arrangement.

[0010] FIG. 2 is a space-filling representation of the cyclic trimer viewed along a threefold axis.

[0011] FIG. 3 is a representation of the cyclic trimer of FIG. 2 viewed perpendicular to the axis of FIG. 2.

[0012] FIG. 4 is a space-filling representation of a spheroidal guest-host assembly.

DETAILED DESCRIPTION OF THE INVENTION

[0013] The present invention involves an organic supramolecular framework that contains large, unoccupied lattice voids which are stabilized predominately by van der Waals interactions. The lattice voids of these framework systems are utilized to entrap and retain highly volatile gases. This can be accomplished indefinitely at high temperatures even under vacuum. The supramolecular assemblies involved in the present invention are based upon assemblies of calixarenes or derivatives of calixarenes. The preferred application of the invention involves the use of calix[4]arene; however, other calixarenes, such as calix[6]arene and calix[8]arene, can be employed in carrying out the invention. Derivatives of such calixarenes can be employed to achieve the closely-packed spheroidal assemblies involved in the present invention. However, contrary to functionalized calixarenes, such as resorcinarenes, the calixarenes employed in the present invention are assembled predominantly by van der Waals forces as opposed to strong chemical bonding, such as may be achieved through the use of functional substituents on the aromatic nuclei. The invention will be described in detail with regard to the use of calix[4]arene to form hexagonal close-packed assemblies for the inclusion of low molecular weight guest moieties.

[0014] The calixarenes comprise an extensively studied class of macrocyclic polyphenolic compounds that are usually strongly associated with host/guest inclusion chemistry. The simplest representative of this family of compounds is calix[4]arene, which forms from four methylene-bridged phenyl groups, as indicated by the following structural formula: 1

[0015] Calix[4]arene provides a bowl-shaped molecule with a shallow cleft and a rigid cone conformation which is stabilized by a cyclic array of hydrogen bonds between adjacent phenolic OH groups at the lower rim. As indicated by the experimental work described below respecting calix[4]arene, its crystalline inclusion compounds exhibit particularly unusual structural characteristics, in addition to extraordinary thermal stability.

[0016] While the calixarene compounds employed in carrying out the present invention will normally be fully aromatized, as indicated by the Structure (1), one or more of the aryl groups may be hydrogenated. For example, a calixarene suitable for use in carrying out the present invention would include cyclohexylcalixarene in which one aromatic group has been hydrogenated to form a cyclohexyl group, as indicated by the following structural formula. 2

[0017] In addition, the bridge groups formed by the methylene bridges can be replaced by other bridged structures which are sterically similar to the methylene bridges. For example, sulfur bridges can be provided in lieu of the carbon bridges, as indicated by the thiacalixarene shown by the following structural formula. 3

[0018] Other suitable bridging agents would include silanyl groups in which the methylene groups are replaced with silanyl, —SiH2—. As will be recognized by those skilled in the art, such calixarene derivatives bear a very close stearic configuration to the normally encountered calixarenes. Such compounds may also incorporate hydrogenated aromatic groups, similarly as shown by the cyclohexyl-calix[4]arene of Formula (2).

[0019] The embodiment of the invention carried out involving calix[4]arene will be described with reference to the fully aromatized methylene-bridged calix[4]arene depicted by Formula (1). However, it will be recognized that such description is also applicable to the use of calix[4]arene involving hydrogenated aryl groups, as depicted by Formula (2), or by calix[4]arenes formed with bridges other than methylene bridges, such as depicted by Formula (3)

[0020] Calix[4]arene is soluble in a variety of aromatic and aliphatic solvents. The structure of an acetone solvate, resulting from evaporation of a solution of calix[4]arene in acetone, is characterized as a 1:1 host/guest complex with each acetone guest molecule inserting one of its methyl groups into a calixarene cavity. When exposed to air, the crystalline material decomposes readily as ⅔ of the acetone is released in vapor form, with concomitant rearrangement of the host lattice and the remaining acetone guest. Desolvation results in powdering of the crystals, and even mild heating at 50° C. accelerates the process considerably.

[0021] Diffraction-quality single crystals of pure calix[4]arene were grown by sublimation at 300° C. under reduced pressure (2 torr), and the guest-free structure was elucidated. Comparison of the calculated powder diffraction (XRD) pattern of the sublimed phase with that obtained experimentally for the ⅔ desolvated acetone phase confirms that the two structures are isomorphous. Pure calix[4]arene crystallizes in the hexagonal space group P63/m: As shown in the schematic three-dimensional representation of FIG. 1, three calixarene molecules, 2, 3, and 4, adopt a cyclic, mutually included arrangement in the form of a trimer. The trimer thus formed is approximately spherical in shape and the extended structure is a hexagonal close-packed assembly of trimers. No intermolecular hydrogen bonds are present in the structure and the trimer appears to be held together predominantly, and perhaps solely, by the relatively weak van der Waals interactions.

[0022] FIG. 2 illustrates a space-filling representation of the cyclic trimer of calix[4]arene illustrated schematically in FIG. 1. Here, the space-filling representation is viewed along the threefold axis. The generally spherical configuration illustrated by reference numeral 6 has a radius of about 7.3 Å. The calix[4]arene moieties are indicated generally by carbon atoms indicated by spheres 8 and hydrogen atoms indicated generally by lightly colored smaller spheres indicated by reference numeral 9.

[0023] FIG. 3 illustrates a space-filling representation of the cyclic trimeric arrangement of calixarenes viewed perpendicular to the threefold axis. Carbon and hydrogen atoms are again indicated generally by the spheroids 8 and 9, respectively

[0024] An ideal hexagonal close-packed (hcp) lattice of spherical entities contains a three-dimensional network of parallel and oblique channels (with respect to the crystallographic c axis)that link interstitial voids. Two types of channels that run parallel to [001] can be identified. One type of channels, characterized as type a channels, are continuous and link voids that are rounded by a trigonal antiprismatic arrangement of six spheres. Another type of channels, type b channels, is not continuous and is surrounded by five spheres in a trigonal bipyramidal environment. The structure of the hexagonal close-packed assembly of this invention deviates from ideal spherical geometry such that minor protrusions and indentations manifest themselves, as shown in FIGS. 2 and 3. These undulations result in substantial dilation of the type b channels to yield “solvent accessible” voids of about 153 Å3. Furthermore, constriction of the oblique and type a channels ensures that the bulk structure is non-porous. The hexagonal close-packed (hcp) assembly arrangement of trimers, as described above, also obtains in the dichloromethane, chloroform, and acetonitrile solvates. In all three cases, the guest is situated in the interstitial void and is intricately disordered as a result of its loose fit and the presence of high crystallographic site symmetry.

[0025] In order to probe the cavity size, crystals of the CCl4 solvate were prepared by slow evaporation of a solution of calix[4]arene in CCl4. Again we observe the hexagonal close-packed host framework, but in this case the more symmetrical CCl4 solvent is not disordered and therefore easily modeled. The guest is trapped in the interstitial lattice cavity and makes only van der Waals contact with the host. An investigation was undertaken of the thermal stability of the hexagonal close-packed assembly inclusion compounds of calix[4]arene relative to that of its pure phase. Thermogravimetric analysis (TGA) of the CCl4 solvate shows that the inclusion compound is stable up to 200° C. This temperature marks the onset temperature of guest release (Ton) (the weight loss recorded between 200 and 250° C. corresponds to a 1:1 complex of trimers and CCl4).

[0026] The parameter (Ton−Tb) has been shown to be a reliable measure of the relative thermal stability of host-guest systems, where Tb is the normal boiling point of the guest. The thermal stability of the hexagonal close-packed host lattice is remarkably high, despite the presence of a relatively volatile guest (Ton−Tb for trimers·CCl4=120° C.). In view of these findings, experimental work was undertaken to assess the ability of the host lattice to stabilize increasingly volatile guests that are structurally related to CCl4. The possibility thus presents itself of entrapping a range of highly volatile freon and halon compounds in the interstitial cavity which results from the hexagonal close-packed assembly. Several such host-guest compounds were prepared as single crystals, and pertinent parameters are given in Table 1. All of these crystals exhibited remarkable thermal stability as determined by TGA.

TABLE 1
Inclusion compounds of calix[4]arene with selected guest compounds,
guest boiling points (b.p.) and hexagonal unit cell parameters.
No.	Complex host	guest b.p./° C.	a/Å	c/Å
—	†	—	14.344	18.627
3	1-CCl4	76.8	14.592	18.386
4	1-CHCl3	61.2	14.697	17.953
5	1-CH2C12	39.8	14.69	17.99
6	1-CFCl3	23.7	14.636	18.245
7	1-CF2ClBr	−4	14.643	18.235
8	1-CF3CH2F	−15	14.640	18.220
9	1-CF3Br	−57.7	14.487	18.227
10	1-C2F6	−78.2	14.647	18.195
11	1-CF4	−127.9	14.615	18.284
12	1-(CH4)2	−160	14.599	18.283
†Guest-free calix[4]arene trimer formed from pure calix[4]arene obtained by sublimation at 300° C. under vacuum.

[0027] The very low solubility of calix[4]arene in condensed volatile freons such as CF3Br, C2F6 and CF4 precludes the growth of diffraction quality crystals after the procedure used to obtain the trimer.CCl4 assembly (1.CCl4). However, solvent-free hexagonal close-packed assembly crystals can be precipitated by the addition of propan-2-ol to a solution of calix[4]arene in toluene. A modification of this method involving dissolution of a condensed freon or halon of interest in the toluene can be employed to obtain diffraction-quality single crystals within 30 min. In some cases, satisfactory modeling of the guest within the hexagonal close-packed lattice was hampered by disorder and thermal motion. However, in all cases, microanalysis and solution 19F nuclear magnetic resonance (NMR) confirmed the presence of the halocarbon guest. Host-guest ratios were determined by means of TGA. In the case of the CF3Br inclusion compound, the guest was simply disordered over two positions and easily modeled. CF3Br, positioned in the interstitial cavity of the hexagonal close-packed assembly lattice, is shown in FIG. 4. FIG. 4 is a space-filling representation of a spheroidal guest-host assembly in which the host assembly is formed by five trimers of calix[4]arene with the interstitial void (type b channels) of the host lattice occupied by one molecule of CF3Br, as indicated generally by reference numeral 16. In FIG. 4 one of the five units of the calix[4]arene trimer has been omitted in order to reveal the position of the CF3Br guest within the cavity. The calix[4]arene trimers are indicated by reference numerals 17, 18, 19, and 20.

[0028] The dilated type b channels provided by the hexagonal close-packed host assemblies employed in the present invention provide void volumes within the range of 100-200 Å 3. In preferred applications of the present invention involving relatively volatile guest components, the dilated channels will usually exhibit void volumes within the range of 140-170 cubic Angstroms and, more specifically, within the range of 150-160 Å 3.

[0029] As described below embodiments of the present invention involve confinement of volatile hosts in replenishable vessels or containers. In consideration of applications involving gas confinement (e.g., size-selective separation and storage procedures), it might not be convenient to implement the technique of precipitation from a toluene solution in which the gas of interest is also dissolved. The hcp phase has the structural characteristics of an interstitial solid solution. While the host lattice does not require occupancy of the interstitial void in order to maintain its structural integrity, the presence of suitably sized guest species favors formation of an even more densely packed structure based upon an already stable host framework.

[0030] Since clathration involves a phase transformation of the host lattice in order for the guest to become lodged in the lattice voids, experimental work was carried out involving the previously observed desolvation of the metastable, non-hcp calix[4]arene acetone solvate. Large single crystals of the acetone 1:1 complex were grown, crushed, and placed in a steel pressure vessel. Freon gas was introduced into the vessel, which was then sealed and heated to 50° C. After approximately 12 hours, the crystals were removed and subjected to x-ray diffraction (XRD), NMR, TGA, and microanalysis, which together confirmed the hexagonal structure as well as the near-stoichiometric lattice inclusion of the freon gas. These results show that, in the presence of a suitable guest vapor, even a solid-solid phase transition of the host to the hexagonal close-packed lattice facilitates guest inclusion.

[0031] Further experimental work was carried out to entrap CH4 at room temperature by exposure at 100 atm. for 72 hours. The resulting powder was dissolved in d6-benzene and analyzed by 1H-NMR, which revealed the presence of methane. TGA analysis yielded a weight-loss of 2.43% with Ton within the range of 150-170° C., corresponding to two methane molecules per lattice void. (The calculated CH4 weight loss for 1.(CH4)2 is 2.45%.) Although single crystals containing methane could be obtained from toluene/propan-2-ol under a high pressure of methane, a reasonable model incorporating methane could not be elucidated because of guest disorder.

[0032] The thermal stability for the hexagonal close-packed inclusion compounds is indicated by the following values of Ton−Tb for the guests CF3Br (260° C.), CF4 (370° C.), and.CH4 (320° C.). This remarkable thermal stability of the hexagonal close-packed assembly inclusion compounds is attributed to the host lattice being isomorphous with its pure phase; that is, the host lattice cannot gain much stability by releasing the guest because the initial and final lattices would be identical, even at elevated temperatures. In contrast to the zeolites, the guest cannot easily diffuse through the host lattice since the channels are non-porous.

[0033] A preferred application of the present invention is in the storage of volatile fuels, such as hydrogen and methane. Because of the high temperature stability of the calixarene-based host assemblies, they can advantageously be employed in fuel storage cells for vehicles powered by the combustion of hydrogen or methane as the fuel source. For example, the dilated type b channels as defined, the hexagonal close-packed assembly of calix[4]arenes as described above, are characterized as “dumbbell”-shaped voids with enlarged chambers at each end, interconnected by a reduced diameter channel extending between the chambers. For methane storage, two methane molecules may occupy a dilated channel, one molecule in each of the enlarged chambers. For hydrogen storage, hydrogen molecules may be retained within the end chambers as well as within the reduced diameter channel extending between the chambers. The guest hydrogen or methane molecules are retained within the hexagonal close-packed assembly of the calix[4]arenes predominantly by van der Waals forces as contrasted with strong chemical bonding.

[0034] In this embodiment of the invention, the fuel cell incorporating lattice structure of calixarene molecules in a hexagonal close-packed assembly can be used to retain a volatile fuel component, such as hydrogen, within the void spaces. The fuel cell can be heated by means of either direct or indirect heat exchange using the internal combustion engine, to which the hydrogen fuel is supplied. The hydrogen fuel released through destabilization of the guest-host assembly is then supplied to fuel the internal combustion engine. The fuel cell from which the hydrogen is supplied can be regenerated by cooling the host assembly molecules to reassemble them into the hexagonal close-packed assembly. The fuel cell can then be infused with hydrogen from a suitable source to reestablish the fuel cell in which the hydrogen fuel component is retained as a guest in the guest-host assembly predominantly by van der Waals forces.

[0035] As noted above, host assemblies incorporating calix[4]arene molecules are particularly preferred for fuel cells involving the storage of very low molecular weight volatile fuel components, specifically methane, ethane, and hydrogen, H2. Propane and butane can also be stored in such host assemblies. Further, the invention may be utilized in forming fuel cells suitable for the storage of higher molecular weight but still volatile fuel components, such as propane and butane and higher molecular weight hydrocarbons. In this case, guest-host assemblies based upon somewhat higher molecular weight calixarenes, such as calix[6]arene and calix[8]arene, may be conveniently employed to provide somewhat larger dilated channels to entrap the higher molecular volatile fuels, such as butane and heavier hydrocarbons, as guest components.

[0036] Another application of the invention involves the operation of a replenishable canister for release and subsequent recovery of a volatile component in a consrained environment. For example, the canister can be employed to retain a halon, which is effective as a combustion suppressant. Such an application will involve vehicles, such as space vehicles and the like, having constrained environments which may be susceptible to combustion when a heated source of combustion or potential combustion occurs within the constrained environment. The vessel containing the halon as a guest in a host/guest assembly of calixarene embodying the present invention is heated in order to arrive at a temperature sufficient to destabilize the guest-host assembly and to release the halon or other volatile component. The released component is supplied to the utilization location, such as a source of combustion or potential combustion. The host assembly molecules are then cooled in order to reassemble the molecules to form a hexagonal close-packed assembly of calixarenes, which, as described previously, are associated together predominantly by van der Waals forces. All or part of the halon can be recovered within the enclosed environment by circulating the oxygen-containing atmosphere through a compressor and separator to recover the halon and reintroduce the halon into the canister.

[0037] As noted previously, various host/guest assemblies can be prepared using calix[4]arene and various guest components. The following examples illustrate the preparation of various calixarene-based crystals as including calixarene crystals having guest-free structures as well as calixarene inclusion complexes formed with various guest components.

EXAMPLE 1

Preparation of the Calix[4]arene Crystals of the Guest-free Hexagonal Structure (1)

[0038] Diffraction-quality single crystals of pure calix[4]arene were grown by sublimation. A quantity of 50 mg (0.12 mmol) of calix[4]arene was placed in a pressure test tube attached to a vacuum line. The sample was heated to 300° C. under vacuum of ca. 2 torr, and within 5-6 minutes crystals of the guest-free structure, suitable for X-ray analysis were grown.

[0039] X-ray data were collected at room temperature on a Bruker SMART CCD diffractometer. All non-hydrogen atoms of the host molecules were refined anisotropically. Hydrogen atoms were placed using standard geometric models and with their thermal parameters riding on those of their parent atoms. Hydroxyl hydrogen atoms were located in difference electron density maps and refined with nominal geometric restraints.

[0040] The guest-free structure crystallizes in the hexagonal space group P63/m. Three calixarene molecules adopt a cyclic, mutually included arrangement. The trimer thus formed is approximately spherical in shape and the extended structure is simply a hexagonal close packed (hcp) assembly. No intermolecular hydrogen bonds are present in the structure and the trimer appears to be held together only by the relatively weak forces characterized as van der Waals interactions.

EXAMPLE 2

Preparation of the Non-hcp Calix[4]arene Crystals of the Acetone 1:1 Complex (1a)

[0041] The complex was prepared by slow evaporation of acetone from a saturated solution of calix[4]arene at room temperature. The saturated solution was prepared by successive addition of the solid material, i.e.: calix[4]arene, into 50 mL acetone at reflux temperature (58° C. at 1 atm). Large crystals of the non-hcp 1:1 complex were grown within 2-3 hours by cooling of the saturated solution. The crystals were kept in the mother liquor for further experiments.

[0042] The already reported structure (Cambridge Structural Database, Refcode: DACLUO) itself is of limited interest and is adequately described as a 1:1 host:guest complex with each acetone guest molecule inserting one of its methyl groups into a calix[4]arene cavity.

[0043] Crystals of 1 a are metastable and, when exposed to the atmosphere, crystals of la decompose readily as ⅔ of the acetone is released in vapor form from the crystals (confirmed by TGA), with concomitant rearrangement of the host lattice and the remaining acetone guest. Desolvation results in powdering of the crystals, and even mild heating (50° C.) accelerates the process. The X-ray powder diffraction (XRD) pattern of the material formed during the phase change compared to that of the sublimed phase confirms that the two structures are isomorphous. This would indicate that the ⅔ desolvated powder possesses a hcp structure, as does the sublimed guest-free calix[4]arene.

EXAMPLE 2

Preparation and Examination of the Thermal Stability of the CCl4 1:1 Inclusion Complex with 1 (Where 1 is the hcp Structure)

[0044] 100 mg (0.24 mmol) of calix[4]arene was dissolved in carbon tetrachloride and to facilitate the dissolution the mixture was heated to boiling. X-ray quality crystals were grown by slow evaporation of the solvent within 2 hrs. The crystals exhibit the hcp-host framework, as confirmed by X-ray diffraction analysis, but in this case the more symmetrical CCl4 guest is not disordered, and therefore easily modeled. The guest is trapped in the interstitial lattice cavity and makes only van der Waals contact with the host calix[4]arene trimers.

[0045] In order to test the thermal stability of the hcp inclusion compounds of 1 relative to that of its pure phase, thermogravimetric analysis (TGA) was performed. TGA of the CCl4 guest containing hcp shows that the inclusion compound is stable up to 200° C., the onset (Ton) of guest release. The weight loss recorded between 200 and 250° C. corresponds to a 1:1 complex of CCl4, 1.CCl4. This is in sharp contrast to the decomposition of 1a described above where guest release by the non-hcp structure occurs readily (Ton=50° C.).

EXAMPLE 4

Preparation of the CF3Br 1:1 Inclusion Complex with 1, Method A

[0046] A quantity of 100 mg (0.21 mmol) non-hcp acetone complex, 1a, was placed in a steel pressure vessel. CF3Br gas was introduced into the vessel, which was then sealed and heated to 50° C. After approximately 12 hrs, the crystals were removed and subjected to X-ray diffraction analysis, nuclear magnetic resonance analysis (NMR), TGA and microanalysis, which, together, confirmed the hexagonal structure as well as the near 1:1 stoichiometric lattice of the gas.

EXAMPLE 5

Preparation of the CF3Br 1:1 Inclusion Complex with 1, Method B

[0047] The very low solubility of calix[4]arene in condensed CF3Br precludes the growth of diffraction quality crystals from saturated solutions. However, it had been noted that solvent-free hcp crystals could be precipitated by the addition of propan-2-ol to a solution of 1 in toluene. A modification of this method involving dissolution of condensed CF3Br in toluene under pressure (1-2 atms) affords diffraction-quality single crystals within 30 minutes. The structure was elucidated and showed one molecule of CF3Br in the hcp lattice void. TGA analysis showed [Ton−Tb] for 1·CF3Br=260° C.

EXAMPLE 6

Preparation of the CF4 1:1 Inclusion Complex with 1, Method A

[0048] A quantity of 100 mg (0.21 mmol) non-hcp acetone solvate, la, was placed in a steel pressure vessel. CF4 gas was introduced into the vessel, which was then sealed and heated to 50° C. After approximately 12 hrs, the crystals were removed and subjected to TGA that the almost stoichiometric amount of guest in 1.CF4. TGA further confirmed [Ton−Tb] 1.CF4=370° C.

EXAMPLE 7

Preparation of the CF4 1:1 Inclusion Complex with 1, Method B

[0049] To 1.0 mL saturated solution of calix[4]arene was added a partial drop of propane-2-ol and the mixture was placed in a pressure vessel. CF4 gas was introduced and within 2 hrs single crystals of 1.CF4 were precipitated. The X-ray data were collected at room temperature on a Bruker SMART CCD diffractometer. The structure was solved and refined to prove the location and stoichiometry of the CF4 guest.

EXAMPLE 8

Preparation of the CF2BrCl 1:1 Inclusion Complex with 1, Method A

[0050] A quantity of 100 mg (0.21 mmol) non-hcp acetone solvate, la, was placed in a steel pressure vessel. CF2BrCl gas was introduced into the vessel, which was then sealed and heated to 50° C. After approximately 12 hrs, the crystals were removed and subjected to TGA that confirmed the almost stoichiometric amount of guest in 1.CF2BrCl.

EXAMPLE 9

Preparation of the CF2BrCl 1:1 Inclusion Complex with 1, Method B

[0051] X-ray quality single crystals were grown by precipitation. To 1.0 ml saturated solution of calix[4]arene in toluene was added a drop of propane-2-ol, and the mixture was placed in a pressure vessel. CF2BrCl gas (ca. 2 atm) was introduced and within 1 hr single crystals of 1.CF2BrCl were precipitated. The structure was elucidated, but satisfactory modeling of the guest within the hcp lattice was hampered by disorder. Further NMR investigation unambiguously confirmed the presence of the CF2BrCl and the near stoichiometric lattice inclusion of the gas was determined by TGA.

EXAMPLE 10

Preparation of the CFCl3 1:1 Inclusion Complex with 1, Method A

[0052] A quantity of 100 mg (0.24 mmol) pure calix[4]arene was mixed with liquid CFCl3 (b.p. 25° C., ca. 2 atm) in a pressure test tube. The closed tube was heated to 100° C., at which temperature all the solid was dissolved in solvent. The homogeneous solution was cooled down and the precipitated crystals were subjected to X-ray diffraction analysis that confirmed the presence of the guest and thermogravimetric analysis showed that all the hcp lattice voids were occupied by guest molecules.

EXAMPLE 11

Preparation of the CF3CH2F 1:1 Inclusion Complex with 1 (the Inclusion Complex with Office Duster)

[0053] To 1.0 mL toluene was added enough calix[4]arene to produce a saturated solution. Then the mixture was heated to 100° C. to facilitate the dissolution of the solid material. The addition of the calix[4]arene and the heating-cooling cycle were repeated until the room temperature solution becomes saturated. To this solution one drop of condensed CF3CH2F (office duster, b.p. −15° C.) was added, and single crystals were grown within 15-20 minutes. The crystals were subjected to X-ray diffraction analysis that confirmed the presence of the guest and thermogravimetric analysis showed that all the hcp lattice voids were occupied by guest molecules.

EXAMPLE 12

Preparation of the CH4 2:1 Inclusion Complex with 1

[0054] A quantity of 500 mg (1.04 mmol) non-hcp calix[4]arene:acetone complex was placed in a pressure vessel, and then methane gas was introduced. The conversion of the metastable phase to the hexagonal structure takes 72 hrs at room temperature and 1500 psi (100 atm). The resulting powder was dissolved in d6-benzene and analyzed by 1H NMR, which unequivocally revealed the presence of methane (0.15 ppm). TGA analysis yielded a weight-loss of 2.43% with Ton=150-170° C. ([Ton−Tb]=370° C.) corresponding to two methane molecules per lattice void (calculated CH4 weight loss for 1.(CH4)2=2.45%). Single crystals containing methane were obtained from toluene/propan-2-ol under a high pressure of methane, and methane was shown to be present as a disordered guest.

EXAMPLE 13

Preparation of the H2 10:1 Inclusion Complex with 1

[0055] Theoretical calculations show that there can be 9-10 hydrogen molecules per void in the above hexagonal crystal lattice. The methane protocol was carried out to encapsulate hydrogen in the solid. A quantity of 500 mg (1.04 mmol) non-hcp calix[4]arene:acetone complex was placed in a pressure vessel, and hydrogen gas was introduced. After 72 hrs, at 80 atm and room temperature, TGA analysis showed conversion to the H2 inclusion complex with ca. (H2)10.1.

[0056] Having described specific embodiments of the present invention, it will be understood that modifications thereof may be suggested to those skilled in the art, and it is intended to cover all such modifications as fall within the scope of the appended claims.

Claims

1. A composition of matter comprising a stable guest-host assembly having: (a) a generally spheroidal host assembly formed of trimers of calixarene molecules in a hexagonal close-packed assembly of said trimers associated together predominantly by van der Waals forces to provide at least one dilated channel having a void volume within the range of 100-200 Å3; (b) a guest component encapsulated within said at least one dilated channel of said spheroidal host assembly and retaining within said channel predominantly by van der Waals forces; and (c) said guest-host assembly being stable at a temperature of at least 150° C.

2. The composition of claim 1, having a thermal stability, K, within the range of 70°-460° C., as defined by:

3. The composition of claim 1 wherein said calixarene molecules are selected from the group consisting of calix[4]arenes, calix[6]arenes, and calix[8]arenes and mixtures thereof.

4. The composition of claim 3 wherein said guest component is selected from the group consisting of normally gaseous hydrocarbons, halocarbons having boiling points within the range of −252° to 10° C.

5. The composition of claim 1 wherein said calixarene molecules comprise calix[4]arene, cyclohexyl-calix[4]arene, and thiacalix[4]arene molecules.

6. The composition of claim 5 wherein said guest component is selected from the group consisting of methane, hydrogen, carbon tetrachloride, fluorocarbons, bromofluorocarbons, iodofluorocarbons, bromochlorofluorocarbons, iodochlorofluorocarbons, iodocarbons, and chlorofluorocarbons having boiling points within the range of −252° C. to 190° C.

7. The composition of claim 6 wherein said guest component is selected from the group consisting of hydrogen, methane, and ethane.

8. The composition of claim 1 wherein said guest component is hydrogen.

9. The composition of claim 7 wherein said guest component is methane.

10. The composition of claim 1 wherein said guest/host assembly is stable at a temperature of at least 200° C.

11. A method of forming a guest-host assembly and releasing a guest component from said guest-host assembly, comprising: (a) providing a spheroidal guest-host assembly having a host component formed of trimers of calixarene molecules in a hexagonal close-packed assembly of said trimers associated together predominantly by van der Waals forces to provide at least one dilated channel having a void volume within the range of 100-200 Å3 and having a guest component encapsulated within said at least one dilated channel of said spheroidal host assembly and retaining within said channel predominantly by van der Waals forces, said guest-host assembly being stable at a temperature of at least 150° C. (b) heating said guest-host assembly to a temperature in excess of 150° C., which is sufficient to destabilize said guest-host assembly and release the guest molecules; (c) cooling said host assembly molecules and reassembling said molecules to form a generally spherical assembly formed of trimers of said calixarene molecules in a hexagonal close-packed assembly of said trimers associated together predominantly by van der Waals forces to provide at least one dilated channel having a void volume within the range of 100-200 Å3; and (d) infusing a guest component in the dilated channel of said host assembly to provide a guest-host assembly in which said guest component is retained in said assembly predominantly by van der Waals forces and is stable at a temperature of at least 150° C.

12. The method of claim 11 wherein said guest/host assembly is stable at a temperature of at least 200° C.

13. The method of claim 12 wherein said calixarene molecules comprise calix[4]arene molecules.

14. The method of claim 13 wherein said guest component is selected from the group consisting of hydrogen, methane, and ethane.

15. A method of forming a guest-host assembly and releasing a guest component from said guest-host assembly, comprising: (a) providing a generally spherical host assembly formed of trimers of calixarene molecules in a hexagonal close-packed assembly of said trimers associated together predominantly by van der Waals forces to provide at least one dilated channel having a void volume within the range of 100-200 Å3; (b) infusing a guest component into the dilated channel of said host assembly to provide a guest-host assembly in which said guest component is retained in said assembly predominantly by van der Waals forces and is stable at a temperature of at least 150° C.; and (c) heating said guest-host assembly to a temperature in excess of 150° C., which is above the boiling point of said guest component and is sufficient to destabilize said guest-host assembly and release the molecules of said guest component.

16. The method of claim 15 wherein said generally spherical host assembly is formed of trimers of calix[4]arene molecules.

17. The method of claim 16 wherein said assembly of calix[4]arene molecules comprise dilated channels having void volumes within the range of 140-170 Å3.

18. The method of claim 16 wherein said guest/host assembly is stable at a temperature in excess of 200° C.

19. The method of claim 16 wherein said guest component is selected from the group consisting of hydrogen, methane, and ethane.

20. A method of forming a guest-host assembly and releasing a guest component from said guest-host assembly, comprising: (a) providing a generally spherical host assembly formed of trimers of calixarene molecules in a hexagonal close-packed assembly of said trimers associated together predominantly by van der Waals forces to provide at least one dilated channel having a void volume within the range of 80-180 Å 3; (b) infusing a guest component into the dilated channel of said host assembly to provide a guest-host assembly in which said guest component is retained in said assembly predominantly by van der Waals forces and is stable at a temperature of at least 200° C.; (c) heating said guest-host assembly to a temperature in excess of 200° C., which is sufficient to destabilize said guest-host assembly and release the molecules of said guest component; (d) cooling said host assembly molecules and reassembling said molecules to form a generally spherical assembly formed of trimers of said calixarene molecules in a hexagonal close-packed assembly of said trimers associated together predominantly by van der Waals forces to provide at least one dilated channel having a void volume within the range of 100-200 Å3; and (e) infusing a guest component in the dilated channel of said host assembly to provide a guest-host assembly in which said guest component is retained in said assembly predominantly by van der Waals forces and is stable at a temperature of at least 200° C.

21. The method of claim 20 wherein said calixarene molecules comprise calix[4]arene molecules.

22. The method of claim 21 wherein said guest/host assembly has a thermal stability, K, within the range of 70°-460° C., as defined by:

23. The method of claim 21 wherein said guest component is selected from the group consisting of hydrogen, methane, and ethane.

24. A method of operating a replenishable fuel cell comprising: (a) providing a vessel containing a solid fuel cell structure having a lattice structure of molecular crystals having lattice voids and incorporating calixarene molecules in a hexagonal close-packed assembly of trimers of said calixarene molecules associated together predominantly by van der Waals forces to provide a host assembly having interstitial voids capable of sustaining a guest component within said voids predominantly by van der Waals forces and being stable at a temperature substantially in excess of ambient temperature conditions; (b) retaining a volatile fuel component which is normally gaseous at ambient temperature conditions within the interstitial voids of said lattice structure predominantly by van der Waals forces to provide a guest/host assembly of said lattice structure and said volatile fuel component; (c) heating said fuel cell to heat said hexagonal close-packed assembly of said calixarene molecules to a temperature sufficient to destabilize said guest/host assembly and disassembling said calixarene molecules to release said fuel component; (d) supplying said released fuel component to an internal combustion engine; (e) cooling said host assembly molecules to reassemble said molecules to form a hexagonal close-packed assembly of trimers of said calixarene molecules associated together predominantly by van der Waals forces to provide a fuel cell lattice structure as set forth in subparagraph (a) which is stable at a temperature substantially in excess of ambient temperature; and (f) infusing a volatile fuel component as recited in subparagraph (b) to said fuel cell lattice structure to reestablish said fuel cell in which said fuel component is retained as a guest in said assembly predominantly by van der Waals forces.

25. The method of claim 24 wherein said volatile fuel component is selected from the group consisting of hydrogen and at least one C1-C4 hydrocarbon.

26. The method of claim 24 wherein said volatile fuel component is selected from the group consisting of hydrogen and methane.

27. The method of claim 26 wherein said calixarene is calix[4]arene.

28. A method of operating a replenishable canister for release and recovery of a volatile component in a constrained environment comprising: (a) providing a vessel containing a solid structure having a lattice structure of molecular crystals having lattice voids and incorporating calixarene molecules in a hexagonal close-packed assembly of trimers of said calixarene molecules associated together predominantly by van der Waals forces to provide a host assembly having interstitial voids capable of sustaining a guest component within said voids predominantly by van der Waals forces and being stable at a temperature substantially in excess of the normal ambient temperature conditions of said constrained environment; (b) retaining a volatile component which is normally gaseous at said ambient temperature conditions within the interstitial voids of said lattice structure predominantly by van der Waals forces to provide a guest/host assembly of said lattice structure and said volatile component; (c) heating said vessel to heat said hexagonal close-packed assembly of said calixarene molecules to a temperature sufficient to destabilize said guest/host assembly and disassembling said calixarene molecules to release said volatile component; (d) supplying said released volatile component to utilization location within said constrained environment; (e) cooling said host assembly molecules to reassemble said molecules to form a hexagonal close-packed assembly of trimers of said calixarene molecules associated together predominantly by van der Waals forces to provide a lattice structure as set forth in subparagraph (a) which is stable at a temperature substantially in excess of said normal ambient temperature conditions; and (f) recovering at least a portion of said volatile component from said utilization location and transferring said recovered volatile component to said canister to infuse said recovered volatile component to reestablish said volatile component in a guest/host assembly to reestablish said canister containing said recovered volatile component in which said volatile component is retained as a guest in said assembly predominantly by van der Waals forces.

29. The method of claim 28 wherein said utilization location is a heated source of combustion or potential combustion within said constrained environment and said volatile component is a halon effective to suppress combustion at said location within said constrained environment.