SELF-BINDING SUSPENSIONS COMPRISING TITANIUM DIOXIDE AND ZINC OXIDE NANOPARTICLES AND COATED SUBSTRATES PREPARED USING SELF-BINDING SUSPENSIONS

Information

  • Patent Application
  • 20230023077
  • Publication Number
    20230023077
  • Date Filed
    January 10, 2020
    4 years ago
  • Date Published
    January 26, 2023
    a year ago
  • Inventors
    • ARAMPATZIS; Ioannis
  • Original Assignees
    • NanoPhos SA
Abstract
Provided are self-binding suspensions and coated substrates prepared using self-binding suspensions. Also provided are methods of preparing self-binding suspensions. Methods may include preparing a binder solution; preparing a titanium dioxide-zinc oxide suspension using ultrasonication; mixing the binder solution with the titanium dioxide-zinc oxide suspension and a surfactant to form a self-binding suspension composition; and coating a glass substrate with the self-binding suspension composition to form a coated glass substrate.
Description
FIELD OF THE INVENTION

This disclosure relates to self-binding suspensions for preparing transparent photocatalytic thin films. Specifically, this disclosure relates to self-binding suspensions comprising titanium dioxide, zinc oxide, and silicon dioxide nanoparticles for enhanced photocatalytic activity.


BACKGROUND OF THE INVENTION

Transparent coatings with anti-fogging, anti-reflective, photocatalytic and self-cleaning properties may be used in products such as windshields, lenses, or solar energy devices. Particularly for solar energy devices, the transparent coatings should meet certain requirements including: enhance the light collection yield; prevent the aging process of the substrate; and minimize maintenance costs. Additionally, coatings or thin inorganic films developed for the surface of solar energy devices should be permanent and have a minimum lifetime of five years.


Conventional nanocomposite formulations and thin films coatings include TiO2 nanoparticles, SiO2 nanoparticles, and/or hydrolyzed silanes for hydrophilicity and/or improved adhesion. TiO2 nanocrystallites exist in three distinct crystal phases: anatase, brookite and rutile. Of these three phases, anatase is generally preferred for photocatalytic activity because of its energy gap in the range of 3.23 eV (n-type semiconductor). When the photoactive titanium dioxide nanoparticles are irradiated by ultraviolet light (i.e., light having a wavelength below 390 nm), electrons from the electron-filled valence band are transferred to the vacant conduction band and subsequently leave positive-charged holes in the valence band. This photo-generated charge separation is responsible for photoreduction and photooxidation of different target compounds surrounding the semiconductor particles.


Conventional methods of improving photocatalytic activity of TiO2 include doping. Doping may be achieved with the addition of dyes, transition metals (e.g., Cr, Zr, Mn), non-metals (e.g., N, S, C), and/or semiconductors (e.g., SiO2, SnO2, ZrO2, ZnO). Furthermore, doping crystal phases of titanium dioxide nanocrystallites can result in better photocatalytic performance and enhance photon capture for solar applications, due to the higher refractive index of rutile vs. anatase (2,488 for anatase and 2,609 for rutile).


BRIEF SUMMARY OF INVENTION

Provided herein are self-binding suspensions, coated substrates prepared using self-binding suspensions, and methods of preparing self-binding suspensions. Self-binding suspensions provided herein may be prepared using ultrasonication and may bind to a substrate without the application of heat. Films produced using the disclosed suspensions may be used to produce windshields, lenses, solar energy devices, and the like.


Self-binding suspensions provided herein can be used to prepare high-quality thin films. For example, thin films used in solar light applications may be transparent in the visible or near-infrared spectrum. If these thin films are not transparent, they could interfere with the light supplied to the solar energy converter. Further, such films should be able to retain their initial properties (e.g., photocatalytic activity, anti-reflective activity) for a minimum of five years under variable weather conditions and exhibit suitable adhesion to the substrate.


Thus, suspensions provided herein incorporate monodispersed nanoparticles comprising agglomerates not exceeding 200 nm to improve the transparency of the thin films produced from the provided suspensions and minimize the scattering of the visible light. Further, the binary system of titanium dioxide with zinc oxide can provide synergistic effects and performance (e.g., photocatalytic reaction rate, overall refraction) that cannot be achieved when either of the titanium dioxide or zinc oxide nanocrystalline particles are present alone. In particular, the binary system of TiO2—ZnO shows improved photocatalytic activity compared to pure TiO2. When the two photoactive oxides (i.e., titanium dioxide and zinc oxide) are combined, a material having improved photocatalytic activity is generated. This is because the valence semiconductor band and the conduction semiconductor band positions of each of the independent nanoparticles are close to each other and tend to overlap (0.30 eV for valance band and 2.94 eV for conduction band for titanium dioxide and 0.32 eV for valance band and 2.88 eV for conduction band for zinc oxide). Therefore, the interaction of semiconductors with close valence/conduction band positions results in more effective photocatalytic performance, as a) electron hopping is easier when intermediate bands are present and b) charge separation is more effective, i.e. positive holes and negative electron recombination rate is significantly reduced.


Additionally, suspensions disclosed can readily adhere to porous or non-porous substrates due to the presence of a binder that acts as an adhesion promotor (e.g., silicon dioxide). Further, doping with zinc oxide in particular may be used for its high chemical stability, high refractive index, high thermal conductivity, antibacterial properties, UV-protection and non-toxicity.


In some embodiments, provided is a self-binding suspension composition, the composition comprising: 0.0001 to 0.25 wt. % titanium dioxide nanoparticles; 0.00001 to 0.5 wt. % zinc oxide nanoparticles; 4 to 7 wt. % alkoxysilane; 0.000025 to 0.00125 wt. % salt; 0.0002 to 0.01 wt. % dispersant; 0.2 to 0.8 wt. % surfactant; 7 to 12 wt. % alcohol; 0.1 to 0.2 wt. % basic solution; and 80 to 90 wt. % solvent.


In some embodiments of the composition, the salt comprises at least one of Na4P2O7, sodium hydroxide, or sodium chloride.


In some embodiments of the composition, the alcohol comprises at least one of methanol or ethanol.


In some embodiments of the composition, the solvent comprises deionized water.


In some embodiments of the composition, the titanium dioxide nanoparticles are formed from applying ultrasonication to titanium dioxide powder.


In some embodiments of the composition, the zinc oxide nanoparticles are formed from applying ultrasonication to zinc oxide powder.


In some embodiments, a coated glass substrate is provided, the coated glass substrate comprising: a glass substrate; and a thin-film coating on the glass substrate, the thin-film coating comprising: 0.001 to 5 wt. % titanium dioxide powder; 0.0001 to 10 wt. % zinc oxide powder; 20 to 35 wt. % alkoxysilane; 0.00025 to 0.026 wt. % salt; 0.002 to 0.2 wt. % dispersant; 1 to 8 wt. % surfactant; 35 to 60 wt. % alcohol; and 0.5 to 4 wt. % basic solution.


In some embodiments of the coated glass substrate, the salt comprises at least one of Na4P2O7, sodium hydroxide, or sodium chloride.


In some embodiments of the coated glass substrate, the alcohol comprises at least one of methanol or ethanol.


In some embodiments of the coated glass substrate, the solvent comprises deionized water.


In some embodiments of the coated glass substrate, 0.01 to 0.03 L/m2 of a self-binding suspension composition is applied to the glass substrate to form the coated glass substrate.


In some embodiments of the coated glass substrate, the coated glass substrate comprises a windshield, a lens, or a solar energy device.


In some embodiments, a method of producing a coated glass substrate is provided, the method comprising: preparing a binder solution; preparing a titanium dioxide-zinc oxide suspension; mixing the binder solution with the titanium dioxide-zinc oxide suspension and a surfactant to form a self-binding suspension composition; and depositing the self-binding suspension onto a glass substrate to form a coated glass substrate.


In some embodiments of the method, preparing a binder solution comprises mixing alkoxysilane, an alcohol, a Lewis base, and a first solvent.


In some embodiments of the method, preparing a titanium dioxide-zinc oxide suspension comprises ultrasonifying a salt, a dispersant, titanium dioxide powder, zinc oxide powder, and a second solvent.


In some embodiments of the method, the coated glass substrate comprises a windshield, a lens, or a solar energy device.


In some embodiments of the method, the salt comprises at least one of Na4P2O7, sodium hydroxide, or sodium chloride.


In some embodiments of the method, the alcohol comprises at least one of methanol or ethanol.


In some embodiments of the method, the first solvent and the second solvent comprise deionized water.


In some embodiments of the method, depositing the self-binding suspension onto a glass substrate comprises depositing 0.01 to 0.03 L/m2 of the self-binding suspension composition to the glass substrate.





BRIEF DESCRIPTION OF THE DRAWINGS

The invention will now be described, by way of example only, with reference to the accompanying drawings, in which:



FIG. 1 provides a process diagram for preparing a self-binding suspension, according to some embodiments;



FIG. 2 shows the water droplet contact angle on an untreated glass substrate and on a glass substrate treated with a self-binding suspension, according to some embodiments;



FIG. 3 shows x-ray diffraction data from a sample of TiO2—ZnO suspension powder, according to some embodiments;



FIG. 4 shows a scanning electron microscope image of a sample of TiO2—ZnO suspension powder, according to some embodiments;



FIG. 5 shows decomposition data for a sample of TiO2—ZnO suspension powder and material disclosed in GR20110100056, according to some embodiments;



FIG. 6 shows gas concentrations under ultraviolet radiation for a self-binding suspension, according to some embodiments; and



FIG. 7 shows a transmittance spectrum of glass, material disclosed in GR20110100056, and a sample of TiO2—ZnO suspension powder, according to some embodiments.





DETAILED DESCRIPTION OF THE INVENTION

Provided herein are self-binding suspensions, coated substrates prepared using self-binding substrates, and methods of preparing self-binding suspensions using ultrasonication. In particular, the suspensions disclosed herein may be used to prepare thin films for products such as windshields, lenses, and solar energy devices. Due to the binary TiO2—ZnO system, suspensions provided herein can provide more transparent films with improved photocatalytic activity than suspensions only having one of TiO2 or ZnO.


To achieve these properties, the suspensions provided herein may include nanoparticles that are monodispersed and comprise agglomerates no larger than 200 nm.


Self-Binding Suspension Composition

Suspensions provided herein may include at least two metal oxides, a salt, a dispersant, a surfactant, alcohol, a Lewis base, and a solvent. Each individual component is described in detail below.


The metal oxides can include TiO2, SiO2 and/or ZnO nanoparticles.


TiO2 nanoparticles may be obtained from a powder. For example, a commercially available and low-cost titanium dioxide powder may be used as the titanium dioxide source. Suitable commercially available titanium dioxide powders can include Evonik Aeroxide™ P90, Evonik Aeroxide™ P25, or Kronos KRONOClean™ 7000. When diluted in water, a colloidal solution is prepared. In some embodiments, self-binding suspensions provided herein may include 0.00001 to 1 wt. % TiO2 powder. In some embodiments, self-binding suspensions provided herein may include less than 1 wt. %, less than 0.5 wt. %, less than 0.1 wt. %, less than 0.05 wt. %, less than 0.01 wt. %, less than 0.005 wt. %, less than 0.001 wt. %, less than 0.0005 wt. %, less than 0.0001 wt. %, or less than 0.00005 wt. % TiO2 powder. In some embodiments, self-binding suspensions provided herein may include more than 0.00001 wt. %, more than 0.00005 wt. %, more than 0.0001 wt. %, more than 0.0005 wt. %, more than 0.001 wt. %, more than 0.005 wt. %, more than 0.01 wt. %, more than 0.05 wt. %, 0.1 wt. %, or more than 0.5 wt. % TiO2 powder. Self-binding suspensions comprising insufficiently low concentrations of TiO2 powder may result in thin films having too little photocatalytic activity. Conversely, self-binding suspensions comprising exceedingly high concentrations of TiO2 powder may not meet the optical criteria of coating transparency.


ZnO nanoparticles may be obtained from a powder. For example, a commercially available and low-cost zinc oxide powder may be used as the zinc oxide source. Suitable commercially available zinc oxide powders may include EverZinc EPM-E™, or Bochemie Nano ZnO. When diluted in water, a colloidal solution can be prepared. In some embodiments, self-binding suspensions provided herein may include 0.00001 to 1 wt. % ZnO powder. In some embodiments, self-binding suspensions provided herein may include less than 1 wt. %, less than 0.5 wt. %, less than 0.1 wt. %, less than 0.05 wt. %, less than 0.01 wt. %, less than 0.005 wt. %, less than 0.001 wt. %, less than 0.0005 wt. %, less than 0.0001 wt. %, or less than 0.00005 wt. % ZnO powder. In some embodiments, self-binding suspensions provided herein may include more than 0.00001 wt. %, more than 0.00005 wt. %, more than 0.0001 wt. %, more than 0.0005 wt. %, more than 0.001 wt. %, more than 0.005 wt. %, more than 0.01 wt. %, more than 0.05 wt. %, 0.1 wt. %, or more than 0.5 wt. % ZnO powder. Self-binding suspensions comprising insufficiently low concentrations of ZnO powder may not assist the photocatalytic effect. Conversely, self-binding suspensions comprising exceedingly high concentrations of ZnO powder may be block incident photons capturing by titanium dioxide nanoparticles and therefore, permanently block the photocatalytic effect.


SiO2 nanoparticles may be obtained from a sol-gel procedure. For example, commercially available silicon alkoxide raw materials can be used for the preparation of a colloidal suspension comprising SiO2 powder. Suitable aminosilanes or silicon alkoxides can be any compound with chemical formula (H2NCnH2nO)(CkH2k+1O)(CmH2m+1O)(CpH2p+1O)Si or (CnH2n+1O)(CkH2k+1O)(CmH2m+1O)(CpH2p+1O)Si or polydimethylsiloxane (C2H6OSi)q (CnH2n+1O)(CkH2k+1O)(CmH2m+1O)Si(C1H21)Si(CxH2x+1O)(CyH2y+1O)(CzH2z+1O) (where n, k, l, m, p, x, y, z are positive, integer numbers from zero to eight and q is a positive integer numbers from zero to one thousand). For example, commercially available alkoxysilanes can include DOWSIL™ Z-6162, DOWSIL™ Xiameter 6697, and/or Dynasylan A. In some embodiments, the colloidal SiO2 nanoparticles prepared from a sol-gel technique may be preferred to SiO2 nanoparticles obtained from powders because they can enhance the superhydrophilicity of the final coating and act as adhesion binders to the substrate.


In some embodiments, self-binding suspensions provided herein may comprises 1 to 15 wt. % alkoxysilane. In some embodiments, self-binding suspensions provided herein may comprise less than 15 wt. %, less than 12 wt. %, less than 10 wt. %, less than 8 wt. %, less than 6 wt. %, less than 4 wt. %, or less than 2 wt. % alkoxysilane. In some embodiments, self-binding suspensions provided herein may comprise more than 1 wt. %, more than 2 wt. %, more than 4 wt. %, more than 6 wt. %, more than 8 wt. %, more than 10 wt. %, or more than 12 wt. % alkoxysilane.


In some embodiments, self-binding suspensions provided herein may include a salt. For example, a salt may be used to control the ionic strength of the preparation emulsion or suspension. Salts dissociate in aqueous media to ions (ionic strength increase). Ions are absorbed on nanoparticle surface and electrostatically repel each other to prevent agglomeration and sedimentation. Therefore, fine tuning of ionic strength results in more stable nanoparticle emulsions and increase their commercial exploitation potential. To control the ionic strength of the preparation solution, the salt may induce electrostatic interactions between the ionic double layers surrounding the TiO2 and ZnO nanoparticles. Examples of suitable salts include polyelectrolytes (e.g. poly(sodium styrene sulfonate), Na4P2O7, sodium hydroxide, or sodium chloride. In some embodiments, self-binding suspensions provided herein may include 0.00001 to 0.005 wt. % salt. In some embodiments, the amounts, a self-binding suspension may include less than 0.005 wt. %, less than 0.0025 wt. %, less than 0.001 wt. %, less than 0.0005 wt. %, less than 0.0001 wt. %, or less than 0.00005 wt. % salt. In some embodiments, a self-binding suspension may include more than 0.00001 wt. %, more than 0.00005 wt. %, more than 0.0001 wt. %, more than 0.0005 wt. %, or more than 0.001 wt. % salt. Self-binding suspensions including an insufficiently low amount of salt may present sedimentation within hours after preparation, making the resulting formulation impractical to use. Conversely, self-binding suspensions including exceedingly high concentrations of salt may result in reduced photocatalytic activity, as salt ions create multilayers around nanoparticles and prevent chemical interaction with water or oxygen molecules.


Self-binding suspensions provided herein may include a dispersant for promoting the formation and stabilization of the nanoparticles in the solution. For example, commercially available dispersants can include Surfynol CT-231, Tego Flow 425, carboxylmethyl cellulose (CMC), dimethyl sulfoxide (DMSO), 1,2-Dipalmitoyl-sn-glycero-3-phosphocholine, Tween 80, bovine serum albumin (BSA), and fetal bovine serum (FBS). In some embodiments, self-binding suspensions provided herein may include 0.0001 to 0.1 wt. % dispersant. In some embodiments, self-binding suspensions may include less than 0.1 wt. %, less than 0.05 wt. %, less than 0.01 wt. %, less than 0.005 wt. %, less than 0.001 wt. %, or less than 0.0005 wt. % dispersant. In some embodiments, self-binding suspensions may include more than 0.0001 wt. %, more than 0.0005 wt. %, more than 0.001 wt. %, more than 0.005 wt. %, more than 0.01 wt. %, or more than 0.05 wt. % dispersant.


Self-binding suspensions provided herein may include a surfactant. Surfactants may help improve substrate wetting by reducing the surface tension between the self-binding suspension/thin film and the substrate. Suitable commercially available surfactants may include Tego Wet 500, Tego Wet 270, and siloxane formulations. In some embodiments, self-binding suspensions provided herein may include 0.1 to 5 wt. % surfactant. In some embodiments, self-binding suspensions may include less than 5 wt. %, less than 4 wt. %, less than 3 wt. %, less than 2 wt. %, less than 1 wt. %, or less than 0.5 wt. % surfactant. In some embodiments, self-binding suspensions may include more than 0.1 wt. %, more than 0.5 wt. %, more than 1 wt. %, more than 2 wt. %, more than 3 wt. %, or more than 4 wt. % surfactant.


In some embodiments, self-binding suspensions provided herein may include a liquid alcohol to hydrolyze the chemical binder. A suitable alcohol may include up to five carbon atoms (e.g., methanol, ethanol) and up to two oxygen atoms (CiH2i+2O or CjH2j+2O2, where i and j are positive, integer numbers from one to five). In some embodiments, self-binding suspensions provided here may include 1 to 25 wt. % alcohol. In some embodiments, self-binding suspensions may include less than 25 wt. %, less than 20 wt. %, less than 15 wt. %, less than 10 wt. %, or less than 5 wt. % alcohol. In some embodiments, suspensions may include more than 1 wt. %, more than 5 wt. %, more than 10 wt. %, more than 15 wt. %, or more than 20 wt. % alcohol.


In some embodiments, a Lewis base may be included in a suspension provided herein to adjust the pH value during hydrolysis. In some embodiments, the pH may be adjusted and controlled to a value from 9 to 10. In some embodiments, self-binding suspensions provided herein may include 0.01 to 0.5 wt. % Lewis base. In some embodiments, self-binding suspensions may include less than 0.5 wt. %, less than 0.4 wt. %, less than 0.3 wt. %, less than 0.2 wt. %, less than 0.1 wt. %, or less than 0.05 wt. % Lewis base. In some embodiments, self-binding suspensions may include more than 0.01 wt. %, more than 0.05 wt. %, more than 0.1 wt. %, more than 0.2 wt. %, more than 0.3 wt. %, or more than 0.4 wt. % Lewis base.


Self-binding suspensions provided herein may include a solvent. Suitable solvents can include water (e.g., deionized) or alcohol. In some embodiments, self-binding suspensions provided herein may include 75 to 95 wt. % solvent. In some embodiments, self-binding suspensions may include less than 95 wt. %, less than 90 wt. %, less than 85 wt. %, or less than 80 wt. % solvent. In some embodiments, self-binding suspensions may include more than 75 wt. %, more than 80 wt. %, more than 85 wt. %, or more than 90 wt. % solvent.


Coated Substrates

The above-described self-binding suspension can be used to prepare coated substrates for applications including, but not limited to, windshields, lenses, and/or solar energy devices. Discussed below are various application/deposition methods for preparing coated substrates.


Self-binding suspensions provided can be considered “self-binding” due to the ability of particularly the nanoparticles in the self-binding suspension to easily adhere to the substrate. Specifically, the silicon oxide nanoparticles act as a binder. In some embodiments, no heat treatment step is needed for the self-binding suspension to adhere to the substrate.


In some embodiments, a self-binding suspension may be used to form the coating on a thin-film substrate. For example, 0.001 to 0.1 L/m2 of self-binding suspension may be deposited to the substrate. In some embodiments, less than 0.1 L/m2, less than 0.08 L/m2, less than 0.06 L/m2, less than 0.04 L/m2, less than 0.02 L/m2, less than 0.01 L/m2, or less than 0.005 L/m2 self-binding suspension may be deposited on a substrate. In some embodiments, more than 0.001 L/m2, more than 0.005 L/m2, more than 0.01 L/m2, more than 0.02 L/m2, more than 0.04 L/m2, more than 0.06 L/m2, or more than 0.08 L/m2 self-binding suspension may be deposited on a substrate.


In some embodiments, the substrate of the coated substrate may comprise an organic or an inorganic material. For example, suitable substrate materials may include glass, aluminum, metal substrates, cement and concrete, plasters and renders, polymer films, polycarbonate films, acrylic paint films, styrene-acrylic paint films, polyurethane paint films and epoxy paint films,


Example 1


FIG. 1 shows the flow chart of a preparation process of a self-binding suspension, according to some embodiments. As shown in the figure and explained in detail below, the binder solution is prepared separate from the TiO2/ZnO colloidal suspension and combined in the final step to form a self-binding suspension according to embodiments provided herein.


Preparing the Binder Solution: Twenty Liters of alkoxysilane (1,6-bis(trimethoxysilyl)hexane; DOWSIL™ Z-6162, Dow Corning Europe SA) were mixed with 1 L of methanol in a stainless steel 200 L chemical reactor. Deionized water (75 L) was added to the mixture and stirred for five minutes. A water-soluble Lewis base (25 wt. % ammonium hydroxide NH4OH) was added dropwise to adjust the pH to 9.5. The mixture was stirred for 600 minutes until becoming a transparent liquid.


Preparation of the TiO2/ZnO colloidal suspension: Deionized water (150 L) was placed into a 250 L stainless steel continuously stirring tank reactor. A stabilizing salt (Na4P2O7, 0.3 kg) and 0.075 kg of dispersant (Surfynol CT-231, Air Products and Chemicals, Inc.) were diluted into the deionized water. The solution was vigorously stirred for 60 minutes at 600 rpm. After stirring, 0.75 kg titanium dioxide powder (Evonik Aeroxide™ P90) and 0.075 kg zinc oxide (EverZinc EPM-E™) were added to the solution, resulting in a colloidal solution.


A Heilscher, UIP1000hd ultrasonic processor (power output: 800 Watts at 20 kHz) having a robust stainless steel reactor vessel was connected to the continuous-stirring tank reactor for 30 minutes. The ultrasonication tip was connected in the colloidal solution. After 30 minutes of ultrasonication, the resulting material was a stable TiO2—ZnO suspension.


Preparation of Final Self-Binding Suspension: As depicted in FIG. 1, the binder solution and the TiO2—ZnO suspension, the preparation of each of which is described above, are combined with the surfactant (EVONIK, Tego Wet 500). The combination is mixed and stirred for 20 minutes at 600 rpm. The product is stable for at least six months (i.e., little or no sedimentation or precipitation of solid phase). Additionally, the resulting suspension may be applied to substrates using industrial deposition methods.


Table 1, below, provides the weight-percent of each of the components described with respect to Example 1.
















Component
Wt. %
















Binder Solution










Alkoxysilane
14.35 



Alcohol
24.06 



H2O
61.27 



Lewis base
 0.32 







TiO2/ZnO Suspension










H2O
94.275-98.675 



Regulating Salt
 0.025



Dispersant
 0.2  



TiO2
0.1-5   



ZnO
0.01-10.0*







Final Self-Binding Suspension










Binder Solution
30-50 



Dispersant
 0.5 



Alcohol
 0.5 



H2O
43.5-68.4 



TiO2/ZnO Suspension
0.1-5   



Surfactant
 0.5 







*Weight percentage in relevance to the actual titanium dioxide wt. %.






Example 2


FIG. 1 equally applies to the process of Example 2, described below, as it does with Example 1. As shown in the figure and explained in detail below, the binder solution is prepared separate from the TiO2/ZnO colloidal suspension and combined in the final step to form a suspension according to embodiments provided herein.


Preparation of the Binder Solution: Twenty Liters of alkoxysilane (tetraethoxy silane; DOWSIL™ Xiameter 6697, Dow Corning Europe SA, and/or EVONIK™, Dynasylan A) were mixed with 1 L of ethanol in a 200 L stainless steel chemical reactor. Deionized water (75 L) was added to the mixture and stirred for 5 minutes. Sodium hydroxide in an aqueous solution was added dropwise to adjust the pH to 9.5. The mixture was stirred for 600 minutes until a transparent liquid was achieved.


Preparation of the TiO2/ZnO colloidal suspension: Deionized water (130 L) was placed in a 250 L stainless steel continuous stirring tank reactor. The stabilizing salt (0.25 kg, NaCl) and 0.07kg of dispersant (Surfynol CT-231, Air Products and Chemicals, Inc.) were diluted in the deionized water. The solution was vigorously stirred for 60 minutes at 600 rpm. After stirring, 0.65 kg of titanium dioxide powder (Evonik Aeroxide™ P90) and 0.013 kg of zinc oxide (EverZinc EPM-E™) are added to create a colloidal solution.


A Hielscher, UIP1000hd ultrasonic processor (power output: 800 Watts at 20 kHz) having a robust stainless steel reactor vessel was connected to the continuous-stirring tank reactor for 30 minutes. The ultrasonication tip was connected in the colloidal solution. After 30 minutes of ultrasonication, the resulting material was a stable TiO2—ZnO suspension.


Preparation of the Final Self-binding Suspension: As depicted in FIG. 1, the binder solution and the TiO2—ZnO suspension, the preparation of each of which is described above, are combined with the surfactant (EVONIK, Tego Wet 270). The combination is mixed and stirred for 20 minutes at 600 rpm. The product is stable for at least six months (i.e., little or no sedimentation or precipitation of solid phase). Additionally, the resulting suspension may be applied to substrates using industrial deposition methods.


Table 1, provided above, provides the weight-percent of each component described with respect to Example 2.


Example 3

Applying the Prepared Suspension to Glass Substrates: The prepared self-binding suspension (i.e., the suspension of Example 1 or Example 2) was mist air-sprayed onto glass substrates. Specifically, the amount of suspension that was deposited onto the glass substrate was 0.0285 L/m2. The wet suspension dried and resulted in an immobilized Si02/TiO2/ZnO thin film. Note that no heat treatment was used.



FIG. 2 shows the contact angle of a water droplet on an untreated glass substrate and on a glass substrate coated with a thin film formed from a suspension according to embodiments provided herein. The contact angle was measured using a computer-controlled optical tensiometer. Results show that contact angle of water with the coating is less than 10 degrees, therefore intense hydrophilicity is observed. As shown in FIG. 4, the high contact angle of the water droplet on the treated glass substrate demonstrates that the thin-film coating prepared using suspensions according to embodiments provided herein are hydrophilic.



FIG. 3 shows x-ray diffraction data obtained from TiO2—ZnO suspension powder. In particular, FIG. 3 shows the XRD characteristic peaks obtained from the TiO2/ZnO colloidal suspension. The marked peaks (marked with numbers) are in accordance with the characteristic peaks of pure TiO2 nanoparticles. In detail, the observed peaks for TiO2 are: 24.20° (A), 27.30° (R), 37.79° (A), 48.01° (A), 53.79° (A), 62.73° (A), 68.79° (A), 70.00° (A) and 75.10° (A), which correspond to the (101), (110), (004), (200), (105), (204), (116), (220), (116), (220) and (215) crystal planes for pure TiO2. The symbols A and R denote anatase and rutile phase, respectively. From the XRD-pattern it is clear that the TiO2 nanoparticles consist from two crystal phases; one is anatase and the other is rutile. In addition, is possible to calculate the ratio of anatase/rutile in the solution from the relative intensities. By using the equations A(%)=100/{1+1.265(IR/IA)} and R(%)=100−A(%), the mass ratio of anatase/rutile in our solutions is 80%/20%. Where A(%) and R(%) are the percentages of anatase and rutile, respectively. IR is the intensity corresponds to the main peak for rutile (110) at angle 2θ equal to 27.30° and IA is the intensity corresponds to the main peak for anatase (101) at angle 2θ equal to 24.20° . This mass percentage 80/20 is in totally accordance with the specifications provided for the raw material used for preparation of the samples. In the case of ZnO nanoparticles the peaks are allocated at angles 2θ around 32°, 34°, 36°, 47°, 57°, 63°, 66°, 68° and 69° correspond to the (100), (002), (101), (102), (110), (103), (200), (112) and (201) crystal planes for pure ZnO nanoparticles. It should be noticed that the peaks of ZnO due to the low percentage used in the solutions can be shifted depending the composition of the solution. For the ZnO nanoparticles the main peak is at 36.38° which corresponds to (101) crystal plane. For this reason, the quantitative analysis for calculation of the ZnO percentage is difficult in the presence of TiO2 nanoparticles. In addition, the XRD peaks are very sharp indicating that the NANOPARTICLEs are crystalline and well within the nano-range. Owing to this fact, by using the Scherrer equation d=0.9λ/B cos θ, (where d is the mean size of the nanoparticles, λ is the X-ray wavelength equal to 1.542 Å, B is the peak width at half the maximum intensity and θ is the angle corresponding to the main peak), we calculated that the nanoparticles which form the TiO2—ZnO suspension is in in the range of 26 nm.



FIG. 4 shows a scanning electron microscope image obtained from TiO2—ZnO suspension powder. As shown in the figure, the powder comprises nanoparticles and porosity, which can extend the surface area of the powders. From the scanning electron microscope characterization it is obvious that the primary nanoparticles do not exceed the size of 50 nm.


Evaluating the Photocatalytic Activity of the Self-Binding Suspension: The photocatalytic activity of the final self-binding suspension was evaluated by two procedures: (1) degradation of methyl orange (pollutant, organic compound) under UV illumination; and (2) by nitric oxide (inorganic pollutant) oxidation under UV and visible light irradiation.


The first procedure, degradation of methyl orange, was conducted using round-bottom photocatalytic cells with a near UV-transparent window (cut off below 340 nm). A laboratory-constructed irradiation box equipped with four Sylvania GTE 15W F15W/T8 blacklight blue fluorescent light tubes was used. The photon source had a maximum emission at 350 nm and emitted 71.7 μW/cm to simulate natural sunlight. The concentration was correlated to the absorption of the methyl orange solution at 464 nm, using a single beam Shimadzu UV 1240 spectrophotometer. The sample was stirred throughout the procedure.


Based on the methyl orange degradation test, the final self-binding suspension demonstrates improved photocatalytic properties compared to the colloidal suspension of GR20110100056. FIG. 5 shows the decomposition of methyl orange as a function of time for the material of GR20110100056, and the self-binding suspension of the present invention. In particular, FIG. 5 shows the degradation of methyl orange versus time for each of these two samples.


The second procedure, nitric oxide oxidation under UC and visible light irradiation, was evaluated under UV-A light illumination with intensity 10 W/m2. The duration of the experiments was almost 5 h. The NO gas was supplied from gas container with 50 ppm NO concentration in nitrogen N2. The NO concentration in the reactor was adjusted to 1 ppm and the relative humidity was kept at 50% using dry and wet air. The NO gas flow rate over the samples was approximately 3 L/min. Under UV illumination, NO gas was adsorbed on the surface of photocatalysts and successively oxidized to NO2 gas first and then to nonvolatile nitrates. The NOx concentration in the air was retrieved by the summation of NO and NO2 concentrations. The measurement results are presented in FIG. 6. The photocatalytic study includes measurements of the NO monoxide, measurements of the NO2 dioxide and determination of NOx removal. The investigated sample with photocatalytic material exhibited stable photocatalytic activity in NOx removal during 5 h illumination period and revealed production of NO2 gas in the range of 20%.



FIG. 6 shows gas concentration under ultraviolet irradiation of a self-binding suspension. As shown in the Figure, nitric acid oxidation shows superior photocatalytic behavior under visible light irradiation. This behavior is easily attributed to the favorable modified band gaps edges existing in the presented ternary system.



FIG. 7 shows a transmittance spectrum of untreated glass, glass treated with material of GR20110100056, and glass treated with the self-binding suspension described herein. As shown in the figure, the glass treated with the self-binding suspension described herein consistently transmits more light than untreated glass or the glass treated with material of GR20110100056, across wavelengths 375-1975nm.


Aging Test: The adhesion behavior of coatings prepared using self-binding suspensions provided herein was tested using an aging test. In particular, the aging test according to ISO EN 11507 was conducted. During the test, no coating exfoliation was observed (i.e., no physical change on the surface of the coated glass).


The preceding description sets forth exemplary methods, parameters and the like. It should be recognized, however, that such description is not intended as a limitation on the scope of the present disclosure but is instead provided as a description of exemplary embodiments. The illustrative embodiments described above are not meant to be exhaustive or to limit the disclosure to the precise forms disclosed. Many modifications and variations are possible in view of the above teachings. The embodiments were chosen and described to best explain the principles of the disclosed techniques and their practical applications. Others skilled in the art are thereby enabled to best utilize the techniques, and various embodiments with various modifications as are suited to the particular use contemplated.


Although the disclosure and examples have been thoroughly described with reference to the accompanying figures, it is to be noted that various changes and modifications will become apparent to those skilled in the art. Such changes and modifications are to be understood as being included within the scope of the disclosure and examples as defined by the claims. In the preceding description of the disclosure and embodiments, reference is made to the accompanying drawings, in which are shown, by way of illustration, specific embodiments that can be practiced. It is to be understood that other embodiments and examples can be practiced, and changes can be made without departing from the scope of the present disclosure.


Although the preceding description uses terms first, second, etc. to describe various elements, these elements should not be limited by the terms. These terms are only used to distinguish one element from another.


Also, it is also to be understood that the singular forms “a,” “an,” and “the” used in the preceding description are intended to include the plural forms as well unless the context indicates otherwise. It is also to be understood that the term “and/or” as used herein refers to and encompasses any and all possible combinations of one or more of the associated listed items. It is further to be understood that the terms “includes, “including,” “comprises,” and/or “comprising,” when used herein, specify the presence of stated features, integers, steps, operations, elements, components, and/or units but do not preclude the presence or addition of one or more other features, integers, steps, operations, elements, components, units, and/or groups thereof.


The term “if” may be construed to mean “when” or “upon” or “in response to determining” or “in response to detecting,” depending on the context.


Although the disclosure and examples have been fully described with reference to the accompanying figures, it is to be noted that various changes and modifications will become apparent to those skilled in the art. Such changes and modifications are to be understood as being included within the scope of the disclosure and examples as defined by the claims.

Claims
  • 1. A self-binding suspension composition comprising: 0.0001 to 0.25 wt. % titanium dioxide nanoparticles;0.00001 to 0.5 wt. % zinc oxide nanoparticles;4 to 7 wt. % alkoxysilane;0.000025 to 0.00125 wt. % salt;0.0002 to 0.01 wt. % dispersant;0.2 to 0.8 wt. % surfactant;7 to 12 wt. % alcohol;0.1 to 0.2 wt. % basic solution; and80 to 90 wt. % solvent.
  • 2. The composition of claim 1, wherein the salt comprises at least one of Na4P2O7, sodium hydroxide, or sodium chloride.
  • 3. The composition of claim 1, wherein the alcohol comprises at least one of methanol or ethanol.
  • 4. The composition of claim 1, wherein the solvent comprises deionized water.
  • 5. The composition of claim 1, wherein the titanium dioxide nanoparticles are formed from applying ultrasonication to titanium dioxide powder.
  • 6. The composition of claim 1, wherein the zinc oxide nanoparticles are formed from applying ultrasonication to zinc oxide powder.
  • 7. A coated glass substrate comprising: a glass substrate; anda thin-film coating on the glass substrate, the thin-film coating comprising: 0.001 to 5 wt. % titanium dioxide powder;0.0001 to 10 wt. % zinc oxide powder;20 to 35 wt. % alkoxysilane;0.00025 to 0.026 wt. % salt;0.002 to 0.2 wt. % dispersant;1 to 8 wt. % surfactant;35 to 60 wt. % alcohol; and0.5 to 4 wt. % basic solution.
  • 8. The coated glass substrate of claim 7, wherein the salt comprises at least one of Na4P2O7, sodium hydroxide, or sodium chloride.
  • 9. The coated glass substrate of claim 7, wherein the alcohol comprises at least one of methanol or ethanol.
  • 10. The coated glass substrate of claim 7, wherein the solvent comprises deionized water.
  • 11. The coated glass substrate of claim 7, wherein 0.01 to 0.03 L/m2 of a self-binding suspension composition is applied to the glass substrate to form the coated glass substrate.
  • 12. The coated glass substrate of claim 7, wherein the coated glass substrate comprises a windshield, a lens, or a solar energy device.
  • 13. A method of producing a coated glass substrate comprising: preparing a binder solution;preparing a titanium dioxide-zinc oxide suspension;mixing the binder solution with the titanium dioxide-zinc oxide suspension and a surfactant to form a self-binding suspension composition; anddepositing the self-binding suspension onto a glass substrate to form a coated glass substrate.
  • 14. The method of claim 13, wherein preparing a binder solution comprises mixing alkoxysilane, an alcohol, a Lewis base, and a first solvent.
  • 15. The method of claim 13, wherein preparing a titanium dioxide-zinc oxide suspension comprises ultrasonifying a salt, a dispersant, titanium dioxide powder, zinc oxide powder, and a second solvent.
  • 16. The method of any of claim 13, wherein the coated glass substrate comprises a windshield, a lens, or a solar energy device.
  • 17. The method of claim 15, wherein the salt comprises at least one of Na4P2O7, sodium hydroxide, or sodium chloride.
  • 18. The method of claim 14, wherein the alcohol comprises at least one of methanol or ethanol.
  • 19. The method of claim 14, wherein the first solvent and the second solvent comprise deionized water.
  • 20. The method of claim 13, wherein depositing the self-binding suspension onto a glass substrate comprises depositing 0.01 to 0.03 L/m2 of the self-binding suspension composition to the glass substrate.