Self-cleaning ceramic layers for baking ovens and method for production of self-cleaning ceramic layers

Abstract

The invention concerns a method for producing a highly-porous ceramic layer and for application of this layer onto metallic, ceramic, enameled and/or glass substrates using porous, ceramic particles, preferably aluminum oxide, titanium oxide and zircon oxide, and an inorganic binder system. The inorganic binder system contains at least one ceramic nanoparticle of a particle size of less than 100 nm, preferably less than 50 nm and particularly preferred less than 25 nm, the solvent being water. Layers produced in this fashion are suited as self-cleaning catalytically active layers e.g. in ovens, in combustion engines etc. or for general coating of substances to considerably increase their specific surface e.g. for catalytic substrates.

Description

BACKGROUND OF THE INVENTION

[0001] The invention concerns a method for producing a highly-porous, ceramic layer which can be applied to metallic, ceramic, enameled and/or glass substrates using porous, ceramic particles, preferably aluminum oxide, titanium oxide and zirconium oxide and an inorganic binder system. The inorganic binder system contains at least one ceramic nanoparticle of a particle size of less than 100 nm, preferably less than 50 nm and particularly preferred less than 25 nm, the solvent being water. Layers produced in this fashion are suited for self-cleaning catalytically active layers e.g. in ovens, in combustion engines etc. or for general coating of substrates, to considerably increase their specific surface area e.g. for catalytic applications.

[0002] Ovens contain a cooking chamber which is lockable by a door and is delimited by an oven muffle. During roasting and baking, the side walls of the cooking chamber are soiled e.g. by splashing fat or meat juice or the like. This soiling during baking and roasting cannot be prevented. For this reason, the manufacturers have proposed several ways to clean the walls, top and bottom, i.e. the inner space of the cooking chamber. One generally differentiates between catalytic and pyrolytic cleaning.

[0003] For pyrolytic cleaning, the cooking chamber has so-called grill rods which can be controlled and heated through a separate, electronically controlled program and are preferably mounted to the top of the cooking chamber. The organic soiling is carbonized, i.e. completely burnt, at temperatures of more than 500° C. (Cepem Cie Euro Equip Menager [FR2605391] or Bosch Siemens Haushaltsgeräte GmbH [DE2526096]. Pyrolytic cleaning is demanding and expensive due to the required high temperatures. Ovens with pyrolytic cleaning must have suitable protective mechanism to block the door of the cooking chamber during pyrolysis (from approximately 320° C., Bosch Siemens Hausgeräte GmbH [EP 0940631] to protect the oven from improper operation. Since these ovens furthermore require more expensive heating elements to be able to control the high temperature at all, pyrolysis systems have been established only in ovens of the top price bracket.

[0004] In view of the costs, the catalyst systems are preferable to pyrolysis systems since catalytic combustion of soiling takes place at lower temperatures, i.e. below 500° C. Matsushita Elec. Ind. Co. Ltd. [JP03056144] proposes lining of the interior of the oven with a catalytically active coating which consists of a binder system and a catalytically active powder. Metal oxides are used as catalyst, preferably manganese dioxide and silicon resins are used as binders. This catalytic coating permits cleaning of the oven interior already between 380° C. and 400° C. as stated by the manufacturer. Mixture of a catalyst and a binder 15 system or a layer matrix for coating the inner surface of an oven can also be found with other oven manufacturers. Toshiba [JP60147478] uses manganese oxide or ferrite as catalyst and sodium silicate as binder phase. In an analog fashion, Sharp KK [JP54135076] uses quartz sand or sodium silicate as binder phase and iron oxide or copper oxide as catalyst. These protective rights give no statement about the effectivity of the two latter catalytic coatings. The onset temperature of the coating, i.e. the temperature at which the layer starts to work, was reduced in accordance with the above-mentioned documents to 270° C. to 300° C. (Toshiba) and even to 250° C. (Sharp KK). In practice this means, that there are catalytic coatings which start to break down fat etc. in the interior of the oven at temperatures below 320° C., however, the efficiency of the coating is not sufficient to completely finish this decomposition. After each baking or roasting cycle, residues of non-decomposed fat remain in or on the layer lining the interior of the oven, such that after a very short time, the function of the layer is impaired since it is varnished. For complete decomposition, these systems still require temperatures of usually more than 380° C.

[0005] Finally, NGK Insulators Ltd [JP56095022] should be mentioned, which use manganese oxide, copper oxide and iron oxide as catalysts, and a porous enamel as layer matrix to increase the amount of applied catalyst, as well as the protective rights of Matsushita [JP02069574], Cie Euripeenne pour L'Equ [FR2040822] and Hoover LtD [GB1177434] which all use flouropolymers as carrier layer for the catalysts to minimize the surface energy of the carrier layer and prevent adhesion.

[0006] Pyrolytic cleaning is very effective at temperatures above 500° C. but is expensive due to the facts given by process technology. These systems are currently used only for ovens of the top price bracket (maximally 10% of all ovens). The reduction in cost promoted the development of catalytic cleaning. The inner walls of the cooking chamber are thereby lined with a layer which always contains a catalyst. Suitable catalysts are manganese oxide, iron oxide and copper oxide, wherein temperature-resistant polymers, sodium silicate, quartz sand and enamel are used as binder phase of the catalyst or as layer component. The catalysts operate at temperatures of more than 380° C. which requires safety measures producing additional costs. Only a few catalytically active coatings are known whose onset temperature, i.e. start of fat disintegration in the layer is between 250° C. and 350° C. In these cases, large amounts of residues remain in or on the layer during permanent operation of the oven below 350° C. with the consequence that these oven inner coatings varnish very quickly.

[0007] Catalysis is subject to thermo-dynamic rules. A catalyst cannot change the thermodynamics of a system but only lower the activation energy, i.e. the tendency to start the reaction. Although combustion of the organic soiling occurs thermodynamically only at a higher temperature, it starts at a lower temperature if initiated by a catalyst. Not all parts of the organic soiling disintegrate at this low temperature, which leaves residues which cause varnishing of the interior of the oven with the consequence that the optic and haptic appearance of the oven interior drastically deteriorates after only a few baking and roasting cycles.

[0008] It is the underlying purpose of the invention to develop a coating for the interior of an oven which automatically eliminates the soiling produced through roasting and baking, i.e. through application of a temperature of considerably less than 320° C., wherein the working temperature of the layer is preferably 250° C.

SUMMARY OF THE INVENTION

[0009] This object is achieved by a ceramic composition (mass), a mixture of a porous ceramic powder and an inorganic binder system, which comprises at least one porous ceramic powder with a primary particle size of between 1 nm and 500 m, preferably between 50 μm and 150 μm and an inorganic binder system which contains at least one nano-scale particle.

[0010] In this fashion, porous ceramic layers can be produced having high temperature stability and abrasion resistance. These layers contain large pores/pore volumes which are accessible for organic soiling (e.g. fats), and also small pores through the introduced porous ceramic particles, which are not accessible for organic soiling. The porous ceramic layers have a very high suction capacity and transport the organic soiling (e.g. fat and meat juice) initially inside the inventive layer. The soiling is spread, i.e. distributed on a very large surface. At a temperature of 250° C., the soiling is almost completely disintegrated with no catalyst being contained in the layer. Precise matching of the binder system and the fact that at least one nanoparticle is used as binding phase, produces a very large inner surface, preferably larger than 20 m2/g, particularly preferred larger than 70 m2/g and particularly preferred larger than 120 m2/g which is loaded with organic soiling. On the other hand, the reaction partner oxygen which is required for combustion, is stored already in the porous ceramic parts, similar to a reservoir and is directly available such that the oxidative combustion of the soiling is initiated early and carried out in quantity already at 250° C.

[0011] First-time production of a self-cleaning layer for ovens is achieved, which removes almost in quantity organic soiling at temperatures of considerably less than 380° C., preferably considerably less than 320° C. A new possibility to clean ovens consists in the production of an active ceramic layer without catalyst, which, however, offers the possibility to spread organic soiling on a very large surface (due to the nanoparticles) and provide the reaction partner, required for oxidation, in the form of a reservoir in the layer. Compared to commercially available catalytic cleaning systems, the inventive self-cleaning layer is moreover characterized by a considerably higher efficiency at lower temperatures, preferably between 280° C. and 250° C. preventing early varnishing of the coating.

[0012] The inventive ceramic layer is characterized by the presence of numerous pores of different sizes and a high inner pore volume. To generate these pores, the inventive composition (mass) preferably contains two different ceramic powder s particles and particularly preferred three different ceramic powder particles. The ceramic particles used are, in particular, chalcogenide, carbide or nitride powders, wherein at least one of these powders is nano-scale. The chalcogenide powders may be oxide powder, sulfide powder, selenide powder or telluride powder, wherein oxide powder is preferred. Any powder which is conventionally used for powder sintering, can be used. Examples are (optionally hydrated) oxides such as ZnO, CeO2, SnO2, Al2O3, SiO2, TiO2, In2O3, ZrO2, yttrium-stabilized ZrO2, Fe2O3, Fe3O4, Cu2O or WO3 as well as phosphates, silicates, zirconates, aluminates and stannates, carbides such as WC, CdC2 or SiC, nitrides such as BN, AIN, Si3N4, and Ti3N4 corresponding mixed oxides such as metal-tin-oxides, e.g. indium-tin-oxide (ITO). Moreover, also mixtures of the stated powder parts can be used.

[0013] The inventive composition (mass) contains a ceramic powder which is characterized by a high specific, largely inner surface, larger than 50 m2/g, preferably larger than 100 m2/g, and particularly preferred larger than 150 m2/g. This porous ceramic powder has an average particle size distribution of more than 500 nm, preferably larger than 1 μm and particularly preferred larger than 30 μm. This ceramic powder is an oxide, hydroxide, chalcogenide, nitride or carbide of Si, Al, B, Zn, Zr, Cd, Ti, Ce, Sn, In, La, Fe, Cu, Ta, Nb, V, Mo or W, particularly preferred of Si, Zr, Al, Fe and Ti. The use of oxides is particularly preferred. Preferred inorganic solid particles are aluminum oxide, boehmite, zircon oxide, iron oxide, silicon dioxide, titanium dioxide, silicates, stone powder, perlites and zeolites or mixtures of these inorganic solids.

[0014] The inventive composition moreover contains an inorganic binder system, which consists of a solvent and at least one nano-scale powder. The primary parts of the nano-scale powder may be present in an agglomerated form, preferably in a non-agglomerated or substantially non-agglomerated form. Any conventional alcohols can be used as solvent, preferably 2-butoxy ethanol, ethanol, 1-propanol, 2-propanol, particularly preferred water. The ceramic powder is an oxide, hydroxide, chalcogenide, nitride or carbide of Si, Al, B, Zn, Zr, Cd, Ti, Ce, Sn, In, La, Fe, Cu, Ta, Nb, V, Mo or W, particularly preferred of Si, Zr, Al, Fe, and Ti. The use of oxides is particularly preferred. Preferred inorganic nano-scale solid particles are aluminum oxide, boehmite, zircon oxide, iron oxide, silicon dioxide, titanium dioxide, and goethite or mixtures of these inorganic nano-scale solids. To adjust the viscosity of the inorganic binder system, all conventional inorganic and organic acids and lyes can be used, preferably hydrochloric acid, phosphoric acid, sulfuric acid and nitric acid.

[0015] A third ceramic powder may be added to the inventive composition, optionally for precise adjustment of the porosity. This powder consists of ceramic particles of an average particle size distribution of between 10 nm and 1 μm, preferably between 150 nm and 600 nm. The substance of the third ceramic powder is oxide, hydroxide, chalcogenide, nitride or carbide of Si, Al, B, Zn, Zr, Cd, Ti, Ce, Sn, In, La, Fe, Cu, Ta, Nb, V, Mo or W, particularly preferred of Si, Zr, Al, Fe and Ti. The use of oxides is particularly preferred. Preferred inorganic solid particles are aluminum oxide, boehmite, zircon oxide, iron oxide, silicon dioxide, titanium dioxide, silicates, and stone powder.

[0016] The inventive composition can optionally be extended through adding one or more coloring inorganic components. Any conventional inorganic colorants can be used as coloring component, preferably spinels. The combination of several coloring components permits arbitrary adjustment of color effects (patterns and spots) in addition to pure colors.

[0017] The third optionally used ceramic powder is mixed with the likewise optionally used coloring powders and slurried with the solvent. The porous ceramic powder and the inorganic binder system are added to this slurry, thereby producing a ceramic suspension which can be applied, dried and subsequently compacted into a porous ceramic layer through spin coating, dip coating, immersion, flooding or preferably spraying onto a desired substrate. For compacting, temperatures of up to 1200° C. can be used, preferably between 400° C. and 1000° C. and particularly preferred between 700° C. and 850° C.

[0018] The inventive ceramic composition permits application of porous, ceramic layers onto metal, glass, enamel or ceramic surfaces having layer thicknesses of between 20 μm and 1 mm, preferably between 70 μm and 600 μm.

[0019] In a particular embodiment of the invention, these porous, ceramic layers can be covered with catalysts to permit utilization of these layers for catalytic reactions, e.g. in the chemical industry.

[0020] The following example explains the invention without limiting it:

EXAMPLE 1

[0021] 15.0 g of the aluminum oxide powder Martoxid MR70 (company Martinswerk) is mixed with 10.0 g of the spinel pigment PK 3060 (company Ferro) and slurried with 52.0 g water. 70.0 g of a porous aluminum oxide (Nabalox NG100, company Nabaltec) is added thereby obtaining a highly viscous pasty slurry. Addition of 3.8 g of a 65% nitric acid greatly reduces the viscosity producing a stirrable suspension. 26.38 g of an inorganic binder solution (40% nano-scale zircon oxide/60% water) is added to this suspension. The viscosity of the now sprayable suspension can be arbitrarily adjusted by small amounts of water and/or nitric acid.

[0022] The invention concerns a method for producing a highly porous, ceramic layer and for applying this layer onto metallic, ceramic, enameled and/or glass substrates using porous ceramic particles, preferably aluminum oxide, titanium oxide and zircon oxide and an inorganic binder system. The inorganic binder system contains at least one ceramic nano particle of a particle size of less than 100 nm, preferably less than 50 nm and particularly preferred less than 25 nm. The solvent is water. Layers produced in this fashion are suited as self-cleaning active layers, e.g. in ovens, in combustion engines etc. or generally for coating substrates to drastically increase their specific surface, e.g. for catalyst substrates.

Claims

1-17. Cancelled.

18. A method for producing a highly porous ceramic layer, said method comprising: providing a porous ceramic powder having an inner surface larger than 50 m2/g and an average particle size distribution of more than 500 nm; providing an inorganic binder system containing at least one nano-scale powder and a solvent; and mixing the porous powder and inorganic binder system to form a composition.

19. The method according to claim 18 wherein said solvent comprises water.

20. The method according to claim 18 wherein the porous ceramic powder inner surface is larger than 100 m2/g and the average particle size distribution is more than 1 μm.

21. The method according to claim 18 wherein the porous ceramic powder inner surface is larger than 150 m2/g and the average particle size distribution is more than 30 μm.

22. The method according to claim 18 wherein the porous ceramic powder is selected from a group consisting of aluminum oxide, boehmite, zircon oxide, iron oxide, silicon dioxide, titanium dioxide, silicates, stone powder, perlites, zeolites and mixtures thereof.

23. The method according to claim 18 wherein the composition comprises between 20% and 80% by weight related to a solid content of the composition.

24. The method according to claim 18 wherein said nano-scale powder is selected from a group consisting of Al2O3, AlO(OH), ZrO2, TiO2, SiO2, Fe3O2, SnO2 and mixtures thereof and wherein an average primary particle size of the nano-scale powder is below 100 nm and the solvent comprises an alcohol selected from a group consisting of 2-butoxy ethanol, ethanol, 1-propanol, 2-propanol and water.

25. The method according to claim 18 wherein the composition comprises between 1% and 20% by weight of nano-scale powder.

26. The method according to claim 18 further comprising providing a third ceramic powder in an amount providing precise adjustment of composition porosity, said third ceramic powder having an average particle size distribution of between about 10 nm and 1 μm and said third ceramic powder is selected from a group consisting of an oxide, aluminum oxide, boehmite, zircon oxide, iron oxide, silicon dioxide, titanium dioxide, silicates and stone powder.

27. The method according to claim 26 wherein the composition comprises between 5% and 50% by weight referred to a solid content of the composition.

28. The method according to claim 18 further comprising providing at least one inorganic colorant and mixing the colorant with the porous powder and inorganic binder system.

29. The method according to claim 18 further comprising providing a plurality of inorganic colorants in amounts enabling adjustment of color effects including patterns and spots in the composition, the colorant comprising spinels.

30. The method according to claim 18 further comprising applying, drying and condensing the composition onto a ceramic, metallic, enameled or glass-like substrate through a step selected from a group consisting of spin coating, dip coating, immersion, flooding and spraying.

31. The method according to claim 30 wherein the composition is condensed at a temperature of up to 1200° C.

32. A porous ceramic layer produced in accordance with the method of one of the claims 18 through 31.

33. The method according to claim 30 further comprises applying the composition to an oven surface to act as a self-cleaning layer.

34. The method according to claim 30 further comprising applying the composition to a medical device to act as a medicine carrier.

35. The method according to claim 34 further comprising providing a bactericidal substance in the applied composition for bactericide applications.

36. The method according to claim 30 further comprising providing an aromatic substrate and adding said aromatic substrate to the applied composition.

37. The method according to claim 30 further comprising providing a catalyst and adding said catalyst to the applied composition.