Self-Supporting Structures Having Active Materials

Information

  • Patent Application
  • 20200114299
  • Publication Number
    20200114299
  • Date Filed
    December 12, 2019
    4 years ago
  • Date Published
    April 16, 2020
    4 years ago
Abstract
A method and system for manufacturing and using a self-supporting structure in processing unit for adsorption or catalytic processes. The self-supporting structure has greater than 50% by weight of the active material in the self-supporting structure to provide a foam-geometry structure providing access to the active material. The self-supporting structures, which may be disposed in a processing unit, may be used in swing adsorption processes and other processes to enhance the recovery of hydrocarbons.
Description
FIELD

The present techniques relate to fabrication of self-supporting structures being foam-geometry structures including an active material. In particular, the self-supporting structures may be used in separation and/or catalysis processes, such as swing adsorption processes and other processes to enhance the recovery of hydrocarbons.


BACKGROUND

Processing techniques are useful in many industries and can typically be accomplished by flowing a mixture of fluids over an active material, such as a catalyst or adsorbent material, to provide the preferred product stream. For adsorption process, the adsorbent materials preferentially adsorbs one or more gas components, while not adsorbing one or more other gas components. The non-adsorbed components are recovered as a separate product. For catalytic processes, the catalyst is configured to interact with the components in the stream to increase the rate of a chemical reaction.


By way of example, one particular type of gas separation technology is swing adsorption, such as temperature swing adsorption (TSA), pressure swing adsorption (PSA), partial pressure purge swing adsorption (PPSA), rapid cycle pressure swing adsorption (RCPSA), rapid cycle partial pressure swing adsorption (RCPPSA), and not limited to but also combinations of the fore mentioned processes, such as pressure and temperature swing adsorption. As an example, PSA processes rely on the phenomenon of gases being more readily adsorbed within the pore structure or free volume of an active material, such as an adsorbent material, when the gas is under pressure. That is, the higher the gas pressure, the greater the amount of readily-adsorbed gas adsorbed. When the pressure is reduced, the adsorbed component is released, or desorbed from the adsorbent material.


The swing adsorption processes (e.g., PSA and TSA) may be used to separate gases of a gas mixture because different gases tend to fill the micropore of the adsorbent material to different extents. For example, if a gas mixture, such as natural gas, is passed under pressure through a vessel containing an adsorbent material that is more selective towards carbon dioxide than it is for methane, at least a portion of the carbon dioxide is selectively adsorbed by the adsorbent material, and the gas exiting the vessel is enriched in methane. When the adsorbent material reaches the end of its capacity to adsorb carbon dioxide, it is regenerated in a PSA process, for example, by reducing the pressure, thereby releasing the adsorbed carbon dioxide. The adsorbent material is then typically purged and repressurized. Then, the adsorbent material is ready for another adsorption cycle.


Typically, the structures used in catalytic processes and adsorption processes have a limited array of physical structure types. The active material are often structured into beads, granules, spheres or pellets using binders and processing techniques like extrusion or spray drying. The beads, granules, spheres or pellets are then packed together within a unit as a packed bed for the catalytic or adsorption processes. As a result, the conventional fabrication of catalysts or adsorbents, involve extrusions of small sphere-like active materials to be used in packed beds (e.g., spheres, pellets, lobes, etc.). However, the packed beds provide tortuous paths through the packed bed, which result in large pressure drops.


In other configurations, the structure may be an engineered structure, such as a monolith. In engineered structures, the active materials are coated onto substrates, such as a metal or ceramic monolith. The engineered structures provide substantially uniform flow paths, which lessen pressure drops as compared to packed beds. However, with these structures the majority of weight is inactive material that is used to form the underlying support structure.


As a result, typical fabrication approaches of structures involve extrusions of small sphere-like active materials to be used in packed beds (e.g., spheres, pellets, lobes, etc.), or the application of thin coatings of active material on monolith substrates (e.g., ceramic or metal monoliths). The packed beds have large pressure drops as compared with engineered structures. Also, the engineered structures include additional weight from structural support that is inactive material, which increases the size and weight of the structure.


Other related materials include Rezaei, F. et al., 2009, Optimum structured adsorbents for gas separation processes, Chemical Engineering Science 64, p. 5182 to 5191; Patcas, F. C. et al., 2007, CO oxidation over structured carriers: A comparison of ceramic foams, honeycombs and beads, Chemical Engineering Science 62, p. 3984 to 3990; U.S. Patent Application Publication No. 20030145726; and Richardson, J. T. et al., 2000, Properties of ceramic foam catalyst supports: pressure drop, Applied Catalysis A: General 204, p. 19 to 32; and Stemmet, C. P. et al., 2006, Solid Foam Packings for Multiphase Reactors: Modelling of Liquid Holdup and Mass Transfer, Chemical Engineering Research and Design 84(A12), p 1134 to 1141.


Accordingly, there remains a need in the industry for apparatus, methods, and systems that provide enhancements in processes having self-supporting structures that include active materials and may include forming foam-geometry structures having complex geometries. Further, the present techniques provide enhancements by integrating self-supporting foam-geometry structures with adsorption or catalytic processes, such as swing adsorption processes to separate contaminants from a feed stream. Accordingly, the present techniques overcome the drawbacks of conventional structures in separation and/or catalysis processes.


SUMMARY OF THE INVENTION

In one embodiment, a processing unit is described. The processing unit includes a housing forming an interior region; a self-supporting structure disposed within the interior region, wherein the self-supporting structure has greater than 50% by weight of the active material in the self-supporting structure, wherein the self-supporting structure is a foam-geometry structure configured to provide one or more tortuous channels for fluid flow paths through the self-supporting structure; and a plurality of valves secured to the housing, wherein each of the plurality of valves is configured to control fluid flow along a flow path extending between the self-supporting structure and a location external to the housing.


In one or more embodiment, the processing unit may include various enhancements. For example, the processing unit may include two or more of the plurality of valves are operated via common actuation mechanism; the processing unit may be a cyclical swing adsorbent bed unit configured to remove contaminants from a gaseous feed stream that passes through the self-supporting structure; the self-supporting structure may have greater than 60% by weight of the active material in the self-supporting structure or the self-supporting structure may have greater than 70% by weight of the active material in the self-supporting structure; may include a flow distributor disposed between the adsorbent bed and the plurality of valves; the housing may be configured to maintain a pressure from 5 pounds per square inch absolute (psia) and 1,400 psia; wherein the self-supporting structure has pores in the range between 10 pores per inch and 100 pores per inch, pores in the range between 15 pores per inch and 60 pores per inch; or pores in the range between 20 pores per inch and 40 pores per inch; wherein the self-supporting structure comprises a plurality of first sheets having a first composition and a first pore density and a plurality of second sheets having a second composition and second pore density, wherein the first pore density is in the range from 1 pores per linear inch (ppi) to 20 ppi and the second pore density is in the range from 20 ppi to 100 ppi and/or the self-supporting structure has a low thermal mass.


In yet another embodiment, a method for removing contaminants from a feed stream is described. The method comprises: a) performing one or more adsorption steps in an adsorbent bed unit, wherein each of the one or more adsorption steps comprise: passing a gaseous feed stream through the self-supporting structure disposed in an interior region of a housing of the adsorbent bed unit to remove one or more contaminants from the gaseous feed stream, wherein the self-supporting structure has greater than 50% by weight of the active material in the self-supporting structure, wherein the self-supporting structure is a foam-geometry structure configured to provide one or more tortuous channels for fluid flow paths through the self-supporting structure; b) performing one or more regeneration steps, wherein each of the one or more regeneration steps comprise conducting away at least a portion of the one or more contaminants in a contaminant output stream; and c) repeating the steps a) to b) for at least one additional cycle.


Further, in one or more embodiment, the method for removing contaminants from a feed stream may include various enhancements. For example, the method may be a swing adsorption method and the cycle duration may be for a period greater than 1 second and less than 600 seconds or a period greater than 1 second and less than 300 seconds; wherein the performing one or more regeneration steps comprises performing one or more purge steps, wherein each of the one or more purge steps comprise passing a purge stream through the self-supporting structure to conduct away at least a portion of the one or more contaminants in the contaminant output stream; wherein the gaseous feed stream may be a hydrocarbon containing stream having greater than one volume percent hydrocarbons based on the total volume of the gaseous feed stream; wherein a feed pressure of the gaseous feed stream may be in the range between 400 pounds per square inch absolute (psia) and 1,400 psia; wherein performing the one or more adsorption steps may be configured to lower the carbon dioxide (CO2) level to less than 50 parts per million volume; wherein performing the one or more adsorption steps may be configured to lower the water (H2O) level to less than 105 parts per million volume; and/or the self-supporting structure has a low thermal mass.


In yet another embodiment, a method of manufacturing a processing unit is described. The method may include: mixing an active material with a binder material, wherein the mixture has greater than 50% by weight of the active material and the remaining mixture includes binder material; forming a self-supporting structure from the mixture, wherein the self-supporting structure is a foam-geometry structure configured to provide one or more tortuous channels for fluid flow paths through the self-supporting structure; drying the self-supporting structure and disposing the self-supporting structure within housing of a processing unit having an interior region.


Moreover, in one or more embodiment, the method of manufacturing a processing unit may include various enhancements. For example, the method may include sintering the binder material and active material into a cohesive solid structure that is the self-supporting structure; wherein the sintering further comprises exposing the self-supporting structure to temperatures in the range between 400° C. and 800° C. and/or may include creating a plurality of valve ports into the housing; and securing a valve to the housing in each of the plurality of valve ports to form a plurality of valves, wherein each of the plurality of valves is configured to control fluid flow between the self-supporting structure and a location external to the housing.





BRIEF DESCRIPTION OF THE FIGURES

The foregoing and other advantages of the present disclosure may become apparent upon reviewing the following detailed description and drawings of non-limiting examples of embodiments.



FIG. 1 is a flow diagram of a method for fabricating and using a self-supporting structure in accordance with an embodiment of the present techniques.



FIG. 2 is a flow diagram of a method for fabricating a self-supporting structure in accordance with an embodiment of the present techniques.



FIGS. 3A, 3B and 3C are diagrams associated with self-supporting structures in accordance with an embodiment of the present techniques.



FIG. 4 is a diagram of the weight loss for 3A, due to loss of adsorbed water, as a function of temperature.



FIGS. 5A to 5D are diagrams of various profiles.



FIG. 6 is a three-dimensional diagram of the swing adsorption system with six adsorbent bed units and interconnecting piping in accordance with an embodiment of the present techniques.





DETAILED DESCRIPTION OF THE INVENTION

Unless otherwise explained, all technical and scientific terms used herein have the same meaning as commonly understood by one of ordinary skill in the art to which this disclosure pertains. The singular terms “a,” “an,” and “the” include plural referents unless the context clearly indicates otherwise. Similarly, the word “or” is intended to include “and” unless the context clearly indicates otherwise. The term “includes” means “comprises.” All patents to and publications mentioned herein are incorporated by reference in their entirety, unless otherwise indicated. In case of conflict as to the meaning of a term or phrase, the present specification, including explanations of terms, control. Directional terms, such as “upper,” “lower,” “top,” “bottom,” “front,” “back,” “vertical,” and “horizontal,” are used herein to express and clarify the relationship between various elements. It should be understood that such terms do not denote absolute orientation (e.g., a “vertical” component can become horizontal by rotating the device). The materials, methods, and examples recited herein are illustrative only and not intended to be limiting.


As used herein, “majority component” means greater than 50% by weight.


As used herein, “foam-geometry” refers to structures having open channel networks, compared to extruded solid shapes, such as spheres or pellets. The foam-geometry structures include monoliths or other engineered structures that provide flow paths through tortuous channels or passages in the respective structure. The foam-geometry structures includes a network of interconnected voids surrounded by a web of struts.


As used herein, “stream” refers to a fluid (e.g., solids, liquid and/or gas) being conducted through various equipment. The equipment may include conduits, vessels, manifolds, units or other suitable devices.


As used herein, volume percent is based on standard conditions. The standard conditions for a method may be normalized to the temperature of 0° C. (Celsius) (e.g., 32° F. (Fahrenheit)) and absolute pressure of 100 kiloPascals (kPa) (1 bar).


The present techniques relate to the fabrication of self-supporting structures from active material, which may be foam-geometry structures that have tortuous flow paths. In particular, the present techniques relate to enhancements in the self-supporting structures that contain a majority of active material (e.g., greater than 50% by weight or greater than or equal to 60% by weight) to provide enhanced structures. The enhanced structures may provide flexibility through configurations, which may enhance the interaction of the stream with the active material through the tortuous flow paths and provide higher volumetric efficiency in the configurations, which are lighter in weight than conventional structures. The self-supporting structures may be configured to have various tortuous channels to provide fluid flow paths through the self-supporting structure.


The self-supporting structures may be useful in various chemical and engineering applications. By way of example, certain methods may be enhanced with the active materials, such as adsorption and catalytic processes. In particular, a self-supporting structure may be used instead of a packed adsorbent bed, which have higher pressure drops and slower mass transfer rates. In the packed bed configurations, the pressure drops and mass transfer limitations do not permit or are inefficient in operating the adsorption or catalytic processes at rapid cycles. Further, large volume gas separation processes, which rely upon pressure swing adsorption and rapid cycling, involve self-supporting structures with low pressure drop and high volumetric efficiency. The present techniques may provide enhancements to the associated structures to enhance the respective method and associated economics.


The self-supporting structure may be fabricated from various techniques, such as foam techniques. By way of example, the fabrication method may include a polymeric sponge method and a direct foaming method. The polymeric-sponge method produces open-cell structures by impregnating a polymeric sponge with a slurry, which is then burned out to leave a porous structure. The direct foaming method uses a mixture containing the desired component and organic materials, which on processing, causes foaming and evolves a gas. A resulting porous material is then dried and fired.


As an additional example, the present techniques may include providing a self-supported foam structure of a mixture having a foam-like geometry, wherein the self-supported structure includes a network of interconnected voids and struts, wherein the mixture has greater than 50% by weight of active material in the self-supporting structure and the remaining mixture includes binder material. The self-supporting structure may be a foam-geometry structure forming various tortuous paths through the respective structure. Once formed, the self-supporting structure may be dried and then be subjected to a calcining process. The calcining process may involve temperatures in the range between 400° C. and 800° C. to form a mechanically stable, active structure. The foam network of the self-supporting structure may provide higher external surface area and a tortuous path for gas flow compared to laminar flow extruded monoliths. Further, the pore density of the self-supported structure may be in the range between 10 pores per linear inch (ppi) and 100 ppi, in the range between 15 ppi and 60 ppi or in the range between 20 ppi and 40 ppi.


In other configurations, the self-supporting structure may include different layers or sheets of materials disposed adjacent to each other. The first sheets may have a first composition and a first pore density and the second sheets may have a second composition and second pore density. The first pore density is in the range from 1 pores per linear inch (ppi) to 20 ppi, in the range from 3 ppi to 17 ppi or in the range from 5 ppi to 15 ppi. The second pore density is in the range from 20 ppi to 100 ppi, in the range from 30 ppi to 70 ppi or in the range from 30 ppi to 60 ppi. Further, the first composition and the second composition may be different and the first composition may provide additional rigidity to the self-supporting structure. The first sheet may be configured to distribute the fluid stream from the respective first sheet into one of the second sheets. Further, the self-supporting structure may include additional layers or strips that is configured to distribute the fluid stream, such as diverting fluid flow into one or more of the first sheets.


The fabrication methods may utilize active materials, such as active inorganic materials, that are stable to high temperature calcinations (e.g., equal to or greater than 500° C.) and combination of organic and inorganic binders.


The present techniques may also include a foam method to produce bulk foam structures, which have the active material as the majority component. In contrast, conventional techniques involve applying a thin coating of active material to an inactive substrate, such as an inert ceramic or metal substrates. The inactive substrate, which typically provides mechanical support for the thin coating of active material, is more than 90% of the total weight of the self-supporting structure. Accordingly, the thin coating of active material in conventional self-supporting structures equal to or less than 10% of the total weight of the self-supporting structure.


In certain configurations, the self-supporting structure may include different combinations of active material and binder material. For example, the self-supporting structure may be fabricated from a microporous zeolites, which may be the active material. In certain configurations, the active material may be greater than or equal to 25% by weight of the self-supporting structure; greater than or equal to 40% by weight of the self-supporting structure; greater than or equal to 50% by weight of the self-supporting structure; greater than or equal to 60% by weight of the self-supporting structure; or greater than or equal to 70% by weight of the self-supporting structure; while the remaining portion may include binder material. In other configurations, the binder material may be less than 75% by weight of the self-supporting structure; less than 60% by weight of the self-supporting structure; less than 50% by weight of the self-supporting structure; less than 40% by weight of the self-supporting structure; or less than 30% by weight of the self-supporting structure; while the remaining portion may include active material.


The self-supporting structure may include higher masses of active material per unit volume that is greater than conventional coating techniques. For example, the layer or thickness of active material that is greater than 10 micrometers, is greater than 100 micrometers or is greater than 200 micrometers.


The active materials may include one or more adsorbent materials in certain configurations to adsorb contaminants from the stream. By way of example, the active materials may include zeolites, aluminophosphate molecular sieves (e.g., AlPOs and SAPOs), ZIFs (zeolitic imidazolate frameworks (e.g., ZIF-7, ZIF-9, ZIF-8, ZIF-11, etc.) and carbons, as well as mesoporous materials, such as the amine functionalized MCM materials (e.g., Mobil Composition of Matter or Mobil Crystillaine Material, such as MCM-22, MCM-41 or MCM-48), SBA materials, KIT materials and/or other suitable structures. Other example of active materials may include cationic zeolites, amine-functionalized mesoporous materials, stannosilicates, and/or carbons. In other configurations, the adsorbent materials may include zeolite type A (e.g., Linde type A (LTA) structures), such as 3A, 4A, 5A and/or 13X (which are highly porous adsorbents that have a high affinity and high capacity to adsorb water, as well as other molecules that have dimensions small enough to fit into the uniform pores of these structures), 8-member ring zeolite materials (e.g., ZSM 58 and/or DDR).


In other configurations, the active material may include one or more catalytic materials that are configured to react with the components in the stream.


The binder material may include organic and inorganic binder. The binder may include 1% aqueous solution of polyethylene oxide or methyl cellulose derivatives. For example, the binder material may include polyethylene oxide, and/or silicon dioxide (SiO2). Silica particle diameter may be in the range between 25 nanometer and 1000 nanometer and silica particles in a string of pearls configuration.


As noted above, foam-geometry structures do not have parallel channels, such as the parallel channels in self-supported monolith structures. The foam-geometry structures have a network of interconnected voids and struts that result in a tortuous path flow, rather than laminar flow produced by parallel channel structures in monoliths. With the self-supporting structures, the external surface area per unit volume is directly associated to the mass transfer rate. The foam-geometry structures have a higher external surface area than monolith structures having defined channels and flow paths. The monoliths having defined channels and flow paths can only approximate the external surface area of foam-geometry structures if they have high cell density, such as, for example, in cell density of greater than 2000 cells per square inch. However, the high cell density reduces the voidage in a monolith substrate, which results in increased pressure drop and increased difficulty to coat the monolith substrate with active materials.


In the foam-geometry structures, the open cell ceramic foam structures include a network of interconnected voids surrounded by a web of ceramic struts, which is shown below in FIGS. 3A and 3B. The pore size of ceramic foams is defined as pores per linear inch (ppi). In contrast, a ceramic honeycomb with channels, the unit of measure is cells per square inch (cpsi). For ceramic foams, the pore sizes may range between 10 ppi and 100 ppi, 10 ppi and 80 ppi, 15 ppi and 60 ppi or 20 ppi and 40 ppi. For ceramic honeycombs used in monoliths, the cell densities generally range from 10 cpsi to 900 cpsi. The pressure drop through ceramic foam structures is between that of monoliths and packed beds.


The foam-geometry structures may be created by a polymeric sponge method and/or a direct foaming method. The polymeric-sponge method produces foam-geometry structures by impregnating a polymeric sponge with an active material slurry, which is then burned out to leave a porous material. The direct foaming method uses a mixture containing the desired active material component and organic materials, which on processing, causes foaming and evolves a gas. A resulting porous material is then dried and fired to form the self-supporting structure.


The foam-geometry structures may provide various enhancements over monolith configurations because the foam sheets are open cell structures in various directions, and the volume is small and there is no metal in the sheets. For PSA configurations, the gas streams may flow in one direction and the heat generated by the heat of adsorption may be captured and used to supplement an external heat source. Further, a heated purge stream may be used for a TSA process, with the purge stream flowing in perpendicular direction to the PSA flow.


By way of example, a processing unit may include a housing forming an interior region; a self-supporting structure disposed within the interior region, wherein the self-supporting structure has greater than 50% by weight of the active material in the self-supporting structure, wherein the self-supporting structure is a foam-geometry structure configured to provide one or more tortuous channels for fluid flow paths through the self-supporting structure; and a plurality of valves secured to the housing, wherein each of the plurality of valves is configured to control fluid flow along a flow path extending between the self-supporting structure and a location external to the housing. In various configurations, the processing unit may include two or more of the plurality of valves are operated via common actuation mechanism; the processing unit may be a cyclical swing adsorbent bed unit configured to remove contaminants from a gaseous feed stream that passes through the self-supporting structure; the self-supporting structure may have greater than 60% by weight of the active material in the self-supporting structure or the self-supporting structure may have greater than 70% by weight of the active material in the self-supporting structure; may include a flow distributor disposed between the adsorbent bed and the plurality of valves; the housing may be configured to maintain a pressure from 5 pounds per square inch absolute (psia) and 1,400 psia; wherein the self-supporting structure has pores in the range between 10 pores per inch and 100 pores per inch, pores in the range between 15 pores per inch and 60 pores per inch; or pores in the range between 20 pores per inch and 40 pores per inch and/or the self-supporting structure has a low thermal mass.


As yet another example, a method for removing contaminants from a feed stream may include: a) performing one or more adsorption steps in an adsorbent bed unit, wherein each of the one or more adsorption steps comprise: passing a gaseous feed stream through the self-supporting structure disposed in an interior region of a housing of the adsorbent bed unit to remove one or more contaminants from the gaseous feed stream, wherein the self-supporting structure has greater than 50% by weight of the active material in the self-supporting structure, wherein the self-supporting structure is a foam-geometry structure configured to provide one or more tortuous channels for fluid flow paths through the self-supporting structure; b) performing one or more regeneration steps, wherein each of the one or more regeneration steps comprise conducting away at least a portion of the one or more contaminants in a contaminant output stream; and c) repeating the steps a) to b) for at least one additional cycle. In certain configurations, the method may be a swing adsorption method and the cycle duration may be for a period greater than 1 second and less than 600 seconds or a period greater than 1 second and less than 300 seconds; wherein the performing one or more regeneration steps comprises performing one or more purge steps, wherein each of the one or more purge steps comprise passing a purge stream through the self-supporting structure to conduct away at least a portion of the one or more contaminants in the contaminant output stream; wherein the gaseous feed stream may be a hydrocarbon containing stream having greater than one volume percent hydrocarbons based on the total volume of the gaseous feed stream; wherein a feed pressure of the gaseous feed stream may be in the range between 400 pounds per square inch absolute (psia) and 1,400 psia; wherein performing the one or more adsorption steps may be configured to lower the carbon dioxide (CO2) level to less than 50 parts per million volume; wherein performing the one or more adsorption steps may be configured to lower the water (H2O) level to less than 105 parts per million volume; wherein the self-supporting structure has pores in the range between 10 pores per inch and 100 pores per inch; in the range between 15 pores per inch and 60 pores per inch or in the range between 20 pores per inch and 40 pores per inch and/or the self-supporting structure has a low thermal mass.


As yet another example, a method of manufacturing a processing unit may include: mixing an active material with a binder material, wherein the mixture has greater than 50% by weight of the active material and the remaining mixture includes binder material; forming a self-supporting structure from the mixture, wherein the self-supporting structure is a foam-geometry structure configured to provide one or more tortuous channels for fluid flow paths through the self-supporting structure; drying the self-supporting structure and/or disposing the self-supporting structure within housing of a processing unit having an interior region. Moreover, the method of manufacturing a processing unit may include various enhancements. For example, the method may include sintering the binder material and active material into a cohesive solid structure that is the self-supporting structure; wherein the sintering further comprises exposing the self-supporting structure to temperatures in the range between 400° C. and 800° C. and/or may include creating a plurality of valve ports into the housing; and securing a valve to the housing in each of the plurality of valve ports to form a plurality of valves, wherein each of the plurality of valves is configured to control fluid flow between the self-supporting structure and a location external to the housing.


Beneficially, the present techniques provide self-supporting structures that may be utilized to provide various enhancements over conventional approaches. For example, the present techniques may provide structures that provide tortuous channels or passages to promote interaction between the active material and the stream passing through the self-supporting structure. Further, by utilizing the active material to form the self-supporting structure, the working capacity may be increased and volumetric efficiency may be enhanced, which may further lessen the size of the structure and associated weight of the structure. The lessening of the size and weight may also lessen the associated size of the equipment utilized with the housing that contains the self-supporting structure. The present techniques may be further understood with reference to the FIGS. 1 to 6 below.



FIG. 1 is a flow diagram 100 of a method for fabricating and using a self-supporting structure in accordance with an embodiment of the present techniques. In this diagram 100, the method includes fabricating a self-supporting structure including active material along with using the self-supporting structure. In particular, the method may include determining a configuration for the self-supporting structure, as shown in block 102, creating a mixture for the self-supporting structure, as shown in block 104, creating the self-supporting structure as shown in blocks 106 and 108, and forming a processing unit with the self-supporting structure and utilizing the self-supporting structure in processing of feeds, as shown in blocks 110 and 112.


The method begins at block 102. In block 102, a configuration for a self-supporting structure is determined. This determination may involve modeling and identifying various aspects of the self-supporting structure to enhance process engineering selections, such as determining the mechanical features of the self-supporting structure, determining the cell size within the self-supporting structure, determining the pressure drop for flow through the self-supporting structure, determining the operating conditions that the self-supporting structure may be subject to during process operations (e.g., pressures, temperatures and stream compositions) and/or determining the contaminants to be adsorbed by the active material in the self-supporting structure.


Once the configuration for the self-supporting structure is determined, a mixture is created for the self-supporting structure, as shown in block 104. The mixture may include an active material with organic and/or inorganic binders to provide a specific formulation. The mixture, which may be an aqueous slurry. Once the mixture is created, the self-supporting structure is produced, as shown in blocks 106 and 108. At block 106, the self-supporting structure is created having a foam-geometry structure. The creation of the self-supporting structure may include provided the mixture to a container or vessel. The container or vessel may be used to perform foaming techniques on the mixture to form the struts and voids within the self-supporting structure. Then, the mixture may be processed to cure the mixture into a solid form. The processing may include heating the mixture to dry and/or cure the mixture. The method of producing active foam materials include a polymeric sponge method and a direct foaming method. The polymeric-sponge method produces open-cell structures by impregnating a polymeric sponge with an active material slurry, which is then burned out to leave a porous ceramic. The direct foaming method uses a mixture containing the desired ceramic component and organic materials, which on processing, causes foaming and evolves a gas. A resulting porous ceramic material is then dried and fired. At block 108, the created self-supporting structure may be verified. The verification of the created self-supporting structure may include using sensors to obtain measurements on the created self-supporting structure to identify voids, fractures and/or non-homogeneous sections of the created self-supporting structure. The verification may include performing a high temperature x-ray diffraction on the self-supporting structure. For example, a high temperature x-ray diffraction scan analysis may be used to determine maximum temperatures and time for calcination of the self-supporting structures.


Once the self-supporting structure is produced, the self-supporting structure is formed into a processing unit, as shown in block 110. The forming the processing unit, may involve disposing the self-supporting structure within a housing, coupling a head to the housing, coupling one or more valves (e.g., poppet valves) to the housing and coupling one or more conduits to the housing and/or one or more of the valves. The processing unit may be an adsorbent bed unit that includes a housing, which may include a head portion coupled to one or more body portions, that forms a substantially gas impermeable partition. The housing may include the self-supporting structure (e.g., formed as an adsorbent bed) disposed within an interior region enclosed by the housing. Various valves may be configured to provide fluid flow passages through openings in the housing between the interior region of the housing and locations external to the housing. Then, the self-supporting structure may be utilized in processing of fluids, as shown in block 112. For example, the processing of feeds may include performing swing adsorption method (e.g., rapid cycle processes) for the removal of one of more contaminants from a feed stream. Other examples may include utilizing the self-supporting structure in a catalytic process.


One method for forming the self-supporting structure may involve the use of foaming techniques. By way of example, the self-supporting structure may be prepared by such processes. As a result, the self-supporting structure may be a foam-geometry structure configured to provide tortuous channels for fluid flow paths through the structure.


As example of the creation of the self-supporting structure is shown in FIG. 2. FIG. 2 is a flow diagram 200 of a method for fabricating a self-supporting structure in accordance with an embodiment of the present techniques. The method begins at block 202. In block 202, a mixture of an active material and a binder material is obtained. The mixture may include an active material with organic and/or inorganic binders to provide a specific formulation. Once the mixture is obtained, the self-supporting structure is formed, as shown in block 204. The formation of the self-supporting structure may include provided the mixture to a container or vessel. The container or vessel may be used to perform foaming techniques on the mixture to form the struts and voids within the self-supporting structure. Then, the mixture may be processed to cure the mixture into a solid form. At block 206, the created self-supporting structure may be dried. Then, the self-supporting structure may be subjected to a calcination process, as shown in block 208. The method may include sintering or calcining the binder material and active material into a cohesive solid structure that is the self-supporting structure. The calcining or sintering may include exposing the self-supporting structure to temperatures in the range between 400° C. and 800° C.


Beneficially, the self-supporting structure having a foam-geometry structure provide various enhancement. For example, the foam-geometry structure provide a higher geometric surface area per unit volume than other conventional monoliths. Further, in contrast to monoliths, the foam-geometry structure provides tortuous flow paths and have a higher mass transfer rate. While the pressure drop may be higher than conventional monoliths having substantially parallel channels, the foam-geometry structure have significantly lower pressure drop than packed bed configurations. In addition, the foam-geometry structure may be formed into rectangular sheet structures to permit modular unit designs. Various diagrams of the foam structure are shown in FIGS. 3A, 3B and 3C.



FIGS. 3A, 3B and 3C are diagrams 300, 320 and 340 associated with self-supporting structures in accordance with an embodiment of the present techniques. FIGS. 3A and 3B are examples of Al2O3 ceramic foams, as shown in diagrams 300 and 320. In FIG. 3A, the diagram 300 includes various struts 302 and pores 304. In FIG. 3B, the diagram 320 includes various struts, such as strut 322, which forms cells, such as cell 324, and pores, such as pore 326. The cell 324 has a width of 330, while the pore has a width 332. The foam-geometry structure provide enhanced mass transfer performance to laminar flow monolith structures, may be easier and cheaper to produce than extruded structures, and may provide flexibility in the adsorbent bed configurations. For example, foam sheet beds for rectangular modular design, and foams made of 70% by weight of active material can reduce bed volumes. The mixture used in the resulting self-supporting structures may include 3A/SiO2 having about a 70:30 ratio of active material by weight to binder by weight for the self-supporting structure (w/w).


To cure the mixture into the self-supporting structure, the thermal stability of active material by high temperature may be assessed. As noted above, one of the final steps in creating a self-supporting structure may include calcination. Calcination at high temperatures, which may include temperatures equal to or greater than 400° C. or even equal to or greater than 500° C., dehydrates the zeolite and SiO2 particle mixture and coalesces the mixture into more dense structures that result in enhanced mechanical strength. To assess the high temperature stability of the active material (e.g., adsorbent or catalyst material) for calcination purposes, a high temperature x-ray diffraction may be performed on the self-supporting structure. For example, a high temperature x-ray diffraction scans may provide a representation to indicate that the 5A zeolite (e.g., active material) was stable at a specific temperature for a certain period of time (e.g., about 860° C. for several minutes) and then loses stability, which may be shown by decreasing peak heights. Accordingly, this type of analysis may be used to determine the maximum temperatures and time for calcination of the structures. The mechanical strength of the self-supporting structures is related to calcination temperatures greater than 500° C.


In certain configurations, the self-supporting structure may include different layers or sheets of materials intermixed and disposed adjacent to each other. The respective sheets may have different compositions and pore densities. For example, a first pore density may be in the range from 1 pores per linear inch (ppi) to 20 ppi, in the range from 3 ppi to 17 ppi or in the range from 5 ppi to 15 ppi. The second pore density may be in the range from 20 ppi to 100 ppi, in the range from 30 ppi to 70 ppi or in the range from 30 ppi to 60 ppi. In such configurations, one of the different sheets may provide additional rigidity to the self-supporting structure and may be configured to distribute the fluid stream from that respective sheet into one of the other sheets. Also, additional layers or strips may be used and may be configured to distribute the fluid stream, such as diverting fluid flow into one or more of the distribution sheets.



FIG. 3C is an example of a conceptual zeolite foam-geometry module of a self-supporting structure. This module may be utilized to process 1 million cubic feet (ft3) of CH4 containing 2 weight percent (wt. %) H2O. In FIG. 3C, the diagram 340 includes various the sheets, such as sheets 342, are 10 ppi Al2O3 structures. Each of these Al2O3 sheets may be 40 inches in width by 40 inches in length and 0.5 inches in depth. The Al2O3 sheets may be disposed between the 3A/SiO2 foam sheets, such as sheets 344. These Al2O3 uncoated sheets may act as mechanical support and for diffusing gas into the 3A/SiO2 foam sheets. The sheets 344 may be 65 ppi 3A/SiO2 active material foam-geometry sheets. Each of the 3A/SiO2 foam sheets may be 20 inches in width by 20 inches in length by 1 inch in depth. Further, the strips, such as strips 346, are stainless steel (SS) that block incoming flow from entering of the 3A/SiO2 foam sheets. The strips 346 may be 40 inches in width by 1 inch in length and 0.04 inches in depth. Further, the arrows show flow direction for PSA flows, such as arrow 348, and TSA flows, such as arrow 350.


In this configuration, the active 3A/SiO2 foam sheets may be stacked in a module and disposed between the Al2O3 foam sheets 342. The Al2O3 foam sheets have a pore density of 10 ppi, which has large pores for a low pressure drop. Incoming and outgoing gas flow may be parallel to 3A/SiO2 foam sheet surfaces. For example, the incoming gas flow may be channeled through the uncoated Al2O3 foam sheets. The Al2O3 foam sheet provides rigidity to the structure and aids with incoming gas distribution. The uncoated Al2O3 foam sheets are only 50% as thick as the 3A/SiO2 foam sheets. The effective gas flow path into the zeolite foam sheet is half the thickness. Laminates can be effective absorbents if excessive pressure drops are avoided. If the pressure drop perpendicular to the 3A/SiO2 foam sheet is small, the foam may effectively perform as a laminar sheet with a large surface area.


In this configuration, various performance metrics may be calculated. For example, the pressure drop through 1 meter of an Al2O3 foam sheet may be calculated to be less than 18 Torr for a gas velocity of 5 meters per second (m/s). The pressure drop through 1 meter of Al2O3 foam sheet may be calculated to be approximately 1.5 pounds per square inch (psi) for a gas velocity of 5 m/s. Further, the open flow area of Al2O3 foam sheets for twenty nine sheets times the 0.5 inches times 40 inches is 580 inches squared (in3) (0.374 square meters (m2)).


In addition, the amount of zeolite material may also be calculated for the structure. For this calculation, the r is 1.7 gram per cubic centimeter (gm/cm3), for the 70 wt. % zeolite and 30 wt. % SiO2 binder foam and 75% porosity are used. The volume of one sheet is 20 inches times 20 inches times 1 inch, which is 400 cubic inches (in3) (6,554.5 cubic centimeters (cm3)). The total mass of one sheet is 6,554.8 cm3 times 1.7 gm/cm3 times 0.25 (solid), which is 2,786 grams per sheet (gm/sheet). The total mass of 3A zeolite in one sheet is 2,786 gm/sheet times 0.7, which is 1,950 gm/sheet.


The amount of H2O adsorption may also be calculated for the structure. In this calculation, a conservative estimate of 10 wt. % H2O loading per sheet is 195 gm/sheet. For 2 wt. % H2O in 1 million cubic feet of CH4 is 412,782 gm. The number of sheets needed is 412,782 gm divided by 195 gm/sheet, which is 2,117 sheets. Each module has four sheets per layer times 28 layers, which is 112 sheets. As a result, the total modules needed is 2,117 sheets divided by 112 sheets/module, which is 18.9 modules.


Further, the estimated volume may also be calculated. The number of 3A/SiO2 foam sheets needed for 19 modules is 19 modules times 112 sheets/module, which is 2,128 sheets. The module volume with 29 Al2O3 sheets and 28 3A/SiO2 foam sheets is 42.5 inches times 40 inches times 40 inches, which is 68,000 cubic inches (in3) (1.114 m3). The total volume of 19 modules times 1.114 m3 is 21.166 m3. Then, in converting this to gallons, the amount is 21,166 liter is 5,591.5 gallons. Accordingly, the estimated volume (in gallons) of 19 module of the foam-geometry structure is 5,591 gallons.


The self-supporting structures, which may be foam-geometry active material monoliths, formed by the present techniques are made to be formed from 70% by weight of active material, calcined to much lower temperatures than ceramics (e.g., calcined to 400° C. to 800° C.). The lower temperatures are utilized to maintain activity of the zeolite. The strength for the resulting self-supporting structures is provided by the inorganic SiO2 binder. However, the self-supporting structures, while mechanically stable, are not as strong as ceramic monoliths. While clay may be used as a binder for zeolites, it does not provide the strength of sintered SiO2.


As a selection for the active material, the zeolite type A (e.g., LTA structures), such as 3A, 4A and/or 5A, are highly porous adsorbents that have a high affinity and high capacity to adsorb water, as well as other molecules that have dimensions small enough to fit into the uniform pores of these structures. Accordingly, processes that involve drying and purification of gases and liquids rely on the adsorption capacity and efficiency of LTA-type zeolites, such as swing adsorption methods. These 3A, 4A, 5A LTA-type zeolites have the ability to readily adsorb water over a wide range of conditions. They also release the adsorbed water when heated, without the zeolite structure degrading. Thus, they have the ability to cycle between releasing water when heated and readsorbing water upon cooling.


The use of 3A in water desorption is shown in relation to a thermogravimetric analysis (TGA). The TGA was performed by starting with a 3A zeolite powder without binder additives. The TGA experiment yields data on weight loss to the sample versus temperature, as shown in FIG. 4.



FIG. 4 is a diagram 400 of the weight loss for 3A, due to loss of adsorbed water, as a function of temperature. In this diagram 400, a first response 408 and a second response 410 are shown along a time axis 402 in minutes (min), a weight percentage axis 404 in percent and a temperature axis 406 in ° C. The sample was heated in air from 30° C. to 600° C., at a rate of 10° C. per minute, as shown along the second response 410. The first response 408 represents a total weight loss of 15.3%, indicating that the 3A powder had adsorbed 15.3% by weight of water at ambient conditions. The adsorbed water was removed from the sample at 280° C. (e.g., 25 minutes times 10° C./minute plus 30° C. starting temperature).


Further enhancements may be described by comparing H2O desorption in 3A powder with H2O adsorption in a 500° C. calcined 3A/SiO2 intrusion structure, which is also expected to perform similar to the foam-geometry structure. As noted below, Table 1 compares the water adsorption in a calcined 3A/SiO2 (e.g., 70:30 w/w) structure, to the water desorption results in response 408 of FIG. 4 on the 3A powder.



















TABLE 1












3A in

3A powder
Agreement







Wt

structure
3A wt. %
TGA result
between


3A/Si02
3A



increase

(dry.
increase
(above) wt.
TGA wt. loss


structure
wt. (%)

Si02
Structure
due to
Wt. %
500° C. +
due to
loss due to
and structure


wt. after
in
3A wt.
wt
wt. after
H20
increase in
H2O
H20
H20
H2O uptake


500° C.
3A/SiO2
calcd.
calcd
3 dsys RT
uptake
3A/SiO2
uptake
uptake
desorption
(% of


(grams)
sturcture
(grams)
(grams)
(grams)
(grams)
sturcture
(grams)
(%)
(%)
agreement)







20.560
70%
14.392
6.168
22.837
2.217
11.07%
16.609
15.4%
15.3%
99.3%









In Table 1, the 3A/SiO2 structure is a 70:30 w/w 3A:SiO2 laminar sheet. The structure was calcined to 500° C. to decompose organic binder and sinter the 3A and SiO2 25 nm particles together. The 3A/SiO2 laminar sheet structure was stored in a 120° C. furnace, after 500° C. calcination process. The 3A component of the structure was expected to have no adsorbed water. The 3A/SiO2 structure, which is 1 inch diameter by 2 inch length, was weighed at 120° C. from the furnace and its weight, as recorded in Table 1 was 20.560 grams, which has 70% of the 20.560 gram total weight, or 14.392 grams is the 3A component. The remaining 30% of the 20.560 grams of total weight, or 6.168 grams, is the 25 nm diameter SiO2 binder particles.


After weighing the 3A/SiO2 structure devoid of water (H2O), the structure was exposed on a lab bench for seventy-two hours to ambient conditions. After seventy-two hours of being exposed to ambient conditions, the 3A/SiO2 structure was re-weighed, and its weight was 22.837 grams. This increase in weight was 11.07%, which is a result of adsorbing 2.217 grams of water from the ambient air. The majority of the water could only be adsorbed by the 3A component in the 3A/SiO2 structure. When determining the water uptake for the 3A component of the structure, it corresponds to a 15.4% weight increase. This weight increase is similar to the 15.3% weight loss in 3A powder, due to water desorption in response 408 of FIG. 4. As a result, the weight increase in the 3A/SiO2 laminar sheet structure indicates that the 3A component in the structure is accessible to the water molecules.


For examples, the 3A component in the 3A/SiO2 structure is porous. The windows or pores of the 3A structure have openings of 3 angstroms size. Water molecules have a diameter of about 2.8 angstroms and may fit into the 3A structure or adsorbed to the inside of the 3A structure. The SiO2 binder is non-porous. The SiO2 spheres do not have pores and thus, do not adsorb water into its structure. The water can wet the surface of the SiO2 spheres, but that amount of water may be a very small fraction of the total amount of water that could be adsorbed by a 3A zeolite (70 wt %)/SiO2 (30 wt %) structure. Thus, the 3A zeolite component is the primary material to adsorb water in the 3A/SiO2 composite structure. TGA (thermal gravimetric analysis) measures weight loss versus temperature. FIG. 4 is the TGA analysis of 3A zeolite only. It shows that the 3A powder lost 15.3% of weight, which is due to desorbing the water that it adsorbed under ambient conditions.


From the example above, this TGA result on 3A zeolite powder is approximately equal to the 15.4% weight gain in the 3A/SiO2 structure in the example due to adsorption of water under ambient conditions. The nearly identical TGA desorption (weight loss) result and adsorption (weight gain) result in the 3A/SiO2 structure shows that the 3A zeolite component was accessible to the water. These results indicate that the SiO2 binder does not block access to the 3A crystals. Accordingly, the 3A/SiO2 structure does not hinder access to the 3A component.


As an additional enhancement, gas adsorption break-through tests were also performed on the self-supporting structures. A gas adsorption break-through unit, which is referred to as NatGas Unit, was used to measure gas adsorption and break-through profiles of coated substrates. A sample of known weight is wrapped to prevent gas bypass and inserted into a tube in the gas adsorption break-through unit. The samples are exposed to a total 1000 standard cubic centimeters per minute (sccm) gas flow rate, comprised of 300 sccm N2 saturated with H2O at 25° C., 100 sccm He and 600 sccm N2. The gas break-through is monitored by a mass spectrometry. The gas flow measurement term of sccm represents cubic centimeters per minute (cm3/min) at standard temperature and pressure.


As part of this testing, an aqueous slurry with 35 wt % solids, comprised of 3A/SiO2 (70:30) and methyl cellulose (temporary organic binder), was formulated, as described above in the example 3A/SiO2 slurry preparation. The slurry was applied to an Al2O3 ceramic monolith, which has dimensions suitable for testing in the gas adsorption break-through unit. The washcoat on the ceramic monolith had a similar composition to the self-supported structures after calcination. Thus, the 3A/SiO2 washcoated monolith was used as a suitable surrogate for the self-supporting foam structures and, hence, breakthrough results should be and are expected to be comparable.


In this testing, the 900 cpsi Al2O3 monoliths had dimensions of 0.5 inch diameter by 1 inch length, 30% wall porosity and 55% open frontal area. The starting, uncoated weight of the monolith was 4.099 gram. Two coatings of the slurry were applied by conventional washcoating techniques and the sample was dried and calcined to 500° C. The sample weight after calcination was 4.893 grams. The resulting 3A/SiO2 (25 nm diameter) washcoated monolith contained approximately 0.556 gram of 3A adsorbent and was a representative sample for formulations used in self-supporting foam-geometry structures. Prior to break-through testing, the 3A/SiO2 coated monolith was dried for twelve hours at 150° C. and 100 sccm He flow.



FIGS. 5A and 5B are diagrams 500 and 520 of break-through profiles. The breakthrough profile is reasonably sharp. In FIG. 5A, the He response 506 and H2O response 508 are shown along a time axis 502 in minutes (mins) versus a mass spectrometer axis 504 in counts per second (c/s) to water. The estimated rate of water feed is 5.48 milligrams (mg) per minutes (min). The estimated time for 0.55 grams of 3A in the 3A/SiO2 washcoat to adsorb water before break-through is 25 minutes (e.g., 30 minutes at uptake level off minus 5 minutes at beginning of uptake). The response 506 represents a blank trace (e.g., no sample), which from time 0 to 50 minutes of dry He purge and the response 506 is flat and near the baseline, indicating no counts for H2O. Then, after 50 minutes, the valve switches to feed humidified He. The response 506 rises vertically as the mass spectrometer shows increasing counts per second of H2O, until the H2O is removed at 300 minutes. Then, the response 506 returns to the baseline indicating no counts of H2O. The response 508 shows a shows a similar experiment through a sample of 3A/SiO2 coated onto Al2O3 ceramic monolith. As indicated by this response 508, it is about 5 minutes longer for the response 508 to rise as compared to the response 506 for the blank sample, which indicates that H2O breakthrough is being slowed by the adsorption of H2O in the 3A component until the sample reaches water saturation and equilibrium.


In FIG. 5B, the He response 526 and H2O response 528 are shown along a time axis 522 in minutes versus a normalized fractional concentration of H2O axis 524 in normalized concentration (C/Co), which expresses the normalized fractional concentration of H2O being measured by a mass spectrometer as a function of time axis 522 in minutes (mins). In this diagram 520, the 3A adsorbs water for about 25 minutes, indicating that the 3A adsorbent particles are accessible without signs of major diffusional hindrance. The response 526 represents a dry He purge passing through an empty cell for 5 minutes, which is flat and near the baseline. Once a valve is switched to feed humidified He stream, the mass spectrometer indicates a breakthrough of the He at time 0 minutes. In comparison, the response 528 represents a sample cell with 3A/SiO2 washcoated ceramic monolith responding to a humidified He flow. The response 528 indicates the normalized H2O concentration versus time. Accordingly, it indicates that it takes several minutes (e.g., about 25 minutes) until the 3A component in the sample is saturated with H2O and the full concentration (100%) of H2O is indicated by the mass spectrometer.



FIGS. 5C and 5D are diagrams 540 and 560 of transition feed versus purge temperature profiles. In this diagrams 540 and 560, ceramic monoliths perform than the metal monoliths. The ceramic materials should perform similar to the self-supported active structures, which have a low thermal mass structures similar to ceramics and should exhibit similar thermal swing advantages. Further, the self-supported structures of the present techniques are composed of a majority of active material, which is the material that the thermal swing.


In the diagrams 540 and 560, a cyclic process was used that involved fluid flows for 20 seconds each for feed and purge steps of the cycle. The gas flow rates were 14 standard cubic feed per minute (scfm) for feed gas and 22 scfm for purge gas. Nitrogen gas was used for feed and purge streams, which were introduced at opposite ends of the monoliths or adsorbent bed. The feed stream was at ambient temperature, while the purge stream was at 180° C. To monitor the temperature, fast response thermocouples were used to measure and store the temperatures, which had a first thermocouple positioned to measure temperatures at the feed gas inlet side of the structure and a second thermocouple positioned to measure temperatures at the purge gas inlet side of feed gas.


In FIG. 5C, the temperature responses 546 and 548 are shown along a time axis 542 in seconds (e.g., 1 second data recordings) versus a temperature axis 544 in ° C. The metal monolith used as a sample bed were three monoliths of 0.75 inches in diameter by 2 inches in length, made of stainless steel, with cell density greater than 1000 cell per square inch (cpsi), with 50 micron thick cell walls and a center steel arbor of ⅜ inch diameter. The monolith cells were coated with thin layer of adsorbent and the monoliths were wrapped with fibrous insulation to prevent gas bypass. The resulting structure was loaded into a sample tube. The diagram 540 with temperature responses 546 and 548 for the metal monoliths indicate a large temperature gap of approximately 70° C. in responding to temperature transitions between 180° C. purge gas and ambient temperature feed gas. This indicates that the metal monolith is adsorbing significant heat into the structure.


In FIG. 5D, the temperature responses 566 and 568 are shown along a time axis 562 in seconds versus a temperature axis 564 in ° C. The ceramic monolith used as a sample bed includes the monoliths of 0.75 inch diameter and 2 inch length, made of alumina ceramic, with cell density of 900 cpsi, with 100 micron thick cell walls, no center arbor. Ceramic monoliths were wrapped with fibrous insulation to prevent gas bypass. The resulting structure was loaded into a sample tube. The diagram 560 with the temperature responses 566 and 568 for the alumina ceramic monoliths indicate that the temperature transitions during the temperature cycle has a smaller temperature change than the metal monolith, as shown in FIG. 5C. The temperature gap in the responses 566 and 568 for the ceramic monoliths is approximately 20° C. during cycling process. This indicates that the ceramic monoliths adsorb less heat into the structure than the metal monoliths, as shown in FIG. 5C.


Testing may be performed on the self-supporting structure. For example, an ambient air exposure test may be performed, which is a passive test. There is no driving force to add water to the 3A/SiO2 structure. It slowly adsorbs water from the air and it is affected by conditions of relative humidity and temperature, which are measured. This test delivers a calibrated flow of gas in sccm with known concentration of water and monitors the time until the 3A/SiO2 structure has adsorbed water to its capacity. There is a mass spectrometer instrument monitoring the exit gas stream from the structure. The mass spectrometer instrument is monitoring water in the gas versus time. When water is detected, which is referred to as “breakthrough”, it indicates that the 3A component of structures is saturated with water at these specific conditions and may not adsorb more water.


In certain configurations, the present techniques may be utilized in a swing adsorption method (e.g., a rapid cycle process) for the removal of one of more contaminants from a feed stream. In particular, the present techniques involve a one or more adsorbent bed units to perform a swing adsorption method or groups of adsorbent bed unit configured to perform a series of swing adsorption methods. Each adsorbent bed unit is configured to perform a specific cycle, which may include an adsorption step and a regeneration step. By way of example, the steps may include one or more feed steps, one or more depressurization steps, one or more purge steps, one or more recycle steps, and one or more re-pressurization steps. The adsorption step may involve passing a feed stream through the adsorbent bed to remove contaminants from the feed stream. The regeneration step may include one or more purge steps, one or more blowdown steps, one or more heating steps and/or one or more repressurization steps.


The present techniques may also include active materials that are configured to perform at various operating conditions. For example, the feed pressure may be based on the preferred adsorption feed pressure, which may be in the range from 400 pounds per square inch absolute (psia) to 1,400 psia, or in the range from 600 psia to 1,200 psia. Also, the purge pressure may be based on the sales pipeline pressure, which may be in the range from 400 psia to 1400 psia or in the range from 600 psia to 1200 psia.


By way of example, FIG. 6 is a three-dimensional diagram of the swing adsorption system 600 having six adsorbent bed units and interconnecting piping. While this configuration is a specific example, the present techniques broadly relate to adsorbent bed units that can be deployed in a symmetrical orientation, or non-symmetrical orientation and/or combination of a plurality of hardware skids. Further, this specific configuration is for exemplary purposes as other configurations may include different numbers of adsorbent bed units. In this configuration, the adsorbent bed units may include self-supporting structures.


In this system, the adsorbent bed units, such as adsorbent bed unit 602, may be configured for a cyclical swing adsorption method for removing contaminants from feed streams (e.g., fluids, gaseous or liquids). For example, the adsorbent bed unit 602 may include various conduits (e.g., conduit 604) for managing the flow of fluids through, to or from the adsorbent bed within the adsorbent bed unit 602. These conduits from the adsorbent bed units 602 may be coupled to a manifold (e.g., manifold 606) to distribute the flow of the stream to, from or between components. The adsorbent bed within an adsorbent bed unit may separate one or more contaminants from the feed stream to form a product stream. As may be appreciated, the adsorbent bed units may include other conduits to control other fluid steams as part of the process, such as purge streams, depressurizations streams, and the like. Further, the adsorbent bed unit may also include one or more equalization vessels, such as equalization vessel 608, which are dedicated to the adsorbent bed unit and may be dedicated to one or more step in the swing adsorption process.


In certain configurations, the self-supporting structure may be utilized in an adsorbent bed unit that includes a housing, which may include a head portion and other body portions, that forms a substantially gas impermeable partition. The housing may include the self-supporting structure (e.g., formed as an adsorbent bed) disposed within the housing and a plurality of valves (e.g., poppet valves) providing fluid flow passages through openings in the housing between the interior region of the housing and locations external to the interior region of the housing. Each of the poppet valves may include a disk element that is seatable within the head or a disk element that is seatable within a separate valve seat inserted within the head (not shown). The configuration of the poppet valves may be any variety of valve patterns or configuration of types of poppet valves. As an example, the adsorbent bed unit may include one or more poppet valves, each in flow communication with a different conduit associated with different streams. The poppet valves may provide fluid communication between the adsorbent bed and one of the respective conduits, manifolds or headers. The term “in direct flow communication” or “in direct fluid communication” means in direct flow communication without intervening valves or other closure means for obstructing flow. As may be appreciated, other variations may also be envisioned within the scope of the present techniques.


The adsorbent bed comprises adsorbent material formed into the self-supporting structure, which is capable of adsorbing one or more components from the feed stream. Such adsorbent materials are selected to be durable against the physical and chemical conditions within the adsorbent bed unit and can include metallic, ceramic, or other materials, depending on the adsorption process.


In certain configurations, the swing adsorption system, which includes the active material, may process a feed stream that predominately comprises hydrocarbons along with one or more contaminants. For example, the feed stream may be a hydrocarbon containing stream having greater than one volume percent hydrocarbons based on the total volume of the feed stream. Further, the feed stream may include hydrocarbons along with H2O, H2S, and CO2. By way of example, the stream may include H2O as one of the one or more contaminants and the gaseous feed stream may comprise H2O in the range of 50 parts per million (ppm) molar to 1,500 ppm molar; or in the range of 500 ppm to 1,500 ppm molar. Moreover, the feed stream may include hydrocarbons and H2O, wherein the H2O is one of the one or more contaminants and the feed stream comprises H2O in the range of two ppm molar to saturation levels in the feed stream.


In addition, the present techniques may provide an adsorption system that utilizes a rapid cycle swing adsorption method to separate acid gas contaminants from feed streams, such as acid gas from hydrocarbon streams. Acid gas removal technology may be useful for gas reserves exhibit higher concentrations of acid gas (e.g., sour gas resources). Hydrocarbon feed streams vary widely in amount of acid gas, such as from several parts per million acid gas to 90 volume percent (vol. %) acid gas. Non-limiting examples of acid gas concentrations from exemplary gas reserves include concentrations of at least: (a) 1 vol. % H2S, 5 vol. % CO2, (b) 1 vol. % H2S, 15 vol. % CO2, (c) 1 vol. % H2S, 60 vol. % CO2, (d) 15 vol. % H2S, 15 vol. % CO2, and (e) 15 vol. % H2S, 30 vol. % CO2. Accordingly, the present techniques may include equipment to remove various contaminants, such as H2S and CO2 to desired levels. In particular, the H2S may be lowered to levels less than 4 ppm, while the CO2 may be lowered to levels less than 1.8 molar percent (%) or, preferably, less than 50 ppm. As a further example, the acid gas removal system may remove CO2 to LNG specifications (e.g., less than or equal to 50 parts per million volume (ppmv) CO2).


In certain configurations, the active material may be used in a rapid cycle swing adsorption method, such as a rapid cycle PSA process, to remove moisture from the feed stream. The specific level may be related to dew point of desired output product (e.g., the water content should be lower than the water content required to obtain a dew point below the lowest temperature of the stream in subsequent process and is related to the feed pressure). As a first approximation, and not accounting for fugacity corrections as a function of pressure, the water concentration in ppm that yields a certain dew point varies inversely with the pressure. For example, the output stream from the adsorbent bed may be configured to be the cryogenic processing feed stream, which satisfies the cryogenic processing specifications (e.g., approximately −150° F. (−101.1° C.) dew point for natural gas liquid (NGL) processes or approximately −60° F. (−51.1° C.) for Controlled Freeze Zone (CFZ) processes. The cryogenic processing feed stream specification may include a water content in the stream (e.g., output stream from the adsorbent bed or feed stream to the to be cryogenic processing) to be in the range between 0.0 ppm and 10 ppm, in the range between 0.0 ppm and 5.0 ppm, in the range between 0.0 ppm and 2.0 ppm, or in the range between 0.0 ppm and 1.0 ppm. The resulting output stream from the adsorbent beds during the purge step may include a water content in the stream to be in the range between 0.0 ppm and 7 pounds per standard cubic feet (lb/MSCF).


In one or more embodiments, the present techniques can be used for any type of swing adsorption method. Non-limiting swing adsorption methods for which the present techniques may include pressure swing adsorption (PSA), vacuum pressure swing adsorption (VPSA), temperature swing adsorption (TSA), partial pressure swing adsorption (PPSA), rapid cycle pressure swing adsorption (RCPSA), rapid cycle thermal swing adsorption (RCTSA), rapid cycle partial pressure swing adsorption (RCPPSA), as well as combinations of these methods, such as pressure and/or temperature swing adsorption. Exemplary kinetic swing adsorption methods are described in U.S. Patent Application Publication Nos. 2008/0282892, 2008/0282887, 2008/0282886, 2008/0282885, 2008/0282884, 2014/0013955, 2017/0056810, 2017/0056813, 2017/0056814 and 2017/0056815, which are each herein incorporated by reference in their entirety. However, rapid cycle may be preferred to process the stream. However, the self-supporting structures may be preferably utilized with rapid cycle swing adsorption methods.


Further, in certain configurations of the system, the present techniques may include a specific process flow to remove contaminants, such as water (H2O) or acid gas, in the swing adsoprtion system. For example, the method may include an adsorbent step and a regeneration step, which form the cycle. The adsorbent step may include passing a feed stream at a feed pressure and feed temperature through an adsorbent bed unit having an active material structure to separate one or more contaminants from the feed stream to form a product stream. The feed stream may be passed through the adsorbent bed in a forward direction (e.g., from the feed end of the adsorbent bed to the product end of the adsorbent bed). Then, the flow of the feed stream may be interrupted for a regeneration step. The regeneration step may include one or more depressurization steps, one or more purge steps and/or one or more re-pressurization steps. The depressurization steps may include reducing the pressure of the adsorbent bed unit by a predetermined amount for each successive depressurization step, which may be a single step and/or may be a blowdown step. The depressurization step may be provided in a forward direction or may preferably be provided in a countercurrent direction (e.g., from the product end of the adsorbent bed to the feed end of the adsorbent bed). The purge step may include passing a purge stream into the adsorbent bed unit, which may be a once through purge step and the purge stream may be provided in countercurrent flow relative to the feed stream. The purge product stream from the purge step may be conducted away and recycled to another system or in the system. Then, the one or more re-pressurization steps may be performed, wherein the pressure within the adsorbent bed unit is increased with each re-pressurization step by a predetermined amount with each successive re-pressurization step. Then, the cycle may be repeated for additional feed streams and/or the cycle may be adjusted to perform a different cycle for a second configuration. The cycle duration may be for a period greater than 1 second and less than 600 seconds, for a period greater than 2 second and less than 300 seconds, for a period greater than 2 second and less than 200 seconds, or for a period greater than 2 second and less than 90 seconds.


Also, the present techniques may be integrated into a various configurations, which may include a variety of compositions for the streams. Adsorptive separation methods, apparatus, and systems, as described above, are useful for development and production of hydrocarbons, such as gas and oil processing. Particularly, the provided methods, apparatus, and systems are useful for the rapid, large scale, efficient separation of a variety of target gases from gas mixtures. In particular, the methods, apparatus, and systems may be used to prepare feed products (e.g., natural gas products) by removing contaminants and heavy hydrocarbons (e.g., hydrocarbons having at least two carbon atoms). The provided methods, apparatus, and systems are useful for preparing gaseous feed streams for use in utilities, including separation applications. The separation applications may include dew point control; sweetening and/or detoxification; corrosion protection and/or control; dehydration; heating value; conditioning; and/or purification. Examples of utilities that utilize one or more separation applications include generation of fuel gas; seal gas; non-potable water; blanket gas; instrument and control gas; refrigerant; inert gas; and/or hydrocarbon recovery.


To provide fluid flow paths through the self-supporting structure in an adsorbent bed unit, valve assemblies may include poppet valves, which each may include a disk element connected to a stem element which can be positioned within a bushing or valve guide. The stem element may be connected to an actuating means, such as actuating means, which is configured to have the respective valve impart linear motion to the respective stem. As may be appreciated, the actuating means may be operated independently for different steps in the method to activate a single valve or a single actuating means may be utilized to control two or more valves. Further, while the openings may be substantially similar in size, the openings and inlet valves for inlet manifolds may have a smaller diameter than those for outlet manifolds, given that the gas volumes passing through the inlets may tend to be lower than product volumes passing through the outlets. Further, while this configuration has valve assemblies, the number and operation of the valves may vary (e.g., the number of valves) based on the specific cycle being performed.


In one or more embodiments, the rapid cycle swing adsorption method that utilize the self-supporting structures in the present techniques may include rapid cycle temperature swing adsorption (RCTSA) and/or rapid cycle pressure swing adsorption (RCPSA). For example, the total cycle times may be less than 600 seconds, less than 300 seconds, preferably less than 200 seconds, more preferably less than 90 seconds, and even more preferably less than 60 seconds.


In view of the many possible embodiments to which the principles of the disclosed invention may be applied, it should be recognized that the illustrative embodiments are only preferred examples of the invention and should not be taken as limiting the scope of the invention.

Claims
  • 1. A method for removing contaminants from a feed stream, the method comprising: a) performing one or more adsorption steps in an adsorbent bed unit, wherein each of the one or more adsorption steps comprise: passing a gaseous feed stream through the self-supporting structure disposed in an interior region of a housing of the adsorbent bed unit to remove one or more contaminants from the gaseous feed stream, wherein: the self-supporting structure has greater than 50% by weight of an active material in the self-supporting structure;the self-supporting structure is an foam-geometry structure configured to provide one or more tortuous channels for fluid flow paths through the self-supporting structure; anda plurality of valves are secured to the housing, wherein each of the plurality of valves is configured to control the flow of the gaseous feed stream along a flow path extending between the self-supporting structure and a location external to the housing;b) performing one or more regeneration steps, wherein each of the one or more regeneration steps comprise conducting away at least a portion of the one or more contaminants in a contaminant output stream; andc) repeating the steps a) to b) for at least one additional cycle.
  • 2. The method of claim 1, wherein the method is a swing adsorption method and the cycle duration is for a period greater than 1 second and less than 600 seconds.
  • 3. The method of claim 1, wherein the cycle duration is for a period greater than 1 second and less than 300 seconds to separate one or more contaminants from the gaseous feed stream to form the product stream.
  • 4. The method of claim 1, wherein the performing one or more regeneration steps comprises performing one or more purge steps, wherein each of the one or more purge steps comprise passing a purge stream through the self-supporting structure to conduct away at least a portion of the one or more contaminants in the contaminant output stream.
  • 5. The method of claim 1, wherein the gaseous feed stream is a hydrocarbon containing stream having greater than one volume percent hydrocarbons based on the total volume of the gaseous feed stream.
  • 6. The method of claim 1, wherein a feed pressure of the gaseous feed stream is in the range between 400 pounds per square inch absolute (psia) and 1,400 psia.
  • 7. The method of claim 1, wherein performing the one or more adsorption steps is configured to lower the carbon dioxide (CO2) level to less than 50 parts per million volume.
  • 8. The method of claim 1, wherein performing the one or more adsorption steps is configured to lower the water (H2O) level to less than 105 parts per million volume.
  • 9. The method of claim 1, wherein the self-supporting structure has a low thermal mass.
  • 10. The method of claim 1, wherein the self-supporting structure has pores in the range between 15 pores per inch and 60 pores per inch.
  • 11. The method of claim 1, wherein the adsorbent bed unit operates as a cyclical swing process.
  • 12. The method of claim 11, wherein the cyclical swing process is selected from a temperature swing adsorption (TSA) process, a pressure swing adsorption (PSA) process, a partial pressure purge swing adsorption (PPSA) process, a rapid cycle pressure swing adsorption (RCPSA) process, and a rapid cycle partial pressure swing adsorption (RCPPSA).
  • 13. The method of claim 1, wherein the self-supporting structure has greater than 70% by weight of the active material in the self-supporting structure.
  • 14. The method of claim 1, wherein the adsorbent bed unit further comprises a flow distributor disposed between the self-supporting structure and the plurality of valves.
  • 15. The method of claim 1, wherein the self-supporting structure comprises a plurality of first sheets having a first composition and a first pore density and a plurality of second sheets having a second composition and second pore density, wherein the first pore density is in the range from 1 pores per linear inch (ppi) to 20 ppi and the second pore density is in the range from 20 ppi to 100 ppi.
CROSS-REFERENCE TO RELATED APPLICATIONS

This application claims the priority benefit of U.S. Patent Application No. 62/437,319 filed Dec. 21, 2016 entitled “SELF-SUPPORTING STRUCTURES HAVING ACTIVE MATERIALS”, the entirety of which is incorporated by reference herein. This application is related to U.S. Provisional Patent Application No. 62/437,327 entitled “SELF-SUPPORTING STRUCTURES HAVING ACTIVE MATERIALS,” and U.S. Patent Application No. 62/585,574 filed Nov. 14, 2017 entitled “SELF-SUPPORTING STRUCTURES HAVING ACTIVE MATERIALS,” both having common inventors and assignee, the disclosure of which is incorporated by reference herein in its entirety.

Provisional Applications (1)
Number Date Country
62437319 Dec 2016 US
Divisions (1)
Number Date Country
Parent 15826283 Nov 2017 US
Child 16712300 US