The invention relates generally to a device and method for processing molten and/or semi-molten metal; particularly to a device and method for at least partially monitoring and/or controlling the heating, cooling, and/or stirring of molten and/or semi-molten material; more particularly to a device and method for at least partially monitoring and/or controlling the heating, cooling, and/or stirring of molten and/or semi-molten material and sensing the condition of the molten and/or semi-molten material; and still more particularly to a device and method for at least partially monitoring and/or controlling the heating, cooling, and/or stirring of molten and/or semi-molten material and sensing the condition of the molten and/or semi-molten material, and providing an arrangement to transfer the molten and/or semi-molten material to a forming device.
Metal processing and forming is an important industrial process. It is often desirable to form or cast a metal product from a metal that is in a molten state that is not entirely liquid. At the same time, it is desirable to control selected properties of the material, such as viscosity. One known process of controlling the material properties consists of shearing a molten alloy with a stirring apparatus, while at the same time cooling the metal through the semi-solid temperature range of the alloy (i.e., a temperature ranging between the liquidus temperature and the solidus temperature) during which time the material will have a varying solids fraction (fs), but will have a consistency more solid than liquid. The liquidus temperature is the minimum temperature at which all components of a mixture (such as a metal alloy) can be in a liquid state. Below the liquidus temperature, the mixture will be partly or entirely solid. The solidus temperature is the maximum temperature at which all components of a mixture (such as a metal alloy) can be in a solid state. Above the solidus temperature, some or all of the mixture will be in a liquid state.
This type of metal processing results in initiation nucleation in the mixture when the melt temperature of the mixture has dropped below the liquidus temperature, thereby preventing the normally-occurring formation of a dendritic (i.e., needle-like, crystalline structure in the material). During this type of metal processing and when the semi-solid material is at a specific solids fraction, the multi-constituent alloy material has a structure consisting of solid, spheroidal “α-particles” (i.e., solid particles having a higher melting point primary constituent) that are surrounded by a eutectic liquid (i.e., a liquid comprising lower melting point constituents). As such, during the processing of the mixture, the semi-solid material, hereinafter referred to as “SSM,” has a viscosity which enables the mixture to be handled as a semi-rigid mass. Such semi-rigid mass of the mixture can be injected into a mold under conditions of laminar flow, unlike the turbulent flow usually characterizing a conventional fully molten alloy forming and injection process.
Injecting SSM into a mold under laminar flow can eliminate many common defects associated with a conventional molten metal process for producing die castings, permanent mold castings and other casting methods. These defects include shrinkage porosity, formation of oxides, and gas porosity. Each of these defects can cause reduced mechanical properties of the formed mixture, such as lowered strength, reduced fatigue life, and/or reduced ability of the castings to satisfactorily be heat treated, which is typically employed to optimize strength and elongation of the casted product.
Another beneficial feature of a process that includes the shearing of a molten alloy is that after processing the SSM, the material can be allowed to fully solidify, and upon subsequent re-heating, the material retains the spheroidal “α-particle” SSM structure throughout its semi-solid temperature range. This latter reheating process has been a common and preferred practice due to the ability to create metal stock having the SSM structure through a high-volume bar casting operation. The bars can be readily shipped to a production facility, cut to a selected size, and then re-heated to a semi-solid condition in preparation for a forming or casting operation. However, this process is expensive due to costs associated with equipment used for reheating the SSM and casting the processed bar stock, as well as the inability to recycle processed material and scrap on-site while retaining the SSM structure.
Melting, cooling, and processing of SSM material on-site from standard raw metal stock can result in economies in both equipment and material recycling compared to the reheating process, in large part because expensive re-heating equipment is not required, and large quantities of material are not maintained in process-material that can be rendered unusable if an interruption of the heating or forming process should occur. This standard metal production process is performed with standard furnaces and molten metal transfer equipment. Scrapped metal can be readily recycled and reprocessed into an SSM condition on-site, as needed. Some cost is incurred for an on-site processing unit, but this is typically significantly less than the total cost of all the specialized equipment needed for the reheating process.
In both the reheating process and a conventional production process, the goal is to create a selected microstructure in the finished metal. A significant benefit of the SSM process and subsequent forming of the material into finished products is the ability for the viscous SSM material to flow in a laminar fashion into a mold, which minimizes the occurrence of defects.
Benefits from this process include improved mechanical properties and fatigue life, based on the minimization of oxides, gas porosity and shrinkage porosity. Safety-critical and pressure-sensitive components are prime candidates for these SSM forming processes.
Conventionally, the desired SSM condition is determined by the temperature of the molten metal charge using a thermocouple. The thermocouple is either immersed in the material, or embedded in the container holding the material. An alternate method is to retrieve a sample of material, and cut or knead the material with a spatula to get a “feel” for the viscosity. However, such alternate methods are imprecise, destructive, and involve a separate process step that is not “in line” with the essential melting and casting process. The thermocouple has limitations because it is effectively sacrificial, and can degrade, erode, or become fouled during use.
Other methods of process control are performed on a time basis, programmed via an algorithm that takes into account only the initial molten metal temperature through thermocouple sensing, and the known thermal characteristics of the metal alloy. This control method is unreliable since it does not take into account all variables, such as container temperatures and ambient temperatures. Existing methods also do not enable continuous monitoring of the condition of the SSM material throughout the charging, processing, delivery or transfer steps of the forming process.
A semi-liquid material, hereinafter referred to as “SLM,” also has a temperature ranging between the liquidus temperature and the solidus temperature, but with a consistency more liquid than solid. SLM is also utilized for forming and casting operations. Existing SLM methods also suffer from limitations. Such methods do not account for irregular forming cycle times caused by downstream machine interruptions, operator interruptions, or short-term maintenance interruptions. If a standard cooling cycle is delayed or interrupted, the SLM charge must be scrapped, and another metal charge must be processed when the machine interruption has been resolved. This can result in wasted material, and with attendant increased costs. Also, existing SLM methods are unable to control the SLM process in a manner that ensures that the temperature and viscosity conditions of the SLM charge are consistently the same for each metal charge.
In view of the current state of the art, there is a need for an apparatus and method that overcomes the past deficiencies associated with processing SSM/SLM. In particular, there is a need for an apparatus and method that can be used to control the SSM/SLM process in a manner that ensures that the temperature and/or viscosity conditions of the SSM/SLM charge are consistently the same for each metal charge, and which apparatus and method allows for continuous monitoring of the condition of the SSM/SLM material throughout the charging, processing, and delivery or transfer steps of a forming process.
The present invention is directed to a semi-liquid metal (SLM) and/or semi-solid metal (SSM) processing and sensing device that overcomes the past deficiencies associated with processing SSM/SLM. As used herein, the terms SSM and SLM will be used interchangeably, and both refer to a metal or metal alloy that is at a temperature ranging between the liquidus temperature and the solidus temperature of the metal or metal alloy.
In one non-limiting embodiment of the invention, there is provided a processing and sensing device that includes a crucible or container system that is at least partially encircled by at least one induction coil. The semi-liquid condition of the metal or metal alloy in the crucible or container system can be designed to be sensed and/or be actively controlled by the induction power supply via real time or non-real time analysis of electrical feedback signals that are obtained from the at least one induction coil. In one non-limiting aspect of this embodiment, the one or more induction heating coils can be water-cooled solenoid induction coils; however, this is not required. In another and/or alternative non-limiting aspect of this embodiment, the one or more induction coils can be designed to generate a variable power and/or variable frequency magnetic field which can be modulated to control the cooling of a molten metal charge in the crucible or container system from the liquid, molten metal temperature to a selected heat content, resistivity and/or viscosity below the liquidus temperature of the material. In still another and/or alternative non-limiting aspect of this embodiment, the one or more induction coils can be designed to create a magnetic field that induces toroidal agitation of the metal charge in the crucible or container system. In yet another and/or alternative non-limiting aspect of this embodiment, the one or more induction coils can be designed to create a single zone of heating and/or stirring in the crucible or container system, or multiple induction coils can be used to create multiple zones of heating and/or stirring in the crucible or container system. Several prior art arrangements of the apparatuses and method that can be used in the present invention to process metals and metal alloys between the liquidus temperature and the solidus temperature of the metal or metal alloy are disclosed in U.S. Pat. Nos. 7,216,690; 7,169,350; 7,132,077; 6,991,970; 6,932,938; 6,796,362; 6,637,927; 6,443,216; 6,432,160; 6,402,367; 6,399,017; 5,219,018; and 4,434,837; and United States Publication No. 2007/0187060; all of which are fully incorporated herein by reference. For example, U.S. Pat. Nos. 7,169,350; 6,991,970; and 6,432,160 disclose an apparatus and method for producing an “on-demand” semi-solid material for use in a casting process. The apparatus can include various stations which have the requisite components and structural arrangements that are to be used as part of the process. The apparatus and method includes the use of electromagnetic stirring and various temperature control and cooling control techniques and an apparatus that is used to facilitate in the production of the semi-solid material within a comparatively short cycle time. The apparatus and method also includes structural arrangements and techniques that are used to discharge the semi-solid material directly into a casting machine shot sleeve. The apparatus and method disclosed in U.S. Pat. Nos. 7,169,350; 6,991,970; and 6,432,160 can be fully or partially used in the present invention. U.S. Pat. Nos. 7,132,077; 6,932,938; 6,796,362; 6,443,216; and 6,399,017 disclose a crucible or container system for holding metals and metal alloys between the liquidus temperature and the solidus temperature of the metal or metal alloy. The crucible or container system can include a mechanical or electromagnetic ejection system for discharging the processed metal or metal alloy from the crucible or container system. The crucible or container system can include a cooling arrangement and/or insulation arrangement. The crucible or container system disclosed in U.S. Pat. Nos. 7,132,077; 6,932,938; 6,796,362; 6,443,216; and 6,399,017 can be fully or partially used in the present invention. U.S. Pat. Nos. 7,169,350; 6,991,970; 6,637,927; 6,432,160; 6,402,367; 5,219,018; and 4,434,837 disclose an apparatus and method for mechanical or electromagnetic stirring of metals and metal alloys between the liquidus temperature and the solidus temperature of the metal or metal alloy that are contained in a crucible or container system. The stirring arrangements disclosed in U.S. Pat. Nos. 7,169,350; 6,991,970; 6,637,927; 6,432,160; 6,402,367; 5,219,018; and 4,434,837 can be fully or partially used in the present invention.
In another and/or alternative non-limiting embodiment of the invention, there is provided a processing and sensing device that includes the use of a crucible or container system that is at least partially encircled by at least one induction coil and which the temperature of the metal or metal alloy in the crucible can be determined via real time or non-real time analysis of electrical feedback signals that are obtained from the at least one induction coil. In such an arrangement, the use of prior art thermocouples can be eliminated. As stated above, prior art thermocouples were contact thermocouples positioned in or about a crucible or container system. Such prior art thermocouples had a tendency to erode over time, thus providing inaccurate readings that could result in improper temperatures in the crucible or container system. Additionally, the maintenance of these prior art thermocouples could be difficult, time consuming, and costly.
In another and/or alternative non-limiting embodiment of the invention, there is provided a processing and sensing device that includes the use of a crucible or container system that is at least partially encircled by at least one induction coil and which the induction coil can be designed to be sensed and be actively controlled by the induction power supply via real time or non-real time analysis of electrical feedback signals that are obtained from the at least one induction coil. As such, the prior art method of control of the process of heating, cooling and/or dispensing a metal or metal alloy from a crucible or container system based on a predetermined time basis, and/or a preprogrammed algorithm which only takes into account the initial metal or metal alloy temperature as such metal or metal alloy is initially placed in the crucible or container system is eliminated by the process of the present invention. Such prior art control process are unreliable since the prior art process does not and cannot take into account all of the variables associated with the metal or metal alloy in the crucible or container system (e.g., container temperature, ambient temperature, etc.). The control system in accordance with the present invention has the ability to constantly or periodically monitor the temperature of the metal or metal alloy in the crucible or container system and thereby provide realtime or near realtime control of the temperature of the metal or metal alloy in the crucible or container system throughout the charging, processing and delivery/transfer stages of the metal or metal alloy. Prior art control systems have no way to account for irregular forming cycle times caused by downstream machine interruptions, operator interruptions or short-term maintenance interruptions. As such, if the standard cooling cycle is delayed or interrupted, the metal or metal alloy in the crucible or container system will likely have to be scrapped and another charge processed when the machine is ready to restart casting. The control system in accordance with the present invention has the ability to monitor and maintain the temperature of the metal or metal alloy in the crucible or container system during such interruptions so that the metal or metal alloy does not have to be scrapped and that the metal or metal alloy is delivered to the cast and/or shot sleeve at the desired temperature. Prior art control systems have no satisfactory way to control the temperature of the metal or metal alloy in the crucible or container system so as to guarantee that the condition/consistency/viscosity of the metal or metal alloy dispensed from the crucible or container system has the same physical characteristics (e.g., temperature, viscosity, etc.). The control system in accordance with the present invention has the ability to monitor and maintain the physical characteristics of the metal or metal alloy each time the metal or metal alloy is dispensed from the crucible or container system. As such, the control system in accordance with the present invention overcomes many of the deficiencies of prior art control systems and to provide a control system that is more economical, repeatable and robust than it is practiced currently in the casting industry.
In one non-limiting specific arrangement of the present invention, there is provided a control system that includes a generator (i.e., processing device), which control system is designed to 1) periodically or continually sense the condition of a metal or metal alloy in the generator from the time the metal or metal alloy is introduced in the generator to the time the metal or metal alloy is poured out of or otherwise expelled from the generator to a receptacle of a forming machine (i.e., shot sleeve, sprue, funnel, etc.), 2) control of the cooling, heating and/or stirring (for thermal homogeneity) of the metal or metal alloy in the generator so as to ensure that the metal or metal alloy delivered to the forming machine is of repeatable, consistent thermal, micro-structural and viscous condition shot-to-shot, and/or 3) provide a continuous means for transfer of the material (e.g., after the molten metal or metal alloy is introduced into the generator) from the generator to the forming machine. The generator can be uncoupled to either the molten metal source and/or forming machine receptacle; however, this is not required; however, it can be appreciated that the generator is physically coupled to the molten metal source and/or the forming machine receptacle. In one non-limiting design, the generator includes a generally cylindrical chamber or crucible (e.g., graphite, ceramic/refractory, combination of metal and graphite and/or ceramic, etc.) which holds the molten metal (e.g., molten aluminum, molten aluminum alloy, etc.) that is initially poured or otherwise inserted into the generator. The generally cylindrical chamber or crucible can be at least partially surrounded on the outside within about 0.01-1 inch of the outer surface of the generally cylindrical chamber or crucible by a solenoid induction coil. This coil is generally fixed at a generally uniform distance from the outer surface of the generally cylindrical chamber or crucible with refractory spacers so as to insure a centering of the generally cylindrical chamber or crucible within the induction coil; however, this is not required. The wound coil height is generally sufficient to enclose the entire generally cylindrical chamber or crucible, and can include an extension beyond the length of the crucible at the top and/or bottom of the generally cylindrical chamber or crucible a distance of up to one third of the generally cylindrical chamber or crucible height (e.g., for a 6 inch high crucible, the total length of the induction coil could be up to about 10 inches long). This over extension of the induction coil, when used, facilitates in 1) the even heating of the generally cylindrical chamber or crucible at the top and bottom of the generally cylindrical chamber or crucible, and/or 2) the proper stirring of the metal or metal inside the generally cylindrical chamber or crucible by the electromagnetic force of the induction field generated by the induction coil. The annular space between the induction coil and the generally cylindrical chamber or crucible can be at least partially filled either with rammed/compacted dry refractory material, mica paper, or cast into place within the induction coil using a refractory type cement; however, this is not required. The purpose of the rammed/compacted dry refractory material, mica paper, or cast refractory type cement, when used, is to provide intimate contact between the induction coil and the generally cylindrical chamber or crucible. This intimate contact, when created, enables heat extraction from the generally cylindrical chamber or crucible to the water-cooled induction coil, while at the same time heating of the metal or metal alloy in the generally cylindrical chamber or crucible can be provided by the induction coil. The total effect of the cooling capacity of the induction coil and the heating capacity of the induction coil is to provide a fast response method to control the temperature, viscosity and/or fraction solid (fs) content of the metal or metal alloy in the generally cylindrical chamber or crucible. The ability to control the cooling rate and the temperature of the metal or metal alloy in the generally cylindrical chamber or crucible enables the delivery of a metal or metal alloy charge in a repeatable fashion to a forming device, even in the event of a cycle delay or production interruption. The entire crucible and coil assembly can be contained inside a protective, electrically non-conductive housing for safety and protection of the equipment; however, this is not required. The induction coil is generally powered by a variable frequency power supply (e.g., 10-10000 Hz, etc.). This power supply can be designed to operate in a single frequency range or a simultaneous, multiple frequency mode to enhance toroidal stirring for homogeneity and/or to better control the heating/cooling process. The control system for the generator can be designed to 1) sense the condition of the molten/semi-solid/liquid metal or metal alloy charge in the generator, and/or 2) control the heating and/or cooling rates of the metal or metal alloy charge in the generator based on control signal from the induction coil. In one non-limiting arrangement, a feedback or control signal is obtained from the induction coil that is doing the heating and cooling. This signal can be also or alternatively be obtained from a second, unpowered solenoid coil in close proximity to the metal or metal alloy charge in the generator. As such, the feedback or control signal can be obtained from direct contact with the induction coil or indirectly (i.e., a non-contact source) from the induction coil. For instance, the control board of the induction power unit can be equipped with signal conditioning that monitors (e.g., continuously, periodically) the load on the induction coil. This load is the induction coil and the conductive material inside the induction coil. The conductive material can be considered the metal or metal alloy charge in the generator and the generator itself if the generator material is conductive (e.g., graphite, metal, etc.). Electrically sensed changes in the load are due to thermal changes and metallurgical changes in the metal or metal alloy charge in the generator as the metal or metal alloy cools down and heats up. One of the changes of electrical parameters that can be sensed is a resistivity change in the metal or metal alloy charge in the generator which produces a change in the induction coil voltage. As can be appreciated, other or additional electrical parameters can be sensed for purposes of monitoring and/or controlling the operation of the generator. These one or more sensed electrical parameters can be used to at least partially determine, monitor and/or control a property of the metal charge includes, but is not limited to, a load resistance inside a region that is at least partially encircled by the induction coil, a resistivity of the metal charge, a temperature of the metal charge, a solid fraction of the metal charge, and/or a liquid fraction of the metal charge. As can be appreciated, other properties of the metal charge can be monitored, determined and/or controlled by the sensing of one or more electrical parameters. This voltage change can be used as a feedback signal to control the heating and cooling process for the metal or metal alloy charge in the generator. Using various signal conditioning features in the induction control system, this voltage signal and/or other available signals reflecting the condition of the metal or metal alloy charge in the generator can be used to modulate and control the physical process of cooling, heating and/or holding the temperature metal or metal alloy charge in the generator. The induction control system can be designed to provide the signal and track the signal even when modulating the power output. Therefore the control of the heating and cooling process of the metal or metal alloy charge in the generator can be 1) continuous, 2) non-contact (i.e., no thermocouple required in the molten metal or metal alloy or crucible wall), 3) able to be adjusted to a desired operating point, and/or 4) able to deliver the metal or metal alloy charge in the generator to the forming station. The heating and cooling control system for the metal or metal alloy charge in the generator can be used in conjunction with one of the other SSM/SLM production methods. For example, some other control system can be used to initiate the nucleation process of the metal or metal alloy and then the process control can be used to control the heating and cooling of the metal or metal alloy in the generator to insure a homogeneous temperature for the metal or metal alloy. The control system can also be used to obtain and then maintain, if necessary, a desired temperature of the metal or metal alloy in the generator to the point that the metal or metal alloy is delivered to the forming station. Depending on the design of the forming machine and its charge receptacle, the generator can be designed to be tilted so as to pour a charge into a vertically or horizontally oriented shot sleeve. The generator and the connecting induction power leads can be affixed to a multi-axis (e.g., typically 3 or more axes) robot/mechanical arm; however, this is not required. This robot arm, when used, can have sufficient motion to move the generator to a position to accept a molten metal charge (e.g., from a ladle, metal pump, dosing furnace, etc.). The robot arm can be designed to move the generator and the connecting induction power leads to an intermediate position to create the SLM structure at a separate nucleation device or to create the SLM structure by the generator internally in transit to the delivery point at the forming station. The robot arm can then be designed to move the generator and the connecting induction power leads to a forming station wherein the generator is tilted to pour or slide out of the metal or metal alloy charge or actively is engaged via a plunger/piston to inject the metal or metal alloy charge into the forming or injection chamber of the forming machine. The induction power supply can either be an integral part of the delivery unit or placed separately, remote from the robot arm and process area. As can be appreciated, the generator can be part of a fully coupled unit. In such an arrangement, the generator accepts a metered charge though a heated transfer tube directly from a dosing furnace or molten metal pump. The molten metal passes through the generator wherein the charge is cooled and stirred. The induction coil can be a single solenoid powered by a single frequency generator or triple-wound independent coil supplied by a three phase frequency induction generator to enhance metal movement through the generator. The charge would be held in the generator section at a controlled condition. When the cycle calls for metal for injection, the metal supply device (pump or dosing unit) is actuated and the generator proceeds to move the charge along the heated conduit into the forming/injection chamber as a new volume of molten metal is introduced into the generator. Some of the non-limiting features of the control system are:
It is one non-limiting object of the present invention to provide an apparatus and method that can determine, monitor and/or control one or more physical properties of a metal or metal alloy in a crucible or container system via analysis of one or more sensed electrical parameters (e.g., electrical feedback signals obtained from the at least one induction coil that is positioned at least partially about the crucible or container system, etc.).
It is another and/or alternative non-limiting object of the present invention to provide an apparatus and method that can determine the temperature, solids fraction, and/or liquid fraction of a metal or metal alloy in a crucible or container system via analysis of electrical feedback signals obtained from the at least one induction coil that is positioned at least partially about the crucible or container system.
It is still another and/or alternative non-limiting object of the present invention to provide an apparatus and method that can determine and/or control of the temperature of a metal or metal alloy in a crucible or container system via analysis of electrical feedback signals obtained from at least one induction coil that is positioned at least partially about the crucible or container system.
It is yet another and/or alternative non-limiting object of the present invention to provide an apparatus and method that can control the processing of a metal or metal alloy from the time the metal or metal alloy is deposited in a crucible or container system to the time the metal or metal alloy is poured out of or ejected from the crucible or container system, and wherein at least a portion of the information for such processing control is obtained from the analysis of electrical feedback signals obtained from the at least one induction coil that is positioned at least partially about the crucible or container system.
It is still yet another and/or alternative non-limiting object of the present invention to provide an apparatus and method that can determine the temperature of a metal or metal alloy in a crucible or container system without the use of a thermocouple.
It is another and/or alternative non-limiting object of the present invention to provide an apparatus and method that can determine and control the temperature of a metal or metal alloy in a crucible or container system without the use of a thermocouple.
It is still another and/or alternative non-limiting object of the present invention to provide an apparatus and method that can determine, monitor, and/or control at least one property of a metal charge in a generator is subjected to a magnetic field formed by at least one induction coil by using a sensing arrangement to directly sense and/or indirectly sense at least one electrical parameter, which at least one electrical parameter can be used to at least partially determine a load resistance inside a region that is at least partially encircled by the at least one induction coil, a resistivity of the metal charge, a temperature of the metal charge, a solid fraction of the metal charge, and/or a liquid fraction of the metal charge.
It is still another and/or alternative non-limiting object of the present invention to provide an apparatus and method that includes the use of a controller to at least partially control a power level to an at least one induction coil based on at least one sensed electrical parameter.
It is yet another and/or alternative non-limiting object of the present invention to provide an apparatus and method that includes the use of a controller to at least partially controls a reduction of temperature of a metal charge from a liquidus temperature of the metal charge to a temperature greater than a solidus temperature of the metal charge so that the metal charge has a certain solid fraction and liquid fraction just prior to a time the metal charge is poured from or otherwise ejected from a generator.
It is still yet another and/or alternative non-limiting object of the present invention to provide an apparatus and method that senses at least one electrical parameter from feedback from at least one induction coil.
It is another and/or alternative non-limiting object of the present invention to provide an apparatus and method that senses at least one electrical parameter from a solenoid coil in proximity to at least one induction coil.
It is still another and/or alternative non-limiting object of the present invention to provide an apparatus and method that mathematically manipulates (e.g., taking derivatives of parameters, correlating data, curve fitting, etc.) at least one sensed electrical parameter to at least partially used to determine one or more tends in physical properties (e.g., temperature of metal charge over time, resistivity of metal charge over time, load resistance encountered by induction coil over time, resistivity of metal charge to power to induction coil, resistivity of metal charge to temperature of metal charge, etc.) of the metal charge.
These and other objects and advantages will become apparent to those skilled in the art upon the reading and following of this description taken together with the accompanying drawings.
Reference may now be made to the drawings, which illustrate various embodiments that the invention may take in physical form and in certain parts and arrangements of parts wherein;
Referring now in greater detail to the drawings, wherein the showings are for the purpose of illustrating various embodiments of the invention only, and not for the purpose of limiting the invention, the present invention is directed to a SML/SSM processing and sensing device, hereinafter also referred to as a “generator,” for preparing SML/SSM for use in metal forming or casting operations. In general, the process includes cooling the metal charge to the liquid, molten metal temperature of the metal charge after the metal charge has been inserted into the generator, then further cooling the metal charge in a controlled manner with electromagnetic stirring and/or other types of stirring in order to minimize the formation of a dendritic crystalline structure, and/or to facilitate the formation or nucleation of a spheroid α-particle structure in the metal charge. The rate of cooling, and the condition of the molten metal charge below the liquidus temperature can be at least partially determined by measuring the heat content of the molten metal charge. In accordance with one non-limiting aspect of the present invention, the heat content of the molten metal and/or SML/SSM in the generator can be at least partially determined indirectly by determining the electrical resistivity of the molten metal charge and/or SML/SSM in the generator by measuring the changing voltage, current, resistance, and/or power that is reflected in the feedback of the heating/cooling coil as the condition and temperature of the molten metal charge and/or SML/SSM changes in the generator. In accordance with another non-limiting aspect of the present invention, the molten metal charge and/or SML/SSM in the generator can be agitated by exposing the molten metal charge and/or SML/SSM to an alternating magnetic field. In accordance with still another non-limiting aspect of the present invention, the SML/SSM in the generator can be maintained within a desired temperature range and/or maintained to have desired physical properties up to the point of delivery of the SML/SSM to a forming or casting apparatus.
Referring to
Referring to
Crucible 20 is generally fabricated of a material having suitable strength, durability, and thermal properties for the temperatures and metal charge mass to which the crucible 20 will be exposed. Suitable materials can include, but are not limited to, graphite, known ceramic or refractory materials, or a combination of metal and graphite or ceramic materials. The open end of the crucible 20 can be circumscribed by an annular top flange 32 transitioning to the crucible 20 through an annular refractory cap 34; however, this is not required. The annular top flange can be provided with a means to close the crucible opening for the purpose of introducing an inert gas (i.e., nitrogen and/or argon, etc.) so as to inhibit or reduce the formation of oxides in the SLM/SSM material; however, this is not required.
Extending circumferentially around the crucible 20 is a generally well-known solenoid induction coil 24. As can be appreciated, more than one coil can extend at least partially around the crucible. In one non-limiting embodiment, induction coil 24 is cooled internally with a coolant such as, but not limited to, water. As can be appreciated, induction coil 24 can be designed to not be cooled by an internally flowing coolant. As can also be appreciated, one or more cooling coils can be positioned about the crucible so as to cool the crucible in one or more zones and/or one or more heating coils can be positioned about the crucible to heat the crucible in one or more zones; however, this is not required. Induction coil 24 can include a pair of cooling fluid leads 44, 46. In one non-limiting embodiment, cooling fluid leads 44, 46 can include a heavy-duty hose or tubing encasing a copper cable such as used in welding equipment; however, it can be appreciated that cooling fluid leads 44, 46 can be formed in other ways. The tubing, when used for cooling fluid leads 44, 46, can comprise copper tubing; however, this is not required. A the cooling fluid can be water W or some other type of cooling fluid. As illustrated in
In another non-limiting embodiment, induction coil 24 is spaced from crucible 20. When induction heating coil is spaced from crucible 20, the spacing is generally uniform; however, this is not required. Furthermore, when induction heating coil is spaced from crucible 20, the spacing is generally at least about 0.01 inch, typically at least about 0.02 include, more typically less than about 10 inches, still more typically about 0.05-5 inches, and yet more typically about 0.1-1 inch. Induction coil 24 can be spaced at a uniform distance from the crucible perimeter with refractory spacers, which facilitate centering of the crucible 20 within the coil 24; however, this is not required.
In another non-limiting embodiment, the height of induction coil 24 can be selected to encircle the entire crucible 20, at least partially encircle the crucible, and/or extend beyond the top and/or bottom of crucible 20. Typically, the height of induction coil 24 is selected to encircle the entire crucible 20 so that uniform heating of the metal charge in the crucible can be achieved. The height of induction coil 24 can be selected to not only encircle the entire crucible 20, but to also extend above the top and/or below the bottom of the crucible; however, this is not required. When the height of induction coil 24 extends above the top and/or below the bottom of the crucible, the top and bottom extensions can either or both be up to one third the crucible height above the top and/or bottom of the crucible. For example, for a six inch crucible height, induction coil 24 can extend up to two inches above the top of the crucible and/or up to two inches below the bottom of the crucible; however, it can be appreciated that the induction coil 24 can be more than a third of the crucible height above and/or below the crucible. The extension of the induction coil above the top and/or below the bottom of the crucible facilitates in achieving even heating and/or agitation of metal charge 22 at both the bottom and top of crucible 20.
Induction coil 24 can be at least partially encased within a coupling material 26, which material 26 contacts the circumferential perimeter of crucible 20. As illustrated in
The crucible 20 and induction coil 24 can be at least partially enclosed within a housing comprising a protective, electrically non-conductive outer shell 28. The housing, when used, can include an intermediate assembly 30 of phenolic spacers and structure hoards; however, this is not required. Along the closed end or bottom of crucible 20, a coupling material 26 can be provided with an insulating layer 36, and an end cap 38 can be configured to extend over the closed end in contact with outer shell 28; however, this is not required.
Referring again to
The alternating current in induction coil 24 sets up an electromagnetic field that creates a circulating current in metal charge 22. The alternating current flow in the coil generates or induces an opposite current flow in the conducting metal charge, and depending on the resistivity of the metal charge, causes the metal charge to heat at a faster or slower heating rate. As an example, for a metal charge comprising 20 pounds of aluminum, approximately 25 kW of power will be sufficient to maintain the aluminum in a molten state. In one non-limiting arrangement, the 3-phase AC input power can be converted to a DC voltage, and then inverted to a single phase AC power at a selected frequency; however, this is not required. The choice of a variable-frequency induction power supply enables the frequency to be tailored to facilitate in matching the load. Lower frequencies exert a higher electromotive repulsive force on the metal charge in the crucible.
The induction power supply 42 can be controlled by a controller 40 comprising a known closed-loop feedback system based upon voltage, power phase, and/or current feedback; however, this is not required. The closed-loop feedback system, when used, can be utilized to maintain the metal charge 22 at a predetermined heat content, fs, and/or viscosity, or a predetermined cooling rate during processing. In one non-limiting embodiment, the control of the system can be based on changes in the phase angle of the voltage and current from the induction coil. Since the phase angle is independent of the magnitude of the current and the voltage, it can provide a reliable signal even when the power is being modulated up or down in order to meet a heating and/or cooling profile or ramp.
The induction coil 24 can be instrumented with one or more sensors (not shown). These one or more sensors are typically not connected to the induction power supply. The one or more sensors can be designed to monitor one or more electrical parameters such as, but not limited to, current, voltage, power consumption, and/or frequency. From the output of the one or more sensors, particularly voltage, current, the true power load resistance on the induction coil, and/or the resistivity of the metal charge can be determined through mathematical relationships. These calculations can be performed by formulas programmed into a PLC or other type of device, which in turn is used to control the overall heating and cooling process. The ability to sense the condition of the molten charge from the feedback sensed from the induction coil eliminates the need for the typical, sacrificial thermocouples that are used to control most prior art metal working and casting processes.
The following Table 1 sets forth the grades and associated constituents for selected commercially-available alloys of aluminum. As Table 1 indicates, the constituent proportions can vary between grades and within a selected grade, including the proportions of aluminum. These variations will affect the properties of the SLM/SSM, including the liquidus temperature, the solidus temperature, the viscosity at selected temperatures, the electrical resistivity at selected temperatures, the solids fraction at selected temperatures, and the heat content at selected temperatures.
Generator 10 can be designed to control the cooling of metal charge 22 that has been heated to at least the liquidus temperature until the molten metal charge reaches a selected SLM/SSM state, and can then be delivered to a foaming apparatus for fabrication of a selected product. The cooling of the metal charge can be at least partially controlled by monitoring the resistivity behavior of the metal charge. This type of control is based on the principles that a) resistivity of the metal charge varies with the heat content and/or temperature of the metal charge, b) the heat content and/or temperature of the metal charge controls the solids fraction of the metal charge, and c) the solids fraction of the metal charge correlates to the viscosity of the metal charge. Ultimately, it is desired to prepare a SLM/SSM charge having a selected viscosity for a selected forming operation. The selected viscosity can be identified by the resistivity behavior of the metal charge as a consequence of the interrelationship of resistivity, heat content, solids fraction, and/or viscosity for a selected metal charge.
Referring to
Referring again to
As briefly discussed above, the temperature and viscosity of the metal charge 20 in generator 10 can be determined empirically by comparison to resistivity and/or resistance measurements. This empirical relationship will now be discussed in more detail. The relationship of the resistance of the load (RL) of the induction coil to the temperature of the metal charge 22 in the generator can be based on information that is calculated by use of empirical methods. The basis of this method is the change in resistance of the metal charge (e.g., aluminum alloy in the generator) as reflected in the feedback response of a powered induction coil surrounding the generator. The powered induction coil positioned about the generator operates at some known alternating frequency (e.g., 10-10,000 Hz, 500-5000 Hz, etc.). Due to the alternating current flow in the conducting coil turns, an alternating magnetic field is established in the vicinity of the coil that induces an opposite current flow in the load material (e.g., metal charge 22 and generator, when the generator is formed of a conductive material). It is this rapidly changing current flow induced into the load material that generates heat and also physical forces that act upon the load, which, in the present case, cause a toroidal stirring effect in the molten metal charge in the generator. For instance, a Lorentz Force acts upon the metal charge in the generator, which force is derived from Equation F=(Jx,y×B). This force represents the repulsion between the applied current creating the magnetic field flux density, B, and the induced current, J, in the molten metal charge.
The induction coil used in the present invention is multi-functional since it is designed to both heat the metal charge in the generator and to also regulate the cooling of the metal charge in the generator. The cooling of the metal charge is accomplished by conduction with internal coil cooling water via the generator and any intermediate material used to electrically isolate the induction coil from the metal charge and/or crucible of the generator. As stated above, the induction coil also serves as a source of heat to the metal charge due to the generation of eddy currents directly in the metal charge from the creation of alternating magnetic fields, which is the typical application for induction technology. The simultaneous heating and cooling effects allow for a precise and instantaneous control of the heating and/or cooling rate of the metal charge in the generator.
An induction system consists of a power supply source, load matching/tuning means and coil that acts upon the conducting load. The typical low-medium frequency induction power supply (PS) first creates DC power by rectifying incoming 3-phase line power and then by employing an inverter that creates a 1-phase alternating power output. This alternating power source, to affect a high efficiency utilization of power, must be matched, or tuned to the load to create a resonance effect. At resonance in a tuned circuit, a relationship exists between the frequency f, the capacitance C, and the inductance L as follows: At resonance: f=1/((2p)·(L·C)1/2). When tuned properly, the PS will have an output that will be at a fixed frequency. This reduces the impact of frequency variation on sensing and control. The frequency in an induction system also establishes the effective depth of the induced current penetration. The relationship is based on the following formula: Penetration depth/reference depth δ=3160 (ρ/μf)1/2 inches; where ρ is the resistivity of the metal charge, μ is the relative permeability of the metal charge, and f is the frequency of the alternating power source. For non-magnetic materials such as ceramics and non-ferrous metals, μ=1. Although the actual field penetrates to the center of the metal charge, the induced current density is greatest at the surface of the metal charge or generator if formed of a conductive material, and decays exponentially such that the reference depth accounts for the major portion of the generated heat in the metal charge.
The magnitude of the voltage output from the PS to the induction coil determines the current flow in the coil turns. It is this alternating current that creates the alternating magnetic field. The actual power (kilowatts) at the coil is determined by the voltage, current and the power factor of the load circuit. The power is represented by the following formula: Pc=Ic·Vc·cos θ; where θ is the phase angle between the AC current and the voltage. The power factor, or phase angle is dependent upon the dynamic interaction of the tuning components, PS frequency, the induction coil & load material coupling (e.g., geometric relationship and material properties of the induction coil). At near resonance in the practical parallel LCR circuit, the load impedance is primarily governed by the resistance in the transmission lines, induction coil and metal charge and generator if formed of a conductive material, thus the capacitance part of the circuit has no pure resistance component. As such, XL and the associated resistance RL comprise the impedance relationship of interest. The portion of the circuit of interest in this case is the inductive branch of the circuit, at which, the response of the load can be measured. This relationship is governed by the following formulas: IC=V/RL; PC=I2·RL; and therefore RL=PC/I2. As can be appreciated, if the frequency has a fixed value, then the only variables that will change are the resistance of the components that are affected by temperature and geometry, namely the load system (e.g., @ metal charge crucible and induction coil).
The voltage, current and power all change in response to changes in the material properties of the load system (metal charge, crucible and induction coil). These changes are typically temperature related as the load system heats up or cools down. The particular material property of the load system that is affected by temperature at the same time impacts the electrical characteristics of the load system is the resistivity ρ, which in turn is reflected in the resistance of the load system RL. This relationship is represented by the following formula: RL=ρ·(1/A); where l is the length of the load material, and A is the cross-sectional area of the material along length l. A is thus the cross-section of the conducing path, represented by A=δ·hL; wherein δ is the reference depth. The voltage, current and power are also sensitive to the amount and shape of the metal charge in the generator as it relates to the geometric coupling of the induction coil to the load system. Therefore the response of the voltage, current and power of the circuit can be used to determine what temperature changes have taken place in the load system by solving for RL and/or ρ.
Induction coils are commonly made from copper and are water-cooled. As such, the temperature changes in the induction coil are minimal; thus its resistivity is relatively stable and can be treated as a constant thereby having little impact on the electrical parameters. The gout or insulating material that can be used between the induction coil and crucible of the generator is typically a ceramic mixture that is stable and the resistivity values of such materials are at such a high value that they can be considered non-conductors and thus insignificant. The same principles can be applied to the crucible of the generator if the crucible is made from ceramic materials. However, if the crucible is a graphite material that is conductive, the crucible will have a resistivity value that changes with resulting temperature effects. The metal charge in the generator is not only influenced by conducted temperatures from the induction coil and generator, but the metal charge also generates its own internal inductive heat. The heat generated by the metal charge is dependent upon the operating temperature range of the metal charge and the frequency of the alternating magnetic field. The increase in heat generated in a gaphite crucible is approximately 0.7% at a constant frequency of 1200 Hz, and over the temperature range of 550-650° C. Correspondingly, an aluminum alloy A356 increases its generated heat 39.0% over the same temperature range, with the same electrical, heating and physical conditions. Therefore the resistance contribution of a graphite crucible can be considered a constant over the temperature range of interest that is cited above. The changes in the properties (resistivity) of the metal charge in the generator due to the temperature are reflected in the electrical feedback signals measured at the load coil. In the case of metals and metal alloys, there are phase transformations that occur during heating of the metal and metal alloy from a solid to the liquid condition, and also in the reverse cooling mode. The solid melting point (solidus temperature) and the liquid melting point (liquidus temperature) define the lower and upper temperatures of the melting range of the metal or metal alloy, respectively. In this range for multiphase, nonferrous alloys, these temperatures are often difficult to measure accurately and to use for sensing the degree of melting or fraction solid (fs) of the metal or metal alloy. In addition, most of these measurement methods depend on sensors in direct contact with the molten metal and are prone to damage and degradation over time, such as thermocouples. However, several other material properties change in a more normal or near-linear fashion in this range which can be translated/correlated to temperature values for the metal or metal alloy. Some of these material properties are fs, relative heat content (enthalpy) and resistivity of the metal or metal alloy. The relationships between heat content vs. temperature, fs vs. temperature, and resistivity vs. temperature can be used to monitor and/or determine several properties of the metal charge in the generator. By sensing the resistance (RTOT) and/or resistivity from the electrical feedback of the induction coil, various parameters can be deduced regarding the metal charge in the generator. For example various induction principles can be used to sense and consequently control the (slurry) process in an indirect fashion. As such, an induction coil of one or more windings can be used to sense the electrical reaction response of a load independently of the heating/cooling coil. A separately wound coil, typically of fine insulated wire, cooled or un-cooled can be placed in close proximity to the load container such that it is able to be influenced by the field induce in the load by the main heating/cooling coil; however, this is not required. This arrangement is called “eddy current” sensing. The sensing coil can be powered independently or unpowered and the generated feedback signals can be used in the same fashion as in the coupled case arrangement as discussed above to establish the condition of the load material.
A specific non-limiting process control system in accordance with the present invention will now be described. The process control system can include the use of an Ajax TOCCO Magnethermic “Coil Monitor” unit, a current transducer and potential transformers (PT) for measuring voltage. A current transducer (CT) can be connected to one of the leads supplying the 1-phase high frequency power to the induction coil. The leads from the PT's can be connected directly to the induction coil; one set across all of the induction coil turns and the other set across half of the induction coil turns on the bottom half of the induction coil. The signals from the CT and the first PT can be connected as inputs to the coil monitor unit. As can be appreciated, other configurations can be used in accordance with the present invention.
The metal charge that is to be introduced into the crucible of the generator is maintained in a melting/holding furnace. This melting/holding furnace is designed to hold a repeatable and accurate temperature (±3.0° C.) from a temperature set point. When the metal charge is inserted into the crucible, the power level of the induction coil about the generator (P initial) is such that the metal charge in the crucible does not immediately begin to cool, and the power level of the induction coil is such that it induces forces into the molten metal charge to cause a toroidal stirring action of the metal charge in the crucible. The stirring action is believed to be important in creating a homogeneous melt from the edge of the crucible to the center of the molten metal mass.
The setting for the power from the PS is reduced (P cooling) to the induction coil to cause the cooling capacity of the load system to overcome the heating capacity of the induction system, thereby causing the metal charge in the crucible to begin to cool. The metal charge continues to be stirred during the cooling process since power is still being applied by the induction coil to the metal charge. During the cooling process, the metal charge begins to cool rapidly from the molten phase to the semi-liquid/solid phase, thus passing through the liquidus temperature of the metal charge. Since the liquidus temperature is at the phase transition between the fully liquid/molten metal charge and the initiation of solidification of the metal charge, solid particles of high melting point constituents begin to nucleate and disperse via stirring into the homogeneous mass. This mass particle nucleation takes place due to the rapid cooling rate in the presence of the stirring of the metal charge. Typically, in molten metal alloy systems, dendritic crystal growth occurs when the alloy is in contact with a cooled stationary surface, where stirring is not present in the molten metal bath. The formation of dendritic structure thus reduces the ability of the material to flow at these temperatures and fs levels, and thus increases the force required to move the material into a mold to form a cast part. In contrast, in the slurry system form by the process of the present invention, the creation of individual, free moving, individual partially rounded particles are beneficial to semi-solid slurry material flow since they allow the mass to exhibit a lower viscosity than dendritic material and require less force to move the material into a mold.
The monitoring of the generator can be accomplished by monitoring the single phase, high frequency AC electrical current and voltage feedback from the induction coil and converting the feedback to 0-5 VAC signals by the CT and PT units. These signals can then be inputted to the Ajax TOCCO Magnethermic “Coil Monitor” unit wherein the signals are multiplied to provide a true power signal, compared to an apparent power so as to determine the phase relationship, and then output as scaled 0-10 Vdc sigmals for Coil Current (Ic), Voltage (Vc) and true Power (PT). This relationship is set forth by the following two formulas: PT(Ic·Vc)·cos θ, wherein θ is the phase angle between the high frequency AC voltage and current phasors; and Papp=(Ic·Vc), wherein (Ic) and (Vc) are the scalar values of voltage and current at the induction coil. The output sigmals from the Ajax TOCCO Magnethermic “Coil Monitor” unit can be connected as analog inputs to the System Programmable Logic Controller (PLC). In the control program, the measured true power seen at the induction coil (PT) is divided by the square of the measured value of induction coil current (Ic2). This value yields a value for R (RTOT=PT/Ic2). The equivalent resistance of the load is calculated by the following formula: Req1=Rtot−Rc−Rcr−Rb, wherein Rc is the resistance of the coil, Rcr is the resistance of the crucible, and Rb is the resistance of the coil buss. The actual load resistance of the system is calculated by the following formula: R Load=Reg1/N2, wherein N is the number of coil turns of the induction coil. The resistivity of the load of the system is calculated by the following formula: ρ1=[(Req1·hl·3160)/(2·π·rl·N2)]2·1/f, wherein hl is the length of the load, π is the mathematical value of Pi, and f is the current frequency to the induction coil. The (RTOT) value has been found to correlate well with the resistivity value ρ (load). This correlation is illustrated in
As illustrated in
The use of this “R Load” or “RTOT” signal for control takes place in the PLC. The calculated “R Load” or “RTOT” signal can be tracked as a first derivative with respect to time. When the liquid metal charge is initially poured into the crucible of the generator, the value of the power to the induction coil is reduced to a predetermined value allowing the metal charge in the crucible to begin to cool. A few seconds is typically allowed for the signal to stabilize and for the establishment of the d(R)/dt value and the monitoring of this value. When the metal charge cools to the liquidus temperature, the temperature rate of change reduces as the material becomes semi-solid. Correspondingly, the resistance signal changes as well. However, the resistance change is such that the d(R)/dt decreases. This change in resistance at the liquidus temperature can be used in the control scheme as an initial reference point for determining the degree of semi-solid condition, fs, and control requirements; however, this is not required.
The PLC can be programmed to perform an iterative time and magnitude gate check of the signal as the resistance change occurs. This check can function as verification that the change seen is real and not a response to random signal noise (variation). The verified “R Load” or “RTOT” signal can be measured and continues to decrease in value until a preset ΔR=(RLIQ−R) is achieved. The preset R value can be chosen as representative of the desired fraction solid of the metal charge for the subsequent forming operation. As can be appreciated, the value of the resistance feedback, which reflects the temperature/fs, is prone to some degree of variation during the cooling of the metal charge.
The resulting variation in cycle time of the cooling of the metal charge in the generator will introduce downstream variations in the forming process, and consequently introduce potential problems relating to part quality and defects that are formed in the forming machine. A correction process can be performed in the PLC which measures the feedback signal dR/dt and calculates the real projected cycle time and then compares this value to the target cycle time. Based on this projected time, a new cooling power level can be determined and entered into the high frequency power supply. As a result of this correction, a cooling rate that arrives at the Target Cycle time as the R value reaches the preset RTARGET can be achieved so as to not impede the delivery of the metal charge from the generator to the forming machine.
An additional active control can be used to assist in achieving repeatable cycle time, such as a “Hold” segment of the PLC program. If the RTARGET value is achieved before the cycle time window is completed, then the program can be designed to perform an internal PID control with the target value (RTARGET) as a set-point. The control will maintain the target R value until the cycle time is complete. When the RTARGET and Cycle Time conditions are satisfied, the signal to pour is given to the process system and the tilt mechanism pours the contents of the generator directly into the receiver or shot sleeve of the forming device. The forming device could be a die cast machine (either a horizontal or a vertical unit), gravity semi-permanent mold machine, sand mold or other configuration. Generally a die cast machine is used which can benefit from the slurry charge control and short cycle times, which can lead to increased productivity. At the same time as productivity increases occur, the quality of the product will be improved by the high fs structure of the slurry material.
Referring now to
Referring now to
As discussed above, generator 10 can be designed to perform one or more of the following functions:
A non-limiting feature of generator 10 is the ability to remotely sense the condition of the SLM/SSM charge, and/or to control the heating and/or cooling process based on feedback from the non-contact sensing apparatus, i.e., the induction coil 24. Additionally or alternately, a feedback signal can be obtained from a second, unpowered coil (not shown) in close proximity to the molten metal charge 22. The induction power unit can comprise a controller 40 as illustrated in
Electrically sensed changes in the load are due to thermal changes and metallurgical changes in the molten metal charge as it either cools or heats. One of the changes is a resistivity change in the metal charge that produces a change in the induction coil voltage. This voltage can be used as a feedback signal to control the heat/cooling process of the metal charge in the crucible. Using the signal conditioning features in the induction control system, this voltage and/or other available signals reflecting the metal charge condition can be used to modulate and control the physical process of cooling, heating, and/or maintaining the condition of the metal charge in the generator. Many induction control systems have the added ability to generate and track a signal even when modulating the power output. Therefore, control of the SLM/SSM process can be designed to be continuous, non-contact control system (i.e., no thermocouple required in the metal charge and/or crucible wall), and/or be capable of adjustment to a desired operating point while delivering the metal charge to the forming station.
Another non-limiting embodiment of the device and its application is the use of generator 10 in conjunction with other SSM/SLM production methods. For example, generator 10 can be operably combined with a device that can initiate the nucleation process. Generator 10 can be utilized to maintain a homogeneous melt temperature. After nucleation, the nucleated SLM/SSM mixture can be further cooled and maintained at controlled delivery conditions by generator 10.
Generator 10 also can be designed to control the delivery of the metal charge 22 in a carefully controlled condition to the forming station 18. Depending on the design of the forming machine, and its charge receptacle, generator 10 can either be tilted to pour the metal charge into a vertically or horizontally oriented shot sleeve, such as typically used in a die-cast machine, or a low-pressure permanent mold forming device. In a forming process that requires the metal charge to be highly viscous, similar to an SSM billet, the metal charge can be processed in generator 10, and the generator can deliver the metal charge into a specialized sleeve adapted to receive the more highly viscous SLM/SSM shaped billet (e.g., cylindrical shaped billet, etc.). Generator 10 can be adapted with bottom-sealed refractory or a metal piston that can function as a physical plunger to eject the metal charge 22 from the crucible 20, and be coupled with a hydraulic cylinder to function as an integral shot rod and plunger tip; however, this is not required.
Because the generator 10 is induction powered, any unintended cooling or freezing that might occur in the crucible 20 can be melted out. The ability of generator 10 to heat can also be utilized to prevent the accumulation of solidified oxide skins or skulls in the crucible 20, which skins and skulls can cause product defects such as pre-solidified inclusions. The capability of the Generator 10 to “self clean” without the use of a separate physical contact device is very advantageous.
An alternate non-limiting embodiment of generator 10 is that it can be part of a fully coupled unit. A coupled generator can be adapted to accept a metered metal charge though a heated transfer tube directly from a dosing furnace or molten metal pump. The molten metal charge can be designed to pass through a generator wherein the metal charge is cooled and agitated as in the above-described generator. The induction coil can be a single solenoid coil powered by a single frequency generator, or triple-wound independent coil supplied by a three phase frequency induction generator to enhance metal movement through the generator portion. The metal charge can be maintained in the generator portion at a controlled condition. When the process cycle calls for SLM/SSM to be injected, the metal supply device (e.g., pump or dosing unit) is actuated, and the generator portion allows or causes the metal charge to proceed to a heated conduit and into a forming or injection chamber as a new volume of molten metal is introduced into the generator portion. This method is suitable for a dedicated forming station that produces SLM/SSM parts exclusively.
The semi-liquid metal processing and sensing device of the present invention provides the ability to precisely control the cooling and/or holding process for a metal charge in the generator by cooling rate and end condition, which enables the delivery of a SLM/SSM charge in a repeatable fashion to a forming device, even in the event of a cycle delay or production interruption. This arrangement is a unique feature of generator 10 that is not currently available from prior art SLM/SSM devices.
Generator 10 can be designed to be relatively easy to operate, and not require extensive training, and/or be capable of delivery of repeatable, consistent metal charge to a forming station. The non-contact sensing and control, as well as the ability to fully control the thermal behavior of the metal charge in the generator enables a highly efficient and effective production process. Generator 10 can be readily incorporated into a production line, and can be designed to be easy maintained by simply exchanging generator units on the robot arm.
It will thus be seen that the objects set forth above, among those made apparent from the preceding description, are efficiently attained, and since certain changes may be made in the constructions set forth without departing from the spirit and scope of the invention, it is intended that all matter contained in the above description and shown in the accompanying drawings shall be interpreted as illustrative and not in a limiting sense. The invention has been described with reference to preferred and alternate embodiments. Modifications and alterations will become apparent to those skilled in the art upon reading and understanding the detailed discussion of the invention provided herein. This invention is intended to include all such modifications and alterations insofar as they come within the scope of the present invention. It is also to be understood that the following claims are intended to cover all of the generic and specific features of the invention herein described and all statements of the scope of the invention, which, as a matter of language, might be said to fall therebetween. The invention has been described with reference to the preferred embodiments. These and other modifications of the preferred embodiments as well as other embodiments of the invention will be obvious from the disclosure herein, whereby the foregoing descriptive matter is to be interpreted merely as illustrative of the invention and not as a limitation. It is intended to include all such modifications and alterations insofar as they come within the scope of the appended claims.
The present invention is a continuation of U.S. patent application Ser. No. 12/680,652 filed Jun. 8, 2010, now U.S. Pat. No. 8,241,390, which in turn claims priority on International Application No. PCT/US2008/079465 filed Oct. 10, 2008, which in turn claims priority on U.S. Provisional Patent Application Ser. No. 60/979,511 filed Oct. 12, 2007, which is incorporated in its entirety by reference herein.
| Number | Name | Date | Kind |
|---|---|---|---|
| 3478156 | Segsworth | Nov 1969 | A |
| 4434837 | Winter | Mar 1984 | A |
| 5219018 | Meyer | Jun 1993 | A |
| 5925199 | Shiina et al. | Jul 1999 | A |
| 6114675 | Wada et al. | Sep 2000 | A |
| 6399017 | Norville | Jun 2002 | B1 |
| 6402367 | Lu | Jun 2002 | B1 |
| 6432160 | Norville | Aug 2002 | B1 |
| 6443216 | Lombard | Sep 2002 | B1 |
| 6542535 | Fishman et al. | Apr 2003 | B2 |
| 6637927 | Lu | Oct 2003 | B2 |
| 6796362 | Lombard | Sep 2004 | B2 |
| 6796363 | Arai | Sep 2004 | B2 |
| 6932938 | Norville | Aug 2005 | B2 |
| 6991970 | Fogal | Jan 2006 | B2 |
| 7132077 | Norville | Nov 2006 | B2 |
| 7168350 | Hsieh | Jan 2007 | B1 |
| 7169350 | Norville | Jan 2007 | B2 |
| 7216690 | Han | May 2007 | B2 |
| 7457344 | Fishman et al. | Nov 2008 | B2 |
| 7598632 | Fishman et al. | Oct 2009 | B2 |
| 8241390 | Koch | Aug 2012 | B2 |
| 20020085614 | Tsuda et al. | Jul 2002 | A1 |
| 20070137827 | Vogt et al. | Jun 2007 | A1 |
| 20070187060 | Han | Aug 2007 | A1 |
| 20080063025 | Fishman et al. | Mar 2008 | A1 |
| Number | Date | Country |
|---|---|---|
| 58-181283 | Oct 1983 | JP |
| 07-022167 | Jan 1995 | JP |
| 07-316611 | Dec 1995 | JP |
| 10-140260 | May 1998 | JP |
| 10-272548 | Oct 1998 | JP |
| 11-172402 | Jun 1999 | JP |
| 2001-026428 | Jan 2001 | JP |
| 2004-230462 | Aug 2004 | JP |
| 2005-002394 | Jan 2005 | JP |
| Number | Date | Country | |
|---|---|---|---|
| 20120227542 A1 | Sep 2012 | US |
| Number | Date | Country | |
|---|---|---|---|
| 60979511 | Oct 2007 | US |
| Number | Date | Country | |
|---|---|---|---|
| Parent | 12680652 | US | |
| Child | 13477298 | US |