Claims
- 1. In the process of preparing a linear aromatic polyester by transesterification melt polymerization of monomer reactants consisting essentially of a bisphenol and a diaryl ester of a dicarboxylic acid in a polymerization reaction zone which comprises reacting said bisphenol and said diaryl ester in a first reaction stage of said zone to prepare a polyester oligomer, and thereafter continuing the reaction in a second reaction stage of said zone to produce the polyester product, wherein the diaryl ester is the diaryl ester of a mixture of about 15 to about 85 mole percent isophthalic acid and about 85 to about 15 mole percent terephthalic acid;
- the improvement wherein the polymerization is carried out in the first reaction stage either batchwise or substantially continuously, and the polymerization is continued in the second reaction stage substantially continuously, with the provision that when the polymerization in the first reaction stage is carried out batchwise, the polymerization in the second stage is carried out in a wiped film reaction zone.
- 2. The process of claim 1 wherein the polymerization is conducted in the presence of a catalyst that is normally solid at 30.degree. C. but which is introduced to the polymerization process in liquid form.
- 3. The process of claim 1 wherein the wiped film reaction zone provides for countercurrent flow of the reaction mixture and the vapor by-product of the reaction.
- 4. The process of claim 1 wherein the bisphenol is bisphenol A.
- 5. The process of claim 1 wherein the diaryl ester is diphenyl isophthalate, diphenyl terephthalate or a mixture thereof.
- 6. The process of claim 1 wherein the liquid catalyst is a normally solid material in molten form or a normally solid material in solution in a solvent for the catalyst.
- 7. The process of claim 6 wherein the liquid catalyst is a solution of a metal phenoxide in phenol.
- 8. The process of claim 7 wherein the metal phenoxide is potassium phenoxide.
- 9. The process of claim 7 wherein the metal phenoxide is rubidium phenoxide.
- 10. The process of claim 7 wherein the metal phenoxide is lithium phenoxide.
- 11. The process of claim 7 wherein the metal phenoxide is sodium phenoxide.
- 12. The process of claim 6 wherein the liquid catalyst is the reaction product of potassium borohydride and phenol.
- 13. In the process of preparing a linar aromatic polyester by transesterification melt polymerization of monomer reactants consisting essentially of a bisphenol and a diaryl ester of a dicarboxylic acid in a polymerization reaction zone, wherein the diaryl ester is the diaryl ester of a mixture of about 15 to about 85 mol percent isophthalic acid and about 85 to about 15 mol percent terephthalic acid;
- the improvement which comprises introducing said reactants substantially continuously to said polymerization reaction zone, and withdrawing said polyester product substantially continuously from the polymerization zone.
- 14. The process of claim 13 wherein the bisphenol is bisphenol A.
- 15. The process of claim 13 wherein the diaryl ester is diphenyl isophthalate, diphenyl terephthalate or a mixture thereof.
- 16. In the process of preparing a linear aromatic polyester by tranesterification melt polymerication of monomer reactants consisting essentially of a bisphenol and a diaryl ester of a dicarboxylic acid in the presence of a basic catalyst for the polymerization in a polymerization reaction zone, wherein the diaryl ester is the diaryl ester of a mixture of about 15 to about 85 mol percent isophthalic acid and about 85 to about 15 mol percent terephthalic acid;
- the improvement which comprises introducing said reactants substantially continuously to said polymerization reaction zone, and withdrawing said polyester product substantially continuously from the polymerization zone.
- 17. The process of claim 16 wherein the bisphenol is bisphenol A.
- 18. The process of claim 16 wherein the diaryl ester is diphenyl isophthalate, diphenyl terephthalate or a mixture thereof.
- 19. The process of claim 16 wherein the liquid catalyst is a normally solid material in molten form or a normally solid material in solution in a solvent for the catalyst.
- 20. The process of claim 19 wherein the liquid catalyst is a solution of a metal phenoxide in phenol.
- 21. The process of claim 20 wherein the metal phenoxide is potassium phenoxide.
- 22. The process of claim 20 wherein the metal phenoxide is rubidium phenoxide.
- 23. The process of claim 20 wherein the metal phenoxide is lithium phenoxide.
- 24. The process of claim 20 wherein the metal phenoxide is sodium phenoxide.
- 25. The process of claim 19 wherein the liquid catalyst is the reaction product of potassium borohydride and phenol.
- 26. In the process of preparing a linear aromatic polyester by transesterification melt polymerization of monomer reactants consisting essentially of a bisphenol and a diaryl ester of a dicarboxylic acid in a polymerization zone, said zone comprising a series of at least two reaction stages, wherein the diaryl ester is the diaryl ester of a mixture of about 15 to about 85 mol percent isophthalic acid and about 85 to about 15 mol percent terephthalic acid;
- the improvement which comprises carrying out the polymerization reaction in the final stage of the series continuously in a wiped film reaction zone.
- 27. The process of claim 26 wherein the wiped film reaction zone provides for countercurrent flow of the reaction mixture and the vapor by-product of the reaction.
- 28. The process of claim 26 wherein the bisphenol is bisphenol A.
- 29. The process of claim 26 wherein the diaryl ester is diphenyl isophthalate, diphenyl terephthalate or a mixture thereof.
- 30. In the process of preparing a linear aromatic polyester by transesterification melt polymerization of monomer reactants consisting essentially of a bisphenol and a diaryl ester of a dicarboxylic acid in the presence of a basic catalyst for the polymerization reaction, wherein the diaryl ester is the diaryl ester of a mixture of about 15 to 85 mol percent isophthalic acid and about 85 to 15 mol percent terephthalic acid;
- the improvement which comprises introducing a basic catalyst that is normally solid at 30.degree. C., to the polymerization reaction in liquid form, said polymerization reaction being carried out in a polymerization zone which comprises a series of at least two reaction stages wherein the polymerization reaction in the final reaction stage of said series is carried out continuously in a wiped film reaction zone.
- 31. The process of claim 30 wherein the wiped film reaction zone provides for countercurrent flow of the reaction mixture and the vapor by-product of the reaction.
- 32. The process of claim 30 wherein the bisphenol is bisphenol A.
- 33. The process of claim 30 wherein the diaryl ester is diphenyl isophthalate, diphenyl terephthalate or a mixture thereof.
- 34. The process of claim 30 wherein the liquid catalyst is a normally solid material in molten form or a normally solid material in solution in a solvent for the catalyst.
- 35. The process of claim 30 wherein the liquid catalyst is a solution of a metal phenoxide in phenol.
- 36. The process of claim 35 wherein the metal phenoxide is potassium phenoxide.
- 37. The process of claim 35 wherein the metal phenoxide is rubidium phenoxide.
- 38. The process of claim 35 wherein the metal phenoxide is lithium phenoxide.
- 39. The process of claim 35 wherein the metal phenoxide is sodium phenoxide.
- 40. The process of claim 34 wherein the liquid catalyst is the reaction product of potassium borohydride and phenol.
- 41. In the process of preparing a linear aromatic polyester by transesterification melt polymerization of monomer reactants consisting essentially of a bisphenol and a diaryl ester of a dicarboxylic acid in the presence of a basic catalyst for said polymerization wherein said reactants are introduced to the polymerization reaction in the liquid state, wherein the diaryl ester is the diaryl ester of a mixture of about 15 to about 85 mol percent isophthalic acid and about 85 to about 15 mol percent terephthalic acid;
- the improvement which comprises introducing a basic catalyst that is normally solid at 30.degree. C., in liquid form to the polymerization reaction substantially continuously and withdrawing the polyester product from the polymerization reaction substantially continuously.
- 42. The process of claim 41 wherein at least one reactant is melted prior to mixing with the catalyst.
- 43. In the process of preparing a linear aromatic polyester by transesterification melt polymerization of monomer reactants, consisting essentially of a bisphenol and a diaryl ester of a dicarboxylic acid in the presence of a basic catalyst for said polymerization wherein said reactants are introduced to the polymerization reaction in the liquid state, wherein the diaryl ester is the diaryl ester of a mixture of about 5 to about 85 mol percent isophthalic acid and about 85 to about 15 mol percent terephthalic acid;
- the improvement which comprises introducing a basic catalyst that is normally solid at 30.degree. C., in liquid form to the polymerization reaction substantially concurrently with introduction of the liquid state reactants to the polymerization, wherein the polymerization reaction is carried out in a polymerization zone which comprises a series of at least two reaction stages wherein the polymerization reaction in the final stage of the series is carried out continuously in a wiped film reaction zone.
- 44. The process of claim 43 wherein the first stage of the reaction is carried out batchwise.
- 45. The process of claim 41 wherein the polymerization reaction is carried out in a polymerization zone which comprises a series of at least two reaction stages wherein the polymerization reaction in the final stage of the series is carried out continuously in a wiped film reaction zone.
- 46. The process of claim 41, wherein the liquid catalyst is a normally solid material in molten form or a normally solid material in solution in a solvent for the catalyst.
- 47. The process of claim 46 wherein the liquid catalyst is a solution of a metal phenoxide in phenol.
- 48. The process of claim 47 wherein the liquid catalyst is the reaction product of potassium borohydride and phenol.
- 49. The process of claim 45, wherein the bisphenol is bisphenol A.
- 50. The process of claim 49 wherein the diaryl ester is diphenyl isophthalate, diphenyl terephthalate or mixtures thereof.
- 51. In the process of preparing a linear aromatic polyester by transesterification melt polymerization of monomer reactants consisting essentially of a bisphenol and a diaryl ester of a dicarboxylic acid in the presence of a basic catalyst for said polymerization wherein said reactants are introduced to the polymerization reaction in the liquid state, wherein the diaryl ester is the diaryl ester of a mixture of about 15 to about 85 mol percent isophthalic acid, and about 85 to about 15 mol percent terephthalic acid;
- the improvement which comprises introducing the catalyst and liquid state reactants substantially concurrently and continuously to a polymerization zone and withdrawing said polyester product substantially continuously from said polymerization zone.
- 52. The process of claim 51 wherein the polymerization reaction is carried out in a polymerization zone which comprises a series of at least two reaction stages wherein the polymerization reaction in the final stage of the series is carried out continuously in a wiped film reaction zone.
- 53. The process of claim 52 wherein the first stage of the reaction is carried out batchwise.
- 54. The process of claim 51, wherein the liquid catalyst is a normally solid material in molten form or a normally solid material in solution in a solvent for the catalyst.
- 55. The process of claim 54 wherein the liquid catalyst is a solution of a metal phenoxide in phenol.
- 56. The process of claim 55 wherein the liquid catalyst is the reaction product of potassium borohydride and phenol.
- 57. The process of claim 51, wherein the bisphenol is bisphenol-A.
- 58. The process of claim 57 wherein the diaryl ester is diphenyl isophthalate, diphenyl terephthalate or mixtures thereof.
- 59. In the process of preparing a linear aromatic polyester by transesterification melt polymerization of monomer reactants consisting essentially of a bisphenol and a diaryl ester of a dicarboxylic acid in the presence of a basic catalyst for said polymerization wherein said reactants are introduced to the polymerization reaction in the liquid state, wherein the diaryl ester is the isophthalic acid and about 15 to about 85 mol percent isophthalic acid and about 85 to about 15 mol percent terephthalic acid;
- the improvement which comprises introducing the catalyst to the polymerization substantially concurrently with introduction of the reactants to the polymerization, said polymerization reaction being carried out in a polymerization zone which comprises a series of at least two reaction stages wherein the polymerization reaction in the final stages of said series is carried out continously in a wiped film reaction zone.
- 60. The process of claim 59 wherein the first stage of the reaction is carried out batchwise.
- 61. The process of claim 59 wherein the liquid catalyst is a normally solid material in molten form or a normally solid material in solution in a solvent for the catalyst.
- 62. The process of claim 61 wherein the liquid catalyst is a solution of a metal phenoxide in phenol.
- 63. The process of claim 62 wherein the liquid catalyst is the reaction product of potassium borohydride and phenol.
- 64. The process of claim 59, wherein the bisphenol is bisphenol A.
- 65. The process of claim 64 wherein the diaryl ester is diphenyl isophthalate, diphenyl terephthalate or mixtures thereof.
- 66. The process of claim 27, wherein said wiped film reaction zone provides for countercurrent flow of the reaction mixture and the vapor by-product of the reaction.
- 67. The product of the process of claim 1.
- 68. The product of the process of claim 2.
- 69. The product of the process of claim 13.
- 70. The product of the process of claim 16.
- 71. The product of the process of claim 26.
- 72. The product of the process of claim 30.
- 73. The product of the process of claim 41.
- 74. The product of the process of claim 43.
- 75. The product of the process of claim 45.
- 76. The product of the process of claim 51.
- 77. The product of the process of claim 59.
- 78. The process of claim 1, wherein the diaryl ester is the diphenyl ester.
- 79. The product of the process of preparing a linear aromatic polyester by transesterification polymerization of monomer reactants consisting essentially of a bisphenol and a diphenyl ester of a dicarboxylic acid in a polymerization reaction zone which comprises reacting said bisphenol and said phenyl ester in a first reaction stage of said zone to prepare a polyester oligomer, and thereafter continuing the reaction in a second reaction stage of said zone to produce the polyester product, wherein the polymerization is carried out in the first reaction stage either batchwise or substantially continuously, and the polymerization is continued in the second reaction stage substantially continuously, with the provision that when the polymerization in the first reaction stage is carried out batchwise, the polymerization in the second stage is carried out in a wiped film reaction zone.
- 80. The product of the process of preparing a linear aromatic polyester by transesterification polymerization of monomer reactants consisting essentially of a bisphenol and a diaryl ester of a dicarboxylic acid in a polymerization reaction zone which comprises reacting said bisphenol and said diaryl ester in a first reaction stage of said zone to prepare a polyester oligomer, and thereafter continuing the reaction in a second reaction stage of said zone to produce the polyester product, wherein the polymerization is carried out in the first reaction stage either batchwise or substantially continuously, with the provision that when the polymerization in the first reaction stage is carried out batchwise, the polymerization in the second stage comprises polymerization in a wiped film reaction zone followed by polymerization in a vented extrusion reaction zone.
- 81. The product of claim 80 wherein the polymerization is conducted in the presence of a catalyst that is normally solid at 30.degree. C., but which is introduced to the polymerization process in liquid form.
- 82. The product of the process of preparing a linear aromatic polyester by transesterification polymerization of monomer reactants consisting essentially of a bisphenol and a diaryl ester of a dicarboxylic acid in a polymerization zone, said zone comprising a series of at least two reaction stages, wherein the polymerization reaction is carried out in the final stage of the series continuously, in a wiped film reaction zone followed by polymerization in a vented extrusion reaction zone.
- 83. The product of the process of preparing a linear aromatic polyester by transesterification polymerization of monomer reactants comprising a bisphenol and a diaryl ester of a dicarboxylic acid in the presence of a basic catalyst for the polymerization reaction, wherein a basic catalyst that is normally solid at 30.degree. C., is introduced to the polymerization reaction in liquid form, said polymerization reaction being carried out in a polymerization zone which comprises a series of at least two reaction stages wherein the polymerization reaction in the final reaction stage of said series is carried out continuously in a wiped film reaction zone followed by polymerization carried out continuously in a vented extrusion reaction zone.
- 84. The product of the process of preparing a linear aromatic polyester by transesterification polymerization of monomer reactants comprising a bisphenol and a diaryl ester of a dicarboxylic acid in the presence of a basic catalyst for said polymerization reaction in the liquid state, wherein a basic catalyst that is normally solid at 30.degree. C., is introduced in liquid form to the polymerization reaction substantially concurrently with introduction of the liquid state reactants to the polymerization, wherein the polymerization reaction is carried out in a polymerization zone which comprises a series of at least two reaction stages wherein the polymerization reaction in the final stage of the series is carried out continuously in a wiped film reaction zone followed by polymerization carried out continuously in a vented extrusion reaction zone.
- 85. The product of the process of preparing a linear aromatic polyester by transesterification polymerization of monomer reactants comprising a bisphenol and a diaryl ester of a dicarboxylic acid in the presence of a basic catalyst for said polymerization wherein said reactants are introduced to the polymerization reaction in the liquid state, wherein a basic catalyst that is normally solid at 30.degree. C., is introduced in liquid form to the polymerization reaction substantially concurrently with introduction of the liquid state reactants to the polymerization, and introducing the catalyst and reactants to the polymerization reaction substantially continuously and withdrawing the polyester product from the polymerization reaction substantially continuously, wherein the polymerization reaction is carried out in a polymerization zone which comprises a series of at least two reaction stages wherein the polymerization reaction in the final stage of the series is carried out continuously in a wiped film reaction zone followed by polymerization carried out continuously in a vented extrusion reaction zone.
- 86. The product of preparing a linear aromatic polyester by transesterification polymerization of monomer reactants comprising a bisphenol and a diaryl ester of a dicarboxylic acid in the presence of a basic catalyst for said polymerization wherein said reactants are introduced to the polymerization reaction in the liquid state, wherein the catalyst and liquid state reactants are introduced substantially concurrently and continuously to a polymerization zone and said polyester product is withdrawn substantially continuously from said polymerization zone, wherein the polymerization reaction is carried out in a polymerization zone which comprises a series of at least two reaction stages wherein the polymerization reaction in the final stage of the series is carried out continuously in a wiped film reaction zone followed by polymerization carried out continuously in a vented extrusion reaction zone.
- 87. The product of the process of preparing a linear aromatic polyester by transesterification polymerization of monomer reactants comprising a bisphenol and a diaryl ester of a dicarboxylic acid in the presence of a basic catalyst for said polymerization wherein said reactants are introduced to the polymerization reaction in the liquid state, wherein the catalyst to the polymerization is introduced substantially concurrently with introduction of the reactants to the polymerization, said polymerization reaction being carried out in a polymerization zone which comprises a series of at least two reaction stages wherein the polymerization reaction in the final stage of said series is carried out continuously in a wiped film reaction zone followed by polymerization carried out continuously in a vented extrusion reaction zone.
REFERENCE TO COPENDING APPLICATIONS
This is a division of application Ser. No. 232,929 filed Feb. 9, 1983, now U.S. Pat. No. 4,415,721 which is a continuation-in-part of copending U.S. Application Ser. No. 198,979, filed Oct. 21, 1980 now abandoned which, in turn, is a continuation-in-part of copending U.S. Application Ser. No. 128,742, filed Mar. 10, 1980 now U.S. Pat. No. 4,319,017.
US Referenced Citations (2)
Number |
Name |
Date |
Kind |
4319017 |
Kosanovich et al. |
Mar 1982 |
|
4415721 |
Kosanovich et al. |
Nov 1983 |
|
Divisions (1)
|
Number |
Date |
Country |
Parent |
232929 |
Feb 1983 |
|
Continuation in Parts (2)
|
Number |
Date |
Country |
Parent |
198979 |
Oct 1980 |
|
Parent |
128742 |
Mar 1980 |
|