Claims
- 1. In the process of preparing a linear aromatic polyester by transesterification melt polymerization of monomer reactants consisting essentially of a bisphenol and a diaryl ester of a dicarboxylic acid in a polymerization reaction zone which comprises reacting said bisphenol and said diaryl ester in a first reaction stage of said zone to prepare a polyester oligomer, and thereafter continuing the reaction in a second reaction stage of said zone to produce the polyester product,
- the improvement wherein the polymerization is carried out in the first reaction stage either batchwise or substantially continuously, and the polymerization is continued in the second reaction stage substantially continuously, with the provision that when the polymerization in the first reaction stage is carried out batchwise, the polymerization in the second stage comprises polymerization in a wiped film reaction zone followed by polymerization in a vented extrusion reaction zone.
- 2. The process of claim 1 wherein the polymerization is conducted in the presence of a catalyst that is normally solid at 30.degree. C., but which is introduced to the polymerization process in liquid form.
- 3. The process of claim 1 or 2 wherein the wiped film reaction zone provides for counter-current flow of the reaction mixture and the vapor by-product of the reaction.
- 4. The process of claim 1 or 2 wherein the bisphenol is bisphenol-A.
- 5. The process of claim 1 or 2 wherein the diaryl ester is the diaryl ester of a mixture of about 15 to about 85 mol percent isophthalic acid and about 85 to about 15 mol percent terephthalic acid.
- 6. The process of claim 5 wherein the diaryl ester is the diphenyl ester.
- 7. The process of claim 1 or 2 wherein the liquid catalyst is a normally solid material in molten form or a normally solid material in solution in a solvent for the catalyst.
- 8. The process of claim 7 wherein the liquid catalyst is a solution of a metal phenoxide in phenol.
- 9. The process of claim 8 wherein the metal phenoxide is potassium phenoxide.
- 10. The process of claim 8 wherein the metal phenoxide is rubidium phenoxide.
- 11. The process of claim 8 wherein the metal phenoxide is lithium phenoxide.
- 12. The process of claim 8 wherein the metal phenoxide is sodium phenoxide.
- 13. The process of claim 1 wherein the liquid catalyst is the reaction product of potassium borohydride and phenol.
- 14. In the process of preparing a linear aromatic polyester by transesterification polymerization of monomer reactants consisting essentially of a bisphenol and a diaryl ester of a dicarboxylic acid in a polymerization zone, said zone comprising a series of at least two reaction stages,
- the improvement which comprises carrying out the polymerization reaction in the final stage of the series continuously, in a wiped film reaction zone followed by polymerization in a vented extrusion reaction zone.
- 15. In the process of claim 14 wherein the reaction is a transesterification melt polymerization and the wiped film reaction zone provides for counter-current flow of the reaction mixture and the vapor by-product of the reaction.
- 16. The process of claim 14 wherein the bisphenol is bisphenol-A.
- 17. The process of claim 14 wherein the diaryl ester is the diaryl ester of a mixture of about 15 to about 85 mol percent isophthalic acid and about 85 to about 15 mole percent terephthalic acid.
- 18. The process of claim 17 wherein the diaryl ester is the diphenyl ester.
- 19. In the process of preparing a linear aromatic polyester by transesterification polymerization of monomer reactants consisting essentially of a bisphenol and a diaryl ester of a dicarboxylic acid in the presence of a basic catalyst for the polymerization reaction,
- the improvement which comprises introducing a basic catalyst that is normally solid at 30.degree. C., to the polymerization reaction in liquid form, said polymerization reaction being carried out in a polymerization zone which comprises a series of at least two reaction stages wherein the polymerization reaction in the final reaction stage of said series is carried out continuously in a wiped film reaction zone followed by polymerization carried out continuously in a vented extrusion reaction zone.
- 20. The process of claim 19 wherein the reaction is a transesterification melt polymerization and the wiped film reaction zone provides for counter-current flow of the reaction mixture and the vapor by-product of the reaction.
- 21. The process of claim 20 wherein the bisphenol is bisphenol-A.
- 22. The process of claim 19 wherein the diaryl ester is the diaryl ester of a mixture of about 15 to about 85 mol percent isophthalic acid and about 85 to about 15 mol percent terephthalic acid.
- 23. The process of claim 22 wherein the diaryl ester is the diphenyl ester.
- 24. The process of claim 19 wherein the liquid catalyst is a normally solid material in a molten form or a normally solid material in solution in a solvent for the catalyst.
- 25. The process of claim 19 wherein the liquid catalyst is a solution of a metal phenoxide in phenol.
- 26. The process of claim 25 wherein the metal phenoxide is potassium phenoxide.
- 27. The process of claim 25 wherein the metal phenoxide is rubidium phenoxide.
- 28. The process of claim 25 wherein the metal phenoxide is lithium phenoxide.
- 29. The process of claim 25 wherein the metal phenoxide is sodium phenoxide.
- 30. The process of claim 24 wherein the liquid catalyst is the reaction product of potassium borohydride and phenol.
- 31. In the process of preparing a linear aromatic polyester by transesterification polymerization of monomer reactants consisting essentially of a bisphenol and a diaryl ester of a dicarboxylic acid in the presence of a basic catalyst for said polymerization reaction in the liquid state,
- the improvement which comprises introducing a basic catalyst that is normally solid at 30.degree. C., in liquid form to the polymerization reaction substantially concurrently with introduction of the liquid state reactants to the polymerization, wherein the polymerization reaction is carried out in a polymerization zone which comprises a series of at least two reaction stages wherein the polymerization reaction in the final stage of the series is carried out continuously in a wiped film reaction zone followed by polymerization carried out continuously in a vented extrusion reaction zone.
- 32. The process of claim 31 wherein the first stage of the reaction is carried out batchwise and the reaction is a transesterification melt polymerization.
- 33. The process of claim 31 or 32, wherein the liquid catalyst is a normally solid material in molten form or a normally solid material in solution in a solvent for the catalyst.
- 34. The process of claim 33 wherein the liquid catalyst is a solution of a metal phenoxide in phenol.
- 35. The process of claim 34 wherein the liquid catalyst is the reaction product of potassium borohydride and phenol.
- 36. The process of claim 34 or 35 wherein the bisphenol is bisphenol-A.
- 37. The process of claim 36 wherein the diaryl ester is the diaryl ester of a mixture of about 15 to about 85 mol percent isophthalic acid and about 85 to 15 mol percent terephthalic acid.
- 38. The process of claim 37 wherein the diaryl ester is the diphenyl ester.
- 39. In the process of preparing a linear aromatic polyester by transesterification polymerization of monomer reactants consisting essentially of a bisphenol and a diaryl ester of a dicarboxylic acid in the presence of a basic catalyst for said polymerization wherein said reactants are introduced to the polymerization reaction in the liquid state,
- the improvement which comprises introducing the catalyst to the polymerization substantially concurrently with introduction of the reactants to the polymerization, said polymerization reaction being carried out in a polymerization zone which comprises a series of at least two reaction stages wherein the polymerization reaction in the final stage of said series is carried out continuously in a wiped film reaction zone followed by polymerization carried out continuously in a vented extrusion reaction zone.
- 40. The process of claim 39 wherein the first stage of the reaction is carried out batchwise and the reaction is a transesterification melt polymerization.
- 41. The process of claim 39 or 40 wherein the liquid catalyst is a normally solid material in molten form or a normally solid material in solution in a solvent for the catalyst.
- 42. The process of claim 41 wherein the liquid catalyst is a solution of a metal phenoxide in phenol.
- 43. The process of claim 42 wherein the liquid catalyst is the reaction product of potassium borohydride and phenol.
- 44. The process of claim 39, 42 or 43 wherein the bisphenol is bisphenol-A.
- 45. The process of claim 44 wherein the diaryl ester is the diaryl ester of a mixture of about 15 to about 85 mol percent isophthalic acid and about 85 to 15 mol percent terephthalic acid.
- 46. The process of claim 45 wherein the diaryl ester is the diphenyl ester.
- 47. The process of claim 15, 19, 31, or 39 wherein said wiped film reaction zone provides for counter-current flow of the reaction mixture and the vapor by-product of the reaction.
REFERENCE TO COPENDING APPLICATIONS
This application is a continuation-in-part of copending U.S. application Ser. No. 198,979, filed Oct. 21, 1980 and now abandoned, which, in turn, is a continuation-in-part of copending U.S. application Ser. No. 128,742, filed Mar. 10, 1980, now U.S. Pat. No. 4,319,017.
US Referenced Citations (1)
Number |
Name |
Date |
Kind |
4319017 |
Kosanovich et al. |
Mar 1982 |
|
Continuation in Parts (2)
|
Number |
Date |
Country |
Parent |
198979 |
Oct 1980 |
|
Parent |
128742 |
Mar 1980 |
|