Patent Application
20050016709
The present invention relates generally to casting aluminum-silicon metal alloys. More particularly, the present invention relates to semi-solid metal casting of hypoeutectic aluminum-silicon alloys using titanium alloy grain refiners.
Conventional casting methods such as die casting, gravity permanent mold casting, and squeeze casting have long been used for Aluminum-Silicon (Al-Si) alloys. However, where semi-solid metal (SSM) casting of Al-Si alloy materials has been involved, the conventional methods have not been employed successfully to date. Rheocasting and thixocasting are casting methods that were developed in an attempt to convert conventional casting means to SSM casting. However, these SSM methods require costly retrofitting to conventional casting machinery.
Challenges also remain in the ability to manipulate the mechanical and metallurgical properties of SSM castings. As the performance of the cast product is predicated, in part, by the microstructures of primary Al and/or Si particles in the part, attempts have been made to improve methods to achieve the requisite microstructure. One approach is to achieve homogeneous distribution of primary Al or Si, while another is to limit the growth and size of the particles themselves.
The physical characteristics of the primary particles depends on the imposed temperature gradient, presence of impurities, and ease of nucleation. Known strategies to affect these parameters include the use of electromagnetic stirring and grain refiners, such as titanium alloys. Alternatively, control of the cooling rate and isothermal hold time of the alloy at the SSM temperature can also affect the microstructures. Most, if not all, of the research in this regard has been, however, related to conventional casting of Al-Si alloys and little has been employed in SSM casting of Al-Si alloys.
Accordingly, it is desirable to provide a method of casting SSM Al-Si alloys utilizing both conventional and rheocasting means that can impart desirable mechanical properties. In particular, there is a need for controlling the nucleation of primary Al particles in Al-Si alloys to limit the formation of large primary Al particles.
The foregoing needs are met, to a great extent, by the present invention, wherein in one embodiment a method is provided for using titanium alloys as grain refiners in SSM casting. In some embodiments the titanium alloy may be a titanium boron alloy.
In accordance with another embodiment of the present invention at least one Al-Si hypoeutectic alloy or titanium alloy is heated, the Al-Si hypoeutectic alloy is then mixed with the titanium alloy, the hypoeutectic alloy-titanium alloy mixture is cooled for a length of time to form a semi-solid metal, and then the semi-solid metal is cast. In some embodiments both the Al-Si hypoeutectic alloy and the titanium alloy are heated. The titanium alloy may be a titanium boron alloy and preferably the TIBOR® alloy. The amount of the titanium boron alloy to be added is chosen to achieve a finer Al particle size as compared to casting the Al-Si hypoeutectic alloy without addition of the titanium boron alloy. Generally, the amount of titanium boron alloy is chosen to achieve a cast product having Al particles with an average diameter ranging from about 40 microns to about 60 microns, and preferably also chosen to achieve a cast product with Al particles that are more uniformly dispersed than a cast product made by a conventional SSM rheocasting process without the addition of a titanium boron alloy. The hypoeutectic Al-Si alloy may be less than about 11.7 percent by weight Si, and more preferably, about 6 to about 8 percent Si by weight. The hypoeutectic alloy may also be a 357 alloy.
In accordance with another embodiment of the present invention, an SSM cast product that is manufactured by an SSM casting process using a titanium alloy is provided. The titanium alloy can be a titanium boron alloy and preferably, the TIBOR® alloy.
There has thus been outlined, rather broadly, certain embodiments of the invention in order that the detailed description thereof herein may be better understood, and in order that the present contribution to the art may be better appreciated. There are, of course, additional embodiments of the invention that will be described below and which will form the subject matter of the claims appended hereto.
In this respect, before explaining at least one embodiment of the invention in detail, it is to be understood that the invention is not limited in its application to the details of construction and to the arrangements of the components set forth in the following description or illustrated in the drawings. The invention is capable of embodiments in addition to those described and of being practiced and carried out in various ways. Also, it is to be understood that the phraseology and terminology employed herein, as well as the abstract, are for the purpose of description and should not be regarded as limiting.
As such, those skilled in the art will appreciate that the conception upon which this disclosure is based may readily be utilized as a basis for the designing of other structures, methods and systems for carrying out the several purposes of the present invention. It is important, therefore, that the claims be regarded as including such equivalent constructions insofar as they do not depart from the spirit and scope of the present invention.
The invention will now be described with reference to the drawing figures. An embodiment in accordance with the present invention enables a method for controlling the composition and microstructure of Al-Si alloys prior to SSM casting in an attempt to control the mechanical properties of the final cast product. Generally, this is accomplished by mixing a hypoeutectic Al-Si alloy with a grain refiner. By definition, aluminum alloys with up to but less than about 11.7 weight percent Si are defined “hypoeutectic”, whereas those alloys with greater than about 11.7 weight percent Si are defined “hypereutectic”. In all instances, the term “about” has been incorporated in this disclosure to account for the inherent inaccuracies associated with measuring chemical weights and measurements known and present in the art. Aluminum alloys of this invention are defined to also include varying purities of aluminum.
In one embodiment of the invention, a body of molten aluminum is grain refined by providing in the body a controlled level of a titanium alloy which forms small, discrete titanium compounds such as TiB2 that provide nucleation sites for grain refining aluminum. It will also be appreciated that in order for the titanium to function as a refiner, a material or compound, which first reacts with the titanium and/or the aluminum to form a titanium based grain refiner nuclei, is required. For purposes of the invention, so called reducible binary or titanium reactive material materials may be added separately to the melt or can be included with the titanium as in the form of a metal alloy.
Titanium reactive materials suitable for grain refining in combination with titanium include compounds which provide at least one of the following elements: boron, carbon, sulfur, phosphorus and nitrogen in the molten aluminum. It should be understood that any compound or material may be used which provides an element, which in combination with titanium, operates to provide grain refining nuclei. As noted, however, it is preferred that titanium be introduced in the form of an alloy, which includes the titanium reactive material.
Referring now to
According to the embodiment in
The ladle 50 then next moves into position to receive the titanium alloy 60. Multiple titanium alloys are known and present in the art and may be used in a manner described herein. Even though the invention has been described particularly with respect to titanium alloys, it will be appreciated that other metals are contemplated within the scope of the invention, including but not limited to niobiumin, tantalum, vanadium, molybdenum, zirconium and beryllium. In some embodiments, the titanium boron (TiB) alloy is preferable.
Once the ladle 50 is in the receiving position, a dosing furnace 70 is pressurized through an inlet 80 with preferably compressed air. Any gas, and preferably inert gas, can also be operational. The amount of pressure can be calibrated to accurately and consistently dose substantially equal amounts of the titanium alloy 60. Regardless, with adequate pressure, the titanium alloy 60 is ejected through a spout 90 and into the ladle 50, thereby mixing the titanium alloy 60 with the molten alloy 30. Alternatively, the combined alloys 30 and 60 may be mechanically stirred to adequately mix the alloys.
The ladle 50 is then moved into position over the shot sleeve 10. The contents are poured into the shot sleeve 10 which may optionally be preheated to just above the liquidus temperature of the alloy 30. Once the combined alloys 30 and 60 are cooled to the SSM range, the slurry is then injected by any one of a variety of methods known in the art into the die cavity and proceeds to be cast.
Without being held to or limited by theory, the refining of the aluminum is generally thought to be instantaneous in the art, but longer times may be necessary. It is better, however, to minimize the time between casting the molten aluminum 30 and adding the titanium alloy 60. That is, if the titanium alloy 60 is added earlier, it may permit some settling of the titanium particles to occur. Thus, for purposes of the present invention, to minimize settling (sometimes referred to as fade) of the titanium alloy 60, it is preferred to add the titanium alloy 60 as near the casting time as possible.
Additionally, the growth of Al particles in the semi-solid phase can be directly correlated to the initial temperature and the time of cooling of the alloy before casting. The longer an alloy remains in the semi-solid phase, the likelihood for undesirable growth of large Al particles is increased. Alternatively, shortening the time an alloy spends in the SSM phase before casting minimizes the growth of large Al particles by maximizing the number of nucleating events, producing more Al particles of smaller size.
In some embodiments, the titanium grain refiner, such as TiB, can be added to the molten Al-Si alloy as a metal alloy and preferably, an aluminum metal alloy. TIBOR® is an TiB-Al alloy commercially available from KB Alloys, Inc. located in Reading, Pa. The TIBOR® master alloy supplies titanium in many ratios with boron. In some embodiments, the Ti:B ratio is 5:1 as in TIBOR® Alloy Product No. H2252. No matter the vehicle, the titanium alloy is heated to a liquid state. Generally, the TIBOR® alloy is heated to a range from about 600° C. to about 700° C. and preferably from about 612° C. to about 630° C. in some embodiments.
It should be noted that the titanium alloy 60 can be added anywhere in the process as long as it is added concurrently or prior to casting. Preferably, the titanium alloy 60 is added to the molten alloy 30 as shown in
In the present invention, the amount of titanium refiner material added is important. That is, it is preferred to add the titanium material or compound at a level below its solubility limit in molten aluminum. If the solubility limit of the titanium in molten aluminum is exceeded, then undesirable compound or precipitates form. Further, it is preferred that the titanium concentration is maintained stoichiometrically in excess of the reactive material or compound in the molten aluminum body. Thus, the molar ratio of titanium to reactive material in the melt is maintained such that there is an excess of titanium present in the active nuclei being formed. The concentration and ratio depends to some extent on the titanium reactive material used and can be experimentally determined. In some embodiments, the amount of titanium in the final part will be less than about 1% Ti by weight. In other embodiments the amount of titanium in the final part will range from about 0.2% to about 0.5%
Two separate cross sections of the cast product were taken from the edge and center. Microanalysis of the various sections of the casting demonstrates that the primary Al particles are relatively evenly distributed with minimal aggregate formation. The Al particles are seen as the light colored particles in the microstructure, and the darker background is the eutectic (i.e., a mixture of Al-Si). The Al particles shown range in size from about 40 microns to about 60 microns in diameter from the center of the cast though to the edge of the cast. These results are comparable to the final parts obtained in thixocasting which are prepared to contain Al particles of desirable size and distribution.
Analysis of the edge cross sections of
The presence of the grain refiner provides greater nucleating events than in its absence. This has the desirable effect of generating multiple Al particles that are smaller in size (width and length), but also generally uniformly distributed through out the alloy. The even distribution of the Al particles from the center of the cast product, as best seen in
The many features and advantages of the invention are apparent from the detailed specification, and thus, it is intended by the appended claims to cover all such features and advantages of the invention which fall within the true spirit and scope of the invention. Further, since numerous modifications and variations will readily occur to those skilled in the art, it is not desired to limit the invention to the exact construction and operation illustrated and described, and accordingly, all suitable modifications and equivalents may be resorted to, falling within the scope of the invention.
This application claims priority to U.S. patent application entitled, Semi-Solid Metal Casting Process of Hypoeutectic Aluminum Alloys, filed May 1, 2003, having Ser. No. 10/426,799, the disclosure of which is hereby incorporated by reference.