Embodiments described herein relate to semi-solid electrodes with carbon additives, and methods of making the same. In some embodiments, a semi-solid electrode, can include about 35% to about 75% by volume of an active material, about 0.5% to about 8% by volume of a conductive material, and about 0.2% to about 5% by volume of a carbon additive. The carbon additive is different from the conductive material. The active material, the conductive material, and the carbon additive are mixed with a non-aqueous electrolyte to form the semi-solid electrode. In some embodiments, the carbon additive includes carbon nanofibers, vapor-grown carbon fibers (VCGF), carbon nanotubes (CNT's), single-walled carbon nanotubes (SWNT's), and/or multi-walled carbon nanotubes (MWNT's). In some embodiments, the semi-solid electrode can have a yield stress of less than about 100 kPa. In some embodiments, the semi-solid electrode can have a conductivity of at least about 30 mS/cm, at least about 100 mS/cm, or at least about 130 mS/cm. In some embodiments, the conductive material can include Ketjen, vapor-grown carbon fibers, carbon nanotubes, and/or carbon nanofiber. In some embodiments, the conductive material can include a the conductive material further comprises at least one of a metal, a metal carbide, a metal nitride, a metal oxide, an allotrope of carbon, carbon black, graphitic carbon, carbon fibers, carbon microfibers, VGCF, fullerenic carbons, “buckyballs”, CNT's, MWNT's, SWNT's, graphene sheets, aggregates of graphene sheets, materials comprising fullerenic fragments, electronically insulating organic redox compounds rendered electronically active by mixing or blending with an electronically conductive polymer, polyaniline based conductive polymers, polyacetylene based conductive polymers, poly(3,4-ethylenedioxythiophene) (PEDOT), polypyrrole, polythiophene, poly(p-phenylene), poly(triphenylene), polyazulene, polyfluorene, polynaphtalene, polyanthracene, polyfuran, polycarbazole, tetrathiafulvalene-substituted polystyrene, ferrocene-substituted polyethylene, carbazole-substituted polyethylene, polyoxyphenazine, polyacenes, and/or poly(heteroacenes). In some embodiments, the carbon additive can include VGCF. In some embodiments, the carbon additive can include carbon nanofibers, CNT's, SWNT's, carbon black, and/or MWNT's.
Consumer electronic batteries have gradually increased in energy density with the progress of lithium-ion battery technology. The stored energy or charge capacity of a manufactured battery is a function of: (1) the inherent charge capacity of the active material (mAh/g), (2) the volume of the electrodes (cm3) (i.e., the product of the electrode thickness, electrode area, and number of layers (stacks)), and (3) the loading of active material in the electrode media (e.g., grams of active material per cm3 of electrode media). Therefore, to enhance commercial appeal (e.g., increased energy density and decreased cost), it is generally desirable to increase the areal charge capacity (mAh/cm2) also referred to as “area specific capacity” or “area capacity” herein. The areal charge capacity can be increased, for example, by utilizing active materials that have a higher inherent charge capacity, increasing relative percentage of active charge storing material (i.e., “loading”) in the overall electrode formulation, and/or increasing the relative percentage of electrode material used in any given battery form factor. Said another way, increasing the ratio of active charge storing components (e.g., the electrodes) to inactive components (e.g., the separators and current collectors), increases the overall energy density of the battery by eliminating or reducing components that are not contributing to the overall performance of the battery. One way to accomplish increasing the areal charge capacity, and therefore reducing the relative percentage of inactive components, is by increasing the thickness of the electrodes.
Conventional electrode compositions have capacities of approximately 150-200 mAh/g and generally cannot be made thicker than about 100 μm because of certain performance and manufacturing limitations. For example, i) conventional electrodes having a thickness over 100 μm (single sided coated thickness) typically have significant reductions in their rate capability due to diffusion limitations through the thickness of the electrode (e.g. porosity, tortuosity, impedance, etc.) which grows rapidly with increasing thickness; ii) thick conventional electrodes are difficult to manufacture due to drying and post processing limitations, for example, solvent removal rate, capillary forces during drying that leads to cracking of the electrode, poor adhesion of the electrode to the current collector leading to delamination (e.g., during the high speed roll-to-roll calendering process used for manufacturing conventional electrodes), migration of binder during the solvent removal process and/or deformation during a subsequent compression process; iii) without being bound to any particular theory, the binders used in conventional electrodes may obstruct the pore structure of the electrodes and increase the resistance to diffusion of ions by reducing the available volume of pores and increasing tortuosity (i.e., effective path length) by occupying a significant fraction of the space between the functional components of the electrodes (i.e., active and conductive components). It is also known that binders used in conventional electrodes can at least partially coat the surface of the electrode active materials, which slows down or completely blocks the flow of ions to the active materials, thereby increasing tortuosity.
Furthermore, known conventional batteries either have high capacity or high rate capability, but not both. A battery having a first charge capacity at first C-rate, for example, 0.5 C generally has a second lower charge capacity when discharged at a second higher C-rate, for example, 2 C. This is due to the higher energy loss that occurs inside a conventional battery due to the high internal resistance of conventional electrodes (e.g. solid electrodes with binders), and a drop in voltage that causes the battery to reach the low-end voltage cut-off sooner. The theoretical area specific capacity can hypothetically be increased without limit by increasing the thickness of the electrode and/or by increasing the volume fraction of the active material in the electrode. However, such arbitrary increases in theoretical area specific capacity are not useful if the capacity cannot be used at a practical C-rate. Increases in area specific capacity that cannot be accessed at practical C-rates are highly detrimental to battery performance. The capacity appears as unused mass and volume rather than contributing to stored energy, thereby lowering the energy density and area specific capacity of the battery. Moreover, a thicker electrode generally has a higher internal resistance and therefore a lower rate capability. For example, a lead acid battery does not perform well at 1 C C-rate. They are often rated at a 0.2 C C-rate and even at this low C-rate, they cannot attain 100% capacity. In contrast, ultracapacitors can be discharged at an extremely high C-rate and still maintain 100% capacity, however, they have a much lower capacity than conventional batteries. Accordingly, a need exists for batteries with thicker electrodes, but without the aforementioned limitations. The resulting batteries with superior performance characteristics, for example, superior rate capability and charge capacity, and also are simpler to manufacture.
Semi-solid electrodes described herein can be made: (i) thicker (e.g., greater than about 100 μm-up to about 2,000 μm or even greater) due to the reduced tortuosity and higher electronic conductivity of the semi-solid electrode, (ii) with higher loadings of active materials, (iii) with a simplified manufacturing process utilizing less equipment, and (iv) can be operated between a wide range of C-rates while maintaining a substantial portion of its theoretical charge capacity. These relatively thick semi-solid electrodes decrease the volume, mass and cost contributions of inactive components with respect to active components, thereby enhancing the commercial appeal of batteries made with the semi-solid electrodes. In some embodiments, the semi-solid electrodes described herein are binderless and/or do not use binders that are used in conventional battery manufacturing. Instead, the volume of the electrode normally occupied by binders in conventional electrodes, is now occupied by: 1) electrolyte, which has the effect of decreasing tortuosity and increasing the total salt available for ion diffusion, thereby countering the salt depletion effects typical of thick conventional electrodes when used at high rate, 2) active material, which has the effect of increasing the charge capacity of the battery, or 3) conductive additive, which has the effect of increasing the electronic conductivity of the electrode, thereby countering the high internal impedance of thick conventional electrodes. The reduced tortuosity and a higher electronic conductivity of the semi-solid electrodes described herein, results in superior rate capability and charge capacity of electrochemical cells formed from the semi-solid electrodes. Since the semi-solid electrodes described herein, can be made substantially thicker than conventional electrodes, the ratio of active materials (i.e., the semi-solid cathode and/or anode) to inactive materials (i.e., the current collector and separator) can be much higher in a battery formed from electrochemical cell stacks that include semi-solid electrodes relative to a similar battery formed form electrochemical cell stacks that include conventional electrodes. This substantially increases the overall charge capacity and energy density of a battery that includes the semi-solid electrodes described herein.
In some embodiments, an electrochemical cell includes an anode, and a semi-solid cathode. The semi-solid cathode includes a suspension of about 35% to about 75% by volume of an active material and about 0.5% to about 8% by volume of a conductive material in a non-aqueous liquid electrolyte. An ion-permeable membrane is disposed between the anode and the semi-solid cathode. The semi-solid cathode has a thickness in the range of about 100 μm to about 2,000 μm and the electrochemical cell has an area specific capacity of at least about 7 mAh/cm2 at a C-rate of C/4. In some embodiments, the semi-solid cathode suspension has an electronic conductivity of at least about 10−3 S/cm. In some embodiments, the semi-solid cathode suspension has a mixing index of at least about 0.9.
In some embodiments, an electrochemical cell includes a semi-solid anode and a semi-solid cathode. The semi-solid anode includes a suspension of about 35% to about 75% by volume of a first active material and about 0% to about 10% by volume of a first conductive material in a first non-aqueous liquid electrolyte. The semi-solid cathode includes a suspension of about 35% to about 75% by volume of a second active material, and about 0.5% to about 8% by volume of a second conductive material in a second non-aqueous liquid electrolyte. An ion-permeable membrane is disposed between the semi-solid anode and the semi-solid cathode. Each of the semi-solid anode and the semi-solid cathode have a thickness of about 100 μm to about 2,000 μm and the electrochemical cell has an area specific capacity of at least about 7 mAh/cm2 at a C-rate of C/4. In some embodiments, the first conductive material included in the semi-solid anode is about 0.5% to about 2% by volume. In some embodiments, the second active material included in the semi-solid cathode is about 50% to about 75% by volume.
In some embodiments, an electrochemical cell includes an anode and a semi-solid cathode. The semi-solid cathode includes a suspension of about 35% to about 75% by volume of an active material and about 0.5% to about 8% by volume of a conductive material in a non-aqueous liquid electrolyte. An ion-permeable membrane is disposed between the anode and semi-solid cathode. The semi-solid cathode has a thickness in the range of about 100 μm to about 2,000 μm, and the electrochemical cell has an area specific capacity of at least about 7 mAh/cm2 at a C-rate of C/2. In some embodiments, the semi-solid cathode suspension has a mixing index of at least about 0.9.
In some embodiments, an electrochemical cell includes a semi-solid anode and a semi-solid cathode. The semi-solid anode includes a suspension of about 35% to about 75% by volume of a first active material and about 0% to about 10% by volume of a first conductive material in a first non-aqueous liquid electrolyte. The semi-solid cathode includes a suspension of about 35% to about 75% by volume of a second active material, and about 0.5% to about 8% by volume of a second conductive material in a second non-aqueous liquid electrolyte. An ion-permeable membrane is disposed between the semi-solid anode and the semi-solid cathode. Each of the semi-solid anode and the semi-solid cathode have a thickness of about 100 μm to about 2,000 μm and the electrochemical cell has an area specific capacity of at least about 7 mAh/cm2 at a C-rate of C/2. In some embodiments, the first conductive material included in the semi-solid anode is about 0.5% to about 2% by volume. In some embodiments, the second active material included in the semi-solid cathode is about 50% to about 75% by volume.
In some embodiments, the electrode materials described herein can be a flowable semi-solid or condensed liquid composition. A flowable semi-solid electrode can include a suspension of an electrochemically active material (anodic or cathodic particles or particulates), and optionally an electronically conductive material (e.g., carbon) in a non-aqueous liquid electrolyte. Said another way, the active electrode particles and conductive particles are co-suspended in an electrolyte to produce a semi-solid electrode. Examples of battery architectures utilizing semi-solid suspensions are described in International Patent Publication No. WO 2012/024499, entitled “Stationary, Fluid Redox Electrode,” and International Patent Publication No. WO 2012/088442, entitled “Semi-Solid Filled Battery and Method of Manufacture,” the entire disclosures of which are hereby incorporated by reference. Further examples of semi-solid electrodes and methods of manufacturing the same are described in U.S. Pat. No. 8,993,159, entitled “Semi-Solid Electrodes Having High Rate Capability,” filed Apr. 29, 2013 (the '159 patent), and in U.S. Pat. No. 9,362,583, entitled “Semi-Solid Electrodes Having High Rate Capability,” filed May 22, 2015 (“the '583 patent), the entire disclosures of which are hereby incorporated by reference. In some embodiments, the electrode materials described herein can include one or more polymer additives. Examples of electrodes with polymer additives are described in U.S. Pat. No. 10,122,044, entitled “Semi-solid Electrodes with Gel Polymer Additive,” filed Jul. 21, 2014 (the '044 patent), the entire disclosure of which is hereby incorporated by reference.
In some embodiments, semi-solid electrode compositions (also referred to herein as “semi-solid suspension” and/or “slurry”) described herein can be mixed in a batch process e.g., with a batch mixer that can include, e.g., a high shear mixture, a planetary mixture, a centrifugal planetary mixture, a sigma mixture, a CAM mixture, and/or a roller mixture, with a specific spatial and/or temporal ordering of component addition, as described in more detail herein. In some embodiments, semi-solid electrode compositions described herein can include mixtures of solid and liquid phases. In some embodiments, slurry components can be mixed in a continuous process (e.g. in an extruder), with a specific spatial and/or temporal ordering of component addition.
The mixing and forming of a semi-solid electrode generally includes: (i) raw material conveyance and/or feeding, (ii) mixing, (iii) mixed slurry conveyance, (iv) dispensing and/or extruding, and (v) forming. In some embodiments, multiple steps in the process can be performed at the same time and/or with the same piece of equipment. For example, the mixing and conveyance of the slurry can be performed at the same time with an extruder. Each step in the process can include one or more possible embodiments. For example, each step in the process can be performed manually or by any of a variety of process equipment. Each step can also include one or more sub-processes and, optionally, an inspection step to monitor process quality.
In some embodiments, the process conditions can be selected to produce a prepared slurry having a mixing index of at least about 0.80, at least about 0.90, at least about 0.95, or at least about 0.975. In some embodiments, the process conditions can be selected to produce a prepared slurry having an electronic conductivity of at least about 10−6 S/cm, at least about 10−5 S/cm, at least about 10−4 S/cm, at least about 10−3 S/cm, or at least about 10−2 S/cm. In some embodiments, the process conditions can be selected to produce a prepared slurry having an apparent viscosity at room temperature of less than about 100,000 Pa-s, less than about 10,000 Pa-s, or less than about 1,000 Pa-s, all at an apparent shear rate of 1,000 s−1. In some embodiments, the process conditions can be selected to produce a prepared slurry having two or more properties as described herein. Examples of systems and methods that can be used for preparing the semi-solid compositions and/or electrodes are described in U.S. Pat. No. 9,484,569, (“the '569 patent”) filed Mar. 15, 2013, entitled “Electrochemical Slurry Compositions and Methods for Preparing the Same,” the entire disclosure of which is hereby incorporated by reference.
As used herein, the term “about” and “approximately” generally mean plus or minus 10% of the value stated, e.g., about 250 μm would include 225 μm to 275 μm, about 1,000 μm would include 900 μm to 1,100 μm.
As used herein, the term “semi-solid” refers to a material that is a mixture of liquid and solid phases, for example, such as particle suspension, colloidal suspension, emulsion, gel, or micelle.
As used herein, the term “condensed ion-storing liquid” or “condensed liquid” refers to a liquid that is not merely a solvent, as in the case of an aqueous flow cell semi-solid cathode or anode, but rather, it is itself redox active. Of course, such a liquid form may also be diluted by or mixed with another, non-redox active liquid that is a diluent or solvent, including mixing with such a diluent to form a lower-melting liquid phase, emulsion or micelles including the ion-storing liquid.
As used herein, the terms “activated carbon network” and “networked carbon” relate to a general qualitative state of an electrode. For example, an electrode with an activated carbon network (or networked carbon) is such that the carbon particles within the electrode assume an individual particle morphology and arrangement with respect to each other that facilitates electrical contact and electrical conductivity between particles and through the thickness and length of the electrode. Conversely, the terms “unactivated carbon network” and “unnetworked carbon” relate to an electrode wherein the carbon particles either exist as individual particle islands or multi-particle agglomerate islands that may not be sufficiently connected to provide adequate electrical conduction through the electrode.
As used herein, the term “area specific capacity”, “area capacity”, or “areal capacity” are used interchangeably to define the charge capacity of an electrode or an electrochemical cell per unit area having units of mAh/cm2.
In some embodiments, an electrochemical cell for storing energy includes an anode, a semi-solid cathode including a suspension of an active material and a conductive material in a non-aqueous liquid electrolyte, and an ion permeable separator disposed between the anode and the cathode. The semi-solid cathode can have a thickness in the range of about 100 μm to about 2,000 μm. In some embodiments, the electrochemical cell is configured such that at a C-rate of C/4, the electrochemical cell has an area specific capacity of at least about 7 mAh/cm2, at least about 8 mAh/cm2, at least about 9 mAh/cm2, or at least about 10 mAh/cm2. In some embodiments, at a C-rate of C/2, the electrochemical cell has an area specific capacity of at least about 7 mAh/cm2, at least about 8 mAh/cm2, or at least about 9 mAh/cm2. In some embodiments, at a C-rate of 1 C, the electrochemical cell has an area specific capacity of at least about 4 mAh/cm2, at least about 5 mAh/cm2, at least about 6 mAh/cm2, or at least about 7 mAh/cm2. In some embodiments, at a C-rate of 2 C, the electrochemical cell has an area specific capacity of at least about 3 mAh/cm2, at least about 4 mAh/cm2, or at least about 5 mAh/cm2. In some embodiments, at C-rates between about 2 C and about 5 C, the electrochemical cell has an area specific capacity of at least about 1 mAh/cm2, or at least about 2 mAh/cm2.
In some embodiments, the thickness of the semi-solid cathode is at least about 100 μm. In some embodiments, the thickness of the semi-solid cathode is at least about 110 μm. In some embodiments, the thickness of the semi-solid cathode is at least about 120 μm. In some embodiments, the thickness of the semi-solid cathode is at least about 130 μm. In some embodiments, the thickness of the semi-solid cathode is at least about 140 μm. In some embodiments, the thickness of the semi-solid cathode is at least about 150 μm. In some embodiments, the thickness of the semi-solid cathode is at least about 200 μm. In some embodiments, the thickness of the semi-solid cathode is at least about 250 μm. In some embodiments, the thickness of the semi-solid electrodes can be at least about 300 μm, at least about 350 μm, at least about 400 μm, at least about 450 μm, at least about 500 μm, at least about 600 μm, at least about 700 μm, at least about 800 μm, at least about 900 μm, at least about 1,000 μm, at least about 1,500 μm, and up to about 2,000 μm, inclusive of all thicknesses therebetween.
In some embodiments, the anode can be a conventional anode, for example, a lithium metal anode or a calendered anode. In some embodiments, the anode can be a semi-solid anode that can have a thickness that is substantially similar to the thickness of the semi-solid cathode such as, for example, of at least about 100 μm, at least about 110 μm, at least about 120 μm, at least about 130 μm, at least about 140 μm, at least about 150 μm, at least about 200 μm, at least about 250 μm, at least about 300 μm, at least about 350 μm, at least about 400 μm, at least about 450 μm, at least about 500 μm, and so on.
In some embodiments, the thickness of the semi-solid electrodes can be in the range of about 100 μm to about 2,000 μm, about 110 μm to about 2,000 μm, about 120 μm to about 2,000 μm, about 130 μm to about 2,000 μm, about 140 μm to about 2,000 μm, about 150 μm to about 2,000 μm, about 200 μm to about 2,000 μm, about 250 μm to about 2,000 μm, about 300 μm to about 2,000 μm, about 350 μm to about 2,000 μm, 400 μm to about 2,000 μm, about 450 μm to about 2,000 μm, about 500 to about 2,000 μm, about 150 μm to about 1,500 μm, about 200 μm to about 1,500 μm, about 250 μm to about 1,500 μm, about 300 μm to about 1,500 μm, about 350 μm to about 1,500 μm, about 400 μm to about 1,500 μm, about 450 μm to about 1,500 μm, about 500 to about 1,500 μm, about 100 μm to about 1,500 μm, about 110 μm to about 1,500 μm, about 120 μm to about 1,500 μm, about 130 μm to about 1,500 μm, about 140 μm to about 1,500 μm, about 150 μm to about 1,500 μm, about 200 μm to about 1,500 μm, about 250 μm to about 1,000 μm, about 300 μm to about 1,000 μm, about 350 μm to about 1,000 μm, about 400 μm to about 1,000 μm, about 450 μm to about 1,000 μm, about 500 μm to about 1,000 μm, about 100 μm to about 750 μm, about 110 μm to about 750 μm, about 120 μm to about 750 μm, about 130 μm to about 750 μm, about 140 μm to about 750 μm, about 150 μm to about 750 μm, about 200 μm to about 750 μm, about 250 μm to about 750 μm, about 300 μm to about 750 μm, about 350 μm to about 750 μm, about 400 μm to about 750 μm, about 450 μm to about 750 μm, about 500 μm to about 750 μm, about 150 μm to about 700 μm, about 100 μm to about 700 μm, about 110 μm to about 700 μm, about 120 μm to about 700 μm, about 130 μm to about 700 μm, about 140 μm to about 700 μm, about 150 μm to about 700 μm, about 250 μm to about 700 μm, about 300 μm to about 700 μm, about 350 μm to about 700 μm, about 400 μm to about 700 μm, about 450 μm to about 700 μm, about 500 μm to about 700 μm, about 100 μm to about 650 μm, about 110 μm to about 650 μm, about 120 μm to about 650 μm, about 130 μm to about 650 μm, about 140 μm to about 650 μm, about 150 μm to about 650 μm, about 150 μm to about 650 μm, about 250 μm to about 650 μm, about 300 μm to about 650 μm, about 350 μm to about 650 μm, about 400 μm to about 650 μm, about 450 μm to about 650 μm, about 500 μm to about 650 μm, about 100 μm to about 600 μm, about 110 μm to about 600 μm, about 120 μm to about 600 μm, about 130 μm to about 600 μm, about 140 μm to about 600 μm, about 150 μm to about 600 μm, about 150 μm to about 600 μm, about 250 μm to about 600 μm, about 300 μm to about 600 μm, about 350 μm to about 600 μm, about 400 μm to about 600 μm, about 450 μm to about 600 μm, about 500 μm to about 600 μm, about 100 μm to about 550 μm, about 110 μm to about 550 μm, about 120 μm to about 550 μm, about 130 μm to about 550 μm, about 140 μm to about 550 μm, about 150 μm to about 550 μm, about 150 μm to about 550 μm, about 250 μm to about 550 μm, about 300 μm to about 550 μm, about 350 μm to about 550 μm, about 400 μm to about 550 μm, about 450 μm to about 550 μm, or about 500 μm to about 550 μm, inclusive of all ranges or any other distance therebetween.
In some embodiments, a semi-solid anode can include an anode active material selected from lithium metal, carbon, lithium-intercalated carbon, lithium nitrides, lithium alloys and lithium alloy forming compounds of silicon, bismuth, boron, gallium, indium, zinc, tin, tin oxide, antimony, aluminum, titanium oxide, molybdenum, germanium, manganese, niobium, vanadium, tantalum, gold, platinum, iron, copper, chromium, nickel, cobalt, zirconium, yttrium, molybdenum oxide, germanium oxide, silicon oxide, silicon carbide, any other materials or alloys thereof, and any other combination thereof.
In some embodiments, a semi-solid cathode can include about 35% to about 75% by volume of an active material. In some embodiments, a semi-solid cathode can include about 40% to about 75% by volume, about 45% to about 75% by volume, about 50% to about 75% by volume, about 55% to about 75% by volume, about 60% to about 75% by volume, or about 65% to about 75% by volume of an active material, inclusive of all ranges therebetween.
In some embodiments, a semi-solid cathode can include about 0.5% to about 8% by volume of a conductive material. For example, in some embodiments, a semi-solid cathode can include about about 0.6% to about 7.5% by volume, about 0.7% to about 7.0% by volume, about 0.8% to about 6.5% by volume, about 0.9% to about 6% by volume, about 1.0% to about 6% by volume, about 1.5% to about 5.0% by volume, or about 2% to about 4% by volume of a conductive material, inclusive of all ranges therebetween.
In some embodiments, a semi-solid cathode can include about 25% to about 70% by volume of an electrolyte. In some embodiments, a semi-solid cathode can include about 30% to about 50%, or about 20% to about 40% by volume of an electrolyte, inclusive of all ranges therebetween.
In some embodiments, a semi-solid anode can include about 35% to about 75% by volume of an active material. In some embodiments, a semi-solid anode can include about 40% to about 75% by volume, about 45% to about 75% by volume, about 50% to about 75% by volume, about 55% to about 75% by volume, about 60% to about 75% by volume, or about 65% to about 75% by volume of an active material, inclusive of all ranges therebetween.
In some embodiments, a semi-solid anode can include about 0% to about 10% by volume of a conductive material. In some embodiments, a semi-solid anode can include about 0.2% to about 9% by volume, about 0.4% to about 8% by volume, about 0.6% to about 7% by volume, about 0.8% to about 6% by volume, about 1% to about 5% by volume, or about 2% to about 4% by volume of a conductive material, inclusive of all ranges therebetween. In some embodiments, the semi-solid anode includes about 1% to about 6% by volume of a conductive material. In some embodiments, the semi-solid anode includes about 0.5% to about 2% by volume of a conductive material.
In some embodiments, a semi-solid anode can include about 10% to about 70% by volume of an electrolyte. In some embodiments, a semi-solid anode can include about 30% to about 50%, or about 20% to about 40% by volume of an electrolyte, inclusive of all ranges therebetween.
In some embodiments, a semi-solid cathode or semi-solid anode can include less than about 10% by volume of a polymeric binder. In some embodiments, a semi-solid cathode or semi-solid anode can include less than about 5% by volume, or less than about 3% by volume, or less than about 1% by volume of a polymeric binder. In some embodiments, the polymeric binder comprises polyvinylidene difluoride (PVdF).
In some embodiments, an electrochemical cell includes a semi-solid cathode that can include about 35% to about 75% by weight of an active material, about 0.5% to about 8% by weight of a conductive material, and about 20% to about 40% by weight of a non-aqueous liquid electrolyte. The semi-solid cathode suspension can have mixing index of at least about 0.9. The semi-solid cathode can have a thickness in the range of about 100 μm to about 2,000 μm. The electrochemical cell also includes a semi-solid anode that can include about 35% to about 75% by weight of an active material, about 1% to about 10% by weight of a conductive material, and about 20% to about 40% by weight of a non-aqueous liquid electrolyte. The semi-solid anode suspension can have a mixing index of at least about 0.9. The semi-solid anode can have a thickness in the range of about 100 μm to about 2,000 μm. The semi-solid anode and the semi-solid cathode are separated by an ion permeable membrane disposed therebetween. In such embodiments, the electrochemical cell can have an area specific capacity of at least about 7 mAh/cm2.
The semi-solid cathode 140 and/or anode 150 can be disposed on the positive current collector 110 and the negative current collector 120, respectively using any suitable method, for example, coated, casted, drop coated, pressed, roll pressed, or deposited. The positive current collector 110 and the negative current collector 120 can be any current collectors that are electronically conductive and are electrochemically inactive under the operation conditions of the cell. Typical current collectors for lithium cells include copper, aluminum, or titanium for the negative current collector and aluminum for the positive current collector, in the form of sheets or mesh, or any combination thereof. Current collector materials can be selected to be stable at the operating potentials of the positive and negative electrodes of an electrochemical cell 100. For example, in non-aqueous lithium systems, the positive current collector 110 can include aluminum, or aluminum coated with conductive material that does not electrochemically dissolve at operating potentials of 2.5-5.0V with respect to Li/Li+. Such materials include platinum, gold, nickel, conductive metal oxides such as vanadium oxide, and carbon. The negative current collector 120 can include copper or other metals that do not form alloys or intermetallic compounds with lithium, carbon, and/or coatings comprising such materials disposed on another conductor.
The separator 130 is disposed between the semi-solid cathode 140 and the anode 150 (e.g., a semi-solid anode) can be any conventional membrane that is capable of ion transport. In some embodiments, the separator 130 is a liquid impermeable membrane that permits the transport of ions therethrough, namely a solid or gel ionic conductor. In some embodiments the separator 130 is a porous polymer membrane infused with a liquid electrolyte that allows for the shuttling of ions between the cathode 140 and anode 150 electroactive materials, while preventing the transfer of electrons. In some embodiments, the separator 130 is a microporous membrane that prevents particles forming the positive and negative electrode compositions from crossing the membrane. In some embodiments, the separator 130 is a single or multilayer microporous separator, optionally with the ability to fuse or “shut down” above a certain temperature so that it no longer transmits working ions, of the type used in the lithium ion battery industry and well-known to those skilled in the art. In some embodiments, the separator 130 material can include polyethyleneoxide (PEO) polymer in which a lithium salt is complexed to provide lithium conductivity, or Nafion™ membranes which are proton conductors. For example, PEO based electrolytes can be used as the membrane, which is pinhole-free and a solid ionic conductor, optionally stabilized with other membranes such as glass fiber separators as supporting layers. PEO can also be used as a slurry stabilizer, dispersant, etc. in the positive or negative redox compositions. PEO is stable in contact with typical alkyl carbonate-based electrolytes. This can be especially useful in phosphate-based cell chemistries with cell potential at the positive electrode that is less than about 3.6 V with respect to Li metal. The operating temperature of the redox cell can be elevated as necessary to improve the ionic conductivity of the membrane.
The cathode 140 can be a semi-solid stationary cathode or a semi-solid flowable cathode, for example of the type used in redox flow cells. The cathode 140 can include an active material such as a lithium bearing compound as described in further detail below. The cathode 140 can also include a conductive material such as, for example, graphite, carbon powder, pyrolytic carbon, carbon black, carbon fibers, carbon microfibers, carbon nanotubes (CNTs), single walled CNTs, multi walled CNTs, fullerene carbons including “bucky balls,” graphene sheets and/or aggregate of graphene sheets, any other conductive material, alloys or combination thereof. The cathode 140 can also include a non-aqueous liquid electrolyte as described in further detail below.
In some embodiments, the anode 150 can be a semi-solid stationary anode. In some embodiments, the anode 150 can be a semi-solid flowable anode, for example, of the type used in redox flow cells.
The anode 150 can also include a carbonaceous material such as, for example, graphite, carbon powder, pyrolytic carbon, carbon black, carbon fibers, carbon microfibers, carbon nanotubes (CNTs), single walled CNTs, multi walled CNTs, fullerene carbons including “bucky balls”, graphene sheets and/or aggregate of graphene sheets, any other carbonaceous material or combination thereof. In some embodiments, the anode 150 can also include a non-aqueous liquid electrolyte as described in further detail herein.
In some embodiments, the semi-solid cathode 140 and/or the anode 150 (e.g. a semi-solid anode) can include active materials and optionally conductive materials in particulate form suspended in a non-aqueous liquid electrolyte. In some embodiments, the semi-solid cathode 140 and/or anode 150 particles (e.g., cathodic or anodic particles) can have an effective diameter of at least about 1 μm. In some embodiments, the cathodic or anodic particles can have an effective diameter between about 1 μm and about 10 μm. In other embodiments, the cathodic or anodic particles can have an effective diameter of at least about 10 μm or more. In some embodiments, the cathodic or anodic particles can have an effective diameter of at less than about 1 μm. In other embodiments, the cathodic or anodic particles can have an effective diameter of at less than about 0.5 μm. In other embodiments, the cathodic or anodic particles can have an effective diameter of at less than about 0.25 μm. In other embodiments, the cathodic or anodic particles can have an effective diameter of at less than about 0.1 μm. In other embodiments, the cathodic or anodic particles can have an effective diameter of at less than about 0.05 μm. In other embodiments, the cathodic or anodic particles can have an effective diameter of at less than about 0.01 μm.
In some embodiments, the semi-solid cathode 140 can include about 35% to about 75% by volume of an active material. In some embodiments, the semi-solid cathode 140 can include about 40% to about 75% by volume, 45% to about 75% by volume, about 50% to about 75% by volume, about 55% to about 75% by volume, about 60% to about 75% by volume, or about 65% to about 75% by volume of an active material, inclusive of all ranges therebetween.
In some embodiments, the semi-solid cathode 140 can include at least about 35%, at least about 40%, at least about 45%, at least about 50%, at least about 55%, at least about 60%, at least about 65%, at least about 70%, at least about 75%, or at least about 80% by volume of an active material. In some embodiments, the semi-solid cathode 140 can include no more than about 85%, no more than about 80%, no more than about 75%, no more than about 70%, no more than about 65%, no more than about 60%, no more than about 55%, no more than about 50%, no more than about 45%, or no more than about 40% by volume of an active material. Combinations of the above referenced ranges of the volume percentage of active material in the semi-solid cathode 140 are also possible (e.g., at least about 35% and no more than about 85% by volume or at least about 55% and no more than about 60% by volume), inclusive of all values and ranges therebetween. In some embodiments, the semi-solid cathode 140 can include about 35%, about 40%, about 45%, about 50%, about 55%, about 60%, about 65%, about 70%, about 75%, about 80%, or about 85% by volume of an active material.
In some embodiments, the semi-solid cathode 140 can include about 0.5% to about 8% by volume of a conductive material. In some embodiments, the semi-solid cathode 140 can include about 0.6% to about 7.5% by volume, about 0.7% to about 7.0% by volume, about 0.8% to about 6.5% by volume, about 0.9% to about 6% by volume, about 1.0% to about 6%, about 1.5% to about 5.0% by volume, or about 2% to about 4% by volume of a conductive material, inclusive of all ranges therebetween.
In some embodiments, the semi-solid cathode 140 can include at least about 0.5%, at least about 0.6%, at least about 0.7%, at least about 0.8%, at least about 0.9%, at least about 1%, at least about 1.5%, at least about 2%, at least about 2.5%, at least about 3%, at least about 3.5%, at least about 4%, at least about 4.5%, at least about 5%, at least about 5.5%, at least about 6%, at least about 6.5%, at least about 7%, or at least about 7.5% by volume of a conductive material. In some embodiments, the semi-solid cathode 140 can include no more than about 8%, no more than about 7.5%, no more than about 7%, no more than about 6.5%, no more than about 6%, no more than about 5.5%, no more than about 5%, no more than about 4.5%, no more than about 4%, no more than about 3.5%, no more than about 3%, no more than about 2.5%, no more than about 2%, no more than about 1.5%, no more than about 1%, no more than about 0.9%, no more than about 0.8%, no more than about 0.7%, or no more than about 0.6% by volume of a conductive material. Combinations of the above-referenced volume percentage of conductive material in the semi-solid cathode 140 are also possible (e.g., at least about 0.5% and no more than about 8% by volume or at least about 0.7% and no more than about 1.5% by volume), inclusive of all values and ranges therebetween. In some embodiments, the semi-solid cathode 140 can include about 0.5%. about 0.6%, about 0.7%, about 0.8%, about 0.9%, about 1%, about 1.5%, about 2%, about 2.5%, about 3%, about 3.5%, about 4%, about 4.5%, about 5%, about 5.5%, about 6%, about 6.5%, about 7%, about 7.5%, or about 8% by volume of a conductive material.
In some embodiments, the semi-solid cathode 140 can include a carbon additive. The addition of a carbon additive can improve the conductivity of the semi-solid cathode 140 such that less conductive material can be used. In some embodiments, the inclusion of the carbon additive in the semi-solid cathode 140 can enable the semi-solid cathode 140 to have less carbon overall than a semi-solid cathode 140 without the carbon additive. Said another way, the carbon additive can at least partially replace the conductive material and have a greater effect per unit mass than the conductive material, such that less overall carbon can be included in the semi-solid cathode 140 with the carbon additive. Similar conductivity can be achieved with less material. Improved conductivity can lead to slower area specific impedance (ASI) growth better capacity retention in electrochemical cells.
In some embodiments, the carbon additive can coat the active material. In some embodiments, coating active material particles in the semi-solid cathode 140 with the carbon additive can improve the conductivity of the semi-solid cathode 140 while balancing the stiffness of the semi-solid cathode 140. The inclusion of a carbon additive in the semi-solid cathode 140 can increase the conductivity and the cycling performance of the semi-solid cathode 140 without substantially increasing the yield strength of the semi-solid cathode 140. Increased yield strength can lead to solid-like behavior in the semi-solid cathode 140, so preventing an increase in yield strength can aid in maintaining the semi-solid properties (e.g., malleability, dispensability) of the semi-solid cathode 140. In some embodiments, the carbon additive can be different from the conductive material. In some embodiments, the carbon additive can be chemically different from the conductive material. In some embodiments, the carbon additive can have a different crystalline structure from the conductive material. In some embodiments, the carbon additive can include CNF. In some embodiments, the carbon additive can include VGCF. In some embodiments, the carbon additive can include carbon nanotubes. In some embodiments, the carbon additive can include single-walled carbon nanotubes. In some embodiments, the carbon additive can include multi-walled carbon nanotubes. In some embodiments, the carbon additive can include carbon black. In some embodiments, the carbon additive can have a 2-dimensional (2D) morphology. In some embodiments, coating the active material with a carbon additive with 2D morphology can provide good mixing and consistent slurry conductivity throughout the semi-solid cathode 140. In some embodiments, the carbon additive can include graphene with a 2D layered structure. In some embodiments, the carbon additive can include expanded graphite with a 2D layered structure. In some embodiments, the carbon additive can have a lower surface area than the conductive material. Without wishing to be bound by any particular theory, a material with a high surface area can absorb a large amount of liquid, effectively drying up the electrolyte in the semi-solid cathode 140, causing the semi-solid cathode 140 to behave more like a solid than a semi-solid.
In some embodiments, the active material and the conductive material can be dry-mixed to form a mixture. In some embodiments, the active material, the conductive material, and the carbon additive can be dry-mixed to form a mixture. In some embodiments, the active material and the carbon additive can be dry-mixed to form a mixture. In some embodiments, the dry-mixing can include milling. In some embodiments, the electrolyte can be added to the mixture to form a semi-solid electrode material.
In some embodiments, the active material and the conductive material can be dry-mixed during a first time period to form a first mixture, and the carbon additive can be added to the first mixture during a second time period to form a second mixture. In some embodiments, the active material and a first amount of the carbon additive can be dry-mixed during a first time period to form a first mixture, and a second amount of the carbon additive can be added to the first mixture during a second time period to form a second mixture. In some embodiments, the dry-mixing can include milling. In some embodiments, the electrolyte can be added to the second mixture to form a semi-solid electrode material.
In some embodiments, the active material and the conductive material can be milled together to form a mixture. In some embodiments, the active material and the carbon additive can be milled together to form a mixture. In some embodiments, the active material, the conductive material, and the carbon additive can be milled together to form a mixture. In some embodiments, the conductive material, the active material, and the electrolyte can be milled together to form a mixture. In some embodiments, the active material, the conductive material, the carbon additive, and the electrolyte can be milled together to form a mixture. In some embodiments, the milling can be for a time sufficient to coat the active material particles in very fine particles of conductive material and/or carbon additive. In some embodiments, the milling can be at a low enough milling power or milling shear force such that the active material particles are not significantly fractured.
In some embodiments, the active material, the conductive material, the carbon additive, and/or the electrolyte can be milled together via blade mixing. In some embodiments, the blade mixing can be via a rotating blade. In some embodiments, the blade mixing can be via a fixed blade. In some embodiments, the active material, the conductive material, the carbon additive, and/or the electrolyte can be directly mixed via a V-blender. In some embodiments, the active material, the conductive material, the carbon additive, and/or the electrolyte can be mixed via ball milling in a ball mill. In some embodiments, active material, the conductive material, the carbon additive, and/or the electrolyte can be mixed via roller milling in a roller mill.
In some embodiments, the electrolyte can be added before the mixing or milling process. In some embodiments, electrolyte can be added during the mixing or milling process. In other words, the mixing or milling process can include wet mixing or wet milling. In some embodiments, the electrolyte can include an electrolyte with a high boiling temperature, such that a high shear energy can be applied to the mixture during mixing without the electrolyte boiling away. In other words, incorporating an electrolyte with a high boiling point into the mixture can aid in keeping the mixture as a semi-solid during mixing or milling, such that it does not dry up and become a solid. Some carbon additives can be difficult to break down into smaller particles, so a higher shear energy can more easily break down these carbon additives. In some embodiments, the electrolyte can include ethylene carbonate (EC), propylene carbonate (PC), γ-butyrolactone (GBL), or any combination thereof.
In some embodiments, a solvent can be added before the mixing or milling process. In some embodiments, the solvent can be added during the mixing or milling process. In other words, the mixing or milling process can include wet mixing or wet milling. In some embodiments, the solvent can include a solvent with a high boiling temperature, such that a high shear energy can be applied to the mixture during mixing without the solvent boiling away. In other words, incorporating a solvent with a high boiling point into the mixture can aid in keeping the mixture as a semi-solid during mixing or milling, such that it does not dry up and become a solid. Some carbon additives can be difficult to break down into smaller particles, so a higher shear energy can more easily break down these carbon additives. Also, carbon additive particles can disperse in organic solvents more easily than active material particles. Adding a solvent with a high boiling point can act as a buffer between the carbon additive particles and the active material particles. Also, the solvent can act as a buffer between the active material and the mixing media (e.g., mixing impeller). This buffer can aid in preventing the active material particles from breaking down. Additionally, the use of a solvent with a high boiling point can aid in reducing temperature rise during mixing or milling, as heat is distributed to the liquid. Also, if the solvent does not include an electrolyte salt (e.g., LiPF6), and the electrolyte salt is added after the mixing or milling, this can aid in preventing the electrolyte salt from being broken down during mixing. In some embodiments, the solvent can include ethylene carbonate (EC), propylene carbonate (PC), γ-butyrolactone (GBL), or any combination thereof. In some embodiments, the solvent can be free or substantially free of salts (i.e., the solvent can be a non-electrolyte). In some embodiments, the electrolyte can be added to the mixture after the solvent, the active material, the conductive material, and/or the carbon additive have been mixed or milled together. In some embodiments, the electrolyte can be added via spraying. In some embodiments, the electrolyte can be added via injection.
In some embodiments, the milling or mixing can be for at least about 5 minutes, at least about 6 minutes, at least about 7 minutes, at least about 8 minutes, at least about 9 minutes, at least about 10 minutes, at least about 11 minutes, at least about 12 minutes, at least about 13 minutes, at least about 14 minutes, at least about 15 minutes, at least about 16 minutes, at least about 17 minutes, at least about 18 minutes, at least about 19 minutes, at least about 20 minutes, at least about 21 minutes, at least about 22 minutes, at least about 23 minutes, at least about 24 minutes, at least about 25 minutes, at least about 26 minutes, at least about 27 minutes, at least about 28 minutes, at least about 29 minutes, or at least about 30 minutes.
The energy imparted by the milling or mixing can be fine-tuned to the composition of the semi-solid cathode 140. For example, Ketjen can require significantly more energy to break apart than carbon fibers. Mixing energy should be substantially high to break agglomerations of carbon-containing particles, but not so high that it breaks the particles of the semi-solid cathode 140 (i.e., the active particles, the carbon-containing particles, and the conductive particles) apart from each other. Mixing energy can influence the yield strength of the semi-solid cathode 140. In some embodiments, a semi-solid cathode 140 with a relatively low yield stress can have better cycling stability than a semi-solid electrode with a high yield stress. Without being bound by any particular theory, low yield stress in the semi-solid cathode 140 can improve the spreading quality of the semi-solid cathode 140. Low yield stress in the semi-solid cathode 140 can correlate to a desired piston pressure to ensure little or no phase separation during the spreading of the semi-solid cathode 140. Low yield stress can make the semi-solid cathode 140 more uniformly mixed at a given mixing energy due to the more flowable composition of the semi-solid cathode 140. Also, tap density of the carbon additive in the semi-solid cathode 140 can increase with decreasing yield strength, such that the electrolyte will be freed up to further wet the surfaces of the particles in the semi-solid cathode 140.
In some embodiments, the milling or mixing can impart a mixing energy of at least about 400 kJ/kg, at least about 450 kJ/kg, at least about 500 kJ/kg, at least about 550 kJ/kg, at least about 600 kJ/kg, at least about 650 kJ/kg, at least about 700 kJ/kg, at least about 750 kJ/kg, at least about 800 kJ/kg, at least about 850 kJ/kg, at least about 900 kJ/kg, at least about 950 kJ/kg, at least about 1,000 kJ/kg, at least about 1,050 kJ/kg, at least about 1,100 kJ/kg, at least about 1,150 kJ/kg, at least about 1,200 kJ/kg, at least about 1,250 kJ/kg, at least about 1,300 kJ/kg, at least about 1,350 kJ/kg, at least about 1,400 kJ/kg, at least about 1,450 kJ/kg, at least about 1,500 kJ/kg, at least about 1,550 kJ/kg, at least about 1,600 kJ/kg, at least about 1,650 kJ/kg, at least about 1,700 kJ/kg, at least about 1,750 kJ/kg, at least about 1,800 kJ/kg, at least about 1,850 kJ/kg, at least about 1,900 kJ/kg, at least about 1,950 kJ/kg, at least about 2,000 kJ/kg, at least about 2,100 kJ/kg, at least about 2,200 kJ/kg, at least about 2,300 kJ/kg, at least about 2,400 kJ/kg, at least about 2,500 kJ/kg, at least about 2,600 kJ/kg, at least about 2,700 kJ/kg, at least about 2,800 kJ/kg, at least about 2,900 kJ/kg, or at least about 3,000 kJ/kg. In some embodiments, the milling or mixing can impart a mixing energy of no more than about 3,000 kJ/kg, no more than about 2,900 kJ/kg, no more than about 2,800 kJ/kg, no more than about 2,700 kJ/kg, no more than about 2,600 kJ/kg, no more than about 2,500 kJ/kg, no more than about 2,400 kJ/kg, no more than about 2,300 kJ/kg, no more than about 2,200 kJ/kg, no more than about 2,100 kJ/kg, no more than about 2,000 kJ/kg, no more than about 1,950 kJ/kg, no more than about 1,900 kJ/kg, no more than about 1,850 kJ/kg, no more than about 1,800 kJ/kg, no more than about 1,750 kJ/kg, no more than about 1,700 kJ/kg, no more than about 1,650 kJ/kg, no more than about 1,600 kJ/kg, no more than about 1,550 kJ/kg, no more than about 1,500 kJ/kg, no more than about 1,450 kJ/kg, no more than about 1,400 kJ/kg, no more than about 1,350 kJ/kg, no more than about 1,300 kJ/kg, no more than about 1,250 kJ/kg, no more than about 1,200 kJ/kg, no more than about 1,150 kJ/kg, no more than about 1,100 kJ/kg, no more than about 1,050 kJ/kg, no more than about 1,000 kJ/kg, no more than about 950 kJ/kg, no more than about 900 kJ/kg, no more than about 850 kJ/kg, no more than about 800 kJ/kg, no more than about 750 kJ/kg, no more than about 700 kJ/kg, no more than about 650 kJ/kg, no more than about 600 kJ/kg, or no more than about 550 kJ/kg.
Combinations of the above-referenced mixing energy ranges are also possible (e.g., at least about 400 kJ/kg and no more than about 3,000 kJ/kg or at least about 500 kJ/kg and no more than about 1,000 kJ/kg), inclusive of all values and ranges therebetween. In some embodiments, the milling or mixing can impart a mixing energy of about 400 kJ/kg, about 450 kJ/kg, about 500 kJ/kg, about 550 kJ/kg, about 600 kJ/kg, about 650 kJ/kg, about 700 kJ/kg, about 750 kJ/kg, about 800 kJ/kg, about 850 kJ/kg, about 900 kJ/kg, about 950 kJ/kg, about 1,000 kJ/kg, about 1,050 kJ/kg, about 1,100 kJ/kg, about 1,150 kJ/kg, about 1,200 kJ/kg, about 1,250 kJ/kg, about 1,300 kJ/kg, about 1,350 kJ/kg, about 1,400 kJ/kg, about 1,450 kJ/kg, about 1,500 kJ/kg, about 1,550 kJ/kg, about 1,600 kJ/kg, about 1,650 kJ/kg, about 1,700 kJ/kg, about 1,750 kJ/kg, about 1,800 kJ/kg, about 1,850 kJ/kg, about 1,900 kJ/kg, about 1,950 kJ/kg, about 2,000 kJ/kg, about 2,100 kJ/kg, about 2,200 kJ/kg, about 2,300 kJ/kg, about 2,400 kJ/kg, about 2,500 kJ/kg, about 2,600 kJ/kg, about 2,700 kJ/kg, about 2,800 kJ/kg, about 2,900 kJ/kg, or about 3,000 kJ/kg.
Milling power can also be fine-tuned to the composition of the electrode. In other words, milling power should be sufficiently high to break up agglomerates of carbon additives but not high enough to significantly damage the molecules of the carbon additives. For example, materials with long chain structures should be subject to low milling powers so that the long chain structures do not break during the milling. In some embodiments, the milling or mixing can impart a mixing power of at least about 4 kW/kg, at least about 4.5 kW/kg, at least about 5 kW/kg, at least about 5.5 kW/kg, at least about 6 kW/kg, at least about 6.5 kW/kg, at least about 6.7 kW/kg, at least about 7 kW/kg, at least about 7.5 kW/kg, at least about 8 kW/kg, at least about 8.5 kW/kg, at least about 9 kW/kg, or at least about 9.5 kW/kg. In some embodiments, the milling or mixing can impart a mixing power of no more than about 10 kW/kg, no more than about 9.5 kW/kg, no more than about 9 kW/kg, no more than about 8.5 kW/kg, no more than about 8 kW/kg, no more than about 7.5 kW/kg, no more than about 7 kW/kg, no more than about 6.7 kW/kg, no more than about 6.5 kW/kg, no more than about 6 kW/kg, no more than about 5.5 kW/kg, no more than about 5 kW/kg, or no more than about 4.5 kW/kg. Combinations of the above-referenced mixing power ranges are also possible (e.g., at least about 4 kW/kg and no more than about 10 kW/kg or at least about 5 kW/kg and no more than about 7 kW/kg), inclusive of all values and ranges therebetween. In some embodiments, the milling or mixing can impart a mixing power of about 4 kW/kg, about 4.5 kW/kg, about 5 kW/kg, about 5.5 kW/kg, about 6 kW/kg, about 6.5 kW/kg, about 6.7 kW/kg, about 7 kW/kg, about 7.5 kW/kg, about 8 kW/kg, about 8.5 kW/kg, about 9 kW/kg, or about 9.5 kW/kg, or about 10 kW/kg.
In some embodiments, the carbon additive can have a surface area of less than about 100 m2/g, less than about 90 m2/g, less than about 80 m2/g, less than about 70 m2/g, less than about 60 m2/g, less than about 50 m2/g, less than about 40 m2/g, less than about 30 m2/g, less than about 20 m2/g, or less than about 10 m2/g, inclusive of all values and ranges therebetween.
In some embodiments, the carbon additive can have an average oil absorption of less than about 600 ml oil/100 g absorbent, less than about 550 ml oil/100 g absorbent, less than about 500 ml oil/100 g absorbent, less than about 450 ml oil/100 g absorbent, less than about 400 ml oil/100 g absorbent, less than about 350 ml oil/100 g absorbent, less than about 300 ml oil/100 g absorbent, less than about 250 ml oil/10 g absorbent, or less than about 200 ml oil/100 g absorbent, inclusive of all values and ranges therebetween.
In some embodiments, the semi-solid cathode 140 can include at least about 0.1%, at least about 0.2%, at least about 0.3%, at least about 0.4%, at least about 0.5%, at least about 0.6%, at least about 0.7%, at least about 0.8%, at least about 0.9%, at least about 1%, at least about 1.5%, at least about 2%, at least about 2.5%, at least about 3%, at least about 3.5%, at least about 4%, at least about 4.5%, at least about 5%, at least about 5.5%, at least about 6%, at least about 6.5%, at least about 7%, or at least about 7.5% by volume of a carbon additive. In some embodiments, the semi-solid cathode 140 can include no more than about 8%, no more than about 7.5%, no more than about 7%, no more than about 6.5%, no more than about 6%, no more than about 5.5%, no more than about 5%, no more than about 4.5%, no more than about 4%, no more than about 3.5%, no more than about 3%, no more than about 2.5%, no more than about 2%, no more than about 1.5%, no more than about 1%, no more than about 0.9%, no more than about 0.8%, no more than about 0.7%, no more than about 0.6%, no more than about 0.5%, no more than about 0.4%, no more than about 0.3%, or no more than about 0.2% by volume of a carbon additive.
Combinations of the above-referenced volume percentage of carbon additive in the semi-solid cathode 140 are also possible (e.g., at least about 0.1% and no more than about 8% by volume or at least about 1% and no more than about 1.5% by volume), inclusive of all values and ranges therebetween. In some embodiments, the semi-solid cathode 140 can include about 0.1%, about 0.2%, about 0.3%, about 0.4%, about 0.5%, about 0.6%, about 0.7%, about 0.8%, about 0.9%, about 1%, about 1.5%, about 2%, about 2.5%, about 3%, about 3.5%, about 4%, about 4.5%, about 5%, about 5.5%, about 6%, about 6.5%, about 7%, about 7.5%, or about 8% by volume of a carbon additive.
In some embodiments, the ratio of carbon additive to conductive material in the semi-solid cathode 140 can be at least about 0.1, at least about 0.15, at least about 0.2, at least about 0.25, at least about 0.3, at least about 0.35, at least about 0.4, at least about 0.45, at least about 0.5, at least about 0.55, at least about 0.6, at least about 0.65, at least about 0.7, at least about 0.75, at least about 0.8, or at least about 0.85. In some embodiments, ratio of carbon additive to conductive material in the semi-solid cathode 140 can be no more than about 0.9, no more than about 0.85, no more than about 0.8, no more than about 0.75, no more than about 0.7, no more than about 0.65, no more than about 0.6, no more than about 0.55, no more than about 0.5, no more than about 0.45, no more than about 0.4, no more than about 0.35, no more than about 0.3, no more than about 0.25, no more than about 0.2, or no more than about 0.15. Combinations of the above-referenced ratios of carbon additive to conductive material in the semi-solid cathode 140 are also possible (e.g., at least about 0.1 and no more than about 0.9 or at least about 0.45 and no more than about 0.55), inclusive of all values and ranges therebetween. In some embodiments, the ratio of carbon additive to conductive material in the semi-solid cathode 140 can be about 0.1, about 0.15, about 0.2, about 0.25, about 0.3, about 0.35, about 0.4, about 0.45, about 0.5, about 0.55, about 0.6, about 0.65, about 0.7, about 0.75, about 0.8, about 0.85, or about 0.9.
In some embodiments, the semi-solid cathode 140 can have a yield strength of no more than about 170 kPa, no more than about 160 kPa, no more than about 150 kPa, no more than about 140 kPa, no more than about 130 kPa, no more than about 120 kPa, no more than about 110 kPa, no more than about 100 kPa, no more than about 90 kPa, no more than about 80 kPa, no more than about 70 kPa, no more than about 60 kPa, no more than about 50 kPa, no more than about 40 kPa, or no more than about 30 kPa, inclusive of all values and ranges therebetween.
In some embodiments, the semi-solid cathode 140 can include about 25% to about 70% by volume of an electrolyte. In some embodiments, the semi-solid cathode 140 can include about 30% to about 50%, or about 20% to about 40% by volume of an electrolyte, inclusive of all ranges therebetween.
In some embodiments, the semi-solid cathode 140 can have an electronic conductivity of at least about 1 mS/cm, or at least about 10 mS/cm. In some embodiments, the semi-solid cathode 140 can have an electronic conductivity of at least about 20 mS/cm, at least about 30 mS/cm, at least about 40 mS/cm, at least about 50 mS/cm, at least about 60 mS/cm, least about 70 mS/cm, at least about 80 mS/cm, at least about 90 mS/cm, at least about 100 mS/cm, at least about 110 mS/cm, at least about 120 mS/cm, at least about 130 mS/cm, at least about 140 mS/cm, at least about 150 mS/cm, at least about 200 mS/cm, at least about 250 mS/cm, at least about 300 mS/cm, at least about 350 mS/cm, at least about 400 mS/cm, at least about 450 mS/cm, at least about 500 mS/cm, at least about 550 mS/cm, at least about 600 mS/cm, at least about 650 mS/cm, at least about 700 mS/cm, at least about 750 mS/cm, at least about 800 mS/cm, at least about 850 mS/cm, at least about 900 mS/cm, at least about 950 mS/cm, or at least about 1,000 mS/cm. In some embodiments, the semi-solid cathode 140 suspension can have a mixing index of at least about 0.9, at least about 0.95, or at least about 0.975.
In some embodiments, the semi-solid cathode 140 can have an area specific capacity of at least about 7 mAh/cm2, at least about 8 mAh/cm2, at least about 9 mAh/cm2, or at least about 10 mAh/cm2 at a C-rate of C/4. In some embodiments, the semi-solid cathode 140 can have an area specific capacity of at least about 7 mAh/cm2, at least about 8 mAh/cm2, at least about 9 mAh/cm2, or at least about 10 mAh/cm2 at a C-rate of C/2.
In some embodiments, the semi-solid anode 150 can include about 35% to about 75% by volume of an active material. In some embodiments, the semi-solid anode 150 can include about 40% to about 75% by volume, about 45% to about 75% by volume, about 50% to about 75% by volume, about 55% to about 75% by volume, about 60% to about 75% by volume, or about 65% to about 75% by volume of an active material, inclusive of all ranges therebetween.
In some embodiments, the semi-solid anode 150 can include at least about 35%, at least about 40%, at least about 45%, at least about 50%, at least about 55%, at least about 60%, at least about 65%, or at least about 70%, at least about 75%, or at least about 80% by volume of an active material. In some embodiments, the semi-solid anode 150 can include no more than about 85%, no more than about 80%, no more than about 75%, no more than about 70%, no more than about 65%, no more than about 60%, no more than about 55%, no more than about 50%, no more than about 45%, or no more than about 40% by volume of an active material. Combinations of the above referenced ranges of the volume percentage of active material in the semi-solid anode 150 are also possible (e.g., at least about 35% and no more than about 85% by volume or at least about 55% and no more than about 60% by volume), inclusive of all values and ranges therebetween. In some embodiments, the semi-solid anode 150 can include about 35%, about 40%, about 45%, about 50%, about 55%, about 60%, about 65%, about 70%, about 75%, about 80%, or about 85% by volume of an active material.
In some embodiments, the semi-solid anode 150 can include about 0% to about 10% by volume of a conductive material. In some embodiments, the semi-solid anode 150 can include about 0.2% to about 9% by volume, about 0.4% to about 8% by volume, about 0.6% to about 7% by volume, about 0.8% to about 6% by volume, about 1% to about 5% by volume, or about 2% to about 4% by volume of a conductive material, inclusive of all ranges therebetween. In some embodiments, the semi-solid anode 150 can include about 1% to about 6% by volume of a conductive material. In some embodiments, the semi-solid anode 150 can include about 0.5% to about 2% by volume of a conductive material, inclusive of all ranges therebetween.
In some embodiments, the semi-solid anode 150 can include at least about 0%, at least about 0.1%, at least about 0.2%, at least about 0.3%, at least about 0.4%, at least about 0.5%, at least about 0.6%, at least about 0.7%, at least about 0.8%, at least about 0.9%, at least about 1%, at least about 1.5%, at least about 2%, at least about 2.5%, at least about 3%, at least about 3.5%, at least about 4%, at least about 4.5%, at least about 5%, at least about 5.5%, at least about 6%, at least about 6.5%, at least about 7%, at least about 7.5%, at least about 8%, at least about 8.5%, at least about 9%, or at least about 9.5%, by volume of a conductive material. In some embodiments, the semi-solid anode 150 can include no more than about 10%, no more than about 9.5%, no more than about 9%, no more than about 8.5%, no more than about 8%, no more than about 7.5%, no more than about 7%, no more than about 6.5%, no more than about 6%, no more than about 5.5%, no more than about 5%, no more than about 4.5%, no more than about 4%, no more than about 3.5%, no more than about 3%, no more than about 2.5%, no more than about 2%, no more than about 1.5%, no more than about 1%, no more than about 0.9%, no more than about 0.8%, no more than about 0.7%, no more than about 0.6%, no more than about 0.5%, no more than about 0.4%, no more than about 0.3%, no more than about 0.2%, or no more than about 0.1%, by volume of a conductive material. Combinations of the above-referenced volume percentage of conductive material in the semi-solid anode 150 are also possible (e.g., at least about 0% and no more than about 10% by volume or at least about 0.7% and no more than about 1.5% by volume), inclusive of all values and ranges therebetween. In some embodiments, the semi-solid anode 150 can include about 0.1%, about 0.2%, about 0.3%, about 0.4%, about 0.5%, about 0.6%, about 0.7%, about 0.8%, about 0.9%, about 1%, about 1.5%, about 2%, about 2.5%, about 3%, about 3.5%, about 4%, about 4.5%, about 5%, about 5.5%, about 6%, about 6.5%, about 7%, about 7.5%, about 8%, about 8.5%, about 9%, about 9.5%, or about 10% by volume of a conductive material.
In some embodiments, the semi-solid anode 150 can include a carbon additive. The addition of a carbon additive can improve the conductivity of the semi-solid anode 150 such that less conductive material can be used. In some embodiments, the inclusion of the carbon additive in the semi-solid anode 150 can enable the semi-solid anode 150 to have less carbon overall than a semi-solid anode 150 without the carbon additive. Said another way, the carbon additive can at least partially replace the conductive material and have a greater effect per unit mass than the conductive material, such that less overall carbon can be included in the semi-solid anode 150 with the carbon additive. Similar conductivity can be achieved with less material. Improved conductivity can lead to slower area specific impedance (ASI) growth better capacity retention in electrochemical cells.
In some embodiments, the carbon additive can coat the active material. In some embodiments, coating active material particles in the semi-solid anode 150 with the carbon additive can improve the conductivity of the semi-solid anode 150 while balancing the stiffness of the semi-solid anode 150. The inclusion of a carbon additive in the semi-solid anode 150 can increase the conductivity and the cycling performance of the semi-solid anode 150 without substantially increasing the yield strength of the semi-solid anode 150. Increased yield strength can lead to solid-like behavior in the semi-solid anode 150, so preventing an increase in yield strength can aid in maintaining the semi-solid properties (e.g., malleability, dispensability) of the semi-solid anode 150. In some embodiments, the carbon additive can be different from the conductive material. In some embodiments, the carbon additive can be chemically different from the conductive material. In some embodiments, the carbon additive can have a different crystalline structure from the conductive material. In some embodiments, the carbon additive can include CNF. In some embodiments, the carbon additive can include VGCF. In some embodiments, the carbon additive can include carbon nanotubes. In some embodiments, the carbon additive can include single-walled carbon nanotubes. In some embodiments, the carbon additive can include multi-walled carbon nanotubes. In some embodiments, the carbon additive can include carbon black. In some embodiments, the carbon additive can have a 2D morphology. In some embodiments, coating the active material with a carbon additive with 2D morphology can provide good mixing and consistent slurry conductivity throughout the semi-solid anode 150. In some embodiments, the carbon additive can include graphene with a 2D layered structure. In some embodiments, the carbon additive can include expanded graphite with a 2D layered structure. In some embodiments, the carbon additive can have a lower surface area than the conductive material. Without wishing to be bound by any particular theory, a material with a high surface area can absorb a large amount of liquid, effectively drying up the electrolyte in the semi-solid anode 150, causing the semi-solid anode 150 to behave more like a solid than a semi-solid.
In some embodiments, the active material and the conductive material can be dry-mixed to form a mixture. In some embodiments, the active material, the conductive material, and the carbon additive can be dry-mixed to form a mixture. In some embodiments, the active material and the carbon additive can be dry-mixed to form a mixture. In some embodiments, the dry-mixing can include milling. In some embodiments, the electrolyte can be added to the mixture to form a semi-solid electrode material.
In some embodiments, the active material and the conductive material can be dry-mixed during a first time period to form a first mixture, and the carbon additive can be added to the first mixture during a second time period to form a second mixture. In some embodiments, the active material and a first amount of the carbon additive can be dry-mixed during a first time period to form a first mixture, and a second amount of the carbon additive can be added to the first mixture during a second time period to form a second mixture. In some embodiments, the dry-mixing can include milling. In some embodiments, the electrolyte can be added to the second mixture to form a semi-solid electrode material.
In some embodiments, the active material and the conductive material can be milled together to form a mixture. In some embodiments, the active material and the carbon additive can be milled together to form a mixture. In some embodiments, the active material, the conductive material, and the carbon additive can be milled together to form a mixture. In some embodiments, the conductive material, the active material, and the electrolyte can be milled together to form a mixture. In some embodiments, the active material, the conductive material, the carbon additive, and the electrolyte can be milled together to form a mixture. In some embodiments, the milling can be in Nippon Coke. In some embodiments, the milling can be for a time sufficient to coat the active material particles in very fine particles of active material. In some embodiments, the milling can be at a low enough milling power or milling shear force such that the active material particles are not significantly fractured.
In some embodiments, the active material, the conductive material, the carbon additive, and/or the electrolyte can be milled together via blade mixing. In some embodiments, the blade mixing can be via a rotating blade. In some embodiments, the blade mixing can be via a fixed blade. In some embodiments, the active material, the conductive material, the carbon additive, and/or the electrolyte can be directly mixed via a V-blender. In some embodiments, the active material, the conductive material, the carbon additive, and/or the electrolyte can be mixed via ball milling in a ball mill. In some embodiments, active material, the conductive material, the carbon additive, and/or the electrolyte can be mixed via roller milling in a roller mill.
In some embodiments, the electrolyte can be added before the mixing or milling process. In some embodiments, electrolyte can be added during the mixing or milling process. In other words, the mixing or milling process can include wet mixing or wet milling. In some embodiments, the electrolyte can include an electrolyte with a high boiling temperature, such that a high shear energy can be applied to the mixture during mixing without the electrolyte boiling away. In other words, incorporating an electrolyte with a high boiling point into the mixture can aid in keeping the mixture as a semi-solid during mixing or milling, such that it does not dry up and become a solid. Some carbon additives can be difficult to break down into smaller particles, so a higher shear energy can more easily break down these carbon additives. In some embodiments, the electrolyte can include ethylene carbonate (EC), propylene carbonate (PC), γ-butyrolactone (GBL), or any combination thereof.
In some embodiments, a solvent can be added before the mixing or milling process. In some embodiments, the solvent can be added during the mixing or milling process. In other words, the mixing or milling process can include wet mixing or wet milling. In some embodiments, the solvent can include a solvent with a high boiling temperature, such that a high shear energy can be applied to the mixture during mixing without the solvent boiling away. In other words, incorporating a solvent with a high boiling point into the mixture can aid in keeping the mixture as a semi-solid during mixing or milling, such that it does not dry up and become a solid. Some carbon additives can be difficult to break down into smaller particles, so a higher shear energy can more easily break down these carbon additives. Also, carbon additive particles can disperse in organic solvents more easily than active material particles. Adding a solvent with a high boiling point can act as a buffer between the carbon additive particles and the active material particles. Also, the solvent can act as a buffer between the active material and the mixing media (e.g., mixing impeller). This buffer can aid in preventing the active material particles from breaking down. Additionally, the use of a solvent with a high boiling point can aid in reducing temperature rise during mixing or milling, as heat is distributed to the liquid. Also, if the solvent does not include an electrolyte salt (e.g., LiPF6), and the electrolyte salt is added after the mixing or milling, this can aid in preventing the electrolyte salt from being broken down during mixing. In some embodiments, the solvent can include ethylene carbonate (EC), propylene carbonate (PC), γ-butyrolactone (GBL), or any combination thereof. In some embodiments, the solvent can be free or substantially free of salts (i.e., the solvent can be a non-electrolyte). In some embodiments, the electrolyte can be added to the mixture after the solvent, the active material, the conductive material, and/or the carbon additive have been mixed or milled together. In some embodiments, the electrolyte can be added via spraying. In some embodiments, the electrolyte can be added via injection.
In some embodiments, the milling or mixing can be for at least about 5 minutes, at least about 6 minutes, at least about 7 minutes, at least about 8 minutes, at least about 9 minutes, at least about 10 minutes, at least about 11 minutes, at least about 12 minutes, at least about 13 minutes, at least about 14 minutes, at least about 15 minutes, at least about 16 minutes, at least about 17 minutes, at least about 18 minutes, at least about 19 minutes, at least about 20 minutes, at least about 21 minutes, at least about 22 minutes, at least about 23 minutes, at least about 24 minutes, at least about 25 minutes, at least about 26 minutes, at least about 27 minutes, at least about 28 minutes, at least about 29 minutes, or at least about 30 minutes.
The energy imparted by the milling or mixing can be fine-tuned to the composition of the semi-solid anode 150. For example, Ketjen can require significantly more energy to break apart than carbon fibers. Mixing energy should be substantially high to break agglomerations of carbon-containing particles, but not so high that it breaks the particles of the semi-solid anode 150 (i.e., the active particles, the carbon-containing particles, and the conductive particles) apart from each other. Mixing energy can influence the yield strength of the semi-solid anode 150. In some embodiments, a semi-solid anode 150 with a relatively low yield stress can have better cycling stability than a semi-solid electrode with a high yield stress. Without being bound by any particular theory, low yield stress in the semi-solid anode 150 can improve the spreading quality of the semi-solid anode 150. Low yield stress in the semi-solid anode 150 can correlate to a desired piston pressure to ensure little or no phase separation during the spreading of the semi-solid anode 150. Low yield stress can make the semi-solid anode 150 more uniformly mixed at a given mixing energy due to the more flowable composition of the semi-solid anode 150. Also, tap density of the carbon additive in the semi-solid anode 150 can increase with decreasing yield strength, such that the electrolyte will be freed up to further wet the surfaces of the particles in the semi-solid anode 150.
In some embodiments, the milling or mixing can impart a mixing energy of at least about 400 kJ/kg, at least about 450 kJ/kg, at least about 500 kJ/kg, at least about 550 kJ/kg, at least about 600 kJ/kg, at least about 650 kJ/kg, at least about 700 kJ/kg, at least about 750 kJ/kg, at least about 800 kJ/kg, at least about 850 kJ/kg, at least about 900 kJ/kg, at least about 950 kJ/kg, at least about 1,000 kJ/kg, at least about 1,050 kJ/kg, at least about 1,100 kJ/kg, at least about 1,150 kJ/kg, at least about 1,200 kJ/kg, at least about 1,250 kJ/kg, at least about 1,300 kJ/kg, at least about 1,350 kJ/kg, at least about 1,400 kJ/kg, at least about 1,450 kJ/kg, at least about 1,500 kJ/kg, at least about 1,550 kJ/kg, at least about 1,600 kJ/kg, at least about 1,650 kJ/kg, at least about 1,700 kJ/kg, at least about 1,750 kJ/kg, at least about 1,800 kJ/kg, at least about 1,850 kJ/kg, at least about 1,900 kJ/kg, at least about 1,950 kJ/kg, at least about 2,000 kJ/kg, at least about 2,100 kJ/kg, at least about 2,200 kJ/kg, at least about 2,300 kJ/kg, at least about 2,400 kJ/kg, at least about 2,500 kJ/kg, at least about 2,600 kJ/kg, at least about 2,700 kJ/kg, at least about 2,800 kJ/kg, at least about 2,900 kJ/kg, or at least about 3,000 kJ/kg. In some embodiments, the milling or mixing can impart a mixing energy of no more than about 3,000 kJ/kg, no more than about 2,900 kJ/kg, no more than about 2,800 kJ/kg, no more than about 2,700 kJ/kg, no more than about 2,600 kJ/kg, no more than about 2,500 kJ/kg, no more than about 2,400 kJ/kg, no more than about 2,300 kJ/kg, no more than about 2,200 kJ/kg, no more than about 2,100 kJ/kg, no more than about 2,000 kJ/kg, no more than about 1,950 kJ/kg, no more than about 1,900 kJ/kg, no more than about 1,850 kJ/kg, no more than about 1,800 kJ/kg, no more than about 1,750 kJ/kg, no more than about 1,700 kJ/kg, no more than about 1,650 kJ/kg, no more than about 1,600 kJ/kg, no more than about 1,550 kJ/kg, no more than about 1,500 kJ/kg, no more than about 1,450 kJ/kg, no more than about 1,400 kJ/kg, no more than about 1,350 kJ/kg, no more than about 1,300 kJ/kg, no more than about 1,250 kJ/kg, no more than about 1,200 kJ/kg, no more than about 1,150 kJ/kg, no more than about 1,100 kJ/kg, no more than about 1,050 kJ/kg, no more than about 1,000 kJ/kg, no more than about 950 kJ/kg, no more than about 900 kJ/kg, no more than about 850 kJ/kg, no more than about 800 kJ/kg, no more than about 750 kJ/kg, no more than about 700 kJ/kg, no more than about 650 kJ/kg, no more than about 600 kJ/kg, or no more than about 550 kJ/kg.
Combinations of the above-referenced mixing energy ranges are also possible (e.g., at least about 400 kJ/kg and no more than about 2,000 kJ/kg or at least about 500 kJ/kg and no more than about 1,000 kJ/kg), inclusive of all values and ranges therebetween. In some embodiments, the milling or mixing can impart a mixing energy of about 400 kJ/kg, about 450 kJ/kg, about 500 kJ/kg, about 550 kJ/kg, about 600 kJ/kg, about 650 kJ/kg, about 700 kJ/kg, about 750 kJ/kg, about 800 kJ/kg, about 850 kJ/kg, about 900 kJ/kg, about 950 kJ/kg, about 1,000 kJ/kg, about 1,050 kJ/kg, about 1,100 kJ/kg, about 1,150 kJ/kg, about 1,200 kJ/kg, about 1,250 kJ/kg, about 1,300 kJ/kg, about 1,350 kJ/kg, about 1,400 kJ/kg, about 1,450 kJ/kg, about 1,500 kJ/kg, about 1,550 kJ/kg, about 1,600 kJ/kg, about 1,650 kJ/kg, about 1,700 kJ/kg, about 1,750 kJ/kg, about 1,800 kJ/kg, about 1,850 kJ/kg, about 1,900 kJ/kg, or about 1,950 kJ/kg, or about 2,000 kJ/kg, about 2,100 kJ/kg, about 2,200 kJ/kg, about 2,300 kJ/kg, about 2,400 kJ/kg, about 2,500 kJ/kg, about 2,600 kJ/kg, about 2,700 kJ/kg, about 2,800 kJ/kg, about 2,900 kJ/kg, or about 3,000 kJ/kg.
Milling power can also be fine-tuned to the composition of the electrode. In other words, milling power should be sufficiently high to break up agglomerates of carbon additives but not high enough to significantly damage the molecules of the carbon additives. For example, materials with long chain structures should be subject to low milling powers so that the long chain structures do not break during the milling. In some embodiments, the milling or mixing can impart a mixing power of at least about 4 kW/kg, at least about 4.5 kW/kg, at least about 5 kW/kg, at least about 5.5 kW/kg, at least about 6 kW/kg, at least about 6.5 kW/kg, at least about 6.7 kW/kg, at least about 7 kW/kg, at least about 7.5 kW/kg, at least about 8 kW/kg, at least about 8.5 kW/kg, at least about 9 kW/kg, or at least about 9.5 kW/kg. In some embodiments, the milling can impart a mixing power of no more than about 10 kW/kg, no more than about 9.5 kW/kg, no more than about 9 kW/kg, no more than about 8.5 kW/kg, no more than about 8 kW/kg, no more than about 7.5 kW/kg, no more than about 7 kW/kg, no more than about 6.7 kW/kg, no more than about 6.5 kW/kg, no more than about 6 kW/kg, no more than about 5.5 kW/kg, no more than about 5 kW/kg, or no more than about 4.5 kW/kg. Combinations of the above-referenced mixing power ranges are also possible (e.g., at least about 4 kW/kg and no more than about 10 kW/kg or at least about 5 kW/kg and no more than about 7 kW/kg), inclusive of all values and ranges therebetween. In some embodiments, the milling can impart a mixing power of about 4 kW/kg, about 4.5 kW/kg, about 5 kW/kg, about 5.5 kW/kg, about 6 kW/kg, about 6.5 kW/kg, about 6.7 kW/kg, about 7 kW/kg, about 7.5 kW/kg, about 8 kW/kg, about 8.5 kW/kg, about 9 kW/kg, or about 9.5 kW/kg, or about 10 kW/kg.
In some embodiments, the carbon additive can have a surface area of less than about 100 m2/g, less than about 90 m2/g, less than about 80 m2/g, less than about 70 m2/g, less than about 60 m2/g, less than about 50 m2/g, less than about 40 m2/g, less than about 30 m2/g, less than about 20 m2/g, or less than about 10 m2/g, inclusive of all values and ranges therebetween.
In some embodiments, the carbon additive can have an average oil absorption of less than about 600 ml oil/100 g absorbent, less than about 550 ml oil/100 g absorbent, less than about 500 ml oil/100 g absorbent, less than about 450 ml oil/100 g absorbent, less than about 400 ml oil/100 g absorbent, less than about 350 ml oil/100 g absorbent, less than about 300 ml oil/100 g absorbent, less than about 250 ml oil/10 g absorbent, or less than about 200 ml oil/100 g absorbent, inclusive of all values and ranges therebetween.
In some embodiments, the semi-solid anode 150 can include at least about 0.1%, at least about 0.2%, at least about 0.3%, at least about 0.4%, at least about 0.5%, at least about 0.6%, at least about 0.7%, at least about 0.8%, at least about 0.9%, at least about 1%, at least about 1.5%, at least about 2%, at least about 2.5%, at least about 3%, at least about 3.5%, at least about 4%, at least about 4.5%, at least about 5%, at least about 5.5%, at least about 6%, at least about 6.5%, at least about 7%, or at least about 7.5% by volume of a carbon additive. In some embodiments, the semi-solid anode 150 can include no more than about 8%, no more than about 7.5%, no more than about 7%, no more than about 6.5%, no more than about 6%, no more than about 5.5%, no more than about 5%, no more than about 4.5%, no more than about 4%, no more than about 3.5%, no more than about 3%, no more than about 2.5%, no more than about 2%, no more than about 1.5%, no more than about 1%, no more than about 0.9%, no more than about 0.8%, no more than about 0.7%, no more than about 0.6%, no more than about 0.5%, no more than about 0.4%, no more than about 0.3%, or no more than about 0.2% by volume of a carbon additive.
Combinations of the above-referenced volume percentage of carbon additive in the semi-solid anode 150 are also possible (e.g., at least about 0.1% and no more than about 8% by volume or at least about 1% and no more than about 1.5% by volume), inclusive of all values and ranges therebetween. In some embodiments, the semi-solid anode 150 can include about 0.1%, about 0.2%, about 0.3%, about 0.4%, about 0.5%, about 0.6%, about 0.7%, about 0.8%, about 0.9%, about 1%, about 1.5%, about 2%, about 2.5%, about 3%, about 3.5%, about 4%, about 4.5%, about 5%, about 5.5%, about 6%, about 6.5%, about 7%, about 7.5%, or about 8% by volume of a carbon additive.
In some embodiments, the ratio of carbon additive to conductive material in the semi-solid anode 150 can be at least about 0.1, at least about 0.15, at least about 0.2, at least about 0.25, at least about 0.3, at least about 0.35, at least about 0.4, at least about 0.45, at least about 0.5, at least about 0.55, at least about 0.6, at least about 0.65, at least about 0.7, at least about 0.75, at least about 0.8, or at least about 0.85. In some embodiments, ratio of carbon additive to conductive material in the semi-solid anode 150 can be no more than about 0.9, no more than about 0.85, no more than about 0.8, no more than about 0.75, no more than about 0.7, no more than about 0.65, no more than about 0.6, no more than about 0.55, no more than about 0.5, no more than about 0.45, no more than about 0.4, no more than about 0.35, no more than about 0.3, no more than about 0.25, no more than about 0.2, or no more than about 0.15. Combinations of the above-referenced ratios of carbon additive to conductive material in the semi-solid anode 150 are also possible (e.g., at least about 0.1 and no more than about 0.9 or at least about 0.45 and no more than about 0.55), inclusive of all values and ranges therebetween. In some embodiments, the ratio of carbon additive to conductive material in the semi-solid anode 150 can be about 0.1, about 0.15, about 0.2, about 0.25, about 0.3, about 0.35, about 0.4, about 0.45, about 0.5, about 0.55, about 0.6, about 0.65, about 0.7, about 0.75, about 0.8, about 0.85, or about 0.9.
In some embodiments, the semi-solid anode 150 can have a yield strength of no more than about 170 kPa, no more than about 160 kPa, no more than about 150 kPa, no more than about 140 kPa, no more than about 130 kPa, no more than about 120 kPa, no more than about 110 kPa, no more than about 100 kPa, no more than about 90 kPa, no more than about 80 kPa, no more than about 70 kPa, no more than about 60 kPa, no more than about 50 kPa, no more than about 40 kPa, or no more than about 30 kPa, inclusive of all values and ranges therebetween.
In some embodiments, the semi-solid anode 150 can include about 10% to about 70% by volume of an electrolyte. In some embodiments, the semi-solid anode 150 can include about 30% to about 50%, or about 20% to about 40% by volume of an electrolyte, inclusive of all ranges therebetween.
In some embodiments, the semi-solid anode 150 can have an electronic conductivity of at least about 1 mS/cm, or at least about 10 mS/cm. In some embodiments, the semi-solid anode 150 can have an electronic conductivity of at least about 20 mS/cm, at least about 30 mS/cm, at least about 40 mS/cm, at least about 50 mS/cm, at least about 60 mS/cm, at least about 70 mS/cm, at least about 80 mS/cm, at least about 90 mS/cm, at least about 100 mS/cm, at least about 110 mS/cm, at least about 120 mS/cm, at least about 130 mS/cm, at least about 140 mS/cm, at least about 150 mS/cm, at least about 200 mS/cm, at least about 250 mS/cm, at least about 300 mS/cm, at least about 350 mS/cm, at least about 400 mS/cm, at least about 450 mS/cm, at least about 500 mS/cm, at least about 550 mS/cm, at least about 600 mS/cm, at least about 650 mS/cm, at least about 700 mS/cm, at least about 750 mS/cm, at least about 800 mS/cm, at least about 900 mS/cm, at least about 950 mS/cm, at least about 1,000 mS/cm, at least about 1,100 mS/cm, at least about 1,200 mS/cm, at least about 1,300 mS/cm, at least about 1,400 mS/cm, at least about 1,500 mS/cm, at least about 1,600 mS/cm, at least about 1,700 mS/cm, at least about 1,800 mS/cm, at least about 1,900 mS/cm, at least about 2,000 mS/cm, at least about 2,100 mS/cm, at least about 2,200 mS/cm, at least about 2,300 mS/cm, at least about 2,400 mS/cm, at least about 2,500 mS/cm, at least about 2,600 mS/cm, at least about 2,700 mS/cm, at least about 2,800 mS/cm, at least about 2,900 mS/cm, or at least about 3,000 mS/cm. In some embodiments, the semi-solid anode 150 suspension can have a mixing index of at least about 0.9, at least about 0.95, or at least about 0.975.
In some embodiments, the semi-solid cathode 140 and/or the semi-solid anode 150 can have a thickness in the range of about 100 μm to about 2,000 μm. In some embodiments, the semi-solid cathode 140 and/or the semi-solid anode 150 can have a thickness in the range of about 100 μm to about 600 μm, about 110 μm to about 600 μm, about 120 μm to about 600 μm, about 130 μm to about 600 μm, about 140 μm to about 600 μm, about 150 μm to about 600 μm, about 200 μm to about 600 μm, about 250 μm to about 600 μm, about 300 μm to about 600 μm, about 350 μm to about 600 μm, about 400 μm to about 600 μm, about 450 μm to about 600 μm, or about 500 μm to about 600 μm, inclusive of all ranges therebetween.
In some embodiments, the electrochemical cell 100 can include the semi-solid cathode 140 and a semi-solid anode 150. In such embodiments, the electrochemical cell 100 can have an area specific capacity of at least about 7 mAh/cm2 at a C-rate of C/4. In some embodiments, the electrochemical cell 100 can have an area specific capacity of at least about 8 mAh/cm2, at least about 9 mAh/cm2, or at least about 10 mAh/cm2 at a C-rate of C/4. In some embodiments, the electrochemical cell 100 can have an area specific capacity of at least about 7 mAh/cm2, at a C-rate of C/2. In some embodiments, the electrochemical cell 100 can have an area specific capacity of at about least 8 mAh/cm2, or at least about 9 mAh/cm2, at a C-rate of C/2.
In some embodiments, the electrochemical cell 100 can have high capacity retention through one or more cycles. In some embodiments, the electrochemical cell 100 can retain at least about 65%, at least about 70%, at least about 75%, at least about 80%, at least about 85%, or at least about 90% of its first cycle discharge capacity after 3 cycles at 1 C when recharging to 100% state of charge (SOC). In some embodiments, the electrochemical cell 100 can retain at least about 40%, at least about 45%, at least about 50%, at least about 55%, at least about 60%, at least about 65%, at least about 70%, at least about 75%, at least about 80%, at least about 85%, or at least about 90% of its first cycle discharge capacity after 3 cycles at 2 C when recharging to 100% state of charge (SOC).
In some embodiments, the electrochemical cell 100 can retain at least about 50%, at least about 55%, at least about 60%, at least about 65%, at least about 70%, at least about 75%, at least about 80%, or at least about 90% of its first cycle discharge capacity after 1,000 cycles at a C-rate of C/4. In some embodiments, the electrochemical cell 100 can retain at least about 50%, at least about 55%, at least about 60%, at least about 65%, at least about 70%, at least about 75%, at least about 80%, or at least about 90% of its first cycle discharge capacity after 1,000 cycles at a C-rate of C/3.
In some embodiments, a redox mediator is used to improve the charge transfer within the semi-solid suspension. In some embodiments, the redox mediator is based on Fe2+ or V2+, V3+, or V4+. In some embodiments, the redox mediator is ferrocene.
In some embodiments, the conductive particles have shapes, which may include spheres, platelets, or rods to optimize solids packing fraction, increase the semi-solid's net electronic conductivity, and improve rheological behavior of semi-solids. In some embodiments, low aspect or substantially equiaxed or spherical particles are used to improve the ability of the semi-solid to flow under stress.
In some embodiments, the particles have a plurality of sizes so as to increase packing fraction. In particular, the particle size distribution can be bi-modal, in which the average particle size of the larger particle mode is at least 5 times larger than average particle size of the smaller particle mode. In some embodiments, the mixture of large and small particles improves flow of the material during cell loading and increases solid volume fraction and packing density in the loaded cell.
In some embodiments, the nature of the semi-solid cathode 140 and/or the semi-solid anode 150 suspensions can be modified prior to and subsequent to filling of the negative electroactive zone and the positive electroactive zone of an electrochemical cell to facilitate flow during loading and packing density in the loaded cell.
In some embodiments, the particle suspension is initially stabilized by repulsive interparticle steric forces that arise from surfactant molecules. After the particle suspension is loaded into the positive electroactive zone and/or the negative electroactive zone, chemical or heat treatments can cause these surface molecules to collapse or evaporate and promote densification. In some embodiments, the suspension's steric forces are modified intermittently during loading.
For example, the particle suspension can be initially stabilized by repulsive interparticle electrostatic double layer forces to decrease viscosity. The repulsive force reduces interparticle attraction and reduces agglomeration. After the particle suspension is loaded into the positive electroactive zone and/or negative electroactive zone, the surface of the particles can be further modified to reduce interparticle repulsive forces and thereby promote particle attraction and packing. For example, ionic solutions such as salt solutions can be added to the suspension to reduce the repulsive forces and promote aggregation and densification so as to produce increased solids fraction loading after filling of the electroactive zones. In some embodiments, salt is added intermittently during suspension loading to increase density in incremental layers.
In some embodiments, the positive and/or negative electroactive zones are loaded with a particle suspension that is stabilized by repulsive forces between particles induced by an electrostatic double layer or short-range steric forces due to added surfactants or dispersants. Following loading, the particle suspension is aggregated and densified by increasing the salt concentration of the suspension. In some embodiments, the salt that is added is a salt of a working ion for the battery (e.g., a lithium salt for a lithium ion battery) and upon being added, causes the liquid phase to become an ion-conducting electrolyte (e.g., for a lithium rechargeable battery, may be one or more alkyl carbonates, or one or more ionic liquids). Upon increasing the salt concentration, the electrical double layer causing repulsion between the particles is “collapsed”, and attractive interactions cause the particle to floc, aggregate, consolidate, or otherwise densify. This allows the electrode of the battery to be formed from the suspension while it has a low viscosity, for example, by pouring, injection, or pumping into the positive and/or negative electroactive zones that can form a net-shaped electrode, and then allows particles within the suspension to be consolidated for improved electrical conduction, higher packing density and longer shelf life.
In some embodiments, the cathode 140 and/or anode 150 semi-solid suspensions can initially be flowable, and can be caused to become non-flowable by “fixing”. In some embodiments, fixing can be performed by the action of electrochemically cycling the battery. In some embodiments, electrochemical cycling is performed within the current, voltage, or temperature range over which the battery is subsequently used. In some embodiments, fixing is performed by electrochemical cycling of the battery to a higher or lower current, higher or lower voltage, or higher or lower temperature, that the the range over which the battery is subsequently used. In some embodiments, fixing can be performed by the action of photopolymerization. In some embodiments, fixing is performed by action of electromagnetic radiation with wavelengths that are transmitted by the unfilled positive and/or negative electroactive zones of the electrochemical cell 100 formed from the semi-solid cathode 140 and/or the semi-solid anode 150. In some embodiments, one or more additives are added to the semi-solid suspensions to facilitate fixing.
In some embodiments, the injectable and flowable cathode 140 and/or anode 150 semi-solid is caused to become less flowable or more flowable by “plasticizing”. In some embodiments, the rheological properties of the injectable and flowable semi-solid suspensions can be modified by the addition of a thinner, a thickener, and/or a plasticizing agent. In some embodiments, these agents promote processability and help retain compositional uniformity of the semi-solid under flowing conditions and positive and negative electroactive zone filling operations. In some embodiments, one or more additives can be added to the flowable semi-solid suspension to adjust its flow properties to accommodate processing requirements.
In some embodiments, the semi-solid cathode 140 and in some embodiments, the anode 150 (e.g., a semi-solid anode) suspensions provide a means to produce a substance that functions collectively as an ion-storage/ion-source, electron conductor, and ionic conductor in a single medium that acts as a working electrode.
The cathode 140 and/or anode 150 semi-solid ion-storing redox composition as described herein can have, when taken in moles per liter (molarity), at least 10M concentration of redox species. In some embodiments, the cathode 140 and/or the anode 150 semi-solids ion-storing redox composition can include at least 12M, at least 15M, or at least 20M of the redox species. The electrochemically active material can be an ion storage material and or any other compound or ion complex that is capable of undergoing Faradaic reaction in order to store energy. The electroactive material can also be a multiphase material including the above described redox-active solid mixed with a non-redox-active phase, including solid-liquid suspensions, or liquid-liquid multiphase mixtures, including micelles or emulsions having a liquid ion-storage material intimately mixed with a supporting liquid phase. Systems that utilize various working ions can include aqueous systems in which Li+, Na+, or other alkali ions are the working ions, even alkaline earth working ions such as Ca2+, Mg2+, or Al3+. In each of these instances, a negative electrode storage material and a positive electrode storage material may be required, the negative electrode storing the working ion of interest at a lower absolute electrical potential than the positive electrode. The cell voltage can be determined approximately by the difference in ion-storage potentials of the two ion-storage electrode materials.
Systems employing negative and/or positive ion-storage materials that are insoluble storage hosts for working ions, meaning that said materials can take up or release the working ion while all other constituents of the materials remain substantially insoluble in the electrolyte, are particularly advantageous as the electrolyte does not become contaminated with electrochemical composition products. In addition, systems employing negative and/or positive lithium ion-storage materials are particularly advantageous when using non-aqueous electrochemical compositions.
In some embodiments, the semi-solid ion-storing redox compositions include materials proven to work in conventional lithium-ion batteries. In some embodiments, the semi-solid cathode 140 electroactive material contains lithium positive electroactive materials and the lithium cations are shuttled between the anode 150 (e.g., a semi-solid anode) and the semi-solid cathode 140, intercalating into solid, host particles suspended in a liquid electrolyte.
In some embodiments, at least one of the semi-solid cathode 140 and/or anode 150 (e.g., a semi-solid anode) includes a condensed ion-storing liquid of a redox-active compound, which may be organic or inorganic, and includes but is not limited to lithium metal, sodium metal, lithium-metal alloys, gallium and indium alloys with or without dissolved lithium, molten transition metal chlorides, thionyl chloride, and the like, or redox polymers and organics that can be liquid under the operating conditions of the battery. Such a liquid form may also be diluted by or mixed with another, non-redox-active liquid that is a diluent or solvent, including mixing with such diluents to form a lower-melting liquid phase. In some embodiments, the redox-active component can comprise, by mass, at least 10% of the total mass of the electrolyte. In other embodiments, the redox-active component will comprise, by mass, between approximately 10% and 25% of the total mass of the electrolyte. In some embodiments, the redox-active component will comprise by mass, at least 25% or more of the total mass of the electrolyte.
In some embodiments, the redox-active electrode material, whether used as a semi-solid or a condensed liquid format as defined above, comprises an organic redox compound that stores the working ion of interest at a potential useful for either the positive or negative electrode of a battery. Such organic redox-active storage materials include “p”-doped conductive polymers such as polyaniline or polyacetylene based materials, polynitroxide or organic radical electrodes (such as those described in: H. Nishide et al., Electrochim. Acta, 50, 827-831, (2004), and K. Nakahara, et al., Chem. Phys. Lett., 359, 351-354 (2002)), carbonyl based organics, and oxocarbons and carboxylate, including compounds such as Li2C6O6, Li2C8H4O4, and Li2C6H4O4 (see for example M. Armand et al., Nature Materials, DOI: 10.1038/nmat2372) and organosulfur compounds.
In some embodiments, organic redox compounds that are electronically insulating are used. In some instance, the redox compounds are in a condensed liquid phase such as liquid or flowable polymers that are electronically insulating. In such cases, the redox active slurry may or may not contain an additional carrier liquid. Additives can be combined with the condensed phase liquid redox compound to increase electronic conductivity. In some embodiments, such electronically insulating organic redox compounds are rendered electrochemically active by mixing or blending with particulates of an electronically conductive material, such as solid inorganic conductive materials including but not limited to metals, metal carbides, metal nitrides, metal oxides, and allotropes of carbon including carbon black, graphitic carbon, carbon fibers, carbon microfibers, vapor-grown carbon fibers (VGCF), fullerenic carbons including “buckyballs”, carbon nanotubes (CNTs), multiwall carbon nanotubes (MWNTs), single wall carbon nanotubes (SWNTs), graphene sheets or aggregates of graphene sheets, and materials comprising fullerenic fragments.
In some embodiments, such electronically insulating organic redox compounds are rendered electronically active by mixing or blending with an electronically conductive polymer, including but not limited to polyaniline or polyacetylene based conductive polymers or poly(3,4-ethylenedioxythiophene) (PEDOT), polypyrrole, polythiophene, poly(p-phenylene), poly(triphenylene), polyazulene, polyfluorene, polynaphtalene, polyanthracene, polyfuran, polycarbazole, tetrathiafulvalene-substituted polystyrene, ferrocene-substituted polyethylene, carbazole-substituted polyethylene, polyoxyphenazine, polyacenes, or poly(heteroacenes). The conductive additives form an electrically conducting framework within the insulating liquid redox compounds that significantly increases the electrically conductivity of the composition. In some embodiments, the conductive addition forms a percolative pathway to the current collector. In some embodiments the redox-active electrode material comprises a sol or gel, including for example metal oxide sols or gels produced by the hydrolysis of metal alkoxides, amongst other methods generally known as “sol-gel processing.” Vanadium oxide gels of composition VxOy are amongst such redox-active sol-gel materials.
Other suitable positive active materials for use in the semi-solid cathode 140 include solid compounds known to those skilled in the art as those used in NiMH (Nickel-Metal Hydride) Nickel Cadmium (NiCd) batteries. Still other positive electrode compounds for Li storage include those used in carbon monofluoride batteries, generally referred to as CFx, or metal fluoride compounds having approximate stoichiometry MF2 or MF3 where M comprises, for example, Fe, Bi, Ni, Co, Ti, or V. Examples include those described in H. Li, P. Balaya, and J. Maier, Li-Storage via Heterogeneous Reaction in Selected Binary Metal Fluorides and Oxides, Journal of The Electrochemical Society, 151 [11] A1878-A1885 (2004), M. Bervas, A. N. Mansour, W.-S. Woon, J. F. Al-Sharab, F. Badway, F. Cosandey, L. C. Klein, and G. G. Amatucci, “Investigation of the Lithiation and Delithiation Conversion Mechanisms in a Bismuth Fluoride Nanocomposites”, J. Electrochem. Soc., 153, A799 (2006), and I. Plitz, F. Badway, J. Al-Sharab, A. DuPasquier, F. Cosandey and G. G. Amatucci, “Structure and Electrochemistry of Carbon-Metal Fluoride Nanocomposites Fabricated by a Solid State Redox Conversion Reaction”, J. Electrochem. Soc., 152, A307 (2005).
As another example, fullerenic carbon including single-wall carbon nanotubes (SWNTs), multiwall carbon nanotubes (MWNTs), or metal or metalloid nanowires may be used as ion-storage materials. One example is the silicon nanowires used as a high energy density storage material in a report by C. K. Chan, H. Peng, G. Liu, K. McIlwrath, X. F. Zhang, R. A. Huggins, and Y. Cui, High-performance lithium battery anodes using silicon nanowires, Nature Nanotechnology, published online 16 Dec. 2007; doi:10.1038/nnano.2007.411. In some embodiments, electroactive materials for the semi-solid cathode 140 in a lithium system can include the general family of ordered rocksalt compounds LiMO2 including those having the α-NaFeO2 (so-called “layered compounds”) or orthorhombic-LiMnO2 structure type or their derivatives of different crystal symmetry, atomic ordering, or partial substitution for the metals or oxygen. M comprises at least one first-row transition metal but may include non-transition metals including but not limited to Al, Ca, Mg, or Zr. Examples of such compounds include LiCoO2, LiCoO2 doped with Mg, LiNiO2, Li(Ni, Co, Al)O2 (known as “NCA”) and Li(Ni, Mn, Co)O2 (known as “NMC”). Other families of exemplary cathode 140 electroactive materials includes those of spinel structure, such as LiMn2O4 and its derivatives, so-called “layered-spinel nanocomposites” in which the structure includes nanoscopic regions having ordered rocksalt and spinel ordering, olivines LiMPO4 and their derivatives, in which M comprises one or more of Mn, Fe, Co, or Ni, partially fluorinated compounds such as LiVPO4F, other “polyanion” compounds as described below, and vanadium oxides VxOy including V2O5 and V6O11.
In some embodiments, the semi-solid cathode 140 electroactive material comprises a transition metal polyanion compound, for example as described in U.S. Pat. No. 7,338,734. In some embodiments the active material comprises an alkali metal transition metal oxide or phosphate, and for example, the compound has a composition Ax(M′1-aM″a)y(XD4)z, Ax(M′1-aM″a)y(DXD4)z, or Ax(M′1-aM″a)y(X2D7)z, and have values such that x, plus y(1-a) times a formal valence or valences of M′, plus ya times a formal valence or valence of M″, is equal to z times a formal valence of the XD4, X2D7, or DXD4 group; or a compound comprising a composition (A1-aM″a)xM′y(XD4)z, (A1-aM″a)xM′y(DXD4)z(A1-aM″a)xM′y(X2D7)z and have values such that (1- a)x plus the quantity ax times the formal valence or valences of M″ plus y times the formal valence or valences of M′ is equal to z times the formal valence of the XD4, X2D7 or DXD4 group. In the compound, A is at least one of an alkali metal and hydrogen, M′ is a first-row transition metal, X is at least one of phosphorus, sulfur, arsenic, molybdenum, and tungsten, M″ any of a Group IIA, IIIA, IVA, VA, VIA, VIIA, VIIIA, IB, IIB, IIIB, IVB, VB, and VIB metal, D is at least one of oxygen, nitrogen, carbon, or a halogen. The positive electroactive material can be an olivine structure compound LiMPO4, where M is one or more of V, Cr, Mn, Fe, Co, and Ni, in which the compound is optionally doped at the Li, M or O-sites. Deficiencies at the Li-site are compensated by the addition of a metal or metalloid, and deficiencies at the O-site are compensated by the addition of a halogen. In some embodiments, the positive active material comprises a thermally stable, transition-metal-doped lithium transition metal phosphate having the olivine structure and having the formula (Li1-xZx)MPO4, where M is one or more of V, Cr, Mn, Fe, Co, and Ni, and Z is a non-alkali metal dopant such as one or more of Ti, Zr, Nb, Al, or Mg, and x ranges from 0.005 to 0.05.
In other embodiments, the lithium transition metal phosphate material has an overall composition of Li1-x-zM1+zPO4, where M comprises at least one first row transition metal selected from the group consisting of Ti, V, Cr, Mn, Fe, Co and Ni, where x is from 0 to 1 and z can be positive or negative. M includes Fe, z is between about 0.15-0.15. The material can exhibit a solid solution over a composition range of 0<x<0.15, or the material can exhibit a stable solid solution over a composition range of x between 0 and at least about 0.05, or the material can exhibit a stable solid solution over a composition range of x between 0 and at least about 0.07 at room temperature (22-25° C.). The material may also exhibit a solid solution in the lithium-poor regime, e.g., where x≥0.8, or x≥0.9, or x≥0.95.
In some embodiments the redox-active electrode material comprises a metal salt that stores an alkali ion by undergoing a displacement or conversion reaction. Examples of such compounds include metal oxides such as CoO, Co3O4, NiO, CuO, MnO, typically used as a negative electrode in a lithium battery, which upon reaction with Li undergo a displacement or conversion reaction to form a mixture of Li2O and the metal constituent in the form of a more reduced oxide or the metallic form. Other examples include metal fluorides such as CuF2, FeF2, FeF3, BiF3, CoF2, and NiF2, which undergo a displacement or conversion reaction to form LiF and the reduced metal constituent. Such fluorides may be used as the positive electrode in a lithium battery. In other embodiments, the redox-active electrode material comprises carbon monofluoride or its derivatives. In some embodiments the material undergoing displacement or conversion reaction is in the form of particulates having on average dimensions of 100 nanometers or less. In some embodiments the material undergoing displacement or conversion reaction comprises a nanocomposite of the active material mixed with an inactive host, including but not limited to conductive and relatively ductile compounds such as carbon, or a metal, or a metal sulfide. FeS2 and FeF3 can also be used as cheap and electronically conductive active materials in a nonaqueous or aqueous lithium system. In some embodiments, a CFx electrode, FeS2 electrode, or MnO2 electrode is a positive electrode used with a lithium metal negative electrode to produce a lithium battery. In some embodiments, such battery is a primary battery. In some embodiments, such battery is a rechargeable battery.
In some embodiments, the working ion is selected from the group consisting of Li+, Na+, H+, Mg2+, Al3+, or Ca2+.
In some embodiments, the working ion is selected from the group consisting of Li+ or Na+.
In some embodiments, the semi-solid ion-storing redox composition includes a solid including an ion-storage compound.
In some embodiments, the ion is proton or hydroxyl ion and the ion storage compound includes those used in a nickel-cadmium or nickel metal hydride battery.
In some embodiments, the ion is lithium and the ion storage compound is selected from the group consisting of metal fluorides such as CuF2, FeF2, FeF3, BiF3, CoF2, and NiF2.
In some embodiments, the ion is lithium and the ion storage compound is selected from the group consisting of metal oxides such as CoO, Co3O4, NiO, CuO, MnO.
In some embodiments, the ion is lithium and the ion storage compound includes an intercalation compound selected from compounds with formula (Li1-xZx)MPO4, where M is one or more of V, Cr, Mn, Fe, Co, and Ni, and Z is a non-alkali metal dopant such as one or more of Ti, Zr, Nb, Al, or Mg, and x ranges from 0.005 to 0.05.
In some embodiments, the ion is lithium and the ion storage compound includes an intercalation compound selected from compounds with formula LiMPO4, where M is one or more of V, Cr, Mn, Fe, Co, and Ni, in which the compound is optionally doped at the Li, M or O-sites.
In some embodiments, the ion is lithium and the ion storage compound includes an intercalation compound selected from the group consisting of Ax(M′1-aM″a)y(XD4)z, Ax(M′1-aM″a)y(DXD4)z, and Ax(M′1-aM″a)y(X2D7)z, wherein x, plus y(1-a) times a formal valence or valences of M′, plus ya times a formal valence or valence of M″, is equal to z times a formal valence of the XD4, X2D7, or DXD4 group; and A is at least one of an alkali metal and hydrogen, M′ is a first-row transition metal, X is at least one of phosphorus, sulfur, arsenic, molybdenum, and tungsten, M″ any of a Group IIA, IIIA, IVA, VA, VIA, VIIA, VIIIA, IB, IIB, IIIB, IVB, VB, and VIB metal, D is at least one of oxygen, nitrogen, carbon, or a halogen.
In some embodiments, the ion is lithium and the ion storage compound includes an intercalation compound selected from the group consisting of A1-aM″a)xM′y(XD4)z, (A1-aM″a)xM′y(DXD4)z and A1-aM″a)xM′y(X2D7)z, where (1-a)x plus the quantity ax times the formal valence or valences of M″ plus y times the formal valence or valences of M′ is equal to z times the formal valence of the XD4, X2D7 or DXD4 group, and A is at least one of an alkali metal and hydrogen, M′ is a first-row transition metal, X is at least one of phosphorus, sulfur, arsenic, molybdenum, and tungsten, M″ any of a Group IIA, IIIA, IVA, VA, VIA, VIIA, VIIIA, IB, IIB, IIIB IVB, VB, and VIB metal, D is at least one of oxygen, nitrogen, carbon, or a halogen.
In some embodiments, the ion is lithium and the ion storage compound includes an intercalation compound selected from the group consisting of ordered rocksalt compounds LiMO2 including those having the α-NaFeO2 and orthorhombic-LiMnO2 structure type or their derivatives of different crystal symmetry, atomic ordering, or partial substitution for the metals or oxygen, where M includes at least one first-row transition metal but may include non-transition metals including but not limited to Al, Ca, Mg or Zr.
In some embodiments, the semi-solid ion storing redox composition includes a solid including amorphous carbon, disordered carbon, graphitic carbon, or a metal-coated or metal decorated carbon.
In some embodiments, the semi-solid ion storing redox composition can include a solid including nanostructures, for example, nanowires, nanorods, and nanotetrapods.
In some embodiments, the semi-solid ion storing redox composition includes a solid including an organic redox compound.
In some embodiments, the positive electrode can include a semi-solid ion storing redox composition including a solid selected from the groups consisting of ordered rocksalt compounds LiMO2 including those having the α-NaFeO2 and orthorhombic-LiMnO2 structure type or their derivatives of different crystal symmetry, atomic ordering, or partial substitution for the metals or oxygen, wherein M Includes at least one first-row transition metal but may include non-transition metals including but not limited to Al, Ca, Mg, or Zr. The anode 150 can include a semi-solid ion-storing composition including a solid selected from the group consisting of amorphous carbon, disordered carbon, graphitic carbon, or a metal-coated or metal-decorated carbon.
In some embodiments, the semi-solid cathode 140 can include a semi-solid ion-storing redox composition such as, for example, a solid selected from the group consisting of Ax(M′1-aM″a)y(XD4)z, Ax(M′1-aM″a)y(DXD4)z, and Ax(M′1-aM″a)y(X2D7)z, and where x, plus y(1-a) times a formal valence or valences of M′, plus ya times a formal valence or valence of M″, is equal to z times a formal valence of the XD4, X2D7, or DXD4 group, and A is at least one of an alkali metal and hydrogen, M′ is a first-row transition metal, X is at least one of phosphorus, sulfur, arsenic, molybdenum, and tungsten, M″ any of a Group IIA, IIIA, IVA, VA, VIA, VIIA, VIIIA, IB, IIB, IIIB, IVB, VB, and VIB metal, D is at least one of oxygen, nitrogen, carbon, or a halogen. In some embodiments, the anode 150 can be semi-solid anode which includes a semi-solid ion-storing redox composition such as, for example, a solid selected from the group consisting of amorphous carbon, disordered carbon, graphitic carbon, or a metal-coated or metal-decorated carbon. In some embodiments, the anode 150 can include a semi-solid ion-storing redox composition including a compound with a spinel structure.
In some embodiments, the semi-solid cathode 140 can include a semi-solid ion-storing redox composition such as, for example, a compound selected from the group consisting of LiMn2O4 and its derivatives; layered-spinel nanocomposites in which the structure includes nanoscopic regions having ordered rocksalt and spinel ordering; so-called “high voltage spinels” with a potential vs. Li/Li+ that exceeds 4.3V including but not limited to LiNi0.5Mn1.5O4; olivines LiMPO4 and their derivatives, in which M includes one or more of Mn, Fe, Co, or Ni, partially fluorinated compounds such as LiVPO4F, other “polyanion” compounds, and vanadium oxides VxOy including V2O5 and V6O11.
In some embodiments the semi-solid battery is a lithium battery, and the anode 150 compound includes graphite, graphitic or non-graphitic carbon, amorphous carbon, mesocarbon microbeads, boron-carbon alloys, hard or disordered carbon, lithium titanate spinel, or a solid metal or metal alloy or metalloid or metalloid alloy that reacts with lithium to form intermetallic compounds, e.g., Si, Ge, Sn, Bi, Zn, Ag, Al, any other suitable metal alloy, metalloid alloy or combination thereof, or a lithiated metal or metal alloy including such compounds as LiAl, Li9Al4, Li3Al, LiZn, LiAg, Li10Ag3, Li5B4, Li7B6, Li12S17, Li21Si8, Li13S14, Li21Si5, Li5Sn2, Li13Sn5, Li7Sn2, Li22Sn5, Li2Sb, Li3Sb, LiBi, or Li3Bi, or amorphous metal alloys of lithiated or non-lithiated compositions, any other materials or alloys thereof, or any other combination thereof.
In some embodiments, the electrochemical function of the electrochemical cell 100 can be improved by mixing or blending the semi-solid cathode 140 and/or the semi-solid anode 150 particles with particulates of an electronically conductive material, such as solid inorganic conductive materials including but not limited to metals, metal carbides, metal nitrides, metal oxides, and allotropes of carbon including carbon black, graphitic carbon, carbon fibers, carbon microfibers, vapor-grown carbon fibers (VGCF), fullerenic carbons including “buckyballs”, carbon nanotubes (CNTs), multiwall carbon nanotubes (MWNTs), single wall carbon nanotubes (SWNTs), graphene sheets or aggregates of graphene sheets, and materials comprising fullerenic fragments. In some embodiments, such electronically insulating organic redox compounds are rendered electronically active by mixing or blending with an electronically conductive polymer, including but not limited to polyaniline or polyacetylene based conductive polymers or poly(3,4-ethylenedioxythiophene) (PEDOT), polypyrrole, polythiophene, poly(p-phenylene), poly(triphenylene), polyazulene, polyfluorene, polynaphtalene, polyanthracene, polyfuran, polycarbazole, tetrathiafulvalene-substituted polystyrene, ferrocene-substituted polyethylene, carbazole-substituted polyethylene, polyoxyphenazine, polyacenes, or poly(heteroacenes).). In some embodiments, the resulting semi-solid cathode 140 and/or semi-solid anode 150 mixture has an electronic conductivity of at least about 10−3 S/cm, of at least about 10−2 S/cm or more.
In some embodiments, the particles included in the semi-solid cathode 140 and/or semi-solid anode 150 can be configured to have a partial or full conductive coating.
In some embodiments, the semi-solid ion-storing redox composition includes an ion-storing solid coated with a conductive coating material. In some embodiments, the conductive coating material has higher electron conductivity than the solid. In some embodiments, the solid is graphite and the conductive coating material is a metal, metal carbide, metal oxide, metal nitride, or carbon. In some embodiments, the metal is copper.
In some embodiments, the solid of the semi-solid ion-storing material is coated with metal that is redox inert at the operating conditions of the redox energy storage device. In some embodiments, the solid of the semi-solid ion storing material is coated with copper to increase the conductivity of the storage material particle, to increase the net conductivity of the semi-solid, and/or to facilitate charge transfer between energy storage particles and conductive additives. In some embodiments, the storage material particle is coated with, about 1.5% by weight metallic copper. In some embodiments, the storage material particle is coated with about 3.0% by weight metallic copper. In some embodiments, the storage material particle is coated with about 8.5% by weight metallic copper. In some embodiments, the storage material particle is coated with about 10.0% by weight metallic copper. In some embodiments, the storage material particle is coated with about 15.0% by weight metallic copper. In some embodiments, the storage material particle is coated with about 20.0% by weight metallic copper.
In some embodiments, the conductive coating is placed on the semi-solid cathode 140 and/or anode 150 particles by chemical precipitation of the conductive element and subsequent drying and/or calcination.
In some embodiments, the conductive coating is placed on the semi-solid cathode 140 and/or anode 150 particles by electroplating (e.g., within a fluidized bed).
In some embodiments, the conductive coating is placed on the semi-solid cathode 140 and/or anode 150 particles by co-sintering with a conductive compound and subsequent comminution.
In some embodiments, the electrochemically active particles have a continuous intraparticle conductive material or are embedded in a conductive matrix.
In some embodiments, a conductive coating and intraparticulate conductive network is produced by multicomponent-spray-drying, a semi-solid cathode 140 and/or anode 150 particles and conductive material particulates.
In some embodiments, the semi-solid composition (e.g., the semi-solid cathode 140 composition or the semi-solid anode 150 composition) also includes conductive polymers that provide an electronically conductive element. In some embodiments, the conductive polymers can include one or more of a polyacetylene, polyaniline, polythiophene, polypyrrole, poly(p-phenylene), poly(triphenylene), polyazulene, polyfluorene, polynaphtalene, polyanthracene, polyfuran, polycarbazole, polyacenes, poly(heteroacenes). In some embodiments, the conductive polymer can be a compound that reacts in-situ to form a conductive polymer on the surface of the active material particles. In some embodiments, the compound can be 2-hexylthiophene or 3-hexylthiophene and oxidizes during charging of the battery to form a conductive polymer coating on solid particles in the cathode semi-solid suspension. In other embodiments, redox active material can be embedded in conductive matrix. The redox active material can coat the exterior and interior interfaces in a flocculated or agglomerated particulate of conductive material. In some embodiments, the redox-active material and the conductive material can be two components of a composite particulate. Without being bound by any theory or mode of operation, such coatings can pacify the redox active particles and can help prevent undesirable reactions with carrier liquid or electrolyte. As such, it can serve as a synthetic solid-electrolyte interphase (SEI) layer.
In some embodiments, inexpensive iron compounds such as pyrite (FeS2) are used as inherently electronically conductive ion storage compounds. In some embodiments, the ion that is stored is Li+.
In some embodiments, redox mediators are added to the semi-solid to improve the rate of charge transfer within the semi-solid electrode. In some embodiments, this redox mediator is ferrocene or a ferrocene-containing polymer. In some embodiments, the redox mediator is one or more of tetrathiafulvalene-substituted polystyrene, ferrocene-substituted polyethylene, carbazole-substituted polyethylene.
In some embodiments, the surface conductivity or charge transfer resistance of the positive current collectors 110 and/or the negative current collector 120 included in the electrochemical cell 100 is increased by coating the current collector surface with a conductive material. Such layers can also serve as a synthetic SEI layer. Non-limiting examples of conductive coating materials include carbon, a metal, metal-carbide, metal nitride, metal oxide, or conductive polymer. In some embodiments, the conductive polymer includes but is not limited to polyaniline or polyacetylene based conductive polymers or poly(3,4-ethylenedioxythiophene) (PEDOT), polypyrrole, polythiophene, poly(p-phenylene), poly(triphenylene), polyazulene, polyfluorene, polynaphtalene, polyanthracene, polyfuran, polycarbazole, tetrathiafulvalene-substituted polystyrene, ferrocene-substituted polyethylene, carbazole-substituted polyethylene, polyoxyphenazine, polyacenes, or poly(heteroacenes). In some embodiments, the conductive polymer is a compound that reacts in-situ to form a conductive polymer on the surface of the current collector. In some embodiments, the compound is 2-hexylthiophene and oxidizes at a high potential to form a conductive polymer coating on the current collector. In some embodiments; the current collector is coated with metal that is redox-inert at the operating conditions of the redox energy storage device.
The semi-solid redox compositions can include various additives to improve the performance of the redox cell. The liquid phase of the semi-solids in such instances would comprise a solvent, in which is dissolved an electrolyte salt, and binders, thickeners, or other additives added to improve stability, reduce gas formation, improve SEI formation on the negative electrode particles, and the like. Examples of such additives included vinylene carbonate (VC), vinylethylene carbonate (VEC), fluoroethylene carbonate (FEC), or alkyl cinnamates, to provide a stable passivation layer on the anode or thin passivation layer on the oxide cathode, propane sultone (PS), propene sultone (PrS), or ethylene thiocarbonate as antigassing agents, biphenyl (BP), cyclohexylbenzene, or partially hydrogenated terphenyls, as gassing/safety/cathode polymerization agents, or lithium bis(oxatlato)borate as an anode passivation agent.
In some embodiments, the semi-solid cathode 140 and/or anode 150 can include a non-aqueous liquid electrolyte that can include polar solvents such as, for example, alcohols or aprotic organic solvents. Numerous organic solvents have been proposed as the components of Li-ion battery electrolytes, notably a family of cyclic carbonate esters such as ethylene carbonate, propylene carbonate, butylene carbonate, and their chlorinated or fluorinated derivatives, and a family of acyclic dialkyl carbonate esters, such as dimethyl carbonate, diethyl carbonate, ethylmethyl carbonate, dipropyl carbonate, methyl propyl carbonate, ethyl propyl carbonate, dibutyl carbonate, butylmethyl carbonate, butylethyl carbonate and butylpropyl carbonate. Other solvents proposed as components of Li-ion battery electrolyte solutions include y-butyrolactone, dimethoxyethane, tetrahydrofuran, 2-methyl tetrahydrofuran, 1,3-dioxolane, 4-methyl-1,3-dioxolane, diethyl ether, sulfolane, methylsulfolane, acetonitrile, propiononitrile, ethyl acetate, methyl propionate, ethyl propionate, dimethyl carbonate, tetraglyme, and the like. These nonaqueous solvents are typically used as multicomponent mixtures, into which a salt is dissolved to provide ionic conductivity. Exemplary salts to provide lithium conductivity include LiClO4, LiPF6, LiBF4, LiTFSI, LiBETI, LiBOB, and the like.
In some embodiments, the non-aqueous cathode 140 and/or anode 150 semi-solid compositions are prevented from absorbing impurity water and generating acid (such as HF in the case of LiPF6 salt) by incorporating compounds that getter water into the active material suspension, or into the storage tanks or other plumbing of the system, for example, in the case of redox flow cell batteries. Optionally, the additives are basic oxides that neutralize the acid. Such compounds include but are not limited to silica gel, calcium sulfate (for example, the product known as Drierite), aluminum oxide and aluminum hydroxide.
In some embodiment, the cathode 140 can be a semi-solid cathode and the anode 150 can be a conventional anode for example, a solid anode formed from the calendering process as is commonly known in the arts. In some embodiments, the cathode 140 can be a semi-solid cathode and the anode 150 can also be a semi-solid anode as described herein. In some embodiments, the cathode 140 and the anode 150 can both be semi-solid flowable electrodes, for example, for use in a redox flow cell.
In some embodiments, the semi-solid cathode 140 and the semi-solid anode 150 can be prepared by combining a quantity of an active material with an electrolyte and a conductive material, and mixing until a substantially stable suspension forms that has a mixing index of at least about 0.9, at least about 0.95, or at least about 0.975, inclusive of all ranges therebetween. In some embodiments, the semi-solid cathode 140 and/or the semi-solid anode 150 material is mixed until the electrode material has an electronic conductivity of at least about 10−3 S/cm, or at least about 10−2 S/cm, inclusive of all ranges therebetween. In some embodiments, the electrode material is mixed until the electrode material has an apparent viscosity of less than about 25,000 Pa-s, less than about 10,000 Pa-s, less than about 1,000 Pa-s, or less than about 100 Pa-s at an apparent shear rate of about 5 s−1, inclusive of all ranges therebetween. In such embodiments, the semi-solid cathode 140 can include about 35-75 vol % of active material and about 0.5-8 vol % of conductive material, and the semi-solid anode 150 can include about 35-75 vol % of active material and about 0-10 vol % of conductive material. Furthermore, the electrochemical cell 100 that includes the semi-solid cathode 140 and/or the semi-solid anode 150 can have an area specific capacity of at least about 7 mAh/cm2, for example, at least about 8 mAh/cm2, at least about 9 mAh/cm2, or at least about 10 mAh/cm2. In some embodiments, the active material included in the semi-solid cathode 140 can be LFP. In such embodiments, the electrochemical 100 can have an area specific capacity of at least about 7 mAh/cm2 at a C-rate of C/4. In some embodiments, the active material included in the semi-solid cathode can be NMC. In such embodiments, the electrochemical cell 100 can have an area specific capacity of at least about 7 mAh/cm2 at a C-rate of C/4.
In some embodiments, the mixing of the electrode material (e.g., the semi-solid cathode 140 or the semi-solid anode 150) can be performed with, for example, any one of a high shear mixer, a planetary mixer, a centrifugal planetary mixture, a sigma mixture, a CAM mixture and/or a roller mixture. In some embodiments, the mixing of the electrode material can supply a specific mixing energy of at least about 90 J/g, at least about 100 J/g, about 90 J/g to about 150 J/g, or about 100 J/g to about 120 J/g, inclusive of all ranges therebetween.
In some embodiments, the composition of the electrode material and the mixing process can be selected to homogeneously disperse the components of the slurry, achieve a percolating conductive network throughout the slurry and sufficiently high bulk electrical conductivity, which correlates to desirable electrochemical performance as described in further detail herein, to obtain a rheological state conducive to processing, which may include transfer, conveyance (e.g., extrusion), dispensing, segmenting or cutting, and post-dispense forming (e.g., press forming, rolling, calendering, etc.), or any combination thereof.
During mixing, the compositional homogeneity of the slurry will generally increase with mixing time, although the microstructure of the slurry may be changing as well. The compositional homogeneity of the slurry suspension can be evaluated quantitatively by an experimental method based on measuring statistical variance in the concentration distributions of the components of the slurry suspension. For example, mixing index is a statistical measure, essentially a normalized variance or standard deviation, describing the degree of homogeneity of a composition. (See, e.g., Erol, M, & Kalyon, D. M., Assessment of the Degree of Mixedness of Filled Polymers, Intern. Polymer Processing XX (2005) 3, pps. 228-237). Complete segregation would have a mixing index of zero and a perfectly homogeneous mix a mixing index of one. Alternatively, the homogeneity of the slurry can be described by its compositional uniformity (+x %/−y %), defined herein as the range: (100%−y)*C to (100%+x)*C. All of the values x and y are thus defined by the samples exhibiting maximum positive and negative deviations from the mean value C, thus the compositions of all mixed material samples taken fall within this range.
The basic process of determining mixing index includes taking a number of equally and appropriately sized material samples from the aggregated mix and conducting compositional analysis on each of the samples. The sampling and analysis can be repeated at different times in the mixing process. The sample size and volume is based on considerations of length scales over which homogeneity is important, for example, greater than a multiple of both the largest solid particle size and the ultimate mixed state average intra-particle distance at the low end, and 1/Nth of the total volume where N is the number of samples at the high end. Optionally, the samples can be on the order of the electrode thickness, which is generally much smaller than the length and width of the electrode. Capabilities of certain experimental equipment, such as a thermo-gravimetric analyzer (TGA), will narrow the practical sample volume range further. Sample “dimension” means the cube root of sample volume. For, example, a common approach to validating the sampling (number of samples) is that the mean composition of the samples corresponding to a given mixing duration matches the overall portions of material components introduced to the mixer to a specified tolerance. The mixing index at a given mixing time is defined, according to the present embodiments, to be equal to 1σ/σref, where σ is the standard deviation in the measured composition (which may be the measured amount of any one or more constituents of the slurry) and σref is equal to [C(1−C)]1/2, where C is the mean composition of the N samples, so as the variation in sample compositions is reduced, the mixing index approaches unity. It should be understood in the above description that “time” and “duration” are general terms speaking to the progression of the mixing event.
In one embodiment, a total sample volume of 43 cubic centimeters containing 50% by volume active material powder with a particle size distribution with D50=10 um and D90=15 um, and 6% by volume conductive additive agglomerates powder with D50=8 um and D90=12 um in organic solvent is prepared. This mixture can, for example, be used to build electrodes with an area of 80 cm2, and a thickness of 500 μm. The sample dimension should be larger than the larger solid particle size, i.e., 15 μm, and also the larger mixed state intra-particle length scale, i.e., about 16 μm, by a predetermined factor. With a target of N=14 samples, the sample dimension should be less than 2,500 μm. The specific dimension of interest is in the middle of this range, i.e., 500 μm. Accordingly, to quantify mixing index, the samples are taken with a special tool having a cylindrical sampling cavity with a diameter of 0.5 mm and a depth of 0.61 mm. In this example, the sample volume would be 0.12 mm3.
In some embodiments, the sample volume selection for mixing index measurement is guided by length scales over which uniformity is important. In some embodiments, this length scale is the thickness (e.g., 100 μm to 2,000 μm) of an electrode in which the slurry will be used. For example, if the electrode is 0.5 mm thick, the sample volume should preferably be on the order of (0.5 mm)3=0.125 mm3, i.e., between about 0.04 mm3 and about 0.4 mm3. If the electrode is 0.2 mm thick, the sample volume should preferably be between 0.0025 and 0.025 mm3. If the electrode is 2.0 mm thick, the sample volume should preferably be between 2.5 mm3 and 25 mm3. In some embodiments, the sample volume by which mixing index is evaluated is the cube of the electrode thickness ±10%. In some embodiments, the sample volume by which mixing index is evaluated is 0.12 mm3 ±10%. In one embodiment, the mixing index is measured by taking N samples where N is at least 9, each sample having the sample volume, from a batch of the electrode slurry or from a formed slurry electrode that has a volume greater than the total volume of the N samples. Each of the sample volumes is heated in a thermo gravimetric analyzer (TGA) under flowing oxygen gas according to a time-temperature profile wherein there is 3 minute hold at room temperature, followed by heating at 20° C./min to 850° C., with the cumulative weight loss between 150° C. and 600° C. being used to calculate the mixing index. Measured in this manner, the electrolyte solvents are evaporated and the measured weight loss is primarily that due to pyrolysis of carbon in the sample volume.
As described herein, conductive additives can have technical characteristics and morphologies (i.e., hierarchical clustering of fundamental particles) that influence their dispersive and electrochemical behavior in dynamic and/or static suspensions. Characteristics that can influence dispersive and electrochemical behavior of conductive additives include surface area and bulk conductivity. For example, in the case of certain conductive carbon additives, morphological factors can impact the dispersion of the carbon particles. The primary carbon particles have dimensions on the order of nanometers, the particles typically exist as members of larger aggregates, consisting of particles either electrically bound (e.g., by Van der Waals forces) or sintered together. Such agglomerates may have dimensions on the order of nanometers to microns. Additionally, depending on the surface energies of the particles, environment, and/or temperature, aggregates can form larger scale clusters commonly referred to as agglomerates, which can have dimensions on the order of microns to tens of microns.
When such conductive additives are included in a slurry, fluid shearing forces, e.g., imparted during mixing, can disrupt the carbon network, for example, by overcoming agglomerate and aggregate binding forces. By disrupting the conductive network, the additives can be present in a finer scale (more granular and more homogeneous) dispersion of the conductive solid. Mixing can also densify clusters of the conductive solid. In some embodiments, mixing can both disrupt the conductive network and densify clusters, which can sever electrical conduction pathways and adversely impact electrochemical performance.
The quantity of a conductive additive, i.e., the mass or volume fraction of the conductive additive (also referred to herein as the conductive additive “loading”) that is used in a given mixture relative to other components, such as an active material, that is suitable for the mixture to achieve a specified level of bulk electrical conductivity depends on the cluster state. Percolation theory can be used to select a loading of conductive additive. Referring now to
In some embodiments, it is desirable for the electrochemically active slurry to be “workable,” in order to facilitate material handling associated with battery manufacturing. For example, if a slurry is too fluid it can be compositionally unstable. In other words, the homogeneity can be lost under exposure to certain forces, such as gravity (e.g., solids settling) or centrifugal forces. If the slurry is unstable, solid phase density differences, or other attributes, can give rise to separation and/or compositional gradients. Said another way, if the slurry is overly fluidic, which may be the result of low solids loadings or a significantly disrupted conductive network, the solids may not be sufficiently bound in place to inhibit particle migration. Alternatively, if an electrochemically active slurry is too solid, the slurry may break up, crumble, and/or otherwise segregate into pieces, which can complicate processing and dimensional control. Formulating the slurry within a band of adequate workability can facilitate easier slurry-based battery manufacturing. Workability of a slurry can typically be quantified using rheological parameters which can be measured using rheometers. Some examples of different types of rheometers that can be used to quantify slurry workability include: strain or stress-controlled rotational, capillary, slit, and extensional.
In some embodiments, the ratios between active material, conductive additive, and electrolyte can affect the stability, workability, and/or rheological properties of the slurry.
In some embodiments, the conductive additive can affect the rheology of the suspension. Thus, in such embodiments, at the same loading levels of conductive additive, increasing concentrations of active materials can contribute to the rheology of the slurry by increasing the shear viscosity of the suspension.
The slurry suspensions can be prone to separation and flow instabilities, structure development, mat formation and/or binder filtration when flowing under a critical shear stress values due to a low viscosity liquid matrix in the formulation. Such behavior can be characterized using a capillary rheometer using a small diameter and a long L/D. The compositional formulation, especially conductive carbon loading levels, and the extrusion temperature can impact such structural changes during a pressure driven flow.
As mixing energy increases, homogeneity of the mixture can increase. If mixing is allowed to continue, eventually excessive mixing energy can be imparted to the slurry. For example, as described herein, excessive mixing energy can produce a slurry characterized by low electronic conductivity. As mixing energy is added to the slurry, the aggregates of conductive additive can be broken up and dispersed, which can tend to form a network like conductive matrix, as described above with reference to
As described herein, compositional homogeneity of the slurry will generally increase with mixing time and the compositional homogeneity can be characterized by the mixing index.
In some embodiments, the mixing time can have a simultaneous impact on the mixing index and conductivity of an electrode slurry.
In some embodiments, shear rate can influence mixing dynamics and conductivity. As a result, in some embodiments, the selection of mixing element rotation speed, container and/or roller size, clearance dimensions/geometry, and so forth can have an effect on conductivity.
In some embodiments, the progression of mixing index over time for a fixed RPM (e.g., 100 RPM) mixing speed can depend on the composition of the materials being mixed. For example,
The following examples show the electrochemical properties of various electrochemical cells that include the semi-solid electrodes described herein, compared with two conventional tablet batteries that include Li-ion Tablet Battery 1 and Li-ion Tablet Battery 2.
A first commercially available tablet battery, Li-ion Tablet Battery 1 (also referred to as “Comp Ex 1”) was discharged at various C-rates as shown in
A second commercially available tablet battery, Li-ion Tablet Battery 2 (also referred to as “Comp Ex 2”) was discharged at various C-rates as shown in
An electrochemical full cell (also referred to as “Comp Ex 3”) included a semi-solid cathode formulated from 46 vol % LiFePO4. The semi-solid cathode was tested against a semi-solid anode formulated from 50 vol % graphite and 2 vol % carbon additive. The LFP semi-solid cathode was prepared by mixing 46 vol % LFP and 0.9 vol % Ketjen with E13 electrolyte. The cathode slurry was prepared using a centrifugal planetary mixer at 1250 rpm for 90 seconds. The graphite semi-solid anode was prepared by mixing 50 vol % graphite and 2 vol % carbon black using the same electrolyte as the cathode. The anode slurry formulation was prepared using a centrifugal planetary mixer at 650 rpm for about 5 minutes.
An electrochemical half cell Example 1 (also referred to as “Ex 1”) was prepared using a semi-solid cathode and a Li metal anode. The LFP semi-solid cathode was prepared by mixing 45 vol % LFP and 2 vol % carbon black with an ethylene carbonate/dimethyl carbonate/LiPF6 based electrolyte. The cathode slurry was prepared using a batchmixer with a roller mill blade fitting. Mixing was performed at 100 rpm for about 2 minutes. The semi-solid slurry had a mixing index greater than 0.9 and a conductivity of 1.5×10−4 S/cm. The slurry was made into an electrode of about 250 μm thickness and was tested against a Li metal anode in a Swagelok cell configuration. The cell was tested using a Maccor battery tester and was cycled between a voltage range of V=2-4.2 V. The cell was charged using a constant current-constant voltage (CC-CV) procedure with a constant current rate at C/10 and C/8 for the first two cycles then at C/5 for the latter cycles. The constant current charge is followed by a constant voltage hold at 4.2 V until the charging current decreased to less than C/20. The cell was discharged over a range of current densities corresponding to C-rates between C/10 and 5 C. As shown in
An electrochemical half cell Example 2 (also referred to as “Ex 2”) was prepared using a semi-solid cathode and a lithium metal anode. The cathode slurry was prepared by mixing 45 vol % Li(Ni,Mn,Co)O2 and 8 vol % carbon additive with an ethylene carbonate/dimethyl carbonate/LiPF6 based electrolyte. The cathode slurry was prepared using a batchmixer fitted with roller blades. Mixing was performed at 100 rpm for about 4 minutes. The slurry was made into an electrode of about 250 μm thickness and was tested against a Li metal anode in a Swagelok cell configuration. The cell was tested using a Maccor battery tester and was cycled over a voltage range of V=2-4.3 V. The cell was charged using a CC-CV procedure with the constant current portion being at C/10 and C/8 rate for the first two cycles then at C/5 rate for later cycles. The constant current charge step was followed by a constant voltage hold at 4.2 V until the charging current decreased to less than C/20. The cell was then discharged over a range of current density. As shown in
An electrochemical full cell Example 3 (also referred to as “Ex 3”) included a semi-solid cathode formulated from 35 vol % Li(Ni,Mn,Co)O2 such that the semi-solid cathode had a thickness of about 250 μm, and was tested against a semi-solid anode formulated from 40 vol % graphite and 2 vol % carbon additive such that the anode had a thickness of about 500 μm. The NMC semi-solid cathode was prepared by mixing 35 vol % NMC and 8 vol % carbon black with an ethylene carbonate/dimethyl carbonate/LiPF6 based electrolyte. The cathode slurry was prepared using a batchmixer fitted with roller blades. Mixing was performed at 100 rpm for 4 minutes. The graphite semi-solid anode was prepared by mixing 40 vol % graphite and 2 vol % carbon black using the same electrolyte as the cathode. The anode slurry formulation was mixed at 100 rpm for about 30 seconds to yield a semi-solid anode suspension. The electrodes were used to form a NMC-Graphite based electrochemical full cell having active areas for both cathode and anode of approximately 80 cm2. The electrochemical full cell Ex 3 was charged using a CC-CV procedure and a constant current discharge between 2.75-4.2 V using a Maccor tester. The cell was discharged over a range of current densities. As shown in
An electrochemical full cell Example 4 (also referred to as “Ex 4”) included a semi-solid cathode formulated from 35 vol % Li(Ni,Mn,Co)O2 such that the semi-solid cathode had a thickness of about 500 μm. The semi-solid cathode tested against a semi-solid anode formulated from 40 vol % graphite and 2 vol % carbon additive such that the anode had a thickness of about 500 μm. The NMC semi-solid cathode was prepared by mixing 35 vol % NMC and 8 vol % carbon additive with an ethylene carbonate/dimethyl carbonate/LiPF6 based electrolyte. The cathode slurry was mixed in a mixer fitted with roller blades for about 4 minutes at about 100 rpm. The graphite semi-solid anode was prepared by mixing 40 vol % graphite and 2 vol % carbon additive using the same electrolyte as the cathode. The anode slurry formulation was also mixed in a mixer fitted with roller blades for about 30 seconds at 100 rpm. The Ex 4 electrochemical full cell had active areas for both cathode and anode of approximately 80 cm2. The Ex 4 full cell was charged and discharge using a CC-CV procedure and a constant current discharge between 2.75-4.2 V using a Maccor tester. The cell was discharged over a range of current densities. As shown in
An electrochemical half cell Example 5 (also referred to as “Ex 5”) was prepared using a semi-solid cathode and a lithium metal anode. The cathode slurry was prepared by mixing a 55 vol % Li(Ni,Mn,Co)O2 and 4 vol % carbon additive with an ethylene carbonate/dimethyl carbonate/LiPF6 based electrolyte. The cathode slurry was prepared using a batch mixer fitted with roller blades. Mixing was performed at 100 rpm for about 4 minutes. The cathode slurry was formed into an about 250 μm thick semi-solid cathode which was tested against the Li metal anode in a Swagelok cell configuration. The cell was tested using a Maccor battery tester and was cycled over a voltage range of 2-4.3 V. The cell was charged using a CC-CV procedure with the constant current portion being at C/10 and C/8 rate for the first two cycles than at C/5 rate for later cycles. The constant current charge step was followed by a constant voltage hold at 4.2 V until the charging current decreased to less than C/20. The cell was discharged over a range of current densities. As shown in
An electrochemical half cell Example 6 (also referred to as “Ex 6”) was prepared using a semi-solid cathode and a lithium metal anode. The cathode slurry was prepared by mixing a 60 vol % Li(Ni,Mn,Co)O2 and 2 vol % carbon additive with an ethylene carbonate/dimethyl carbonate/LiPF6 based electrolyte. The cathode slurry was prepared using a batch mixer fitted with roller blades. Mixing was performed at 100 rpm for about 4 minutes. The cathode slurry was formed into an about 250 μm thick semi-solid which was tested against the Li metal anode in a Swagelok cell configuration. The cell was tested using a Maccor battery tester and was cycled over a voltage range of 2-4.3 V. The Ex 6 cell was charged using a CC-CV procedure with the constant current portion being at C/10 and C/8 rate for the first two cycles than at C/5 rate for later cycles. The constant current charge step was followed by a constant voltage hold at 4.2 V until the charging until the charging current decreased to less than C/20. The cell was discharged over a range of current density. As shown in
An electrochemical full cell Example 7 (also referred to as “Ex 7”) included a semi-solid cathode formulated from 40 vol % LiFePO4 such that the semi-solid cathode had a thickness of about 500 μm. The semi-solid cathode was tested against a semi-solid anode formulated from 35 vol % graphite and 2 vol % carbon additive such that the anode had a thickness of about 500 μm. The LFP semi-solid cathode was prepared by mixing 40 vol % LFP and 2 vol % carbon additive with an ethylene carbonate/dimethyl carbonate/LiPF6 based electrolyte. The cathode slurry was prepared using a batchmixer fitted with roller blades. Mixing was performed at 100 rpm for about 4 minutes. The graphite semi-solid anode was prepared by mixing 40 vol % graphite and 2 vol % carbon black using the same electrolyte as the cathode. The anode slurry formulation was mixed at 100 rpm for about 30 seconds to yield a semi-solid anode suspension. The Ex 7 electrochemical cell had active areas for both cathode and anode of approximately 80 cm2. The electrochemical full cell Ex 7 was charged using a CC-CV procedure and a constant current discharge was performed between 2.0-3.9 V using a Maccor tester. The cell was discharged over a range of current densities. As shown in
An electrochemical full cell Example 8 (also referred to as “Ex 8”) included a semi-solid cathode formulated from 45 vol % LiFePO4 such that the semi-solid cathode had a thickness of about 330 μm. The semi-solid cathode was tested against a semi-solid anode formulated from 40 vol % graphite and 2 vol % carbon additive such that the anode had a thickness of about 500 μm. The LFP semi-solid cathode was prepared by mixing 45 vol % LFP and 1.9 vol % carbon additive with an ethylene carbonate/dimethyl carbonate/LiPF6 based electrolyte. The cathode slurry was prepared using a batchmixer fitted with roller blades. Mixing was performed at 100 rpm for about 25 minutes. The graphite semi-solid anode was prepared by mixing 40 vol % graphite and 2 vol % carbon black using the same electrolyte as the cathode. The anode slurry formulation was mixed at 100 rpm for about 30 seconds to yield a semi-solid anode suspension. The Ex 8 electrochemical cell had active areas for both cathode and anode of approximately 80 cm2. The electrochemical full cell Ex 8 was charged using a CC-CV procedure. A constant current discharge was performed between 2.0-3.9 V using a Maccor tester. The cell was discharged over a range of current densities. As shown in
An electrochemical full cell Example 9 (also referred to as “Ex 9”) included a semi-solid cathode formulated from 45 vol % LiFePO4 such that the semi-solid cathode had a thickness of about 470 μm. The semi-solid cathode was tested against a semi-solid anode formulated from 40 vol % graphite and 2 vol % carbon additive such that the anode had a thickness of about 500 μm. The LFP semi-solid cathode was prepared by mixing 45 vol % LFP and 2 vol % carbon additive with an ethylene carbonate/dimethyl carbonate/LiPF6 based electrolyte. The cathode slurry was prepared using a batchmixer fitted with roller blades. Mixing was performed at 100 rpm for about 25 minutes. The graphite semi-solid anode was prepared by mixing 40 vol % graphite and 2 vol % carbon black using the same electrolyte as the cathode. The anode slurry formulation was mixed at 100 rpm for about 30 seconds to yield a semi-solid anode suspension. The Ex 9 electrochemical cell had active areas for both cathode and anode of approximately 80 cm2. The electrochemical full cell Ex 9 was charged using a CC-CV procedure and a constant current discharge between 2.0-3.9 V using a Maccor tester. The cell was discharged over a range of current densities. As shown in
An electrochemical full cell Example 10 (also referred to as “Ex 10”) included a semi-solid cathode formulated from 45 vol % LiFePO4 such that the semi-solid cathode had a thickness of about 500 μm. The semi-solid cathode was tested against a semi-solid anode formulated from 40 vol % graphite and 1.5 vol % carbon additive such that the anode had a thickness of about 500 μm. The LFP semi-solid cathode was prepared by mixing 45 vol % LFP and 2 vol % carbon additive with an ethylene carbonate/dimethyl carbonate/LiPF6 based electrolyte. The cathode slurry was prepared using a high speed blade mixer. Mixing was performed for about 15 seconds until the semi-solid cathode slurry was homogeneous. The graphite semi-solid anode was prepared by mixing 40 vol % graphite and 1.5 vol % carbon black using the same electrolyte as the cathode. The anode slurry formulation was also mixed in the high speed blade mixer for about 15 seconds until homogeneous. The Ex 10 electrochemical cell had active areas for both cathode and anode of approximately 80 cm2. The electrochemical full cell Ex 10 was charged using a CC-CV procedure and a constant current discharge between 2.0-3.9 V using a Maccor tester. The cell was discharged over a range of current densities. As shown in
An electrochemical full cell Example 11 (also referred to as “Ex 11”) included a semi-solid cathode formulated from 50 vol % LiFePO4 such that the semi-solid cathode had a thickness of about 454 μm. The semi-solid cathode was tested against a semi-solid anode formulated from 50 vol % graphite and 2 vol % carbon additive such that the anode had a thickness of about 386 μm. The LFP semi-solid cathode was prepared by mixing 50 vol % LFP and 0.8 vol % carbon additive with an ethylene carbonate/dimethyl carbonate/LiPF6 based electrolyte. The cathode slurry was prepared using a centrifugal planetary mixer at 1250 rpm for 90 seconds. The graphite semi-solid anode was prepared by mixing 50 vol % graphite and 2 vol % carbon black using the same electrolyte as the cathode. The anode slurry formulation was prepared using a centrifugal planetary mixer at 650 rpm for about 5 minutes. The Ex 11 electrochemical cell had active areas for both cathode and anode of approximately 80 cm2. The electrochemical full cell Ex 11 was charged using a CC-CV procedure and a constant current discharge was performed between 2.0-3.9 V using a Maccor tester. As shown in
An electrochemical full cell Example 12 (also referred to as “Ex 12”) included a semi-solid cathode formulated from 60 vol % LiCoO2 such that the semi-solid cathode had a thickness of about 408 μm. The semi-solid cathode was tested against a semi-solid anode formulated from 67 vol % graphite and 2 vol % carbon additive such that the anode had a thickness of about 386 μm. The semi-solid cathode was prepared by mixing 60 vol % LiCoO2 and 0.9 vol % carbon additive with an ethylene carbonate/dimethyl carbonate/LiPF6 based electrolyte. The cathode slurry was prepared using a centrifugal planetary mixer at 1300 rpm for 90 seconds. The graphite semi-solid anode was prepared by mixing 67 vol % graphite and 2 vol % carbon black using the same electrolyte as the cathode. The anode slurry formulation was prepared using a centrifugal planetary mixer at 1300 rpm for about 90 seconds. The Ex 12 electrochemical cell had active areas for both cathode and anode of approximately 80 cm2. The electrochemical full cell Ex 12 was charged using a CC-CV procedure and a constant current discharge was performed between 2.75-4.1 V using a Maccor tester. As shown in
A semi-solid cathode Example 13 (also referred to as “Ex 13”) included a semi-solid cathode formulated from 57 vol % NMC with 1.14 vol % VGCF and 1.25 vol % Ketjen. The NMC, VGCF, and Ketjen are mixed with 40.61 vol % electrolyte with LiPF6 in ethylene carbonate (EC), propylene carbonate (PC), ethyl methyl carbonate (EMC), and diethyl carbonate (DEC) to form the semi-solid cathode material. The semi-solid cathode material was mixed in an acoustic mixer for 5 minutes to form the semi-solid cathode. The conductivity and yield stress of the Ex 13 semi-solid cathode were tested. As shown in
A semi-solid cathode Example 14 (also referred to as “Ex 14”) included a semi-solid cathode formulated from 57 vol % NMC with 3.42 vol % VGCF and 1.25 vol % Ketjen. The NMC, VGCF, and Ketjen are mixed with 38.33 vol % electrolyte with LiPF6 in EC/PC/EMC/DEC to form the semi-solid cathode material. The semi-solid cathode material was mixed in an acoustic mixer for 5 minutes to form the semi-solid cathode. The conductivity and yield stress of the Ex 14 semi-solid cathode were tested. As shown in
A semi-solid cathode Example 15 (also referred to as “Ex 15”) included a semi-solid cathode formulated from 57 vol % NMC with 6.84 vol % VGCF and 1.25 vol % Ketjen. The NMC, VGCF, and Ketjen are mixed with 34.91 vol % electrolyte with LiPF6 in EC/PC/EMC/DEC to form the semi-solid cathode. The semi-solid cathode material was mixed in an acoustic mixer for 5 minutes to form the semi-solid cathode. The conductivity and yield stress of the Ex 15 semi-solid cathode were tested. As shown in
Ex 13, Ex 14, and Ex 15 demonstrate technical effects that can result from replacement of all or a portion of conductive material with VGCF. The slope of the plot of conductivity vs. yield stress increases significantly such that an electrode can have higher conductivity while maintaining its yield stress or the electrode can maintain its conductivity while reducing its yield stress.
An electrochemical full cell Example 16 (also referred to as “Ex 16”) included a semi-solid cathode formulated from 45 vol % LiFePO4. The semi-solid cathode was tested against a semi-solid anode formulated from 50 vol % graphite and 2.6 vol % carbon additive. The LFP semi-solid cathode was prepared by mixing 45 vol % LFP, 0.9 vol % Ketjen, and 1 vol % CNF with E13 electrolyte. The semi-solid cathode material was mixed in an acoustic mixer for 5 minutes to form the semi-solid cathode. The graphite semi-solid anode was prepared by mixing 50 vol % graphite and 2 vol % carbon black using the same electrolyte as the cathode. The anode slurry formulation was prepared using a speedmix batch mixer at 900 rpm for about 15 seconds. The Ex 16 electrochemical cell was discharged at C/4, C/2, 1 C, and 2 C in four consecutive cycles. The Ex 16 electrochemical cell was compared to the Comp Ex 3 electrochemical cell, as shown in
As a basis of comparison, an LFP cathode with 45 vol % LFP and 1.9 vol % Ketjen in E13 electrolyte that is mixed in an acoustic mixer for 5 minutes behaves like a solid and cannot be casted like a semi-solid electrode. Additionally, an LFP cathode with 45 vol % LFP and 1.9 vol % VGCF that is mixed in an acoustic mixer for 5 minutes can result in an unstable or “runny” mixture.
A semi-solid cathode Example 17 (also referred to as “Ex 17”) included a semi-solid cathode formulated from 60 vol % NMC with 3 vol % Ketjen. NMC and Ketjen were milled together in a Nippon Coke mixer for 10 minutes at low shear stress and low power. The longer mixing at a low shear stress allows the conductive particles to become very fine and coat the outside of the active particles without breaking the active particles. The NMC and Ketjen are mixed with 37 vol % electrolyte with LiPF6 in ethylene carbonate (EC), propylene carbonate (PC), ethyl methyl carbonate (EMC), and diethyl carbonate (DEC) to form the semi-solid cathode. The conductivity and yield stress of the Ex 17 semi-solid cathode were tested. Ex. 17 exhibited a conductivity of about 450 mS/cm and a yield stress of about 159 kPa.
A semi-solid cathode Example 18 (also referred to as “Ex 18”) included a semi-solid cathode formulated from 57 vol % NMC with 3 vol % Ketjen. NMC and Ketjen were milled together in a Nippon Coke mixer for 10 minutes at high shear stress and high power. The mixing shear energy was measured as 70 J/m3 or 392 kJ/kg. The optimized shear stress allows the conductive particles to become very fine and coat the outside of the active particles without breaking the active particles. The NMC and Ketjen are mixed with 40 vol % electrolyte with LiPF6 in ethylene carbonate (EC), propylene carbonate (PC), ethyl methyl carbonate (EMC), and diethyl carbonate (DEC) to form the semi-solid cathode. The semi-solid cathode was tested against a semi-solid anode formulated from 50 vol % graphite and 2.6 vol % carbon additive. Upon formation of the electrochemical cell, the cell was discharged over 1,000 cycles at C/3 and recharged at C/4.
A semi-solid cathode Example 19 (also referred to as “Ex 19”) included a semi-solid cathode formulated from 57 vol % NMC with 1.25 vol % Ketjen. NMC and Ketjen were direct mixed in a v-blend mixer without milling. The NMC and Ketjen are mixed with 41.75 vol % electrolyte with LiPF6 in ethylene carbonate (EC), propylene carbonate (PC), ethyl methyl carbonate (EMC), and diethyl carbonate (DEC) to form the semi-solid cathode. The semi-solid cathode was tested against a semi-solid anode formulated from 50 vol % graphite and 2.6 vol % carbon additive. Upon formation of the electrochemical cell, the cell was discharged over 250 cycles at C/3 and recharged at C/4.
A semi-solid cathode Example 20 (also referred to as “Ex 20”) included a semi-solid cathode formulated from 57 vol % NMC with 1.5 vol % Ketjen. NMC and Ketjen were direct mixed in a v-blend mixer without milling . The longer mixing at a low shear stress allows the conductive particles to become very fine and coat the outside of the active particles without breaking the active particles. The NMC and Ketjen are mixed with 41.5 vol % electrolyte with LiPF6 in ethylene carbonate (EC), propylene carbonate (PC), ethyl methyl carbonate (EMC), and diethyl carbonate (DEC) to form the semi-solid cathode. The semi-solid cathode was tested against a semi-solid anode formulated from 50 vol % graphite and 2.6 vol % carbon additive. Upon formation of the electrochemical cell, the cell was discharged over 250 cycles at C/3 and recharged at C/4.
A semi-solid cathode Example 21 (also referred to as “Ex 21”) included a semi-solid cathode formulated from 57 vol % NMC with 3.42 vol % LiTX 50 conductive additive and 1.25 vol % Ketjen. NMC and LiTX 50 were milled together in a ball milling machine for 24 hrs with PTFE media at low shear stress and low power. The mixing shear energy was measured as 10 J/m3 or 47 kJ/kg. The longer mixing at a low shear stress allows the conductive particles to become very fine and coat the outside of the active particles without breaking the active particles. Then the NMC/LiTX50 powders is directly mixed with Ketjen by v-blend mixer without media. The NMC and Ketjen are mixed with 38.33 vol % electrolyte with LiPF6 in ethylene carbonate (EC), propylene carbonate (PC), ethyl methyl carbonate (EMC), and diethyl carbonate (DEC) to form the semi-solid cathode. The semi-solid cathode was tested against a semi-solid anode formulated from 50 vol % graphite and 2.6 vol % carbon additive. Upon formation of the electrochemical cell, the cell was discharged over 450 cycles at C/3 and recharged at C/4.
The cells with the Ex 18, Ex 19, Ex 20, and Ex 21 semi-solid cathodes are compared in
Various concepts may be embodied as one or more methods, of which at least one example has been provided. The acts performed as part of the method may be ordered in any suitable way. Accordingly, embodiments may be constructed in which acts are performed in an order different than illustrated, which may include performing some acts simultaneously, even though shown as sequential acts in illustrative embodiments. Put differently, it is to be understood that such features may not necessarily be limited to a particular order of execution, but rather, any number of threads, processes, services, servers, and/or the like that may execute serially, asynchronously, concurrently, in parallel, simultaneously, synchronously, and/or the like in a manner consistent with the disclosure. As such, some of these features may be mutually contradictory, in that they cannot be simultaneously present in a single embodiment. Similarly, some features are applicable to one aspect of the innovations, and inapplicable to others.
In addition, the disclosure may include other innovations not presently described. Applicant reserves all rights in such innovations, including the right to embodiment such innovations, file additional applications, continuations, continuations-in-part, divisional s, and/or the like thereof. As such, it should be understood that advantages, embodiments, examples, functional, features, logical, operational, organizational, structural, topological, and/or other aspects of the disclosure are not to be considered limitations on the disclosure as defined by the embodiments or limitations on equivalents to the embodiments. Depending on the particular desires and/or characteristics of an individual and/or enterprise user, database configuration and/or relational model, data type, data transmission and/or network framework, syntax structure, and/or the like, various embodiments of the technology disclosed herein may be implemented in a manner that enables a great deal of flexibility and customization as described herein.
All definitions, as defined and used herein, should be understood to control over dictionary definitions, definitions in documents incorporated by reference, and/or ordinary meanings of the defined terms.
As used herein, in particular embodiments, the terms “about” or “approximately” when preceding a numerical value indicates the value plus or minus a range of 10%. Where a range of values is provided, it is understood that each intervening value, to the tenth of the unit of the lower limit unless the context clearly dictates otherwise, between the upper and lower limit of that range and any other stated or intervening value in that stated range is encompassed within the disclosure. That the upper and lower limits of these smaller ranges can independently be included in the smaller ranges is also encompassed within the disclosure, subject to any specifically excluded limit in the stated range. Where the stated range includes one or both of the limits, ranges excluding either or both of those included limits are also included in the disclosure.
The phrase “and/or,” as used herein in the specification and in the embodiments, should be understood to mean “either or both” of the elements so conjoined, i.e., elements that are conjunctively present in some cases and disjunctively present in other cases. Multiple elements listed with “and/or” should be construed in the same fashion, i.e., “one or more” of the elements so conjoined. Other elements may optionally be present other than the elements specifically identified by the “and/or” clause, whether related or unrelated to those elements specifically identified. Thus, as a non-limiting example, a reference to “A and/or B”, when used in conjunction with open-ended language such as “comprising” can refer, in one embodiment, to A only (optionally including elements other than B); in another embodiment, to B only (optionally including elements other than A); in yet another embodiment, to both A and B (optionally including other elements); etc.
As used herein in the specification and in the embodiments, “or” should be understood to have the same meaning as “and/or” as defined above. For example, when separating items in a list, “or” or “and/or” shall be interpreted as being inclusive, i.e., the inclusion of at least one, but also including more than one, of a number or list of elements, and, optionally, additional unlisted items. Only terms clearly indicated to the contrary, such as “only one of” or “exactly one of,” or, when used in the embodiments, “consisting of,” will refer to the inclusion of exactly one element of a number or list of elements. In general, the term “or” as used herein shall only be interpreted as indicating exclusive alternatives (i.e., “one or the other but not both”) when preceded by terms of exclusivity, such as “either,” “one of” “only one of,” or “exactly one of” “Consisting essentially of,” when used in the embodiments, shall have its ordinary meaning as used in the field of patent law.
As used herein in the specification and in the embodiments, the phrase “at least one,” in reference to a list of one or more elements, should be understood to mean at least one element selected from any one or more of the elements in the list of elements, but not necessarily including at least one of each and every element specifically listed within the list of elements and not excluding any combinations of elements in the list of elements. This definition also allows that elements may optionally be present other than the elements specifically identified within the list of elements to which the phrase “at least one” refers, whether related or unrelated to those elements specifically identified. Thus, as a non-limiting example, “at least one of A and B” (or, equivalently, “at least one of A or B,” or, equivalently “at least one of A and/or B”) can refer, in one embodiment, to at least one, optionally including more than one, A, with no B present (and optionally including elements other than B); in another embodiment, to at least one, optionally including more than one, B, with no A present (and optionally including elements other than A); in yet another embodiment, to at least one, optionally including more than one, A, and at least one, optionally including more than one, B (and optionally including other elements); etc.
In the embodiments, as well as in the specification above, all transitional phrases such as “comprising,” “including,” “carrying,” “having,” “containing,” “involving,” “holding,” “composed of,” and the like are to be understood to be open-ended, i.e., to mean including but not limited to. Only the transitional phrases “consisting of” and “consisting essentially of” shall be closed or semi-closed transitional phrases, respectively, as set forth in the United States Patent Office Manual of Patent Examining Procedures, Section 2111.03.
While specific embodiments of the present disclosure have been outlined above, many alternatives, modifications, and variations will be apparent to those skilled in the art. Accordingly, the embodiments set forth herein are intended to be illustrative, not limiting. Various changes may be made without departing from the spirit and scope of the disclosure. Where methods and steps described above indicate certain events occurring in a certain order, those of ordinary skill in the art having the benefit of this disclosure would recognize that the ordering of certain steps may be modified and such modification are in accordance with the variations of the invention. Additionally, certain of the steps may be performed concurrently in a parallel process when possible, as well as performed sequentially as described above. The embodiments have been particularly shown and described, but it will be understood that various changes in form and details may be made.
This application claims priority and benefit of U.S. Provisional Application No. 63/082,629, filed Sep. 24, 2020 and entitled “Semi-Solid Electrodes with Carbon Additives, and Methods of Making the Same,” the disclosure of which is hereby incorporated by reference in its entirety.
Number | Date | Country | |
---|---|---|---|
63082629 | Sep 2020 | US |