Patent Application
20140151690
This application claims priority under 35 U.S.C. §119 to Korean Patent Application Nos. 10-2012-0138508 and 10-2013-0097345, respectively filed on Nov. 30, 2012 and Aug. 16, 2013, in the Korean Intellectual Property Office, the disclosures of which are incorporated herein in their entirety by reference.
1. Field
Example embodiments relate to semiconductor materials and/or devices including the same, and more particularly, to semiconductor materials, transistors including the same, and/or electronic devices including the transistors.
2. Description of Related Art
Transistors are widely used as switching devices and/or driving devices in electronic devices. In particular, since a thin film transistor (TFT) may be manufactured on a glass substrate or a plastic substrate, TFTs may be used in display apparatuses such as organic light-emitting display apparatuses or liquid crystal display apparatuses. The performance of a TFT may depend on properties of a channel layer (e.g., semiconductor layer).
Many commercially available display apparatuses use a TFT including a channel layer formed of amorphous silicon (hereinafter, referred to as an amorphous silicon TFT) or a TFT including a channel layer formed of polycrystalline silicon (hereinafter, referred to as a polycrystalline silicon TFT). An amorphous silicon TFT may have a charge mobility of about 0.5 cm2/Vs or so, which is so low and may limit an operating speed of a display apparatus including an amorphous silicon TFT. A polycrystalline silicon TFT may be formed by a manufacturing process that includes crystallization, impurity doping, and activation processes. As a result, manufacturing processes and costs for a polycrystalline silicone TFT may be higher than those for an amorphous silicon TFT. Also, it may be difficult to ensure uniformity of a polycrystalline silicon layer in the polycrystalline silicon TFT; consequently, image quality may be reduced when the polycrystalline silicon layer is used as a channel layer of a large-size display apparatus.
In order to realize a next generation high-performance and/or high-resolution large-size display apparatus, a TFT having excellent performance is desirable. In this regard, research has been conducted on an oxide TFT using an oxide semiconductor having a high carrier mobility as a material of a channel layer. However, a conventional oxide TFT may not ensure excellent switching characteristics (e.g., ON/OFF characteristics) and high reliability. Accordingly, there is a demand for a transistor (TFT) having excellent switching characteristics and high reliability as well as having a high mobility.
Example embodiments relate to semiconductor materials (e.g., semiconductor thin films).
Example embodiments relate to transistors using the semiconductor materials as channel materials.
Example embodiments relate to transistors having a high mobility and excellent switching characteristics.
Example embodiments relate to transistors having a low subthreshold swing value.
Example embodiments relate to transistors having a low OFF current level.
Example embodiments relate to electronic devices (e.g., display apparatuses) including transistors according to example embodiments.
Additional aspects will be set forth in part in the description that follows and, in part, will be apparent from the description, or may be learned by practice of example embodiments.
According to example embodiments, a compound semiconductor includes: zinc (Zn), nitrogen (N), and fluorine (F).
In example embodiments, the compound semiconductor may further include oxygen (O). The compound semiconductor may include zinc oxynitride (ZnON) containing fluorine (F).
In example embodiments, a composition ratio of fluorine (F) with respect to materials except for zinc (Zn) in the compound semiconductor is 3 at % or more.
In example embodiments, the compound semiconductor may include zinc fluoronitride (ZnFN).
In example embodiments, the compound semiconductor may include an amorphous phase.
In example embodiment, the compound semiconductor may include a nanocrystalline phase.
In example embodiments, the compound semiconductor may further include at least one of a Group I element, a Group II element, a Group III element, a Group IV element, a Group V element, and a Lanthanide (Ln) element. The Lanthanide element may be selected from the group consisting of La, Ce, Pr, Nd, Pm, Sm, Eu, Gd, Tb, Dy, Ho, Er, Tm, Yb, and Lu.
According to example embodiments, a thin film transistor (TFT) may include: a gate electrode; a channel corresponding (e.g., adjacent to) to the gate electrode; a gate insulating layer between the gate electrode and the channel; and a source and a drain respectively contacting two portions of the channel. The compound semiconductor may include zinc (Zn), nitrogen (N), and fluorine (F). The gate insulating layer may contact the gate electrode and the channel.
In example embodiments, the compound semiconductor of the TFT may further include oxygen (O). The compound semiconductor may include zinc oxynitride (ZnON) containing fluorine (F).
In example embodiments, a composition ratio of fluorine (F) with respect to materials except for zinc (Zn) in the compound semiconductor of the TFT is about 3 at % or more.
In example embodiments, the compound semiconductor of the TFT may include zinc fluoronitride (ZnFN).
In example embodiments, the compound semiconductor may include an amorphous phase.
In example embodiment, the compound semiconductor may include a nanocrystalline phase.
In example embodiments, the gate electrode may be on a substrate, the gate insulating layer may be on the gate electrode, and the channel may be on a region of the gate insulating layer corresponding to the gate electrode. In this case, the transistor may have a bottom-gate structure.
In example embodiments, the source and drain electrodes may be on the substrate, the channel may be on the substrate between the source and drain electrodes, the gate insulating layer is on the channel, and the gate electrode may be on a region of the gate insulating layer corresponding to the channel. In this case, the transistor may have a top-gate structure.
According to example embodiments, a semiconductor material includes: zinc (Zn), fluorine (F), oxygen (O), and nitrogen (N).
In example embodiments, the semiconductor material may include zinc fluorooxynitride.
In example embodiments, the semiconductor material may include zinc oxynitride containing fluorine.
In example embodiments, the semiconductor material may include a compound semiconductor.
In example embodiments, the semiconductor material may be a quaternary compound.
In example embodiments, a content ratio of fluorine to a sum of nitrogen, oxygen, and fluorine [(100×F/(N+O+F)] in the semiconductor material may be equal to or greater than about 3 at %.
In example embodiments, a content ratio of fluorine to a sum of nitrogen, oxygen, and fluorine [(100×F/(N+O+F)] in the semiconductor material may be equal to or greater than about 5 at %.
In example embodiments, a content ratio of fluorine to the sum of nitrogen, oxygen, and fluorine [(100×F/(N+O+F)] in the semiconductor material may range from about 5 at % to about 35 at %.
In example embodiments, a content ratio of nitrogen to a sum of nitrogen, oxygen, and fluorine [(100×N/(N+0+F)] in the semiconductor material may be equal to or greater than about 50 at %.
In example embodiments, a content ratio of nitrogen to a sum of nitrogen, oxygen, and fluorine [(100×N/(N+0+F)] in the semiconductor material may be equal to or greater than about 60 at %.
In example embodiments, the content ratio of nitrogen to the sum of nitrogen, oxygen, and fluorine [(100×N/(N+0+F)] in the semiconductor material may range from about 60 at % to about 90 at %.
In example embodiments, a content ratio of oxygen to a sum of nitrogen, oxygen, and fluorine [(100×O/(N+O+F)] in the semiconductor material may be equal to or smaller than about 40 at %.
In example embodiments, a content ratio of oxygen to a sum of nitrogen, oxygen, and fluorine [(100×O/(N+O+F)] in the semiconductor material may be equal to or smaller than about 30 at %.
In example embodiments, the content ratio of oxygen to the sum of nitrogen, oxygen, and fluorine [(100×O/(N+O+F)] in the semiconductor material may range from about 5 at % to about 30 at %.
In example embodiments, a Hall mobility of the semiconductor material may be equal to or greater than about 10 cm2/Vs.
In example embodiments, the semiconductor material may have a Hall mobility of equal to or greater than about 20 cm2/Vs.
In example embodiments, the semiconductor material may include an amorphous phase.
In example embodiments, the semiconductor material may include a nanocrystalline phase.
In example embodiments, the semiconductor material may further include at least one of a Group I element, a Group II element, a Group III element, a Group IV element, a Group V element, a transition metal element, and a Lanthanide (Ln) element.
In example embodiments, the semiconductor material may further include at least one of lithium (Li), potassium (K), magnesium (Mg), calcium (Ca), strontium (Sr), barium (Ba), gallium (Ga), aluminum (Al), indium (In), boron (B), silicon (Si), tin (Sn), germanium (Ge), antimony (Sb), yttrium (Y), titanium (Ti), zirconium (Zr), vanadium (V), niobium (Nb), tantalum (Ta), scandium (Sc), hafnium (Hf), molybdenum (Mo), manganese (Mn), iron (Fe), cobalt (Co), nickel (Ni), copper (Cu), tungsten (W), lanthanum (La), cerium (Ce), praseodymium (Pr), neodymium (Nd), promethium (Pm), samarium (Sm), europium (Eu), gadolinium (Gd), terbium (Tb), dysprosium (Dy), holmium (Ho), erbium (Er), thulium (Tm), ytterbium (Yb), and lutetium (Lu).
In example embodiments, the semiconductor material may include a compound composed of zinc (Zn), fluorine (F), oxygen (O), and nitrogen (N).
According to example embodiments, a semiconductor material includes zinc (Zn), nitrogen (N), and fluorine (F).
In example embodiments, the semiconductor material may include zinc fluoronitride (ZnFN).
In example embodiments, the semiconductor material may include a compound semiconductor.
In example embodiments, a content ratio of fluorine to a sum of nitrogen and fluorine [(100×F/(N+F)] in the semiconductor material may be equal to or greater than about 3 at %.
In example embodiments, a content ratio of fluorine to a sum of nitrogen and fluorine [(100×F/(N+F)] in the semiconductor material may be equal to or greater than about 5 at %.
In example embodiments, a content ratio of fluorine to the sum of nitrogen and fluorine [(100×F/(N+F)] in the semiconductor material may range from about 5 at % to about 45 at %.
In example embodiments, a content ratio of nitrogen to a sum of nitrogen and fluorine [(100×N/(N+F)] in the semiconductor material may be equal to or greater than about 55 at %.
In example embodiments, a content ratio of nitrogen to a sum of nitrogen and fluorine [(100×N/(N+F)] in the semiconductor material may be equal to or greater than about 65 at %.
In example embodiments, the content ratio of nitrogen to the sum of nitrogen and fluorine [(100×N/(N+F)] in the semiconductor material may range from about 65 at % to about 95 at %.
In example embodiments, a Hall mobility of the semiconductor material may be equal to or greater than about 10 cm2/Vs.
In example embodiments, the semiconductor material may have a Hall mobility equal to or greater than about 20 cm2/Vs.
In example embodiments, the semiconductor material may include an amorphous phase.
In example embodiments, the semiconductor material may include a nanocrystalline phase.
In example embodiments, the semiconductor material may further include at least one of a Group I element, a Group II element, a Group III element, a Group IV element, a Group V element, a transition metal element, and a lanthanide (Ln) element.
In example embodiments, the semiconductor material may further include at least one of lithium (Li), potassium (K), magnesium (Mg), calcium (Ca), strontium (Sr), barium (Ba), gallium (Ga), aluminum (Al), indium (In), boron (B), silicon (Si), tin (Sn), germanium (Ge), antimony (Sb), yttrium (Y), titanium (Ti), zirconium (Zr), vanadium (V), niobium (Nb), tantalum (Ta), scandium (Sc), hafnium (Hf), molybdenum (Mo), manganese (Mn), iron (Fe), cobalt (Co), nickel (Ni), copper (Cu), tungsten (W), lanthanum (La), cerium (Ce), praseodymium (Pr), neodymium (Nd), promethium (Pm), samarium (Sm), europium (Eu), gadolinium (Gd), terbium (Tb), dysprosium (Dy), holmium (Ho), erbium (Er), thulium (Tm), ytterbium (Yb), and lutetium (Lu).
In example embodiments, the semiconductor material may include a compound composed of zinc (Zn), fluorine (F), and nitrogen (N).
According to example embodiments, a thin film transistor (TFT) includes: a channel element; a gate electrode corresponding (e.g., adjacent) to the channel element; a gate insulating layer that is between the channel element and the gate electrode; and a source and a drain that respectively contact first and second regions of the channel element. The semiconductor material may include zinc (Zn), fluorine (F), oxygen (O), and nitrogen (N). The gate insulating layer may contact the gate electrode and the channel.
In example embodiments, the semiconductor material of the channel element may include zinc fluorooxynitride.
In example embodiments, the semiconductor material of the channel element may include zinc oxynitride containing fluorine.
In example embodiments, the semiconductor material of the channel element may include a compound semiconductor.
In example embodiments, the semiconductor material of the channel element may be a quaternary compound.
In example embodiments, a content ratio of fluorine to a sum of nitrogen, oxygen, and fluorine in the semiconductor material of the channel element may be equal to or greater than about 3 at %.
In example embodiments, a content ratio of fluorine to a sum of nitrogen, oxygen, and fluorine [(100×F/(N+O+F)] in the semiconductor material of the channel element may be equal to or greater than about 5 at %.
In example embodiments, a content ratio of fluorine to the sum of nitrogen, oxygen, and fluorine [(100×F/(N+O+F)] in the semiconductor material of the channel element may range from about 5 at % to about 35 at %.
In example embodiments, a content ratio of nitrogen to a sum of nitrogen, oxygen, and fluorine [(100×N/(N+O+F)] in the semiconductor material of the channel element may be equal to or greater than about 50 at %.
In example embodiments, a content ratio of nitrogen to a sum of nitrogen, oxygen, and fluorine [(100×N/(N+O+F)] in the semiconductor material of the channel element may be equal to or greater than about 60 at %.
In example embodiments, a content ratio of nitrogen to the sum of nitrogen, oxygen, and fluorine [(100×N/(N+O+F)] in the semiconductor material of the channel element may range from about 60 at % to about 90 at %.
In example embodiments, a content ratio of oxygen to a sum of nitrogen, oxygen, and fluorine in the semiconductor material of the channel element may be equal to or smaller than about 40 at %.
In example embodiments, a content ratio of oxygen to a sum of nitrogen, oxygen, and fluorine [(100×O/(N+O+F)] in the semiconductor material of the channel element may be equal to or smaller than about 30 at %.
In example embodiments, a content ratio of oxygen to the sum of nitrogen, oxygen, and fluorine [(100×O/(N+O+F)] in the semiconductor material of the channel element may range from about 5 at % to about 30 at %.
In example embodiments, a Hall mobility of the semiconductor material of the channel element may have be equal to or greater than about 10 cm2/Vs.
In example embodiments, the Hall mobility of the semiconductor material of the channel element may be equal to or greater than about 20 cm2/Vs.
In example embodiments, a field-effect mobility of the TFT may be equal to or greater than about 10 cm2/Vs.
In example embodiments, a field-effect mobility of the TFT may be equal to or greater than about 20 cm2/Vs.
In example embodiments, a subthreshold swing (S.S.) value of the TFT may be equal to or lower than about 0.95 V/dec.
In example embodiments, a subthreshold swing (S.S.) value of the TFT may be equal to or lower than about 0.75 V/dec.
In example embodiments, the channel element may be on the gate electrode.
In example embodiments, when the gate electrode is under the channel element, the TFT may further include an etch-stop layer on the channel element.
In example embodiments, the gate electrode may be on the channel element.
In example embodiments, the channel element may correspond to a first region of an active layer, the source and the drain may be on the active layer on both sides of the channel element, and the gate insulating layer and the gate electrode may be sequentially stacked on the first region of the active layer. The TFT may have a self-aligned top gate structure.
In example embodiments, the gate insulating layer may include a first layer and a second layer, the first layer may be between the gate electrode and the second layer, and the second layer may be between the first layer and the channel element. The first layer may include silicon nitride, and the second layer may include silicon oxide.
In example embodiments, a passivation layer may cover the TFT. The passivation layer may include a silicon oxide layer and a silicon nitride layer that are sequentially stacked.
In example embodiments, at least one of the gate electrode, the source electrode, and the drain electrode may have a tri-layer electrode structure.
In example embodiments, the tri-layer electrode structure may include a first layer, a second layer, and a third layer that are sequentially stacked. At least one of the first layer and the third layer may include one of titanium (Ti), molybdenum (Mo), and a combination thereof. The second layer may include one of aluminum (Al), aluminum-neodymium (AlNd), copper (Cu), and a combination thereof.
According to example embodiments, an electronic device may include the thin film transistor (TFT).
In example embodiments, the electronic device may be a display apparatus.
In example embodiments, the display apparatus may be an organic light-emitting display apparatus or a liquid crystal display apparatus.
In example embodiments, the TFT may be used as a switching device or a driving device.
According to example embodiments, a thin film transistor (TFT) includes: a channel element; a gate electrode that is disposed to correspond to the channel element; a gate insulating layer that is disposed between the channel element and the gate electrode; and a source and a drain that respectively contact first and second regions of the channel element. The semiconductor material may include zinc (Zn), nitrogen (N), and fluorine (F). The gate insulating layer may contact the gate electrode and the channel element.
In example embodiments, the semiconductor material of the channel element may include zinc fluoronitride.
In example embodiments, the semiconductor material of the channel element may include a compound semiconductor.
In example embodiments, a content ratio of fluorine to a sum of nitrogen and fluorine [(100×F/(N+F)] in the semiconductor material of the channel element may be equal to or greater than about 3 at %.
In example embodiments, a content ratio of fluorine to a sum of nitrogen and fluorine [(100×F/(N+F)] in the semiconductor material of the channel element may be equal to or greater than about 5 at %.
In example embodiments, content ratio of fluorine to the sum of nitrogen and fluorine [(100×F/(N+F)] in the semiconductor material of the channel element may range from about 5 at % to about 45 at %.
In example embodiments, a content ratio of nitrogen to a sum of nitrogen and fluorine [(100×F/(N+F)] in the semiconductor material of the channel element may be equal to or greater than about 55 at %.
In example embodiments, a content ratio of nitrogen to a sum of nitrogen and fluorine [(100×N/(N+F)] in the semiconductor material of the channel element may be equal to or greater than about 65 at %.
In example embodiments, a content ratio of nitrogen to the sum of nitrogen and fluorine [(100×N/(N+F)] in the semiconductor material of the channel element may range from about 65 at % to about 95 at %.
In example embodiments, a Hall mobility of the semiconductor material of the channel element may be equal to or greater than about 10 cm2/Vs.
In example embodiments, a Hall mobility of the semiconductor material of the channel element may be equal to or greater than about 20 cm2/Vs.
In example embodiments, a field-effect mobility of the TFT may have be equal to or greater than about 10 cm2/Vs.
In example embodiments, a field-effect mobility of the TFT may be equal to or greater than about 20 cm2/Vs.
In example embodiments, a subthreshold swing (S.S.) value of the TFT may be equal to or lower than about 0.95 V/dec.
In example embodiments, a subthreshold swing (S.S.) value of the TFT may be equal to or lower than about 0.75 V/dec.
In example embodiments, the channel element may be on the gate electrode.
In example embodiments, when the gate electrode is below the channel element, the TFT may further include an etch-stop layer on the channel element.
In example embodiments, the gate electrode may be on the channel element.
In example embodiments, the channel element may correspond to a first region of an active layer, the source and the drain may be on both ends of the channel element, and the gate insulating layer and the gate electrode may be sequentially stacked on the first region of the active layer. In example embodiments, the TFT may have a self-aligned top gate structure.
In example embodiments, the gate insulating layer may include a first layer and a second layer, the first layer may be between the gate electrode and the second layer, the second layer may be between the first layer and the channel element, the first layer may include silicon nitride, and the second layer may include silicon oxide.
In example embodiments, the TFT may further include a passivation layer that covers the TFT. The passivation layer may include a silicon oxide layer and a silicon nitride layer that are sequentially stacked.
In example embodiments, at least one of the gate electrode, the source electrode, and the drain electrode may have a tri-layer electrode structure.
In example embodiments, the tri-layer electrode structure may include a first layer, a second layer, and a third layer that are sequentially stacked. At least one of the first layer and the third layer may include one of titanium (Ti), molybdenum (Mo), and a combination thereof, and the second layer includes one of aluminum (Al), aluminum-neodymium (AlNd), copper (Cu), and a combination thereof.
According to example embodiments, an electronic device may include the thin film transistor (TFT).
In example embodiments, the electronic device may be a display apparatus.
In example embodiments, the display apparatus may be an organic light-emitting display apparatus or a liquid crystal display apparatus.
In example embodiments, the TFT may be used as a switching device or a driving device.
According to example embodiments, a semiconductor material includes: zinc (Zn), nitrogen (N), and fluorine (F), and an amount of fluorine (F) is less than an amount of nitrogen (N) in the semiconductor material.
In example embodiments, the semiconductor material may include an amorphous phase.
In example embodiments, the semiconductor material may include a nanocrystalline phase.
In example embodiments, the semiconductor material may further include oxygen.
In example embodiments, the semiconductor may include an amorphous phase and a nanocrystalline phase.
In example embodiments, the nanocrystalline phase may include at least one of zinc nitride, zinc oxide, and zinc fluoride.
In example embodiments, a content ration of fluorine to a sum of nitrogen, oxygen, and fluorine [(100×F/(N+O+F)] in the semiconductor material may range from about 3 at % to about 35 at %.
In example embodiments, a content ratio of oxygen to a sum of nitrogen, oxygen, and fluorine [(100×O/(N+O+F)] in the semiconductor material may range from about 2 at % to about 35 at %.
According to example embodiments, a thin film transistor (TFT) includes: a gate electrode; a channel element, source and drain electrodes that respectively contact first and second regions of the channel element; and a gate insulating layer between the channel element and the gate electrode. The gate insulating layer contacts the gate electrode and the source and drain electrodes.
In example embodiments, the gate electrode may be on the gate insulating layer.
In example embodiments, the gate insulating layer may be on the gate electrode.
According to example embodiments, a method of manufacturing a semiconductor material includes: co-sputtering a Zn target and a ZnF2 target onto a substrate in a process chamber; and supplying nitrogen (N2) gas into the process chamber during the co-sputtering the Zn target and the ZnF2 target.
In example embodiments, oxygen (O2) gas may be supplied into the process chamber during the co-sputtering the Zn target and the ZnF2 target, and a supply amount of the nitrogen (N2) gas may be greater than a supply amount of the oxygen (O2) gas into the process chamber during the supplying nitrogen (N2) gas and the supplying oxygen (O2) gas.
In example embodiments, (Ar) gas may be supplied into the process chamber during the co-sputtering the Zn target and the ZnF2 target.
In example embodiments, Ar) gas may be supplied into the process chamber during the co-sputtering the Zn target and the ZnF2 target, a temperature of the substrate may be maintained between 25° C. and 300° C. during the co-sputtering the Zn target and the ZnF2 target, and a pressure in the process chamber may be maintained between about 0.05 Pa to about 15 Pa during the co-sputtering the Zn target and the ZnF2 target.
In example embodiments, a power applied to the Zn target is greater than a power applied to the ZnF2 target during the co-sputtering the Zn target and the ZnF2 target.
These and/or other aspects will become apparent and more readily appreciated from the following description of non-limiting embodiments, as illustrated in the accompanying drawings in which like reference characters refer to like parts throughout the different views. The drawings are not necessarily to scale, emphasis instead being placed upon illustrating the principles of inventive concepts:
Example embodiments will now be described more fully with reference to the accompanying drawings, in which some example embodiments are shown. Example embodiments, may, however, be embodied in many different forms and should not be construed as being limited to the embodiments set forth herein; rather, these example embodiments are provided so that this disclosure will be thorough and complete, and will fully convey the scope of example embodiments of inventive concepts to those of ordinary skill in the art. In the drawings, the thicknesses of layers and regions are exaggerated for clarity. Like reference numerals in the drawings denote like elements, and thus their description may be omitted.
It will be understood that when an element is referred to as being “connected” or “coupled” to another element, it can be directly connected or coupled to the other element or intervening elements may be present. In contrast, when an element is referred to as being “directly connected” or “directly coupled” to another element, there are no intervening elements present. Other words used to describe the relationship between elements or layers should be interpreted in a like fashion (e.g., “between” versus “directly between,” “adjacent” versus “directly adjacent,” “on” versus “directly on”). As used herein, the term “and/or” includes any and all combinations of one or more of the associated listed items. Expressions such as “at least one of,” when preceding a list of elements, modify the entire list of elements and do not modify the individual elements of the list.
It will be understood that, although the terms “first”, “second”, etc. may be used herein to describe various elements, components, regions, layers and/or sections, these elements, components, regions, layers and/or sections should not be limited by these terms. These terms are only used to distinguish one element, component, region, layer or section from another element, component, region, layer or section. Thus, a first element, component, region, layer or section discussed below could be termed a second element, component, region, layer or section without departing from the teachings of example embodiments.
Spatially relative terms, such as “beneath,” “below,” “lower,” “above,” “upper” and the like, may be used herein for ease of description to describe one element or feature's relationship to another element(s) or feature(s) as illustrated in the figures. It will be understood that the spatially relative terms are intended to encompass different orientations of the device in use or operation in addition to the orientation depicted in the figures. For example, if the device in the figures is turned over, elements described as “below” or “beneath” other elements or features would then be oriented “above” the other elements or features. Thus, the term “below” can encompass both an orientation of above and below. The device may be otherwise oriented (rotated 90 degrees or at other orientations) and the spatially relative descriptors used herein interpreted accordingly.
The terminology used herein is for the purpose of describing particular embodiments only and is not intended to be limiting of example embodiments. As used herein, the singular forms “a,” “an” and “the” are intended to include the plural forms as well, unless the context clearly indicates otherwise. It will be further understood that the terms “comprises” and/or “comprising,” when used in this specification, specify the presence of stated features, integers, steps, operations, elements, and/or components, but do not preclude the presence or addition of one or more other features, integers, steps, operations, elements, components, and/or groups thereof.
Example embodiments are described herein with reference to cross-sectional illustrations that are schematic illustrations of idealized embodiments (and intermediate structures) of example embodiments. As such, variations from the shapes of the illustrations as a result, for example, of manufacturing techniques and/or tolerances, are to be expected. Thus, example embodiments should not be construed as limited to the particular shapes of regions illustrated herein but are to include deviations in shapes that result, for example, from manufacturing. For example, an implanted region illustrated as a rectangle will, typically, have rounded or curved features and/or a gradient of implant concentration at its edges rather than a binary change from implanted to non-implanted regions. Likewise, a buried region formed by implantation may result in some implantation in the region between the buried region and the surface through which the implantation takes place. Thus, the regions illustrated in the figures are schematic in nature and their shapes are not intended to illustrate the actual shape of a region of a device and are not intended to limit the scope of example embodiments.
Unless otherwise defined, all terms (including technical and scientific terms) used herein have the same meaning as commonly understood by one of ordinary skill in the art to which example embodiments belong. It will be further understood that terms, such as those defined in commonly-used dictionaries, should be interpreted as having a meaning that is consistent with their meaning in the context of the relevant art and will not be interpreted in an idealized or overly formal sense unless expressly so defined herein.
Semiconductor Material (I)
Referring to
In the semiconductor material 100, a content ratio of fluorine to the sum of nitrogen, oxygen, and fluorine, that is, [F/(N+O+F)]×100, may be equal to or greater than, for example, about 3 at % or about 5 at %. The content ratio of fluorine may range from about 3 at % to about 35 at % or from about 5 at % to about 35 at %. Alternatively, the content ratio of fluorine may range from about 3 at % to about 25 at % or from about 5 at % to about 25 at %. In the semiconductor material 100, a content ratio of nitrogen to the sum of nitrogen, oxygen, and fluorine, that is, [N/(N+O+F)]×100, may be equal to or greater than, for example, about 50 at % or about 60 at %. The content ratio of nitrogen may range from about 55 at % to about 95 at % or from about 70 at % to about 95 at %. Alternatively, the content ratio of nitrogen may range from about 60 at % to about 90 at %. In the semiconductor material 100, a content ratio of oxygen to the sum of nitrogen, oxygen, and fluorine, that is, [O/(N+O+F)]×100, may be equal to or less than, for example, about 40 at %. The content ratio of oxygen may range from about 2 at % to about 35 at % or from about 5 at % to about 30 at %.
The semiconductor material 100 may have a Hall mobility equal to or greater than about 10 cm2/Vs, or about 20 cm2/Vs, or about 30 cm2/Vs. According to a condition for forming the semiconductor material 100, the Hall mobility of the semiconductor material 100 may be increased to 100 cm2/Vs or more. For example, the Hall mobility of the semiconductor material 100 may range from about 10 cm2/Vs to about 120 cm2/Vs. A carrier density of the semiconductor material 100 may range, for example, from about 1011/cm3 to about 1018/cm3, or from about 1012/cm3 to about 1017/cm3. Since a conductivity type of the semiconductor material 100 may be an n-type, the term “carrier density” may refer to a concentration of electrons, and may be represented with a negative (−) sign. For convenience, herein, the carrier density (electron concentration) is expressed in a positive (+) value (without a negative sign). Meanwhile, a resistivity p of the semiconductor material 100 may range, for example, from about 0.01 Ωcm to about 106 Ωcm, or from about 0.01 Ωcm to about 105 Ωcm. Properties of the semiconductor material 100 may vary according to the forming condition and a composition ratio.
The semiconductor material 100 may include an amorphous phase. The semiconductor material 100 may partially or entirely have an amorphous phase. Also, the semiconductor material 100 may include a nanocrystalline phase. The semiconductor material 100 may have both an amorphous phase and a nanocrystalline phase. For example, the semiconductor material 100 may have a plurality of nanocrystals (nanocrystalline phase) in an amorphous matrix. The amorphous matrix may include zinc fluorooxynitride. The nanocrystals (nanocrystalline phase) may include, for example, zinc nitride. A size (diameter) of the nanocrystals (nanocrystalline phase) may range, for example, from about several nm to tens of nm. For example, a size (diameter) of the nanocrystals may range from about 1 to about 900 nm, from about 3 to 900 nm, and/or from about 5 to 850 nm.
The semiconductor material 100 may basically include zinc fluorooxynitride, and may further include at least one of zinc nitride, zinc oxide, and zinc fluoride. The zinc fluorooxynitride may be amorphous, and the zinc nitride, the zinc oxide, and the zinc fluoride may be crystalline. Also, the semiconductor material 100 may further include at least one of zinc oxynitride, zinc fluoronitride, and zinc fluorooxide. The zinc oxynitride, the zinc fluoronitride, and the zinc fluorooxide may be amorphous.
Additionally, the semiconductor material 100 may further include one or more other elements in addition to zinc, fluorine, oxygen, and nitrogen. For example, the semiconductor material 100 may further include at least one of a group I element, a Group II element, a Group III element, a Group IV element, a Group V element, a transition metal element, and a Lanthanide (Ln) element. For example, the semiconductor material 100 may further include at least one of a Group I element such as lithium (Li) or potassium (K), a group II element such as magnesium (Mg), calcium (Ca), strontium (Sr), or barium (Ba), a Group III element such as gallium (Ga), aluminum (Al), indium (In), or boron (B), a Group IV element such as silicon (Si), tin (Sn), or germanium (Ge), a Group V element such as antimony (Sb), a transition metal element such as yttrium (Y), titanium (Ti), zirconium (Zr), vanadium (V), niobium (Nb), tantalum (Ta), scandium (Sc), hafnium (Hf), molybdenum (Mo), manganese (Mn), iron (Fe), cobalt (Co), nickel (Ni), copper (Cu), or tungsten (W), and a Lanthanide element such as lanthanum (La), cerium (Ce), praseodymium (Pr), neodymium (Nd), promethium (Pm), samarium (Sm), europium (Eu), gadolinium (Gd), terbium (Tb), dysprosium (Dy), holmium (Ho), erbium (Er), thulium (Tm), ytterbium (Yb), or lutetium (Lu). Such an additional element may be doped in the semiconductor material 100. Alternatively, the additional element may constitute a compound along with basic elements of the semiconductor material 100.
Since a conductivity type of the semiconductor material 100 may be an n-type, the content ratio of the one or more elements (in addition to Zn, F, O, and N) may be controlled so as to not alter the semiconductor material 100 from being an n-type conductivity. In other words, according to example embodiments, even if the semiconductor material 100 includes one more elements (in addition to Zn, F, O, and N), a content ratio of the one or more elements may be relatively low. For example, if Li, K, or Cu are added as a dopant to the semiconductor material 100, a content ratio of the Li, K, or Cu may be less than 3 at % with respect to entire cations including Zn in the semiconductor material 100.
Although not shown in
The term “compound semiconductor” used herein refers to a compound having semiconductor characteristics formed by combining two or more types of elements at a desired (and/or alternatively predetermined) composition ratio, unlike a silicon or germanium semiconductor composed of a single element. A compound semiconductor may have properties different from those of each of constituent elements thereof. In the above description, zinc fluorooxynitride, zinc nitride, zinc oxide, zinc fluoride, zinc oxynitride, zinc fluoronitride, and zinc fluorooxide may each be a compound formed by combining a zinc component and a component such as oxygen, nitrogen, or fluorine at a desired (and/or alternatively predetermined) composition ratio or a material including such a compound. Each compound may have relatively uniform characteristics, and may have properties different from those of each of constituent elements thereof. The above materials may be compound semiconductor materials or semiconductor materials including compounds. Also, the semiconductor material 100 of
A method of forming the semiconductor material 100 will now be explained.
The semiconductor material 100 may be formed by using, for example, physical vapor deposition (PVD) such as sputtering. The PVD process may be performed in a process chamber. The sputtering may be reactive sputtering. Also, the sputtering may be co-sputtering using a plurality of targets. When the semiconductor material 100 is formed by using co-sputtering, a Zn target and a ZnF2 target may be used. In this case, a nitrogen (N2) gas or an oxygen (O2) gas may be used as a reactive gas, and additionally, an argon (Ar) gas may be further used. The nitrogen gas may be a source of nitrogen, and the oxygen gas may be a source of oxygen. The argon gas may act as a carrier gas. Also, the argon gas may improve deposition efficiency by generating plasma. A flow rate of the nitrogen gas may range from about 20 sccm to about 200 sccm, and a flow rate of the oxygen gas may range from about 1 sccm to about 15 sccm. A flow rate of the argon gas may range from about 1 sccm to about 100 sccm. A supply amount of the nitrogen gas may be greater than a supply amount of the oxygen gas. For example, a supply amount of the nitrogen gas may be 10 times or more greater, or 50 times or more greater than a supply amount of the oxygen gas. Since a reactivity of oxygen to zinc is higher than that of nitrogen to zinc, the semiconductor material 100 that is nitrogen-rich may be obtained by supplying the nitrogen gas more than the oxygen gas. Also, a supply amount of the nitrogen gas may be greater than a supply amount of the argon gas. The sputtering may be performed at a room temperature or a relatively low temperature (for example, 25 to 300° C.). In other words, when the semiconductor material 100 is formed by using the sputtering, a temperature of a substrate may be maintained at a room temperature or a relatively low temperature (for example, 25 to 300° C.). A pressure of a reaction chamber may range from about 0.05 Pa to about 15 Pa. Sputtering power for the Zn target may range from about tens to thousands of W (watt), and sputtering power for the ZnF2 target may range from about several to thousands of W. A fluorine content of the semiconductor material 100 may be adjusted by adjusting the sputtering power for the ZnF2 target. As the sputtering power for the ZnF2 target increases, the fluorine content of the semiconductor material 100 may increase. However, the aforesaid detailed process conditions are non-limiting examples, and may vary according to a sputtering system.
When a single ZnF2 target is used without the Zn target, since it is difficult to break bonding between zinc and fluorine in the single ZnF2 target, it may not be easy for zinc to combine with nitrogen and oxygen. In example embodiments, since the Zn target as well as the ZnF2 target is used, zinc separated from the Zn target may easily combine with nitrogen and oxygen.
The aforesaid method of forming the semiconductor material 100 is a non-limiting example, and may be changed in various ways. For example, the semiconductor material 100 may be formed by using, for example, metal organic chemical vapor deposition (MOCVD). Alternatively, the semiconductor material 100 may be formed by using chemical vapor deposition (CVD), atomic layer deposition (ALD), or evaporation.
Semiconductor Material (II)
Referring to
In the semiconductor material 100′, a content ratio of fluorine to the sum of nitrogen and fluorine, that is, [F/(N+F)]×100, may be equal to or greater than, for example, about 3 at % or about 5 at %. The content ratio of fluorine may range from about 3 at % to about 45 at % or from about 5 at % to about 45 at %. Alternatively, the content ratio of fluorine may range from about 3 at % to about 40 at % or from about 5 at % to about 40 at %. In the semiconductor material 100′, a content ratio of nitrogen to the sum of nitrogen and fluorine, that is, [N/(N+F)]×100, may be equal to or greater than, for example, about 55 at % or about 65 at %. The content ratio of nitrogen may range from about 55 at % to about 95 at % or from about 65 at % to about 95 at %. A Hall mobility and a carrier density of the semiconductor material 100′ may be similar to or higher than those of the semiconductor material 100 of
The semiconductor material 100′ may have an amorphous phase and/or a nanocrystalline phase. The semiconductor material 100′ may entirely have an amorphous phase, or may have both an amorphous phase and a nanocrystalline phase. In the latter case, the semiconductor material 100′ may have a plurality of nanocrystals (nanocrystalline phase) in an amorphous matrix. The nanocrystals (nanocrystalline phase) may be, for example, zinc nitride. The nanocrystals (nanocrystalline phase) may also be zinc fluoride. The amorphous phase may be zinc fluoronitride.
Also, the semiconductor material 100′ may basically include zinc fluoronitride, and may further include at least one of zinc nitride and zinc fluoride. The zinc fluoronitride, the zinc nitride, and the zinc fluoride may each be a “compound” or a “material including a compound”. In this regard, the above materials may be compound semiconductor materials or semiconductor materials including compounds, and the semiconductor material 100′ of
Additionally, the semiconductor material 100′ may further include one or more other elements in addition to zinc, fluorine, and nitrogen. For example, the semiconductor material 100′ may further include at least one of a group I element, a group II element, a group III element, a group IV element, a group V element, a transition metal element, and a lanthanum (Ln)-based element, like the semiconductor material 100 of
Since a conductivity type of the semiconductor material 100′ may be an n-type, the content ratio of the one or more elements (in addition to Zn, F, and N) may be controlled so as to not alter the semiconductor material 100′ from being an n-type conductivity. In other words, according to example embodiments, even if the semiconductor material 100′ includes one more elements (in addition to Zn, F, and N), a content ratio of the one or more elements may be relatively low. For example, if Li, K, or Cu are added as a dopant to the semiconductor material 100′, a content ratio of the Li, K, or Cu may be less than 3 at % with respect to entire cations including Zn in the semiconductor material 100′.
A method of forming the semiconductor material 100′ of
Transistor (I)
Referring to
The channel layer C10 may be disposed on the gate insulating layer GI10. The channel layer C10 may be disposed over the gate electrode G10 to face the gate electrode G10. A width of the channel layer C10 in an X-axis direction may be greater than a width of the gate electrode G10 in the X-axis direction. However, in some cases, a width of the channel layer C10 may be similar to or less than a width of the gate electrode G10. A material of the channel layer C10 may be the same as the semiconductor material 100 of
An etch-stop layer ES10 may be disposed on the channel layer C10. A width of the etch-stop layer ES10 in the X-axis direction may be less than that of the channel layer C10. Both ends of the channel layer C10 may not be covered by the etch-stop layer ES10. The etch-stop layer ES10 may include, for example, silicon oxide, silicon oxynitride, silicon nitride, or an organic insulating material.
A source electrode S10 and a drain electrode D10 respectively contacting first and second regions (for example, both ends) of the channel layer C10 may be disposed on the gate insulating layer GI10. The source electrode 510 and the drain electrode D10 may each have a single-layer structure or a multi-layer structure. Materials of the source electrode 510 and the drain electrode D10 may be the same as or similar to that of the gate electrode G10. The source electrode S10 and the drain electrode D10 may each be formed of the same material as the gate electrode G10, or a different material than the gate electrode G10. For example, each of the source electrode 510 and/or the drain electrode D10 may be formed of a metal such as Ti, Pt, Ru, Au, Ag, Mo, Al, W, Cu, Nd, Cr, Ta, or an alloy including the metal, or a conductive oxide such as IZO, AZO, ITO, GZO, or ZTO, or a compound including the conductive oxide. The source electrode S10 may have a structure that contacts the first region (for example, one end) of the channel layer C10 and extends over one end of the etch-stop layer ES10, and the drain electrode D10 may have a structure that contacts the second region (for example, the other end) of the channel layer C10 and extends over the other end of the etch-stop layer ES10. The etch-stop layer ES10 may limit (and/or prevent) the channel layer C10 from being damaged during an etching process for forming the source electrode S10 and the drain electrode D10.
A passivation layer P10 that covers the etch-stop layer ES10, the source electrode S10, and the drain electrode D10 may be disposed on the gate insulating layer GI10. The passivation layer P10 may be a silicon oxide layer, a silicon oxynitride layer, a silicon nitride layer, or an organic layer, or may have a structure in which at least two of the silicon oxide layer, the silicon oxynitride layer, the silicon nitride layer, and the organic layer are stacked. For example, the passivation layer P10 may have a single-layer structure formed of silicon oxide or silicon nitride, or a multi-layer structure including a silicon oxide layer and a silicon nitride layer that is disposed on the silicon oxide layer. Also, the passivation layer P10 may have a multi-layer structure including three or more layers. In this case, the passivation layer P10 may include a silicon oxide layer, a silicon oxynitride layer, and a silicon nitride layer that are sequentially stacked. Thicknesses of the gate electrode G10, the gate insulating layer GI10, the source electrode and drain electrodes S10 and D10, and the passivation layer P10 may respectively range from about 50 to about 300 nm, from about 50 to about 400 nm, from about 10 to about 200 nm, and from about 50 to about 1200 nm. However, thickness ranges may be changed in some cases.
Whether to use the etch-stop layer ES10 may be determined according to a material of the channel layer C10 and materials of the source electrode S10 and the drain electrode D10. Alternatively, whether to use the etch-stop layer ES10 may be determined according to an etching process for forming the source electrode S10 and the drain electrode D10. Accordingly, in some cases, the etch-stop layer ES10 may be omitted from the TFT of
Referring to
A field-effect mobility of each of the TFTs of
Analysis/Evaluation (I)
Referring to
When power for the ZnF2 target (ZnF2 power) is 15 W, a Hall mobility p, a carrier density n, and a resistivity ρ of the manufactured semiconductor film are respectively 81.0 cm2/Vs, 8.80×1017/cm3, and 0.08759 Ωcm. When power for the ZnF2 target (ZnF2 power) is 30 W, a Hall mobility μ, a carrier density n, and a resistivity ρ of the manufactured semiconductor film are respectively 60.3 cm2/Vs, 3.15×1016/cm3, and 3.281 Ωcm. When power for the ZnF2 target (ZnF2 power) is 0 W, a Hall mobility μ, a carrier density n, and a resistivity ρ of the manufactured semiconductor film are respectively 78.7 cm2/Vs, 2.15×1018/cm3, and 0.03693 Ωcm. When power for the ZnF2 target (ZnF2 power) is 0 W (comparative example), the manufactured semiconductor film may be a “zinc oxynitride (ZnOxNy)” thin film not including fluorine. Based on these measurement results, a variation in a Hall mobility, a carrier density, or the like of a semiconductor film according to ZnF2 power may be estimated.
Referring to
Referring to
Table 1 shows a field-effect mobility (cm2/Vs) and a subthreshold swing (S.S.) value (V/dec) of each of the TFTs of
Meanwhile, as a content ratio of fluorine of a channel layer increases as shown from
Referring to
A TFT using an existing semiconductor film, for example, a ZnOxNy thin film, has a relatively high mobility but has a problem of a high subthreshold swing (S.S.) value. For example, when a ratio of oxygen to nitrogen is increased in order to control a threshold voltage, a carrier density is reduced but a subthreshold swing (S.S.) value is increased. Accordingly, it may be difficult to ensure a high mobility and excellent ON/OFF switching characteristics by using an existing semiconductor film.
Analysis/Evaluation (II)
Referring to
When power for the ZnF2 target (ZnF2 power) is 15 W, a Hall mobility p, a carrier density n, and a resistivity ρ of the manufactured semiconductor film are respectively 103.0 cm2/Vs, 1.39×1018/cm3, and 0.04361 Ωcm. When power for the ZnF2 target (ZnF2 power) is 30 W, a Hall mobility μ, a carrier density n, and a resistivity ρ of the manufactured semiconductor film are respectively 86.8 cm2/Vs, 2.61×1017/cm3, and 0.2752 Ωcm. When power for the ZnF2 target (ZnF2 power) is 45 W, a Hall mobility μ, a carrier density n, and a resistivity ρ of the manufactured semiconductor film are respectively 69.1 cm2/Vs, 2.37×1016/cm3, and 3.808 Ωcm. When power for the ZnF2 target (ZnF2 power) is 0 W, a Hall mobility ρ, a carrier density n, and a resistivity ρ of the manufactured semiconductor film are respectively 105.0 cm2/Vs, 4.06×1018/cm3, and 0.01458 Ωcm. Comparing these results with the results for the thin films of
The result of
Referring to
Table 2 shows a field-effect mobility (cm2/Vs) and a subthreshold swing (S.S.) value (V/dec) of each of the TFTs of
Meanwhile, as a content ratio of fluorine of a channel layer increases as shown from
Referring to
As a content ratio of fluorine of a semiconductor film (e.g., channel layer) increases, a field-effect mobility of a TFT increases to some extent and then decreases. That is, as power for a ZnF2 target increased from 0 W to 30 W, a field-effect mobility increased to a value equal to or greater than 110 cm2/Vs and decreased thereafter in which the power increased from 30 W to 75 W. Also, an average mobility value is higher than that of
Analysis/Evaluation (III)
Referring to
Table 3 shows a field-effect mobility (cm2/Vs) and a subthreshold swing (S.S.) value (V/dec) of the TFTs of
Meanwhile, a threshold voltage of a TFT corresponding to
Analysis/Evaluation (IV)
Referring to
Transistor (II)
A configuration and modifications of a TFT according to example embodiments will now be explained in detail. That is, detailed structures and modifications of elements of TFTs of
Referring to
When the multi-layer electrode ME10 configured as described with reference to
A detailed structure (multi-layer structure) which may be used for the gate insulating layer GI10 of
Referring to
The structure of the gate insulating layer GI11 of
The passivation layer P10 of
Referring to
Referring to
Although
Transistor (III)
Referring to
A stacked structure SS20 in which a gate insulating layer GI20 and a gate electrode G20 are sequentially stacked may be disposed on the channel region C20 of the active layer A20. A source region S20 and a drain region D20 may be disposed in the active layer A20 on both sides of the stacked structure SS20. The source region S20 and the drain region D20 may each have an electrical conductivity higher than that of the channel region C20. The source region S20 and the drain region D20 may be conductive regions. The source region S20 and the drain region D20 may be regions that are treated (processed) with plasma. For example, the source region S20 and the drain region D20 may be regions treated (processed) with plasma including hydrogen (H). When the active layer A20 on both sides of the stacked structure SS20 is treated (processed) by using plasma of a gas including hydrogen (H), the source region S20 and the drain region D20 having conductive property may be formed. In this case, the gas including the hydrogen (H) may be NH3, H2, or the like. When both end portions of the active layer A20 are treated (processed) by using the plasma of the gas including the hydrogen (H), the hydrogen may act as a carrier by entering the active layer A20. Also, the plasma of the hydrogen may remove an anion (oxygen or the like) of the active layer A20, and thus, an electrical conductivity of a plasma-treated region may be increased. Thus, the source region S20 and the drain region D20 may each include a region whose anion (oxygen or the like) concentration is relatively low. In other words, the source region S20 and the drain region D20 may each include a region whose cation concentration is relatively high, for example, a zinc-rich region.
An interlayer insulating layer ILD20 that covers the gate electrode G20, and the source region S20 and the drain region D20 may be disposed on the substrate SUB20. First and second electrodes E21 and E22 that are electrically connected to the source region S20 and the drain region D20 may be disposed on the interlayer insulating layer ILD20. The source region S20 and the first electrode E21 may be connected to each other through a conductive plug PG21, and the drain region D20 and the second electrode E22 may be connected to each other through a second conductive plug PG22. The first and second electrodes E21 and E22 may be respectively referred to as a source electrode and a drain electrode. Alternatively, the source region S20 and the drain region D20 may be referred to as a source electrode and a drain electrode. A passivation layer (not shown) that covers the first and second electrodes E21 and E22 may be further disposed on the interlayer insulating layer ILD20.
Although not shown in
The TFT of
Referring to
Referring to
A gate insulating layer GI30 that covers the channel layer C30, and the source electrode S30 and the drain electrode D30 may be disposed on the substrate SUB30. A gate electrode G30 may be disposed on the gate insulating layer GI30. The gate electrode G30 may be disposed over the channel layer C30. A passivation layer P30 that covers the gate electrode G30 may be disposed on the gate insulating layer GI30.
Materials and thicknesses of the substrate SUB30, the source electrode S30, the drain electrode D30, the channel layer C30, the gate insulating layer GI30, the gate electrode G30, and the passivation layer P30 of
Method of Manufacturing Transistor
Methods of manufacturing TFTs including semiconductor materials according to example embodiments will now be explained.
Referring to
Referring to
The channel semiconductor layer C100 may be deposited by using PVD such as sputtering. The sputtering may be reactive sputtering. Also, the sputtering may be co-sputtering using a plurality of targets. The sputtering may be performed in a process chamber. When the channel semiconductor layer C100 is formed by using co-sputtering, a Zn target and a ZnF2 target may be used. In this case, a nitrogen (N2) gas or an oxygen (O2) gas may be used as a reactive gas, and additionally, an argon (Ar) gas may be further used. The nitrogen gas may be a source of nitrogen, and the argon gas may be a source of oxygen. The argon gas may act as a carrier gas. Also, the argon gas may improve deposition efficiency by generating plasma. A flow rate of the nitrogen gas may range from about 20 sccm to about 200 sccm, and a flow rate of the oxygen gas may range from about 1 sccm to about 15 sccm. A flow rate of the argon gas may range from about 1 sccm to about 100 sccm. A supply amount of the nitrogen gas may be greater than a supply amount of the oxygen gas. For example, a supply amount of the nitrogen gas may be 10 times more greater, or 50 times or more greater than a supply amount of the oxygen gas. Since a reactivity of oxygen to zinc is higher than that of nitrogen to zinc, the channel semiconductor layer C100 that is nitrogen-rich may be obtained by supplying the nitrogen gas more than the oxygen gas. Also, a supply amount of the nitrogen gas may be greater than a supply amount of the argon gas. The sputtering may be performed at room temperature or a relatively low temperature (for example, 25 to 300° C.). In other words, when the channel semiconductor layer C100 is formed by using the sputtering, a temperature of a substrate may be maintained at room temperature or a relatively low temperature (for example, 25 to 300° C.). A pressure of a reaction chamber may range from about 0.05 Pa to about 15 Pa. Sputtering power for the Zn target may range from about tens to thousands of W, and sputtering power for the ZnF2 target may range from about several to thousands of W. A content ratio of fluorine (F) of the channel semiconductor layer C100 may be adjusted by adjusting the sputtering power for the ZnF2 target. As the sputtering power for the ZnF2 target increases, a content ratio of fluorine of the channel semiconductor layer C100 may increase. Also, when the oxygen (O2) gas is not used in the method of forming the channel semiconductor layer C100, that is, when a flow rate of the oxygen (O2) gas is 0 sccm, the channel semiconductor layer C100 formed of zinc, fluorine, and nitrogen may be formed.
The detailed process conditions may be a non-limiting example, and may vary according to a sputtering system. Also, the method of forming the channel semiconductor layer C100 may be changed in various ways. For example, the channel semiconductor layer C100 may be formed by using a method other than the sputtering, for example, MOCVD. Alternatively, the channel semiconductor layer C100 may be formed by using another method such as CVD, ALD, or evaporation.
Referring to
Referring to
Referring to
Referring to
Referring to
The method of
Referring to
Referring to
Referring to
Referring to
Referring to
The method of
Electronic Device
TFTs according to example embodiments may be applied as a switching device or a driving device of a display apparatus such as an organic light-emitting display apparatus or a liquid crystal display apparatus. As described above, since the TFT has a high mobility, a low swing value, a low OFF current, and excellent switching characteristics (ON/OFF characteristics), when the TFT is applied to a display apparatus, the performance of the display apparatus may be improved. Accordingly, the TFT may be effectively used to realize a next generation high-performance/high-resolution/large-size display apparatus. Also, the TFT may be applied for various purposes to other electronic devices such as a memory device or a logic device as well as a display apparatus. For example, the TFT may be used as a transistor constituting a peripheral circuit of a memory device or a selection transistor.
While TFTs according to example embodiments having one gate electrode have been described with reference to
Referring to
The substrate SUB40 may be formed of the same materials as the substrate SUB 10 described previously with regard to
A material of the channel layer C40 may be the same as the semiconductor material 100 of
Materials of the source and drain electrodes S40 and D40 may be the same as materials of the source electrode S10 and the drain electrode D10 described previously with regard to
Referring to
Although some TFTs according to example embodiments have been described, it will be understood by one of ordinary skill in the art that elements and structures of the TFTs of
While some example embodiments have been particularly shown and described with reference to example embodiments thereof, it will be understood by one of ordinary skill in the art that various changes in form and details may be made therein without departing from the spirit and scope of the claims.
| Number | Date | Country | Kind |
|---|---|---|---|
| 10-2012-0138508 | Nov 2012 | KR | national |
| 10-2013-0097345 | Aug 2013 | KR | national |