Semiconductor pressure sensor with method diaphragm

Information

  • Patent Grant
  • 4840067
  • Patent Number
    4,840,067
  • Date Filed
    Friday, May 15, 1987
    37 years ago
  • Date Issued
    Tuesday, June 20, 1989
    35 years ago
Abstract
A semiconductor pressure sensor having a cylindrical housing with an opening formed at its tip end which is exposed to a pressure atmosphere and a metal diaphragm for receiving pressure which is formed in a wall of the cylindrical housing defining the opening. A metal oxide layer is formed in a surface of the metal diaphragm by oxidizing the surface of the metal diaphragm, and a glass layer is formed on the metal oxide layer. A semiconductor chip, on which a strain gauge is formed, is firmly and surely bonded to the metal diaphragm through the glass layer by virtue of the metal oxide layer. This semiconductor pressure sensor can measure high pressure with sufficient sensitivity and high accuracy.
Description

BACKGROUND OF THE INVENTION
1. Field of the Invention
The present invention relates to a semiconductor pressure sensor and a method for bonding a semiconductor chip to a metal diaphragm thereof, and more particularly to an accurate semiconductor pressure sensor suitable for the detection of high pressure and a bonding method therefor.
2. Description of the Prior Art
In many cases, there have been used pressure sensors, each being provided with such a pressure sensing diaphragm as to deform in response to the measured pressure. These pressure sensors sense the amount of deformation of the diaphragm by means of a strain gauge. In particular, for measuring high pressure, it is desired to use a metal diaphragm having pressure resistance. For example, Japanese examined patent publication No. Sho 58-5372 discloses a pressure sensor provided with a measuring portion composed of a metal diaphragm and a metal strain gauge bonded to the metal diaphragm. However, this metal strain gauge has a defect that the output sensitivity is low. This results in multistage amplification and noise removal being required, and accordingly the measuring circuit becomes complex.
Recently, pressure sensors, each being provided with a semiconductor strain gauge having a linear and high sensitive output have been noted. In each of these pressure detectors, a semiconductor chip itself composes a pressure receiving diaphragm (U.S. Pat. No. 3,858,150 for example). Therefore, these pressure sensors cannot be used for sensing high pressure.
For obtaining a pressure sensor durable against high pressure and having excellent output sensitivity, it has been thought of to combine the metal diaphragm with the semiconductor chip composing the semiconductor strain gauge. However, such a bonding structure to bond the semiconductor chip to the metal diaphragm with sufficient strength has not been found as yet.
SUMMARY OF THE INVENTION
Accordingly, it is an object of the present invention to provide a semiconductor pressure sensor of good performance, wherein a strain gauge semiconductor chip may be firmly and surely bonded to a metal diaphragm.
The semiconductor pressure sensor according to the present invention has a metal diaphragm for receiving pressure, a metal oxide layer formed in a surface of the metal diaphragm by oxidizing the surface of the metal diaphragm, a glass layer formed on the metal oxide layer and a semiconductor chip on which a strain gauge is formed. The semiconductor chip is firmly bonded to the glass layer.
In the semiconductor pressure sensor having the above-described structure, the semiconductor chip is firmly and surely bonded to the metal diaphragm. And this semiconductor pressure sensor can measure high pressure with sufficient sensitivity and high accuracy.





BRIEF EXPLANATION OF THE DRAWINGS
FIG. 1 is a sectional view of a main part of a semiconductor pressure sensor according to the present invention, which is an enlarged sectional view of the portion A of FIG. 2;
FIG. 2 is a sectional view of an overall semiconductor pressure detector;
FIG. 3 is a plan view of a semiconductor chip;
FIG. 4 is a wiring diagram of strain gauge elements;
FIG. 5 is a graph showing the relation between the surface roughness of a sensing body and the tensile strength;
FIG. 6 is a graph showing the relation between the thickness of an oxide layer and the tensile strength; and
FIG. 7 is a schematic block diagram of the bonding process.





DETAILED DESCRIPTION OF THE EMBODIMENTS
In FIG. 2, a housing 501 is composed of a cylindrical metal body. The upper half portion of the housing 501 has a hexagonal section and the lower half portion thereof is provided with a screw portion 501a in its outer periphery.
A sensing body 1 is inserted into the housing 501. The sensing body 1 is composed of a cylindrical body having a closed upper end and an open lower end. The peripheral edge of the open lower end is welded to the inner edge of an opening of the housing 501. The sensing body 1 is made of Fe-Ni-Co alloy having a low coefficient of thermal expansion. The central portion of the closed upper end surface of the sensing body 1 is formed into a thin-walled diaphragm 11 for receiving pressure.
A semiconductor chip 4 is bonded to the upper surface of the diaphragm 11 by a bonding structure as described later. The semiconductor chip 4 is connected to electrodes formed on a ring-shaped ceramic substrate 502 provided on the upper surface of the housing 501 so as to surround the semiconductor chip 4, by way of lead wires 503.
A ceramic substrate 504 on which an IC circuit for processing signals is formed is disposed above the semiconductor chip 4. The IC circuit is connected to the electrodes formed on the substrate 502 through pins 505 which support the substrate 504.
A cylindrical cover 506 is bonded to the outer peripheral edge of the upper surface of the housing 501, and a lead holder 507 is closely fit in an upper opening of the cover 506. A lead wire 508 extends from the substrate 504 to the outside of the sensor, penetrating the lead holder 507. In FIG. 2, reference numeral 509 denotes a seal ring, 510, 511 denote seal resins, and 512 denotes a push ring for the seal ring 509.
The semiconductor chip 4 is provided with P-type semiconductor strain gauge elements 41, 42, 43, and 44 which are formed at four points on a silicon(Si) substrate surface by doping boron(B) as shown in FIG. 3. The strain gauge elements 41 and 43 are positioned just above the center of the diaphragm 11 while strain gauge elements 42 and 44 are placed just above the peripheral portion of the diaphragm 11. These elements 41 to 44 are connected to each other through electrode leads (not shown) formed on the silicon substrate to form a full bridge as shown in FIG. 4.
The bonding structure of the semiconductor chip 4 and the sensing body 1 is shown in FIG. 1. In FIG. 1, the portion encircled by a circle A shown in FIG. 2 is enlarged.
The whole upper surface of the sensing body 1 is oxidized to form an oxide layer 2. Then, the semiconductor chip 4 is bonded on the oxide layer 2 through a low melting point glass layer 3.
The bonding strength in bonding portions of the bonding structure shown in FIG. 1 is measured by a tensile test, the results being shown in FIGS. 5 and 6. As shown in FIG. 5, when the surface-roughness of the sensing body 1 is 0.5 .mu.m to 3 .mu.m, good tensile strength higher than 150 kg/cm.sup.2 can be obtained. When the depth of the oxide layer 2 is about 1.5 .mu.m to 5.5 .mu.m, on the other hand, sufficient bonding strength higher than 150 kg/cm.sup.2 can be obtained as shown in FIG. 6.
Non-crystal low melting point glass containing lead oxide as a main ingredient is used as the glass layer 3. It is preferable to form the thickness of the glass layer 3 to 40 to 60 .mu.m (Table 1) and to form the particle diameter of a filler thereof to about 2.0 .mu.m as an average value and about 20 .mu.m as the maximum (Table 2). However, when the thickness of the glass layer 3 is larger than 60 .mu.m, both the sensitivity and strength are drastically decreased.
The thermal shock test of cooling at -40.degree. C. and heating at 120.degree. C. shown in Tables 1 and 2 is repeated 200 times per hour and a high pressure operation test of applying a pressure load of 200 kg/cm.sup.2 four time per minute is repeated one million times. In Tables 1 and 2, "0" denotes that no drift occurs in the output signals from the semiconductor chip after these tests while "X" denotes that some drift occurs in output signals from the semiconductor chip 4 after these tests.
The method for forming the above-described bonding structure is roughly shown in FIG. 7.
At first, the surface of the sensing body 1 is subjected to the acid-pickling step and the decarburization step. The acid-pickling step is performed by removing oil components from the surface of the sensing body 1, using nitrohydrochloric acid. The decarburization step is performed by supplying steam in a deoxidizing and weak deoxidizing atmosphere containing H.sub.2 and N.sub.2 at 800.degree. to 1100.degree. C. for about 1 hour (Table 3, D, F, J, K, L).
Next, the surface of the sensing body 1 is subjected to the oxidation process in an O.sub.2 (oxygen) atmosphere at 800.degree. to 850.degree. C. for 5 to 10 minutes (Table 3, D, F, J, K, L), whereby an oxide layer 2 of which the depth is 1.5 .mu.m to 5.5 .mu.m is formed.
The glass layer 3 is formed by printing a glass paste on the oxide layer 2 and calcining the printed glass paste at about 400.degree. C. The thickness of the formed glass layer 3 is preferably 40 .mu.m to 60 .mu.m. The glass paste is obtained by mixing glass powder with an organic solvent.
The semiconductor chip 4 is placed on the calcined glass layer 3 and then is sintered at about 500.degree. C., whereby the semiconductor chip 4 is firmly bonded to the sensing body 1.
In the semiconductor pressure sensor having the above-described structure, when the diaphragm 11 is deformed due to the introduced pressure, tensile stress is generated in the semiconductor chip 4 bonded to the diaphragm 11. This results in the resistance value of each of the strain gauge elements 41 and 43 on the chip 4 being drastically changed to obtain a linear output signal of high sensitivity, which corresponds to the measured pressure. Furthermore, when the inner peripheral surface of the sensing body 1 composing a pressure inlet port is subjected to the oxidation process, excellent corrosion resistance can be obtained.
As described above, according to the present invention, the diaphragm for directly receiving a high pressure is made of a metal of a high strength. Therefore, the diaphragm is durable against high pressure. Furthermore, the semiconductor chip provided with a semiconductor strain gauge is firmly bonded to the metallic diaphragm through glass under most proper conditions. This results in the highly sensitive pressure sensor being obtained. According to the present invention, the semiconductor chip is previously formed and then jointed on the metal diaphragm. Therefore, mass-producible pressure sensors can be provided.
TABLE 1______________________________________Glass Thickness of Thermal High PressureNo. Glass Layer Shock Test Operation Test______________________________________C 20 .mu.m X XC 40 .mu.m O OC 60 .mu.m O O______________________________________
TABLE 2______________________________________ Particle Thermal High PressureGlass Diameter of Filler Shock OperationNo. Average Maximum Test Test______________________________________A 5.4 .mu.m 1l0 .mu.m X XB 5.4 .mu.m 70 .mu.m X XC 2.0 .mu.m 20 .mu.m O O______________________________________
TABLE 3______________________________________Condition of Condition of BondingDecarburization Oxidization State______________________________________A -- -- Insufficient X Formation of Oxide LayerB -- 800.degree. C. .times. 10 min Generation of X Bubbles in Glass Layer (Insufficient Bonding Strength)C 1000.degree. C. .times. 1 hr -- Insufficient X Formation of Oxide LayerD 1000.degree. C. .times. 1 hr 800.degree. C. .times. 10 min Good Bonding OE 1000.degree. C. .times. 1 hr 800.degree. C. .times. 1 min Insufficient X Formation of Oxide LayerF 1000.degree. C. .times. 1 hr 800.degree. C. .times. 5 min Good Bonding OG 1000.degree. C. .times. 1 hr 800.degree. C. .times. 30 min Too thick Oxide X Layer (Insufficient Bonding Strength)H 1000.degree. C. .times. 1 hr 700.degree. C. .times. 10 min Insufficient X Formation of Oxide LayerI 1000.degree. C. .times. 1 hr 900.degree. C. .times. 10 min Too thick Oxide X LayerJ 800.degree. C. .times. 1 hr 800.degree. C. .times. 10 min Good Bonding OK 1100.degree. C. .times. 1 hr 800.degree. C. .times. 10 min Good Bonding OL 1000.degree. C. .times. 1 hr 850.degree. C. .times. 5 min Good Bonding O______________________________________
Claims
  • 1. A semiconductor pressure sensor comprising:
  • a metal diaphragm having a surface roughness of 0.5 .mu.m to 3 .mu.m and which deforms in proportion to a change in an applied pressure;
  • a metal oxide layer formed in a surface of said metal diaphragm;
  • a glass layer formed on said metal oxide layer; and
  • a semiconductor chip having a strain gauge which produces output signals responsive to the deformation of said metal diaphragm, said semiconductor chip being bonded to said glass layers.
  • 2. A semiconductor pressure sensor according to claim 1, further comprising a housing having an opening formed at its tip end, which is exposed to a pressure atmosphere, said metal diaphragm being provided in said opening so as to close said opening.
  • 3. A semiconductor pressure sensor according to claim 1, wherein said metal diaphragm is made of Fe-Ni-Co alloy and said semiconductor chip is composed of a silicon substrate.
  • 4. A semiconductor pressure sensor according to claim 1, wherein said metal oxide layer has a thickness of about 1.5 .mu.m to 5.5 .mu.m.
  • 5. A semiconductor pressure sensor comprising:
  • a metal diaphragm which deforms in proportion to a change in an applied pressure;
  • a metal oxide layer formed in a surface of said metal diaphragm;
  • a glass layer formed on said metal oxide layer, said glass layer being made of a low melting point glass having a thickness of about 40 .mu.m to 60 .mu.m, and a filler of said glass layer having an average particle diameter of about 2.0 .mu.m and a maximum particle diameter of about 20 .mu.m; and
  • a semiconductor chip having a strain gauge which produces output signals responsive to the deformation of said metal diaphragm, said semiconductor chip being bonded to said glass layer.
  • 6. A semiconductor pressure sensor according to claim 5, further comprising a housing having an opening formed at its tip end, which is exposed to a pressure atmosphere, said metal diaphragm being provided in said opening so as to close said opening.
  • 7. A semiconductor pressure sensor according to claim 5, wherein said metal diaphragm is made of Fe-Ni-Co alloy and said semiconductor chip is composed of a silicon substrate.
  • 8. A semiconductor pressure sensor according to claim 5, wherein said metal oxide layer has a thickness of about 1.5 .mu.m to 5.5 .mu.m.
Priority Claims (1)
Number Date Country Kind
61-138731 Jun 1986 JPX
US Referenced Citations (12)
Number Name Date Kind
2784593 Peucker Jul 1956
3341796 Eisele Sep 1967
3858150 Gurtler et al. Jan 1975
4293325 Chirino et al. Oct 1981
4319397 Tanabe et al. Mar 1982
4382377 Kleinschmidt et al. May 1983
4481497 Kurtz et al. Nov 1984
4525766 Petersen Jun 1985
4527428 Shimada et al. Jul 1985
4628296 Kitagawa et al. Dec 1986
4633212 Johnson Dec 1986
4712082 Ito et al. Dec 1987
Foreign Referenced Citations (2)
Number Date Country
56-43489 Oct 1981 JPX
58-5372 Jan 1983 JPX