Separation of polyvalent cations by transport through liquid membrane

Abstract

Use of succinosuccinic acid diesters of the formula ##STR1## in which R is an alkyl, alkenyl or cycloalkyl having 4 to 24 C atoms, either dissolved in a water-immiscible organic solvent, or at elevated temperature in the form of their melts, as cation-selective liquid membranes.

Description

The present invention relates to cation-selective liquid membranes consisting of succinosuccinic acid diesters dissolved in organic solvents or of their solvent-free melts, and to their use for the separation of polyvalent cations from monovalent cations or for the selective separation of different polyvalent cations from aqueous solutions.

It is known that the metal cations can be dissolved out of aqueous solutions containing metal salts, by bringing these solutions into contact with organic solvents which contain a dissolved complexing agent. Such organic solutions containing at least one complexing agent, for example phenolic oximes, and their use for obtaining metal cations from aqueous solutions, are described, for example, in U.S. Pats. Nos. 3,592,775 and 3,939,203. In these patent specifications, the two solutions are brought into contact by shaking in a separating funnel or by stirring the organic solution with the aqueous solution.

"Journal of Membrane Science", 2 (1977), pages 213-233, has furthermore disclosed the use of organic solutions which contain a complexing agent or a so-called "carrier agent", as liquid membranes for coupled ion transport. The method of operation of cation-selective liquid membranes which are used between two aqueous solutions of different pH values is described in the said "Journal of Membrane Science" on pages 214-216, using coupled Cu.sup.2+ /H.sup.+ transport as an example. According to this description, at the interface between the liquid membrane and the Cu.sup.2+ salt solution of higher pH value, the copper ion reacts with the "carrier agent", a complex being formed. The Cu complex, which is soluble only in the organic phase of the liquid membrane, is transported through the liquid membrane into the aqueous solution of lower pH value, and, at this liquid membrane/aqueous solution interface, the complexed Cu cation is released into the aqueous solution and the "carrier agent" diffuses back through the liquid membrane to the other interface, taking up 2 protons, and, at the latter interface, complexes Cu cations again.

The reactions taking place at the two interfaces of the liquid membrane can be represented by the following equation

2HR+Cu.sup.2+ .revreaction.CuR.sub.2 +2H.sup.+ in which HR is a "carrier agent". Furthermore, such liquid membranes make it possible to concentrate certain cations against their own concentration gradient in an aqueous solution of lower pH value.

The liquid membranes described in the said "Journal of Membrane Science" operate at relatively low pH values and are cation-selective with respect to Cu.sup.2+ or Fe.sup.3+ cations.

It has now been found that certain succinosuccinic acid diesters are valuable "carrier agents" for liquid membranes, which permit their use with aqueous solutions of comparatively high pH values, i.e. under milder conditions. The liquid membranes according to the invention permit a complete separation of polyvalent cations from monovalent cations and also a selective separation of different polyvalent cations.

The present invention thus relates to liquid membranes for the separation of polyvalent cations from monovalent cations, from aqueous solutions, or for the selective separation of different polyvalent cations from aqueous solutions, which consist of an essentially water-immiscible organic solvent and of an essentially water-insoluble succinosuccinic acid diester, dissolved in the said solvent, of the formula I ##STR2## in which R is an alkyl, alkenyl or cycloalkyl having up to 24 C atoms, in particular having 4 to 24 C atoms, the proportion of the succinosuccinic acid diester in the organic solvent being at least 0.01% by weight, based on the organic solvent, or of the melt of compounds of the formula I.

The liquid membranes preferably consist of a succinosuccinic acid diester of the formula I in which R is an alkyl or alkenyl having 4 to 18 C atoms, and of a water-immisible organic solvent.

In particular, the liquid membranes according to the invention consist of an aprotic non-polar solvent and dioleyl succinosuccinate.

The succinosuccinic acid diesters of the formula I are known and can be prepared, for example, by the process described in "Helvetica Chimica Acta", Volume 62, 1979, pages 1,682-1,687, by the transesterification of diethyl succinosuccinate with the corresponding Na alcoholates.

British Pat. No. 2,016,471 has furthermore disclosed the use of polymers modified by succinosuccinic acid esters for the preparation of membranes for use in processes for the separation of material, and that the modified polymers have groups which form metal chelates. By means of chelation with certain heavy metal salts, the biological degradability of these membranes can be effectively inhibited. On the other hand, the high hydrophobicity of the metal-chelated succinosuccinic acid diesters of the formula I, and the suitability of the compounds of the formula I as "carrier agents" in liquid membranes, cannot be inferred from British Patent Specification No. 2,016,471.

Because succinosuccinic acid diesters are readily soluble in organic solvents, any water-immiscible organic solvents can be used for the liquid membranes according to the invention. It is preferred to use aprotic nonpolar solvents, for example benzene, toluene and other hydrocarbons, such as n-pentane or n-hexane, and also chlorinated aliphatic or aromatic hydrocarbons, for example methylene chloride, chloroform, ethylene chloride or chlorobenzene.

The liquid membranes according to the invention can be used even with small amounts of dissolved succinosuccinic acid diesters. The proportion of the succinosuccinic acid diester dissolved in the organic solvent must be at least 0.01% by weight, based on the organic solvent, and can vary up to 100% by weight. It is also possible to use solvent-free liquid membranes by using the melt of the succinosuccinic acid diesters of the formula I and carrying out the separation process at elevated temperature, preferably just above the melting point of the succinosuccinic acid diester employed. Bis-(2-ethylhexyl) succinosuccinate (melting point: 30-33.degree. C.) or dioleyl succinosuccinate (melting point: 62.degree. C.), and also mixtures of these diesters with other succinosuccinic acid diesters of the formula I, are especially suitable for this purpose. If the separation process is carried out at elevated temperature, an acceleration of the flow of cations through the liquid membrane is generally also achieved. The liquid membranes according to the invention can be employed in the conventional manner for the cation-selective separation process, the apparatus used for carrying out the separation process depending essentially on the density of the liquid membrane. If, for example, the liquid membrane has a greater density than the aqueous solution, the separation process is advantageously carried out in a U-tube, the liquid membrane filling the lower part of the U-tube in such a way that the aqueous solutions present in the two arms of the U-tube are completely separated from one another. If the liquid membrane contains a high-boiling solvent, the separation process can also advantageously be carried out at elevated temperature. If the density of the liquid membrane is less than that of water, an inverted or doublebent U-tube is suitable for carrying out the separation process.

The liquid membranes according to the invention can also be used in the form of supported membranes. To achieve a better membrane stability, the organic solutions of the succinosuccinic acid diesters of the formula I are absorbed by, for example, a porous plastic matrix or ceramic matrix. Intercellular membranes, such as porous foam plastic sheets or glass filters with capillary interstices, or also cell filter membranes, such as those described, for example, in "Journal of the Chemical Society, Chemical Communications", No. 17/1979 (September), on pages 729 to 730, are especially suitable for this purpose.

As mentioned at the outset, the liquid membranes according to the invention are outstandingly suitable for the separation of polyvalent cations from monovalent cations and also for the selective separation of different polyvalent cations from aqueous solutions, according to the principle of coupled ion transport. In this process, the liquid membrane is used as a barrier between two aqueous solutions, so that these solutions are completely separated from one another.

The present invention thus also relates to a process for the separation of polyvalent cations from monovalent cations or for the selective separation of different polyvalent cations from aqueous solutions, according to the principle of coupled ion transport and using a liquid membrane, which comprises using the liquid membrane according to the invention between two aqueous solutions having different pH values, the aqueous solution into which the polyvalent cations are transported through the liquid membrane having a pH value of 1 to 8, and this pH value necessarily being lower than the pH value of the other aqueous solution, which contains the cations to be separated selectively.

The aqueous solution into which the polyvalent cations are transported through the liquid membrane preferably has a pH value of 1 to 5, and this value is at least one whole unit lower than the pH value of the other aqueous solution, which contains the cations to be separated selectively.

The pH value of the aqueous solution which contains the cations to be separated can be either in the acid range or in the weakly alkaline range and must be higher than the pH value of the other aqueous solution, into which the cations are transported. The pH value of the latter solution can be adjusted either with inorganic acids or with organic acids. Hydrochloric or sulphuric acid is advantageously used.

For the selective separation of different or identical polyvalent cations, it is suitable to use several liquid membranes in series. The number of such membranes in series depends on the number of cations to be separated or on the flow of these cations in the liquid membrane.

The process according to the invention is suitable, for example, for the purification of effluents from electroplating processes or for the recovery of metals from these effluents, for the concentration of metal cations from solutions of low concentration, for the extraction of valuable metals from sea water or ash, especially industrial ash, or for isotope separation.

The following examples illustrate the invention in greater detail:

EXAMPLE 1

30 ml of a 0.5 molar solution of dioleyl succinosuccinate in chloroform were filled into a U-tube. 20 ml of a 0.25 molar aqueous Cu acetate solution were then introduced into one arm of the U-tube and 20 ml of a 10% aqueous hydrochloric acid solution were introduced into the other arm. The two aqueous solutions were separated from one another by the chloroform phase present at the bottom of the U-tube. The initial pH value of the Cu acetate solution was 4.9 and that of the hydrochloric acid solution was .about.1.

After 138 days, the concentration of Cu.sup.2+ ions in the hydrochloric acid solution was 15.5.times.10.sup.-2 mols/liter. No Cl.sup.- ions could be determined in the Cu acetate solution, which indicates that Cu.sup.2+ /H.sup.+ exchange has really taken place.

The concentrations of Cu.sup.2+ ions determined, during the flow of Cu.sup.2+ ions, in the hydrochloric acid solution initially free of Cu.sup.2+ ions are given in Table 1.

TABLE 1__________________________________________________________________________Concentration of Cu.sup.2+ ions after ion transportthrough the liquid membraneDays 1.75 4.6 6 11 14 20.8 25 29 33 39 54 78 98 138__________________________________________________________________________10.sup.-2 0.025 0.44 1.1 1.4 1.73 2.4 2.83 3.05 3.05 3.4 5.1 6.53 11.5 15.5mol/literof Cu.sup.2+__________________________________________________________________________ In a blind experiment, the above example was repeated, but the chloroform phase contained no dioleyl succinosuccinate. After 116 days, the concentration of Cu.sup.2+ ions in the hydrochloric acid solution was only 7.6.times.10.sup.-4 mols/liter. The concentrations of Cu.sup.2+ ions determined in the hydrochloric acid solution are summarised in Table 2. TABLE 2______________________________________Concentration of Cu.sup.2+ ions in the hydrochloricacid solutionDays 8 12 18 33 53 63 76 116______________________________________10.sup.-5 mol/liter 2.3 2.3 2.3 9.9 17.9 25.0 36.0 76.0of Cu.sup.2+______________________________________

EXAMPLE 2

A U-tube was separated into two compartments with 30 ml of a 0.5 M solution of dioleyl succinosuccinate in chloroform. 30 ml of a 0.5 M aqueous Cu acetate solution were introduced into each of the two arms. The pH value of one of the Cu salt solutions was 5.5 (solution b) and the Cu salt solution in the other arm of the U-tube was acidfied with hydrochloric acid to pH 2 (solution a). Cu.sup.2+ ions flowed into the chloroform phase and from there into the hydrochloric acid solution of lower pH value. After 116 days, the concentration of Cu.sup.2+ ions was 1.9.times.10.sup.-2 mols/liter in solution b and 7.8.times.10.sup.-2 mols/liter in solution a. The concentrations determined in solution a and solution b are reproduced in Table 3.

TABLE 3______________________________________Cu.sup.2+ ion concentrations in solution a andsolution bDays 4 8 12 14.75 18 33 53 63 76 116______________________________________10.sup.-2 solu- 4.9 4.9 4.9 4.9 4.4 4.4 5.4 5.3 6.2 7.8 tionmol/ aliter of solu- 5.0 4.8 4.8 4.6 4.4 4.4 4.0 3.5 3.2 1.9 tionCu.sup.2+ b______________________________________

EXAMPLE 3

An aqueous solution containing a mixture of Cu acetate (concentration: 8.66.times.10.sup.-2 mols/liter), Ca acetate (concentration: 4.24.times.10.sup.-2 mols/liter) and K acetate (concentration: 16.9.times.10.sup.-2 mols/liter) was introduced into one side of a U-tube which contained the chloroform solution described in Example 1 as the liquid membrane. The initial pH value of this acetate solution was 5.75. The other side of the U-tube was filled with an aqueous hydrochloric acid solution of pH value .about.1. After 76 days, the concentration of Cu.sup.2+ ions was 8.0.times.10.sup.-3 mols/liter and that of the Ca.sup.2+ ions was 3.74.times.10.sup.-5 mols/liter, in the hydrochloric acid solution. Although the concentration of K.sup.+ ions in the acetate solution was the highest, no K.sup.+ ions could be determined in the hydrochloric acid solution after 76 days. The ion concentrations determined in the hydrochloric acid solution are given in Table 4.

TABLE 4______________________________________Ion concentrations after transport throughthe liquid membraneDays 3 7 11 17 32 52 63 76 116______________________________________10.sup.-3 0.17 0.35 0.35 0.48 1.5 3.9 5.2 8.0 10.5mol/literof Cu.sup.2+10.sup.-5 1.75 1.5 1.5 2.2 3.1 4.0 4.9 --* --mol/literof Ca.sup.2+______________________________________ *means that the concentration was not determined.

EXAMPLE 4

3 U-tubes were filled with the chloroform solution according to Example 1 as the liquid membrane. One arm of each of the three U-tubes was filled with aqueous hydrochloric acid solution of pH value .about.1, and a Co acetate solution (concentration: 0.25 mol/liter; pH value: 6.9), a Ni acetate solution (concentration: 0.25 mol/liter; pH value: 6.9) or a Ca acetate solution (concentration: 0.25 mol/liter; pH value: 8.2) was introduced into the other arms of the U-tubes.

After 20.8 days, the concentration of Co.sup.2+ ions was 8.15.times.10.sup.-4 mols/liter, that of the Ni.sup.2+ ions was 6.5.times.10.sup.-4 mols/liter and that of the Ca.sup.2+ ions was 5.0.times.10.sup.-4 mols/liter, in the hydrochloric acid solution. Cl.sup.- ions could not be determined in any of the three acetate solutions.

The ion concentrations determined in the respective hydrochloric acid solution are given in Table 5.

TABLE 5______________________________________Ion concentrations after transport through theliquid membranesDays 1 1.75 4.6 6 11 14 20.8______________________________________10.sup.-4 mol/ Co.sup.2+ -- 0.17 0.34 1.19 2.02 5.43 8.14liter of Ni.sup.2+ -- -- -- -- 6.80 22.28 64.96 Ca.sup.2+ 0.025 -- 0.175 0.599 0.848 3.144 5.015______________________________________

EXAMPLE 5

A porous hydrophobic sheet consisting of polypropylene was impregnated at 60.degree. C. with dioleyl succinosuccinate by laying the sheet, at this temperature, in a chloroform solution containing the succinosuccinic acid ester. After draining, the impregnated sheet was then set up as a dividing wall between two cells, one of the cells containing aqueous hydrochloric acid solution of pH value .about.1 and the other cell containing an aqueous Cu acetate solution with a concentration of 4.3.times.10.sup.-2 mols/liter and of pH value .about.5. The experimental vessel containing the two cells was kept at 80.degree. C. and the development of the Cu.sup.2+ ion concentration in the hydrochloric acid solution was followed continuously. After 36.1 days, the Cu.sup.2+ ion concentration in the aqueous hydrochloric acid solution was 5.81.times.10.sup.-5 mols/liter. The measured ion concentrations are given in Table 6 below.

TABLE 6__________________________________________________________________________Cu.sup.2+ concentration after ion transport throughthe impregnated sheetDays 0.8 1.8 5.8 6.8 8.8 9.8 12.8 15.8 19.8 22.8 27.1 36.1__________________________________________________________________________10.sup.-6 mol/ 1.9 1.9 5.8 8.0 11.3 16.5 25.2 24.3 29.9 37.6 37.4 58.1Cu.sup.2+__________________________________________________________________________

EXAMPLE 6

30 ml of a uranyl acetate solution (concentration: 0.16 mol/liter, pH value: .about.4) were introduced into one side of a U-tube which had been filled, in the lower part, with a 0.5 M solution of dioleyl succinosuccinate in chloroform. Aqueous hydrochloric acid solution (pH value: .about.1) was introduced into the other side of the U-tube. The concentration of UO.sub.2.sup.2+ ions in the originally uranyl-free hydrochloric acid solution was 3.times.10.sup.-5 mols/liter after 7 days and 6.52.times.10.sup.-5 mols/liter after 14 days.

EXAMPLE 7

An aqueous acetate solution containing uranyl acetate in a concentration of 8.8 .times.10.sup.-2 mols/liter and Cu acetate in a concentration of 9.8.times.10.sup.-2 mols/liter, which had a ph value of .about.5, was filled into one side of a U-tube, into the lower part of which the chloroform solution used in Example 6 had been introduced. An aqueous hydrochloric acid solution, which had a pH value of 1, was introduced into the other side of the U-tube.

After 7 and 14 days, the content of UO.sup.2.sup.2+ ions in the hydrochloric acid solution was 2.43.times.10.sup.-5 mols/liter and 6.08.times.10.sup.-5 mols/liter, respectively, and the content of Cu.sup.2+ ions was 25.2.times.10 .sup.-5 mols/liter and 51.5.times.10.sup.-5 mols/liter, respectively.

EXAMPLE 8

30 ml of a 0.5 molar solution of diethyl succinosuccinate in chloroform were filled into a U-tube. 25 ml of an aqueous acetate salt solution (solution a), containing 9.6.times.10.sup.-2 mols/liter of Cu.sup.2+, 8.5.times.10.sup.-2 mols/liter of Ni.sup.2+, 8.6.times.10.sup.-2 mols/liter of Cd.sup.2+, 8.times.10.sup.-2 mols/liter of Ca.sup.2+ and 13.times.10.sup.-2 mols/liter of K.sup.+, were then introduced into one arm of the U-tube and 25 ml of a 10% aqueous hydrochloric acid solution (solution b) were introduced into the other arm of the U-tube. The two aqueous solutions were separated from one another by the chloroform phase.

After 150 days, the concentration of copper ions in the hydrochloric acid solution was 6.9.times.10.sup.-2 mols/liter, whilst the concentration of all other cations was lower than 10.sup.-4 mols/liter. The depletion of the copper ions in solution a and their concentration in solution b are summarised in the following table.

__________________________________________________________________________Days 0 14 56 100 150__________________________________________________________________________c(Cu.sup.2+), Solution a 9.6 .times. 10.sup.-2 3.5 .times. 10.sup.-2 4.8 .times. 10.sup.-3 1.5 .times. 10.sup.-3 4.6 .times. 10.sup.-4mols/liter Solution b <2.10.sup.-4 2.7 .times. 10.sup.-2 4.3 .times. 10.sup.-2 6.0 .times. 10.sup.-2 6.9 .times. 10.sup.-2__________________________________________________________________________ What is claimed is:

Claims

1. A process for the separation of polyvalent cations from monovalent cations or for the selective separation of different polyvalent cations from aqueous solutions, according to the principle of coupled ion transport and using a liquid membrane, which comprises using a liquid membrane, which consists of an essentially water-immiscible organic solvent and of an essentially water-insoluble succinosuccinic acid diester, dissolved in the said solvent, of the formula I ##STR3## in which R is an alkyl, alkenyl or cycloalkyl having up to 24 C atoms, the proportion of the succinosuccinic acid diester in the organic solvent being at least 0.01% by weight, based on the organic solvent, or of the melt of a compound of the formula I, between two aqueous solutions having different pH values, the aqueous solution into which the polyvalent cations are transported through the liquid membrane having a pH value of 1 to 8, and this pH value necessarily being lower than the pH value of the other aqueous solution, which contains the cations to be separated selectively.

2. A process according to claim 1, wherein the aqueous solution into which the polyvalent cations are transported through the liquid membrane has a pH value of 1 to 5, and this value is at least one whole unit lower than the pH value of the other aqueous solution, which contains the cations to be separated selectively.