The present invention relates to an electrolysis cell comprising a cathode space comprising a cathode, an anode space comprising an anode, and a salt bridge space disposed between the cathode and anode, wherein the cathode space and the salt bridge space are delimited from one another by the cathode, and the salt bridge space and the anode space by the anode, and the cathode and the anode take the form of a gas diffusion electrode, to an electrolysis system comprising a corresponding electrolysis cell, and to methods of electrochemical conversion with the electrolysis cell or electrolysis system.
The combustion of fossil fuels currently covers about 80% of global energy demand. These combustion processes emitted about 34 032.7 million metric tons of carbon dioxide (CO2) globally into the atmosphere in 2011. This release is the simplest way of disposing of large volumes of CO2 as well (brown coal power plants exceeding 50 000 t per day).
Discussion about the adverse effects of the greenhouse gas CO2 on the climate has led to consideration of reutilization of CO2. In thermodynamic terms, CO2 is at a very low level and can therefore be reduced again to usable products only with difficulty.
In nature, CO2 is converted to carbohydrates by photosynthesis. This process, which is divided up into many component steps over time and spatially at the molecular level, is copiable on the industrial scale only with great difficulty. The more efficient route at present compared to pure photocatalysis is the electrochemical reduction of the CO2. A mixed form is light-assisted electrolysis or electrically assisted photocatalysis. The two terms can be used synonymously, according to the viewpoint of the observer.
As in the case of photosynthesis, in this process, CO2 is converted to a higher-energy product (such as CO, CH4, C2H4, etc.) with supply of electrical energy (optionally in a photo-assisted manner) which is obtained for example from renewable energy sources such as wind or sun. The amount of energy required in this reduction corresponds ideally to the combustion energy of the fuel and should advantageously only come from renewable sources. However, overproduction of renewable energies is not continuously available, but at present only at periods of strong insolation and strong wind. However, this is likely to change in the near future with the further rollout of sources of renewable energy.
The electrochemical reduction of CO2 at solid-state electrodes in aqueous electrolyte solutions offers a multitude of possible products for which illustrative Faraday efficiencies at different metal cathodes are shown in table 1, taken from “Electrochemical CO2 reduction on metal electrodes” by Y. Hori, published in: C. Vayenas, et al. (Eds.), Modern Aspects of Electrochemistry, Springer, New York, 2008, pp. 89-189.
There are currently discussions about the electrification of the chemical industry. This means that chemical commodities or fuels are to be produced advantageously from CO2 (CO), H2O with supply of surplus electrical energy, advantageously from renewable sources. In the phase of introduction of such technology, the aim is for the economic value of a substance to be distinctly greater than its calorific value.
Electrolysis methods have undergone significant further development in the last few decades. PEM water electrolysis has been optimized to give high current densities. Large electrolyzers having outputs in the megawatt range are already being introduced onto the market.
However, CO2 electrolysis still faces some further specific challenges. Firstly, unlike in the case of water electrolysis, the electrolyte medium and the substrate are not identical. Therefore, a functional CO2 electrolyzer must normally cope with more components (additional gas feed). Secondly, the CO2 substrate can also react with the electrolyte medium and form “adducts” with the charge carriers present therein, for example:
CO2+OH−→HCO3− or
CO2+2OH−→CO32−+H2O
according to the pH in the mode of operation
The “CO2” may therefore occur as different species, either charged or uncharged, in multiple or even in all streams of matter present in the electrolyzer. Similar problems can occur with other gases, for example in the generation of O2 or the production of H2O.
An efficient mass transfer concept has therefore typically been essential to date for CO2 electrolysis.
It is therefore an object of the present invention to provide an electrolysis cell in which an efficient process regime can be achieved when a gas is being converted and/or generated.
The inventors have found that it is advantageous to execute both electrodes of an electrolysis cell as gas diffusion electrodes (GDEs) and indeed to operate them as such. This means that separators, especially membranes and diaphragms, that serve to separate product gases are superfluous since this function can now be assumed by the electrodes themselves. As a result, both the additional ionic conduction resistance of these separators, for example membranes, and any disruption of current flow or the insulation of parts of the electrode surface by the product gases in the form of gas bubbles can be avoided. This constitutes a major advantage of the cells having solid anodes or those having zero-gap lattice anodes.
In a first aspect, the present invention relates to an electrolysis cell comprising—a cathode space comprising a cathode;—an anode space comprising an anode; and—a salt bridge space disposed between the cathode and anode, wherein the cathode space and the salt bridge space are delimited from one another by the cathode, and the salt bridge space and the anode space by the anode, and the cathode and the anode take the form of a gas diffusion electrode, wherein the salt bridge space has no separator and wherein the cathode and the anode have no separator on the salt bridge space side, further comprising a first feed device for a first reactant gas which is connected to the cathode space and is designed to supply the cathode space with a first reactant gas, and/or a first removal device for a first product gas which is connected to the cathode space and is designed to remove a first product gas from the cathode space, and/or a second feed device for a second reactant gas which is connected to the anode space and is designed to supply the anode space with a second reactant gas, and/or a second removal device for a second product gas which is connected to the anode space and is designed to remove a second product gas from the anode space, a third feed device for an electrolyte which is designed to supply the salt bridge space with an electrolyte, and a third removal device for an electrolyte which is designed to remove an electrolyte from the salt bridge space.
The present invention further relates to an electrolysis system comprising the electrolysis cell of the invention.
Additionally disclosed are a method of electrochemical conversion of at least one reactant gas in an electrolysis cell of the invention or an electrolysis system of the invention, wherein at least one reactant gas is supplied to a cathode space and/or anode space of the electrolysis cell, and a method of generating at least one product gas in an electrolysis cell of the invention or an electrolysis system of the invention, wherein at least one product gas is produced from an electrolyte in the salt bridge space and removed from the cathode space and/or the anode space.
Further aspects of the present invention can be inferred from the dependent claims and the detailed description.
The appended drawings are intended to illustrate embodiments of the present invention and impart further understanding thereof. In association with the description, they serve to explain concepts and principles of the invention. Other embodiments and many of the advantages mentioned are apparent with regard to the drawings. The elements of the drawings are not necessarily shown true to scale with respect to one another. Elements, features and components that are the same, have the same function and the same effect are each given the same reference numerals in the figures of the drawings, unless stated otherwise.
Unless defined differently, technical and scientific expressions used herein have the same meaning as commonly understood by a person skilled in the art in the specialist field of the invention.
Figures given in the context of the present invention relate to % by weight, unless stated otherwise or apparent from the context. In the gas diffusion electrode of the invention, the percentages by weight add up to 100% by weight.
“Hydrophobic” in the context of the present invention is understood to mean water-repellent. According to the invention, hydrophobic pores and/or channels are thus those that repel water. More particularly, hydrophobic properties are associated in accordance with the invention with substances or molecules having nonpolar groups.
“Hydrophilic”, by contrast, is understood to mean the ability to interact with water and other polar substances.
Gas diffusion electrodes (GDE) in general are electrodes in which liquid, solid and gaseous phases are present, and where a conductive catalyst in particular can catalyze an electrochemical reaction between the liquid and gaseous phases.
The catalyst can be executed in different ways, for example as a porous “all-active material catalyst”, optionally with auxiliary layers to adjust the hydrophobicity; or in the form of a conductive porous carrier to which a catalyst may be applied in a thin layer.
In the context of this invention, a gas diffusion electrode (GDE) is especially a porous electrode having an interior in which gases can move by diffusion. It serves in each case to separate the anode space and the cathode space from the salt bridge space. It is especially designed, in particular embodiments, to separate a gas space and an electrolyte space from one another. It also has the particular feature, in particular embodiments, that product gases can exit from these gas diffusion electrodes on the opposite side from the counterelectrode, i.e. into the cathode space and/or the anode space. These gaseous products may originate, for example, from a liquid or dissolved reactant (liquid-to-gas electrolysis, e.g. 2H2O→O2+4H++4e−) or form from a gaseous reactant that has especially penetrated into the electrode from its opposite side from the counterelectrode (gas-to-gas electrolysis, e.g. 2CO2→CO+CO32−). It is not necessary in the context of this invention for the GDE to be gas-permeable through its plane since no passage of the gases into the electrolyte is required, nor does it occur in particular embodiments—i.e. there is no flow-through arrangement. Liquid and/or dissolved products and/or by-products of the electrochemical conversion, especially the charge carriers generated, may be released by the electrode into the electrolyte. If the main product of the electrochemical conversion should be liquid or dissolved at the GDE, this can be transferred from the electrode into the electrolyte (gas-to-liquid electrolysis, e.g. CO2+2H2O+2e→HCOOH+2OH−).
Standard pressure is 101 325 Pa=1.01325 bar.
Electroosmosis: Electroosmosis is understood to mean an electrodynamic phenomenon in which a force toward the cathode acts on particles having a positive zeta potential that are present in solution and a force toward the anode on all particles having negative zeta potential. If conversion takes place at the electrodes, i.e. a galvanic current flows, there is also a flow of matter of the particles having positive zeta potential to the cathode, irrespective of whether or not the species is involved in the conversion. The same is true of a negative zeta potential and the anode. If the cathode is porous, the medium is also pumped through the electrode. This is also referred to as an electroosmotic pump.
The flows of matter resulting from electroosmosis can also flow counter to concentration gradients. Diffusion-related flows that compensate for the concentration gradients can be overcompensated as a result.
A separator in the context of the invention is a barrier, for example a layer, that can accomplish a spatial and, at least to some degree, also physical separation between different spaces in the electrolysis cell, for example anode space, salt bridge space, cathode space, and also electrical separation between anode and cathode, but permits ion transport between the different spaces. A separator especially does not have a fixed assigned potential like an electrode does. Moreover, a separator in particular embodiments is especially a barrier in two-dimensional form with uniform surface coverage. More particularly, membranes and diaphragms should be regarded as separators. Thus, in an electrolysis cell of the invention, the salt bridge space especially does not have any membrane and any diaphragm, and the cathode and anode additionally do not have any membrane and any diaphragm on either side of the salt bridge space.
In particular embodiments, the electrolysis cell of the invention does not comprise a fixed two-dimensional layer with ion transport at a fixed location, especially in “incorporated” form. The ion transport function may be taken on by the electrolyte itself in the electrolysis cell of the invention.
Separators can bring crucial disadvantages for cell operation through charge carrier accumulation in the electrolyte substreams. This is the case especially when the electrolyte includes ions that are not broken down at the electrodes (anode and/or cathode) and/or the separator has unfavorably low or zero ion selectivity. In the course of passage of the electrolyte streams, it is then possible for cations to pass over into the catholyte (electrolyte stream that comes into contact with the cathode) and/or anions into the anolyte (electrolyte stream that comes into contact with the cathode). Counterions for these charge carriers are then generated by the electrodes. As a result, the electrolytes have a different composition on exit from the cell than on entry. This can become problematic especially in the case of very large cells. In the present dual GDE cell concept with just one electrolyte stream in particular, no such problems can occur in particular embodiments.
Furthermore, especially in particular embodiments, the presence of gastight separators or other gas separation devices such as gastight frits in the salt bridge space is ruled out.
In a first aspect, the present invention relates to an electrolysis cell comprising—a cathode space comprising a cathode;—an anode space comprising an anode; and—a salt bridge space disposed between the cathode and anode, wherein the cathode space and the salt bridge space are delimited from one another by the cathode, and the salt bridge space and the anode space by the anode, and the cathode and the anode take the form of a gas diffusion electrode, wherein the salt bridge space has no separator and wherein the cathode and the anode have no separator on the salt bridge space side.
The term “salt bridge space” is used here with regard to its function of acting as a “bridge” between anode or anode arrangement and cathode or cathode arrangement, and in this context of having cations and anions which, however, need not form salts in the present case. This could also be named as ion bridge space with regard to its function of exchanging charge by means of ions between anode and cathode. Since this term is unfamiliar, however, the space is referred to in accordance with the invention as salt bridge space, even if no salt in the conventional sense need be present therein.
The dimensions of the salt bridge space are not particularly restricted, and it may take the form, for example, of a gap between the anode and the cathode, which are arranged parallel to one another, for example.
The cathode space, the anode space and salt bridge space in the electrolysis cell of the invention are not particularly restricted in terms of shape, material, dimensions, etc., provided that they can accommodate the cathode and the anode and they are delimited from one another, i.e. spatially separated, by the anode and cathode, with possible physical contact within the gas diffusion electrode through the pores of the cathode and anode as gas diffusion electrodes.
In respect of the individual spaces, it is possible here, according to the electrolysis to be conducted, to correspondingly provide feed and removal devices for reactants and products, for example in the form of liquid, gas, solution, suspension, etc., where these may optionally also be recycled in each case. Nor is there any restriction in this regard, and it is also possible for the flow through the individual spaces to be in parallel or in countercurrent. For example, in the case of electrolysis of CO2—where this may also still contain CO, i.e. contains at least 20% by volume of CO2, for example, this is supplied to the cathode as gas—for example in countercurrent to an electrolyte stream in the salt bridge space in the case of a three-chamber construction. There is no restriction here.
Corresponding feed options also exist in the anode space, and are also set out in detail hereinafter. The respective feed may be provided in either continuous or discontinuous form, for example pulsed, etc., for which pumps, valves, etc. may correspondingly be provided in an electrolysis system of the invention—which are also discussed hereinafter, as are cooling and/or heating devices, in order to be able to catalyze correspondingly desired reactions at the anode and/or cathode. In advantageous embodiments, the anode space and the cathode space comprise essentially only gaseous substrates, advantageously solely gaseous substrates, i.e. gaseous reactants and/or products, such that the corresponding feed devices and/or removal devices, if present, are designed to feed and/or remove gaseous substances, and/or liquid substrates, i.e. liquid reactants and/or products, are fed and removed via the electrolyte in the salt bridge space, such that the corresponding feed device and/or removal device is set up to feed and/or remove liquid electrolytes, for example aqueous electrolytes.
The materials in the respective spaces or the electrolysis cell and/or the further constituents of the electrolysis system may also be suitably matched correspondingly here to desired reactions, reactants, products, electrolytes, etc. Furthermore, at least one power source per electrolysis cell is of course also included. Further apparatus parts that occur in electrolysis cells and electrolysis systems may also be provided in the electrolysis system of the invention or the electrolysis cell. In particular embodiments, the single cells are used to form a stack comprising 2-1000, advantageously 2-200, cells, and the operating voltage thereof is advantageously in the range of 3-1500 V, more advantageously 200-600 V.
In particular embodiments, the salt bridge space, for stabilization and to assure force-fitting, for example in a stack, may comprise a filling medium in non-self-contained form, for example in the form of a bed, of a knit, of an elastic element, of a network, of a porous structure, for example in spongelike form, and/or of a porous self-supporting structure, for example in regular form. This filling medium may also have been further functionalized, for example acidically and/or basically, in order to suitably establish a pH of the electrolyte in the salt bridge space and/or to improve electrolyte transport in the salt bridge space and/or to further react any ions formed, for example HCO3− ions in CO2 electrolysis, as a result of which CO2 can in turn be recovered and optionally recycled.
According to the invention, the cathode is not particularly restricted, provided that it is in the form of a gas diffusion electrode, and may be matched to a desired half-reaction, for example with regard to the reaction products. The cathode may have a single-layer or multilayer structure and may include a suitable material as catalyst for electrochemical conversion of a reactant at the cathode, especially of at least one gaseous reactant. It is of course also possible to convert a material in the salt bridge space at the cathode to a gas that can then escape through the cathode space, for example in the case of electrolysis of water to H2.
A cathode for reduction of CO2 and optionally CO may comprise, for example, a metal such as Cu, Ag, Au, Zn, Pb, Sn, Bi, Pt, Pd, Ir, Os, Fe, Ni, Co, W, Mo, etc., or mixtures and/or alloys thereof, advantageously Cu, Ag, Au, Zn, Pb, Sn, or mixtures and/or alloys thereof and/or a salt thereof, where suitable materials may be matched to a desired product. A catalyst may thus be chosen according to the desired product. In the case of reduction of CO2 to CO, for example, the catalyst is advantageously based on Ag, Au, Zn and/or compounds thereof such as Ag2O, AgO, Au2O, Au2O3, ZnO. For preparation of hydrocarbons, advantage is given to Cu or Cu-containing compounds such as Cu2O, CuO and/or copper-containing mixed oxides with other metals, etc. For preparation of formic acid, for example, catalysts based on Pb, Sn and/or Cu, especially Pb, Sn, are possible.
The cathode is the electrode where the reductive half-reaction takes place. It may be in single-layer or multilayer form as a gas diffusion electrode. The gas diffusion electrode may take the form, for example, of a porous catalyst structure optionally having at least one binder; of a composite having a porous catalyst structure; of a porous, conductive, catalytically inactive structure, e.g. carbon-paper GDL (gas diffusion layer), carbon-cloth GDL, and/or polymer-bound film composed of granular glassy carbon impregnated with the cathode catalyst; of a particulate catalyst that has been applied by means of a suitable ionomer to a suitable support, for example a porous conductive support; of a porous conductive support impregnated with a suitable catalyst; of a non-ion-conductive gas diffusion electrode that has subsequently been impregnated with a suitable ionomer, for example an anion-conductive ionomer, for example especially for a CO2 electrolysis; etc.
In addition, the cathode may also display open-pore ion-conductive layers on the electrolyte side of the GDE, for example for protection of the catalyst from mechanical erosion, for example in the form of an open-pore bound layer of a particulate ion exchanger. In particular embodiments, the cathode does not have any self-contained ion-conductive layers.
Various combinations of the above-described electrode structures are also possible as cathode.
The corresponding cathodes here may also contain materials that are customary in cathodes, such as binders, ionomers, for example anion-conductive ionomers, fillers, hydrophilic additives, etc., which are not particularly restricted. As well as the catalyst, the cathode may thus, in particular embodiments, contain at least one support material, for example a conductive support material (e.g. a metal such as titanium), and/or at least one nonmetal such as carbon, Si, boron nitride (BN), boron-doped diamond, etc., and/or at least one conductive oxide such as indium tin oxide (ITO), aluminum zinc oxide (AZO) or fluorinated tin oxide (FTO)—for example as used for production of photoelectrodes, and/or at least one polymer based on polyacetylene, polyethoxythiophene, polyaniline or polypyrrole, for example in polymer-based electrodes; (also possible are nonconductive supports, for example polymer meshes, for example in the case of adequate conductivity of the catalyst layer), binders (e.g. hydrophilic and/or hydrophobic polymers, e.g. organic binders, for example selected from PTFE (polytetrafluoroethylene), PVDF (polyvinylidene difluoride), PFA (perfluoroalkoxy polymers), FEP (fluorinated ethylene-propylene copolymers), PFSA (perfluorosulfonic acid polymers), and mixtures thereof, especially PTFE), conductive fillers (e.g. carbon), nonconductive fillers (e.g. glass) and/or hydrophilic additives (e.g. Al2O3, MgO2, hydrophilic materials such as polysulfones, e.g. polyphenylsulfones, polyimides, polybenzoxazoles or polyetherketones, or generally polymers that are electrochemically stable in the electrolyte, polymerized “ionic liquids”, and/or organic conductors such as PEDOT:PSS or PANI (camphorsulfonic acid-doped polyaniline), which are not particularly restricted.
The anode is likewise also a gas diffusion electrode. It is additionally likewise not particularly restricted in accordance with the invention and may be matched to a desired half-reaction, for example with regard to the reaction products. At the anode, which is electrically connected to the cathode by means of a power source for provision of the voltage for the electrolysis, the oxidation of a substance takes place in the anode space. Furthermore, the anode material is not particularly restricted and depends primarily on the desired reaction. The anode, like the cathode, may have a single-layer or multilayer structure and may include a suitable material as catalyst for electrochemical conversion of a reactant at the anode, especially at least one gaseous reactant. It is of course also possible to convert a material in the salt bridge space at the anode to a gas that can then escape through the anode space, for example in the case of an electrolysis of water to O2.
Illustrative anode materials include platinum or platinum alloys, palladium or palladium alloys, and glassy carbon, iron, nickel, etc. Further anode materials are also conductive oxides such as doped or undoped TiO2, indium tin oxide (ITO), fluorine-doped tin oxide (FTO), aluminum-doped zinc oxide (AZO), iridium oxide, etc. It is also optionally possible for these catalytically active compounds to be applied solely superficially by thin-film methodology, for example on a titanium and/or carbon support. The anode catalyst is not particularly restricted. Catalysts used for O2 or Cl2 production may, for example, also be IrOx (1.5<x<2) or RuO2. These may also be in the form of a mixed oxide with other metals, e.g. TiO2, and/or be supported on a conductive material such as C (in the form of conductive black, activated carbon, graphite, etc.). It is alternatively also possible to use catalysts based on Fe—Ni or Co—Ni for O2 production.
The anode is the electrode where the oxidative half-reaction takes place. It may be in single-layer or multilayer form as a gas diffusion electrode. The gas diffusion electrode may take the form, for example, of a porous catalyst structure optionally having at least one binder; of a composite having a porous catalyst structure; of a porous, conductive, catalytically inactive structure, e.g. carbon-paper GDL (gas diffusion layer), carbon-cloth GDL, and/or polymer-bound film composed of granular glassy carbon impregnated with the cathode catalyst; of a particulate catalyst that has been applied by means of a suitable ionomer to a suitable support, for example a porous conductive support; of a porous conductive support impregnated with a suitable catalyst; of a non-ion-conductive gas diffusion electrode that has subsequently been impregnated with a suitable ionomer, for example an anion-conductive or cation-conductive ionomer; etc.
In addition, the anode may also display open-pore ion-conductive layers on the electrolyte side of the GDE, for example for protection of the catalyst from mechanical erosion, for example in the form of an open-pore bound layer of a particulate ion exchanger. In particular embodiments, the anode does not have any open-pore ion-conductive layers. In particular embodiments, neither the cathode nor the anode has any self-contained ion-conductive layers.
Here too, various combinations of the different anode structures are possible.
The corresponding anodes may likewise contain materials that are customary in anodes, such as binders, ionomers, for example including cation-conducting ionomers, for example containing sulfonic acid and/or phosphonic acid groups, fillers, hydrophilic additives, etc., which are not particularly restricted, and which have also been described above, for example, for the cathode. As well as the catalyst, the anode may thus, in particular embodiments, contain at least one support material, for example a conductive support material (e.g. a metal such as titanium), and/or at least one nonmetal such as carbon, Si, boron nitride (BN), boron-doped diamond, etc., and/or at least one conductive oxide such as indium tin oxide (ITO), aluminum zinc oxide (AZO) or fluorinated tin oxide (FTO)—for example as used for production of photoelectrodes, and/or at least one polymer based on polyacetylene, polyethoxythiophene, polyaniline or polypyrrole, for example in polymer-based electrodes; (also possible are nonconductive supports, for example polymer meshes, for example in the case of adequate conductivity of the catalyst layer), binders (e.g. hydrophilic and/or hydrophobic polymers, e.g. organic binders, for example selected from PTFE (polytetrafluoroethylene), PVDF (polyvinylidene difluoride), PFA (perfluoroalkoxy polymers), FEP (fluorinated ethylene-propylene copolymers), PFSA (perfluorosulfonic acid polymers), and mixtures thereof, especially PTFE), conductive fillers (e.g. carbon), nonconductive fillers (e.g. glass) and/or hydrophilic additives (e.g. Al2O3, MgO2, hydrophilic materials such as polysulfones, e.g. polyphenylsulfones, polyimides, polybenzoxazoles or polyetherketones, or generally polymers that are electrochemically stable in the electrolyte, polymerized “ionic liquids”, and/or organic conductors such as PEDOT:PSS or PANI (camphorsulfonic acid-doped polyaniline), which are not particularly restricted.
In particular embodiments, the anode and/or the cathode are contacted by a conductive structure. The conductive structure here is not particularly restricted. This may comprise, for example, carbon nonwovens, metal foams, metal knits, expanded metals, graphite structures or metal structures.
For some of the electrochemical conversions at the catalyst electrodes, the presence of water is advantageous. e.g. 3CO2+H2O+2e−→CO+2HCO3− or according to pH: 2CO2+2e−→CO+CO32−
Therefore, the anode and/or cathode in particular embodiments have sufficient hydrophilicity at least on a side facing the salt bridge space. This hydrophilicity may optionally be adjusted by hydrophilic additives such as TiO2, Al2O3, or other electrochemically inert metal oxides, etc.
As described above, the anode and/or cathode may have a single-layer or multilayer structure. Examples of layers that may be present in the cathode and/or anode as gas diffusion electrode are elucidated hereinafter. These may be formed by extruding, calendering, pressing, casting, knife-coating, etc., for example onto an electrical contact or a further layer—as described above and hereinafter.
If the anode and/or cathode is constructed as a single-layer electrode, the layer may, for example, be an extruded, calendered, pressed or cast porous layer comprising at least one electrochemically active catalyst as specified above by way of example, for example in powder form, and at least one binder, likewise as specified above. In addition, this layer may also contain further additives for adjusting hydrophilic and/or hydrophobic properties, for improving electrical conductivity, for improving ionic conductivity, mechanical or electrical support structures and/or filler materials, as specified above. It would also be possible to use the catalyst here on a support, for example, likewise as specified above by way of example. The amount of catalyst here is not particularly restricted and for example 5-10% loading.
When the cathode and/or anode takes the form of a multilayer GDE, it may contain the layers which follow, for example.
The porous layer comprising an ion exchange material may serve, for example, to transport charge carriers generated in the active layer away and simultaneously to block alternative unwanted transport pathways by counterions.
The electrochemical conversion of carbon dioxide at a cathode is governed, for example, by the following equation:
3CO2+2e−+H2O→CO+2HCO32−
If charge carriers are destroyed at and/or in the active layer, the porous layer comprising an ion exchange material can improve the supply of these species.
4HCO3−→O2+4CO2+4e−
For adjustment of the charge transport pathway, the porous layer comprising an ion exchange material may also be designed to generate new charge carriers from neutral species, for example by dissociation or auto-protolysis.
H2O→OH−+H+
In particular embodiments, neither the cathode nor the anode comprises a porous layer comprising an ion exchange material, in order to further reduce the electrical resistance of the electrode and to further simplify the construction.
Particular embodiments and arrangements with the above layers are set out in more detail hereinafter.
In particular embodiments, the cathode and/or anode have at least one active layer comprising an electrocatalyst as specified above by way of example. In the active layer, the electrocatalyst may be introduced, for example, into a suitable binder that has been described above and with which the hydrophilicity/hydrophobicity of the layer can be suitably adjusted for transport of a gas and/or a liquid.
In particular embodiments, the cathode and/or the anode have a single- or multilayer structure with the at least one active layer. For example, however, it is also possible for this to be adjoined by a hydrophobic layer for contacting of the cathode space and/or the anode space.
In particular embodiments, the cathode and/or anode consists of the active layer. In particular embodiments, the active layer, especially in the case of a single-layer structure composed of the active layer, comprises a hydrophobic binder that enables good contacting of the cathode space and/or anode space, for example for supply of a gaseous reactant and/or removal of a gaseous product.
In particular embodiments, the cathode has a hydrophobic layer as specified above on the cathode space side and/or the anode has one on the anode space side. This can improve the supply of a gaseous reactant to the cathode space and/or anode space and/or the removal of a gaseous product therefrom. This is advantageous especially in the case of a two-layer structure of the cathode and/or anode with hydrophobic layer and active layer, in which case the active layer can also be suitably adjusted with regard to hydrophilicity for good contacting of an electrolyte of the salt bridge space.
In particular embodiments, the cathode has a hydrophobic layer on the cathode space side and/or the anode has a hydrophobic layer on the anode space side, even in the case of a multilayer structure. It is possible here for the hydrophobic layer to adjoin the active layer. On the other side of the active layer toward the salt bridge space, it is then also possible, for example, for there to be an adjoining layer for contacting of the electrolyte of the salt bridge space and/or a layer for removal of ions formed in the electrolysis, but one which is not in the form of a separator and is especially not two-dimensional.
In particular embodiments, the cathode and/or the anode each comprise a porous layer comprising an ion exchange material, which is not particularly restricted, on the salt bridge space side, wherein the porous layer on the cathode advantageously contains an anion exchanger and/or the porous layer on the anode advantageously contains a cation exchanger. However, these layers do not comprise the ion exchange material in such a way that is in two-dimensional form. For example, such an ion exchange material may be provided solely in the pores of the porous layer and/or else in pores of the active layer. The cathode may comprise, for example, at least one ionomer, for example an anion-conductive or anion-transporting ionomer (e.g. anion exchange resin, anion transport resin), which may comprise, for example, various functional groups for ion exchange, which may be the same or different, for example tertiary amine groups, alkylammonium groups and/or phosphonium groups, and/or the anode may comprise at least one ionomer, for example a cation-conductive or cation-transporting ionomer (e.g. cation exchange resin, cation transport resin), which may comprise, for example, various functional groups for ion exchange, which may be the same or different, for example sulfonates, phosphonates, carboxylates and/or quaternary borates.
In particular embodiments, the cathode and/or the anode does not comprise any ion exchange material, and, in particular, neither the cathode nor the anode comprises any ion exchange material.
In an electrolysis cell of the invention, as also in the methods of the invention, the electrodes mentioned above by way of example may be combined with one another as desired.
In the electrolysis cell of the invention, it is of course also possible to employ commercially available GDEs as anode and/or cathode. For example, it is possible to use GDEs for water oxidation on the anode side from Uhde DeNora or generally all fuel cell manufacturers.
In particular embodiments, the electrolysis cell of the invention further comprises a first feed device for a first reactant gas which is connected to the cathode space and is designed to supply the cathode space with a first reactant gas, and/or a first removal device for a first product gas which is connected to the cathode space and is designed to remove a first product gas from the cathode space, and/or a second feed device for a second reactant gas which is connected to the anode space and is designed to supply the anode space with a second reactant gas, and/or a second removal device for a second product gas which is connected to the anode space and is designed to remove a second product gas from the anode space.
The individual feed and/or removal devices here are not particularly restricted and may be designed as described above. Whether there is a feed and/or removal device in the cathode space and/or anode space depends on the respective half-reaction at cathode and/or anode. If, for example, no gas is converted, no gas supply is required, for example when a gas is formed from an electrolyte in the salt bridge space and is removed. When a gas is converted to a liquid and/or a substance that dissolves in the electrolyte, again, no removal device in the respective electrode space is required. But it is of course possible that the cathode space and/or anode space in each case has a feed and removal device, such that it is possible both to feed a reactant through the cathode space and/or anode space to the cathode and/or anode and to remove a product from the cathode space and/or anode space. It is thus possible to provide the first feed device and the first removal device and/or the second feed device and the second removal device. Combinations of the above arrangements are also possible.
In particular embodiments, the electrolysis cell of the invention further comprises a third feed device for an electrolyte, which is designed to supply the salt bridge space with an electrolyte, and/or a third removal device for an electrolyte, which is designed to remove an electrolyte from the salt bridge space. These are advantageously present even in the case of aqueous electrolytes, in order, for example, to be able to compensate for water entrained in a product gas and/or to balance out the fluctuations in concentration. It may nevertheless also be the case that the electrolyte is consumed, for example in an anodic electrolysis of water to O2, such that supply of electrolyte only may be sufficient. Water can likewise also be formed in an electrolysis, for example, such that only removal of electrolyte may be required. There are also conceivable reactions where electrolyte need not be supplied or removed, e.g. CO2+SO2→CO+SO3
In the electrolysis cell of the invention, in particular embodiments, at least one fluid medium (liquid or gaseous) flows through the cathode space, the anode space and/or the salt bridge space, advantageously all three chambers. In particular embodiments, however, the anode space and/or cathode space, especially both, however, have essentially only a gaseous reactant and/or product, i.e. no liquid, and so the material should be chosen correspondingly. More particularly, the side of the cathode and/or anode facing the cathode space and/or the anode space is thus not flushed with electrolyte.
Illustrative arrangements of electrolysis cells of the invention with periphery are shown in
By contrast, in the concept described here, in particular embodiments, only one electrolyte circuit is required, and so measures for assurance of ion transport can be dispensed with.
The dual GDE cell shown in
In the cathode space I, which is on the side of the cathode gas diffusion electrode GDE-K remote from the counterelectrode or salt bridge space II, the reactant E-K that serves as substrate for the cathode, for example CO2 and/or for example also CO, is introduced. The products P-K of the electrochemical conversion on the cathode side, provided that they are gaseous, are removed from this chamber. This is also true of products of competing reactions, for example H2.
The anode space III serves as flow chamber for the gaseous reactants E-A and products P-A of the anode GDE-A. Since the anode reaction, like the cathode reaction too, is subject to no further restriction within the scope of this invention, either the corresponding gas inlet or the gas outlet, especially at the anode, may be unnecessary. In the case of O2 production at the anode, for example, no gas inlet would be required since O2 can form through water oxidation (H2O—2e−→2H++1/2O2).
In the salt bridge space II, there is an electrolyte containing at least one liquid component that is pumped in circulation, for example, from a reservoir R. It serves firstly for transport of the charge carriers in the cell and secondly for cooling of the electrodes. In particular embodiments of the GDE electrodes, the liquid portion of the electrolyte may contain dissolved traces of the gaseous products and should in that case be degassed.
The presence of gases in the salt bridge space II is not ruled out, especially when they form as a result of chemical reactions in the electrolyte, for example when HCO3− that may originate from the CO2 electrolysis reacts with protons from the electrolyte.
While
Illustrative configurations with falling-film electrodes are shown in
A further illustrative embodiment is shown in
Also disclosed is an electrolysis system comprising the electrolysis cell of the invention. The corresponding embodiments of the electrolysis cell, and also further illustrative components of an electrolysis system of the invention, have already been discussed above and are thus also applicable to the electrolysis system of the invention. In particular embodiments, an electrolysis system of the invention comprises a multitude of electrolysis cells of the invention, although it is not ruled out that other electrolysis cells are present in addition.
In particular embodiments, the electrolysis system of the invention further comprises at least one recycle device, for example one each for the electrolyte in the salt bridge space, the anode space and/or the cathode space, connected to a drain from the salt bridge space and/or the anode space and/or the cathode space and a feed to the salt bridge space and/or the anode space and/or the cathode space, which is set up to guide a reactant from the cathode reaction that can be formed in the salt bridge space and/or can escape from the cathode space and/or anode space (including as unconverted reactant) back into the cathode space, optionally after purification. Corresponding considerations are also possible for a reactant in the anode space with a recycle device to the anode space, according to the reaction. The individual recycle devices are not particularly restricted and can be implemented, for example, by conduits, pipes, etc., provided that they are suitable for recycling the corresponding reactants and/or products on the anode side and/or cathode side—advantageously essentially gases—and/or the electrolyte with any products formed.
In particular embodiments, the electrolysis system of the invention further comprises an external device for electrolyte treatment, especially an apparatus for removal of dissolved gases, with which the electrolyte in the salt bridge space in particular can be treated in order to remove, for example, gases such as CO2 or O2, and hence enable recycling of electrolyte in the salt bridge space. In particular embodiments, the electrolysis system of the invention comprises a recycle device for the electrolyte, which is connected to the third feed device for an electrolyte and the third removal device for an electrolyte and is designed to recycle the electrolyte after it has passed through the electrolysis cell. In particular embodiments, the recycle device for the electrolyte comprises a device for electrolyte treatment and/or a feed for fresh electrolyte which is set up to supply fresh electrolyte to the recycled electrolyte to compensate for electrolyte losses in the system.
By comparison with existing electrolysis systems, a present electrolysis system can manage with much less “periphery” such as pumps, phase separators, etc.
In yet a further aspect, the present invention relates to the use of an electrolysis cell of the invention or of an electrolysis system of the invention that may also comprise a multitude of electrolysis cells of the invention for electrolysis of CO2 and/or CO.
The present invention additionally relates to a method of electrochemical conversion of at least one reactant gas in an electrolysis cell of the invention or an electrolysis system of the invention, wherein at least one reactant gas is supplied to a cathode space and/or anode space of the electrolysis cell. In such a method, it is also possible for at least one product gas to form from an electrolyte in the salt bridge space and/or be removed from the cathode space and/or anode space; in other words, it is possible to supply both a reactant gas to the cathode space and/or anode space of the electrolysis cell, e.g. CO2 and/or CO to the cathode space, and at the same time to obtain a product gas from the electrolyte in the salt bridge space and/or to remove it from the cathode space and/or anode space, for example O2 from the anode space in the case of water electrolysis with water as electrolyte. It is of course also possible, for example, for a product insoluble in the electrolyte of the salt bridge space to form, which is then removed via the cathode space and/or anode space, for example as a gas or liquid or, as the case may be, also in solid form (for example depending on the electrolysis temperature). The two methods of the invention are accordingly not mutually exclusive, but can instead supplement one another. In addition, it is of course also possible to supply at least one reactant gas both to the cathode space and to the anode space.
In particular embodiments, at least one reactant gas is CO2 and/or CO and is supplied to the cathode space. On the anode side, for example, chlorine can be prepared from HCl or O2 from water, etc., and the anode reaction is not particularly restricted, such that embodiments with or without a feed device or with or without a removal device on the anode side are conceivable here, where at least one feed device or removal device is present. On the cathode side, there is at least one feed device for CO2 and/or CO.
A further aspect of the present invention relates to a method of producing at least one product gas in an electrolysis cell of the invention or an electrolysis system of the invention, wherein at least one product gas is produced from an electrolyte in the salt bridge space and removed from the cathode space and/or anode space. In this method, for example, a feed device on the cathode side and/or anode side is not necessarily required, for example in the production of H2 or O2 from water as a constituent of the electrolyte in the salt bridge space. In particular embodiments, a method of the invention, however, is not a water electrolysis under acidic conditions since the cell is too complex for that. The method of the invention, however, is also suitable for an alkaline water electrolysis. If the method of the invention is executed as an alkaline water electrolysis, the use of the two gas diffusion electrodes (GDE) in the electrolysis cell of the invention which are employed in the method of the invention and which may both contain nickel-based catalysts here, for example, may constitute a significant improvement over the grid and perforated sheet electrodes that are currently in common use. Such a GDE-alkali electrolyzer may be operated here at higher current densities, since there would be no need for the insulation of the electrode structures by reaction gases and the additional electrical resistance of a diaphragm.
The methods of the invention may be performed with the electrolysis cell of the invention and the electrolysis system of the invention, and so aspects, configurations and embodiments described in this regard also relate to the present methods.
The electrolyte in the salt bridge space is not particularly restricted in the methods of the invention, provided that it does not damage the electrodes, permits charge transport and contains at least one liquid component. For example, a combination of liquid and solid electrolytes is also possible, as specified, for example, in DE 10 2017 223 521.7 and US 2017/037522 A1, to which reference is made with regard to the electrolyte.
In particular embodiments, the electrolyte in a method of the invention, especially in the second method with the production of at least one product gas, comprises water. In particular embodiments, the salt bridge space is essentially completely filled and advantageously fully filled with electrolyte.
In particular embodiments, the electrolyte is recycled to the electrolysis cell after passing through the electrolysis cell. It is especially advantageous here that the two gas diffusion electrodes can sufficiently protect the electrolyte from contamination, and hence the electrolyte can be reused even without an excessively complex purification. It may be the case, however, that the electrolyte is indeed purified. Nor is it ruled out that electrolyte losses, for example including through reaction of the electrolyte, are replaced in the recycling operation.
In particular embodiments, the anode space and the cathode space in the method of the invention have essentially no liquid, advantageously no liquid, which can be brought about, for example, by appropriate layers in the gas diffusion electrodes. In this way, it is especially possible to configure recycling cycles on the anode side and/or cathode side in a simpler manner, for example with regard to corrosion protection.
A CO2 electrolysis in the dual GDE cell shown in
In the CO2 electrolysis, CO2 is supplied via the cathode space Ito the cathode GDE as reactant gas E-K, which is advantageously converted to gaseous products, for example in the active layer thereof. For example: 3CO2+H2O+2e−→CO+2HCO3−
The gaseous product can be released back into the cathode space I on the side of the cathode GDE remote from the counterelectrode.
Anions produced as a by-product can be released into the electrolyte of the salt bridge space II.
The reaction at the anode is subject to no further restriction.
In the simplest case, it is possible, for example, i.e. when the anode is not provided with any gaseous substrate in the chamber III (as shown in
This case is also shown in the working example.
Alternatively, in a configuration shown in
A 3-chamber cell concept and a mode of operation of this cell are disclosed, these being achievable without any higher—further—development work, which do not require any separators such as membranes and diaphragms and may therefore also include only a single electrolyte circuit.
The above embodiments, configurations and developments can, if viable, be combined with one another as desired. Further possible configurations, developments and implementations of the invention also include combinations that have not been mentioned explicitly of features of the invention that have been described above or are described hereinafter with regard to the working examples. More particularly, the person skilled in the art will also add individual aspects to the respective basic form of the present invention as improvements or supplementations.
The invention is elucidated further in detail hereinafter with regard to various examples thereof. However, the invention is not limited to these examples.
Example 1: This working example illustrates the mode of function of a dual GDE cell. The test setup shown in schematic form in
The construction shown in
The composition of the anode was as follows:
The cathode had the following composition:
For the cathode, the following gas flow rates and current densities of CO2 were established:
As shown in
At the gas inlet of the cathode space I, CO2 was introduced with a 7-fold excess (λ=8) with respect to the current density applied, in accordance with values for complete production of CO at the given current intensity. The product gases from the two spaces I and III, after passing through the cell once, were collected in separate gas pouches and analyzed by gas chromatography.
In addition, the pH of the electrolyte was monitored continuously.
The distance between the electrodes was 6 mm. The active area of the two GDEs was 10 cm2.
First of all, a two-hour preliminary experiment was conducted in order to determine the self-setting pH of the electrolyte. The starting electrolyte used was 1M K2CO3 in distilled water. Since a continuous shift in the pH to the neutral was observed, later on in the experiment, 2M KHCO3 in distilled water was used as electrolyte, pumped in circulation at 120 ml/min.
In order to demonstrate the functionality of the dual GDE cell, one one-hour CO2 electrolysis each was conducted at current densities J of 100, 200 and 300 mA/cm2. After 15 and after 60 min, the composition of the cathode-side and anode-side product gases was measured. The electrolyte was changed before each experiment.
As elucidated above, the anions generated by the cathode are broken down at the anode if there are no charge transport layers present on the electrodes, nor is there a gaseous anode substrate. In this case, the composition of the anode gas suggests carbonate CO32− as the main by-product from the cathode.
The net reaction equation at the cathode here is thus: 2CO2+2e−→CO+CO32−
The fact that the electrolyte pH was nevertheless 8-8.5 suggests physical saturation of the electrolyte with CO2. At higher current densities, isolated formation of gas bubbles in the feeds and in the electrolyte vessel was observed. It should be noted in this regard that the release of CO2 at the anode can be prevented, for example, by the introduction of ion transport layers, for example at the anode.
A linear fit of these data gives a point of intersection with the Y axis at −2.31 V and an approximate ohmic cell resistance of 0.77Ω. For an electrode separation of 2 mm which is more realistic for application purposes, at 300 mA/cm−2, a cell voltage of −3.1 V would be expected. In the event of a change in temperature from 25° C. to 60° C., as would be expected from a stack electrolyzer, the conductivity of the electrolyte rises from 120 mScm−1 to 200 mScm−1. In this case, cell voltages around −2.8 V would be expected.
In order to demonstrate the effective separation of the product gases by the GDEs, the anode gas was analyzed for traces of cathodic product gases.
The traces of the cathodic products found in the anodic product gas are below 200 ppm. Thus, this simple dual GDE cell is equivalent to the construction shown in
It is also therefore advisable, in order to maintain the gas separation, that the salt bridge space II is fully filled with electrolyte, since GDEs are not necessarily designed to separate two gas spaces from one another.
With this invention, a general new cell concept is presented, that can avoid the mixing of different phases in the electrolyzer specifically through use of two gas diffusion electrodes. As a result, the currently customary use of separators, such as membranes, is also superfluous.
| Number | Date | Country | Kind |
|---|---|---|---|
| 10 2018 202 184.8 | Feb 2018 | DE | national |
This application is the US National Stage of International Application No. PCT/EP2019/051241 filed 18 Jan. 2019, and claims the benefit thereof. The International Application claims the benefit of German Application No. DE 10 2018 202 184.8 filed 13 Feb. 2018. All of the applications are incorporated by reference herein in their entirety.