Claims
- 1. A process for making an aqueous dispersion of water-insoluble core/sheath polymer particles comprising
- (a) sequentially emulsion polymerizing at a temperature of from about 10.degree. C. to about 100.degree. C. in an aqueous medium containing a free radical initiator:
- a core monomer system comprising one or more monoethyleneically unsaturated monomers having a group of the formula --HC.dbd.C<, at least one of which has a carboxylic acid group, the core monomer system comprising at least 5% of a carboxylic acid monomer based on the weight of the core monomer system, to thereby form dispersed core particles having an average diameter of from about 0.05 to 1 micron, and
- (b) polymerizing in the presence of the core polymer dispersion resulting from (a) a sheath monomer system comprising at least one monoethylenically unsaturated monomer having no ionizable group to form a sheath polymer on the core particles, any monoethylenically unsaturated carboxylic acid in the sheath monomer mixture being present in an amount of no more than 10% by weight of the sheath monomers, the proportion of carboxylic acid in the sheath monomer mixture being less than 1/3 the proportion thereof in the core monomer mixture, said sheath being (i) permeable to an aqueous volatile base selected from ammonia and amines, (ii) having a T.sub.i of greater than 50.degree. C., and (iii) being non film-forming at 20.degree. C.,
- the resultant core-sheath particles having an average diameter before neutralization and swelling of from about 0.07 to 4.5 microns, the relative amounts of core-forming monomer(s) and sheath-forming monomer(s) being such that the ratio of the weight of the core to the weight of the total polymer in the resulting dispersed particles is from about 1:4 to 1:100, and
- (c) neutralizing with ammonia or amine so as to swell said core and form particles which, when dried, contain a single void and cause opacity in compositions in which they are contained.
- 2. A process according to claim 1 wherein the acid monomer in (a) is selected from the group consisting of acrylic acid, methacrylic acid, acryloxypropionic acid, methacryloxypropionic acid, acryloxyacetic acid, methacryloxyacetic acid, monomethyl acid maleate, monomethyl acid itaconate, crotonic acid, and mixtures thereof.
- 3. A process according to claim 1 wherein the acid in (a) is selected from the group consisting of acrylic acid and methacrylic acid, and the core monomer(s) comprise(s) at least 15% of said acid monomer, the core monomer composition having no more than 40% of butyl acrylate or no more than an amount of an equivalent monomer which would give a comparable T.sub.i when using the same comonomer combination.
- 4. A process according to claim 1 wherein at least about 85% of the core particles are encapsulated as evidenced by titration with aqueous potassium hydroxides.
- 5. A process according to claim 4 in which the formation of dispersed core particles in (a) is a multistage process involving first the preparation of a seed polymer from monoethylenically unsaturated monomers which may or may not comprise a monomer containing an acid group, and a second stage polymerization on the seed particles of ethylenically unsaturated monomers comprising
- (1) 5 to 100 weight % of a carboxylic acid,
- (2) 0 to 95 weight % of at least one monoethylenically unsaturated monomer lacking an ionizable group, and
- (3) 0 to 20 weight % of a polyethylenically unsaturated monomer,
- using conditions to obtain core polymer particles having an average diameter of from 0.1 to 0.5 micron in unswollen condition, and the subsequently polymerized sheath provides core/sheath particles having an average diameter of up to about 2.0 microns in unswollen condition.
- 6. A process according to claim 5 in which the acid is selected from the group consisting of acrylic acid, methacrylic acid, acryloxypropionic acid, methacryloxypropionic acid, acryloxyacetic acid, methacryloxyacetic acid, monomethyl acid maleate, monomethyl acid itaconate, crotonic acid and mixtures thereof, and the core monomer(s) comprise(s) at least 15% of said acid monomer, the core monomer composition having no more than 40% of butyl acrylate or no more than an amount of an equivalent monomer which would give a comparable T.sub.i when using the same comonomer combination.
- 7. A process according to claim 5 in which the acid is selected from the group consisting of acrylic acid, methacrylic acid, and mixtures thereof.
- 8. A process according to claim 7 in which the core/sheath particles have an average diameter of from about 0.2 to about 2.0 microns in unswollen condition and in which 0.1% to 3% of a polyunsaturated crosslinking monomer is included in the core monomer mixture.
- 9. A process according to claim 4 in which the formation of the sheath in (b) is a multistage process.
- 10. A process according to claim 9 in which at least one stage of the multistage process for forming the sheath is the polymerization of a monomer composition comprising at least one nonionic monoethylenically unsaturated monomer.
- 11. A process according to claim 9 in which, in at least one stage of the multistage formation of the sheath, a crosslinked polymer is formed from a mixture of at least one monoethylenically unsaturated monomer and at least one polyethylenically unsaturated monomer, the amount of the latter being in the range of about 1% to about 50% by weight of the mixture, the core/sheath polymer being swollen by at least partial neutralization by application of a volatile base prior to the completion of the crosslinking stage when the amount of polyethylenically unsaturated monomer exceeds about 5% by weight of the monomer mixture.
- 12. A composition comprising an aqueous dispersion of water-insoluble core/sheath polymer particles having an average diameter of 0.07 to 4.5 microns, having a core polymerized from a monomer system comprising one or more monoethylenically unsaturated monomers having a group of the formula --HC.dbd.C<, at least one of said unsaturated monomers having a carboxylic acid group, and having at least one sheath polymerized from at least one different monomer system, at least one of said different monomer systems being hard and producing a polymer (a) having a T.sub.i greater than 50.degree. C., (b) being non film-forming at 20.degree. C., (c) being permeable to ammonia and amines, said core being swollen by neutralization with ammonia or amine in the presence of water, said particles having a property such that when subsequently dried a single cavity forms in said core and said particles cause opacity in compositions in which they are contained.
- 13. A process which comprises mixing the aqueous dispersion of water insoluble core/sheath polymer particles of claim 12 with an aqueous dispersion of a particulate material selected from pigments, extenders, vinyl addition emulsion polymers, and mixtures thereof to form a coating composition.
- 14. A process according to claim 13 which comprises the additional steps of depositing a film of the coating composition on a solid substrate to be coated and/or impregnated, and subsequently drying the composition, forming single cavities in the core of substantially each of said particles so as to contribute to opacity of said film.
- 15. An opaque composition comprising dried core/sheath particles having a single cavity in said core and an average particle size of about 0.07 to 4.5 micron and having a core polymerized from a monomer system comprising one or more monoethylenically unsaturated monomers having a group of the formula --HC.dbd.C<, at least one of said unsaturated monomers having a carboxylic acid group, and having at least one sheath polymerized from at least one different monomer system, at least one of said different monomer systems being hard and producing a polymer (a) having a T.sub.i greater than 50.degree. C., (b) being non film-forming at 20.degree. C., (c) being permeable to ammonia and amines, said core having been swollen by neutralization with ammonia or amine in the presence of water, and subsequently dried.
- 16. A composition for coating and/or impregnating a substrate comprising (1) a film-forming vinyl addition polymer either dissolved or dispersed in an aqueous medium and (2) an aqueous dispersion of water-insoluble core/sheath polymer particles of claim 12.
- 17. A composition adapted for coating and/or impregnating comprising an aqueous dispersion of a water-insoluble emulsion vinyl addition polymer having an apparent second order transition temperature (T.sub.i) of about 17.degree. to 20.degree. C., a core/sheath product of claim 12 at a pigment volume concentration of 5 to 50% or higher, an inorganic pigment and optionally an extender.
- 18. A process according to claim 1 in which the formation of the sheath in (b) is a multistage process comprising first forming a hard and/or crosslinked polymer sheath, then forming a soft polymer sheath of monomers selected to provide a relatively softer polymer having a T.sub.i of less than 50.degree. C. and at least 10.degree. C. lower than that of the hard sheath polymer.
- 19. A process according to claim 18 in which the T.sub.i of the polymer at the exterior surface of the particles is in range from below 0.degree. C. up to about 20.degree. C.
- 20. The process of claim 1 wherein said resultant core/sheath particles are, prior to swelling, essentially impermeable at 20.degree. C. to fixed or permanent bases including sodium, potassium, calcium and magnesium hydroxide.
- 21. The composition of claim 12 wherein said polymer is, prior to swelling, essentially impermeable at 20.degree. C. to fixed or permanent bases including sodium, potassium, calcium and magnesium hydroxide.
- 22. The composition of claim 15 wherein said particles are, prior to swelling, essentially impermeable at 20.degree. C. to fixed or permanent bases including sodium, potassium, calcium and magnesium hydroxide.
- 23. The process of claim 1 wherein, subsequent to neutralizing in step (c), a second sheath stage is polymerized on said core-sheath particles.
- 24. The composition of claim 12 wherein a second sheath is polymerized onto the particles after neutralization.
- 25. The composition of claim 24 wherein the second sheath is crosslinked or uncrosslinked polystyrene.
RELATED APPLICATIONS
This is a Divisional of Serial No. 158,759, filed June 12, 1980, abandoned, which is in turn a continuation-in-part of Ser. No. 52,280, filed June 26, 1979, abandoned. Another divisional of Serial No. 158,759 is being filed on even date herewith by Kowalski, Vogel, and Blankenship.
US Referenced Citations (3)
Divisions (1)
|
Number |
Date |
Country |
Parent |
158759 |
Jun 1980 |
|
Continuation in Parts (1)
|
Number |
Date |
Country |
Parent |
52280 |
Jun 1979 |
|