In various embodiments, the present invention relates to solid-state electrochemical cells such as solid oxide fuel cells, and in particular to fabrication techniques for such cells utilizing setter plates.
Solid oxide fuel cells (SOFCs) are highly efficient, environmentally friendly electrochemical devices that are capable of directly converting chemical energy stored in hydrogen or hydrocarbon fuels into electrical energy. SOFCs are therefore an important type of solid-state electrochemical cell. During SOFC operation, oxygen ions migrate from a cathode to an anode through a dense electrolyte. At the anode, the oxygen ions oxidize the fuel, resulting in the generation of electrons that may be directed through an external circuit. SOFCs may be used for, for example, off-grid and portable power generation.
Most state-of-the-art SOFCs use a nickel-based, planar anode-supported cell architecture, which compared to other configurations and materials sets offers a balance between power density, structural strength, and efficiency. Furthermore, most state-of-the-art SOFCs use a yttria-stabilized zirconia (YSZ) electrolyte. However, the use of nickel-based cermet anode supports and YSZ electrolytes often results in less than desirable robustness and creates the risk for long-term reliability issues. During its operational lifetime an SOFC system is expected to operate reliably and with limited degradation in steady-state or transient conditions. Chemical instability at the interfaces is one of the key issues in stationary applications, whereas thermo-mechanical instability has tended to dominate degradation in transportation applications because of frequent thermal cycles. Advancement of key technologies increase the possibility to use SOFC systems for applications such as distributed generation (DG), in which realistic conditions require the ability to regularly experience load following, thermal cycling, and reduction-oxidation (“redox”) cycling with minimal degradation.
A primary limitation for Ni-based cermet anodes (e.g., NiO/YSZ) is its poor stability during redox cycling. This instability is due, primarily, to the large volume change and coarsening of the Ni-phase in the cermet anode. For example, Ni can undergo 65-69% volume increase upon re-oxidation to NiO. Such redox cycles can be expected during long-term fuel cell operation due to unexpected fuel supply interruptions, high fuel utilization under high current loads, or gas sealing failures. While major advances have been made in the development of SOFC systems—including innovative approaches to lower the operating temperature and increase power density—reliability issues, robustness, and cost remain an impediment to widespread commercialization.
There are various approaches proposed for solving the redox stability problem, with the most economical methods tending to be through modification of SOFC anode materials. For example, with the use of certain all-ceramic anodes an SOFC can become very robust even in the event of extreme redox cycling conditions such as fuel interruption (i.e., the “reducing” fuel shuts off and is replaced by an oxidizing air environment). An all-ceramic anode also presents the opportunity to fine-tune the material properties of the cell for increased power density and/or efficiency. However, most ceramic-based anode SOFCs are difficult to fabricate using conventional, low cost ceramic processing routes, especially when attempting to make larger planar cells (e.g., larger than 5 cm by 5 cm). Such materials often experience warpage, cracks, or other damage during the elevated temperatures required to produce SOFC materials. Thus, there is a need for improved manufacturing techniques for SOFCs incorporating all-ceramic anodes that minimize or substantially eliminate damage and deformation of the cell materials.
In accordance with various embodiments of the present invention, cell materials for solid-state electrochemical cells such as SOFCs, such as partial cells that incorporate one or more anode-related layers and a solid electrolyte layer, are fabricated from ceramic powders and sintered while mounted on and/or loaded by setter plates composed of, or having outer surfaces composed of, materials compatible (i.e., unreactive) with the SOFC cell materials. For example, anode layers in accordance with embodiments of the invention may include a ceramic oxide material containing strontium, iron, cobalt, and molybdenum (i.e., “SFCM”). The Co and Mo of SFCM are volatile and may easily migrate during sintering (or “firing”) and may react with other nearby materials. In various anode materials in accordance with embodiments of the invention, other dopants or additives such as, for example, Ni, Cr, V, Bi, Li, Na, and/or Cu may also be volatile and deleteriously reactive. Other ceramic anode layers in accordance with embodiments of the invention include vanadium- and sodium-doped strontium niobate (SNNV, i.e., Sr0.2Na0.8Nb1−xVxO3±δ, where 0.1≤x≤0.3 and 0≤δ≤1.5), as well as vanadium-doped strontium titanate (SVT, i.e., SrxVyTi1−yO3±δ, where 1.0≥x≥0.8, 0.1≤y≤0.4, and 0≤δ≤1.5), as disclosed in U.S. Pat. No. 9,525,179, filed on Mar. 12, 2014, the entire disclosure of which is incorporated by reference herein. Although SFCM is utilized as an exemplary material in various examples herein, it is understood that other ceramic anode materials (e.g., SNNV, SVT, etc.) are encompassed by embodiments of the invention.
During fabrication processes in accordance with embodiments of the invention, unfired (or “green”) SOFC layered structures are disposed on and/or loaded by a setter plate (or simply, “setter”) for high-temperature sintering processes during which the ceramic constituents within the green ceramic coalesce (or sinter) to become a solid, consolidated part. Conventional sintering processes utilize alumina (Al2O3) setter plates, which are inexpensive and have high melting points. However, SFCM structures that contact alumina setter plates react to form compounds such as Al2(MoO4)3 and CoMoO4, which degrade SOFC performance or even destroy the SFCM-based cell. Moreover, NiO in Ni-cermets may also react with alumina to form nickel aluminate spinel, which may impact cell performance and decrease manufacturing yield. In addition, SFCM-based SOFC materials may crack and/or become stuck to conventional setter plates during sintering, resulting in damage to the cell materials or rendering the fired materials unsuitable for further processing into fuel cells.
Thus, embodiments of the present invention utilize setter plates that are coated with or entirely composed of materials unreactive with the SOFC materials (e.g., SFCM-based anode materials) that they support and/or contact during sintering steps. In general, setter plates in accordance with embodiments of the invention may include, consist essentially of, or consist of one or more materials utilized to fabricate an SOFC anode and/or solid electrolyte layer, but may also include, consist essentially of, or consist of one or more other unreactive or essentially unreactive materials. For example, setter plates in accordance with embodiments of the invention may include, consist essentially of, or consist of ceria (Ce2) or gadolinium-doped ceria (GDC) (e.g., Ce0.9Gd0.1O1.95). The setter plates may either be entirely composed of the unreactive material, or the setter plates may be composed of a different ceramic material (e.g., alumina, YSZ, or silicon carbide) that is coated, at least on the outer surface that faces and/or directly contacts the SOFC material, with the unreactive material. Embodiments of the invention therefore include alumina setter plates that are coated with ceria or GDC, and the SOFC materials fired with such setter plates may be based, at least in part, on doped ceria, GDC, ZrO2, and/or YSZ.
In accordance with some embodiments of the invention, SOFC anode materials and layers are “all-ceramic,” i.e., materials that do not reduce to form metal in the reducing fuel environment of the SOFC. In various embodiments, all-ceramic materials are free of nickel, nickel oxide, and other metals not incorporated within a ceramic-phase network. In various embodiments, this is the case up to and after partial-cell (or half-cell) firing during fabrication. Such materials tend to exhibit superior performance and reliability during load following, thermal cycling, and redox cycling. In various embodiments, setter plates are also free of nickel and nickel oxide. In various embodiments, SOFC anode materials may be infiltrated with various catalysts, including Ni, after half-cell firing and before or after cathode layers are added to the SOFC.
SOFC materials and layers, in accordance with embodiments of the invention, are placed upon and/or loaded by setter plates for firing. After firing, the unreactive nature of the setter-plate material enables the separation of substantially the entire cell material or layer from the setter plate(s), i.e., the removal of the entire bulk layer structure without cracking or breaking thereof, and without all or part of the layer structure deleteriously sticking to a setter plate. While firing of various cell layers in accordance with embodiments of the invention may result in creation of visible discoloration or artifacts (e.g., dust or powder) on a setter plate, as long as the bulk of the layer having the desired shape and dimensions may be removed from the setter plate(s) without cracking, adhesion, or damage, this is considered to be separation of “substantially the entire layer” from the setter plate(s).
Various embodiments of the present invention incorporate thin functional layers between the electrolyte and the cathode in order to reduce the interfacial resistance between the electrolyte and the cathode, as disclosed in U.S. patent application Ser. Nos. 15/461,708 and 15/461,709 (the '708 and '709 applications), both filed on Mar. 17, 2017, the entire disclosures of which are incorporated by reference herein. For example, the functional layer may include, consist essentially of, or consist of cobalt oxide mixed with gadolinium-doped ceria (Co-GDC, for example, Co3O4—Ce0.9Gd0.1O1.95) or cobalt oxide mixed with samarium doped ceria (Co-SDC, for example, Co3O4—Ce0.8Sm0.2O1.9), and the functional layer may be disposed and in direct contact with the solid electrolyte and the cathode material.
SOFCs are utilized herein as exemplary devices in descriptions of embodiments of the present invention, but it should be understood that embodiments of the invention also encompass other types of solid-state electrochemical cells. For example, a second type of solid-state electrochemical cell is known as a solid oxide electrolyzer cell (SOEC), which is like a SOFC that runs in reverse. In other words, the SOEC takes electricity as an input to drive the reverse reaction of the SOFC, where water (and/or carbon dioxide) is converted into hydrogen (and/or carbon monoxide) and oxygen. The SOEC is an electrolytic cell involving the transformation of electrical energy into chemical energy, whereas the SOFC is a galvanic cell involving the transformation of chemical energy into electrical energy. Like the SOFC, the SOEC typically operates between 500° C. and 800° C. and is a layered structure including, consisting essentially of, or consisting of a solid oxide (ceramic) electrolyte, a fuel electrode, and an oxygen electrode. The most common electrolyte of SOECs, similar to SOFCs, is a dense ionic conductor that includes yttria stabilized zirconia (YSZ). Some other choices are scandia stabilized zirconia (ScSZ), doped ceria-based electrolytes, or lanthanum gallate materials. The most common fuel electrode material is a Ni-YSZ cermet. Perovskite-type lanthanum strontium manganese (LSM) is the most common oxygen electrode material though other cathode materials are possible. SOECs may be planar or tubular just like the SOFC. Furthermore, the SOEC may in certain cases be exactly the same as the SOFC and used in both SOFC mode and SOEC mode. This is known as a reversible or regenerative fuel cell.
A third type of solid-state electrochemical cell is known as solid oxide membrane (SOM) reactor, or an electrocatalytic reactor. The reactors have two chambers that are separated by a solid oxide, gas-tight ceramic electrolyte or membrane that is capable of transporting oxide ions (and/or protons) at elevated temperatures (typically between 600° C. and 1,000° C.). Such electrochemical cells can operate in electrolytic mode to convert input feedstock chemicals (e.g., CH4) into other higher value chemicals (e.g., ethylene) and/or reactions can be driven through pressure or concentration gradients on either side of the membrane. Catalyst in each chamber can increase selectivity to a product by offering reaction sites and/or creating reaction pathways that are more favorable to certain products than others. SOM reactors have also been used to drive partial oxidation reactions of methane to form syngas (mostly hydrogen and carbon monoxide), oxidative coupling of methane (OCM) to form ethane and ethylene, and even the generation of high-purity oxygen from air. SOM reactors may be planar or tubular just like the SOFC.
In an aspect, embodiments of the invention feature a method of fabricating a solid oxide fuel cell. A layered structure is provided. The layered structure includes, consists essentially of, or consists of (i) a ceramic anode (e.g., a ceramic anode support layer and a ceramic anode functional layer disposed over the anode support layer), and (ii) a solid electrolyte layer disposed over the anode (e.g., over the anode functional layer). The layered structure is disposed or positioned on a first setter plate. The first setter plate has a top surface (i) in contact with the anode (e.g., with the anode support layer) and (ii) including, consisting essentially of, or consisting of ceria and/or doped ceria. One or more additional surfaces of the first setter plate (e.g., the bottom surface and/or one or more side surfaces spanning the top and bottom surfaces) may include, consist essentially of, or consist of ceria and/or doped ceria. The layered structure is sintered. Substantially the entire, or the entire, sintered layered structure is separated from the first setter plate after sintering.
Embodiments of the invention may include one or more of the following in any of a variety of combinations. A cathode layer (e.g., a ceramic cathode layer) may be formed (e.g., deposited) over the electrolyte layer before sintering (e.g., before the first setter plate is positioned) or after sintering (e.g., after the sintered layered structure is separated from the first setter plate). The cathode layer may include, consist essentially of, or consist of a mixture of samarium strontium cobaltite and doped ceria. A second setter plate may be disposed or positioned on the layered structure before sintering. The second setter plate may have a bottom surface including, consisting essentially of, or consisting of ceria and/or doped ceria. The bottom surface of the second setter plate may be in contact with the uppermost layer of the layered structure (e.g., the electrolyte or a cathode layer). One or more additional surfaces of the second setter plate (e.g., the top surface and/or one or more side surfaces spanning the top and bottom surfaces) may include, consist essentially of, or consist of ceria and/or doped ceria. After the layered structure is sintered, substantially the entire layered structure may be separated from the second setter plate. The bottom surface of the second setter plate may include, consist essentially of, or consist of ceria doped with Gd, Y, La, Pr, Sm, and/or Nd. The second setter plate may include, consist essentially of, or consist of a ceramic setter material coated with a layer of material different from the ceramic setter material. The ceramic setter material may include, consist essentially of, or consist of alumina, and/or the layer of material different from the ceramic setter material may include, consist essentially of, or consist of ceria and/or doped ceria. The second setter plate (i.e., the entire plate) may include, consist essentially of, or consist of ceria and/or doped ceria. A weight of the second setter plate may range between approximately 0.5 g/cm2 and approximately 3 g/cm2. A loading applied to the layered structure during sintering, including any weight of the second setter plate applied to the layered structure, may range between approximately 0.5 g/cm2 and approximately 3 g/cm2. The bottom surface of the second setter plate may further include, mixed with the ceria and/or doped ceria, one or more volatile species selected from the list consisting of Co, Mo, Ni, Cr, V, Bi, Li, Na, and Cu.
The top surface of the first setter plate may include, consist essentially of, or consist of ceria doped with Gd, Y, La, Pr, Sm, and/or Nd. The first setter plate may include, consist essentially of, or consist of a ceramic setter material coated with a layer of material different from the ceramic setter material. The ceramic setter material may include, consist essentially of, or consist of alumina, and/or the layer of material different from the ceramic setter material may include, consist essentially of, or consist of ceria and/or doped ceria. The first setter plate (i.e., the entire plate) may include, consist essentially of, or consist of ceria and/or doped ceria. The top surface of the first setter plate may further include, mixed with the ceria and/or doped ceria, one or more volatile species selected from the list consisting of Co, Mo, Ni, Cr, V, Bi, Li, Na, and Cu. The anode and/or anode functional layer may include, consist essentially of, or consist of a mixture of doped ceria with a ceramic oxide material containing strontium, iron, cobalt, and molybdenum. The electrolyte layer may include, consist essentially of, or consist of doped ceria (e.g., ceria doped with Gd, Y, La, Pr, Sm, and/or Nd). The method may include, prior to disposing the layered structure on the first setter plate, (i) coating a first plate with a layer of ceria and/or doped ceria, and (ii) sintering the first plate at a temperature above 500° C. (e.g., above 1000° C.) to form the first setter plate. The temperature at which the first plate is sintered may be higher than a temperature (e.g., a maximum temperature) at which the layered structure is sintered.
In another aspect, embodiments of the invention feature a method of fabricating a solid oxide fuel cell. A layered structure is provided. The layered structure includes, consists essentially of, or consists of (i) a ceramic anode (e.g., a ceramic anode support layer and a ceramic anode functional layer disposed over the anode support layer), and (ii) a solid electrolyte layer disposed over the anode (e.g., over the anode functional layer). The layered structure is disposed or positioned on a first setter plate. The first setter plate has a top surface (i) in contact with the anode (e.g., with the anode support layer) and (ii) including, consisting essentially of, or consisting of ceria and/or doped ceria. One or more additional surfaces of the first setter plate (e.g., the bottom surface and/or one or more side surfaces spanning the top and bottom surfaces) may include, consist essentially of, or consist of ceria and/or doped ceria. A second setter plate is disposed or positioned on the layered structure. The second setter plate has a bottom surface including, consisting essentially of, or consisting of ceria and/or doped ceria. The bottom surface of the second setter plate is in contact with the uppermost layer of the layered structure (e.g., the electrolyte or a cathode layer). One or more additional surfaces of the second setter plate (e.g., the top surface and/or one or more side surfaces spanning the top and bottom surfaces) may include, consist essentially of, or consist of ceria and/or doped ceria. The layered structure is sintered. Substantially the entire, or the entire, sintered layered structure is separated from the first and second setter plates after sintering.
Embodiments of the invention may include one or more of the following in any of a variety of combinations. A cathode layer (e.g., a ceramic cathode layer) may be formed (e.g., deposited) over the electrolyte layer before sintering (e.g., before one or both setter plates are positioned) or after sintering (e.g., after the sintered layered structure is separated from the first and second setter plates). The cathode layer may include, consist essentially of, or consist of a mixture of samarium strontium cobaltite and doped ceria. The first setter plate and/or the second setter plate may include, consist essentially of, or consist of a ceramic setter material coated with a layer of ceria and/or doped ceria. The doped ceria may include, consist essentially of, or consist of ceria doped with Gd, Y, La, Pr, Sm, and/or Nd. The ceramic setter material may include, consist essentially of, or consist of alumina. The first setter plate and/or the second setter plate (i.e., the entire plate(s)) may include, consist essentially of, or consist of ceria and/or doped ceria. The anode and/or anode support layer may include, consist essentially of, or consist of a mixture of ceria with a ceramic oxide material containing strontium, iron, cobalt, and molybdenum. The anode and/or anode functional layer may include, consist essentially of, or consist of a mixture of doped ceria with a ceramic oxide material containing strontium, iron, cobalt, and molybdenum. The electrolyte layer may include, consist essentially of, or consist of doped ceria. A weight of the second setter plate may range between approximately 0.5 g/cm2 and approximately 3 g/cm2. A loading applied to the layered structure during sintering, including any weight of the second setter plate applied to the layered structure, may range between approximately 0.5 g/cm2 and approximately 3 g/cm2. The method may include, prior to disposing the layered structure on the first setter plate and disposing the second setter plate on the layered structure, (i) coating a first plate with a layer of ceria and/or doped ceria, (ii) coating a second plate with a layer of ceria and/or doped ceria, (iii) sintering the first plate at a temperature above 500° C. (e.g., above 1000° C.) to form the first setter plate, and (iv) sintering the second plate at a temperature above 500° C. (e.g., above 1000° C.) to form the second setter plate. The first temperature and/or the second temperature may be higher than a temperature (e.g., a maximum temperature) at which the layered structure is sintered.
In yet another aspect, embodiments of the invention feature a method of fabricating a solid oxide fuel cell. A layered structure is provided. The layered structure includes, consists essentially of, or consists of (i) a ceramic anode (e.g., a ceramic anode support layer and a ceramic anode functional layer disposed over the anode support layer), and (ii) a solid electrolyte layer disposed over the anode (e.g., over the anode functional layer). The anode and/or anode support layer includes, consists essentially of, or consists of a mixture of a first ceramic material with a ceramic oxide material containing strontium, iron, cobalt, and molybdenum. The anode and/or anode functional layer includes, consists essentially of, or consists of a mixture of a second ceramic material with the ceramic oxide material containing strontium, iron, cobalt, and molybdenum. The electrolyte layer includes, consists essentially of, or consists of a third ceramic material. The layered structure is disposed or positioned on a first setter plate. The first setter plate has a top surface (i) in contact with the anode (e.g., with the anode support layer) and (ii) including, consisting essentially of, or consisting of the first ceramic material, the second ceramic material, and/or the third ceramic material. One or more additional surfaces of the first setter plate (e.g., the bottom surface and/or one or more side surfaces spanning the top and bottom surfaces) may include, consist essentially of, or consist of the first ceramic material, the second ceramic material, and/or the third ceramic material. A second setter plate is disposed or positioned on the layered structure. The second setter plate has a bottom surface including, consisting essentially of, or consisting of the first ceramic material, the second ceramic material, and/or the third ceramic material. The bottom surface of the second setter plate is in contact with the uppermost layer of the layered structure (e.g., the electrolyte or a cathode layer). One or more additional surfaces of the second setter plate (e.g., the top surface and/or one or more side surfaces spanning the top and bottom surfaces) may include, consist essentially of, or consist of the first ceramic material, the second ceramic material, and/or the third ceramic material. The layered structure is sintered. Substantially the entire, or the entire, sintered layered structure is separated from the first and second setter plates after sintering.
Embodiments of the invention may include one or more of the following in any of a variety of combinations. A cathode layer (e.g., a ceramic cathode layer) may be formed (e.g., deposited) over the electrolyte layer before sintering (e.g., before one or both setter plates are positioned) or after sintering (e.g., after the sintered layered structure is separated from the first and second setter plates). The cathode layer may include, consist essentially of, or consist of a mixture of samarium strontium cobaltite and doped ceria. The first ceramic material may include, consist essentially of, or consist of ceria. The second ceramic material may include, consist essentially of, or consist of doped ceria. The third ceramic material may include, consist essentially of, or consist of doped ceria. The first ceramic material may include, consist essentially of, or consist of ceria, and each of the second and third ceramic materials may include, consist essentially of, or consist of doped ceria. The doped ceria may include, consist essentially of, or consist of ceria doped with Gd, Y, La, Pr, Sm, and/or Nd. The first setter plate and/or the second setter plate may include, consist essentially of, or consist of a ceramic setter material coated with a layer of the first ceramic material, the second ceramic material, and/or the third ceramic material. The ceramic setter material may include, consist essentially of, or consist of alumina. The first setter plate and/or the second setter plate (i.e., the entire plate(s)) may include, consist essentially of, or consist of the first ceramic material, the second ceramic material, and/or the third ceramic material. The method may include, prior to disposing the layered structure on the first setter plate and disposing the second setter plate on the layered structure, (i) coating a first plate with a layer of the first ceramic material, the second ceramic material, and/or the third ceramic material, (ii) coating a second plate with a layer of the first ceramic material, the second ceramic material, and/or the third ceramic material, (iii) sintering the first plate at a temperature above 500° C. (e.g., above 1000° C.) to form the first setter plate, and (iv) sintering the second plate at a temperature above 500° C. (e.g., above 1000° C.) to form the second setter plate. The first temperature and/or the second temperature may be higher than a temperature (e.g., a maximum temperature) at which the layered structure is sintered.
Aspects of the invention include sintered layered structures fabricated according to any of the techniques described above.
These and other objects, along with advantages and features of the present invention herein disclosed, will become more apparent through reference to the following description, the accompanying drawings, and the claims. Furthermore, it is to be understood that the features of the various embodiments described herein are not mutually exclusive and may exist in various combinations and permutations. As used herein, the terms “approximately” and “substantially” mean ±10%, and in some embodiments, +5%. The term “consists essentially of” means excluding other materials that contribute to function, unless otherwise defined herein. Nonetheless, such other materials may be present, collectively or individually, in trace amounts. For example, a structure consisting essentially of multiple metals will generally include only those metals and only unintentional impurities (which may be metallic or non-metallic) that may be detectable via chemical analysis but do not contribute to function.
In the drawings, like reference characters generally refer to the same parts throughout the different views. Also, the drawings are not necessarily to scale, emphasis instead generally being placed upon illustrating the principles of the invention. In the following description, various embodiments of the present invention are described with reference to the following drawings, in which:
In various embodiments of the invention, the cathode 110 includes, consists essentially of, or consists of, for example, one or more of lanthanum strontium cobalt ferrite (LSCF) (e.g., La0.6Sr0.4Co0.8Fe0.2O3−δ), lanthanum strontium manganite (LSM) (e.g., La0.8Sr0.2MnO3−δ), lanthanum strontium cobaltite (LSC) (e.g., La0.6Sr0.4Co3−δ), barium strontium cobalt ferrite (BCSF) (e.g., Ba0.5Sr0.5Co0.8Fe0.2O3−δ), samarium strontium cobaltite (SSC) (e.g., Sm0.5Sr0.5CoO3−δ), and/or doped ceria with dopant concentrations ranging from 5 to 30 mol % (or ranging from 10 to 20 mol %), for example samarium-doped ceria (SDC) (e.g., Co—Ce0.8Sm0.2O1.9), gadolinium-doped ceria (GDC) (e.g., Co—Ce0.9Gd0.1O1.95), or ceria doped with any one or more of Y, La, Pr, Sm, or Nd.
For example, the cathode 110 may include, consist essentially of, or consist of a mixture of SSC and GDC, e.g., in a ratio of 3:7 to 7:3 by mass. The cathode 110 may be both an ionic conductor and an electronic conductor, and the cathode 110 may be porous to promote oxygen access for ionization and to provide electrochemically active triple phase boundaries (TPBs) where the electrolyte 120, air, and cathode 110 meet. For example, the cathode 110 may have a porosity ranging from approximately 30% to approximately 60%.
In general, the solid electrolyte 120 is a dense (e.g., ceramic) material that conducts oxygen ions while minimizing electronic conduction therewithin in order to prevent current leakage and corresponding electrical losses. The thickness of the solid electrolyte 120 may range from, for example, approximately 1 μm to approximately 40 μm, or approximately 5 μm to approximately 40 μm, or even from approximately 10 μm to approximately 30 μm. In various embodiments of the invention, the solid electrolyte 120 includes, consists essentially of, or consists of, for example, SDC or GDC. Such solid electrolytes 120 may have dopant concentrations ranging from, for example, approximately 5 to approximately 30 mol %, or from approximately 10 to approximately 20 mol %. In various embodiments, the solid electrolyte 120 may include, consist essentially of, or consist of one or more doped cerias such as yttria-doped ceria (YDC, e.g., Y0.1Ce0.9O1.95), neodymium-doped ceria (NdDC, e.g., Nd0.1Ce0.9O1.95), praseodymium-doped ceria (PrDC, e.g., Pr0.1Ce0.9O1.95), and/or lanthanum-doped ceria (LaDC, e.g., La0.1Ce0.9O1.95). Such solid electrolytes 120 may have dopant concentrations ranging from, for example, approximately 5 to approximately 30 mol %, or from approximately 10 to approximately 20 mol %.
Like the cathode 110, the anode 130 is preferably a porous conductor of at least electrons and, in some embodiments, both ions and electrons in order to provide a conduit for electrons to leave the cell and enter an external circuit (and in some embodiments to additionally promote the electrochemical reaction). In various embodiments of the invention, all or a portion of the anode 130 includes, consists essentially of, or consists of, for example, a ceramic oxide material containing strontium, iron, cobalt, and molybdenum (i.e., SFCM), e.g., SrFe0.1Co0.45Mo0.45O3, SrFe0.2Co0.4Mo0.4O3, SrFe0.34Co0.33Mo0.33O3, or SrFe0.5Co0.25Mo0.25O3. In other embodiments, all or a portion of the anode 130 includes, consists essentially of, or consists of, e.g., vanadium- and sodium-doped strontium niobate (SNNV, i.e., Sr0.2Na0.8Nb1−xVxO3±δ, where 0.1≤x≤0.3 and 0≤δ≤1.5), or vanadium-doped strontium titanate (SVT, i.e., SVT, i.e., SrxVyTi1−yO3±δ, where 1.0≥x≥0.8, 0.1≤y≤0.4, and 0≤δ≤1.5). All or a portion of the anode 130 may include, consist essentially of, or consist of a mixture of SFCM and another material such as GDC. For example, as shown in
Various techniques may be utilized for the fabrication of the SOFC 100 and its constituent layers in accordance with embodiments of the present invention. In various embodiments, a partial cell structure is assembled and then fired (e.g., in a furnace or kiln) using one or more setter plates. For example, as shown in
The fabrication of one or more, or even all, of the electrolyte layer 120, the anode support layer 135, and the anode functional layer 140 may include tape casting. For example, the ceramic powders constituting each of the layers may be individually mixed and tape cast (e.g., onto a polymeric support (e.g., polyethylene terephthalate or biaxially-oriented polyethylene terephthalate)) and dried before being cut into sheets. The tape cast layers may include one or more organic (e.g., polymeric) binders (e.g., polymethylmethacrylate (PMMA), e.g., in particulate or bead form. The sheets may be stacked in the desired configuration and “tacked,” i.e., pressed together under low pressure so that the resulting stacked structure may be handled. The stacked structure may subsequently be laminated together by, e.g., warm isostatic pressing (at a temperature ranging from, e.g., approximately 40° C. to approximately 200° C.), prior to firing.
Once arranged as depicted in
During firing, the ambient atmosphere within the kiln or furnace may be, for example, forced or stagnant air. In other embodiments, the atmosphere within the kiln or furnace may include, consist essentially of, or consist of nitrogen and/or argon containing approximately 1% to approximately 50% oxygen. In yet other embodiments, the atmosphere within the kiln or furnace may include, consist essentially of, or consist of hydrogen (up to approximately 100/6), oxygen (up to approximately 100%), or approximately 1% to approximately 50% hydrogen with the balance being nitrogen and/or argon. The atmosphere may flow at a rate of, e.g., approximately 0.1 to approximately 10 cubic feet per minute.
In various embodiments, the setter plates 200, 210 have areal dimensions at least as large as the material or partial cell structure being fired therebetween. As shown in
The setter plates 200, 210 are coated with or entirely composed of materials unreactive with the SOFC materials (e.g., SFCM-based anode materials) that they support and/or contact during sintering steps. For example, one or both of the setter plates 200, 210 may include, consist essentially of, or consist of ceria. In general, one or both of the setter plates 200, 210 may include, consist essentially of, or consist of one or more materials utilized to fabricate the electrolyte layer 120, the anode support layer 135, and the anode functional layer 140. For example, one or both of the setter plates 200, 210 may include, consist essentially of, or consist of GDC. One or both of the setter plates 200, 210 may either be entirely composed of the unreactive material, and/or one or both of the setter plates 200, 210 may be composed of a different ceramic material (e.g., alumina, YSZ, or silicon carbide) that is coated, at least on the outer surface that faces and/or directly contacts the partial cell, with the unreactive material. Embodiments of the invention therefore include alumina setter plates 200, 210 that are coated with ceria or GDC. For example, embodiments of the invention feature alumina setter plates 200, 210 that are coated with ceria or GDC utilized during the firing of a partial cell structure including an anode support layer 135 that includes, consists essentially of, or consists of a mixture of SFCM and GDC, an anode functional layer 140 that includes, consists essentially of, or consists of a mixture of SFCM and GDC, and an electrolyte layer 120 that includes, consists essentially of, or consists of GDC. In other embodiments, one or both of the setter plates 200, 210 is composed of or coated with a material such as SDC.
Setter plates 200, 210 may be coated with or entirely composed of a mixture of GDC or other doped ceria or ceria and one or more of the volatile species in the ceramic or all-ceramic anode material (e.g., Co, Mo, Ni, Cr, V, Bi, Li, Na, and/or Cu). This may serve multiple functions, including but not limited to improved sintering of the setter or film disposed on the setter to achieve the appropriate particle or pore size and distribution and weight that results in a flat fired cell; to reduce driving forces for diffusion of volatile species into setter during high temperature sintering of cell materials; and to extend the lifetime of the setter for use in manufacturing of all-ceramic anode based cells. The volatile species may be present in the mixture with GDC or ceria in amounts between approximately 50 wt % and approximately 2 mol %. In various embodiments, the volatile species constitutes up to 25 wt % of the mixture with GDC or ceria. In various embodiments, the volatile species constitutes up to 10 wt % of the mixture with GDC or ceria. In an exemplary embodiment, 2 mol % Co3O4 is mixed with GDC and coated on an alumina setter, although other combinations are possible and fall within embodiments of the present invention.
In various embodiments, one of the setter plates 200, 210 is entirely composed of an unreactive material while the other is merely coated with one of the unreactive materials. For example, in an embodiment, setter plate 200 may be entirely composed of ceria, whereas setter plate 210 may be composed of an alumina setter plate with a ceria coating. Alternatively, setter plate 200 may be entirely composed of GDC, whereas setter plate 210 may be composed of an alumina setter plate with a GDC coating. In various embodiments, the setter plates 200, 210 are composed of or coated with the same unreactive material, while in other embodiments, each of the setter plates 200, 210 is composed of or coated with a different unreactive material. For example, setter plate 200 may be entirely composed of ceria, whereas setter plate 210 may be composed of an alumina setter plate with a GDC or Co-GDC coating.
In order to prevent deleterious reactions between the material of the setter plates, each of the setter plates 200, 210, or at least the external surface thereof, desirably has low concentrations of reactive elements (e.g., impurities). For example, in embodiments of the invention, a setter plate, or its external surface (e.g., the coating or an external surface thereof) includes less than 1000 ppm silica or silicon, less than 500 ppm zirconia or zirconium, less than 100 ppm yttria or yttrium, less than 100 ppm phosphorous, and/or less than 250 ppm aluminum. The setter plate or its external surface may contain finite, non-zero concentrations of one or more of these species, e.g., at least 1 ppm, at least 5 ppm, or at least 10 ppm. In various embodiments, a setter plate or its external surface may contain up to approximately 10% zirconia or zirconium. In various other embodiments, a setter plate or its external surface may contain up to approximately 100% stabilized zirconia, which may be stabilized with one or more different dopants (e.g., yttrium, scandium, calcium, magnesium, cerium, and/or aluminum) with concentrations between ˜2 mol % and 10 mol %. In various other embodiments, a setter plate or its external surface may contain up to approximately 100% stabilized zirconia, which may be stabilized with one or more different dopants (e.g., yttrium, scandium, calcium, magnesium, cerium, and/or aluminum) with concentrations between ˜2 mol % and 10 mol %.
Coated setter plates 200, 210 may be coated only on the exterior surface facing and/or contacting the partial cell (i.e., the top surface of bottom setter plate 200 and/or the bottom surface of top setter plate 210), or the setter plates 200, 210 may be coated on all of their external surfaces. The thickness of the coating may be chosen to be to extend the setter lifetime. The thickness of the coating is sufficient to prevent or minimize interaction between any reactive species from the partial cell structure (e.g., Co and/or Mo, and/or others described herein) and the coated interior ceramic material of the setter plate before and during the firing sequence. The desired coating thickness may also be chosen to optimize coated setter plate fabrication processes around the specific materials of the setter plate and film, and particle and/or pore size of the setter plate. For example, the thickness may be optimized to compensate for differences in the coefficients of expansion between the setter plate and the coating so as to prevent flaking or delamination of the coating from the setter plate. For example, the setter plate coating thickness may range from approximately 0.0002 mm to approximately 0.25 mm. Various embodiments have a thickness ranging from approximately 0.0002 mm to approximately 0.025 mm when using thin film deposition techniques such as plasma spray, physical vapor deposition, chemical vapor deposition, or pulsed laser deposition. In other embodiments, the thickness ranges from approximately 0.001 mm to 0.250 mm when using alternate deposition techniques such as dip coating, spray coating, roller coating, or screen printing.
To further extend the lifetime of the coated setter plate, the coating may be reapplied to the setter after the coated setter plate has been utilized in high-temperature sintering processes one or more times. For example, in certain embodiments the coating may be reapplied to the setters after 20 firings. In other embodiments, the coating may be reapplied after 10 firings. The reapplied coating may be of the same formulation as original coating or the reapplied coating may be based primarily on the volatile species found in the all-ceramic or ceramic anode material (e.g., Co, Mo, Ni, Cr, V, Bi, Li, Na, and/or Cu). For example, virgin (uncoated) setter plates 200, 210 may be originally coated with Co-GDC and annealed prior to high temperature sintering of ceramic or all-ceramic anode materials. After one or more (e.g., 20) high-temperature sintering heat treatments, a coating of Co-GDC or Co3O4 may be reapplied to the setters, followed by an optional anneal step prior to using the setters for additional high-temperature sintering heat treatments of the anode materials.
In accordance with embodiments of the present invention, at least setter plate 210 (and, in various embodiments, both setter plates 200, 210) has a weight selected to apply a desired amount of loading on the partial cell structure during firing in order to, e.g., maintain the desired shape and flatness of the partial cell structure during firing, and/or to improve partial cell strength and sintering of particles and the electrolyte densification during firing. (It is understood that, in various embodiments of the invention, either or both of setter plates 200, 210 may actually be formed of multiple discrete, stacked plates, e.g., in order to provide the desired setter weight and/or thickness for a particular material to be fired; thus, a “setter plate” need not be, but may be, a single unitary plate.) In various embodiments, setter plate 210 (and, in various embodiments, both setter plates 200, 210) has a weight (selected by, e.g., adjusting the thickness of the setter plate; the amount by which the edge of the setter plate overhangs the cell structure, if any; the porosity of the setter plate; and/or the density (e.g., apparent density) of the setter plate) ranging from approximately 0.1 g/cm2 to approximately 5 g/cm2, defined relative to the greenbody (i.e., partial cell laminate) area; this represents the amount of loading applied to the cell structure during firing. In various embodiments, the weight ranges from approximately 0.25 g/cm2 to 3 g/cm2. In various embodiments, the amount by which the edge of the setter plate overhands the cell structure may range from approximately 0.01 cm to approximately 3 cm on each side of the greenbody. In various embodiments, the thickness of the setter plate 210 (and, in various embodiments, both setter plates 210) ranges from approximately 3 mm to approximately 16 mm. In accordance with embodiments of the present invention, at least setter plate 210 (and, in various embodiments, both setter plates 210) has a porosity ranging from approximately 25% to approximately 75%, ranging from approximately 55% to approximately 65%, or of approximately 60%. The porosity allows gas permeation during firing for evolved gas (e.g., polymer/organic burnout), and also enables the firing atmosphere to access the cell during firing. The material of the setter plates defining and between the porosity may be substantially fully (i.e., 100%) dense.
Setter pore size may range from approximately 0.001 mm to approximately 1 mm on average. Various embodiments have pore size that may range from approximately 0.001 mm to approximately 0.50 mm on average. Various embodiments have pore size that may range from approximately 0.001 mm to approximately 0.30 mm on average. Various other embodiments have pore sizes that range from approximately 0.005 mm to approximately 0.15 mm on average. Pores present in setter plates in accordance with embodiments of the present invention need not be spherical; therefore, the pores may have different sizes in different dimensions. For example, pore size may be different in the thickness dimension (the “z” dimension) than it is in the areal dimension (the “x-y” dimension). Setter particle size may range from approximately 0.001 mm to approximately 0.500 mm on average. Various embodiments have particle sizes that range from approximately 0.01 mm to approximately 0.15 mm. For the purpose of clarity, the particles may comprise crystallites and grains that are smaller than the particle itself. For the purpose of clarity, for solid phase densities less than 100% dense, there may be nano-sized porosity less than 0.001 mm.
In various embodiments of the invention, the setter plates 200, 210 have a curvature ranging from less than or equal to approximately 10 μm/cm to approximately 25 μm/cm, measured from center to edge. In various embodiments, the curvature is no greater than 10% different when measured in the x- or y-dimension (from any given edge), or from corner to corner over the setter plate. In various embodiments, the setter plates 200, 210 have a maximum-to-minimum height difference of less than or equal to approximately 100 μm, e.g., approximately 25 μm to approximately 50 μm, across the entire setter plate surface. In various other embodiments, the setter plates 200, 210 have a maximum-to-minimum height difference of less than or equal to approximately 50 μm, e.g., approximately 10 μm to approximately 30 μm, across the entire setter plate surface.
Setter plates 200, 210 may be fabricated in accordance with embodiments of the invention in any of a variety of different ways. For example, coated setter plates 200, 210 may feature an interior (or “core”) porous plate or layer that includes, consists essentially of, or consists of a ceramic material such as alumina, YSZ, silicon carbide, or other materials known to persons having ordinary skill in the art. For example, suitable alumina plates are available from commercial sources. The porous ceramic plate may be coated, at least on one surface, with the suitable coating material (as discussed herein) via, for example, a colloidal process or wet chemical deposition, in which a powder or other precursor of the coating material is mixed with agents such as a solvent (e.g., water, ethanol, texanol, terpineol), one or more surfactants (e.g., phosphate ester) or pH adjusters (e.g., acid), pore formers (e.g., PMMA microspheres), and/or a binder (e.g., cellulose), and the resulting slurry or paste applied to the ceramic plate via, e.g., dip coating, rolling, screen printing, spraying, or brushing. In other embodiments, the coating material may be applied by physical vapor deposition (e.g., sputtering from a sputtering target composed of the coating material) or atomic layer deposition or pulsed laser deposition. After coating, the coated plate may be annealed at a temperature of, e.g., approximately 500° C. or higher, or even approximately 1000° C. or higher. For example, the coated plate may be annealed at approximately 1300° C. for approximately 2 hours. Such anneal steps may not be required, depending upon the technique by which the coating is applied.
Setter plates 200, 210 that are entirely composed of the desired unreactive material may be formed by, for example, a wet process in which powders of the desired material are mixed with agents such as a solvent, a surfactant, pore formers, and/or a binder, and the resulting slurry cast into a mold or extruded into the proper shape for the setter. The resulting green (i.e., unfired) setter plate is allowed to dry and then fired at a temperature sufficient for sintering and the appropriate amount of densification to occur (e.g., approximately 1000° C. or higher). The extruded green shape may be a sheet that is prepared using, for instance, tape casting with (green tape) layers of up to approximately 0.250 to 1.2 mm. Multiple layers of the green tape may be laminated together using uniaxial and/or isostatic pressing (e.g., by cold isostatic pressing, warm isostatic pressing, or hot isostatic pressing). In other embodiments, such setter plates may be formed via a dry process in which powders of the desired material are mixed together (typically with binder and possibly other additives), placed in a mold, and then pressed uniaxially or isostatically. The resulting green (i.e., unfired) setter plate may then fired at a temperature sufficient for sintering and the appropriate amount of densification to occur (e.g., approximately 1000° C. or higher), unless sufficient heat was applied during the pressing step itself, in which case such firing may be omitted or curtailed. The coating may be alternately deposited by laminating a green tape of the coating material to the green tape(s) making up the core setter plate and subsequently annealing at high temperatures.
In various embodiments, the thickness, camber, and/or surface roughness of the setter plates may at least partially result from the specific fabrication processes prior to and through the completion of the annealing step(s) of the setter. In other embodiments, the thickness, camber, and/or surface roughness of the setter plates may result from a machining operation (e.g., surface grinding) to one or both surfaces of the setter plate.
In various embodiments, setter plates 200, 210 are fired during fabrication at a temperature greater than that utilized to fire the cell structure using the setter plates. Such thermal treatment may result in increased density of the setter plate 200, 210 and/or the coating thereon such that the setter plate or coating will not further sinter appreciably during firing of the cell structure. This may advantageously result in no crack formation and/or volumetric changes in the setter plates that might deleteriously impact the cell structure during firing thereof.
After firing, the fired partial cell structure including the electrolyte 120 and the anode 130 may be removed from the kiln or furnace, and the setter plates 200, 210. Additional steps may subsequently be performed to complete the fabrication of SOFC 100. For example, the cathode 110 may be applied as a suspension or paste (e.g., mixed with one or more liquid agents) via, e.g., drop coating, spin coating, spray coating, blade coating, or screen printing. The cathode 110 may then be allowed to dry and fired for densification. The cathode 110 may even be fired utilizing one or more setter plates in accordance with embodiments of the invention and described herein. For example, the cathode 110 may be formed on the SOFC 100 prior to firing, in such embodiments, the entire cell structure is co-fired in the same firing step. Alternatively, the cathode may be deposited using physical vapor deposition (e.g., sputtering from a sputtering target composed of the coating material) or atomic layer deposition or pulsed laser deposition. Before or after formation of the cathode 110, the SOFC 100 (or portion thereof) may be cut to a desired size by, for example, laser cutting, and/or may be polished. Electrical contact layers may be formed over SOFC 100 to enable electrical connections to the anode 130 and cathode 110. Any firing steps after the initial partial cell firing may also utilize one or more setter plates in accordance with embodiments of the invention and described herein.
Various different setter plates were utilized to fire a partial cell structure featuring an SFCM anode material in order to demonstrate advantages of setter plates in accordance with the present invention. In the first test, the SFCM material was fired at a temperature of 1300° C. for four hours using an uncoated commercially available alumina setter plate.
The SFCM material was a nominally 5 cm by 5 cm partial cell laminate (size is referenced to the final fired size) composed of different tape cast layers. The anode support layer (ASL) was a composite comprising a mixture of SFCM and gadolinium-doped cerium oxide (Ce0.9Gd0.1O1.95, GDC10) plus ˜2 mol % Co3O4 (the GDC10 and Co3O4 collectively referred to as Co-GDC), where the SFCM had the composition SrFe0.2Co0.4Mo0.4O3 (SFCM244 or simply SFCM). The ASL had 67 wt % SFCM and 33 wt % GDC10 (due to relatively small amount of cobalt oxide, this is essentially Co-GDC). The electrolyte comprised gadolinium-doped ceria and had the composition Ce0.9Gd0.1O1.95 (GDC10).
An ASL tape cast slurry was prepared by mixing, in a ball mill, various powders and other additives, including SFCM, GDC10, PMMA microspheres, cobalt oxide (Co3O4), binder, dispersant, and solvent. An electrolyte tape was prepared by mixing, in a ball mill, various powders and other additives, including GDC10, binder, dispersant, and solvent. The ASL tape thickness was around 200 μm to 250 μm, and the electrolyte tape was about 20 microns thick. The ASL and electrolyte tapes were cut to size with a razor blade, stacked, and laminated into a partial cell green laminate using a heated uniaxial press.
The first test setter was a new (virgin) uncoated setter and required no prior preparation. The partial cell green laminate was placed on the top surface of the first setter plate. A second setter plate was placed on top of the partial cell green laminate. The second setter was sized with an overhang of up to approximately 1.5 mm on each side, and with a weight between 0.9 g/cm2 and 1.2 g/cm2, both defined relative to the partial cell green laminate dimensions. The entire assembly was then placed inside a high-temperature kiln. The kiln temperature increased with at least a single burnout dwell around 400° C. for ˜1 hour before the temperature was ramped to 1300° C., dwelled for approximately 4 hours, and subsequently decreased to room temperature.
In the second test, the SFCM material was fired at a temperature of 1300° C. for four hours utilizing an alumina setter plate that had been coated with an SFCM layer and fired.
The SFCM material was a nominally 5 cm by 5 cm partial cell laminate (size is referenced to the final fired size) made up of different tape cast layers. The ASL was a composite comprising a mixture of SFCM and gadolinium-doped cerium oxide (Ce0.9Gd0.1O1.95, GDC10) plus 2 mol % Co3O4 (the GDC10 and Co3O4 collectively referred to as Co-GDC), where the SFCM had the composition SrFe0.2Co0.4Mo0.4O3 (SFCM244 or simply SFCM). The ASL had 67 wt % SFCM and 33 wt % GDC10 (due to relatively small amount of cobalt oxide, this is essentially Co-GDC). The electrolyte comprised gadolinium-doped ceria and had the composition Ce0.9Gd0.1O1.95 (GDC10).
An ASL tape cast slurry was prepared by mixing, in a ball mill, various powders and other additives, including SFCM, GDC10, PMMA microspheres, cobalt oxide (Co3O4), binder, dispersant, and solvent. An electrolyte tape was prepared by mixing, in a ball mill, various powders and other additives, including GDC10, binder, dispersant, and solvent. The ASL tape thickness was around 200 μm to 250 μm and the electrolyte tape thickness was about 20 microns. The ASL and electrolyte tapes were cut to size with a razor blade, stacked, and laminated into a partial cell green laminate using a heated uniaxial press.
The first setter plate for the second test was prepared by coating a new (virgin) alumina setter with a slurry paste of SFCM. The slurry was prepared by mixing SFCM powder, texanol-based vehicle, and ethanol in a ball mill and subsequently coating the setter with a roller. The film on the setter was then dried and fired at 1300° C. for 4 hours. The second setter plate was an uncoated, new (virgin) alumina setter plate. The second setter was sized with an overhang of up to approximately 1.5 mm on each side, and with a weight between 0.9 g/cm2 and 1.2 g/cm2, both defined relative to the partial cell green laminate dimensions. The partial cell green laminate was placed on the top surface of the first setter plate with the anode facing the first setter plate. The second setter plate was placed on top of the partial cell green laminate. The entire assembly was then placed inside a high temperature kiln. The kiln temperature increased with at least a single burnout dwell around 400° C. for ˜1 hour before the temperature was ramped to 1300° C., dwelled for approximately 4 hours, and was subsequently cooled to room temperature.
In the third test, the SFCM material was fired at a temperature of 1200° C.-1300° C. for four hours utilizing an alumina setter plate that had been coated with a Co3O4 layer and fired.
The SFCM material was a nominally 5 cm by 5 cm partial cell laminate (size is referenced to the final fired size) made up of different tape cast layers. The ASL was a composite comprising a mixture of SFCM and gadolinium-doped cerium oxide (Ce0.9Gd0.1O1.95, GDC10) plus ˜2 mol % Co3O4 (the GDC10 and Co3O4 collectively referred to as Co-GDC), where the SFCM had the composition SrFe0.2Co0.4Mo0.4O3 (SFCM244 or simply SFCM). The ASL had 67 wt % SFCM and 33 wt % GDC10 (due to relatively small amount of cobalt oxide, this is essentially Co-GDC). The electrolyte comprised gadolinium-doped ceria and had the composition Ce0.9Gd0.1O1.95 (GDC10).
An ASL tape cast slurry was prepared by mixing, in a ball mill, various powders and other additives, including SFCM, GDC10, PMMA microspheres, cobalt oxide (Co3O4), binder, dispersant, and solvent. An electrolyte tape was prepared by mixing, in a ball mill, various powders and other additives, including GDC10, binder, dispersant, and solvent. The ASL tape thickness was around 200 μm to 250 μm and the electrolyte tape was about 20 microns thick. The ASL and electrolyte tapes were cut to size with a razor blade, stacked, and laminated into a partial cell green laminate using a heated uniaxial press.
The first setter plate for the second test was prepared by coating a new (virgin) alumina setter with a slurry of Co3O4. The slurry was prepared by mixing Co3O4, texanol-based vehicle, and ethanol in a ball mill and subsequently coating the setter with a roller. The film on the setter was then dried and fired at 1300° C. for 4 hours. The second setter plate was an uncoated, new (virgin) alumina setter plate. The second setter was sized with an overhang of up to approximately 1.5 mm on each side, and with a weight between 0.9 g/cm2 and 1.2 g/cm2, both defined relative to the partial cell green laminate dimensions. The partial cell green laminate was placed on the top surface of the first setter plate with the anode facing the first setter plate. The second setter plate was placed on top of the partial cell green laminate. The entire assembly was then placed inside a high temperature kiln. The kiln temperature increased with at least a single burnout dwell around 400° C. for ˜1 hour before the temperature was ramped to 1200° C., dwelled for approximately 4 hours, and was subsequently cooled to room temperature. Using new (virgin) alumina setters and recoating the first setter plate, the same process was followed using a new partial cell green laminate but the sintering temperature was increased to 1300° C. Sintering at 1300° C. resulted in more reaction than 1200° C., but both cases were better than the first and second tests detailed above.
In the fourth test, an alumina setter was coated with GDC and utilized to fire SFCM materials at a temperature of 1000° C.-1300° C. for four hours. Even after multiple firings of different SFCM materials, the fired cell materials were easily removed from the setter without cracking or fracture.
The SFCM materials were a nominally 5×5 and a nominally 10×10 partial cell laminates (size is referenced to the final fired size) made up of different tape cast layers. The ASL was a composite comprising a mixture of SFCM and gadolinium-doped cerium oxide (Ce0.9Gd0.1O1.95, GDC10) plus ˜2 mol % Co3O4 (the GDC10 and Co3O4 collectively referred to as Co-GDC), where the SFCM had the composition SrFe0.2Co0.4Mo0.4O3 (SFCM244 or simply SFCM). The ASL had 67 wt % SFCM and 33 wt % GDC10 (due to relatively small amount of cobalt oxide, this is essentially Co-GDC). The electrolyte comprised gadolinium-doped ceria and had the composition Ce0.9Gd0.1O1.95 (GDC10).
An ASL tape cast slurry was prepared by mixing, in a ball mill, various powders and other additives, including SFCM, GDC10, PMMA microspheres, cobalt oxide (Co3O4), binder, dispersant, and solvent. An electrolyte tape was prepared by mixing, in a ball mill, various powders and other additives, including GDC10, binder, dispersant, and solvent. The ASL tape thickness was around 200 μm to 250 μm and the electrolyte tape was about 20 microns thick. The ASL and electrolyte tapes were cut to size with a razor blade, stacked, and laminated into a partial cell green laminate using a heated uniaxial press.
The first setter plate for the fourth test was prepared by coating a new (virgin) alumina setter with a slurry of GDC. The slurry was prepared by mixing GDC10, texanol-based vehicle, and ethanol in a ball mill and subsequently coating the setter with a roller. The film on the setter was then dried and fired at 1300° C. for 4 hours. The second setter plate was a new (virgin) alumina setter plate with a GDC10 coating on the side that came into contact with the electrolyte. The second setter was sized with an overhang of up to approximately 1.5 mm on each side, and with a weight between 0.9 g/cm2 and 1.2 g/cm2, both defined relative to the partial cell green laminate dimensions. Keyence microscope images showed the thickness of the GDC10 coating on the alumina setter was approximately 4-8 microns thick measured from the surface of the alumina setter to the top of the film. The GDC10 coating also penetrated into the porous surface of the alumina setter by an additional approximately 10 to 50 microns, coating the alumina particles within the pores of the setter. The partial cell green laminate was placed on the top surface of the first setter plate with the anode in contact with the GDC coating on the setter plate. The second setter plate was placed on top of the partial cell green laminate. The entire assembly was then placed inside a high temperature kiln. The kiln temperature increased with at least a single burnout dwell around 400° C. for ˜1 hour before the temperature ramped to 1000° C., dwelled for approximately 4 hours, and was subsequently cooled to room temperature. After the first firing at 1000° C., the same set of setter plates were used with the same firing process but with the sintering temperature increased for full firings at 1050° C., 1100° C., 1150° C., 1200° C., 1250° C., and 1300° C. using a new partial cell green laminate in each case. The fact that multiple partial cells were successfully fired in separate firings with the same set of GDC-coated setter plates and with no apparent degradation of the GDC coating on the setter plates demonstrates that this is a robust approach for manufacturing large-format, all-ceramic anode cells.
In the fifth test, a bulk ceria setter plate was fabricated by pressing a ceria powder and firing the pressed powder to a temperature greater than 1300° C. The ceria setter plate was subsequently utilized for the firing of SFCM cell materials at a temperature of 1300° C. for four hours. Even after multiple firings of different SFCM materials, the fired cell materials were easily removed from the setter without cracking or fracture, resulting in cells resembling those depicted in
The ceria setter was prepared by mixing binder and ceria powder and placing the mixture in a square die. The powder was subsequently compressed under high pressure using a uniaxial press. The green setter was then fired above 1300° C. for several hours to provide for sintering of the ceria particles.
Two types of SFCM materials were fired on the bulk ceria setter in the fifth test. The SFCM materials were a nominally 5 cm by 5 cm partial cell laminates (size is referenced to the final fired size) made up of different tape cast layers. The first SFCM material included pore formers, while the second material had no pore former added. The ASL of the first and second SFCM materials was a composite comprising a mixture of SFCM and gadolinium-doped cerium oxide (Ce0.9Gd0.1O1.95, GDC10) plus ˜2 mol % Co3O4 (the GDC10 and Co3O4 collectively referred to as Co-GDC), where the SFCM had the composition SrFe0.2Co0.4Mo0.4O3 (SFCM244 or simply SFCM). For the first and second SFCM materials, the ASL had 67 wt % SFCM and 33 wt % GDC10 (due to relatively small amount of cobalt oxide, this is essentially Co-GDC).
For the first and second SFCM materials, the ASL tape cast slurry was prepared by mixing, in a ball mill, various powders and other additives, including SFCM, GDC10, PMMA microspheres (omitted for second SFCM material), cobalt oxide (Co3O4), binder, dispersant, and solvent. An electrolyte tape was prepared by mixing, in a ball mill, various powders and other additives, including GDC10, binder, dispersant, and solvent. The ASL tape thickness was around 200 μm to 250 μm and the electrolyte tape was about 20 microns thick. The ASL and electrolyte tapes were cut to size with a razor blade, stacked, and laminated into a partial cell green laminate using a heated uniaxial press.
The partial cell green laminate was placed on the top surface of the first ceria setter plate. The second ceria setter plate was placed on top of the partial cell green laminate. The second setter was sized with an overhang of up to approximately 1.5 mm on each side, and with a weight between 0.9 g/cm2 and 1.2 g/cm2, both defined relative to the partial cell green laminate dimensions. The entire assembly was then placed inside a high temperature kiln. The kiln temperature increased with at least a single burnout dwell around 400° C. for ˜1 hour before the temperature was ramped to 1300° C., dwelled for approximately 4 hours, and was subsequently cooled to room temperature. None of the two SFCM materials stuck to the ceria setter.
In the sixth test, an alumina setter was coated with a mixture of gadolinium-doped cerium oxide (Ce0.9Gd0.1O1.95, GDC10) and ˜2 mol % Co3O4 (the GDC10 and Co3O4 collectively referred to as Co-GDC) and utilized to fire SFCM materials at a temperature of 1300° C. for four hours. Even after multiple firings of different SFCM materials, the fired cell materials were easily removed from the setter without cracking or fracture, resulting in cells resembling those depicted in
The SFCM material was a nominally 5 cm by 5 cm partial cell laminate (size is referenced to the final fired size) made up of different tape cast layers. The ASL was a composite comprising a mixture of SFCM and gadolinium-doped cerium oxide (Ce0.9Gd0.1O1.95, GDC10) plus ˜2 mol % Co3O4 (the GDC10 and Co3O4 collectively referred to as Co-GDC), where the SFCM had the composition SrFe0.2Co0.4Mo0.4O3 (SFCM244 or simply SFCM). The ASL had 67 wt % SFCM and 33 wt % GDC10 (due to relatively small amount of cobalt oxide, this is essentially Co-GDC). The electrolyte comprised gadolinium-doped ceria and had the composition Ce0.9Gd0.1O1.95 (GDC10).
An ASL tape cast slurry was prepared by mixing, in a ball mill, various powders and other additives, including SFCM, GDC10, PMMA microspheres, cobalt oxide (Co3O4), binder, dispersant, and solvent. An electrolyte tape was prepared by mixing, in a ball mill, various powders and other additives, including GDC10, binder, dispersant, and solvent. The ASL tape thickness was around 200 μm to 250 μm and the electrolyte tape was about 20 microns thick. The ASL and electrolyte tapes were cut to size with a razor blade, stacked, and laminated into a partial cell green laminate using a heated uniaxial press.
The first setter plate for the sixth test was prepared by coating a new (virgin) alumina setter with a slurry of Co3O4 and GDC. The slurry was prepared by mixing GDC, Co3O4, texanol-based vehicle, and ethanol on a ball mill and subsequently coating the setter with a roller. The film on the setter was then dried and fired at 1300° C. for 4 hours. The second setter plate was coated using the same technique. The second setter was sized with an overhang of up to approximately 1.5 mm on each side, and with a weight between 0.9 g/cm2 and 1.2 g/cm2, both defined relative to the partial cell green laminate dimensions. The partial cell green laminate was placed on the top surface of the first setter plate. The second setter plate was placed on top of the partial cell green laminate. The entire assembly was then placed inside a high temperature kiln. The kiln temperature increased with at least a single burnout dwell around 400° C. for ˜1 hour before the temperature ramped to 1300° C., dwelled for approximately 4 hours, and was subsequently cooled to room temperature. The fired cell material was flat and did not stick to the setter plates.
The terms and expressions employed herein are used as terms and expressions of description and not of limitation, and there is no intention, in the use of such terms and expressions, of excluding any equivalents of the features shown and described or portions thereof. In addition, having described certain embodiments of the invention, it will be apparent to those of ordinary skill in the art that other embodiments incorporating the concepts disclosed herein may be used without departing from the spirit and scope of the invention. Accordingly, the described embodiments are to be considered in all respects as only illustrative and not restrictive.
This invention was made with United States Government support under Contract No. DE-AR0000494 awarded by the Department of Energy Advanced Projects Research Agency-Energy (ARPA-E). The United States Government has certain rights in the invention.