Patent Grant
12077464
The present specification generally relates to methods and apparatus for ceramming glass sheets and, more particularly, to setters and parting agents for use in ceramming glass sheets.
Conventional ceram processes utilize ceramic and/or refractory materials as setters. However, such materials are incapable of producing a glass ceramic having an optical quality suitable for use in optical displays. Without being bound by theory, it is believed that the heat transfer and heat capacity limitations of the ceramic and/or refractory materials can warp or produce a skin effect on the glass ceramic.
Warp may also be introduced during the manufacturing process due to the stacking of the glass sheets. In particular, warping may result from the glass sheets in a stack sticking to the other glass sheets and/or the setter, thickness variations of the glass sheets throughout the stacks, and the load applied to the glass stack.
Accordingly, alternative methods and apparatus are needed that are suitable for use in producing glass ceramic sheets having a high optical quality and reduced warping.
According to one embodiment, a method of ceramming a plurality of glass sheets includes positioning the plurality of glass sheets in a stack between a first setter plate and a second setter plate in a glass stack configuration, and exposing the glass stack configuration to a ceramming cycle to ceram the plurality of glass sheets. The first setter plate and the second setter plate each have a specific heat capacity of from about 670 J/kg*K to about 850 J/kg*K, as measured in accordance with ASTM E1461 at room temperature; a bulk density of greater than about 2500 kg/m3, as measured in accordance with ASTM C20; or a thermal diffusivity of greater than about 2.50×10−5 m2/s.
According to another embodiment, a system for ceramming a plurality of glass sheets includes a carrier plate to support the plurality of glass sheets during a ceramming process and at least one setter plate supported by the carrier plate. The at least one setter plate includes reaction bonded silicon carbide and has a maximum flatness of less than or equal to about 100 μm.
Additional features and advantages will be set forth in the detailed description which follows, and in part will be readily apparent to those skilled in the art from that description or recognized by practicing the embodiments described herein, including the detailed description which follows, the claims, as well as the appended drawings.
It is to be understood that both the foregoing general description and the following detailed description describe various embodiments of printing compositions, methods of printing on substrates, and printed substrates and are intended to provide an overview or framework for understanding the nature and character of the claimed subject matter. The accompanying drawings are included to provide a further understanding of the various embodiments, and are incorporated into and constitute a part of this specification. The drawings illustrate the various embodiments described herein, and together with the description serve to explain the principles and operations of the claimed subject matter.
Reference will now be made in detail to various embodiments of methods and apparatus for forming glass ceramic articles having improved optical quality and reduced warping, examples of which are illustrated in the accompanying drawings. Whenever possible, the same reference numerals will be used throughout the drawings to refer to the same or like parts.
In general, described herein are glass stack configurations including a carrier plate, setter plates, and glass sheets for thermal treatment of the glass sheets to form glass ceramic articles. The glass stacking configurations and components described herein are selected to improve thermal uniformity throughout a glass stack during ceramming processes while maintaining or even reducing the stresses in the resultant glass ceramic article. Accordingly, the glass ceramic articles made according to the various embodiments described herein exhibit improved optical qualities and less warp than glass ceramic articles made according to conventional processes. Various embodiments of carrier plates, setter plates, parting agent compositions, and methods of stacking glass sheets will be described herein with specific reference to the appended drawings.
Directional terms as used herein—for example up, down, right, left, front, back, top, bottom, vertical, horizontal—are made only with reference to the figures as drawn and are not intended to imply absolute orientation unless otherwise expressly stated.
Unless otherwise expressly stated, it is in no way intended that any method set forth herein be construed as requiring that its steps be performed in a specific order, nor that with any apparatus specific orientations be required. Accordingly, where a method claim does not actually recite an order to be followed by its steps, or that any apparatus claim does not actually recite an order or orientation to individual components, or it is not otherwise specifically stated in the claims or description that the steps are to be limited to a specific order, or that a specific order or orientation to components of an apparatus is not recited, it is in no way intended that an order or orientation be inferred, in any respect. This holds for any possible non-express basis for interpretation, including: matters of logic with respect to arrangement of steps, operational flow, order of components, or orientation of components; plain meaning derived from grammatical organization or punctuation; and the number or type of embodiments described in the specification.
As used herein, the singular forms “a,” “an” and “the” include plural referents unless the context clearly dictates otherwise. Thus, for example, reference to “a” component includes aspects having two or more such components, unless the context clearly indicates otherwise.
In general, a process for forming a glass ceramic includes forming a glass article and ceramming the glass article to transform the glass article into a glass ceramic form. Referring to
In some embodiments, insulation layers (not shown) may be located on the top surface of the upper setter plate 104 and one the bottom surface of the lower setter plate 104. The insulation layers may be formed from any material having a low thermal conductivity, and can reduce or even eliminate axial temperature gradients of the glass sheets 108 on the top and bottom of the glass stack 106.
As shown in
Generally, to form the glass ceramic, the glass stack 106 is heated at a temperature above its annealing point for a time sufficient to develop crystal nuclei (also called a nucleation phase). The heat treatment can be performed, for example, in a lehr or furnace. After being heated above its annealing point, the glass is then further heated, usually at a higher temperature between the glass annealing point and the glass softening point, to develop the crystal phase (also called a crystallization phase). In various embodiments, the heat treatment, or ceramming process, includes heating the glass stack to a nucleation temperature, maintaining the nucleation temperature for a predetermined period of time, heating the glass stack to a crystallization temperature, and maintaining the crystallization temperature for a predetermined period of time. In some embodiments, the step of heating the glass stack to a nucleation temperature can include heating the glass stack to a nucleation temperature of about 700° C. at a rate of 1-10° C./min. The glass stack may be maintained at the nucleation temperature for a time of from about ¼ hour to about 4 hours. The step of heating the glass stack to the crystallization temperature can include heating the glass stack to a crystallization temperature of about 800° C. at a rate of 1-10° C./min. The glass stack may be maintained at the nucleation temperature for a time of from about ¼ hour to about 4 hours.
However, it is contemplated that other heat treatment schedules (including varying times and/or temperatures) can be used, depending on the particular embodiment. In particular, the temperature-temporal profile of heat treatment steps are selected to produce one or more of the following attributes: crystalline phase(s) of the glass ceramic, proportions of one or more major crystalline phases and/or one or more minor crystalline phases and residual glass, crystal phase assemblages of one or more predominate crystalline phase and/or one or more minor crystalline phases and residual glass, and grain sizes or grain size distributions among one or more major crystalline phases and/or one or more minor crystalline phases, which in turn may influence the final integrity, quality, color and/or opacity of the resultant glass ceramic article.
Following heating to the nucleation temperature and maintaining that temperature for the predetermined time, the glass stack is cooled back to room temperature. In various embodiments, the cooling rate is controlled down to a temperature of about 450° C., after which the glass ceramic article may be quenched without impacting the stress, as shown in
Having described the stack configuration 100 in general, additional detail will now be provided with regard to the components of the stack configuration 100.
Carrier Plate
In various embodiments, the carrier plate 102 supports two or more setter plates 104. The structure and material of the carrier plate 102 may be selected to control the thermal uniformity of the glass sheets loaded on top of it in the stack configuration 100. In some embodiments, the carrier plate 102 has an open carrier design (shown in
To evaluate the thermal impact of the carrier plate, a thermal model assuming production scale capacity with 9 stacks and 23 glass sheets in each stack on a carrier plate and 8 mm setter plates made from reaction bonded silicon carbide was run. As shown in the modeled data of
Accordingly, although various designs and materials may be employed for the carrier plate 102, in various embodiments, the carrier plate is made from steel and has an open grid design, as depicted in
Setter Plate
As shown in
While most conventional ceram processes utilize ceramic and refractory materials to form setter plates, such materials have heat transfer and heat capacity limitations which make them unsuitable for producing a high optical quality that is desired or required for certain applications. Additionally, setter plates made from such materials can experience thermal expansion, oxidation, and creep, which can in turn lead to warp in the glass ceramic article.
Moreover, the setter plates 104 binding the glass stack 106 provide a lateral heat transfer path to spread radiant heat from heating elements, which may lower the in-plane glass sheet temperature variations. Minimizing the temperature variations may in turn lead to a reduction in in-plane stresses and warp in the glass ceramic article. Accordingly, in various embodiments, the setter plates 104 are selected to maximize the reduction in glass sheet temperature variation. In particular, the setter plates 104 are selected to have a particular specific heat capacity, density, and thermal diffusivity.
According to various embodiments, the setter plates have a specific heat capacity (cp) of from about 670 J/kg*K to about 850 J/kg*K, as measured in accordance with ASTM E1461 at room temperature. For example, the setter plates may have a specific heat capacity of from about 670 J/kg*K to about 850 J/kg*K, from about 670 J/kg*K to about 800 J/kg*K, from about 670 J/kg*K to about 750 J/kg*K, or from about 670 J/kg*K to about 700 J/kg*K, as measured in accordance with ASTM E1461 at room temperature and all ranges and subranges therebetween. Without being bound by theory, it is believed that when the specific heat capacity is outside of this range, the material is not able to give up heat and accept heat at the appropriate rate which causes stress and warp in the glass in stacking configurations.
The setter plates in various embodiments additionally or alternatively may be selected to have a bulk density of greater than about 2500 kg/m3, as measured in accordance with ASTM C20. For example, the setter plates may have a bulk density of from about 2500 kg/m3 to about 4000 kg/m3, from about 2750 kg/m3 to about 3750 kg/m3, or from about 3000 kg/m3 to about 3500 kg/m3, as measured in accordance with ASTM C20 and all ranges and subranges therebetween. Without being bound by theory, it is believed that materials having bulk densities in this range have low porosity and do not significantly increase the weight in the stack. A bulk density that is too low can lead to material deterioration over time and decreased life use of the material, whereas a bulk density that is too high can lead to stress in the stack due to increased force on the glass.
Moreover, in various embodiments, the setter plates have a thermal diffusivity of greater than about 2.50×10−5 m2/s. For example, the setter plates may have a thermal diffusivity of from about 2.50×10−5 m2/s to about 5.50×10−4 m2/s, from about 3.0×10−5 m2/s to about 5.00×10−4 m2/s, from about 4.0×10−5 m2/s to about 4.50×10−4 m2/s, from about 4.50×10−5 m2/s to about 4.00×10−4 m2/s, from about 5.00×10−5 m2/s to about 3.50×10−4 m2/s, from about 5.50×10−5 m2/s to about 3.00×10−4 m2/s, from about 6.00×10−5 m2/s to about 2.50×10−4 m2/s, from about 6.50×10−5 m2/s to about 2.0×10−4 m2/s, from about 7.00×10−5 m2/s to about 2.00×10−4 m2/s, or from about 7.50×10−5 m2/s to about 1.50×10−4 m2/s and all ranges and subranges therebetween. Without being bound by theory, if the thermal diffusivity is too low, the material will take too long to heat up and cool down causing thermal gradients in the stack which will lead to stress and warp. However, if the thermal diffusivity is too high, it could also lead to stress due to imparting thermal gradients in the stack. Glass sheets in contact with the setter plates would be affected by heat transfer at different rates as opposed to the glass sheets in the center of the stack. Thermal diffusivity α can be defined according to the following equation:
where k is thermal conductivity (W/m*K), ρ is density (kg/m3), and cp is specific heat capacity (J/kg*K).
Accordingly, in various embodiments, the setter plates have a thermal conductivity (k) of greater than about 100 W/m-K, greater than about 125 W/m-K, greater than about 150 W/m-K, greater than about 175 W/m-K, or even greater than about 180 W/m-K, as measured in accordance with ASTM E1461 at room temperature. For example, the setter plate may have a thermal conductivity of from about 100 W/m-K to about 350 W/m-K, from about 125 W/m-K to about 325 W/m-K, from about 150 W/m-K to about 300 W/m-K, from about 175 W/m-K to about 275 W/m-K, or from about 180 W/m-K to about 250 W/m-K, as measured in accordance with ASTM E1461 at room temperature and all ranges and subranges therebetween. Without being bound by theory, thermal conductivity too high or too low can induce thermal gradients in the stack leading to stress and warp.
Various materials having the desired specific heat capacity, density, and thermal diffusivity may be suitable for use in forming the setter plates described herein. One example material that is particularly suitable for use is reaction bonded silicon carbide (SiSiC). In embodiments, the setter plate 104 may comprise from about 85 wt % to about 90 wt % reaction bonded silicon carbide. The setter plate 104 may further comprise from about 10 wt % to about 15 wt % silicon metal (Si) and binding agents. Commercially available reaction bonded silicon carbide products that may be suitable for use in forming the setter plate 104 can include, by way of example and not limitation, CRYSTAR RB™ available from Saint-Gobain Ceramic Materials.
To confirm the impact of the thermal properties of the material used to form the setter plates, three different materials were used to form setter plates having a thickness of 8 mm. In particular, Example A was formed from reaction bonded silicon carbide, Comparative Example 1 was formed using nitride bonded silicon carbide, and Comparative Example 2 was formed using silicon refractory board. The thermal properties of each of these materials are provided in Table 1.
The ΔT of the glass stack during heating ramp up was modeled. The results are shown in
In addition to decreasing the temperature variation in the glass stack, the setter plate 104 of various embodiments is made from a material that imparts lower stress as compared to conventional materials. For example, the thermal diffusivity of the reaction bonded silicon carbide imparts lower stress in the glass ceramic article following ceramming heat treatment as compared to conventional setter plate materials. As shown in
In various embodiments, the material used to form the setter plate 104 is further selected based on its lack of reactivity with both the carrier plate 102 and the glass ceramic article. Reaction bonded silicon carbide is an example material that demonstrates low or even no reaction with materials typically used to form the carrier plate 102. In particular, setter plates made from reaction bonded silicon carbide in contact with stainless steel alloy and Ni-based super alloy metal carrier plates were tested up to 800° C. in air for 24 hour and for 100 hours. As shown in
Moreover, Li-based glass ceramics in contact with reaction bonded silicon carbide material during a thermal ceramming process do not exhibit any skin effects, according to XRD phase assemblage characterization. For example, as shown in
In addition to having improved thermal properties over other materials, reaction bonded silicon carbide has a low porosity (<1%), which can increase the life of the setter plate during thermal cycling due to increased resistance to oxidation, cracking, and reactivity through diffusion with other elements and materials.
In various embodiments, the setter plate 104 is also dimensioned to reduce warp in the glass ceramic article. In particular, the thickness of the setter plate 104 and the flatness of the setter plate 104 are controlled to reduce both warp and stress in the glass ceramic.
During the ceramming process, the glass sheets 108 forming the glass stack 106, which is in contact with the setter plates 104, move and conform to the flatness of the setter plate 104. In various embodiments, the setter plate 104 may be machined to obtain a particular flatness after formation. As used herein, the term “flatness” refers to a tolerance zone defined by two parallel planes within which the surface lies. For example, a flatness of 100 μm means that the surface must lie entirely between two parallel planes that are at most 100 μm apart. The impact of the flatness of the setter plate 104 on the flatness of the glass ceramic article is shown in
In various embodiments, the setter plate 104 has a maximum flatness of less than or equal to about 100 μm, less than or equal to about 75 μm, less than or equal to about 50 μm, less than or equal to about 45 μm, less than or equal to about 40 μm, less than or equal to about 35 μm, less than or equal to about 30 μm, or even less than or equal to about 25 μm.
Flatness can be measured using a CMM and touch and/or non-touch probes. In various embodiments, the measurement density is 1 point/mm throughout the sweep trajectory and the measurement region is about 10 mm inbound from a side of the setter plate. The origin of alignment is at the center of the shorter edge, as shown in
The thickness t of the setter plate 104 (shown in
The density of the material used to form the setter plate 104 and the thickness of the setter plate 104 may further be selected based on the applied force on the glass stack 106.
Glass Sheets
The glass sheets 108 may be made from any glass composition that is suitable for forming glass ceramic articles, although it should be understood that the glass composition of the glass sheets 108 can impact the mechanical and optical properties of the glass ceramic article. In various embodiments, the glass composition is selected such that the resultant glass ceramic article has a petalite crystalline phase and a lithium silicate crystalline phase and wherein the petalite crystalline phase and the lithium silicate crystalline phase have higher weight percentages than other crystalline phases present in the glass ceramic article.
By way of example and not limitation, in various embodiments, the glass sheets 108 may be formed from a glass composition including from about 55 wt % to about 80 wt % SiO2, from about 2 wt % to about 20 wt % Al2O3, from about 5 wt % to about 20 wt % Li2O, from about 0 wt % to about 10 wt % B2O3, from about 0 wt % to about 5 wt % Na2O, from about 0 wt % to about 10 wt % ZnO, from about 0.5 wt % to about 6 wt % P2O5, and from about 0.2 wt % to about 15 wt % ZrO2.
SiO2, an oxide involved in the formation of glass, can function to stabilize the networking structure of glasses and glass ceramics. In various glass compositions, the concentration of SiO2 should be sufficiently high in order to form petalite crystal phase when the glass sheet is heat treated to convert to a glass ceramic. The amount of SiO2 may be limited to control the melting temperature of the glass, as the melting temperature of pure SiO2 or high-SiO2 glasses is undesirably high. In some embodiments, the glass or glass ceramic composition comprises from about 55 wt % to about 80 wt % SiO2. In some embodiments, the glass or glass ceramic composition comprises from about 69 wt % to about 80 wt % SiO2. In some embodiments, the glass or glass ceramic composition can comprise from about 55 wt % to about 80 wt %, about 55 wt % to about 77 wt %, about 55 wt % to about 75 wt %, about 55 wt % to about 73 wt %, about 60 wt % to about 80 wt %, about 60 wt % to about 77 wt %, about 60 wt % to about 75 wt %, about 60 wt % to about 73 wt %, about 69 wt % to about 80 wt %, about 69 wt % to about 77 wt %, about 69 wt % to about 75 wt %, about 69 wt % to about 73 wt %, about 70 wt % to about 80 wt %, about 70 wt % to about 77 wt %, about 70 wt % to about 75 wt %, about 70 wt % to about 73 wt %, about 73 wt % to about 80 wt %, about 73 wt % to about 77 wt %, about 73 wt % to about 75 wt %, about 75 wt % to about 80 wt %, about 75 wt % to about 77 wt %, or about 77 wt % to about 80 wt % SiO2.
Al2O3 may also provide stabilization to the network and also provides improved mechanical properties and chemical durability. If the amount of Al2O3 is too high, however, the fraction of lithium silicate crystals may be decreased, possibly to the extent that an interlocking structure cannot be formed. The amount of Al2O3 can be tailored to control viscosity. Further, if the amount of Al2O3 is too high, the viscosity of the melt is also generally increased. In some embodiments, the glass or glass ceramic composition can comprise from about 2 wt % to about 20 wt % Al2O3. In some embodiments, the glass or glass ceramic composition can comprise from about 6 wt % to about 9 wt % Al2O3. In some embodiments, the glass or glass ceramic composition can comprise from about 2 wt % to about 20 wt %, about 2 wt % to about 18 wt %, about 2 wt % to about 15 wt %, about 2 wt % to about 12 wt %, about 2 wt % to about 10 wt %, about 2 wt % to about 9 wt %, about 2 wt % to about 8 wt %, about 2 wt % to about 5 wt %, about 5 wt % to about 20 wt %, about 5 wt % to about 18 wt %, about 5 wt % to about 15 wt %, about 5 wt % to about 12 wt %, about 5 wt % to about 10 wt %, about 5 wt % to about 9 wt %, about 5 wt % to about 8 wt %, 6 wt % to about 20 wt %, about 6 wt % to about 18 wt %, about 6 wt % to about 15 wt %, about 6 wt % to about 12 wt %, about 6 wt % to about 10 wt %, about 6 wt % to about 9 wt %, 8 wt % to about 20 wt %, about 8 wt % to about 18 wt %, about 8 wt % to about 15 wt %, about 8 wt % to about 12 wt %, about 8 wt % to about 10 wt %, 10 wt % to about 20 wt %, about 10 wt % to about 18 wt %, about 10 wt % to about 15 wt %, about 10 wt % to about 12 wt %, about 12 wt % to about 20 wt %, about 12 wt % to about 18 wt %, or about 12 wt % to about 15 wt % Al2O3.
In the glass and glass ceramics herein, Li2O aids in forming both petalite and lithium silicate crystal phases. In fact, to obtain petalite and lithium silicate as the predominant crystal phases, it is desirable to have at least about 7 wt % Li2O in the composition. Additionally, it has been found that once Li2O gets too high (greater than about 15 wt %), the composition becomes very fluid. Accordingly, in some embodiments, the glass or glass ceramic composition can comprise from about 5 wt % to about 20 wt % Li2O. In other embodiments, the glass or glass ceramic composition can comprise from about 10 wt % to about 14 wt % Li2O. In some embodiments, the glass or glass ceramic composition can comprise from about 5 wt % to about 20 wt %, about 5 wt % to about 18 wt %, about 5 wt % to about 16 wt %, about 5 wt % to about 14 wt %, about 5 wt % to about 12 wt %, about 5 wt % to about 10 wt %, about 5 wt % to about 8 wt %, about 7 wt % to about 20 wt %, about 7 wt % to about 18 wt %, about 7 wt % to about 16 wt %, about 7 wt % to about 14 wt %, about 7 wt % to about 12 wt %, about 7 wt % to about 10 wt %, about 10 wt % to about 20 wt %, about 10 wt % to about 18 wt %, about 10 wt % to about 16 wt %, about 10 wt % to about 14 wt %, about 10 wt % to about 12 wt %, about 12 wt % to about 20 wt %, about 12 wt % to about 18 wt %, about 12 wt % to about 16 wt %, about 12 wt % to about 14 wt %, about 14 wt % to about 20 wt %, about 14 wt % to about 18 wt %, about 14 wt % to about 16 wt %, about 16 wt % to about 20 wt %, about 16 wt % to about 18 wt %, or about 18 wt % to about 20 wt % Li2O.
As noted above, Li2O is generally useful for forming various glass ceramics, but the other alkali oxides tend to decrease glass ceramic formation and form an aluminosilicate residual glass in the glass ceramic. It has been found that more than about 5 wt % Na2O or K2O, or combinations thereof, leads to an undesirable amount of residual glass, which can lead to deformation during crystallization and undesirable microstructures from a mechanical property perspective. The composition of the residual glass may be tailored to control viscosity during crystallization, minimizing deformation or undesirable thermal expansion, or control microstructure properties. Therefore, in general, the glass sheets may be made from glass compositions having low amounts of non-lithium alkali oxides. In some embodiments, the glass or glass ceramic composition can comprise from about 0 wt % to about 5 wt % R2O, wherein R is one or more of the alkali cations Na and K. In some embodiments, the glass or glass ceramic composition can comprise from about 1 wt % to about 3 wt % R2O, wherein R is one or more of the alkali cations Na and K. In some embodiments, the glass or glass ceramic composition can comprise from 0 wt % to about 5 wt %, 0 wt % to about 4 wt %, 0 wt % to about 3 wt %, 0 wt % to about 2 wt %, 0 wt % to about 1 wt %, >0 wt % to about 5 wt %, >0 wt % to about 4 wt %, >0 wt % to about 3 wt %, >0 wt % to about 2 wt %, >0 wt % to about 1 wt %, about 1 wt % to about 5 wt %, about 1 wt % to about 4 wt %, about 1 wt % to about 3 wt %, about 1 wt % to about 2 wt %, about 2 wt % to about 5 wt %, about 2 wt % to about 4 wt %, about 2 wt % to about 3 wt %, about 3 wt % to about 5 wt %, about 3 wt % to about 4 wt %, or about 4 wt % to about 5 wt % Na2O, K2O, or combinations thereof.
The glass and glass ceramic compositions can include P2O5. P2O5 can function as a nucleating agent to produce bulk nucleation. If the concentration of P2O5 is too low, the precursor glass does crystallize, but only at higher temperatures (due to a lower viscosity) and from the surface inward, yielding a weak and often deformed body. However, if the concentration of P2O5 is too high, the devitrification, upon cooling during the formation of the glass sheets, can be difficult to control. Embodiments can include from >0 wt % to about 6 wt % P2O5. Other embodiments can include from about 2 wt % to about 4 wt % P2O5. Still other embodiments can include from about 1.5 wt % to about 2.5 wt % P2O5. In some embodiments, the glass or glass ceramic composition can include from 0 wt % to about 6 wt %, 0 wt % to about 5.5 wt %, 0 wt % to 5 wt %, 0 wt % to about 4.5 wt %, 0 wt % to about 4 wt %, 0 wt % to about 3.5 wt %, 0 wt % to about 3 wt %, 0 wt % to about 2.5 wt %, 0 wt % to about 2 wt %, 0 wt % to about 1.5 wt %, 0 wt % to about 1 wt %, >0 wt % to about 6 wt %, >0 wt % to about 5.5 wt %, >0 wt % to 5 wt %, >0 wt % to about 4.5 wt %, >0 wt % to about 4 wt %, >0 wt % to about 3.5 wt %, >0 wt % to about 3 wt %, >0 wt % to about >2.5 wt %, 0 wt % to about 2 wt %, >0 wt % to about 1.5 wt %, >0 wt % to about 1 wt %, about 0.5 wt % to about 6 wt %, about 0.5 wt % to about 5.5 wt %, about 0.5 wt % to 5 wt %, about 0.5 wt % to about 4.5 wt %, about 0.5 wt % to about 4 wt %, about 0.5 wt % to about 3.5 wt %, about 0.5 wt % to about 3 wt %, about 0.5 wt % to about 2.5 wt %, about 0.5 wt % to about 2 wt %, about 0.5 wt % to about 1.5 wt %, about 0.5 wt % to about 1 wt %, about 1 wt % to about 6 wt %, about 1 wt % to about 5.5 wt %, about 1 wt % to 5 wt %, about 1 wt % to about 4.5 wt %, about 1 wt % to about 4 wt %, about 1 wt % to about 3.5 wt %, about 1 wt % to about 3 wt %, about 1 wt % to about 2.5 wt %, about 1 wt % to about 2 wt %, about 1 wt % to about 1.5 wt %, about 1.5 wt % to about 6 wt %, about 1.5 wt % to about 5.5 wt %, about 1.5 wt % to 5 wt %, about 1.5 wt % to about 4.5 wt %, about 1.5 wt % to about 4 wt %, about 1.5 wt % to about 3.5 wt %, about 1.5 wt % to about 3 wt %, about 1.5 wt % to about 2.5 wt %, about 1.5 wt % to about 2 wt %, about 2 wt % to about 6 wt %, about 2 wt % to about 5.5 wt %, about 2 wt % to 5 wt %, about 2 wt % to about 4.5 wt %, about 2 wt % to about 4 wt %, about 2 wt % to about 3.5 wt %, about 2 wt % to about 3 wt %, about 2 wt % to about 2.5 wt %, about 2.5 wt % to about 6 wt %, about 2.5 wt % to about 5.5 wt %, about 2.5 wt % to 5 wt %, about 2.5 wt % to about 4.5 wt %, about 2.5 wt % to about 4 wt %, about 2.5 wt % to about 3.5 wt %, about 2.5 wt % to about 3 wt %, about 3 wt % to about 6 wt %, about 3 wt % to about 5.5 wt %, about 3 wt % to 5 wt %, about 3 wt % to about 4.5 wt %, about 3 wt % to about 4 wt %, about 3 wt % to about 3.5 wt %, about 3.5 wt % to about 6 wt %, about 3.5 wt % to about 5.5 wt %, about 3.5 wt % to 5 wt %, about 3.5 wt % to about 4.5 wt %, about 3.5 wt % to about 4 wt %, about 4 wt % to about 6 wt %, about 4 wt % to about 5.5 wt %, about 4 wt % to 5 wt %, about 4 wt % to about 4.5 wt %, about 4.5 wt % to about 6 wt %, about 4.5 wt % to about 5.5 wt %, about 4.5 wt % to about 5 wt %, about 5 wt % to about 6 wt %, about 5 wt % to about 5.5 wt %, or about 5.5 wt % to about 6 wt % P2O5.
In various glass and glass ceramic compositions, it is generally found that ZrO2 can improve the stability of Li2O—Al2O3—SiO2—P2O5 glass by significantly reducing glass devitrification during forming and lowering liquidus temperature. At concentrations above 8 wt %, ZrSiO4 can form a primary liquidus phase at a high temperature, which significantly lowers liquidus viscosity. Transparent glasses can be formed when the glass contains over 2 wt % ZrO2. The addition of ZrO2 can also help decrease the petalite grain size, which aids in the formation of a transparent glass ceramic. In some embodiments, the glass or glass ceramic composition can comprise from about 0.2 wt % to about 15 wt % ZrO2. In some embodiments, the glass or glass ceramic composition can include from about 2 wt % to about 4 wt % ZrO2. In some embodiments, the glass or glass ceramic composition can comprise from about 0.2 wt % to about 15 wt %, about 0.2 wt % to about 12 wt %, about 0.2 wt % to about 10 wt %, about 0.2 wt % to about 8 wt %, about 0.2 wt % to about 6 wt %, about 0.2 wt % to about 4 wt %, about 0.5 wt % to about 15 wt %, about 0.5 wt % to about 12 wt %, about 0.5 wt % to about 10 wt %, about 0.5 wt % to about 8 wt %, about 0.5 wt % to about 6 wt %, about 0.5 wt % to about 4 wt %, about 1 wt % to about 15 wt %, about 1 wt % to about 12 wt %, about 1 wt % to about 10 wt %, about 1 wt % to about 8 wt %, about 1 wt % to about 6 wt %, about 1 wt % to about 4 wt %, about 2 wt % to about 15 wt %, about 2 wt % to about 12 wt %, about 2 wt % to about 10 wt %, about 2 wt % to about 8 wt %, about 2 wt % to about 6 wt %, about 2 wt % to about 4 wt %, about 3 wt % to about 15 wt %, about 3 wt % to about 12 wt %, about 3 wt % to about 10 wt %, about 3 wt % to about 8 wt %, about 3 wt % to about 6 wt %, about 3 wt % to about 4 wt %, about 4 wt % to about 15 wt %, about 4 wt % to about 12 wt %, about 4 wt % to about 10 wt %, about 4 wt % to about 8 wt %, about 4 wt % to about 6 wt %, about 8 wt % to about 15 wt %, about 8 wt % to about 12 wt %, about 8 wt % to about 10 wt %, about 10 wt % to about 15 wt %, about 10 wt % to about 12 wt %, or about 12 wt % to about 15 wt % ZrO2.
B2O3 is conducive to providing a glass sheet with a low melting temperature. Furthermore, the addition of B2O3 in the glass sheet and thus the glass ceramic article helps achieve an interlocking crystal microstructure and can also improve the damage resistance of the glass ceramic article. When boron in the residual glass is not charge balanced by alkali oxides or divalent cation oxides, it will be in trigonal-coordination state (or three-coordinated boron), which opens up the structure of the glass. The network around these three coordinated boron is not as rigid as tetrahedrally coordinated (or four-coordinated) boron. Without being bound by theory, it is believed that glass sheets and glass ceramics that include three-coordinated boron can tolerate some degree of deformation before crack formation. By tolerating some deformation, the Vickers indentation crack initiation values are increased. Fracture toughness of the glass sheets and glass ceramics that include three-coordinated boron may also be increased. Without being bound by theory, it is believed that the presence of boron in the residual glass of the glass ceramic (and glass sheet) lowers the viscosity of the residual glass (or glass sheet), which facilitates the growth of lithium silicate crystals, especially large crystals having a high aspect ratio. A greater amount of three-coordinated boron (in relation to four-coordinated boron) is believed to result in glass ceramics that exhibit a greater Vickers indentation crack imitation load. In some embodiments, the amount of three-coordinated boron (as a percent of total B2O3) may be about 40% or greater, 50% or greater, 75% or greater, 85% or greater, or even 95% or greater. The amount of boron in general should be controlled to maintain chemical durability and mechanical strength of the cerammed bulk glass ceramic.
In one or more embodiments, the glass or glass ceramic composition comprises from 0 wt % to about 10 wt % or from 0 wt % to about 2 wt % B2O3. In some embodiments, the glass or glass ceramic composition can comprise from 0 wt % to about 10 wt %, 0 wt % to about 9 wt %, 0 wt % to about 8 wt %, 0 wt % to about 7 wt %, 0 wt % to about 6 wt %, 0 wt % to about 5 wt %, 0 wt % to about 4 wt %, 0 wt % to about 3 wt %, 0 wt % to about 2 wt %, 0 wt % to about 1 wt %, >0 wt % to about 10 wt %, >0 wt % to about 9 wt %, >0 wt % to about 8 wt %, >0 wt % to about 7 wt %, >0 wt % to about 6 wt %, >0 wt % to about 5 wt %, >0 wt % to about 4 wt %, >0 wt % to about 3 wt %, >0 wt % to about 2 wt %, >0 wt % to about 1 wt %, about 1 wt % to about 10 wt %, about 1 wt % to about 8 wt %, about 1 wt % to about 6 wt %, about 1 wt % to about 5 wt %, about 1 wt % to about 4 wt %, about 1 wt % to about 2 wt %, about 2 wt % to about 10 wt %, about 2 wt % to about 8 wt %, about 2 wt % to about 6 wt %, about 2 wt % to about 4 wt %, about 3 wt % to about 10 wt %, about 3 wt % to about 8 wt %, about 3 wt % to about 6 wt %, about 3 wt % to about 4 wt %, about 4 wt % to about 5 wt %, about 5 wt % to about 8 wt %, about 5 wt % to about 7.5 wt %, about 5 wt % to about 6 wt %, or about 5 wt % to about 5.5 wt % B2O3.
MgO can enter petalite crystals in a partial solid solution. In one or more embodiments, the glass or glass ceramic composition can comprise from 0 wt % to about 8 wt % MgO. In some embodiments, the glass or glass ceramic composition can comprise from 0 wt % to about 8 wt %, 0 wt % to about 7 wt %, 0 wt % to about 6 wt %, 0 wt % to about 5 wt %, 0 wt % to about 4 wt %, 0 wt % to about 3 wt %, 0 wt % to about 2 wt %, 0 wt % to about 1 wt %, about 1 wt % to about 8 wt %, about 1 wt % to about 7 wt %, about 1 wt % to about 6 wt %, about 1 wt % to about 5 wt %, about 1 wt % to about 4 wt %, about 1 wt % to about 3 wt %, about 1 wt % to about 2 wt %, about 2 wt % to about 8 wt %, about 2 wt % to about 7 wt %, about 2 wt % to about 6 wt %, about 2 wt % to about 5 wt %, about 2 wt % to about 4 wt %, about 2 wt % to about 3 wt %, about 3 wt % to about 8 wt %, about 3 wt % to about 7 wt %, about 3 wt % to about 6 wt %, about 3 wt % to about 5 wt %, about 3 wt % to about 4 wt %, about 4 wt % to about 8 wt %, about 4 wt % to about 7 wt %, about 4 wt % to about 6 wt %, about 4 wt % to about 5 wt %, about 5 wt % to about 8 wt %, about 5 wt % to about 7 wt %, about 5 wt % to about 6 wt %, about 6 wt % to about 8 wt %, about 6 wt % to about 7 wt %, or about 7 wt % to about 8 wt % MgO.
ZnO can enter petalite crystals in a partial solid solution. In one or more embodiments, the glass or glass ceramic composition can comprise from 0 wt % to about 10 wt % ZnO. In some embodiments, the glass or glass ceramic composition can comprise from 0 wt % to about 10 wt %, 0 wt % to about 9 wt %, 0 wt % to about 8 wt %, 0 wt % to about 7 wt %, 0 wt % to about 6 wt %, 0 wt % to about 5 wt %, 0 wt % to about 4 wt %, 0 wt % to about 3 wt %, 0 wt % to about 2 wt %, 0 wt % to about 1 wt %, about 1 wt % to about 10 wt %, about 1 wt % to about 9 wt %, about 1 wt % to about 8 wt %, about 1 wt % to about 7 wt %, about 1 wt % to about 6 wt %, about 1 wt % to about 5 wt %, about 1 wt % to about 4 wt %, about 1 wt % to about 3 wt %, about 1 wt % to about 2 wt %, about 2 wt % to about 10 wt %, about 2 wt % to about 9 wt %, about 2 wt % to about 8 wt %, about 2 wt % to about 7 wt %, about 2 wt % to about 6 wt %, about 2 wt % to about 5 wt %, about 2 wt % to about 4 wt %, about 2 wt % to about 3 wt %, about 3 wt % to about 10 wt %, about 3 wt % to about 9 wt %, about 3 wt % to about 8 wt %, about 3 wt % to about 7 wt %, about 3 wt % to about 6 wt %, about 3 wt % to about 5 wt %, about 3 wt % to about 4 wt %, about 4 wt % to about 10 wt %, about 4 wt % to about 9 wt %, about 4 wt % to about 8 wt %, about 4 wt % to about 7 wt %, about 4 wt % to about 6 wt %, about 4 wt % to about 5 wt %, about 5 wt % to about 10 wt %, about 5 wt % to about 9 wt %, about 5 wt % to about 8 wt %, about 5 wt % to about 7 wt %, about 5 wt % to about 6 wt %, about 6 wt % to about 10 wt %, about 6 wt % to about 9 wt %, about 6 wt % to about 8 wt %, about 6 wt % to about 7 wt %, about 7 wt % to about 10 wt %, about 7 wt % to about 9 wt %, about 7 wt % to about 8 wt %, about 8 wt % to about 10 wt %, about 8 wt % to about 9 wt %, or about 9 wt % to about 10 wt % ZnO.
In various embodiments, the glass or glass ceramic composition may further include one or more constituents, such as, by way of example and not limitation, TiO2, CeO2, and SnO2. Additionally or alternatively, antimicrobial components may be added to the glass or glass ceramic composition. Antimicrobial components that may be added to the glass or glass ceramic may include, but are not limited to, Ag, AgO, Cu, CuO, Cu2O, and the like. In some embodiments, the glass or glass ceramic composition may further include a chemical fining agent. Such fining agents include, but are not limited to, SnO2, As2O3, Sb2O3, F, Cl, and Br. Additional details on glass and/or glass ceramic compositions suitable for use in various embodiments may be found in, for example, U.S. Patent Application Publication No. 2016/0102010 entitled “High Strength Glass-Ceramics Having Petalite and Lithium Silicate Structures,” filed Oct. 8, 2015, which is incorporated by reference herein in its entirety.
In various embodiments, the glass compositions can be manufactured into sheets via processes, including but not limited to, slot draw, float, rolling, and other sheet-forming processes known to those skilled in the art.
According to various embodiments herein, the thickness uniformity of the glass sheets 108 is controlled to decrease the warp of the glass ceramic article. In
In various embodiments, the edge bead may be removed from glass sheets to decrease the amount of warp observed in the glass ceramic article. It is believed that the edge beads have higher thickness non-uniformity and therefore contribute to warp during the ceramming process. In particular, in embodiments in which a single sheet of glass is subjected to the ceramming process (e.g., not incorporated into a glass stack), the removal of the edge bead can reduce warp in the glass sheet. As shown in
In various embodiments, part size is also taken into account to control warp and stress in the glass ceramic article. As shown in
Accordingly, in various embodiments, the thickness variation of the glass sheets can be controlled individually and throughout the glass stack, such as by edge bead removal and lapping, to reduce the warp and stress imparted to the glass ceramic article.
Parting Agent Layer
As described hereinabove, in various embodiments, a parting agent layer 110 is deposited between adjacent glass sheets 108 in the glass stack 106. In some embodiments, a parting agent layer 110 may also be deposited between the setter plate 104 and the glass stack 106. For example, a parting agent layer 110 may be coated onto the setter plate 104, or may be deposited on the surface of the glass sheet 108 at the top and/or bottom of the glass stack 106.
In various embodiments, the parting agent layer 110 is formed from a parting agent composition which comprises an aqueous dispersion including boron nitride and a colloidal inorganic binding agent. In embodiments, the parting agent composition is substantially free of volatile organic solvents. Accordingly, processes employing the parting agent composition may generate less hazardous waste than conventional processes using alcohol-based products.
According to various embodiments, the parting agent composition includes boron nitride as a lubricant. The use of boron nitride enables the parting agent composition to be used in high temperatures (e.g., >500° C.) applications, which may not be possible with alternative lubricants. Additionally, boron nitride may be particularly well-suited for use as a lubricant in various embodiments because it maintains its lubrication properties throughout the ceramming process. In the parting agent composition of various embodiments, the boron nitride is present in the form of agglomerated particles having an average particle size of from about 2 μm to about 4 μm. Although the particle size may vary depending on the particular embodiment employed, the particle size generally should not exceed about 4 μm to reduce surface roughness and enable the formation of ultra-thin (e.g., 2 gsm dry weight) coating layers.
As described above, the parting agent composition further includes a colloidal inorganic binding agent. The colloidal inorganic binding agent may include, by way of example and not limitation, aluminum oxide (AlOX). Other colloidal inorganic binding agents may be used, provided that they do not fully decompose during the heat treatment (e.g., ceramming) process.
In some embodiments, the parting agent composition may optionally include one or more dispersants or other additives. For example, antimicrobial additives may be employed. Suitable dispersants include nitric acid or other dispersants known and used in the art. However, in other embodiments, the parting agent composition may be substantially free of additional components in order to reduce the likelihood of reaction between the parting agent layer 110 and the glass sheets 108 and/or the setter plate 104.
The parting agent composition has a specific gravity of from about 1.0 to about 1.2 as measured using a syringe to pull off a predetermined volume of the parting agent composition and weighing that volume. Specifically, to measure the specific gravity, a 20 mL syringe is used to pull about 10 mL of the parting agent composition into the syringe and pushed back out to evacuate bubbles. The syringe is then wiped clean, placed on a scale, and the scale is zeroed out. Then, exactly 20 mL of the parting agent composition is pulled into the syringe, the syringe is wiped clean, and placed on the scale to get the weight in grams in the syringe. The weight is then divided by 20 to get the specific gravity.
Additionally or alternatively, in various embodiments, the parting agent composition has a viscosity of from about 120 centipoise (cP) to about 160 cP as measured on a Brookfield DV2TLV Viscometer, four spindle and all ranges and subranges therebetween. Although the viscosity may vary depending on the particular embodiment, a viscosity greater than 160 cP or less than 120 cP may adversely impact the application of the composition to the glass sheets, and may result in an uneven parting agent layer.
In various embodiments, the parting agent composition has a pH of from about 3 to about 5 and all ranges and subranges therebetween. In particular, when the parting agent composition has a pH in this range, the composition is compatible with application to the surface of the glass sheet without concern for pitting or etching the surface. Suitable commercially available parting agents include those available from Zyp Coatings (Tennessee).
As described above, the parting agent composition may be applied to one or more surfaces of the glass sheets 108 and/or the setter plates 104 to form a parting agent layer 110. In various embodiments, the parting agent composition is applied via a spray dispersion technique, such as rotary atomization and/or air assisted spray dispersion. Without being bound by theory, it is believed that other application techniques, including but not limited to roller coating, dipping, and ultrasonic powder application, are unable to achieve the desired layer thickness and uniformity desired by various embodiments. Accordingly, in various embodiments, the parting agent composition is dried to form a parting agent layer 110 having a dry coat weight of from about 2 gsm to about 6 gsm and all ranges and subranges therebetween. Although the thickness of the parting agent layer 110 can vary depending on the particular embodiment, it is generally expected that dry coat weights of less than about 2 gsm may have an increased risk of sticking. Additionally, in various embodiments, the parting agent layer 110 has a substantially uniform distribution on the surface of the glass sheet 108 and/or the setter plate 104.
In embodiments described herein, coating uniformity was characterized by percent haze and percent transmittance using a BYK Haze-Gard Plus instrument from the Paul N. Gardner Company, Inc. in accordance with ASTM D 1003 (for transmission) and ASTM D 1044 (for haze). The Haze-Gard Plus is capable of directly determining total transmittance, haze and clarity. The instrument utilizes an Illuminant C light source representing average day light with a correlated color temperature of 6774 K. In various embodiments, the cerammed glass sheet 100 having a parting agent layer 110 on one surface thereof has a percent transmission of from about 76% to about 83% as measured in accordance with ASTM D1003 and a percent haze of from about 25% to about 38% as measured in accordance with ASTM D1044.
In various embodiments, glass ceramic articles including the parting agent layer 110 exhibit less warp than glass ceramic articles formed without the parting agent layer 110. In other words, in addition to reducing the sticking between a glass sheet 108 and an adjacent glass sheet 108 and/or the setter plate 104, the parting agent layer 110 can reduce warp in the final glass ceramic article. Without being bound by theory, it is believed that application of a parting agent layer 110 as described herein can prevent localized sticking which contributes to warp in the glass ceramic article. In particular, during the ceramming process, the glass experiences shrinkage during phase change and crystal growth and the presence of the parting agent layer 110 allows the glass to move freely without constraint in the glass stack 106.
In addition to decreasing the warp of the glass ceramic article, the parting agent layer 110 of various embodiments described herein has been found to leave the phase assemblage of the glass ceramic article unchanged.
Thus, in various embodiments, the parting agent layer 110 can reduce CTE mismatch between the glass sheets 108 and the setter plate 104, reduce scuffing, and extend the life of the setter plates 104 by reducing wear. For example, it is believed that the CTE mismatch between the glass sheets 108 and the setter plate 104 can lead to scuffing if the glass sheets 108 stick to the setter plate 104. However, various embodiments of the parting agent composition, and particularly the colloidal binder, do not fully decompose during the thermal process. Accordingly, parting agent composition can be used to coat the setter plate 104 for multiple uses (e.g., greater than about 25 cycles) before the setter plate 104 needs to be re-coated. Therefore, in various embodiments, the parting agent layer 110, when applied in as an ultra-thin and uniform layer, prevents sticking in high temperature glass-glass stacking configurations, which can, in turn, reduce warp of a final glass ceramic article.
Glass Stack Configuration
In various embodiments described herein, multiple glass sheets 108 are arranged in a glass stack 106 for the ceramming process. In addition to the variables described above as impacting the warp and stress of the final glass ceramic article, it was further discovered that various elements of the glass stacking configuration have an impact on the warp and stress of the glass ceramic article.
Accordingly, in various embodiments, interlayer setter plates 112 may be placed within the glass stack 106, as shown in
Additionally, the inclusion of interlayer setter plates 112 reduces the warp and does not significantly impact the stress in the glass ceramic article, as shown in
In addition to including interlayer setter plates 112 within the glass stack 106, warp and stress in the glass ceramic article may further be controlled or reduced by limiting the number of glass sheets incorporated in the glass stack. For example, in some embodiments, the glass stack can be from 6 to 24 glass sheets, or from 10 to 20 glass sheets from setter plate 104 to setter plate 104. In embodiments in which interlayer setter plates are disposed within the glass stack, the number of glass sheets between each interlayer setter plate may be from 5 glass sheets to 15 glass sheets, or from 6 glass sheets to 10 glass sheets.
Accordingly, various embodiments described herein may be employed to produce glass ceramic articles having excellent optical quality and reduced warp while not adversely impacting, or even improving, stress in the glass ceramic articles as compared to glass articles cerammed according to conventional techniques. Such glass ceramic articles may be particularly well-suited for use in portable electronic devices due to their strength performance and high transmission values.
It will be apparent to those skilled in the art that various modifications and variations can be made to the embodiments described herein without departing from the spirit and scope of the claimed subject matter. Thus it is intended that the specification cover the modifications and variations of the various embodiments described herein provided such modification and variations come within the scope of the appended claims and their equivalents. For example, the various features may be combined as per the non-exhaustive list of embodiments set forth below.
This application is a national stage entry of International Patent Application Serial No. PCT/US2019/040568, filed on Jul. 3, 2019, which in turn, claims the benefit of priority under 35 U.S.C. § 119 of U.S. Provisional Application Ser. No. 62/698,582 filed on Jul. 16, 2018 and U.S. Provisional Application Ser. No. 62/749,808 filed on Oct. 24, 2018, the contents of each of which are relied upon and incorporated herein by reference in their entireties.
| Filing Document | Filing Date | Country | Kind |
|---|---|---|---|
| PCT/US2019/040568 | 7/3/2019 | WO |
| Publishing Document | Publishing Date | Country | Kind |
|---|---|---|---|
| WO2020/018290 | 1/23/2020 | WO | A |
| Number | Name | Date | Kind |
|---|---|---|---|
| 2920971 | Stookey | Jan 1960 | A |
| 3129087 | Hagy | Apr 1964 | A |
| 3617317 | Sack et al. | Nov 1971 | A |
| 3809543 | Gaskell et al. | May 1974 | A |
| 3809599 | Pei | May 1974 | A |
| 3817732 | Pei | Jun 1974 | A |
| 3931438 | Beall et al. | Jan 1976 | A |
| 3972704 | Loxley et al. | Aug 1976 | A |
| 4042362 | MacDowell et al. | Aug 1977 | A |
| 4191583 | Armistead et al. | Mar 1980 | A |
| 4219344 | Armistead et al. | Aug 1980 | A |
| 4222760 | Chyung et al. | Sep 1980 | A |
| 4248925 | Ambrogi | Feb 1981 | A |
| 4274857 | Wolfe | Jun 1981 | A |
| 4391914 | Beall | Jul 1983 | A |
| 4786305 | Ball et al. | Nov 1988 | A |
| 4910638 | Berghout et al. | Mar 1990 | A |
| 4940674 | Beall et al. | Jul 1990 | A |
| 5030433 | Mehrotra | Jul 1991 | A |
| 5073181 | Foster et al. | Dec 1991 | A |
| 5082710 | Wright | Jan 1992 | A |
| 5147436 | Blakeslee et al. | Sep 1992 | A |
| 5168193 | Hoegler | Dec 1992 | A |
| 5296294 | Suzuki et al. | Mar 1994 | A |
| 5389582 | Loxley et al. | Feb 1995 | A |
| 5588979 | Miyazaki et al. | Dec 1996 | A |
| 5603147 | Bischoff et al. | Feb 1997 | A |
| 5680685 | Bischoff | Oct 1997 | A |
| 5788731 | Suzuki | Aug 1998 | A |
| 5814262 | Ketcham et al. | Sep 1998 | A |
| 5836760 | Turner et al. | Nov 1998 | A |
| 5840221 | Lau et al. | Nov 1998 | A |
| 5872069 | Abe | Feb 1999 | A |
| 6055151 | Tormey et al. | Apr 2000 | A |
| 6374640 | Fotheringham et al. | Apr 2002 | B1 |
| 6408813 | Wilksch et al. | Jun 2002 | B1 |
| 6409813 | Beesabathina et al. | Jun 2002 | B1 |
| 6410892 | Perschl et al. | Jun 2002 | B1 |
| 6852569 | Nakano et al. | Feb 2005 | B2 |
| 7054136 | Ritter et al. | May 2006 | B2 |
| 7125320 | Brown et al. | Oct 2006 | B1 |
| 7312154 | Cites et al. | Dec 2007 | B2 |
| 7410716 | Garner et al. | Aug 2008 | B2 |
| 7589038 | Goto et al. | Sep 2009 | B2 |
| 7618843 | Nakano et al. | Nov 2009 | B2 |
| 8854623 | Fontaine et al. | Oct 2014 | B2 |
| 9126859 | Nakane et al. | Sep 2015 | B2 |
| 9156726 | Katayama et al. | Oct 2015 | B2 |
| 9260337 | Abramov et al. | Feb 2016 | B2 |
| 9260342 | Borczuch-Laczka et al. | Feb 2016 | B2 |
| 9382603 | Kimura et al. | Jul 2016 | B2 |
| 9604871 | Amin et al. | Mar 2017 | B2 |
| 9701569 | Demartino et al. | Jul 2017 | B2 |
| 9809488 | Beall et al. | Nov 2017 | B2 |
| 10046542 | Adib et al. | Aug 2018 | B2 |
| 20010022705 | Mori et al. | Sep 2001 | A1 |
| 20030100146 | Nakano et al. | May 2003 | A1 |
| 20040053039 | Ekstrom et al. | Mar 2004 | A1 |
| 20040149368 | Wang et al. | Aug 2004 | A1 |
| 20050016214 | Hsu et al. | Jan 2005 | A1 |
| 20050095404 | Schillert et al. | May 2005 | A1 |
| 20050199331 | Nakano et al. | Sep 2005 | A1 |
| 20060026994 | Yoshizawa | Feb 2006 | A1 |
| 20060068112 | Chapman et al. | Mar 2006 | A1 |
| 20060093884 | Seabaugh et al. | May 2006 | A1 |
| 20060185335 | Ichikawa | Aug 2006 | A1 |
| 20070051301 | Hirooka | Mar 2007 | A1 |
| 20070154666 | Coonan et al. | Jul 2007 | A1 |
| 20070199348 | Gudgel et al. | Aug 2007 | A1 |
| 20080041107 | Hsu et al. | Feb 2008 | A1 |
| 20080248316 | Goto et al. | Oct 2008 | A1 |
| 20090162608 | Yagi et al. | Jun 2009 | A1 |
| 20090186489 | Nakamura et al. | Jul 2009 | A1 |
| 20090323157 | Valentin et al. | Dec 2009 | A1 |
| 20100069218 | Baldi et al. | Mar 2010 | A1 |
| 20100116413 | Tanaka et al. | May 2010 | A1 |
| 20100304953 | Liu et al. | Dec 2010 | A1 |
| 20110009254 | Schweiger et al. | Jan 2011 | A1 |
| 20110092353 | Amin et al. | Apr 2011 | A1 |
| 20110135964 | Yagi et al. | Jun 2011 | A1 |
| 20110186431 | Horisaka et al. | Aug 2011 | A1 |
| 20110189440 | Appleby et al. | Aug 2011 | A1 |
| 20110198785 | Kester et al. | Aug 2011 | A1 |
| 20120094079 | Gabel et al. | Apr 2012 | A1 |
| 20120196735 | Bogaerts et al. | Aug 2012 | A1 |
| 20120291493 | Hsu et al. | Nov 2012 | A1 |
| 20130164509 | Siebers et al. | Jun 2013 | A1 |
| 20130277613 | Miyagawa et al. | Oct 2013 | A1 |
| 20130338267 | Appleby et al. | Dec 2013 | A1 |
| 20140050659 | Rimer et al. | Feb 2014 | A1 |
| 20140066285 | Beall et al. | Mar 2014 | A1 |
| 20140124777 | Nakatani et al. | May 2014 | A1 |
| 20140134397 | Amin et al. | May 2014 | A1 |
| 20140141285 | Momono et al. | May 2014 | A1 |
| 20140141960 | Borczuch-Laczka et al. | May 2014 | A1 |
| 20140309793 | Cheng et al. | Oct 2014 | A1 |
| 20140345328 | Folgar | Nov 2014 | A1 |
| 20150064474 | Dejneka et al. | Mar 2015 | A1 |
| 20150086794 | Akita et al. | Mar 2015 | A1 |
| 20150099124 | Beunet et al. | Apr 2015 | A1 |
| 20150113801 | Cao et al. | Apr 2015 | A1 |
| 20150140274 | Burke et al. | May 2015 | A1 |
| 20150140513 | Burke et al. | May 2015 | A1 |
| 20150210029 | Makino et al. | Jul 2015 | A1 |
| 20150239772 | Baker et al. | Aug 2015 | A1 |
| 20150265975 | Liu et al. | Sep 2015 | A1 |
| 20150274581 | Beall et al. | Oct 2015 | A1 |
| 20150274602 | Ishii et al. | Oct 2015 | A1 |
| 20150291468 | Boek et al. | Oct 2015 | A1 |
| 20150329413 | Beall et al. | Nov 2015 | A1 |
| 20150376055 | Fu et al. | Dec 2015 | A1 |
| 20160002092 | Kuehn | Jan 2016 | A1 |
| 20160031736 | Muehlke et al. | Feb 2016 | A1 |
| 20160046520 | Chenu et al. | Feb 2016 | A1 |
| 20160102010 | Beall et al. | Apr 2016 | A1 |
| 20160102014 | Hu et al. | Apr 2016 | A1 |
| 20160130175 | Siebers et al. | May 2016 | A1 |
| 20160159682 | Borczuch-Laczka et al. | Jun 2016 | A1 |
| 20160176752 | Gabel et al. | Jun 2016 | A1 |
| 20160194235 | Hart et al. | Jul 2016 | A1 |
| 20160280589 | Beall et al. | Sep 2016 | A1 |
| 20170022093 | Demartino et al. | Jan 2017 | A1 |
| 20170144921 | Beall et al. | May 2017 | A1 |
| 20170340420 | Burke et al. | Nov 2017 | A1 |
| 20180002227 | Dai et al. | Jan 2018 | A1 |
| 20180097142 | Moriyama et al. | Apr 2018 | A1 |
| 20180155235 | Beall et al. | Jun 2018 | A1 |
| 20180169826 | Bankaitis et al. | Jun 2018 | A1 |
| 20180182549 | Koide et al. | Jun 2018 | A1 |
| 20180210118 | Gollier et al. | Jul 2018 | A1 |
| 20180272783 | Ishihara | Sep 2018 | A1 |
| 20180362390 | Claireaux et al. | Dec 2018 | A1 |
| 20180370194 | Claireaux et al. | Dec 2018 | A1 |
| 20180370846 | Harrison et al. | Dec 2018 | A1 |
| 20190169060 | Jones et al. | Jun 2019 | A1 |
| 20190169061 | Jones et al. | Jun 2019 | A1 |
| 20190194062 | Wlfinger et al. | Jun 2019 | A1 |
| 20190300426 | Fu et al. | Oct 2019 | A1 |
| 20200017398 | Click et al. | Jan 2020 | A1 |
| 20200017399 | Click et al. | Jan 2020 | A1 |
| 20200156994 | Li et al. | May 2020 | A1 |
| 20200263317 | Mori et al. | Aug 2020 | A1 |
| 20220267205 | Chien et al. | Aug 2022 | A1 |
| Number | Date | Country |
|---|---|---|
| 1367149 | Sep 2002 | CN |
| 1575265 | Feb 2005 | CN |
| 101714504 | May 2010 | CN |
| 101962295 | Feb 2011 | CN |
| 102384654 | Mar 2012 | CN |
| 103003212 | Mar 2013 | CN |
| 105731808 | Jul 2016 | CN |
| 105753314 | Jul 2016 | CN |
| 105884184 | Aug 2016 | CN |
| 105899469 | Aug 2016 | CN |
| 106660861 | May 2017 | CN |
| 107001120 | Aug 2017 | CN |
| 107265845 | Oct 2017 | CN |
| 206580739 | Oct 2017 | CN |
| 206683413 | Nov 2017 | CN |
| 107619193 | Jan 2018 | CN |
| 107902909 | Apr 2018 | CN |
| 109071316 | Dec 2018 | CN |
| 111954646 | Nov 2020 | CN |
| 113896410 | Jan 2022 | CN |
| 102010027461 | Jan 2012 | DE |
| 102016111438 | Dec 2017 | DE |
| 202018102534 | May 2018 | DE |
| 0508131 | Oct 1992 | EP |
| 2323955 | May 2011 | EP |
| 2905113 | Aug 2015 | EP |
| 3293157 | Mar 2018 | EP |
| 62-070239 | Mar 1987 | JP |
| 02-116639 | May 1990 | JP |
| 05-043263 | Feb 1993 | JP |
| 05-032334 | May 1993 | JP |
| 2000-072489 | Mar 2000 | JP |
| 2001-097740 | Apr 2001 | JP |
| 2002-087835 | Mar 2002 | JP |
| 2006-232661 | Sep 2006 | JP |
| 2008-303073 | Dec 2008 | JP |
| 4305602 | Jul 2009 | JP |
| 2014-012617 | Jan 2014 | JP |
| 2015-069669 | Apr 2015 | JP |
| 2016-108218 | Jun 2016 | JP |
| 2017-530933 | Oct 2017 | JP |
| 201623179 | Jun 2016 | TW |
| 201731783 | Sep 2017 | TW |
| 2010002477 | Jan 2010 | WO |
| 2012121116 | Sep 2012 | WO |
| 2016057748 | Apr 2016 | WO |
| 2016154235 | Sep 2016 | WO |
| 2017104513 | Jun 2017 | WO |
| 2019022033 | Jan 2019 | WO |
| 2019191358 | Oct 2019 | WO |
| Entry |
|---|
| JP 2002-087835 A (Hashimoto) Mar. 27, 2002 (English language machine translation). [online] [retrieved Jan. 26, 2024]. Retrieved from: Espacenet. (Year: 2002). |
| Beall et al; “High Strength Glass-Ceramics Having Petalite and Lithium Silicate Structures”; Filed as U.S. Appl. No. 62/205,120, filed Aug. 14, 2015; 69 Pages. |
| Bubsey et al; “Closed-Form Expressions for Crack-Mouth Displacement and Stress Intensity Factors for Chevron-Notched Short Bar and Short Rod Specimens Based On Experimental Compliance Measurements,” NASA Technical Memorandum 83796, pp. 1-30 (Oct. 1992). |
| Eppler, “Glass formation and recrystallization in the lithium metasilicate region of the system Li2O-Al2O3-SiO2,” Journal of the American Ceramic Society 46(2) 1963, pp. 97-101. |
| Reddy et al; “Fracture Toughness Measurement of Glass and Ceramic Materials Using Chevron-Notched Specimens,” J. Am. Ceram. Soc., 71 [6], C-310-C-313 (1988). |
| Tang et al; “Automated Apparatus for Measuring the Frangibility and Fragmentation of Strengthened Glass”; Experimental Mechanics (2014) 54: 903-912. |
| ZYP Coatings, “Boron Nitride Lubricoat Boron Nitride Lubricoat-Blue” (Year: 2015), 2 Pages. |
| CeraGlide Boron Nitride coatings as provided by https://www.bn.saint-gobain.com/products/coatings DATAsheet (Year: 2019), 6 pages. |
| Number | Date | Country | |
|---|---|---|---|
| 20210292220 A1 | Sep 2021 | US |
| Number | Date | Country | |
|---|---|---|---|
| 62749808 | Oct 2018 | US | |
| 62698582 | Jul 2018 | US |