This invention relates to shaped, three-dimensional nonwoven fabrics and articles made with shaped, three-dimensional nonwoven fabrics.
Nonwoven fabrics are useful for a wide variety of applications, including absorbent personal care products, garments, medical applications, and cleaning applications. Nonwoven personal care products include infant care items such as diapers, child care items such as training pants, feminine care items such as sanitary napkins, and adult care items such as incontinence products, pads, and pants. Nonwoven garments include protective workwear and medical apparel such as surgical gowns. Other nonwoven medical applications include nonwoven wound dressings and surgical dressings. Cleaning applications for nonwovens include towels and wipes. Still other uses of nonwoven fabrics are well known. The foregoing list is not considered exhaustive.
Various properties of nonwoven fabrics determine the suitability of nonwoven fabrics for different applications. Nonwoven fabrics may be engineered to have different combinations of properties to suit different needs. Variable properties of nonwoven fabrics include liquid-handling properties such as wettability, distribution, and absorbency, strength properties such as tensile strength and tear strength, softness properties, durability properties such as abrasion resistance, and aesthetic properties. The physical shape of a nonwoven fabric also affects the functionality and aesthetic properties of the nonwoven fabric. Nonwoven fabrics are initially made into sheets which, when laid on a flat surface, may have a substantially planar, featureless surface or may have an array of surface features such as aperture or projections, or both. Nonwoven fabrics with apertures or projections are often referred to as three-dimensional shaped nonwoven fabrics. The present disclosure relates to three-dimensional shaped nonwoven fabrics.
Despite prior advances in the art of nonwoven fabrics, there remains a need for improved nonwoven fabrics having three-dimensional surface features.
Further, there remains a need for processes and equipment for manufacturing improved nonwoven fabrics having three-dimensional surface features.
Further, there remains a need for articles, including absorbent articles, utilizing improved nonwoven fabrics having three-dimensional surface features.
Further, there remains a need for absorbent articles utilizing nonwoven fabrics having three-dimensional surface features and which can be packaged in a compressed form while minimizing the loss of the three-dimensional surface features when opened from the package.
Further, there remains a need for absorbent articles utilizing soft, spunbond nonwoven fabrics having three-dimensional surface features that have reduced fuzzing properties when in use.
Further, there remains a need for improved nonwoven fabrics having three-dimensional surface features and physical integrity combined with softness as measured by a Tissue Softness Analyzer marketed by Emtec Electronic GmbH.
Further, there remains a need for improved nonwoven fabrics having three-dimensional surface features with microzones and physical integrity, combined with at least one region of a microzone being hydrophobic and a different region of the same microzone being hydrophilic.
Additionally, there remains a need for packages of absorbent articles comprising soft nonwoven materials that have a reduced in-bag stack height compared to conventional absorbent article packages so the packages are convenient for caregivers to handle and store and so that manufacturers enjoy low distribution costs without a loss of aesthetics clarity, absorbency, or softness of the as-made absorbent article.
A nonwoven fabric is disclosed. The nonwoven fabric can include a first surface and a second surface and a visually discernible pattern of three-dimensional features on one of the first or second surface. Each of the three-dimensional features can define a microzone comprising a first region and a second region. The first and second regions can have a difference in values for an intensive property, wherein the intensive property is one or more of thickness, basis weight, or volumetric density, and wherein in at least one of the microzones, the first region exhibits a Contact Angle of greater than 90 degrees, as measured by the Contact Angle Test Method detailed herein.
The present disclosure provides a shaped nonwoven fabric directly formed on a shaped forming belt with continuous spunbond filaments in a single forming process. The fabric of the present disclosure can assume a shape which corresponds to the shape of the forming belt. A fabric of the present disclosure made on a forming belt of the present disclosure in a method of the present disclosure can be particularly beneficial for use in personal care articles, garments, medical products, and cleaning products. The shaped nonwoven fabric can be fluid permeable for use as a topsheet, backsheet nonwoven, acquisition layer, distribution layer, or other component layer for a diaper, or a topsheet, backsheet nonwoven, acquisition layer, distribution layer, or other component layer for a sanitary napkin, a topsheet, backsheet nonwoven, acquisition layer, distribution layer, or other component layer for an adult incontinent pad or pant, or a pad for a floor cleaning implement.
The beneficial features of the nonwoven fabric will be described in some embodiments herein in the context of an overall area of the nonwoven fabric. The overall area can be an area determined by dimensions suitable for certain uses, for which the various features of the invention provide beneficial properties. For example, the overall area of a fabric can be that of a fabric having dimensions making it suitable for use as a topsheet, backsheet nonwoven, acquisition layer, distribution layer, or other component layer for a diaper, or a topsheet, backsheet nonwoven, acquisition layer, distribution layer, or other component layer for a sanitary napkin, a topsheet, backsheet nonwoven, acquisition layer, distribution layer, or other component layer for an adult incontinent pad or pant, or a pad for a floor cleaning implement. Thus, the overall area can be based on width and length dimensions ranging from 3 cm wide to 50 cm wide and from 10 cm long to 100 cm long, resulting in overall areas of from 30 cm2 to 500 cm2. The aforementioned ranges include as if explicitly stated every integer dimension between the range boundaries. By way of example, an overall area of 176 cm2 defined by a width of 11 cm and a length of 16 cm is disclosed in the above ranges. As will be understood from the description herein, the overall area of a shaped nonwoven fabric may be a smaller area than the area of the web of nonwoven material of which it is a part when it is commercially made. That is, in a given commercially made web of nonwoven material, there can be a plurality of shaped nonwoven fabrics of the invention, each of the shaped nonwoven fabrics of the invention having an overall area less than the area of the web on which it is made.
Photographs of representative examples of shaped nonwoven fabrics 10 are shown in
The exemplary fabrics shown in
As shown in
The three-dimensional features of the nonwoven fabric 10 can be formed by depositing, such as by carding, air laying, spinning from solution, or melt spinning, fibers directly onto a forming belt having a pattern of corresponding three-dimensional features. In one sense the nonwoven fabric 10 is molded onto a forming belt that determines the shapes of the three-dimensional features of the fabric 10. However, importantly, as described herein, the apparatus and method of the invention produce the nonwoven fabric 10 such that in addition to taking the shape of the forming belt, because of the attributes of the forming belt and the apparatus for forming the fabric, it is imparted with beneficial properties for use in personal care articles, garments, medical products, and cleaning products. Specifically, because of the nature of the forming belt and other apparatus elements, as described below, the three-dimensional features of the nonwoven fabric 10 have intensive properties that can differ between first and second regions within a microzone (described more fully below), or from feature to feature in ways that provide for beneficial properties of the nonwoven fabric when used in personal care articles, garments, medical products, and cleaning products. For example, first three-dimensional feature 20 can have a basis weight or density that is different from the basis weight or density of second three-dimensional feature 22, and both can have a basis weight or density that is different from that of third three-dimensional feature 24, providing for beneficial aesthetic and functional properties related to fluid acquisition, distribution and/or absorption in diapers or sanitary napkins.
The intensive property differential between the various three-dimensional features of nonwoven fabric 10 is believed to be due to the fiber distribution and compaction resulting from the apparatus and method described below. The fiber distribution occurs during the fiber laydown process, as opposed to, for example, a post making process such as hydroentangling or embossing processes. Because the fibers are free to move during a process such as a melt spinning process, with the movement determined by the nature of the features and air permeability of the forming belt and other processing parameters, the fibers are believed to be more stable and permanently formed in nonwoven fabric 10.
As can be seen in
Specifically, in the regular repeating pattern of closed, three-dimensional features shown in
Table 1 below shows compression recovery data for two embodiments of the present disclosure. Example 1 corresponds to the nonwoven fabric 10 shown in
A bicomponent spunbond nonwoven fabric that was produced by spinning a 50:50 ratio of polyethylene sheath (Aspun-6850-A obtained from Dow chemical company) and polypropylene core (PH-835 obtained from LyondellBasell) in a trilobal fiber configuration, as shown in
A bicomponent spunbond nonwoven fabric was produced by spinning a 50:50 ratio of polyethylene sheath (Aspun-6850-A obtained from Dow chemical company) and polypropylene core (PH-835 obtained from LyondellBasell) in a trilobal fiber configuration, as shown in
As can be seen from Table 1, fabrics 10 of the invention retain significant amounts of caliper after compression at relatively high pressures. For example, the Example 1 and Example 2 samples retain greater than 70% of their original average caliper after being tested by the Compression Aging Test at a pressure of 35 KPa. The Compression Aging Test is a simulation of the conditions a nonwoven fabric would encounter if packaged in a high compression packaging of diapers and then remain in such a state during distribution to a consumer and then the package finally opened by a consumer.
The present disclosure can utilize the process of melt spinning. In melt spinning, there is no mass loss in the extrudate. Melt spinning is differentiated from other spinning, such as wet or dry spinning from solution, where a solvent is being eliminated by volatilizing or diffusing out of the extrudate resulting in a mass loss.
Melt spinning can occur at from about 150° C. to about 280°, or, in some embodiments, at from about 190° to about 230°. Fiber spinning speeds can be greater than 100 meters/minute, and can be from about 1,000 to about 10.000 meters/minute, and can be from about 2,000 to about 7,000 meters/minute, and can be from about 2.500 to about 5,000 meters/minute. Spinning speeds can affect the brittleness of the spun fiber, and, in general, the higher the spinning speed, the less brittle the fiber. Continuous fibers can be produced through spunbond methods or meltblowing processes.
A nonwoven fabric 10 of the present disclosure can include continuous multicomponent polymeric filaments comprising a primary polymeric component and a secondary polymeric component. The filaments can be continuous bicomponent filaments comprising a primary polymeric component A and a secondary polymeric component B. The bicomponent filaments have a cross-section, a length, and a peripheral surface. The components A and B can be arranged in substantially distinct zones across the cross-section of the bicomponent filaments and can extend continuously along the length of the bicomponent filaments. The secondary component B constitutes at least a portion of the peripheral surface of the bicomponent filaments continuously along the length of the bicomponent filaments. The polymeric components A and B can be melt spun into multicomponent fibers on conventional melt spinning equipment. The equipment will be chosen based on the desired configuration of the multicomponent. Commercially available melt spinning equipment is available from Hills. Inc. located in Melbourne, Florida. The temperature for spinning range from about 180° C. to about 230° C. The processing temperature is determined by the chemical nature, molecular weights and concentration of each component. The bicomponent spunbond filaments can have an average diameter from about 6 to about 40 microns, and preferably from about 12 to about 40 microns.
The components A and B can be arranged in either a side-by-side arrangement as shown in
Methods for extruding multicomponent polymeric filaments into such arrangements are well-known to those of ordinary skill in the art.
A wide variety of polymers are suitable to practice the present disclosure including polyolefins (such as polyethylene, polypropylene and polybutylene), polyesters, polyamides, polyurethanes, elastomeric materials and the like. Non-limiting examples of polymer materials that can be spun into filaments include natural polymers, such as starch, starch derivatives, cellulose and cellulose derivatives, hemicellulose, hemicelluloses derivatives, chitin, chitosan, polyisoprene (cis and trans), peptides, polyhydroxyalkanoates, and synthetic polymers including, but not limited to, thermoplastic polymers, such as polyesters, nylons, polyolefins such as polypropylene, polyethylene, polyvinyl alcohol and polyvinyl alcohol derivatives, sodium polyacrylate (absorbent gel material), and copolymers of polyolefins such as polyethylene-octene or polymers comprising monomeric blends of propylene and ethylene, and biodegradable or compostable thermoplastic polymers such as polylactic acid filaments, polyvinyl alcohol, filaments, and polycaprolactone filaments. In one example, thermoplastic polymer selected from the group consisting of: polypropylene, polyethylene, polyester, polylactic acid, polyhydroxyalkanoate, polyvinyl alcohol, polycaprolactone, styrene-butadiene-styrene block copolymer, styrene-isoprene-styrene block copolymer, polyurethane, and mixtures thereof. In another example, the thermoplastic polymer is selected from the group consisting of: polypropylene, polyethylene, polyester, polylactic acid, polyhydroxyalkanoate, polyvinyl alcohol, polycaprolactone, and mixtures thereof. Alternatively, the polymer can comprise one derived from monomers which are biobased such as bio-polyethylene or bio-polypropylene.
Primary component A and secondary component B can be selected so that the resulting bicomponent filament is providing improved nonwoven bonding and substrate softness. Primary polymer component A has melting temperature which is lower than the melting temperature of secondary polymer component B.
Primary polymer component A can comprise polyethylene or random copolymer of propylene and ethylene. Secondary polymer component B can comprise polypropylene or random copolymer of propylene and ethylene. Polyethylenes include linear low density polyethylene and high density polyethylene. In addition, secondary polymer component B may comprise additives for enhancing the natural helical crimp of the filaments, lowering the bonding temperature of the filaments, and enhancing the abrasion resistance, strength and softness of the resulting fabric.
Inorganic fillers such as the oxides of magnesium, aluminum, silicon, and titanium may be added as inexpensive fillers or processing aides. Other inorganic materials include hydrous magnesium silicate, titanium dioxide, calcium carbonate, clay, chalk, boron nitride, limestone, diatomaceous earth, mica glass quartz, and ceramics.
The filaments of the present invention also contain a slip additive in an amount sufficient to impart the desired haptics to the fiber. As used herein “slip additive” or “slip agent” means an external lubricant. The slip agent when melt-blended with the resin gradually exudes or migrates to the surface during cooling or after fabrication, hence forming a uniform, invisibly thin coating thereby yielding permanent lubricating effects. The slip agent is preferably a fast bloom slip agent, and can be a hydrocarbon having one or more functional groups selected from hydroxide, aryls and substituted aryls, halogens, alkoxys, carboxylates, esters, carbon unsaturation, acrylates, oxygen, nitrogen, carboxyl, sulfate and phosphate.
During the making or in a post-treatment or even in both, the nonwoven fabrics of the present invention can be treated with surfactants or other agents to either hydrophilize the web or make it hydrophobic. This is standard practice for nonwovens used in absorbent articles. For example, a nonwoven fabric used for a topsheet may be treated with a hydrophilizing material or surfactant so as to make it permeable to body exudates such as urine. For other absorbent articles, the topsheet may remain at its naturally hydrophobic state or made even more hydrophobic through the addition of a hydrophobizing material or surfactant.
Suitable materials for preparing the multicomponent filaments of the fabric of the present disclosure include PH-835 polypropylene obtained from LyondellBasell and Aspun-6850-A polyethylene obtained from Dow chemical company.
When polyethylene is component A (sheath) and polypropylene is component B (core), the bicomponent filaments may comprise from about 5 to about 95% by weight polyethylene and from about 95 to about 5% polypropylene. The filaments can comprise from about 40 to about 60% by weight polyethylene and from about 60 to about 40% by weight polypropylene.
Turning to
The process line 30 includes a pair of extruders 32 and 34 driven by extruder drives 31 and 33, respectively, for separately extruding the primary polymer component A and the secondary polymer component B. Polymer component A is fed into the respective extruder 32 from a first hopper 36 and polymer component B is fed into the respective extruder 34 from a second hopper 38. Polymer components A and B can be fed from the extruders 32 and 34 through respective polymer conduits 40 and 42 to filters 44 and 45 and melt pumps 46 and 47, which pump the polymer into a spin pack 48. Spinnerets for extruding bicomponent filaments are well-known to those of ordinary skill in the art and thus are not described here in detail.
Generally described, the spin pack 48 includes a housing which includes a plurality of plates stacked one on top of the other with a pattern of openings arranged to create flow paths for directing polymer components A and B separately through the spinneret. The spin pack 48 has openings arranged in one or more rows. The spinneret openings form a downwardly extending curtain of filaments when the polymers are extruded through the spinneret. For the purposes of the present disclosure, spinnerets may be arranged to form sheath/core or side-by-side bicomponent filaments illustrated in
The process line 30 also includes a quench blower 50 positioned adjacent the curtain of filaments extending from the spinneret. Air from the quench air blower 50 quenches the filaments extending from the spinneret. The quench air can be directed from one side of the filament curtain or both sides of the filament curtain.
An attenuator 52 is positioned below the spinneret and receives the quenched filaments. Fiber draw units or aspirators for use as attenuators in melt spinning polymers are well-known. Suitable fiber draw units for use in the process of the present disclosure include a linear fiber attenuator of the type shown in U.S. Pat. No. 3,802,817 and eductive guns of the type shown in U.S. Pat. Nos. 3,692,618 and 3,423,266, the disclosures of which are incorporated herein by reference.
Generally described, the attenuator 52 includes an elongate vertical passage through which the filaments are drawn by aspirating air entering from the sides of the passage and flowing downwardly through the passage. A shaped, endless, at least partially foraminous, forming belt 60 is positioned below the attenuator 52 and receives the continuous filaments from the outlet opening of the attenuator 52. The forming belt 60 is a belt and travels around guide rollers 62. A vacuum 64 positioned below the forming belt 60 where the filaments are deposited draws the filaments against the forming surface. Although the forming belt 60 is shown as a belt in
In operation of the process line 30, the hoppers 36 and 38 are filled with the respective polymer components A and B. Polymer components A and B are melted and extruded by the respective extruders 32 and 34 through polymer conduits 40 and 42 and the spin pack 48. Although the temperatures of the molten polymers vary depending on the polymers used, when polyethylene and polypropylene are used as primary component A and secondary component B respectively, the temperatures of the polymers can range from about 190° C. to about 240° C.
As the extruded filaments extend below the spinneret, a stream of air from the quench blower 50 at least partially quenches the filaments, and, for certain filaments, to induce crystallization of molten filaments. The quench air can flow in a direction substantially perpendicular to the length of the filaments at a temperature of about 0° C. to about 35° C. and a velocity from about 100 to about 400 feet per minute. The filaments can be quenched sufficiently before being collected on the forming belt 60 so that the filaments can be arranged by the forced air passing through the filaments and forming surface. Quenching the filaments reduces the tackiness of the filaments so that the filaments do not adhere to one another too tightly before being bonded and can be moved or arranged on the forming belt during collection of the filaments on the forming belt and formation of the web.
After quenching, the filaments are drawn into the vertical passage of the attenuator 52 by a flow of the fiber draw unit. The attenuator is can be positioned 30 to 60 inches below the bottom of the spinneret.
The filaments can be deposited through the outlet opening of the attenuator 52 onto the shaped, traveling forming belt 60. As the filaments are contacting the forming surface of the forming belt 60, the vacuum 64 draws the air and filaments against the forming belt 60 to form a nonwoven web of continuous filaments which assumes a shape corresponding to the shape of the forming surface. As discussed above, because the filaments are quenched, the filaments are not too tacky and the vacuum can move or arrange the filaments on the forming belt 60 as the filaments are being collected on the forming belt 60 and formed into the fabric 10.
The process line 30 further includes one or more bonding devices such as the cylinder-shaped compaction rolls 70 and 72, which form a nip through which the fabric can be compacted, i.e., calendared, and which can be heated to bond fibers as well. One or both of compaction rolls 70, 72 can be heated to provide enhanced properties and benefits to the nonwoven fabric 10 by bonding portions of the fabric. For example, it is believed that heating sufficient to provide thermal bonding improves the fabric's 10 tensile properties. The compaction rolls may be pair of smooth surface stainless steel rolls with independent heating controllers. The compaction rolls may be heated by electric elements or hot oil circulation. The gap between the compaction rolls can be hydraulically controlled to impose desired pressure on the fabric as it passes through the compaction rolls on the forming belt. In an embodiment, with a forming belt caliper of 1.4 mm, and a spunbond nonwoven having a basis weight of 30 gsm, the nip gap between the compaction rolls 70 and 72 can be about 1.4 mm.
In an embodiment, upper compaction roll 70 can be heated sufficient to melt bond fibers on the first surface 12 of the fabric 10, to impart strength to the fabric so that it can be removed from forming belt 60 without losing integrity. As shown in
The raised elements of the forming belt 60 may be selected to establish various network characteristics of the forming belt and the bonded regions of the nonwoven substrate 11 or nonwoven fabric 10. The network corresponds to the resin making up the raised elements of the forming belt 60 and may comprise substantially continuous, substantially semi-continuous, discontinuous, or combinations thereof options. These networks may be descriptive of the raised elements of the forming belt 60 as it pertains to their appearance or make-up in the X-Y planes of the forming belt 60 or the three dimensional features comprising the nonwoven substrate 11 or nonwoven fabric 10 of the present invention.
“Substantially continuous” network refers to an area within which one can connect any two points by an uninterrupted line running entirely within that area throughout the line's length. That is, the substantially continuous network has a substantial “continuity” in all directions parallel to the first plane and is terminated only at edges of that region. The term “substantially,” in conjunction with continuous, is intended to indicate that while an absolute continuity can be achieved, minor deviations from the absolute continuity may be tolerable as long as those deviations do not appreciably affect the performance of the fibrous structure (or a molding member) as designed and intended.
“Substantially semi-continuous” network refers an area which has “continuity” in all, but at least one, directions parallel to the first plane, and in which area one cannot connect any two points by an uninterrupted line running entirely within that area throughout the line's length. The semi-continuous framework may have continuity only in one direction parallel to the first plane. By analogy with the continuous region, described above, while an absolute continuity in all, but at least one, directions is preferred, minor deviations from such a continuity may be tolerable as long as those deviations do not appreciably affect the performance of the fibrous structure.
“Discontinuous” network refer to discrete, and separated from one another areas that are discontinuous in all directions parallel to the first plane.
After compaction, the fabric can leave the forming belt 60 and be calendared through a nip formed by calendar rolls 71, 73, after which the fabric can be wound onto a reel. As shown in the schematic cross section of
As described with respect to
Binders used in through-air thermal bonding include crystalline binder fibers, bi-component binder fibers, and powders. When using crystalline binder fibers or powders, the binder melts entirely and forms molten droplets throughout the nonwoven's cross-section. Bonding occurs at these points upon cooling. In the case of sheath/core binder fibers, the sheath is the binder and the core is the carrier fiber. In one embodiment, a nonwoven comprising sheath/core binder fibers, the sheath comprises a polyethylene and the core comprises polypropylene. For such a nonwoven, the through-air thermal bonding air temperature may be in the range of 110° C. to 150° C. and the residence time may be in the range of 0.5 to 10 seconds, 5-30 seconds, or 30-60 seconds as through air bonding time will depend upon basis weight, level of strength desired, and operating speed. Products manufactured using through-air ovens tend to be bulky, open, soft, strong, extensible, breathable and absorbent.
Point bonding as used herein is a method of thermally bonding a nonwoven fabric, web, or substrate. This method involves passing a web through a nip between two rolls consisting of heated male patterned or engraved metal roll and a smooth or patterned metal roll. The male patterned roll can have a plurality of raised, generally cylindrical-shaped pins that produce circular point bonds. The smooth roll may or may not be heated, depending on the application. In a nonwoven production line, the nonwoven fabric, which could be a non-bonded fiber web, is fed into the calendar nip and the fiber temperature is raised to the point for fibers to thermally fuse with each other at the tips of engraved points and against the smooth roll. The heating time is typically in the order of milliseconds. The fabric properties are dependent on process settings such as roll temperatures, web line speeds, and nip pressures, all of which can be determined by the skilled person for the desired level of point bonding. Other types of point bonding known generally as hot calendar bonding may consist of different geometries for the bonds (other than circular shaped), such as oval, lines, circles, etc. In the exemplary embodiment disclosed herein, the point bonding produces a pattern of point bonds being 0.5 mm diameter circles with 10% overall bonding area. Other embodiments comprise bonding shapes where the raised pins have a longest dimension across the bonding surface of a pin of from about 0.1 mm to 2.0 mm and the overall bonding area ranges from 5% to 30%.
As shown in
Forming belt 60 can be made according to the methods and processes described in U.S. Pat. No. 6,610,173, issued to Lindsay et al. on Aug. 26, 2003, or U.S. Pat. No. 5,514,523 issued to Trokhan et al. on May 7, 1996, or U.S. Pat. No. 6,398,910 issued to Burazin et al. on Jun. 4, 2002, or US Pub. No. 2013/0199741, published in the name of Stage et al. on Aug. 8, 2013, each with the improved features and patterns disclosed herein for making spunbond nonwoven webs. The Lindsay, Trokhan. Burazin and Stage disclosures describe belts that are representative of papermaking belts made with cured resin on a woven reinforcing member, which belts, with improvements, can be utilized in the present disclosure as described herein.
An example of a forming belt 60 of the type useful in the present disclosure and which can be made according to the disclosure of U.S. Pat. No. 5,514,523, is shown in
In like manner,
Further, in another non-limiting example.
Another example of a portion of a forming belt 60 of the type useful in the present disclosure is shown in
The portion of the forming belt shown in
The nonwoven fabric 10 can also have visually discernible zones corresponding to the zones of the forming belt. As shown in
The visually discernible zones as shown in
As can be understood, rather than having a constant repeating pattern that is uniform across the entire forming belt, the forming belt 60 of the present disclosure allows the production of a nonwoven material that can have repeats of irregular discrete belt patterns 61, each discrete belt pattern 61 being like the discrete belt pattern shown in
In an embodiment, the pattern within each discrete belt pattern overall area DPOA can be the same or different. That is, the sequentially spaced discrete belt patterns can be substantially identical, or they can differ in visual appearance and/or in the intensive properties produced in nonwoven substrates produced thereon. For example, as shown schematically in
Thus, the invention can be described, with reference to
By way of example, and referring to the discrete belt pattern 61 of forming belt 60 shown in
As can be understood from the description of the forming belt 60 described in
In general, the sequentially ordered nonwoven fabrics 10 of the nonwoven material 11 made on forming belt 60 can vary in their respective overall areas, intensive properties, and visual appearances. A common intensive property is an intensive property possessed by more than one zone (with respect to zonal patterns, such as that shown in
Once produced, the individual nonwoven fabrics 10 can be cut to size and utilized for their intended purposes, such as for topsheets in disposable absorbent articles. For example, a disposable diaper 1006 in a flattened orientation is shown in
As can be understood with reference to
By way of representative sample to compare basis weight differentials in a fabric 10 made with a regular, repeating, uniform pattern and a fabric 10 made with a non-uniform, zonal pattern, the nonwoven fabric 10 of Example 1 was compared with a fabric having a pattern similar to that shown in
A bicomponent spunbond nonwoven fabric that was produced by spinning a 50:50 ratio of polyethylene sheath (Aspun-6850-A obtained from Dow chemical company) and polypropylene core (PH-835 obtained from LyondellBasell) in a trilobal fiber configuration to an average basis weight of 30 grams per square meter. A nonwoven fabric was produced as described with respect to
A bicomponent spunbond nonwoven fabric that was produced by spinning a 50:50 ratio of polyethylene sheath (Aspun-6850-A obtained from Dow chemical company) and polypropylene core (PH-835 obtained from LyondellBasell) in a trilobal fiber configuration to an average basis weight of 30 grams per square meter. A nonwoven fabric was produced as described with respect to
Table 2 below shows average local basis weight, measured according to the Localized Basis Weight test method herein, and averaged over 10 samples. The samples for measurement were taken from the fabrics as shown in
As can be seen in Table 2, fabrics 10 made on forming belts 60 having zones of differing air permeability demonstrate substantial variation in fiber laydown and thus basis weights within the CD of nonwoven fabric 10 suggesting the ability for fibers to travel with air into high permeability zones. The non-zonal, regular repeating pattern fabric 10 exhibits approximately the same basis weights within the CD of fabric.
In addition to differences in air permeability of the various zones of the forming belt 60, the structure of forming belt 60 can affect other intensive properties of zones in the fabric 10, such as average caliper, average softness, average compression resistance, and fluid absorption properties.
Another aspect of this invention relates to spunbond commercial lines where multiple beams are utilized for improved laydown opacity and uniformity of the fabric. In some cases, there the apparatus can include triple spunbond beams (known in the art as “SSS”) and may be combined with meltblown (M), for example, in an apparatus known as an “SSMMS” spunbond line.
By calendaring the nonwoven fabric 10 to have point bonds 90, fuzzing can be reduced. Fuzzing refers to the tendency of fibers to become loose and removed from the fabric 10. Loosening and removal can be because of frictional engagement with manufacturing equipment during production of disposable absorbent articles, or another surface, such as the skin of a person interacting with the fabric 10. In some uses, such as for topsheets in disposable absorbent articles, fuzzing is a negative consumer phenomena. But bonding fibers in place can also be a consumer negative as it can produce roughness on the surface of an otherwise soft nonwoven substrate. We have found expectedly the nonwoven fabrics substrates and nonwoven fabrics of the present disclosure can endure an increase in bonding (and a consequent decrease in fuzzing) with minimal loss in softness. Bonding can be accomplished by relatively closely spaced point bonds 90, with the spacing being determined by the desired level of fuzzing reduction. Bonding can also be achieved by known methods for chemically or thermally bonding nonwoven fibers, such as thermal bonding, ultrasonic bonding, pressure bonding, latex adhesive bonding, and combinations of such methods. Fuzz reduction by bonding is illustrated with respect to Examples 5 and 6 below.
A bicomponent spunbond nonwoven fabric was produced by spinning a 50:50 ratio of polyethylene sheath (Aspun-6850-A obtained from Dow chemical company) and polypropylene core (PH-835 obtained from LyondellBasell) in a trilobal fiber configuration to an average basis weight of about 30 grams per square meter on a forming belt as described with respect to
A bicomponent spunbond nonwoven fabric was produced by spinning a 50:50 ratio of polyethylene sheath (Aspun-6850-A obtained from Dow chemical company) and polypropylene core (PH-835 obtained from LyondellBasell) in a trilobal fiber configuration to an average basis weight of about 30 grams per square meter on a forming belt as described with respect to
The fabrics 10 of Examples 5 and 6 differed only in the absence or presence of point bonds 90. The second side 14 of the fabrics 10 underwent fuzz testing according to the Fuzz Level Test to determine the effectiveness of the point bonds in securing fibers to the surface of the fabric. The results of fuzz testing of Examples 5 and 6 are shown in Table 3.
As shown above, the point bonds 90 result in a dramatic decrease in the MD Fuzz Value. It unexpectedly retained its softness, absorbency, and aesthetic benefits in spite of the bonding treatment and now also has the desired resistance to fuzz upon consumer use. Present disclosure absorbent articles are generally placed into packages for shipping, storing, and selling. The packages may comprise polymeric films and/or other materials. Graphics and/or indicia relating to properties of the absorbent articles may be formed on, printed on, positioned on, and/or placed on outer portions of the packages. Each package may comprise a plurality of absorbent articles. The absorbent articles may be packed under compression so as to reduce the size of the packages, while still providing an adequate amount of absorbent articles per package. By packaging the absorbent articles under compression, caregivers can easily handle and store the packages, while also providing distribution savings to manufacturers owing to the size of the packages.
Packages of the absorbent articles of the present disclosure may have an In-Bag Stack Height of less than about 100 mm, less than about 95 mm, less than about 90 mm, less than about 85 mm, less than about 85 mm, but greater than about 75 mm, less than about 80 mm, less than about 78 mm, less than about 76 mm, or less than about 74 mm, specifically reciting all 0.1 mm increments within the specified ranges and all ranges formed therein or thereby, according to the In-Bag Stack Height Test described herein. Alternatively, packages of the absorbent articles of the present disclosure may have an In-Bag Stack Height of from about 70 mm to about 100 mm, from about 70 mm to about 95 mm, from about 72 mm to about 85 mm, from about 72 mm to about 80 mm, or from about 74 mm to about 78 mm, specifically reciting all 0.1 mm increments within the specified ranges and all ranges formed therein or thereby, according to the In-Back Stack Height Test described herein.
The three-dimensional nonwoven fabrics 10 of the present disclosure can be utilized as a component of absorbent articles, such as diapers, child care items such as training pants, feminine care items such as sanitary napkins, and adult care items such as incontinence products, pads, and pants An example absorbent article in the form of a diaper 220 is represented in
The absorbent article 220 may comprise a liquid permeable material or topsheet 224, a liquid impermeable material or backsheet 225, an absorbent core 228 positioned at least partially intermediate the topsheet 224 and the backsheet 225, and barrier leg cuffs 234. The absorbent article may also comprise an ADS 250, which in the example represented comprises a distribution layer 254 and an acquisition layer 252, which will be further discussed below. The absorbent article 220 may also comprise elasticized gasketing cuffs 232 comprising elastics 233 joined to a chassis of the absorbent article, typically via the topsheet and/or backsheet, and substantially planar with the chassis of the diaper.
The absorbent article 220 comprises a front waist edge 210, a rear waist edge 212 longitudinally opposing the front waist edge 210, a first side edge 203, and a second side edge 204 laterally opposing the first side edge 203. The front waist edge 210 is the edge of the article which is intended to be placed towards the front of the user when worn, and the rear waist edge 212 is the opposite edge. The absorbent article 220 may have a longitudinal axis 280 extending from the lateral midpoint of the front waist edge 210 to a lateral midpoint of the rear waist edge 212 of the article and dividing the article in two substantially symmetrical halves relative to the longitudinal axis 280, with the article placed flat, laid-out and viewed from above as in
The topsheet 224, the backsheet 225, the absorbent core 228, and the other article components may be assembled in a variety of configurations, in particular by gluing or heat embossing, for example.
The absorbent core 228 may comprise an absorbent material comprising at least 80% by weight, at least 85% by weight, at least 90% by weight, at least 95% by weight, or at least 99% by weight of superabsorbent polymers, and a core wrap enclosing the superabsorbent polymers. The core wrap may typically comprise two materials, substrates, or nonwoven materials 216 and 216′ for the top side and the bottom side of the core. These types of cores are known as airfelt-free cores. The core may comprise one or more channels, represented in
These and other components of the example absorbent articles will now be discussed in more details.
In the present disclosure, the topsheet (the portion of the absorbent article that contacts the wearer's skin and receives the fluids) may be formed of a portion of, or all of, one or more of the three-dimensional nonwoven materials described herein and/or have one or more of the nonwoven materials positioned thereon and/or joined thereto, so that the nonwoven material(s) contact(s) the wearer's skin. Other portions of the topsheet (other than the three-dimensional nonwoven materials) may also contact the wearer's skin. The three-dimensional nonwoven materials may be positioned as a strip or a patch on top of the typical topsheet 224. Alternatively, the three-dimensional nonwoven material may only form a central CD area of the topsheet. The central CD area may extend the full MD length of the topsheet or less than the full MD length of the topsheet.
The topsheet 224 may be joined to the backsheet 225, the absorbent core 228 and/or any other layers as is known to those of skill in the art. Usually, the topsheet 224 and the backsheet 225 are joined directly to each other in some locations (e.g., on or close to the periphery of the absorbent article) and are indirectly joined together in other locations by directly joining them to one or more other elements of the article 220.
The topsheet 224 may be compliant, soft-feeling, and non-irritating to the wearer's skin. Further, a portion of, or all of, the topsheet 224 may be liquid permeable, permitting liquids to readily penetrate through its thickness. Furthermore, a portion of, or all of, the topsheet 224 may be treated with surfactants or other agents to either hydrophilize the web or make it hydrophobic. Any portion of the topsheet 224 may be coated with a lotion and/or a skin care composition as is generally disclosed in the art. The topsheet 224 may also comprise or be treated with antibacterial agents.
The backsheet 225 is generally that portion of the absorbent article 220 positioned adjacent the garment-facing surface of the absorbent core 228 and which prevents, or at least inhibits, the fluids and bodily exudates absorbed and contained therein from soiling articles such as bedsheets and undergarments. The backsheet 225 is typically impermeable, or at least substantially impermeable, to fluids (e.g., urine). The backsheet may, for example, be or comprise a thin plastic film such as a thermoplastic film having a thickness of about 0.012 mm to about 0.051 mm. Other suitable backsheet materials may include breathable materials which permit vapors to escape from the absorbent article 220, while still preventing, or at least inhibiting, fluids from passing through the backsheet 225.
The backsheet 225 may be joined to the topsheet 224, the absorbent core 228, and/or any other element of the absorbent article 220 by any attachment methods known to those of skill in the art.
The absorbent article may comprise a backsheet comprising an outer cover or an outer cover nonwoven. An outer cover or outer cover nonwoven of the absorbent article 220 may cover at least a portion of, or all of, the backsheet 225 to form a soft garment-facing surface of the absorbent article. The outer cover or outer cover nonwoven may be formed of the high loft, three-dimensional nonwoven materials described herein. Alternatively, the outer cover or outer cover nonwoven may comprise one or more known outer cover materials. If the outer cover comprises one of the three-dimensional nonwoven materials of the present disclosure, the three-dimensional nonwoven material of the outer cover may or may not match (e.g., same material, same pattern) a three-dimensional nonwoven material used as the topsheet or the topsheet and the acquisition layer of the absorbent article. In other instances, the outer cover may have a printed or otherwise applied pattern that matches or visually resembles the pattern of the three-dimensional nonwoven materials used as the topsheet or the topsheet and the acquisition layer laminate of the absorbent article. The outer cover may be joined to at least a portion of the backsheet 225 through mechanical bonding, ultrasonic, thermal bonding, adhesive bonding, or other suitable methods of attachment.
The absorbent core is the component of the absorbent article that has the most absorbent capacity and that comprises an absorbent material and a core wrap or core bag enclosing the absorbent material. The absorbent core does not include the acquisition and/or distribution system or any other components of the absorbent article which are not either integral part of the core wrap or core bag or placed within the core wrap or core bag. The absorbent core may comprise, consist essentially of, or consist of, a core wrap, an absorbent material (e.g., superabsorbent polymers and little or no cellulose fibers) as discussed, and glue.
The absorbent core 228 may comprise an absorbent material with a high amount of superabsorbent polymers (herein abbreviated as “SAP”) enclosed within the core wrap. The SAP content may represent 70%-100% or at least 70%, 75%, 80%, 85%, 90%, 95%, 99%, or 100%, by weight of the absorbent material, contained in the core wrap. The core wrap is not considered as absorbent material for the purpose of assessing the percentage of SAP in the absorbent core. The absorbent core may contain airfelt with or without superabsorbent polymers.
By “absorbent material” it is meant a material which has some absorbency property or liquid retaining properties, such as SAP, cellulosic fibers as well as synthetic fibers. Typically, glues used in making absorbent cores have no or little absorbency properties and are not considered as absorbent material. The SAP content may be higher than 80%, for example at least 85%, at least 90%, at least 95%, at least 99%, and even up to and including 100% of the weight of the absorbent material contained within the core wrap. This airfelt-free core is relatively thin compared to a conventional core typically comprising between 40-60% SAP by weight and a high content of cellulose fibers. The absorbent material may in particular comprises less than 15% weight percent or less than 10% weight percent of natural, cellulosic, or synthetic fibers, less than 5% weight percent, less than 3% weight percent, less than 2% weight percent, less than 1% weight percent, or may even be substantially free of natural, cellulosic, and/or synthetic fibers.
As referenced above, the airfelt-free cores with very little or no natural, cellulosic and/or synthetic fibers are quite thin compared to conventional cores, thereby making the overall absorbent article thinner than absorbent articles with cores comprising mixed SAP and cellulosic fibers (e.g., 40-60% cellulose fibers). This core thinness can lead to consumer perceptions of reduced absorbency and performance, although technically this is not the case. Presently, these thin cores have typically been used with substantially planer or apertured topsheets. Furthermore, absorbent articles having these thin airfelt-free cores have reduced capillary void space since there is little or no natural, cellulosic, or synthetic fibers in the cores. Thus, there may sometimes not be enough capillary void space in the absorbent article to fully accept multiple insults of bodily exudates or a single large insult.
To solve such problems, the present disclosure provides absorbent articles with these thin airfelt-free cores in combination with one of the high-loft, three-dimensional nonwoven materials described herein as a topsheet or as a topsheet and acquisition layer laminate. In such an instance, consumer perception of absorbency and performance, through the increased thickness of the absorbent article owing to the additional thickness provided by the high-loft, three-dimensional nonwoven material, is increased. Furthermore, the three-dimensional nonwoven materials, when used with these thin airfelt-free cores and as the topsheet or the topsheet and acquisition layer laminate, add capillary void space back into the absorbent articles, while still allowing for minimal stack heights, thereby passing cost savings onto consumers and manufactures. As such, the absorbent articles of the present disclosure may easily absorb multiple bodily exudate insults or single large insults owing to this increased capillary void space. Additionally, absorbent articles that comprise the nonwoven materials as the topsheet or the topsheet and acquisition layer laminate provide consumers with an aesthetically pleasing topsheet relative to a planer topsheet or an apertured topsheet with an increased thickness and thus the consumer perceptions of absorbency and performance.
The example absorbent core 228 of the absorbent article 220 of
The absorbent core may comprise adhesive, for example, to help immobilizing the SAP within the core wrap and/or to ensure integrity of the core wrap, in particular when the core wrap is made of two or more substrates. The adhesive may be a hot melt adhesive, supplied, by H. B. Fuller, for example. The core wrap may extend to a larger area than strictly needed for containing the absorbent material within.
The absorbent material may be a continuous layer present within the core wrap. Alternatively, the absorbent material may be comprised of individual pockets or stripes of absorbent material enclosed within the core wrap. In the first case, the absorbent material may be, for example, obtained by the application of a single continuous layer of absorbent material. The continuous layer of absorbent material, in particular of SAP, may also be obtained by combining two absorbent layers having discontinuous absorbent material application patterns, wherein the resulting layer is substantially continuously distributed across the absorbent particulate polymer material area, as disclosed in U.S. Pat. Appl. Pub. No. 2008/0312622A1 (Hundorf), for example. The absorbent core 228 may comprise a first absorbent layer and a second absorbent layer. The first absorbent layer may comprise the first material 216 and a first layer 261 of absorbent material, which may be 100% or less of SAP. The second absorbent layer may comprise the second material 216′ and a second layer 262 of absorbent material, which may also be 100% or less of SAP. The absorbent core 228 may also comprise a fibrous thermoplastic adhesive material 251 at least partially bonding each layer of absorbent material 261, 262 to its respective material 216 or 216′. This is illustrated in
The fibrous thermoplastic adhesive material 251 may be at least partially in contact with the absorbent material 261, 262 in the land areas and at least partially in contact with the materials 216 and 216′ in the junction areas. This imparts an essentially three-dimensional structure to the fibrous layer of thermoplastic adhesive material 251, which in itself is essentially a two-dimensional structure of relatively small thickness, as compared to the dimension in length and width directions. Thereby, the fibrous thermoplastic adhesive material may provide cavities to cover the absorbent material in the land areas, and thereby immobilizes this absorbent material, which may be 100% or less of SAP.
The thermoplastic adhesive used for the fibrous layer may have elastomeric properties, such that the web formed by the fibers on the SAP layer is able to be stretched as the SAP swell.
The SAP useful with the present disclosure may include a variety of water-insoluble, but water-swellable polymers capable of absorbing large quantities of fluids.
The superabsorbent polymer may be in particulate form so as to be flowable in the dry state. Particulate absorbent polymer materials may be made of poly(meth)acrylic acid polymers. However, starch-based particulate absorbent polymer material may also be used, as well as polyacrylamide copolymer, ethylene maleic anhydride copolymer, cross-linked carboxymethylcellulose, polyvinyl alcohol copolymers, cross-linked polyethylene oxide, and starch grafted copolymer of polyacrylonitrile.
The SAP may be of numerous shapes. The term “particles” refers to granules, fibers, flakes, spheres, powders, platelets and other shapes and forms known to persons skilled in the art of superabsorbent polymer particles. The SAP particles may be in the shape of fibers, i.e., elongated, acicular superabsorbent polymer particles. The fibers may also be in the form of a long filament that may be woven. SAP may be spherical-like particles. The absorbent core may comprise one or more types of SAP.
For most absorbent articles, liquid discharges from a wearer occur predominately in the front half of the absorbent article, in particular for a diaper. The front half of the article (as defined by the region between the front edge and a transversal line placed at a distance of half L from the front waist edge 210 or rear waist edge 212) may therefore comprise most of the absorbent capacity of the core. Thus, at least 60% of the SAP, or at least 65%, 70%, 75%, 80%, or 85% of the SAP may be present in the front half of the absorbent article, while the remaining SAP may be disposed in the rear half of the absorbent article. Alternatively, the SAP distribution may be uniform through the core or may have other suitable distributions.
The total amount of SAP present in the absorbent core may also vary according to expected user. Diapers for newborns may require less SAP than infant, child, or adult incontinence diapers. The amount of SAP in the core may be about 5 to 60 g or from 5 to 50 g. The average SAP basis weight within the (or “at least one”, if several are present) deposition area 8 of the SAP may be at least 50, 100, 200, 300, 400, 500 or more g/m2. The areas of the channels (e.g., 226, 226′, 227, 227′) present in the absorbent material deposition area 8 are deduced from the absorbent material deposition area to calculate this average basis weight.
The core wrap may be made of a single substrate, material, or nonwoven folded around the absorbent material, or may comprise two (or more) substrates, materials, or nonwovens which are attached to another. Typical attachments are the so-called C-wrap and/or sandwich wrap. In a C-wrap, as illustrated, for example, in
The core wrap may be formed by any materials suitable for receiving and containing the absorbent material. Typical substrate materials used in the production of conventional cores may be used, in particular paper, tissues, films, wovens or nonwovens, or laminates or composites of any of these.
The substrates may also be air-permeable (in addition to being liquid or fluid permeable). Films useful herein may therefore comprise micro-pores.
The core wrap may be at least partially sealed along all the sides of the absorbent core so that substantially no absorbent material leaks out of the core. By “substantially no absorbent material” it is meant that less than 5%, less than 2%, less than 1%, or about 0% by weight of absorbent material escape the core wrap. The term “seal” is to be understood in a broad sense. The seal does not need to be continuous along the whole periphery of the core wrap but may be discontinuous along part or the whole of it, such as formed by a series of seal points spaced on a line. A seal may be formed by gluing and/or thermal bonding.
If the core wrap is formed by two substrates 216, 216′, four seals may be used to enclose the absorbent material 260 within the core wrap. For example, a first substrate 216 may be placed on one side of the core (the top side as represented in
The core wrap may also be formed by a single substrate which may enclose as in a parcel wrap the absorbent material and be sealed along the front side and rear side of the core and one longitudinal seal.
The absorbent material deposition area 208 may be defined by the periphery of the layer formed by the absorbent material 260 within the core wrap, as seen from the top side of the absorbent core. The absorbent material deposition area 208 may have various shapes, in particular, a so-called “dog bone” or “hour-glass” shape, which shows a tapering along its width towards the middle or “crotch” region of the core. In this way, the absorbent material deposition area 8 may have a relatively narrow width in an area of the core intended to be placed in the crotch region of the absorbent article, as illustrated in
The absorbent material deposition area 208 may comprise at least one channel 226, which is at least partially oriented in the longitudinal direction of the article 280 (i.e., has a longitudinal vector component) as shown in
In some instances, the channels may be present at least at the same longitudinal level as the crotch point C or the lateral axis 260 in the absorbent article, as represented in
The absorbent core 228 may also comprise more than two channels, for example, at least 3, at least 4, at least 5, or at least 6 or more. Shorter channels may also be present, for example in the rear waist region 206 or the front waist region 205 of the core as represented by the pair of channels 227, 227′ in
The channels may be particularly useful in the absorbent core when the absorbent material deposition area is rectangular, as the channels may improve the flexibility of the core to an extent that there is less advantage in using a non-rectangular (shaped) core. Of course channels may also be present in a layer of SAP having a shaped deposition area.
The channels may be completely oriented longitudinally and parallel to the longitudinal axis or completely oriented transversely and parallel to the lateral axis, but also may have at least portions that are curved.
In order to reduce the risk of fluid leakages, the longitudinal main channels may not extend up to any of the edges of the absorbent material deposition area 208, and may therefore be fully encompassed within the absorbent material deposition area 208 of the core. The smallest distance between a channel and the closest edge of the absorbent material deposition area 208 may be at least 5 mm.
The channels may have a width Wc along at least part of their length which is at least 2 mm, at least 3 mm, at least 4 mm, up to for example 20 mm, 16 mm, or 12 mm, for example. The width of the channel(s) may be constant through substantially the whole length of the channel or may vary along its length. When the channels are formed by absorbent material-free zone within the absorbent material deposition area 208, the width of the channels is considered to be the width of the material free zone, disregarding the possible presence of the core wrap within the channels. If the channels are not formed by absorbent material free zones, for example mainly though bonding of the core wrap through the absorbent material zone, the width of the channels is the width of this bonding.
At least some or all of the channels may be permanent channels, meaning their integrity is at least partially maintained both in the dry state and in the wet state. Permanent channels may be obtained by provision of one or more adhesive materials, for example, the fibrous layer of adhesive material or construction glue that helps adhere a substrate with an absorbent material within the walls of the channel. Permanent channels may also be formed by bonding the upper side and lower side of the core wrap (e.g., the first substrate 216 and the second substrate 216′) and/or the topsheet 224 to the backsheet 225 together through the channels. Typically, an adhesive may be used to bond both sides of the core wrap or the topsheet and the backsheet through the channels, but it is possible to bond via other known processes, such as pressure bonding, ultrasonic bonding, heat bonding, or combination thereof. The core wrap or the topsheet 224 and the backsheet 225 may be continuously bonded or intermittently bonded along the channels. The channels may advantageously remain or become visible at least through the topsheet and/or backsheet when the absorbent article is fully loaded with a fluid. This may be obtained by making the channels substantially free of SAP, so they will not swell, and sufficiently large so that they will not close when wet. Furthermore, bonding the core wrap to itself or the topsheet to the backsheet through the channels may be advantageous.
The absorbent article may comprise a pair of barrier leg cuffs 34. Each barrier leg cuff may be formed by a piece of material which is bonded to the absorbent article so it may extend upwards from a wearer-facing surface of the absorbent article and provide improved containment of fluids and other body exudates approximately at the junction of the torso and legs of the wearer. The barrier leg cuffs are delimited by a proximal edge 64 joined directly or indirectly to the topsheet 224 and/or the backsheet 225 and a free terminal edge 266, which is intended to contact and form a seal with the wearer's skin. The barrier leg cuffs 234 extend at least partially between the front waist edge 210 and the rear waist edge 212 of the absorbent article on opposite sides of the longitudinal axis 280 and are at least present at the level of the crotch point (C) or crotch region. The barrier leg cuffs may be joined at the proximal edge 264 with the chassis of the article by a bond 265 which may be made by gluing, fusion bonding, or a combination of other suitable bonding processes. The bond 265 at the proximal edge 264 may be continuous or intermittent. The bond 265 closest to the raised section of the leg cuffs delimits the proximal edge 264 of the standing up section of the leg cuffs.
The barrier leg cuffs may be integral with the topsheet 224 or the backsheet 225 or may be a separate material joined to the article's chassis. Each barrier leg cuff 234 may comprise one, two or more elastic strings 235 close to the free terminal edge 266 to provide a better seal.
In addition to the barrier leg cuffs 234, the article may comprise gasketing cuffs 232, which are joined to the chassis of the absorbent article, in particular to the topsheet 224 and/or the backsheet 225 and are placed externally relative to the barrier leg cuffs. The gasketing cuffs 232 may provide a better seal around the thighs of the wearer. Each gasketing leg cuff may comprise one or more elastic strings or elastic elements 233 in the chassis of the absorbent article between the topsheet 224 and backsheet 225 in the area of the leg openings. All, or a portion of, the barrier leg cuffs and/or gasketing cuffs may be treated with a lotion or another skin care composition.
The absorbent articles of the present disclosure may comprise an acquisition-distribution layer or system 250 (“ADS”). One function of the ADS is to quickly acquire one or more of the fluids and distribute them to the absorbent core in an efficient manner. The ADS may comprise one, two or more layers, which may form a unitary layer or may remain as discrete layers which may be attached to each other. In an example, the ADS may comprise two layers: a distribution layer 254 and an acquisition layer 252 disposed between the absorbent core and the topsheet, but the present disclosure is not so limited.
In one example, the high loft, three-dimensional nonwoven materials of the present disclosure may comprise the topsheet and the acquisition layer as a laminate. A distribution layer may also be provided on the garment-facing side of the topsheet/acquisition layer laminate.
In an instance where the high loft, three-dimensional nonwoven materials of the present disclosure encompass a topsheet and acquisition layer laminate, the distribution layer may need to be supported by a carrier layer (not illustrated) that may comprise one or more nonwoven materials or other materials. The distribution layer may be applied to or positioned on the carrier layer. As such, the carrier layer may be positioned intermediate the acquisition layer and the distribution layer and be in a facing relationship with the acquisition layer and the distribution layer.
The distribution layer of the ADS may comprise at least 50% by weight of cross-linked cellulose fibers. The cross-linked cellulosic fibers may be crimped, twisted, or curled, or a combination thereof including crimped, twisted, and curled. This type of material is disclosed in U.S. Pat. Publ. No. 2008/0312622 A1 (Hundorf). The cross-linked cellulosic fibers provide higher resilience and therefore higher resistance to the first absorbent layer against the compression in the product packaging or in use conditions, e.g., under wearer weight. This may provide the core with a higher void volume, permeability, and liquid absorption, and hence reduced leakage and improved dryness.
The distribution layer comprising the cross-linked cellulose fibers of the present disclosure may comprise other fibers, but this layer may advantageously comprise at least 50%, or 60%, or 70%, or 80%, or 90%, or even up to 100%, by weight of the layer, of cross-linked cellulose fibers (including the cross-linking agents).
If a three-dimensional nonwoven material of the present disclosure is provided as only the topsheet of an absorbent article, the ADS 250 may comprise an acquisition layer 252. The acquisition layer may be disposed between the distribution layer 254 and the topsheet 224. In such an instance, the acquisition layer 252 may be or may comprise a nonwoven material, such as a hydrophilic SMS or SMMS material, comprising a spunbonded, a melt-blown and a further spunbonded layer or alternatively a carded staple fiber chemical-bonded nonwoven. The nonwoven material may be latex bonded.
The absorbent article may comprise a fastening system. The fastening system may be used to provide lateral tensions about the circumference of the absorbent article to hold the absorbent article on the wearer as is typical for taped diapers. This fastening system may not be necessary for training pant articles since the waist region of these articles is already bonded. The fastening system may comprise a fastener such as tape tabs, hook and loop fastening components, interlocking fasteners such as tabs & slots, buckles, buttons, snaps, and/or hermaphroditic fastening components, although any other suitable fastening mechanisms are also within the scope of the present disclosure. A landing zone 244 is normally provided on the garment-facing surface of the front waist region 205 for the fastener to be releasably attached thereto.
The absorbent article may comprise front ears 246 and rear ears 240. The ears may be an integral part of the chassis, such as formed from the topsheet 224 and/or backsheet 226 as side panels. Alternatively, as represented on
The absorbent article 220 may also comprise at least one elastic waist feature (not represented) that helps to provide improved fit and containment. The elastic waist feature is generally intended to elastically expand and contract to dynamically fit the wearer's waist. The elastic waist feature may extend at least longitudinally outwardly from at least one waist edge of the absorbent core 228 and generally forms at least a portion of the end edge of the absorbent article. Disposable diapers may be constructed so as to have two elastic waist features, one positioned in the front waist region and one positioned in the rear waist region.
In a form, the absorbent articles of the present disclosure may have different colors in different layers, or portions thereof (e.g., the topsheet and the acquisition layer, the topsheet and the nonwoven core cover, a first portion and a second portion of a topsheet, a first portion and second portion of the acquisition layer). The different colors may be shade of the same color (e.g., dark blue and light blue) or may be actual different colors (e.g., purple and green). The different colors may have a Delta E in the range of about 1.5 to about 10, about 2 to about 8, or about 2 to about 6, for example. Other Delta E ranges are also within the scope of the present disclosure.
In an instance, various layers of the absorbent articles may be joined using a colored adhesive. The colored adhesive may be laid down on any suitable layer or layers in a pattern. The pattern of the adhesive may or may not complement the pattern of the topsheet. Such a pattern may increase the appearance of depth in an absorbent article. In certain instances, the colored adhesive may be blue.
In other instances, any of the layers may comprise indicia, such as a printed ink to aid in the appearance, depth impression, absorbency impression, or quality impression of the absorbent articles.
In other instances, the colors may be complimentary, or registered with, the patterns of three-dimensional features of the nonwoven fabric 10 utilized as a component in an absorbent article. For example, a fabric having first and second zones of visually distinct patterns of three-dimensional features may also have printed thereon color to emphasize, highlight, contrast with, or otherwise change the visual appearance of the fabric 10. The color enhancements can be beneficial in communicating to a user of an absorbent article certain functional characteristics of the nonwoven fabric 10 when in use. Thus color can be used in combination with structural, three-dimensional features in one component, or in combinations of components to deliver a visually distinctive absorbent article. For example, a secondary topsheet or acquisition layer may have printed thereon a pattern of color or colors that compliments the pattern of three-dimensional features of a fabric 10 utilized as a topsheet in an absorbent article. Another example is an absorbent article comprising 1) an absorbent core comprising a channel, 2) a topsheet with a three dimensional pattern registered or highlighting the channel or channels in the core, and 3) a graphic, colored component, printed ink, or indicia visible from the topsheet viewing (body contacting surface) or the backsheet viewing surface (garment facing surface) to further emphasize the functional features of the core channel or channels and the overall performance of the absorbent article.
Further characterization of the novel aspects of the present disclosure can be realized by focusing on the three-dimensional features within a visually discernible zone. Each zone, such as Zones 110, 120, and 130, discussed above, can be described further with respect to microzones. A microzone is a portion of the nonwoven fabric 10 within a zone, that has at least two visually discernible regions and there is a common intensive property difference between these two regions. A microzone may comprise a portion of the nonwoven fabric 10 which crosses two or more zone boundaries that has at least two visually discernible regions and there is a common intensive property difference between these two regions
The benefit of considering microzones in the present disclosure is to illustrate that in addition to differences in average intensive properties with a zone, such as zones 110, 120, and 130, as discussed above, the present disclosure also provides for fabrics having differences in actual and/or average intensive properties between regions defined by the three-dimensional features within a zone, with the three-dimensional features precisely placed according to the design of the forming belt used to produce the fabrics. The difference between intensive properties between regions of the three-dimensional features provides for additional visual as well as functional benefits. The sharp visual contrast between regions can provide for extremely fine visually distinctive designs within a zone and between zones. Likewise, the precise placement of regions afforded by the precisely manufactured forming belt can provide for excellent and tailored softness, strength, and fluid handling properties of the zones. Thus, the invention in one embodiment provides for the unexpected combination of differences in average intensive properties between zones and simultaneously differences in intensive properties of the regions making up a microzone.
Regions defined by three-dimensional features can be understood with reference to
In
The invention of the disclosure permits beneficial characteristics best expressed with respect to the regions defined by three-dimensional features in microzones. For example, as shown in
The portion of nonwoven fabric 10 shown in
Regardless of which zone, or which zonal boundary a particular microzone encompasses, the three-dimensional features can be characterized by the differences between intensive properties of the regions defined by them. In general, the nonwoven of the present disclosure can be a spunbond nonwoven fabric having a first surface defining a plane of the first surface. The fabric can have a plurality of three-dimensional features, each three dimensional feature defining a first region and a second region, the regions having a common intensive property that has a different value between them. In an embodiment, the first region can be distinguished as being at a higher elevation than the second region with respect to the plane of the first surface, hence exhibiting a difference in each region's common intensive property of thickness. The two regions can also be distinguished as having different densities, basis weights, and volumetric densities. That is, the two regions can be distinguished within a micro zone of the spunbond nonwoven fabric as being different with respect to common intensive properties, including properties such as thickness, density, basis weight, and volumetric density. In an embodiment one or both regions of a microzone can be fluid permeable. In an embodiment, the higher density region of a microzone can be fluid permeable.
Within zone 110 of the portion of fabric shown in
Likewise, within zone 130 of the portion of fabric shown in
Additionally, within zone 120 of the portion of fabric shown in
Further, a zone that encompasses the boundary between zones 120 and 130 of the portion of fabric shown in
Microzones are discussed in more detail with reference to
As shown in
The Micro-CT scan permits the image to be “cut” and cross-sectioned, as shown by the cut plane 450 in
The Micro-CT technology permits intensive properties to be precisely and directly measured. Thickness measurements can be made directly from imaged cross sections based on the scale magnification, such as the cross section shown in
The graphs shown in
Thus, with reference to
The four representative microzones from two zones are shown in Tables 4-6 for illustration. But as can be understood, each pair of first and second regions in
A microzone spanning two zones, such as zones 110 and zone 130, can have an even greater difference in intensive properties relative to a microzone within a single zone. For example, viewing the data for a microzone spanning a first region of zone 130, for example at first region 32, and a second region of zone 110, for example at second region 8, the microzone exhibits dramatic differences in all of thickness, basis weight and volumetric density. The thickness of first region 32 of zone 130 is about 2100 microns, while the thickness of second region 8 of zone 110 is about 29 microns, or about a 72× differential. Likewise, the basis weight of first region 32 of zone 130 can be as high as 150 gsm, while the basis weight of second region 8 of zone 110 can be about 14 gsm, or about a 1× differential. Further, the volumetric density of first region 32 of zone 130 can be about 0.069 g/cc, while the volumetric density of second region 8 of zone 110 can be 0.492 g/cc, or about a 7× differential.
For each of the measured intensive property parameters of the various regions of a microzone, such a measurement is done using the micro CT method described herein. The resolution of the method supports establishing the intensive properties of microzone regions so differences and ratios comparisons of regions as described herein can be dimensioned.
Further characterization of a fabric 10 can be made with reference to
As can best be seen in
Even in the microzones with the greatest thickness differential, this “bond skinning” effect serves the purpose of maintaining web integrity, while not significantly impacting softness, or other beneficial properties such as fluid handling properties. As can be understood with reference to
Microzones, therefore, play a significant role in the overall physical structure and functioning of a fabric 10 of the present invention. Producing relatively closely spaced, precisely designed three-dimensional features, enabled by the forming belt of the present disclosure, a fabric 10 can exhibit visually distinct zones, microzones, and three-dimensional features that provide for functional superiority in the areas of, at least, softness and fluid handling, as well as visually attractive aesthetic designs. The potential difference in physical properties of the first and second surfaces permits the nonwoven fabric 10 to be designed for both strength and softness, both form and function.
The graphs shown in
In general, regions of a microzone can have broadly varying values for basis weight, thickness, and volumetric density.
Thus, with reference to
The differences in certain intensive properties for point bond microzones can be seen in
Bond points 90 may play a significant role in the overall physical structure and functioning of a fabric 10 of the present invention. By adding bond points 90 to the fabric 10 comprising relatively closely spaced, precisely designed three-dimensional features, enabled by the forming belt of the present disclosure, a fabric 10 can be further improved to exhibit an unexpected combination of visually distinct zones, microzones, and three-dimensional features that provide for functional superiority in the high performance combination of softness, strength, low fuzz, and fluid handling, as well as visually attractive aesthetic designs. The bond point feature provides for a nonwoven fabric 10 to be designed for the highest combined performance of strength, softness, fluid handling, and visual aesthetics, especially considering both form and function.
One benefit of the shaped nonwoven webs of the present disclosure is improved softness. Softness can be measured using the Emtec Tissue Softness Analyzer, available from Emtec Paper Testing Technology. Emtec Electronic, GmbH. Table 5 below shows softness values as TS7 measurements from the Emtec Tissue Softness Analyzer, according to the Emtec Test Method below. For all of the Examples 7-9 below, the nonwoven was made on a belt as described in
A bicomponent spunbond nonwoven fabric web was produced by spinning a 50:50 ratio of polyethylene sheath (Aspun-6850-A obtained from Dow chemical company) and polypropylene core (PH-835 obtained from LyondellBasell) in a trilobal fiber configuration, as discussed above with reference to Example 2. The nonwoven fabric was spun on a forming belt having a repeating pattern as described in
A bicomponent spunbond nonwoven fabric that was produced by spinning a 30:70 ratio of polyethylene sheath (Aspun-6850-A obtained from Dow chemical company) and polypropylene core (HG475 FP obtained from Borealis) in a round fiber configuration, using a dual beam spunbond process, as described in
A bicomponent spunbond nonwoven fabric that was produced by spinning a 30:70 ratio of polyethylene sheath (Aspun-6850-A obtained from Dow chemical company) and polypropylene core (HG475 FP obtained from Borealis) in a round fiber configuration, using a dual beam spunbond process, as described in
Examples 7-9 are representative of shaped nonwoven fabrics of the present disclosure that exhibit an improved softness, as indicated by the Emtec measurements. The Emtec measured values can be from about 1 dB V2 rms to about 15 dB V2 rms, or from about 3 dB V2 rms to about 10 dB V2 rms, or from about 5 dB V2 rms to about 8 dB V2 rms. In general, the Emtec measured values for either the first surface or the second surface can be any integer value up to about 15 dB V2 rms, and any range of integers between 1 and 15. Further, in general, the ratio of the measured Emtec value for the first side to the second side can be between 1 and 3 and any real number between 1 and 3.
Without being bound by theory, it is believed that the improvement in softness exhibited by the shaped nonwoven fabrics of the present invention is achieved the method and apparatus of the invention which permits for differential intensive properties in relatively small zones, including the disclosed zones and microzones. The ability to design and make shaped nonwoven fabrics with the disclosed differences in basis weight, density, or thickness, for example, while simultaneously delivering a consolidated fabric useful for topsheets in absorbent articles, for example, breaks a previously held technical contradictions between surface texture and softness. That is, the shaped nonwoven fabrics of the present disclosure may deliver visibly noticeable surface texture, including in irregular patterns, as well as superior softness, as indicated by measured Emtec values. Additionally, the shaped nonwoven fabrics of the present disclosure may deliver visibly noticeable surface texture in combination physical integrity and reduced fuzzing properties, as well as superior softness, as indicated by measured Emtec values.
As discussed above, in an example, a process for making a shaped nonwoven fabric can be a modified version of the process described with respect to
After spinning fibers onto belt 60, and after being compacted, including optionally thermally bonding during compaction as described above, the shaped nonwoven web can be subject to additional heating by through-air heater 76, which can have multiple chambers, such as three chambers 76A. 76B and 76C, each independently temperature controlled.
Examples 7 and 9 above were fabricated on a twin beam process line and through-air bonded in a process schematically shown in
In addition to the benefits detailed above, another benefit of the shaped nonwoven webs of the present disclosure is the ability to provide a nonwoven web with microzones that have a hydrophobic region and a separate hydrophilic region. The hydrophilicity and/or hydrophobicity in a particular region of the microzone can be determined by a Time to Wick measurement using the Time to Wick Test Method as described herein and/or a Contact Angle measurement using the Contact Angle Test Method as described herein. As used herein, the term “hydrophilic”, in reference to a particular region of the microzone, means that when tested using the Time to Wick Test Method, the Time to Wick for that particular region is less than 10 seconds. As used herein, the term “hydrophobic”, in reference to a particular region of the microzone, means that when tested using the Contact Angle Test Method, the Contact Angle for that particular region is 90° or greater.
Table 6 below details Contact Angle and Time to Wick measurements for shaped nonwovens as detailed herein. For both Examples 10 and 11 below, the nonwoven was made on a belt as described in
A bicomponent spunbond nonwoven fabric web was produced by spinning a 50:50 ratio of polyethylene sheath (Aspun-6850-A obtained from Dow chemical company) and polypropylene core (PH-835 obtained from LyondellBasell) in a trilobal fiber configuration, as discussed above with reference to Example 2. The nonwoven fabric was spun on a forming belt having a repeating pattern as described in
A surfactant, Stantex S 6327 (a combination of castor oil ethoxylates with PEG diesters), supplied by Pulcra Chemicals, was then disposed on the back side surface of the nonwoven fabric (i.e., the flat side surface opposite the side with the relatively pillowy three-dimensional features disposed thereon) through a kiss coating process. The coating process was performed using a Reicofil Kiss Roll and Omega drying process, both of which are commonly known in the art. The surfactant used in the kiss roll process was at a 6% surfactant concentration in water at a temperature of 40° C. The kiss roll contact angle was set at 250° and the drying temperature was 80° C. The nonwoven fabric was then brought into contact with the kiss roll operating at a speed of 13 rpm, delivering 0.45 wt % surfactant to the nonwoven fabric (% surfactant is weight of added surfactant per 1 m2 divided by weight of 1 m2 nonwoven fabric).
A bicomponent spunbond nonwoven fabric web was produced by spinning a 50:50 ratio of polyethylene sheath (Aspun-6850-A obtained from Dow chemical company) and polypropylene core (PH-835 obtained from LyondellBasell) in a trilobal fiber configuration, as discussed above with reference to Example 2. The nonwoven fabric was spun on a forming belt having a repeating pattern as described in
A surfactant, Stantex S 6327 (a combination of castor oil ethoxylates with PEG diesters), supplied by Pulcra Chemicals, was then disposed on the front side surface of the nonwoven fabric (i.e., the side with the relatively pillowy three-dimensional features disposed thereon) through an inkjet printing process. The inkjet printing process was performed using a Dimatix DMP 2831 inkjet printer, fitted with a cartridge model #DMC-11610/PM 700-10702-01 (10pL). The print head temperature was 40° C. The surfactant used in the inkjet printing process consisted of 75% w/w Stantex S 6327 and 25% w/w Ethanol. Surfactant was printed in the second regions of the microzones of the nonwoven fabric by orienting the nonwoven fabric sample such that the second regions of a first row of microzones were aligned with the print head direction and printing a first series of straight lines, with droplet spacing adjusted to 170 um. The nonwoven fabric sample was then turned by an angle such that the second regions of a second row of microzones were aligned with the print head and a second series of straight lines were printed at 170 um. The basis weight of the fibers of the second region is about 16.0 gsm. The basis weight of the surfactant that was inkjet printed onto the second region is about 0.25 gsm. Accordingly, the amount of surfactant printed locally on the second region was determined to be about 1.6 wt % surfactant (0.25 gsm/16.0 gsm). Overall, the amount of surfactant printed on the nonwoven fabric sample was determined by the ratio between printed line width and line spacing to be at about 0.2 wt % surfactant.
In addition to Stantex S 6327, the use of other surfactants to render first and/or second regions of particular microzones hydrophilic and/or hydrophobic (though any application method) is considered within the scope of this disclosure. Other potential surfactants to be used in the processes and nonwoven fabrics detailed here include non-ionic surfactants including esters, amides, carboxylic acids, alcohols, ethers—polyoxyethylene, polyoxypropylene, sorbitan, ethoxylated fatty alcohols, alyl phenol polyethoxylates, lecithin, glycerol esters and their ethoxylates, and sugar based surfactants (polysorbates, polyglycosides), and anionic surfactants including sulfonates, sulfates, phosphates, alkali metal salts of fatty acids, fatty alcohol monoesters of sulfuric acid, linear alkyl benzene sulfonates, alkyl diphenyloxide sulfonates, lignin sulfonates, olefin sulfonates, sulfosuccinates, and sulfated ethoxylates of fatty alcohols, and cationic surfactants including amines (primary, secondary, tertiary), quaternary ammoniums, pyridinium, quaternary ammonium salts—QUATS, alkylated pyridinium salts, alkyl primary, secondary, tertiary amines, and alkanolamides, and zwiterionic surfactants including amino acids and derivatives, amine oxide, betaines, and alkyl amine oxides, and polymeric surfactants including polyamines, carboxylic acid polymers and copolymers, EO/PO block copolymers, ethylene oxide polymers and copolymers, and polyvinylpyrrolidone, and silicone surfactants including dimethyl siloxane polymers with hydrophile, and perfluorocarboxylic acid salts and fluorosurfactants.
The shaped nonwoven fabrics detailed above have microzones with regions having differences in intensive properties, such as basis weight, density, or thickness, for example. Those same shaped nonwoven fabrics can also simultaneously have such regions of the microzones that are particularly and separately hydrophobic and/or hydrophilic. Any of the shaped nonwoven fabric examples detailed herein (e.g., samples that include zones and/or microzones with regions having differences in thickness, basis weight and/or volumetric density, and/or surfaces with the various TS7 values disclosed herein) can further have regions of a microzone with differences in hydrophilicity as detailed herein. Hydrophilicity can be provided through targeted application(s) of surfactant(s) onto particular regions of the microzones of the shaped nonwoven fabric. For example, the second region of a microzone may have surfactant disposed thereon, while the first region of the same microzone may have no surfactant disposed thereon. Moreover, the first region of a microzone may have surfactant disposed thereon, while the second region of the same microzone may have no surfactant disposed thereon. For instance, in one microzone, the first or second region may have from about 0.01% to about 5.0%, about 0.05% to about 4.0%, about 1.0% to about 3.0%, and any concentric range within the range of about 0.01% to about 5.0% surfactant, and the other region has no surfactant (i.e., surfactant free). As an example, in one microzone, the second region may have from about 0.01% to about 5.0%, about 0.05% to about 4.0%, about 1.0% to about 3.0%, and any concentric range within the range of about 0.01% to about 5.0% surfactant, and the first region has no surfactant (i.e., surfactant free). Accordingly, some shaped nonwoven fabrics disclosed herein have a microzone with at least one of the first and second regions having a surfactant, and the ratio of % surfactant in the first region to % surfactant in the second region is less than 1. Further, some shaped nonwoven fabrics disclosed herein have a microzone with at least the second region of the microzone having a surfactant, and the ratio of % surfactant in the first region to % surfactant in the second region is less than 1.
As another example, the second region of a microzone may have a particular amount of surfactant or % surfactant disposed thereon, while the first region of the same microzone may have a different amount of surfactant or % surfactant disposed thereon. For instance, in one microzone, the first region may have from about 0.01% to about 2.0%, about 0.05% to about 1.5%, about 0.1% to about 1.0%, and any concentric range within the range of about 0.01% to about 2.0% surfactant, and the second region may have a differing amount. Moreover, in one microzone, the second region may have from about 0.01% to about 5.0%, about 0.05% to about 4.0%, about 1.0% to about 3.0%, and any concentric range within the range of about 0.01% to about 5.0% surfactant, and the first region may have a differing amount. The % surfactant for a particular region of a microzone may be determined by taking the grams per square meter of surfactant disposed in the particular region and dividing it by the basis weight of the fibers of the shaped nonwoven fabric contained within the same region. The grams per square meter of surfactant disposed in a particular region may be determined using any currently known method in the art (e.g., gravimetric, etc.). The basis weight of the fibers of the shaped nonwoven fabric contained within a particular region of a microzone may also be determined using any currently known method in the art (e.g., gravimetric, micro-CT, etc.). For particular microzone examples, the basis weight ranges/examples of fibers contained in the first and second regions are detailed above.
A surfactant may be disposed on the shaped nonwoven fabrics by any method known in the art. Particular examples include kiss coating, inkjet printing, gravure printing, off-set gravure printing, flexo-graphic printing of the surfactant and registered printing of the surfactant. Any such method can dispose surfactant onto either the first and/or second surface of the shaped nonwoven fabrics. For the overall shaped nonwoven fabric (taking into account all of the individual zones and microzones on the fabric), the surfactant may be added to the shaped nonwoven fabric in an amount from about 0.01% to about 2.0%, about 0.05% to about 1.5%, about 0.1% to about 1.0%, and any concentric range within the range of about 0.01% to about 2.0%. To calculate % surfactant added to the overall shaped nonwoven fabric, divide the grams per square meter of surfactant in the overall shaped nonwoven fabric by the basis weight of the overall shaped nonwoven fabric. The grams per square meter of surfactant disposed in the overall shaped nonwoven fabric may be determined using any currently known method in the art (e.g., gravimetric, etc.). The basis weight of the overall shaped nonwoven fabric may also be determined using any currently known method in the art (e.g., gravimetric, micro-CT, etc.).
Referring again to
Shaped nonwoven fabrics having the above detailed microzones with regions having differences in basis weight, density, or thickness, for example, while also simultaneously having such regions of a particular microzone being separately hydrophobic and/or hydrophilic can provide many useful applications such as topsheet materials for baby care, fem care and adult incontinence products, as well as use in medical pads, wipes and cleaning pads, etc.
The dimensions and/or values disclosed herein are not to be understood as being strictly limited to the exact numerical dimension and/or values recited. Instead, unless otherwise specified, each such dimension and/or value is intended to mean both the recited dimension and/or value and a functionally equivalent range surrounding that dimension and/or value. For example, a dimension disclosed as “40 mm” is intended to mean “about 40 mm”.
Every document cited herein, including any cross referenced or related patent or application is hereby incorporated herein by reference in its entirety unless expressly excluded or otherwise limited. The citation of any document is not an admission that it is prior art with respect to any invention disclosed or claimed herein or that it alone, or in any combination with any other reference or references, teaches, suggests or discloses any such invention. Further, to the extent that any meaning or definition of a term in this document conflicts with any meaning or definition of the same term in a document incorporated by reference, the meaning or definition assigned to that term in this document shall govern.
While particular embodiments of the present invention have been illustrated and described, it would be obvious to those skilled in the art that various other changes and modifications can be made without departing from the spirit and scope of the invention. It is therefore intended to cover in the appended claims all such changes and modifications that are within the scope of this invention.
Aged Compression Method and Aged Caliper Measurement
(Average Aged Caliper/Average Initial Caliper)*100
Localized basis weight of the nonwoven fabric may be determined by several available techniques, but a simple representative technique involves a punch die having an area of 3.0 cm2 which is used to cut a sample piece of the web from the selected region from the overall area of a nonwoven fabric. The sample piece is then weighed and divided by its area to yield the localized basis weight of the nonwoven fabric in units of grams per meter squared. Results are reported as a mean of 2 samples per selected region.
The Fuzz Level Test is used to determine the quantity of fibers removed from a nonwoven materials under an abrasive force (i.e., the fuzz level).
The Fuzz Level Test utilizes the following materials:
Measure and cut aluminum oxide cloth to 7.5 in (19.0 cm) in length. Measure and cut pieces of 3M #3187 tape 6.5 inches (16.5 cm) in length, two tapes for each specimen. Fold under approximately 0.25 inch (0.6 cm) on each end of the 3M #3187 tape to facilitate handling. Lay 3M #3187 tape on the thick-style release paper for use later.
Before handling or testing any of the materials, wash hands with soap and water to remove excess oils from hands. Optionally, latex gloves may be worn. Cut a sample of the nonwoven fabric to be tested to a size at least 11 cm in the MD and 4 cm in the CD. Lay out the sample of nonwoven fabric to be tested with the side to be tested facing down. Cut a piece of 3M #409 two-sided tape off roll at least 11 cm long. Remove the backing and apply the side of two-sided tape that was facing the backing to the sample nonwoven fabric lengthwise in the machine direction (MD). Replace the backing over the exposed tape. Using the paper cutter, cut test samples within the taped area 11 cm MD and 4 cm CD.
For a given sample, add the weight in grams of fuzz collected from the aluminum oxide cloth and the weight in grams of fuzz collected from the abraded Sample nonwoven. Multiply the combined weight in grams by 1000 to convert to milligrams (mg). To convert this measurement from absolute weight loss to weight loss per unit area, divide the total weight of fuzz by the area of the abraded area.
The Air Permeability Test is used to determine the level of air flow in cubic feet per minute (cfm) through a forming belt. The Air Permeability Test is performed on a Textest Instruments model FX3360 Portair Air Permeability Tester, available from Textest AG, Sonnenbergstrasse 72, CH 8603 Schwerzenbach, Switzerland. The unit utilizes a 20.7 mm orifice plate for air permeability ranges between 300-1000 cfm. If air permeability is lower than 300 cfm the orifice plate needs to be reduced; if higher than 100 cfm the orifice plate needs to be increased. Air permeability can be measured in localized zones of a forming belt to determine differences in air permeability across a forming belt.
The in-bag stack height of a package of absorbent articles is determined as follows:
A thickness tester with a flat, rigid horizontal sliding plate is used. The thickness tester is configured so that the horizontal sliding plate moves freely in a vertical direction with the horizontal sliding plate always maintained in a horizontal orientation directly above a flat, rigid horizontal base plate. The thickness tester includes a suitable device for measuring the gap between the horizontal sliding plate and the horizontal base plate to within ±0.5 mm. The horizontal sliding plate and the horizontal base plate are larger than the surface of the absorbent article package that contacts each plate. i.e. each plate extends past the contact surface of the absorbent article package in all directions. The horizontal sliding plate exerts a downward force of 850±1 gram-force (8.34 N) on the absorbent article package, which may be achieved by placing a suitable weight on the center of the non-package-contacting top surface of the horizontal sliding plate so that the total mass of the sliding plate plus added weight is 850±1 grams.
Absorbent article packages are equilibrated at 23±2° C. and 50±5% relative humidity prior to measurement.
The horizontal sliding plate is raised and an absorbent article package is placed centrally under the horizontal sliding plate in such a way that the absorbent articles within the package are in a horizontal orientation (see
The micro-CT intensive property measurement method measures the basis weight, thickness and volumetric density values within visually discernable regions of a substrate sample. It is based on analysis of a 3D x-ray sample image obtained on a micro-CT instrument (a suitable instrument is the Scanco μCT 50 available from Scanco Medical AG, Switzerland, or equivalent). The micro-CT instrument is a cone beam microtomograph with a shielded cabinet. A maintenance free x-ray tube is used as the source with an adjustable diameter focal spot. The x-ray beam passes through the sample, where some of the x-rays are attenuated by the sample. The extent of attenuation correlates to the mass of material the x-rays have to pass through. The transmitted x-rays continue on to the digital detector array and generate a 2D projection image of the sample. A 3D image of the sample is generated by collecting several individual projection images of the sample as it is rotated, which are then reconstructed into a single 3D image. The instrument is interfaced with a computer running software to control the image acquisition and save the raw data. The 3D image is then analyzed using image analysis software (a suitable image analysis software is MATLAB available from The Mathworks. Inc., Natick, MA, or equivalent) to measure the basis weight, thickness and volumetric density intensive properties of regions within the sample.
Sample Preparation:
To obtain a sample for measurement, lay a single layer of the dry substrate material out flat and die cut a circular piece with a diameter of 30 mm.
If the substrate material is a layer of an absorbent article, for example a topsheet, backsheet nonwoven, acquisition layer, distribution layer, or other component layer; tape the absorbent article to a rigid flat surface in a planar configuration. Carefully separate the individual substrate layer from the absorbent article. A scalpel and/or cryogenic spray (such as Cyto-Freeze. Control Company. Houston TX) can be used to remove a substrate layer from additional underlying layers, if necessary, to avoid any longitudinal and lateral extension of the material. Once the substrate layer has been removed from the article proceed with die cutting the sample as described above.
If the substrate material is in the form of a wet wipe, open a new package of wet wipes and remove the entire stack from the package. Remove a single wipe from the middle of the stack, lay it out flat and allow it to dry completely prior to die cutting the sample for analysis.
A sample may be cut from any location containing the visually discernible zone to be analyzed. Within a zone, regions to be analyzed are ones associated with a three-dimensional feature defining a microzone. The microzone comprises a least two visually discernible regions. A zone, three-dimensional feature, or microzone may be visually discernable due to changes in texture, elevation, or thickness. Regions within different samples taken from the same substrate material can be analyzed and compared to each other. Care should be taken to avoid folds, wrinkles or tears when selecting a location for sampling.
Image Acquisition:
Set up and calibrate the micro-CT instrument according to the manufacturer's specifications. Place the sample into the appropriate holder, between two rings of low density material, which have an inner diameter of 25 mm. This will allow the central portion of the sample to lay horizontal and be scanned without having any other materials directly adjacent to its upper and lower surfaces. Measurements should be taken in this region. The 3D image field of view is approximately 35 mm on each side in the xy-plane with a resolution of approximately 5000 by 5000 pixels, and with a sufficient number of 7 micron thick slices collected to fully include the z-direction of the sample. The reconstructed 3D image resolution contains isotropic voxels of 7 microns. Images are acquired with the source at 45 kVp and 133 μA with no additional low energy filter. These current and voltage settings may be optimized to produce the maximum contrast in the projection data with sufficient x-ray penetration through the sample, but once optimized held constant for all substantially similar samples. A total of 1500 projections images are obtained with an integration time of 1000 ms and 3 averages. The projection images are reconstructed into the 3D image, and saved in 16-bit RAW format to preserve the full detector output signal for analysis.
Image Processing:
Load the 3D image into the image analysis software. Threshold the 3D image at a value which separates, and removes, the background signal due to air, but maintains the signal from the sample fibers within the substrate.
Three 2D intensive property images are generated from the threshold 3D image. The first is the Basis Weight Image. To generate this image, the value for each voxel in an xy-plane slice is summed with all of its corresponding voxel values in the other z-direction slices containing signal from the sample. This creates a 2D image where each pixel now has a value equal to the cumulative signal through the entire sample.
In order to convert the raw data values in the Basis Weight Image into real values a basis weight calibration curve is generated. Obtain a substrate that is of substantially similar composition as the sample being analyzed and has a uniform basis weight. Follow the procedures described above to obtain at least ten replicate samples of the calibration curve substrate. Accurately measure the basis weight, by taking the mass to the nearest 0.0001 g and dividing by the sample area and converting to grams per square meter (gsm), of each of the single layer calibration samples and calculate the average to the nearest 0.01 gsm. Following the procedures described above, acquire a micro-CT image of a single layer of the calibration sample substrate. Following the procedure described above process the micro-CT image, and generate a Basis Weight Image containing raw data values. The real basis weight value for this sample is the average basis weight value measured on the calibration samples. Next, stack two layers of the calibration substrate samples on top of each other, and acquire a micro-CT image of the two layers of calibration substrate. Generate a basis weight raw data image of both layers together, whose real basis weight value is equal to twice the average basis weight value measured on the calibration samples. Repeat this procedure of stacking single layers of the calibration substrate, acquiring a micro-CT image of all of the layers, generating a raw data basis weight image of all of the layers, the real basis weight value of which is equal to the number of layers times the average basis weight value measured on the calibration samples. A total of at least four different basis weight calibration images are obtained. The basis weight values of the calibration samples must include values above and below the basis weight values of the original sample being analyzed to ensure an accurate calibration. The calibration curve is generated by performing a linear regression on the raw data versus the real basis weight values for the four calibration samples. This linear regression must have an R2 value of at least 0.95, if not repeat the entire calibration procedure. This calibration curve is now used to convert the raw data values into real basis weights.
The second intensive property 2D image is the Thickness Image. To generate this image the upper and lower surfaces of the sample are identified, and the distance between these surfaces is calculated giving the sample thickness. The upper surface of the sample is identified by starting at the uppermost z-direction slice and evaluating each slice going through the sample to locate the z-direction voxel for all pixel positions in the xy-plane where sample signal was first detected. The same procedure is followed for identifying the lower surface of the sample, except the z-direction voxels located are all the positions in the xy-plane where sample signal was last detected. Once the upper and lower surfaces have been identified they are smoothed with a 15×15 median filter to remove signal from stray fibers. The 2D Thickness Image is then generated by counting the number of voxels that exist between the upper and lower surfaces for each of the pixel positions in the xy-plane. This raw thickness value is then converted to actual distance, in microns, by multiplying the voxel count by the 7 μm slice thickness resolution.
The third intensive property 2D image is the Volumetric Density Image. To generate this image divide each xy-plane pixel value in the Basis Weight Image, in units of gsm, by the corresponding pixel in the Thickness image, in units of microns. The units of the Volumetric Density Image are grams per cubic centimeter (g/cc).
Micro-CT Basis Weight, Thickness and Volumetric Density Intensive Properties:
Emtec Test Method
TS7 and TS750 values are measured using an EMTEC Tissue Softness Analyzer (“Emtec TSA”) (Emtec Electronic GmbH, Leipzig, Germany) interfaced with a computer running Emtec TSA software (version 3.19 or equivalent). According to Emtec, the TS7 value correlates with the real material softness, while the TS750 value correlates with the felt smoothness/roughness of the material. The Emtec TSA comprises a rotor with vertical blades which rotate on the test sample at a defined and calibrated rotational speed (set by manufacturer) and contact force of 100 mN. Contact between the vertical blades and the test piece creates vibrations, which create sound that is recorded by a microphone within the instrument. The recorded sound file is then analyzed by the Emtec TSA software. The sample preparation, instrument operation and testing procedures are performed according the instrument manufacture's specifications.
Test samples are prepared by cutting square or circular samples from a finished product. Test samples are cut to a length and width (or diameter if circular) of no less than about 90 mm, and no greater than about 120 mm, in any of these dimensions, to ensure the sample can be clamped into the TSA instrument properly. Test samples are selected to avoid perforations, creases or folds within the testing region. Prepare 8 substantially similar replicate samples for testing. Equilibrate all samples at TAPPI standard temperature and relative humidity conditions (23° C.±2 C ° and 50%±2%) for at least 2 hour prior to conducting the TSA testing, which is also conducted under TAPPI conditions.
Calibrate the instrument according to the manufacturer's instructions using the 1-point calibration method with Emtec reference standards (“ref.2 samples”). If these reference samples are no longer available, use the appropriate reference samples provided by the manufacturer. Calibrate the instrument according to the manufacturer's recommendation and instruction, so that the results will be comparable to those obtained when using the 1-point calibration method with Emtec reference standards (“ref.2 samples”).
Provide eight replicate samples of a fabric for testing. Mount a test sample into the instrument with a surface facing upwards, and perform the test according to the manufacturer's instructions. When complete, the software displays values for TS7 and TS750. Record each of these values to the nearest 0.01 dB V2 rms. The test sample is then removed from the instrument and discarded. This testing is performed individually on the same surface of four of the replicate samples, and then on the other surface of the other four replicate samples. The first tested surface may be either of the first surface 12 or the second surface 14 of a shaped nonwoven fabric as disclosed herein.
The four test result values for TS7 and TS750 from the first tested surface are averaged (using a simple numerical average); the same is done for the four test result values for TS7 and TS750 from the second tested surface. Report the individual average values of TS7 and TS750 for both the first and second tested surfaces on a particular test sample to the nearest 0.01 dB V2 rms. Additionally, the TS7 ratio of the first tested surface to the second tested surface is calculated by dividing the average TS7 of the first tested surface divided by the average TS7 of the second tested surface.
Contact Angle and Time to Wick measurements are determined using a sessile drop experiment. A specified volume of Type II reagent distilled water (as defined in ASTM D1193) is applied to the surface of a test sample using an automated liquid delivery system. A high speed video camera captures time-stamped images of the drop over a 60 second time period at a rate of 900 frames per second. The contact angle between the drop and the surface of the test sample is determined for each captured image by image analysis software. The time to wick is determined as the time it takes the contact angle of a drop absorbing into the test sample to decrease to a contact angle <10°. All measurements are performed at constant temperature (23° C.±2 C°) and relative humidity (50%±2%).
An automated contact angle tester is required to perform this test. The system consists of a light source, a video camera, a horizontal specimen stage, a liquid delivery system with a pump and micro syringe and a computer equipped with software suitable for video image capture, image analysis and reporting contact angle data. A suitable instrument is the Optical Contact Angle Measuring System OCA 20 (DataPhysics Instruments, Filderstadt, Germany), or equivalent. The system must be able to deliver an 8.2 microliter drop and be capable of capturing images at a rate of 900 frames per second. The system is calibrated and operated per the manufacturer's instructions, unless explicitly stated otherwise in this testing procedure. To obtain a test sample for measurement, lay a single layer of the dry substrate material out flat and cut a rectangular test sample 15 mm in width and about 70 mm in length. The width of the sample may be reduced as necessary to ensure that the test region of interest is not obscured by surrounding features during testing. With a narrower sample strip care must be taken that the liquid drop does not reach the edge of the test sample during testing, otherwise the test must be repeated. Precondition samples at 23° C.±2 C ° and 50%±2% relative humidity for 2 hours prior to testing.
A test sample may be cut from any location containing the visually discernible zone to be analyzed. Within a zone, regions to be analyzed are ones associated with a three-dimensional feature defining a microzone. The microzone comprises at least two visually discernible regions. A zone, three-dimensional feature, or microzone may be visually discernable due to changes in texture, elevation, or thickness. Regions within different test samples taken from the same substrate material can be analyzed and compared to each other. Care should be taken to avoid folds, wrinkles or tears when selecting a location for sampling.
If the substrate material is a layer of an absorbent article, for example a topsheet or backsheet nonwoven, acquisition layer, distribution layer, or other component layer; tape the absorbent article to a rigid flat surface in a planar configuration. Carefully separate the individual substrate layer from the absorbent article. A scalpel and/or cryogenic spray (such as Cyto-Freeze, Control Company, Houston TX) can be used to remove a substrate layer from additional underlying layers, if necessary, to avoid any longitudinal and lateral extension of the material. Once the substrate layer has been removed from the article proceed with cutting the test sample. If the substrate material is in the form of a wet wipe, open a new package of wet wipes and remove the entire stack from the package. Remove a single wipe from the middle of the stack, lay it out flat and allow it to dry completely prior to cutting the sample for analysis.
The test sample is positioned onto the horizontal specimen stage with the test region in the camera's field of view beneath the liquid delivery system needle, with the test side facing up. The test sample is secured in such a way that it lies flat but unstrained, and any interaction between the liquid drop and the underlying surface is avoided to prevent undue capillary forces. A 27 gauge blunt tip stainless steel needle (ID 0.23 mm, OD 0.41 mm) is positioned above the test sample with at least 2 mm of the needle tip in the camera's field of view. Adjust the specimen stage to achieve a distance of about 3 mm between the tip of the needle and the surface of the test sample. An 8.2 microliter drop of reagent distilled water is formed at a rate of 1 microliter per second and allowed to freely fall onto the surface of the test sample. Video image capture is initiated prior to the drop contacting the surface of the test sample, and subsequently a continual series of images is collected for a duration of 60 seconds after the drop contacts the surface of the test sample. Repeat this procedure for a total of five (5) substantially similar replicate test regions. Use a fresh test sample or ensure that the previous drop's wetted area is avoided during subsequent measurements.
On each of the images captured by the video camera, the test sample surface and the contour of the drop is identified and used by the image analysis software to calculate the Contact Angle for each drop image and reported to the nearest 0.1 degree. The Contact Angle is the angle formed by the surface of the test sample and the tangent to the surface of the liquid drop in contact with the test sample. For each series of images from a test, time zero is the time at which the liquid drop makes contact with the surface of the test sample. Measure and record the Contact Angle on the drop image that corresponds to time zero plus five (5) seconds. The Contact Angle at five seconds is reported as 0° if the droplet has been completely absorbed by the test sample within 5 seconds. Repeat this procedure for the five replicate test regions. Calculate the arithmetic mean of the Contact Angle at time zero plus five seconds for the five replicate test regions, and report this value as the Contact Angle to the nearest 0.1 degrees.
Time to Wick is defined as the time it takes the contact angle of a drop absorbing into the test sample to decrease to a contact angle <10°. Time to Wick is measured by identifying the first image of a given series where the contact angle has decreased to a contact angle <10°, and then based on that image, calculating and reporting the length of time that has elapsed from time zero. Time to Wick is reported as 60 seconds if a contact angle less than 10° is not reached within 60 seconds. Repeat this procedure for the five replicate test regions. Calculate the arithmetic mean of the Time to Wick for the five replicate test regions, and report this value to the nearest 0.1 milliseconds.
The invention of the disclosure can be described by any of the following combinations, detailed in the following paragraphs:
The dimensions and values disclosed herein are not to be understood as being strictly limited to the exact numerical values recited. Instead, unless otherwise specified, each such dimension is intended to mean both the recited value and a functionally equivalent range surrounding that value. For example, a dimension disclosed as “40 mm” is intended to mean “about 40 mm.”
Every document cited herein, including any cross referenced or related patent or application and any patent application or patent to which this application claims priority or benefit thereof, is hereby incorporated herein by reference in its entirety unless expressly excluded or otherwise limited. The citation of any document is not an admission that it is prior art with respect to any invention disclosed or claimed herein or that it alone, or in any combination with any other reference or references, teaches, suggests or discloses any such invention. Further, to the extent that any meaning or definition of a term in this document conflicts with any meaning or definition of the same term in a document incorporated by reference, the meaning or definition assigned to that term in this document shall govern.
While particular embodiments of the present invention have been illustrated and described, it would be obvious to those skilled in the art that various other changes and modifications can be made without departing from the spirit and scope of the invention. It is therefore intended to cover in the appended claims all such changes and modifications that are within the scope of this invention.
This application is a continuation of, and claims priority under 35 U.S.C. § 120 to, U.S. patent application Ser. No. 18/179,642, filed on Mar. 7, 2023, which is a continuation of U.S. patent application Ser. No. 17/370,000, filed on Jul. 8, 2021, now granted U.S. Pat. No. 11,666,488, issued on Jun. 6, 2023, which is a continuation of U.S. patent application Ser. No. 15/879,477, filed on Jan. 25, 2018, now granted U.S. Pat. No. 11,090,197, issued on Aug. 17, 2021, which claims the benefit, under 35 U.S.C. § 119(e), of U.S. Provisional Patent Application Ser. No. 62/452,566, filed on Jan. 31, 2017, the entire disclosures of which are fully incorporated by reference herein.
Number | Date | Country | |
---|---|---|---|
62452566 | Jan 2017 | US |
Number | Date | Country | |
---|---|---|---|
Parent | 18179642 | Mar 2023 | US |
Child | 18513963 | US | |
Parent | 17370000 | Jul 2021 | US |
Child | 18179642 | US | |
Parent | 15879477 | Jan 2018 | US |
Child | 17370000 | US |