The present invention generally relates to composites and products made from composites. More specifically, the present invention relates to composite products with a tapered body, such as shims, wedges and/or the like, and methods of producing same.
In general, composites and products made from composites are known and used in the market place. For example, composite products have been known and used as substitutes for products made from wood. In this regard, wood composite products have been used, for example, as a substitute for outdoor decking material made from wood.
As a wood substitute, composite products may exhibit similar, if not better, consistency of properties, such as compression strength, water resistance, pest resistance, rot resistance and/or the like, as compared to wood. In this regard, composites are generally made from a combination of plastics and a wood material, such as wood flour derived from a variety of different wood sources. Depending on the particular use, the composites are typically formed into an extruded product of varying sizes and shapes.
Within the manufactured home industry, for example, there exists a need for low cost and consistent performance in shims, wedges and/or the like. Wood shims and/or wood wedges typically vary with respect to properties and dimensions resulting in increased labor costs during use. In general, shims are utilized to position and level doors, windows, cabinets, framing and the like prior to being secured in place. In general, wedges are used to set and/or level heavy weight bearing objects, such as manufactured homes. Pre-made shims or setting wedges can facilitate operation due to the fact that extra time and effort does not have to be expended, for example, in sorting through a random assortment of commercially available wood shims for one with the necessary dimensions and quality.
However, wood shims, pre-made or otherwise, can split when a nail or nails are driven through a door jamb, for example, and subsequently into the shim to secure the door. This may result in having to replace the split shim and thus ultimately having to re-position the jamb. Further, once the shim has been secured in place, a portion of it generally needs to be removed such that it remains flush with, for example, the door jamb. In this regard, wood shims may not break cleanly or evenly when a portion is removed and thus can leave a jagged edge which may need additional cutting. Wood wedges can be problematic as well due to the fact that they are susceptible to slippage and/or compression over time under weight bearing use. This can cause shifting of the weight bearing objects, such as shifting of manufactured homes, set on the wood wedges.
A need, therefore, exists to provide composite products, such as shims and/or wedges, that can be readily manufactured and that have improved qualities, such as durability with resistance to split, splinter, swell, warp and twist, as compared to, for example, wood-made products.
The present invention generally relates to composites, products made from composites and methods of making same. The present invention includes composites that are at least made from a mixture of thermoplastics and a fibrous component. The composite can be formed into a variety of different molded products, particularly molded building materials, such as composite shims, composite wedges and/or the like. The composite products of the present invention have improved properties, for example, as compared to shims or wedges made from wood, such as resistance to splitting, rot, insects, greater compression strength and durability and/or the like. In this regard, the composite products of the present invention can be a desirable substitute for wood-made products in a variety of different applications, such as applications relating to the manufactured home industry.
To this end, in an embodiment of the present invention, an injection moldable product is provided. The injection moldable product includes a tapered body with one or more cored regions extending through at least a portion of the body wherein the body is composed of a composite material including a fibrous component, a thermoplastic component and a coupling agent.
In an embodiment, the thermoplastic component includes a polypropylene, polyethylene, polyesters, polystyrene, polycarbonate, polyvinylchloride, poly (methyl methacrylate), nylon, copolymers thereof, the like and combinations thereof.
In an embodiment, the fibrous component includes synthetic fiber, such as carbon fiber and/or the like, cellulosic material, natural fiber(s), wood flour, birch wood flour, spruce wood flour, pine wood flour, fir wood flour, maple wood flour, rice hull, peanut shells, recyclable wood waste, recyclable paper, flax sheeve, the like and mixtures thereof.
In an embodiment, the coupling agent includes a copolymer of maleic acid and polypropylene, a copolymer of maleic acid and polyethylene, maleic acid, polyethylene, the like and mixtures thereof.
In an embodiment, the coupling agent ranges from about 3% or less by weight of the shim.
In an embodiment, the composite material includes an additional component that includes a pigment, a scent agent, an ultraviolet light stabilizing agent, a filler, a natural filler including talc and calcium carbonate, a heat stabilizer, an antioxidant, a foaming agent, a fungicide, the like and combinations thereof.
In an embodiment, the thermoplastic component comprises about 30% to about 70% by weight of the injection moldable product and the fibrous component comprises about 30% to about 70% of the injection moldable product.
In another embodiment, a composite shim is provided. The composite shim includes a base material including a fibrous component and a thermoplastic component wherein the base material is formed into a shim-shaped body that has one or more cored regions extending into a portion of the shim-shaped body.
In yet another embodiment, an injection moldable wedge is provided. The injection moldable wedge includes a wedge-shaped body composed of a composite base material including a fibrous component and a thermoplastic component wherein the wedge-shaped body has one or more cored regions extending through a portion of the wedge-shaped body.
In still yet another embodiment, a method of producing an injection moldable product is provided. The method includes the steps of mixing a thermoplastic component and a fibrous component; forming a composite base material at least including the thermoplastic component and the fibrous component; and molding the base material to form a tapered body wherein the body includes one or more cored regions extending through at least a portion thereof.
It is, therefore, an advantage of the present invention to provide improved composite material formulations, composite products, and methods of producing same.
Another advantage of the present invention is to provide improved composite products, such as shims, wedges and/or the like, that can be readily manufactured at reduced costs from a composite material including, for example, recyclable material, such as wood waste and/or the like.
Still another advantage of the present invention is to provide improved composite products that promote the sound recovery of wood waste and/or the like at the production level, thus encouraging recyclable use of such materials.
A further advantage of the present invention is to provide improved composite products that can be readily formed into an injection moldable product having desirable properties, such as durability, strength, resistance to splitting, water, insects, rot and the like.
A still further advantage of the present invention is to provide improved composite products that can be a desirable substitute for wood-made products, such as shims, wedges and/or the like.
Yet a still further advantage of the present invention is to provide an improved composite product that can be utilized in a variety of different applications including the building materials industry, such as the manufactured home industry.
Additional features and advantages of the present invention are described in, and will be apparent from, the following Detailed Description of the Invention and the figures.
The present invention provides composites, products made from composites, such as composite shims, composite wedges and/or the like, and methods of producing same.
The composite product of the present invention includes a composite material that is at least composed of a thermoplastic component and a fibrous component. In an embodiment, the composite product is an injection moldable product that includes a body tapered to an edge, e.g., a tapered body, wherein the body includes one or more cored regions extending through at least a portion of the composite product. The tapered body can be molded into a variety of suitable shapes and sizes, such as a shim, a wedge and/or the like.
As used herein, the term “composite” or other like terms means a material that is composed of a mixture of two or more different components that when mixed together impart properties of the material components, such as the thermoplastic component and the fibrous component of the composite product according to an embodiment of the present invention. In this regard, the thermoplastic component, on its own, would result in a product that is, for example, rot resistant and rubbery, and, on its own, the fibrous component, particularly a wood-derived fibrous component, would result in a product, for example, that is stiff, that contains moisture and that is susceptible to rot. But, when combined, the fibrous component and the thermoplastic component result in a composite product that exhibits properties derived from both the fibrous component and the thermoplastic component thereby making the resultant composite product a desirable substitute for a wood-made product.
As used herein, the terms “shim” and “wedge” or other like terms describe two different types of composite products according to an embodiment of the present invention. In general, the term “shim” or other like terms means a product that is typically constructed and sized for the purpose of positioning and leveling doors, windows and the like prior to securing same in place for use. In general, the term “wedge” or other like terms means a product that is typically constructed and sized for the purpose of setting a weight-bearing object or objects, such as a manufactured home.
Applicants have discovered that a balanced blend of composite materials, such as a blend of thermoplastics and fibrous materials, can be effectively utilized to make a composite product with a tapered body for a variety of different applications. Applicants have found that the well balanced blend of composite materials in combination with specific structural features of the finished molded product can result in the composite product with a tapered body that has improved characteristics, such as durability, compression strength, resistance to moisture, insects, splitting, rot and the like, as compared to, for example, shims and/or wedges made from wood.
In this regard, the composite product of the present invention can provide a number of technological and economic advantages over traditional wood wedges and/or wood shims. Further, the composite products of the present invention can be made from recyclable composite materials, such as thermoplastics and natural and/or synthetic fibers including recyclable wood waste.
The composite product of the present invention can be made from a variety of different and suitable materials. In general, the composite product includes a balanced blend of thermoplastics and fibrous materials. In an embodiment, the composite blend also includes a coupling or binder agent to facilitate the binding of the thermoplastic and fiber components.
The thermoplastic component can include any suitable material. In this regard, it is preferred that the thermoplastic material be essentially composed of a thermoplastic that is more “tough” than “rigid” such that it does not break. In an embodiment, the thermoplastic component includes polypropylene, polyethlyene, polyesters, polystyrene, polycarbonate, polyvinylchloride, poly (methyl methacrylate), nylon, like materials and mixtures thereof. It should be appreciated that the present invention is not limited to a monomeric plastic and thus can include any suitable type of polymeric plastic, including polymers composed of at least two different monomeric components, such as polyethlyene, polyesters, polystyrene, polycarbonate, polyvinylchloride, poly (methyl methacrylate) or other like materials.
The fibrous components of the present invention can include any variety, number and mixture of suitable materials. For example, the fiber component can include synthetic fibers, natural fibers, cellulosic materials or combinations thereof. In an embodiment, the fibrous component includes synthetic fibers, such as carbon fibers, cellulosic materials, natural fibers, wood flour, birch wood flour, maple wood flour, spruce wood flour, pine wood flour, fir wood flour, rice hulls, peanut shells, recyclable wood waste, recyclable paper, flax sheeve, mixtures thereof and the like.
In this regard, the use of wood waste and/or other like fibrous components can promote recyclable use of such fibrous components. This can promote, for example, sound recovery of wood waste and/or the like at the production level, thus encouraging recycling of same.
The composite product of the present invention can include a variety of other materials in combination with the thermoplastic and fiber components. In an embodiment, the additional materials include coupling agents, binders, pigment, scent agents including cedar scent or other wood-like scent, ultraviolet light stabilizing agents, heat stabilizers, antioxidants, fillers, natural fillers including calcium carbonate, talc and/or the like, foaming agents, fungicides, other like components and combinations thereof.
As previously discussed, the coupling agent can be added to the balanced mixture of thermoplastics and fibrous material(s) to facilitate the binding of such materials. In an embodiment, the coupling agent includes a copolymer or grafted copolymer of maleic acid and polypropylene, a copolymer or grafted copolymer of maleic acid and polyethylene, maleic acid, polyethylene, other suitable materials and combinations thereof. The copolymer of maleic acid and polyethylene is preferably used with the thermoplastic component that includes polyethylene.
The various components, such as thermoplastics and fibers, of the composite product can be added in any suitable amount such that the balanced blend of composite materials can be effectively utilized to make a composite product with a tapered body and/or other suitable structural features. In an embodiment, the thermoplastic component ranges from about 30% to about 70% by weight of the composite product, the fiber components ranges from about 30% to about 70% by weight of the composite product and the coupling agent ranges from about 0% to about 3% by weight of the composite product.
Preferably, the fiber component includes a wood flour, such as birch wood flour, maple wood flour, spruce wood flour, pine wood flour, fir wood flour, the like or combinations thereof at about 40% by weight of the composite product, the thermoplastic component includes about 59% by weight of the composite product, and the coupling agent includes about 1% by weight of the composite product. The wood flour can include any suitable size. In an embodiment, the wood flour includes about 20 to about 60 mesh consistency, preferably about 40 mesh consistency.
In an embodiment, the composite product of the present invention includes the fiber component in an amount of about 40% by weight of the composite product with the remaining amounts of the composite product including the thermoplastic component and optionally the coupling agent and other additional ingredients in any suitable amount. It should be appreciated that the amount of the various components of the present invention can be added in any suitable amount to the extent that the desirable properties of the composite product are not compromised, such as strength, durability, resistance to splitting, rotting and/or the like.
The composite product of the present invention can be formed into a variety of different shapes and sizes suitable for use in a variety of different applications, including residential, commercial or industrial use, such as building material for use, for example, in the manufactured home industry. In an embodiment, a composite shim is provided. The composite shim 10 includes a shim-shaped body 12 as illustrated in
In an embodiment, the shim-shaped body 12 includes one or more or cored regions 26 extending into a portion of the body 12 and along at least a portion of the face region 14 of the shim-shaped body 12. As previously discussed, Applicants have uniquely discovered that the combination of a balanced blend of composite materials and the specific structural features of the finished molded product can provide a composite shim that has improved characteristics, such as strength, durability, resistance to splitting, the ability to break cleanly and evenly and the like, as compared to, for example, traditional wood shims. In this regard, the composite shim of the present invention can be desirably utilized as a substitute for wood shims.
The cored regions 26 of the composite shim 10 can include a variety of different suitable sizes, shapes and numbers and can be positioned in any suitable way with respect to the shim-shaped body 12 of the composite shim 10. Applicants have discovered that the addition of the cored regions 26 can provide a number of different beneficial effects with respect to the use and processing of the composite shim 10.
For example, Applicants have found that the composite shim 10 of the present invention is effectively resistant to splitting when a nail(s) is driven through it as compared to conventional wood shims. In this regard, Applicants believe that the cored regions 26 can act to reinforce the composite shim by providing an access region through which a nail can be easily driven. This can minimize, or effectively eliminate, the amount of force exerted by the nail to the remaining portion of the composite shim, and thus, the cored regions effectively halt the propagation of splitting caused by nailing. Further, the cored regions can reduce the cycle time for molding by increasing the cooling surface area, thereby causing the shim-shaped body to cool at a faster rate during injection molding.
In an embodiment, the cored regions 26 are positioned along the face region 14 of the composite shim 10 in one or more rows 28 wherein a row 28 includes a number of cored regions 26, such as three cored regions to a row as illustrated in
The cored regions 26 can include a variety of different and suitable shapes and sizes. In an embodiment, the cored regions 26 include a cylindrical shape as shown in
It should be appreciated that the composite shim of the present invention can be molded with precision and accuracy into a variety of different and suitable shapes, sizes and configurations. An embodiment is illustrated in
As shown in
As shown in
As previously discussed, the composite products of the present invention can be formed into a number of different shapes and sizes. As shown in
In an embodiment, the present invention includes a wedge-shaped composite product as shown in
In an embodiment, the wedge-shaped body 56 includes one or more cored regions 72 extending through a portion of the wedge-shaped body. The cored regions 72 can include a variety of suitable and different shapes and combinations thereof. In an embodiment, the wedge-shaped body 56 includes three rows of a pair of cored regions 72. As shown in
In an embodiment, the wedge composite includes one or more ripples 76 extending across at least a portion of one or both of the face regions 58 and 60 as shown in
The wedge composite of the present invention can include a variety of suitable dimensions depending on the application. In an embodiment, the wedge-shaped composite includes a thickness of about 13/8 inches at the end region 62, a length of about 10 inches, a width of about 31/4 inches and a weight that is comparable to a wood-made wedge. These dimensions make the wedge composite of the present invention particularly suited for setting heavy weight bearing objects, such as manufactured homes.
The composite shim of the present invention can be made in a variety of different and suitable ways. In general, a composite material can be initially formed via a conventional extrusion process under suitable temperatures, pressures and other like process conditions. In this regard, the components of the composite shims are suitably mixed and extruded to form a pellet-sized material or other like-sized or shaped material.
The pre-formed composite material can then be molded to form the composite shim in a variety of different and suitable ways. In an embodiment, the composite material is processed through an injection molding process using temperatures, pressures and setting times in the molding art effective to produce the composite shim. The injection molding process can be carried out in any suitable way. In an embodiment, the injection molding temperature ranges from about 340.degree. F. to about 410.degree. F., preferably from about 390.degree. F. to about 400.degree. F., such that the fiber component of the composite material does not char during the process. In an embodiment, the operating pressure during injection molding ranges from about 1000 pounds (lbs) of pressure to about 1300 lbs of pressure, preferably about 1100 lbs. of pressure.
It should be appreciated that the injection molding process can include a variety of different and suitable equipment components and process parameters effective to produce the composite products of the present invention. For example, the present invention can include a variety of gates and runners sized and positioned in the mold so as to effectively produce the molded composite product(s) of the present invention.
In an embodiment, the composite shim of the present invention can be made with a mold 80 as illustrated in
Each cavity 86 includes a number of protrusions 88 extending along at least a portion of the cavity 86. As shown in
During injection molding, the composite melt is injected into the cavity base 84 through an injection hole 90 as shown in
In an embodiment, the cavities 86 include a draft (not shown) on the side regions 100. This allows the side regions 100 to be angled such that the composite shim can be more easily removed from the cavity 86 during processing.
By way of example and not limitation, the present invention is described below in the following examples.
An experimental test was conducted to evaluate the creep properties of a composite shim made in accordance with an embodiment of the present invention. The test was also conducted on wood-made shims for comparison. In general, a number of each type of test shim were placed in a stacked arrangement and subject to a specific load. The change in stack height was measured initially and after one hour. The types of shims used in the experiment included composite shims made with a 70% thermoplastic component (70%) and 60% thermoplastic component (60%) in accordance with an embodiment of the present invention and shims made from jute, cedar and pine. As indicated below in Table I, the composite shims displayed better creeping properties when subject to the load initially and over time as compared to the wood-made shims.
An experimental test was conducted to evaluate the split resistance properties of a composite shim made in accordance with an embodiment of the present invention. The test was also conducted on wood-made shims for comparison. The tested shims included composite shims made from 60% thermoplastic (60%), 60% thermoplastic at reduced weight (60%-reduced weight) and 70% thermoplastic (70%) in accordance with an embodiment of the present invention and shims made from jute, pine and cedar.
Two-inch nails were driven through a 1 inch cedar board cover then through two shims into a 2.times.4 stud backing while the shims were at 20.degree. F. Prior to nailing, the cover, shims and backing were placed in a 20.degree. F. cooling chamber for 1 hour. Brads were nailed 1 inch, 1.5 inch and 4 inches from the end of the shim stack. Nailing was accomplished with a pneumatic nail gun using 2 inch brads @ 50 psi air pressure. The 70%, 60%, 60%-reduced weight, jute and pine shims exhibited no splitting between nails. The cedar shims had splitting between the end of the shim stack and the 1-inch nail and between the 1.0 inch and 1.5 inch placed nails.
This test evaluated how much energy was required to snap a shim. All the shims were broken at the same thickness of 0.23 inches. The same type of shims were tested as tested in Example II, except that a shim made from jute was not tested. A pendulum impact machine was used to perform the test. A shim was clamped in a suitable fashion into the apparatus exposing 1.10 inch of unsupported shim. At the bottom of the pendulum swing the shim was snapped off and the energy used was recorded. The composite shims were molded smooth on one face and with cored regions on the other face in accordance with an embodiment of the present invention. These specimens were impacted both against the smooth face and against the face with the holes. For comparison purposes, the impact tests were also performed on cedar and pine shims. As can be seen below in Table III, the composite shims made in accordance with an embodiment of the present invention are easier to snap than are the natural wood products. Also, it was consistently easier to snap a composite shim from the hole side than from the smooth side.
It should be understood that various changes and modifications to the presently preferred embodiments described herein will be apparent to those skilled in the art. Such changes and modifications can be made without departing from the spirit and scope of the present invention and without diminishing its intended advantages. It is therefore intended that such changes and modifications be covered by the appended claims.
Although the present invention has been described with reference to preferred embodiments, workers skilled in the art will recognize that changes can be made in form and detail without departing from the spirit and scope of the present invention.
This application is a continuation of, and claims priority to and the benefit of, U.S. patent application Ser. No. 29/332,364 filed on Feb. 13, 2009, which is a continuation of U.S. patent application Ser. No. 10/219,395 filed on Aug. 14, 2002, now U.S. Pat. No. 7,716,880, which claims priority to and the benefit of, U.S. Patent Application Ser. No. 60/312,142 filed on Aug. 14, 2001, and the entire contents of such applications are hereby incorporated by reference.
| Number | Date | Country | |
|---|---|---|---|
| 60312142 | Aug 2001 | US |
| Number | Date | Country | |
|---|---|---|---|
| Parent | 29332364 | Feb 2009 | US |
| Child | 13998742 | US | |
| Parent | 10219395 | Aug 2002 | US |
| Child | 29332364 | US |