This invention relates to a shingle, such as a roofing shingle, and in particular, to a roofing shingle having an improved nail zone.
Asphalt-based roofing materials, such as roofing shingles, roll roofing and commercial roofing, are installed on the roofs of buildings to provide protection from the elements, and to give the roof an aesthetically pleasing look. Typically, the roofing material is constructed of a substrate such as a glass fiber mat or an organic felt, an asphalt coating on the substrate, and a surface layer of granules embedded in the asphalt coating.
A common method for the manufacture of asphalt shingles is the production of a continuous sheet of asphalt material followed by a shingle cutting operation which cuts the material into individual shingles. In the production of asphalt sheet material, either a glass fiber mat or an organic felt mat is passed through a coater containing hot liquid asphalt to form a tacky, asphalt coated sheet. Subsequently, the hot asphalt coated sheet is passed beneath one or more granule applicators which discharge protective and decorative surface granules onto portions of the asphalt sheet material.
In certain types of shingles, it is especially desired that the shingles define a sufficiently wide area, often known in the industry as the “nail zone,” in order to make installation of roofs using shingles, such as laminated shingles, more efficient and secure. One or more lines or other indicia painted or otherwise marked longitudinally on the surface of the shingle may define such a nail zone. It is especially desired that the shingles define a nail zone that allows the installers to have some latitude in the nail placement.
Additionally, the leading edge of some shingles may experience lift off in high wind situations. Therefore, there is also a need for shingles where the shingles have a sufficiently high nail pull-through value so that the installed shingles have improved performance in high wind situations.
According to this invention there is provided a method of making a laminated shingle including the steps of coating a shingle mat with roofing asphalt to make an asphalt-coated sheet, adhering a reinforcement member to a portion of the asphalt-coated sheet, covering the asphalt-coated sheet, and optionally covering the reinforcement member, with granules to make a granule-covered sheet, dividing the granule-covered sheet into an overlay sheet and an underlay sheet, wherein the overlay sheet has a tab portion normally exposed on a roof and a headlap portion normally covered-up on a roof, the headlap portion having a lower zone adjacent the tab portion and an upper zone adjacent the lower zone, and wherein the reinforcement member is adhered to the lower zone of the headlap portion and laminating the overlay sheet and the underlay sheet to make the laminated shingle.
According to this invention this is also provided a method of making a laminated shingle including the steps of coating a shingle mat with roofing asphalt to make an asphalt-coated sheet, adhering a reinforcement member to a portion of the asphalt-covered sheet, covering the asphalt-coated sheet with granules to make a granule-covered sheet, dividing the granule-covered sheet into an overlay sheet and an underlay sheet, wherein the overlay sheet has a tab portion normally exposed on a roof and a headlap portion normally covered-up on a roof, the headlap portion having a lower zone adjacent the tab portion and an upper zone adjacent the lower zone, and wherein the reinforcement member is adhered to the lower zone of the headlap portion and laminating the overlay sheet and the underlay sheet to make the laminated shingle.
According to this invention this is also provided a method of making a shingle including the steps of coating a shingle mat with roofing asphalt to make an asphalt-coated sheet, covering a portion of the asphalt-coated sheet with a material other than roofing granules prior to applying granules thereto to define a nail zone, covering the asphalt-coated sheet, and optionally covering the material, with granules to make a granule-covered sheet and dividing the granule-covered sheet into a shingle which includes a first portion normally exposed on a roof and a headlap portion normally covered-up on a roof, the headlap portion having a lower zone adjacent the first portion and an upper zone adjacent the lower zone, and wherein the material is adhered to the lower zone of the headlap portion.
Various objects and advantages of this invention will become apparent to those skilled in the art from the following detailed description of the various embodiments, when read in light of the accompanying drawings.
Referring now to the drawings, there is shown in
In a first step of the illustrated manufacturing process, a continuous sheet of substrate or shingle mat 12 is payed out from a roll 14. The substrate can be any type known for use in reinforcing asphalt-based roofing materials, such as a non-woven web of glass fibers. The shingle mat 12 may be fed through a coater 16 where an asphalt coating is applied to the mat 12. The asphalt coating can be applied in any suitable manner. In the illustrated embodiment, the mat 12 contacts a roller 17, which is in contact with a supply of hot, melted asphalt. The roller 17 completely covers the mat 12 with a tacky coating of hot, melted asphalt to define a first asphalt coated sheet 18. In other embodiments, however, the asphalt coating could be sprayed on, rolled on, or applied to the sheet by other means. Typically, the asphalt material is highly filled with a ground stone filler material, amounting to at least about 60 percent by weight of the asphalt/filler combination.
A continuous strip of a reinforcement material or tape 19, as will be described in detail herein, may then be payed out from a roll 20. The reinforcement tape 19 adheres to the first asphalt coated sheet 18 to define a second asphalt coated sheet 22. In one embodiment, the reinforcement tape 19 is attached to the sheet 18 by the adhesive mixture of the asphalt in the first asphalt coated sheet 18. The reinforcement tape 19, however, may be attached to the sheet 18 by any suitable means, such as other adhesives. In one embodiment, the tape 19 is formed from polyester. In another embodiment, the tape 19 is formed from polyolefin, such as polypropylene or polyethylene, and may include any polymeric material having the desired properties in the finished product and which will endure the manufacturing environment. The tape 19, can be formed from any material which preferably reinforce and strengthens the nail zone of a shingle, such as, for example, paper, film, scrim material, and woven or non-woven fibers, such as glass, natural or polymer fibers, or the material may not provide such physical properties, but may simply provides an indicia of the nail zone. Additionally, it may be desirable to treat the tape to improve adhesion, such as through coatings, corona treatment, etching, surface treatments, providing perforations or other surface roughening, or adding fillers or other techniques to increase surface area for adhesion. Additionally, it may be desirable to provide another adhesive between the tape and the asphalt coating to improve adhesion thereof.
The resulting second asphalt coated sheet 22 may then be passed beneath a series of granule dispensers 24 for the application of granules to the upper surface of the second asphalt coated sheet 22. The granule dispensers can be of any type suitable for depositing granules onto the asphalt coated sheet. A granule dispenser that can be used is a granule valve of the type disclosed in U.S. Pat. No. 6,610,147 to Aschenbeck. The initial granule blender 26 may deposit partial blend drops of background granules of a first color blend on the tab portion of the second asphalt coated sheet 22 in a pattern that sets or establishes the trailing edge of subsequent blend drops of a second color blend (of an accent color) and a third color blend (of a different accent color). For purposes of this patent application, the first color blend and the background granules are synonymous. The use of initially applied partial blend drops to define the trailing edge of subsequent blend drops is useful where accurate or sharp leading edges are possible, but accurate trailing edges at high shingle manufacturing speeds are difficult.
As is well known in the art, blend drops applied to the asphalt coated sheet are often made up of granules of several different colors. For example, one particular blend drop that is supposed to simulate a weathered wood appearance might actually consist of some brown granules, some dark gray granules, and some light gray granules. When these granules are mixed together and applied to the sheet in a generally uniformly mixed manner, the overall appearance of weathered wood is achieved. For this reason, the blend drops are referred to as having a color blend, which gives an overall color appearance. This overall appearance may be different from any of the actual colors of the granules in the color blend. Also, blend drops of darker and lighter shades of the same color, such as, for example, dark gray and light gray, are referred to as different color blends rather than merely different shades of one color.
As shown in
In one embodiment, the reinforcement tape 19 includes an upper surface to which granules substantially will not adhere. The reinforcement tape 19, however, may include an upper surface to which granules will adhere. For example, the apparatus 10 may include any desired means for depositing granules onto substantially the entire second asphalt coated sheet 22, except for the portion of the second asphalt coated sheet 22 covered by the tape 19, as best shown in
The granule covered sheet 40 may then be turned around a slate drum 44 to press the granules into the asphalt coating and to temporarily invert the sheet so that the excess granules will fall off and will be recovered and reused. Typically, the granules applied by the background blender 34 are made up by collecting the backfall granules falling from the slate drum 44.
The granule covered sheet 40 may subsequently be fed through a rotary pattern cutter 52 which includes a bladed cutting cylinder 54 and a backup roll 56, as shown in
The pattern cutter 52 may also cut the granule covered sheet 40 into a continuous underlay sheet 66 and a continuous overlay sheet 68. The underlay sheet 66 may be directed to be aligned beneath the overlay sheet 68, and the two sheets may be laminated together to form a continuous laminated sheet 70. As shown in
In order to facilitate synchronization of the cutting and laminating steps, various sensors and controls may be employed. For example, sensors, such as photo eyes 86 and 88 can be used to synchronize the continuous underlay sheet 66 with the continuous overlay sheet 68. Sensors 90 can also be used to synchronize the notches and cutouts of the continuous laminated sheet with the end cutter or length cutter 72.
In one embodiment, the reinforcement tape may be attached to the shingle mat 12 prior to the application of the asphalt coating, as shown at 19A in
In another embodiment, the reinforcement tape may be attached to the granule covered sheet 40, as shown at 19B in
In another embodiment, the reinforcement tape may be attached to a lower surface (downwardly facing as viewed in
It will be understood, however, that in any of the embodiments described herein, reinforcement material may be applied as an extruded or liquid material, such as a polymer, that will adhere to the mat 12, the first sheet 18, the second sheet 22, the granule covered sheet 40, or the lower surface of the underlay sheet 66 or the overlay sheet 68. Additionally, the reinforcement material may be applied to the laminated roofing shingle 74, as described below.
Referring now to
The reinforcement tape 19 may be disposed longitudinally on the headlap portion 76. In the illustrated embodiment, the tape 19 extends longitudinally from the first end 74A to the second end 74B of the shingle 74 within the lower zone 76A of the headlap portion 76. A lower edge 19A of the tape 19 may be spaced apart from the line B by a distance D1, and an upper edge 19B of the tape 19 may be spaced apart from the line B by a distance D2. In one embodiment, the distance D1 is within the range of from about ¼ inch to about ¾ inch. In another embodiment, the distance D1 is about ½ inch. In one embodiment, the distance D2 is within the range of from about 1¾ inches to about 2¼ inches. In another embodiment, the distance D2 is about 2 inches. The distances D1 and D2 may, however, be of any other desired length, including zero for D1. For example, if desired, the tape 19 may substantially cover the entire headlap portion 76 of the overlay sheet 68. It will be further understood, however, that one or more additional lengths of tape may be disposed longitudinally on the headlap portion 76, even outside the nail zone, such as shown by the phantom line 19′ in
The tape 19 defines a nail zone 98 and may include text such as “nail here •”, as shown in
In the embodiment illustrated in
In the illustrated embodiment, the third height H3 of the underlay sheet 66 is less than one-half the second height H2 of the overlay sheet 68. The overlay sheet 68 and the underlay sheet 66 thereby define a two-layer portion of the laminated shingle 74 and a single-layer portion of the laminated shingle 74, wherein at least a portion of the tape 19 is preferably adhered to the single-layer portion of the laminated shingle 74. Alternately, the third height H3 of the underlay sheet 66 may be equal to one-half the second height H2 of the overlay sheet 68, or greater than one-half of the second height H2 of the overlay sheet 68. Such a relationship between the underlay sheet 66 and the overlay sheet 68 allows the tape 19 to be positioned such that a reinforced nail zone is provided at a substantially single-layer portion of the shingle 74.
In another embodiment of the invention, another material, such as a granular material. Granular materials may include minerals like talc, sand, or preferably a lightweight material such as expanded shale, which may be applied to the first asphalt coated sheet 18 shown in
In the exemplary shingle 74 illustrated in
In another embodiment, a shingle having a reinforcement tape 19 formed from polyester film having a thickness of about 0.5 mils, may have a nail pull-through value about 13.3 percent greater than in an otherwise identical shingle having no such tape 19.
In another embodiment, a shingle having a reinforcement tape 19 formed from polyester film having a thickness of about 3.0 mils, may have a nail pull-through value about 62.3 percent greater than in an otherwise identical shingle having no such tape 19.
In another embodiment, a shingle having a reinforcement tape 19 formed from polyester film having a thickness of about 4.0 mils, may have a nail pull-through value about 86.0 percent greater than in an otherwise identical shingle having no such tape 19.
In another embodiment, a shingle having a reinforcement tape 19 formed from polyester film having a thickness of about 5.0 mils, may have a nail pull-through value about 112.7 percent greater than in an otherwise identical shingle having no such tape 19.
Because there may be substantially no granules in the portion of the overlay sheet 68 covered by the tape 19 (or other material described above, such as sand), the weight of the shingle 74 may be reduced relative to an otherwise identical shingle having no such tape 19 or material. For example, the weight of the exemplary shingle 74 illustrated in
Although the invention has been disclosed in the context of a laminated shingle 74, it will be understood that the reinforcement tape 19 may be attached to any other type of shingle, such as a single layer shingle. In such a single layer shingle, the reinforcement tape may require UV resistance and/or appropriate coloration if the shingle has tab cutouts and if the tape is visible through the cutouts, and may require electrostatic frosting or other non-glare treatment. In a typical single layer shingle with cutouts, typically a band is provided at the top of the shingle which is not visible through the cutouts, and this zone may be covered by the tape 19 to minimize granule usage. Furthermore, while the tape 19 is referred to as a reinforcing tape, the properties need not include reinforcement characteristics.
As shown in
Additionally, a sealant is applied to a surface of the shingle to provide a bond between shingles on a roof. During a typical shingle manufacturing process, a pattern of adhesive is applied to the headlap portion of the shingles, so that the tab portion of the subsequently laid course of shingles on the roof will adhere to the headlap portion of the lower course. The adhesive bond helps to prevent wind uplift of the shingles on the roof. Alternatively, the sealant is applied to the bottom surface of the underlay at the leading edge 66A to bond to the headlap portion of a shingle installed in the previous course of shingles. It may be necessary to select a reinforcement tape 19 which adheres to the sealant, and in some instances tape 19 may be selected to improve the adhesion of the shingles. In one example, a 2-part adhesive is used as the sealant, where the tape 19 activates the sealant. In a preferred embodiments, the sealant is selected to be adhesively compatible with the reinforcement, and may be otherwise modified to improve adhesion to the reinforcement in a manner known to one skilled in the art. These modifications may include adding filler (such as nanoclays), adding a rubber component and such.
While the illustrations show a laminated shingle, one skilled in the art appreciates the same principles apply to a strip shingle. In such an instance, where the strip shingle includes cutouts, the reinforcement may be visible, and therefore must have properties to serve in an exposed environment, to provide weatherability and durability for the finished shingle when exposed on a roof. Where the shingle does not have cutouts, such as Skyview® manufactured by Owens Corning, most of the principles described above with respect to laminated shingles apply.
The principle and mode of operation of this invention have been described in its various embodiments. However, it should be noted that this invention may be practiced otherwise than as specifically illustrated and described without departing from its scope.
This application is a continuation patent application of pending U.S. patent application Ser. No. 11/997,657, filed Nov. 5, 2008, the disclosure of which is incorporated herein by reference.
| Number | Date | Country | |
|---|---|---|---|
| Parent | 13036200 | Feb 2011 | US |
| Child | 14132125 | US | |
| Parent | 11997657 | Nov 2008 | US |
| Child | 13036200 | US |
| Number | Date | Country | |
|---|---|---|---|
| Parent | 14132125 | Dec 2013 | US |
| Child | 15147141 | US |
| Number | Date | Country | |
|---|---|---|---|
| Parent | 11198522 | Aug 2005 | US |
| Child | 11997657 | US |