Patent Application
20200032517
The present application relates to roofing materials, such as shingles. In particular, the present application relates to roofing materials, such as shingles, with increased hydrophobicity as compared to otherwise identical, roofing materials or shingles.
Asphalt-based roofing materials, such as roofing shingles, roll roofing and commercial roofing, are installed on the roofs of buildings to provide protection from the elements, and to give the roof an aesthetically pleasing look. Typically, the roofing material is constructed of a substrate such as a glass fiber mat or an organic felt, an asphalt coating on the substrate, and a surface layer of granules embedded in the asphalt coating. Furthermore, physical and chemical factors such as surface roughness and heterogeneity as well as particle shape and size have been found to influence the contact angle and wetting behavior of solid particles. See, e.g., T. T. Chau, et al., “A review of factors that affect contact angle and implications for flotation practice,” Advances in Colloid and Interface Science 150, pp. 106-115 (2009). The entire disclosure of the Chau reference is hereby incorporated by reference.
One exemplary embodiment of a shingle includes a substrate having an asphalt coating on a top surface of the substrate and on a bottom surface of the substrate. A surface layer of granules is embedded in the asphalt on the top surface of the substrate. A backdust layer of particles is embedded in the asphalt on the bottom surface of the substrate. A sealant is disposed on the backdust. A hydrophobic material is applied to the sealant.
In the embodiments herein, the invention of the present application is discussed for use with roofing shingles. However, it should be understood that the invention of the present application may be used with any type of roofing material, such as, for example, asphalt-based roll roofing and commercial roofing.
As illustrated in
A shingle may also comprise one or more sheets laminated together to form a laminated shingle. For example, as illustrated in
The substrate of the shingle can be any type known for use in reinforcing asphalt-based roofing materials, such as a web, scrim or felt of fibrous materials such as mineral fibers, cellulose fibers, rag fibers, mixtures of mineral and synthetic fibers, or the like. Combinations of materials can also be used in the substrate. In certain embodiments, the substrate is a nonwoven web of glass fibers. The substrate may be any conventional substrate used in asphalt shingles, roll roofing, low-slope membranes, and the like.
The asphalt coatings are generally formed from a layer of hot, melted asphalt applied to the substrate. The asphalt coating can be applied to the substrate in any suitable manner. For example, the substrate can be submerged in the asphalt or the asphalt can be rolled on, sprayed on, or applied to the substrate by other means. The asphalt coating may also be any type of bituminous material suitable for use on a roofing material, such as asphalts, tars, pitches, or mixtures thereof. The asphalt can be either a manufactured asphalt produced by refining petroleum or a naturally occurring asphalt. The asphalt coating can include various additives and/or modifiers, such as inorganic fillers or mineral stabilizers, organic materials such as polymers, recycled streams, or ground tire rubber. In certain embodiments, the asphalt coatings comprise asphalt and inorganic fillers or mineral stabilizers. The asphalt coatings may be any conventional asphalt used in shingles, and can be applied in any conventional manner and in any conventional amount or thickness.
The granules are generally deposited onto the asphalt coating after the coating is applied to the substrate. The shingles may be passed through rollers to further embed the granules into the asphalt coating. The granules may comprise a variety of different materials. The granules may be ceramic roofing grade granules that are made in any known or conventional manner. Any type of roofing granule may be used. The granules may comprise a variety of different particle sizes and colors. Further, a variety of different granules may be blended together, e.g., to provide different color blends or to provide the appearance of varying thickness to the shingle.
The backdust particles are generally deposited onto the asphalt coating after the coating is applied to the substrate. The shingles may be passed through rollers to further embed the backdust particles into the asphalt coating. The backdust may comprise a variety of different materials, including but not limited to, Quartz (SiO2), K-Feldspar (KAlSi3O8), Na-Feldspar (NaAlSi3O8), Dolomite (CaMg(CO3)2), pulverized sand, talc, mica, calcium carbonate, ground recycled glass, or other common inorganic material. The backdust may comprise a variety of different particle sizes. For example, the backdust particles may have an average particle size between about 20 and 1000 μm, 60 and 600 μm, 100 and 400 μm, or 100 and 300 μm. In certain embodiments, the backdust particles have an average particle size of about 200 μm. The backdust may be any material that prevents the shingles from sticking together after being stacked, packaged, and/or stored for a prolonged period of time.
One or more portions of the shingle may comprise an additional layer, such as a reinforcement layer. In certain embodiments, the additional layer may be attached to the asphalt coating, e.g., by the adhesive mixture of the asphalt coating or other adhesives. In certain embodiments, the additional layer may be a polymeric layer formed from, for example, a polyester, polyolefin (e.g., polypropylene or polyethylene), or the like. However, the additional layer may be formed from other materials, such as, for example, paper, film, scrim material, and woven or non-woven glass.
For example, in certain embodiments, the shingle may include a strip of woven polyester material applied to the surface of the shingle after application of the asphalt coating, such that the asphalt material penetrates the strip between the woven fibers of the polyester fabric, to embed the strip of material in the base asphaltic layer and secure the strip to the shingle. The polyester strip may be applied prior to granule coating of the shingle, and the granules may not adhere to the strip-covered portion of the shingle. The strip of polyester material may, for example, define a shingle nail zone and provide reinforcement for the nailed portion of the shingle.
In certain embodiments, a portion of the lower surface of the shingle may be covered by a sheet of spun-bound nonwoven polyester web or mat material that is pressed into the hot asphalt material of the asphalt coating prior to backdust coating of the shingle. The hot asphalt material penetrates between the nonwoven polyester fibers to embed the mat in the base asphaltic layer. The nonwoven mat may provide additional impact resistance for the shingle, to resist damage caused by hail or other such impacts.
Shingles are generally stacked and packaged for storage and transport, e.g. in a wrapper, bag, box, or the like. The package may take a wide variety of forms, such as a plastic wrapper, a plastic bag, shrink wrap, a cardboard box, a polyethylene wrapper (e.g., 1.5-2.5 mil thick), or the like.
The Applicants have discovered that applying a hydrophobic material to surfaces of the shingles increases the contact angle of the moisture on the surfaces and decreases the wetting of the shingle bundle by prohibiting the moisture from wicking or infiltrating between the stacked shingles. Thus, the greater the contact angle the less moisture infiltrates between the layers of shingles. The contact angle of a moisture droplet is the angle formed by the moisture droplet at the three phase boundary where the liquid, gas, and solid intersect.
For example,
The hydrophobic material applied to the shingles may take a variety of different forms. For example, the hydrophobic material may be a coating on one or more surfaces of the shingle. Further, the backdust and/or granules may be coated with a hydrophobic material before being applied to the shingle (e.g., at the supplier) and/or after being applied to the shingle. Further, the material of the backdust and/or granules themselves may have hydrophobic properties. The hydrophobic material may also be applied to any surface of the shingle, such as, for example, around only the edges of the shingle, only on the back of the shingle, or on the back and front of the shingle. Further, the hydrophobic material may also be applied only to the edges of the shingle bundle to prohibit moisture infiltration between the shingles.
For example,
Referring to
Referring to
In another exemplary embodiment, the hydrophobic material 510 applied only to the edges of the lower surface of the laminated shingle 150. For example, the hydrophobic material 510 extends a distance between about 0.5 and 3 inches in from each edge of the lower surface, such as between 1 and 2 inches from each edge of the lower surface.
The Applicants have found that applying the hydrophobic material to at least one of the upper surface (i.e., top) and lower surface (i.e., back or bottom) of the shingle (e.g., around the edges of the lower surface) prohibits moisture from infiltrating between the stacked shingles. As illustrated in
A variety of different hydrophobic materials may be used. For example, in certain embodiments, a non-polar silane such as methyl, propyl, or similar material is used. The silane material may be applied to the shingle as a dilute water solution and then dried. However, a variety of other hydrophobic materials may be used, such as, for example, wax emulsions, oils, silicones, siloxanes, SBR or esters of acrylic resins. As discussed above, these hydrophobic materials increase the hydrophobicity of the surface as measured by the contact angle of moisture droplets that contact the surface.
In certain embodiments, a silane solution having a silane concentration in the range of about 0.25% to 2% was applied to the back of a shingle sheet during production at a rate of about 0.3 to 6 g silane/sq (One sq is 300 sf of shingles). The silane solution increased the dynamic contact angle of the sheet at 10 minutes from the 40-60 degrees range to the 80-120 degree range. In one exemplary embodiment, a silane solution having a silane concentration of about 0.5% was applied to the back of a shingle sheet during production at a rate of about 1.1 g silane/sq. The silane solution increased the dynamic contact angle of the sheet at 10 minutes from the 40-60 degrees range to the 80-120 degree range. As such, after the silane solution was applied to the back of the sheet and the sheet was cut into shingles and bundled, the bundles of shingles did not wick water in between the layers of shingles.
In certain embodiments, the back of shingle sheets were sprayed with a silane solution having a silane concentration of about 0.5% during production at the rate of about 0.7 g silane/sq. The sheets were cut and laminated into shingles and wrapped into bundles with 2.2 mil polyethylene wrappers. Bundles of shingles (both treated and untreated) were then placed on pallets in a shower that delivered 44 inches of water over a 48 hour period. The wrappers were opened and the shingles were observed for water. The bundles having been treated shingles were almost completely dry (i.e., less than 25% of the bottom surface area of the second shingle from the top of the stack was wet) while the bundles of untreated shingles contained substantial amounts of water between shingles (i.e., greater than 25% of the bottom surface area of the second shingle from the top of the stack was wet).
The silane bonds to the lower surface of the shingle, including the surfaces of the backdust particles, and will generally only be a few monolayers thick at the concentrations used (e.g., between about 0.25% to 2% silane). As such, the silane produces a hydrophobic surface but does not prevent laminating adhesives and sealants from bonding to the back of the shingle. For example,
As shown in
Silicones and wax emulsions are also effective in producing a hydrophobic surface and may block water absorption. However, these types of materials will often act as a release agent and form a barrier film on the surface of the shingle, thus affecting the ability of laminating adhesives and sealants to bond to the back of the shingle.
The hydrophobic material of the present application may also comprise certain particles or materials included in the backdust or granules of the shingle that increase the hydrophobicity of the shingle. The Applicants have discovered that the addition of certain particles or materials in the backdust or granules of the shingles, even in small amounts, affects the hydrophobic/hydrophilic nature of the shingle.
For example,
The Applicants have discovered that certain Titanium minerals make the shingles more hydrophobic as measured both by contact angles and water pickup through the back of the shingle and also as measured with the bundle rain test. For example, in certain embodiments, small amounts of TiO2 are added to the silica sand backdust on the lower surface of shingle sheets. In one embodiment, 0.25% TiO2 was added to the silica sand before the backdust was applied to the back of the shingle. The addition of this TiO2 increased the contact angle of the lower surface greater than 20 degrees, or about 22 degrees. Further, the 0.25% TiO2 shingle was soaked by placing it on a wet sponge for about two weeks to measure the water absorption of the shingle. The weight of the shingle increased less than 1.5% during this time, whereas the weight of a shingle without the 0.25% TiO2 increased almost 2.0%, over a 30% increase. As such, the TiO2 reduced the shingle's ability to absorb moisture.
The 0.25% TiO2 shingle was also tested to determine whether the TiO2 could withstand rain and whether the TiO2 affected the adhesion of the backdust or granules. The Applicants found that no noticeable amount of the TiO2 washed off the lower surface of the shingle and that there was no observable difference in shingle bond strength when compared to the shingle without the TiO2.
As discussed herein, the addition of a hydrophobic material (e.g., the hydrophobic coatings and hydrophobic particles discussed herein) prohibits moisture from infiltrating between the stacked shingles. As such, the hydrophobic material reduces granule loss during handling and installation of the shingles and reduces the ability of the shingles to freeze together in cold weather. Furthermore, the hydrophobic material may increase shingle life by keeping the underside of the shingle dry on the roof and preventing water infiltration under the shingle. The hydrophobic material may also help reduce leaks by preventing water from wicking under shingles. Also, the hydrophobic material may reduce the wet time of shingles on the roof, which has been shown to directly correlate to reduced algae growth, thus reducing the need for algae resistant granules.
As described herein, when one or more components are described as being connected, joined, affixed, coupled, attached, or otherwise interconnected, such interconnection may be direct as between the components or may be in direct such as through the use of one or more intermediary components. Also as described herein, reference to a “member,” “connector”, “component,” or “portion” shall not be limited to a single structural member, component, or element but can include an assembly of components, members or elements.
While the present invention has been illustrated by the description of embodiments thereof, and while the embodiments have been described in considerable detail, it is not the intention of the applicants to restrict or in any way limit the scope of the invention to such details. Additional advantages and modifications will readily appear to those skilled in the art. For example, where components are releasably or removably connected or attached together, any type of releasable connection may be suitable including for example, locking connections, fastened connections, tongue and groove connections, etc. Still further, component geometries, shapes, and dimensions can be modified without changing the overall role or function of the components. Therefore, the inventive concept, in its broader aspects, is not limited to the specific details, the representative apparatus, and illustrative examples shown and described. Accordingly, departures may be made from such details without departing from the spirit or scope of the applicant's general inventive concept.
While various inventive aspects, concepts and features of the inventions may be described and illustrated herein as embodied in combination in the exemplary embodiments, these various aspects, concepts and features may be used in many alternative embodiments, either individually or in various combinations and sub-combinations thereof. Unless expressly excluded herein all such combinations and sub-combinations are intended to be within the scope of the present inventions. Still further, while various alternative embodiments as to the various aspects, concepts and features of the inventions—such as alternative materials, structures, configurations, methods, devices and components, alternatives as to form, fit and function, and so on—may be described herein, such descriptions are not intended to be a complete or exhaustive list of available alternative embodiments, whether presently known or later developed. Those skilled in the art may readily adopt one or more of the inventive aspects, concepts or features into additional embodiments and uses within the scope of the present inventions even if such embodiments are not expressly disclosed herein. Additionally, even though some features, concepts or aspects of the inventions may be described herein as being a preferred arrangement or method, such description is not intended to suggest that such feature is required or necessary unless expressly so stated. Still further, exemplary or representative values and ranges may be included to assist in understanding the present disclosure, however, such values and ranges are not to be construed in a limiting sense and are intended to be critical values or ranges only if so expressly stated. Moreover, while various aspects, features and concepts may be expressly identified herein as being inventive or forming part of an invention, such identification is not intended to be exclusive, but rather there may be inventive aspects, concepts and features that are fully described herein without being expressly identified as such or as part of a specific invention, the inventions instead being set forth in the appended claims. Descriptions of exemplary methods or processes are not limited to inclusion of all steps as being required in all cases, nor is the order that the steps are presented to be construed as required or necessary unless expressly so stated.
The present application is a continuation of U.S. patent application Ser. No. 14/623,688, filed on Feb. 17, 2015, which claims the benefit of U.S. Provisional Patent Application Ser. No. 61/942,673, filed on Feb. 21, 2014, both of which are incorporated herein by reference.
| Number | Date | Country | |
|---|---|---|---|
| 61942673 | Feb 2014 | US |
| Number | Date | Country | |
|---|---|---|---|
| Parent | 14623688 | Feb 2015 | US |
| Child | 16534204 | US |