Patent Application
20200331180
The present disclosure relates generally to a shoe component and a manufacturing method thereof, and more particularly to a Microcellular foam shoe component and a manufacturing method thereof.
Generally, components of a foam shoe component usually includes ethylene vinyl acetate (EVA) and thermoplastic polyurethane (TPU), wherein EVA naturally has properties of lightweight, soft, shockproof and heat insulation, and the price of EVA is lower than that of TPU, so a midsole of a shoe is usually made from EVA.
Though EVA has the aforementioned advantages, the foam shoe component made from EVA, such as a midsole, has poor physical properties; for example, said shoe component is poor in durability and compression set, and said shoe component after injection molding is poor in size stability. In addition, the process of EVA injection molding, which is a chemical foam process, has cumbersome steps, so that the process is usually time-consuming Further, for the process of EVA injection molding needs to add chemical foaming agent and crosslinking agent, such as dicumyl peroxide (DCP), the shoe component containing chemical foaming agent and crosslinking agent is not easy to be decomposed, which is not recyclable, so that EVA is not an environmentally friendly material. Furthermore, most of chemical foaming agent and crosslinking agent are environmental hormones, which are poisonous to human bodies and the environment.
In view of the above, the person in the art developed a physical foaming process which could be made foam shoe components from TPU, whereby to take the place of the chemical foaming process of EVA. However, current foaming shoe components made by the physical foaming process of TPU have higher specific gravity and thicker thickness. Besides, in current physical foaming process of shoe components by injection molding, the products are generally formed as flat-shaped foaming bodies, which are not easy to be three-dimensional foaming bodies having curved surfaces, and are not easy to have a volume ratio to the mold being 1:1. Further, for the evenness of bore size of foaming bodies is difficult to be regulated, the productivity of the foaming shoe components becomes worse.
At least for the above reasons, the conventional foaming shoe components and the manufacturing method thereof still have room for improvements.
In view of the above, the primary objective of the present disclosure is to provide a shoe component and a manufacturing method thereof; through the Microcellular foam process with supercritical fluid provided in the present disclosure, the environmental hazard from the conventional chemical foaming process could be improved, and the uneven quality of the conventional foaming products could be improved, too. The foaming products provided in the present disclosure is suitable to be made into several shoe components including midsole, outsole, overlay of upper or sole and insole, but not limited thereto.
The present disclosure provides a shoe component including a foaming body. The foaming body includes a thermoplastic material and a mixed material, wherein the weight percentage of the thermoplastic material is 90 wt % to 99 wt %, and the weight percentage of the mixed material is 10 wt % to 1 wt %.
In addition, the present disclosure provides a manufacturing method of a shoe component, which includes following steps: making a predetermined gas pressure in a mold; injecting a predetermined dose of a thermoplastic foaming fluid into the mold; releasing the predetermined gas pressure of the mold; and obtaining said shoe component from the mold.
With the aforementioned design, through the Microcellular foam process with supercritical fluid, the foaming shoe component could be made by a physical process, so that the foaming shoe component provided in the present disclosure has a plurality of foaming bores which are dense and uniform, whereby to increase whole mechanical strength of the foaming shoe component. Furthermore, comparing to the conventional foaming shoe component, the foaming shoe component provided in the present disclosure has greater physical properties, such as less bore diameter, greater resilience, less compression set, and greater tear strength.
The present disclosure will be best understood by referring to the following detailed description of some illustrative embodiments in conjunction with the accompanying drawings, in which
In order to illustrate the present disclosure more clearly, the preferred embodiment, the first embodiment, the second embodiment and the accompanying drawings are described in detail below. As illustrated in
In embodiments of the present disclosure, the shoe component in Step 108 is a foaming shoe component, the shoe component includes a foaming body, and according to embodiments of the present disclosure, the foaming body of the shoe component has a Asker C hardness range of 40 to 70, and more preferably, has a Asker C hardness range of 50 to 60. Further, the foaming body of the shoe component has a plurality of bores, and a diameter of each of the bores is in a range of 0.1 μm to 100 μm. According to embodiments of the present disclosure, a diameter of each of the bores is preferably in a range of 0.1 μm to 50 μm. According to one preferred embodiment of the present disclosure, a diameter of each of the bores is more preferably in a range of 0.1 μm to 10 μm. When the diameter of each of the bores becomes smaller, the bore density of the foaming body of the shoe component becomes greater.
In addition, the foaming body of the shoe component made by the manufacturing method of the shoe component according to one preferred embodiment of the present disclosure has a specific gravity greater than or equal to 0.1 g/cm3. According to one preferred embodiment of the present disclosure, a specific gravity of the foaming body in a range of 0.2 to 0.5 g/cm3. According to another one preferred embodiment of the present disclosure, the foaming body has a specific gravity in a range of 0.1 to 0.3 g/cm3.
On the other hand, the foaming body of the shoe component made by the manufacturing method of the shoe component according to one preferred embodiment of the present disclosure has a resilience greater than or equal to 40% (measured according to ASTM D-2632). According to one preferred embodiment of the present disclosure, a resilience of the foaming body is in a range of 50% to 80%. According to embodiments of the present disclosure, a compression set of the foaming body is less than 50% (measured according to ASTM D-395B). According to embodiments of the present disclosure, a tear strength of the foaming body is in a range of 10 to 30 kg/cm (measured according to ASTM D-624).
It is worthy to mention that, a general foaming physical process is not only difficult to form a dense and uniform foaming material, but also difficult to form a three-dimensional foaming material having a complicated structure. However, the manufacturing method of the shoe component according to one preferred embodiment of the present disclosure could be used to manufacture foaming bodies having flat or three-dimensional structure with dense and even foaming bores. Further, the shoe components made from said foaming bodies having three-dimensional structure could have a curved profile. Accordingly, the manufacturing method of the shoe component according to one preferred embodiment of the present disclosure could significantly expand the practical application range of the foaming material in the technical field of the present disclosure. For example, the manufacturing method according to embodiments of the present disclosure is used not only to manufacture shoe components of shoes having greater resilience and greater functionality (such as sports shoes), but also to manufacture shoe components of common shoes (such as casual shoes and slippers). Such shoe components include, but are not limited to, midsole, outsole, overlay of upper or sole and insole.
In embodiments of the present disclosure, the foaming body includes a thermoplastic material and a mixed material, wherein the weight percentage of the thermoplastic material is 90 wt % to 99 wt %, and the thermoplastic material and the mixed material are integrated, and the weight percentage of the mixed material is 10 wt % to 1 wt %.
In accordance with embodiments of the present disclosure, the thermoplastic material includes thermoplastic polyurethane, polyamide, polyester, ionomer or a combination thereof. In embodiments of the present disclosure, the molecular weight of the thermoplastic material is in a range of 30,000 to 100,000, and more preferably, is in a range of 50,000 to 80,000. If the molecular weight of the thermoplastic material is less than 30,000, the foaming body would have poor structural strength, which could not provide dense bores efficiently, so that said bores would be broken easily, whereby the density of the bores is difficult to be regulated. If the molecular weight of the thermoplastic material is greater than 100,000, the generation of the bores would be inhibited because the foaming body has a greater structural strength.
In accordance with embodiments of the present disclosure, the mixed material includes a filler which comprises a mineral fiber, calcium carbonate (CaCO3), silica, talcum powder, sodium bicarbonate (NaHCO3) or a combination thereof. In embodiments of the present disclosure, the mineral fiber includes slag fiber, rock fiber and a combination thereof, wherein the slag fiber could be slag wool, and the rock fiber could be rock wool. In accordance with embodiments of the present disclosure, the mixed material includes a physical foaming material which is a thermally expanded hollow material. In embodiments of the present disclosure, the thermal expanded hollow material could be hollow plastic microspheres (such as Expancel provided from AkzoNobel).
Referring to
In Step 104 of embodiments of the present disclosure, the thermoplastic foaming fluid includes, but not limited thereto, a thermoplastic material, a mixed material and a supercritical fluid uniformly blended with each other, wherein the supercritical fluid includes supercritical N2 fluid or supercritical CO2 fluid. In one preferred embodiment of the present disclosure, the thermoplastic foaming fluid includes said thermoplastic material, said filler and said supercritical fluid uniformly blended with each other, wherein said supercritical fluid includes supercritical N2 fluid or supercritical CO2 fluid. In another one preferred embodiment of the present disclosure, the thermoplastic foaming fluid includes said thermoplastic material, said physical foaming material and said supercritical fluid uniformly blended with each other, wherein said supercritical fluid includes supercritical N2 fluid or supercritical CO2 fluid.
According to the first embodiment of the present disclosure, as shown in
According to the second embodiment of the present disclosure, as shown in
In
In embodiments of the present disclosure, when the predetermined gas pressure of the mold 20 is released, the gas pressure of the mold 20 becomes less, and even would be zero. It is worthy to mention that, in embodiments of the present disclosure, the mold 20 has a pressure releasing hole (not shown) which is used to release the gas pressure of the mold 20, whereby to decrease the gas pressure of the mold 20. Further, the supercritical fluid in the thermoplastic foaming fluid would be gasified to generate a plurality of microbubbles, whereby to form the foaming shoe component. In embodiments of the present disclosure, the gas pressure of the mold 20 is released to 0 bar in 0.2 to 12 seconds. According to embodiments of the present disclosure, the gas pressure of the mold 20 released to 0 bar is in 1, 5 or 10 seconds. In embodiments of the present disclosure, the temperature of the mold 20 keeps in 20 to 60° C. in the manufacturing process of the shoe component.
As mentioned in Step 108 of
As mentioned above, through the Microcellular foam process with supercritical fluid, the foaming shoe component could be made by a physical process, so that the foaming shoe component provided in the present disclosure has a plurality of foaming bores which are dense and uniform, whereby to increase whole mechanical strength of the foaming shoe component. Furthermore, comparing to the conventional foaming shoe component, the foaming shoe component provided in the present disclosure has greater physical properties, such as smaller bore diameter, greater resilience, less compression set, and greater tear strength.
It must be pointed out that the embodiments described above are only some preferred embodiments of the present disclosure. All equivalent structures which employ the concepts disclosed in this specification and the appended claims should fall within the scope of the present disclosure.
| Number | Date | Country | Kind |
|---|---|---|---|