The design of many types of footwear is often driven by conflicting considerations. As but one example, it is normally desirable for an athletic shoe to have a construction that supports and protects a wearer's foot during a particular athletic endeavor. However, “breathability” is also a desirable quality for many types of athletic shoes. Specifically, air flow from the outside to a shoe interior can help relieve the effects of heat and perspiration that typically build up around a foot during sporting activities. Unfortunately, many materials that provide good support and foot protection can block air and moisture flow. Conversely, many materials that facilitate air and moisture flow provide little support or protection to the wearer's foot.
One solution is to fabricate a shoe in which some portions are formed from supportive/protective materials and some portions are formed from breathable materials. However, this can increase the complexity of the fabrication process and increase cost. Moreover, footwear design (including athletic footwear design) is also driven by aesthetics. A complex production process developed to fabricate a complex shoe can potentially limit a manufacturer's ability to vary that shoe's design to achieve different aesthetic effects.
This Summary is provided to introduce a selection of concepts in a simplified form that are further described below in the Detailed Description. This Summary is not intended to identify key features or essential features of the invention.
In at least some embodiments, a shoe has an upper that includes a bonded mesh composite panel. The panel may include a substrate layer formed from synthetic leather or another material chosen to provide support and protection to the foot of a wearer, but that can include ventilation openings. The panel further may include a mesh layer that is bonded to the substrate layer and spans one or more of the ventilation openings. One or more panels of thermoplastic polyurethane (TPU) or other desired material can also be included in certain regions so as to create skin layers that provide abrasion protection for the mesh layer and/or to achieve different aesthetic effects.
A bonded mesh composite panel for an upper is in some embodiments fabricated by first arranging panels of substrate, mesh and skin layer materials into an assembly corresponding to the locations of those panels in a completed upper. The assembly may also include separate layers of hot melt bonding material interposed between the substrate, mesh and skin layers, and/or a bonding material may be a component of a substrate, mesh and/or skin layer material. The assembly is then pressed at an elevated temperature so as to melt the bonding material and/or the skin layers and bond the elements together. Before the pressed assembly completely cools, it may be pressed a second time in an unheated press. A heat-conductive compressible pad can be used in the pressing process to create a surface effect in the skin layers that reveals a pattern of an underlying mesh layer (or other layer).
In some embodiments, a bonded mesh composite panel is used to form a three-dimensional upper shell that includes extensions used for double-lasting and/or to otherwise provide a shelf to support foam padding. The foam padding may be, e.g., a foam midsole. The extensions of the upper shell may be located in a lower portion of the shell and may be bonded to the foam midsole in a heel, midfoot and/or forefoot regions.
Additional aspects of this invention relate to uppers for article of footwear (and blanks for making such uppers). These uppers may include, for example: (a) a base layer (including one or more separate pieces); (b) a first skin layer (in one or more separate pieces) partially covering the base layer; and (c) a second skin layer (in one or more separate pieces) partially covering the base layer. The skin layers may be overlapped in varying manners such that in a single upper: (a) at a first portion of the upper, the first skin layer directly contacts the base layer and is covered by the second skin layer and (b) at a second portion of the upper, the second skin layer directly contacts the base layer and is covered by the first skin layer. The base layer may include a mesh material layer and/or a support layer (such as a synthetic leather, a thermoplastic polyurethane, etc.).
Another potential aspect of this invention relates to uppers for articles of footwear (and blanks for making such uppers) that may include, for example: (a) a base layer; (b) a first skin layer partially covering the base layer, wherein the first skin layer has a first color; and (c) a second skin layer partially covering the base layer, wherein the second skin layer has a second color and is at least partially transparent or translucent. In such upper constructions, at a first portion of the upper, the first skin layer may directly contact the base layer and may be covered by the second skin layer such that a color appearance at the first portion of the upper constitutes a blend of the first color and the second color. If desired, in at least some examples of this invention, the color of the first skin layer may be different from that of the second skin layer. Also, if desired, the first skin layer may be at least partially transparent or translucent. These differently colored skin layers also may be layered in varying manners on a single upper construction as generally described above.
Still another aspect of this invention relating to uppers (or blanks for making them) may include, for example: (a) a base layer having a first color; (b) a support layer (e.g., a mesh layer, a synthetic leather layer, a TPU, a skin layer, an eyelet reinforcing element, a toe reinforcing element, a heel reinforcing element, a decorative element, another support element, etc.) provided at least partially on the base layer, wherein the support layer has a second color; and (c) a first skin layer partially covering the base layer and the support layer, wherein the first skin layer has a third color and is at least partially transparent or translucent. This example upper may have: (a) a first color appearance at a first portion where the first skin layer is absent, (b) a second color appearance different from the first color appearance at a second portion where the first skin layer covers the base layer and the support layer is absent, and (c) a third color appearance different from the first and second color appearances at a third portion where the first skin layer covers the support layer.
Another aspect of uppers in accordance with at least some examples of this invention (and the blanks for making such uppers) may include: (a) a base layer (made from one or more separate pieces); (b) a first skin layer portion applied to the base layer, wherein the first skin layer portion includes a first engagement edge; and (c) a second skin layer portion applied to the base layer, wherein the second skin layer portion includes a second engagement edge. The second engagement edge may be provided on a piece of the base layer that is a unitary, one piece construction with a portion of the base layer that extends around a rear heel area of the upper (if desired, the base layer may be made from multiple pieces such that the first skin layer portion is on a first piece of the base layer and the second skin layer portion is on a second, separate piece of the base layer). The first skin layer portion and the second skin layer portion may be engaged together at a bonded joint (e.g., by hot melt bonding) provided at an overlap of the first engagement edge and the second engagement edge, wherein the bonded joint is located along a medial midfoot side region of the upper. Alternatively, if desired, the bonded joint could be located at a lateral midfoot side region of the upper. Uppers in accordance with this aspect of the invention need not include a seam in the rear heel area.
Another example aspect of this invention relates to tongue members for articles of footwear. Such tongue members may include, for example: (a) an interior layer made from an interior layer panel having a first width in a medial side to lateral side direction; (b) an exterior layer made from an exterior layer panel having a second width in the medial side to lateral side direction, wherein the first width is less than the second width; and, optionally, (c) an intermediate layer between the interior layer panel and the exterior layer panel. The interior layer panel and the exterior layer panel may be bonded to one another using a curved platen or other curved support surface and formed as a curved composite tongue member (e.g., by hot melt bonding).
Finally, additional aspects of this invention will relate to shoes including the uppers and/or other components described above (e.g., by engaging the upper with a sole structure (e.g., a midsole, an outsole, etc.)), as well as to methods of making the uppers, shoes, and/or other components.
Some embodiments are illustrated by way of example, and not by way of limitation, in the figures of the accompanying drawings and in which like reference numerals refer to similar elements.
FIGS. 4A1 through 4L show operations in a process, according to at least some embodiments, to fabricate a unibody upper panel for the shoe of
At least some embodiments include an athletic shoe or other type of footwear in which an upper has a panel formed from a bonded mesh composite. The mesh composite includes an inner substrate layer that provides support and protection in appropriate regions based on activities for which the shoe is intended. The substrate layer can also include one or more openings for ventilation, weight reduction or other purposes. The mesh composite further includes a mesh layer that is bonded to the substrate layer and located on the outer side of the substrate in the finished shoe. This construction offers several advantages. For example, the mesh can reinforce the substrate and help retain individual portions of the substrate in a desired arrangement, thereby permitting larger ventilation holes in the substrate. Moreover, covering those ventilation holes and surrounding substrate regions with a mesh can avoid edges that might separate as the shoe wears. A “skin” layer may cover the mesh layer in one or more areas to provide additional durability and/or for decorative purposes. In some embodiments, all or substantially all of the upper is formed from a mesh composite panel that extends around the heel counter region. In other embodiments, the upper may have a mesh composite panel in a front portion that is bonded or otherwise attached to a separate panel that forms a rear portion of the upper.
To assist and clarify the subsequent description of various embodiments, various terms are defined herein. Unless otherwise indicated, the following definitions apply throughout this specification (including the claims). The “interior” of a shoe refers to space that is occupied by a wearer's foot when the shoe is worn. The “inner side” of a panel or other shoe element refers to the face of that panel or element that is (or will be) oriented toward the shoe interior in a completed shoe. The “outer side” of an element refers to the face of that element that is (or will be) oriented away from the shoe interior in the completed shoe. In some cases, the inner side of an element may have other elements between that inner side and the interior in the completed shoe. Similarly, an outer side of an element may have other elements between that outer side and the space external to the completed shoe.
A “bonded” composite element is an element that includes substituent elements (e.g., panels of textile or other materials) that are bonded to one another. Bonding includes bonding through use of glue or other adhesives, through melting and subsequent solidification of a bonding material, and/or through melting and subsequent solidification of a substituent element, but excludes stitching, stapling or similar types of mechanical attachment. Although a bonded composite element may include stitching or other types of mechanical attachment (e.g., to attach the bonded composite element to another element, to shape the bonded composite element), the bonded composite does not rely on that stitching or other mechanical attachment to structurally connect the substituent elements of the bonded composite.
Certain regions of an upper are defined by reference to the anatomical structures of a human foot wearing a shoe that is properly sized for that foot. One or more of the below-defined regions may overlap. The “forefoot” region of an upper is the portion of the upper that will generally cover the metatarsal and phalangeal bones of the wearer's foot, and which will extend beyond the wearer's toes to the frontmost portion of the upper. The “midfoot” region of an upper is the portion of the upper that will generally cover the cuboid, navicular, medial cuneiform, intermediate cuneiform and lateral cuneiform bones of the wearer's foot. The “hindfoot” region of an upper extends from the midfoot region to the rearmost portion of the upper and covers the wearer heel. The hindfoot region covers the sides of the calcaneus bone of a wearer and may, depending on a particular shoe configuration, cover some or all of the wearer's talus bone (ankle).
The “top forefoot” and “top midfoot” regions of an upper will generally cover the upper surfaces of a wearer's forefoot and midfoot bones described above. The “toe” of the upper is the portion that will generally cover the tops and fronts of the toes and that extends from the top forefoot region to the lowest edge of the upper in the direction of the sole. The “lateral forefoot” region extends between the top forefoot and the lowest edge of the upper in the direction of the sole and between the toe and lateral midfoot regions. The “lateral midfoot” region extends between the top midfoot region and the lowest edge of the upper in the direction of the sole and between the lateral forefoot and hindfoot regions. In a similar manner, the “medial forefoot” region extends between the top forefoot region and the lowest edge of the upper in the direction of the sole and between the toe and medial midfoot regions, the “medial midfoot” region extends between the top midfoot region and the lowest edge of the upper in the direction of the sole and between the medial forefoot and hindfoot regions. The “topfoot region” includes the top forefoot and top midfoot regions. The “lateral side” region includes the lateral forefoot and lateral midfoot regions. The “medial side” region includes the medial forefoot and medial midfoot regions.
Shoe with Mesh Composite Upper Panel
In the embodiment of shoe 10, mesh composite panel 16 generally covers the toe region, the top, lateral and medial forefoot regions, the top, lateral and medial midfoot regions, and portions of the hindfoot region. The foxing panel 17 covers the remainder of the hindfoot region. As explained in more detail below, shoe 10 of
Returning to
The embodiment of
Because mesh layer 28 is directly bonded to substrate layer 27, the combined strength of the mesh and substrate materials obviates the need for another material on the outside surface of upper 11 to provide tensile strength. This permits upper 11 to be much lighter than is possible using various conventional shoe construction techniques. Panels of skin material (which are relatively lightweight) can be included in certain areas of an upper where abrasion protection is helpful.
Ventilation holes 31, 32, 33 and 34 in substrate layer 27 allow air to flow through perforations of the mesh material of layer 28. This air flow helps to cool and dry the foot of a wearer of shoe 10. In some embodiments, there are no additional material layers separating substrate layer 27 and the foot of a wearer (or the socked foot of a wearer) in the regions around one or more of holes 31, 32, 33 and 34, and air can directly reach the interior of shoe 10. In other embodiments, upper 11 of shoe 10 may include an additional lining (e.g., a “bootie”) between substrate layer 27 and a wearer's foot. In such embodiments, air cannot directly reach the wearer's foot through holes 31, 32, 33 and 34, but ventilation is still improved relative to many conventional constructions, as materials used for a bootie or other liner are typically porous and significantly more breathable than materials used for substrate layer 27.
The number, size and location of ventilation holes will vary in different embodiments. In some embodiments, an upper may include ventilation holes as small as (or smaller than) 2 mm in diameter, while in other embodiments, the ventilation holes may be quite large and cover a substantial portion of the upper. In some embodiments, minimum spacing between some ventilation holes can be based on the minimum area needed to effectively bond the mesh and substrate layer materials used for a particular embodiment.
The material of skin layer panels 36a, 36b, 36c and 36d provides abrasion protection for mesh layer 28. A skin material panel can also be added for decorative purposes. For example, skin material elements can include one or more additional elements such as element 36d in the shape of a logo or other identifier of the manufacturer of shoe 10. Although much of skin layer panels 36a-36d are overlaid on the mesh material of layer 28, some portions of skin layer panels are directly bonded to substrate layer 27 without an interposing layer of mesh material. For example, and as described in more detail below in connection with FIGS. 4A1-4K, skin layer panels 36a-36c cover some portions of substrate layer 27 over which mesh layer 28 does not extend. Moreover, and as also described in more detail below, a portion of skin layer panel 36a overlays (and is bonded to) foxing panel 17. In some cases, an interposing mesh layer is omitted for structural purposes. An interposing mesh layer could also be omitted for decorative reasons.
Shoe 10 includes a foamed ankle collar 141, a heel counter (not shown) and a tongue 41. Tongue 41 may be stitched or otherwise bonded to the inside of upper 11. Attachment of collar 141 is described below. Upper 11 may be bonded to a midsole 42 in any of various manners. In some embodiments, upper 11 is slip lasted and attached to a strobel layer, with that strobel layer then bonded to an upper face of midsole 42. Other types of constructions are used in other embodiments to attach upper 11 to a midsole or other sole component. One example of such a construction is discussed below in connection with
As can also be seen in
Shoe 10 of
In some embodiments, a separate panel of hot melt bonding material may not be placed between a skin layer panel and a mesh or substrate layer panel. Instead, the skin layer panel is bonded to the other layer(s) solely through the melting of the skin layer panel so as to fuse the skin layer to one or more other layers. Similarly, inserting a separate panel of hot melt bonding material between a substrate material panel and a mesh material panel is unnecessary in some embodiments. In certain embodiments, for example, a substrate layer 27 may comprise a laminate that includes a first material layer (e.g., artificial leather) and a second material layer (e.g., thermoplastic polyurethane) prelaminated to a face of the first material layer by the substrate material manufacturer. Panels of that two layer substrate material can then be cut to shape by a shoe manufacturer and used as substrate layer 27. In such an embodiment, the second material layer would be oriented to face mesh layer 28 and would melt during pressing so as to fuse to mesh layer 28 (and to the skin layer(s)), and the separate layer of bonding material 39 could be omitted. Indeed, some embodiments may not require any separate bonding material layers, and could rely on melting of the skin and/or substrate layers themselves to achieve bonding. As another alternative, large sections of mesh, substrate or skin material could have a separate hot melt bonding material (e.g., such as would be used for layer 39 or 40) pre-applied (e.g., by the material supplier or in a preprocessing step by a shoe manufacturer) prior to cutting of individual upper panels from the large material sections. Combinations of these techniques could also be used.
Region B in
As also seen in region C, the skin material of panel 36a conforms to the mesh material of layer 28 so that a contour of the mesh material pattern is revealed through panel 36a. Other skin material panels that overlay mesh layer 28 similarly may conform to the mesh material. In this manner, upper 11 can have a more continuous appearance than might otherwise be possible. By providing layers of skin material that have a texture revealing an underlying mesh material, a potential purchaser of shoe 10 is also made aware of the structure of shoe 10. Moreover, it is believed that the conformal nature of the contact between a skin material panel and underlying mesh and substrate layer materials helps to increase the bonded surface areas and overall material strength.
As indicated above, the substrate material of layer 27 provides support and protection for the foot of a wearer of shoe 10. In at least some embodiments, the substrate material is (or includes) a synthetic leather or another material that is sufficiently durable to protect a foot in regions where the upper is likely to contact external objects and/or where foot support is needed, but sufficiently flexible to provide comfort.
Many different substrate materials can be used. In some embodiments, substrate materials are selected so as to provide support for the lamination package (i.e., the stack of substrate, mesh and other materials assembled to create an upper) and to adequately bond to the mesh material. To achieve such goals, substrate materials can be chosen so as to have limited stretch, to bond well and be chemically compatible with TPU hot melt, to have a continuous (i.e., non-mesh) surface so as to provide more bonding surface area, and to be cuttable with clean edges in mass production. Table 1 lists examples of substrate materials that can be used in at least some embodiments; other materials could also be used.
The mesh material of layer 28 reinforces upper 11 by augmenting the strength of the substrate material where the two materials are bonded, thereby allowing use of thinner substrate material elements. Incorporation of mesh material into an upper further allows elimination of substrate material in areas where the full protection and support of the substrate material is not as important, thus permitting further reduction in substrate material and overall shoe weight. The mesh material of layer 28 also allows air to flow through openings in substrate layer 27 to help cool and dry the foot of a wearer.
In at least some embodiments, the mesh material of layer 28 is a single layer warped knit with an open structure (or other type of woven material) and is formed from nylon, polyester, nylon/polyester blends, recycled polyethylene terephthalate (rePET), or other material. In certain embodiments, the mesh material has more than 50% open area (e.g., more than 50% of the material surface area comprises open space through which air can freely flow from one side to the other). In some embodiments, SPANDEX (or other stretchable meshes) and spacer meshes (meshes with filler yarn) are undesirable. Table 2 lists examples of the mesh material in at least some embodiments; other materials could also be used.
The skin material for panels 36a-36d reinforces the mesh and substrate materials, protects the mesh material layer in certain areas (e.g., provides abrasion resistance), and/or provides a decorative surface on upper 11. In at least some embodiments, the skin material is a thermoplastic polyurethane (TPU) or other appropriate material. In certain embodiments, the skin material is a multilayer material having an outer heat-resistant layer for abrasion resistance and an inner layer for hot melt bonding. For example, the outer layer can be thermoset polyurethane (PU) or a TPU with a high melt temperature, and the inner layer can be a TPU having a lower melt temperature suitable for hot melt bonding and production temperatures. Table 3 lists examples of materials that can be used for the skin material in at least some embodiments; other materials could also be used.
In at least some embodiments, and as shown schematically in
In at least some embodiments, a TPU hot melt bonding material could have a melt temperature between 80° C. and approximately 120° C. and be polyester-based. Table 4 lists examples of hot melt bonding materials that can be used in at least some embodiments; other hot melt bonding materials could also be used.
The final material in Table 4 (polyether film) may be desirable, e.g., in certain embodiments in which high humidity is a concern.
According to at least some embodiments, a bonded mesh composite panel of an upper is created by assembling individual panels of material for the various layers in a flat configuration. If the upper is to include additional portions (e.g., a rear portion such as panel 17 of shoe 10), additional material elements can be included as part of the assembly process. The panels and other elements are assembled so as to have an arrangement in which the relative locations of the panels and elements correspond to the locations those panels and elements will have in the completed shoe. After assembling the individual panels and/or other elements into the proper arrangement and tacking the assembly at several locations, the assembly undergoes a series of pressing operations to bond the assembled elements. These operations create a flat, one-piece unibody upper shell that can contain many or all elements to be included in the finished upper. Edges of the unibody upper shell can then be joined to create a three-dimensional upper body ready for further finishing and attachment to a midsole.
FIGS. 4A1 through 4K show a process, according to at least some embodiments, for fabricating the mesh composite panel 16 for shoe 10 of
Other elements of upper 11 are positioned on jig 100 in a similar manner. In step 2 (
In step 3 (
In step 4 (
Other types of reinforcements can be placed in other areas of a shoe upper in a manner similar to that used for eye stay reinforcements 56 and 57. In some embodiments, for example, additional reinforcement could be placed over the area of the substrate layer panel that will be located in the toe region of a completed upper. In another embodiment, reinforcement materials could be placed over the portions of the substrate layer panel that will be located at the lateral and medial sides of a completed shoe, with those reinforcement materials forming reinforcing strap attachment points in a finished upper.
In step 5 (
As seen in
In step 6 (
In some embodiments, extra and/or higher strength bonding material and/or additional adhesives may be included in portions of a composite panel that will correspond to a toe region and/or to other forward regions of an upper of a completed shoe. This additional bonding may be desirable in embodiments where toe portions of an upper may experience significant stresses during various manufacturing operations (e.g., toe forming, lasting).
In step 7 (
Panel 36a of skin layer material is placed onto jig 100 in step 8 (
In step 9 (
The tacking of step 9 results in a partial bonding so that the individual elements of assembly 116 will remain in an assembled condition when assembly 116 is removed from jig 100. In step 10 (
In at least some embodiments, silicone pad 120 is first preheated to 110° C. prior to the pressing operation of step 10. Typical process parameters for the hot pressing operation of step 10 are upper and lower press platen temperatures of 120° C., press pressure of approximately 20 kg/cm2, and press time of 30 to 40 seconds. However, the process parameters for a particular shoe upper will depend on the combination of materials and on the panel arrangement applicable to that upper. In some embodiments, the press time for step 10 can be determined by assembling panels for a particular upper design into a test panel assembly, with thermocouple temperature probes inserted at one or more locations within the test panel assembly. The test panel assembly is then pressed between 120° C. press platens until the temperature probes indicate that the internal assembly temperature has reached a desired melting point for the skin materials in the test panel assembly. If desired, the press time can be adjusted upward or downward by adjusting the press platen temperature. The desired melting point temperature for a particular skin material can be determined by using differential scanning calorimetry (50° C./min scan rate) to find the temperature associated with the maximum heat transfer for that skin material. Press pressure can be adjusted upward if there is insufficient bonding between layers in one or more test panel assemblies or adjusted downward if there is excessive (and undesired) “flattening” of surface features.
After the heated pressing of step 10, assembly 116 is “cold” pressed between room temperature press platens to continue to the bonding process and to enable melted TPU to set while under pressure so as to improve bonding. As used herein, “room temperature” is a temperature between approximately 20° C. and approximately 30° C. By cold pressing assembly 116 immediately after the heated pressing of step 10, individual elements are held in contact while the hot melt bonding material and skin layers solidify, thereby preventing materials rebounding from one another after the initial heated pressing. Without a subsequent cold pressing, for example, a skin layer element in at least some embodiments will not conform to an underlying mesh layer so as to show the mesh pattern on the outer side of the skin layer.
Heat-conductive silicone pads 120 and 129 used in steps 10 and 11, respectively, are at least partially compressible and conformable to the surface features of panel assembly 116. This permits compression of the panel assembly to bond the various layers without overly flattening the surface features. This also allows formation of a profile, such as is shown in region C of
At the completion of step 11, tacked assembly 116 has been transformed into a fused unibody shell that includes mesh composite panel 16 and foxing panel 17.
In step 14 (
In step 17 (
After completion of step 17, the three-dimensional shell 116 (with attached collar 141 and foam element 140) may undergo additional finishing prior to bonding to midsole 42 (
Operations similar to those described above can be used to create a tongue for attachment to shell 116. In particular, a tongue can also be formed by positioning one or more layers on jig, tacking those layers together, and then hot and cold pressing those layers to form a mesh composite panel in the shape of a tongue. The mesh composite of the tongue can have similar materials as are described above (e.g., a substrate, mesh and skin layers) or other combinations of materials. For example, a tongue composite panel can be formed to include a curved composite panel shaped to conform to the top of a wearer's foot and/or to include a padded element that is molded into a desired shape on the outer (or inner) side of the tongue composite. Elements for such a tongue composite could include, for example, a textile layer and a moldable foam padding layer. Instead of a using a set of flat press platens such as is shown in
Hot melt materials may be provided as separate layers and/or provided as part of the outer skin layer 176, the intermediate layer(s) 174, and/or the substrate layer 172, e.g., in the manners described above. Because each of these layers 172, 174, and 176 may be flexible and pliable (e.g., made of fabrics, textiles, thin substrates, etc.), they can conform to the curved shape of the platens 170 and/or 178. At least one of the layers 172, 174, and/or 176 may be made from a shape retaining material so that the overall composite tongue will maintain a curved shape after the pressing step(s). The overall width(s) of the various layers (in the W direction in
If desired, the hot melt material need not bond with intermediate layer(s) 174. Rather, if desired, the intermediate layer(s) 174 may be simply held in place by the bonding of the substrate layer 172 and the skin layer 176. Optionally, if desired, along the edges of the composite tongue assembly, hot melt material may pass through the material of the intermediate layer(s) 174 to reach the opposite side and bond on the opposite side (e.g., to bond the substrate layer 172 to the skin layer 176 and pin the intermediate layer(s) 174 in between). Alternatively, the hot melt material also may bond to the intermediate layer(s) 174.
The composite tongue member may be incorporated into an upper structure in any desired manner and/or at any desired time in the overall construction process without departing from this invention. For example, the composite tongue member may be separately formed and engaged with the upper in any desired manner, such as by stitching, adhesives, hot melt fusion (using heat and pressure), HF welding, mechanical connectors, etc., including in manners conventionally known and used in the art. As other examples, if desired, some or all portions of the composite tongue member can be integrally formed with one of the layers of the remainder of the upper or engaged with one of the layers of the remainder of the upper, e.g., during the processes described above in conjunction with FIGS. 4A1 through 4K. Other ways of engaging the tongue member with the upper also may be used without departing from this invention.
Shoe 10 and the fabrication operations described above are merely examples of shoes and fabrication processes according to various embodiments. As indicated above, the shape and arrangement of a substrate layer, mesh layer and/or skin layer can vary in different embodiments, as can the number, size and arrangement of ventilation openings in a substrate. Moreover, different types of substrate materials, mesh materials and/or skin materials could be employed for different shoe types. For example, a running shoe may utilize a mesh material that is lighter and/or has a different weave pattern than a mesh material used for a basketball shoe. Indeed, a single shoe could include more than one type substrate material and/or more than one type of mesh material and/or more than one type of skin material. In some embodiments, a skin layer might be omitted.
Certain embodiments may incorporate more than one type of mesh material in a single upper in various ways. For example, an upper according to some such embodiments may have a first type of mesh material in one portion of the upper and a second type of mesh material in a different portion. The first type of mesh may be of lighter weight and have larger openings so as to increase ventilation, and may be placed in locations that will correspond to portions of an upper that will be subject to less severe forces. The second type of mesh material may have a denser weave and/or be formed from a higher strength material, and may be placed in locations that will correspond to portions of an upper that will be subject to more severe forces. More than two types of mesh material can be used in an upper, and different mesh material types can be combined for other reasons (e.g., to achieve a desired aesthetic, to reduce unit cost, etc.).
Some embodiments can include uppers in which there may be multiple mesh layers. In some cases, one mesh material panel may overlap another mesh material panel in an area where extra reinforcement is desired. In still other cases, separate mesh material panels may not overlap one another, and may be located at different layers of an upper. For example, a first panel of mesh material could be overlaid on a substrate material layer, a second panel of substrate material (or other type of material) overlaid onto a portion of the first panel, and a third panel of mesh material overlaid so as to overlap a portion of the second panel. In some embodiments, mesh material panels may be located at the same layer but not overlap one another.
Additional types of materials can be added to an upper shell in additional embodiments. Such additional materials can be included so as to form an outrigger, a shank, a heel cup, a toe cap, etc. For example, a panel of rigid nylon or other polymer could be included in the toe region of a composite panel and shaped as part of the toe shaping process described above. As another example, a counter panel formed from nylon or other type(s) of polymer could be included, during the process of assembling upper panels on an assembly jig, in a location that corresponds to the sides and rear of a wearer's heel in a completed shoe. Those counter panels can then be hot melt bonded to the inner side of panel 17 during the pressing operations.
In some embodiments, an upper shell formed according to the above described steps can include extensions in one or more panels (e.g., panel 17 of FIGS. 4A1 et seq.) near regions that will correspond to the heel of a wearer. After completion of step 17 (
In certain embodiments, additional panels and/or panels having extensions can be included in a panel assembly so as to form a carrier layer for foam inserts. For example, such extensions can be included in regions of substrate material panels, foxing panels or other panels that can be wrapped under the bottom of a three-dimensional upper (after step 17 of
In some embodiments, and as shown in
In at least some embodiments mesh material can also be omitted from portions of a composite panel that correspond to the regions where the upper will join a midsole. In this manner, a smoother transition from upper to midsole or other tooling can be achieved. Alternatively, a layer of foam or other moderator can be interposed between the lower edge of an upper and a midsole.
In some embodiments, a substrate material panel can be pre-processed so as to create an indentation in the form of a product name, a logo, or other shape. A skin layer material panel is then placed over the substrate material panel so as to completely cover the indentation and can be melted during the hot pressing operation so as to flow into and completely cover the indentation. The indentation can be created during a pre-processing operation using an HF welding tool having the desired shape, using laser cutting, or by other desired method. In certain embodiments, the skin layer panel used to cover the indentation may be thinner than skin layer panels used in other portions of an upper so as to create crisper and more defined edges of the covered indentation. Indentations can similarly be added to substrate material panels for other purposes. For example, indentations can be created to locate and/or accommodate harder materials used for reinforcement and protection in certain regions (e.g., for eye stay reinforcement, for heel counters, etc.). As another example, indentations can be created to locate and/or accommodate padding layers.
In certain embodiments, and as shown in
In some embodiments, malleolus padding can be included in the region of the upper that will correspond to the portion of the wearer foot near the ankle. In some such embodiments, indentations are formed in the portions of foxing panel 17 (see FIGS. 4A1 et seq.) that will correspond to the regions around the wearer ankles. These indentations can be formed, after step 11 of
Various modifications can also be made to the above-described fabrication process in other embodiments. For example, different types of jigs or jig configurations can be used. In some embodiments, a jig with retractable pins can be employed to eliminate the need for a tacking operation (such as step 9 described above in connection with
In some embodiments, a dual pan assembly jig can be employed so as to avoid a tacking step.
Material panels of assembly 316 are placed in their proper locations on pins 454 in a manner similar to that described above in connection with FIGS. 4A1 through 4H, with the locations for individual panels identified by different groups of pins 454. If surface 455 does not have a non-stick coating, a layer of release paper can be placed onto surface 455 before placing panels of assembly 316. Instead of tacking the panels together as described in connection with
While pad 420 rests over panel assembly 316, and as shown in
In some embodiments, an assembly process using jig 450 can be modified so that some or all of the assembled panels are slightly tacky. This tackiness could prevent panels from slipping if pad 420 is moved after placement onto pan 453, but would allow removal and repositioning of panels during the assembly process. Panel tackiness can be achieved, e.g., by including small amounts of uncured bonding material on some panels. In still other embodiments, panel tackiness can be achieved by including heating elements on lower pan 452 that raise the temperature of pan 453 enough begin the melting of hot melt bonding materials in a panel assembly (and to at least partially preheat upper pan 453 before the hot pressing operation).
The order of at least some steps can also be varied in some embodiments. In some embodiments, a tool used in an HF welding process (e.g., step 16 described above in connection with
As indicated above, some embodiments include upper shells that have extensions used for double-lasting and/or to provide a shelf to support foam padding.
In
Panel 501 will form the inner layer of the upper shell being fabricated. Panel 501 can be formed, e.g., from a synthetic leather or other material from Table 1. Face 502 of panel 501 is visible in
For example, and as will be seen more clearly in connection with
As previously discussed, a wide variety of ventilation openings can be included in upper shells according to various embodiments. For example, instead of relatively large ventilation openings such as holes 31-34 in upper 11 of shoe 10 (see, e.g.,
In
In
In
In the completed shoe, panel 528 will surround the rear of the wearer foot and includes an extension 506 that will extend over the lateral side of a wearer midfoot. Panel 528 further includes medial extension 507 that will surround an ankle opening on a medial side and a lateral extension 508 that will surround an ankle opening on a lateral side. Extensions 507 and 508 respectively include cutouts 509 and 510 that will ultimately create decorative contours in the exposed surface of a completed upper. Additional cutouts could be included in either or both of extensions 507 and 508 and/or in other portions of panel 528.
Panel 527 will extend over the arch region or a wearer foot in a completed shoe. Panels 529 and 530, which may be formed from nylon or other material, will serve as eye stay reinforcements in the completed shoe. The material(s) from which panels 527 and 528 are cut may include a laminated layer of TPU or other heat-activatable bonding material, which layer may then be oriented inward (e.g., toward face 502 of panel 501). A separate layer of hot-melt bonding material can be placed between skin panel 524 and each of eye stay reinforcement panels 529 and 530.
In
The assembly of panels from
Also marked in
In some embodiments, an ankle collar and/or padding can be added to panel 540 after trimming, but prior to bonding regions 571 and 572. The ankle collar (which could be located along edge 575 of panel 540) and the padding (which could be part of the ankle collar and/or located on the inside face of panel 540 below edge 575) could be added using techniques described in connection with previous embodiments.
Also shown in
As part of assembling the shoe that will include shell 540′ and midsole 610, midsole 610 is placed into shell 540′ so that surface 611 contacts last L. This is represented by an arrow in
In a subsequent fabrication step, the extension portions of shell 540′ are folded over and bonded to surface 615. In particular, an adhesive is applied to regions 601a-601k of inner face 600. A fabricator then sequentially pulls on lower portions of shell 540′ so as to stretch shell 540′ tightly against last L and, while maintaining tension on shell 540′, presses those pulled lower portions against surface 615 so as to bond each of regions 601a-601k to surface 615.
In other embodiments, extension portions of an upper shell may not form a support shelf located in heel, medial mid- and forefoot, and lateral mid- and forefoot regions. For example, a shell in some embodiments may only include extensions that form a support shelf located in a heel region. As another example, a shell in other embodiments may only include extensions that form a support shelf located in heel and midfoot regions.
Ridge 616 extends above surface 615 and is used to position additional sole structure elements in subsequent steps. Ridge 616 also compensates for the thickness of the shell 540′ portions bonded to surface 615. In particular, ridge 616 provides additional support in the central portion of the midsole 610 bottom surface that lack the presence of folded over shell 540′ portions.
In other embodiments that include upper shells with extensions used for double-lasting and/or to otherwise provide a shelf to support foam padding, numerous variations are possible. For example, fewer or more reinforcing panels can be used. The thicknesses, shapes, arrangements and other aspects of such reinforcing panels can be varied. Decorative features similar to those resulting from cutouts 509 and 510 can be achieved in additional ways. As but one example, a reinforcing panel can have reduced thickness in a certain area instead of a slot cut all the way through the panel. As another example, a small piece of material (e.g., in the shape of a logo) could be placed on an outer surface of a reinforcing panel so as to create an outline when skin material is later bonded to the reinforcing panel.
In the example construction shown in
This example upper construction includes another skin layer 830, an example of which is shown in
While building this upper structure may be similar to the processes and steps described above in conjunction with FIGS. 4A1 through 4K, various example features of this embodiment of the invention will be described in more detail below in conjunction with
While the next steps are shown separately, the various parts of the first skin layer 820, the second skin layer 830 (and any additional skin layers, when present), and/or the additional structures 840, 842, and 844 may be applied to the support base 850 in any desired order, e.g., depending on the desired aesthetics or other properties (as will be explained in more detail below).
The skin layers 820 and 830 and/or the other structures 840, 842, and 844 need not always be layered on the mesh layer 810 in the same order. For example, in some areas of the upper, skin layer 820 may be outside of skin layer 830, while in other areas of the upper, the skin layer 820 may be inside (beneath) skin layer 830. Changes in the layering order can be accomplished as the various skin layers 820 and 830 and/or other structures (e.g., structures 840, 842, and 844) are placed on the support base 850. Skin layers 820 and 830 may be layered in different manners as they are placed on the support base 850 (e.g., through their pin holes), e.g., by weaving portions of one skin layer 820 or 830 through the openings provided in the other skin layer. Also, when the skin layer is made of different parts (as shown in
1Reference No. 810 refers to the mesh layer 810 discussed above.
2Reference No. 800 refers to the substrate layer 800 discussed above.
3Reference No. 830 refers to the skin layer 830 discussed above.
4Reference No. 820 refers to the skin layer 820 discussed above.
5Reference No. 840 refers to the heel support element 840 discussed above.
6Reference No. 842 refers to the eye support elements 842 discussed above.
7Reference No. 844 refers to the toe support element 844 discussed above.
As evident from a comparison of various closely positioned points (e.g., points H, I, J, and K, or points P and Q), the layering of component parts within a single upper can easily be changed, e.g., to provide a somewhat different look at different areas, to better avoid snagging and delaminating a layer, to otherwise provide different properties to the upper, etc.
If desired, some color blending features may be provided in other ways as well. For example, even if only one skin layer is at least partially transparent or translucent (and colored), the overlapping of that skin layer on other skin layers or other colored areas of the upper will provide color blending and color change areas on the upper, at least in areas of the upper where the colored transparent or translucent skin layer overlays other layers of the shoe, including other layers that may or may not be at least partially transparent or translucent. Therefore, it is not a requirement of the invention that both skin layers have transparent or translucent qualities. In fact, a single skin area that is at least partially transparent or translucent can provide interesting aesthetics and color change areas on the upper, at least in some example constructions according to this invention.
The example upper construction of
In this illustrated example, as noted above, edges 856 and 858 are joined together on the medial side of the shoe. This medial side engagement alleviates stress in the tongue opening area of the shoe and provides a smoother construction in the tongue area (e.g., less binding, billowing, etc.) and a more aesthetically pleasing construction as compared to more symmetric upper blanks that are engaged together in the rear heel area of the shoe. The engagement at the rear heel area of the shoe tends to pull on the sides of the tongue opening and causes an uneven stress and appearance.
A bonded mesh composite panel used in an upper of a shoe such as that of
The above described fabrication processes for creating a bonded mesh composite panel also offer numerous advantages. Using the above-described processes, a relatively complex composite can be quickly formed in a simple manner using relatively simple equipment. Moreover, the above-described processes can also facilitate inexpensive changes to a composite panel design (for either functional or aesthetic reasons) without requiring substantial expensive re-tooling.
The foregoing description of embodiments has been presented for purposes of illustration and description. The foregoing description is not intended to be exhaustive or to limit embodiments of the present invention to the precise form disclosed, and modifications and variations are possible in light of the above teachings or may be acquired from practice of various embodiments. As but one example, techniques such as are described herein can be used to fabricate articles other than footwear uppers. The embodiments discussed herein were chosen and described in order to explain the principles and the nature of various embodiments and their practical application to enable one skilled in the art to utilize the present invention in various embodiments and with various modifications as are suited to the particular use contemplated. Any and all permutations of features from above-described embodiments are the within the scope of the invention.
This application is: (a) a continuation of U.S. patent application Ser. No. 13/467,499, filed May 9, 2012 and entitled “Shoe with Composite Upper and Method of Making the Same, which application is (b) a non-provisional application based on U.S. Provisional Patent Appln. No. 61/460,776, filed May 27, 2011 and entitled “Shoe with Composite Upper and Method of Making Same.” Each of U.S. patent application Ser. No. 13/467,499 and U.S. Provisional Patent Appln. No. 61/460,776 is entirely incorporated herein by reference. Additionally, aspects of the inventions described in this patent application may relate to or be useful with, at least in part, the technology described in: (a) U.S. patent application Ser. No. 13/029,502, titled “Shoe with Composite Upper and Foam Element and Method of Making Same” and filed Feb. 17, 2011, (b) U.S. patent application Ser. No. 12/603,494, titled “Composite Shoe Upper and Method of Making Same” and filed Oct. 21, 2009, and (c) U.S. patent application Ser. No. 12/603,498, also titled “Composite Shoe Upper and Method of Making Same” and filed Oct. 21, 2009. Each of these prior applications is entirely incorporated by reference herein.
| Number | Date | Country | |
|---|---|---|---|
| 61460776 | May 2011 | US |
| Number | Date | Country | |
|---|---|---|---|
| Parent | 13467499 | May 2012 | US |
| Child | 16863305 | US |