Patent Application
20110156324
The present disclosure relates to a sidewall and bottom electrode arrangement for an electrical smelting reactor and to a method for feeding such electrodes.
Aluminum metal is generally manufactured by two techniques: the traditional Hall method, where an electric current is passed between two electrodes to reduce alumina to aluminum metal; and the carbothermic method, where aluminum oxide is chemically reduced to aluminum via chemical reaction with carbon. The overall aluminum carbothermic reduction reaction:
Al2O3+3C→2Al+3CO (1)
takes place, or can be made to take place, via a series of chemical reactions, such as:
2Al2O3+9C→Al4C3+6CO (vapor) (2)
Al4C3+Al2O3→6Al+3CO (vapor) (3)
Al2O3+2C→Al2O (vapor)+2CO (vapor) (4)
Al2O3+4Al→3Al2O (vapor) (5)
Al→Al (vapor) (6)
Reaction (2), generally known as the slag producing step, often takes place at temperatures between 1875° C. and 2000° C. Reaction (3), generally known as the aluminum producing step, often takes place at temperatures above about 2050° C. Aluminum vapor species may be formed during reactions (2) and (3), although aluminum vapor species may be formed via reactions (4), (5), and (6).
The instant disclosure relates to improved carbothermic reactors having improved methods, systems and apparatus for feeding electrodes into the reactor.
In some electric smelting reactor processes it is sometimes of advantage or even necessary to use electrodes inserted through the reactor side walls or inserted through the reactor bottom and into molten material, such as liquid slag, metal, alloys or molten salts contained in the reactor. This is for instance the case in the method for production of aluminum by carbothermic reduction of alumina as described in U.S. Pat. No. 6,440,193. In the process described in this patent energy is supplied to a high temperature compartment of the reactor through electrodes inserted through the reactor side walls into a slag layer. In the method disclosed in U.S. Pat. No. 6,440,193 the high temperature compartment has a lower molten slag layer and an upper molten aluminum layer. It is not possible to use vertical electrodes inserted from above in this high temperature compartment as the upper layer of molten aluminum would short circuit the electrodes. Side walls electrodes or bottom electrodes penetrating into the slag layer must therefore be used.
Usually electrodes for electric smelting reactors are consumable carbon electrodes such as graphite or pre-baked carbon electrodes. When consumable electrodes are used, the electrodes must from time to time be fed into the reactor interior in order to compensate for the electrode consumption. The electrodes must penetrate through the reactor sidewall or bottom in a sealed way to prevent liquid material from escaping from the reactor and the electrode seal must also be able to allow feeding of the electrodes without liquid material penetrating through the electrode seal.
Some liquid materials, like slag, are very aggressive and will attack known refractory linings. Reactors operating at high temperatures therefore often have a freeze lining of solid slag for protection of the reactor wall and bottom. Reactors for production of aluminum by carbothermic reduction of alumina are therefore, at least in the area intended to be covered by molten slag, preferably made of cooled metal panels, particularly cooled copper panels, where cooling of the panels is regulated or adjusted in order to provide and maintain a protective layer of frozen slag on the inside of the cooled panels.
It has been found that it is very difficult to insert electrodes through reactor sidewalls and bottoms both for sidewalls and bottoms made from cooled panels and from conventional sidewalls and bottoms made from refractory materials to create and maintain a reliable sealing between the electrode and the cooled panels and to be able to feed the electrodes without the risk for leakage of slag through the electrode opening.
According to one aspect, the present disclosure relates to an electrode arrangement for sidewall and/or electrodes for a metallurgical reactor intended to contain liquid material where at least one consumable electrode is inserted through the sidewall or the bottom of the reactor through an opening in the sidewall or bottom of the reactor, which electrode arrangement is characterized in that it comprises a contact clamp for conducting operating current to the electrode, said current clamp being arranged about the electrode and having internal channels for circulation of a cooling medium and having an inwardly tapered section; an electric isolation ring inserted into the opening in the sidewall or bottom of the reactor and the surface of the electrode to create a sealing between the surface of the electrode and the sidewall or bottom of the reactor; and means for pressing the current clamp against the isolation ring.
According to one embodiment of the present disclosure the front part of the current clamp extends into an opening between the surface of the electrode and the isolation ring.
According to another preferred embodiment the means for pressing the current clamp against the isolation ring comprises a steel ring arranged about the electrode and affixed to the outside of the sidewall or the bottom of the reactor, said steel ring having an outwardly tapered opening and where the current clamp has a correspondingly inwardly tapered outer surface which is pressed into the opening in the steel ring.
According to yet another preferred embodiment the sidewall and/or the bottom of the reactor consist of cooled metal panels where the steel ring is affixed to the cooled metal panel.
The electrode arrangement according to the present disclosure may provide a safe sealing preventing liquid material in the reactor to penetrate through the electrode sealing.
When the sidewall and/or bottom of the reactor consists of cooled metal panels, a layer of frozen layer of the material in the reactor will, during operation of the reactor, form on the cooled panels and this frozen layer of material will extend to the side of the isolation ring facing the interior of the reactor and to the surface of the electrode thus safeguarding the electrode sealing.
The sidewall electrode of the present disclosure can either be horizontal or having an angle to the horizontal. The bottom electrode of the present disclosure is preferably vertical.
The present disclosure further relates to a method for feeding of a consumable electrode arranged in the sidewall and/or bottom of a metallurgical reactor containing liquid material, where the electrode is fed by electrode feeding cylinders connected to the electrode, which method is characterized in that the feeding of the electrode is done based on temperature increase in or close to the sidewall or bottom where the electrode is inserted into the sidewall or bottom of the reactor.
According to a preferred embodiment of the method of the present disclosure where the sidewall and/or the bottom of the reactor is made from cooled metal panels and where a frozen layer of material is formed on the inside of the cooled metal panels, the feeding of the electrode is based on exerting a pressure on the electrode feeding cylinders to break the frozen slag layer when the tip of the electrode has moved towards the sidewall and/or the bottom to such an extent that the frozen material layer has partly melted away.
In one approach, the disclosure may be characterized as a metallurgical reactor comprising:
In one embodiment, a front part of the current clamp extends into an opening between the surface of the electrode and the isolation ring. In one embodiment, the reactor includes a steel ring arranged about the electrode and affixed to the outside of the sidewall or the bottom of the reactor, where the steel ring has an first mating surface, where the current clamp has a corresponding second mating surface, and where, when the second mating surface of the current clamp engages the first mating surface of the steel ring, that a compressive force is realized on at least the front part of the current clamp. In one embodiment at least one of the sidewall and the bottom of the reactor comprise at least one cooled metal panel. In one embodiment, the steel ring is affixed to at least one cooled metal panel.
On
A current clamp 5 made from copper or a copper alloy and having internal channels for circulation of a cooling medium is arranged about the electrode 2. The current clamp 5 has an inwardly tapered part and is pressed into the opening 3 between the electrode 2 and the isolation ring 4 to seal the sidewall from leaking the molten material intended to be contained in the reactor.
Current conductors 6 for conducting operating current to the electrode 2 from a current source (not shown) are connected to the current clamp 5. The current conductors 6 are in the form of pipes for supply of cooling medium to the current clamp 5.
The current clamp 5 is pressed into the opening 3 between the isolation ring 4 and the electrode 2 in the following way: A steel ring 7 having an outwardly tapered inner surface is affixed to the panel 1 by means of bolts 8. The bolts are isolated from the panel 1. The current clamp 5 is forced against the electrode 2 and the steel ring 7 by means of a second steel ring 9 affixed to the panel 1 by means of bolts 10. An electric isolation ring ills inserted between the current clamp 5 and the second steel ring 9. By tightening the bolts 10, the current clamp 5 is pressed against the electrode 2 and the steel ring 7 with a sufficient amount of preset sealing force to seal the sidewall, and to provide sufficient electrical contact pressure between the electrode 2 and the current clamp 5.
In order to feed the consumable electrode 2, electrode feeding cylinders 13, 14 are affixed to the panel 1 by means of bolts 15 or the like. The electrode feeding cylinders 13, 14 are connected to the electrode 2 by means of an electrode clamping ring 16, which can be clamped against an outer surface of the electrode 2. The electrode clamping ring 16 can be a conventional hydraulic cylinder or a spring packet. The electrode clamping ring 16 is affixed to the electrode feeding cylinders 13, 14 by means of bolt and nut connections.
More particularly, and with reference now to
In
First, the current clamp 5 does not extend into the opening 3 in the copper panel 1. In the embodiment shown in
Secondly, the electrode feeding cylinders 13, 14 are connected to a device 30, which is adapted to push the rear of the electrode into the reactor. The device 30 includes a nipple 31 having threads 32 screwed into a threaded recess in the back end of the electrode 2. The nipple 31 shown in
Even though the present disclosure has been described in connection with reactor sidewall consisting of cooled metal panels, the same will apply to reactor sidewalls and bottoms with conventional refractory linings.
In operation of the described reactor, there will be created, due to the cooling of the panels 1, a frozen slag layer on the interior side of the cooled panels 1 (i.e., the side of the panels facing the interior of the reactor). This frozen slag layer will, for the embodiment shown in
The electrode 2 is consumed during operation of the reactor and the electrode tip 12 will slowly move towards the reactor sidewall. Therefore the electrode 2 is fed into the reactor from time to time as the electrode tip 12 moves closer to the cooled panel 1. Since the temperature at the electrode tip 12 is at a high temperature, the temperature close to the electrode sealing will increase. In some embodiments, the heat at the electrode tip 12 of the electrode may partly melt away the frozen slag layer proximal the electrode 2. In one embodiment, the feeding of the electrode 2 is based on this temperature increase. In a related embodiment, the feeding of the electrode 2 is completed by exerting a pressure on the electrode feeding cylinders 13, 14 that will be sufficient to break the remaining frozen layer of slag whereby the electrode 2 is fed into the reactor (e.g., at a predetermined length). After having fed the electrode, the pressure on the electrode clamping ring 16 is released, and the electrode feeding cylinders 13,14 and the electrode clamping ring 16 are retracted and pressurized and ready for the next feeding cycle of the electrode 2. Since the electrode tip 12 through the feeding of the electrode has been moved further away from the reactor wall, a new layer of frozen slag will be reestablished between the surface of the electrode 2 and the cooled panels 1. In this way a safe feeding of the electrode 2 can be performed without leakage of molten slag.
| Filing Document | Filing Date | Country | Kind | 371c Date |
|---|---|---|---|---|
| PCT/US08/76550 | 9/16/2008 | WO | 00 | 3/4/2011 |