Claims
- 1. A method for the manufacture of silica catalyst supports comprising the steps of mixing precipitated amorphous silica powder having an average particle size in the range consisting essentially of about 10 to 50 millimicrons with a binder for said silica powder; forming the mixture of silica powder and binder into macrosized bodies suitable for use as a catalyst support; and calcining the said bodies of silica powder and binder.
- 2. The method of claim 1 wherein the said mixture of silica powder and binder is comprised of about 70 to 99 weight percent silica powder to 1 to 30 weight percent of binder based on the total of these components.
- 3. The method of claim 1 wherein the binder is comprised of water-soluble starch.
- 4. The method of claim 1 wherein the binder used is comprised of polyvinyl alcohol, methyl cellulose, or colloidal silica.
- 5. The method of claim 1 wherein the means for forming the mixture is extrusion.
- 6. The method of claim 4 wherein a major portion of the binder is colloidal silica.
- 7. The method of claim 1 wherein the means for forming the mixture of silica powder and binder comprises tableting.
- 8. The method of claim 7 wherein a lubricating medium is added to the mixture of silica powder and binder.
- 9. The method of claim 1 wherein the calcining temperatures are in the range about 400.degree. F. to 1600.degree. F. for a period of from about 2 to about 16 hours.
- 10. The method of claim 1 wherein the calcining temperatures are in the range of about 950.degree. F. to 1300.degree. F.
- 11. The method of claim 1 wherein the water content of the macrosized bodies is reduced to less than about 5 weight percent prior to calcining.
- 12. The product of the method of claim 1.
- 13. A calcined catalyst support comprised predominantly of silica and having about 96 or more weight percent silica, a surface area in the range of about 30 to 125 square meters per gram; an average pore diameter of about 100 to about 5000 Angstroms, and a bulk density in the range of about 0.3 to 0.6 gram per cubic centimeter, said support being made by calcining a composite comprised predominantly of precipitated amorphous silica powder having an average particle size consisting essentially of about 10 to about 50 millimicrons.
- 14. The catalytic support of claim 13 wherein the silica content is in excess of about 98 weight percent.
Parent Case Info
This is a continuation of application Ser. No. 603,283 filed Apr. 23, 1984, now abandoned, which is a continuation of application Ser. No. 383,616 filed June 1, 1982, now abandoned, which is a continuation of application Ser. No. 082,530 filed Oct. 9, 1979, now abandoned.
US Referenced Citations (10)
Non-Patent Literature Citations (1)
Entry |
Chem. Abst: 84: 124050v, Nakamura. |
Continuations (3)
|
Number |
Date |
Country |
Parent |
603283 |
Apr 1984 |
|
Parent |
383616 |
Jun 1982 |
|
Parent |
82530 |
Oct 1979 |
|