Claims
- 1. Method for preparing attrition resistant molecular sieve agglomerates comprising:
- (a) forming an initial molecular sieve agglomerate comprising a zeolite and a binder comprising kaolin clay;
- (b) heating the initial agglomerate at a temperature of from about 550.degree.-650.degree. C. and sufficient to set the binder and form a calcined agglomerate;
- (c) contacting said calcined agglomerate with an alkali hydroxide solution comprising from about 5 to about 50% by weight of sodium hydroxide at conditions effective to convert the kaolin binder to Zeolite A to form a converted agglomerate;
- (d) contacting the converted agglomerate with an aqueous alkali metal silicate solution containing from about 1 to 10 wt. % alkali metal oxide and from about 2 to 20 wt. % silicon dioxide to form a treated agglomerate; and
- (e) drying the treated agglomerate at a temperature of from about ambient temperature to 650.degree. C. and sufficient to remove water therefrom.
- 2. Method of claim 1 wherein said zeolite is the potassium-exchanged form of Zeolite A having uniform pore diameters of about 3 Angstroms.
- 3. Method of claim 1 wherein said zeolite is the sodium-exchanged form of Zeolite A having uniform pore diameters of about 4 Angstroms.
- 4. Method of claim 1 wherein the binder comprises from about 5 percent to about 40 percent by weight of said initial agglomerate.
- 5. Method of claim 1 wherein the alkali metal oxide is potassium oxide.
- 6. Method of claim 1 wherein said drying is conducted by heating in air to a temperature of from about 200.degree. C. to 650.degree. C.
- 7. Method of claim 1 wherein the alkali hydroxide solution comprises from about 5 to about 10 percent by weight of sodium hydroxide.
- 8. Method of claim 1 wherein said contacting is performed at a temperature of from about 40.degree. C. to about 110.degree. C.
- 9. Method of claim 8 wherein said contacting is performed at a temperature of from about 90.degree. C. to about 95.degree. C.
- 10. Method of claim 1 which further comprises contacting said converted agglomerate with a sufficient quantity of water to have a pH of between about 9 to about 12 prior to said contacting with the alkali metal silicate solution.
- 11. Method of claim 10 wherein the pH of the converted agglomerate is about 10.
CROSS REFERENCE TO RELATED APPLICATIONS
This application is a divisional application of prior copending application U.S. Ser. No. 310,121, filed Feb. 10, 1989, now allowed the contents of which are incorporated herein by reference.
US Referenced Citations (8)
Foreign Referenced Citations (1)
Number |
Date |
Country |
972833 |
Oct 1964 |
GBX |
Divisions (1)
|
Number |
Date |
Country |
Parent |
310121 |
Feb 1989 |
|