Claims
- 1. A method for preparing an article comprising the steps of:providing a substrate comprising silicon; and applying a calcium containing gaseous species of Si formation inhibiting barrier layer to the substrate wherein the barrier layer inhibits the formation of gaseous species of Si when the article is exposed to a high temperature, aqueous environment.
- 2. A method according to claim 1 wherein the coefficient of thermal expansion of the barrier layer is within ±3.0 ppm/° C. the coefficient of thermal expansion of the substrate.
- 3. A method according to claim 1 wherein the coefficient of thermal expansion of the barrier layer is within ±0.5 ppm/° C. the coefficient of thermal expansion of the substrate.
- 4. A method according to claim 1 further including the step of grit blasting the substrate prior to applying the barrier layer.
- 5. A method according to claim 4 including grit blast with alumina particles having a particle size of ≦30 microns.
- 6. A method according to claim 5 including grit blasting at a velocity of between about 150/m/sec to 200/m/sec.
- 7. A method according to claim 1 including applying the barrier layer by thermal spraying.
- 8. A method according to claim 1 including the step of preoxidizing the substrate to form a layer of SiO2 prior to applying the barrier layer.
- 9. A method according to claim 8 wherein the preoxidizing comprises heating the substrate at a temperature of between about 800° C. to 2000° C. for about 15 minutes to 100 hours.
- 10. A method according to claim 11 including the step of, after applying the barrier layer, heat treating the article.
- 11. A method according to claim 1 including thermal spraying at a temperature of between about 800° C. to 1200° C.
- 12. A method according to claim 1 wherein the coefficient of thermal expansion of the barrier layer is within ±3.0 ppm/° C. the coefficient of thermal expansion of the substrate.
- 13. A method according to claim 1 wherein the coefficient of thermal expansion of the barrier layer is within ±0.5 ppm/° C. the coefficient of thermal expansion of the substrate.
- 14. A method according to claim 1 wherein the barrier layer comprises greater than about 20% by weight CaO, greater than about 38% by weight Al2O3 and greater than about 30% by weight SiO2.
- 15. A method according to claim 1 wherein the barrier layer comprises about 24% by weight CaO, about 40% by weight Al2O3 and about 36% by weight SiO2.
- 16. A method according to claim 1 wherein the barrier layer is non-stoichiometric calcium aluminosilicate.
- 17. A method according to claim 14 including heat treating said article over time to a temperature which allows for crystallization of the calcium aluminosilicate without swelling and/or the formation of pores by the barrier layer.
- 18. A method according to claim 17 including heating the article form room temperature to a temperature of between about 1275° C. to about 1300° C. over a time period of at least 68 hours.
- 19. A method according to claim 18 wherein the article is heated in a stepwise manner at a heat rate of between about 50° C./min to about 3° C./min and held at at least one intermediate temperature.
- 20. A method according to claim 19 wherein said article is heat treated as follows:a) room temperature to 700° C. @ 10° C./min, hold 4 hrs.; b) 700° C. to 800° C. @ 10° C./min, hold 8 hrs.; c) 800° C. to 900° C. @ 10° C./min, hold 16 hrs.; d) 900° C. to 1000° C. @ 10° C./min, hold 16 hrs.; e) 1000° C. to 1100° C. @ 10° C./min, hold 8 hrs.; f) 1100° C. to 1200° C. @ 10° C./min, hold 8 hrs.; g) 1200° C. to 1225° C. @ 5° C./min, hold 2 hrs.; h) 1225° C. to 1250° C. @ 5° C./min, hold 2 hrs.; i) 1250° C. to 1275° C. @ 5° C./min, hold 2 hrs.; j) 1275° C. to 3000° C. @ 5° C./min, hold 2 hrs.; and k) furnace cool to room temperature.
Parent Case Info
This is a Division, of application Ser. No. 09/292,350 filed Apr. 15, 1999.
Government Interests
This invention was made with government support under Contract No. NAS3-26385 awarded by NASA. The government may have certain rights in the invention.