Silicone corrosion protection coating having extended bath life

Description

The present invention relates to improved curable silicone coating compositions. More particularly, the present invention relates to such coating compositions which have an extended bath life and provide corrosion resistance to metal surfaces when cured thereon.
BACKGROUND OF THE INVENTION
In U.S. Pat. No. 4,322,518, assigned to the assignee of the present invention and hereby incorporated by reference, Blizzard discloses silicone coating compositions which comprise a solventless liquid copolymeric organopolysiloxane and a diorganopolysiloxane fluid or gum containing vinyl and/or hydroxyl radicals. When cured on various substrates, these silicone compositions provide release coatings having controllable release forces for adhesives adhered thereto.
Blizzard and Swihart, in U.S. Pat. No. 4,537,829, assigned to the assignee of the present invention, teach compositions similar to those described by Blizzard, cited supra, which further comprise an organosilicon resin consisting essentially of dimethylvinylsiloxy units, trimethylsiloxy units and SiO.sub.4/2 units and a hydrosilylation catalyst. These compositions, when cured, provided improved resistance to fuels and a high degree of corrosion protection to metal substrates.
In U.S. Pat. No. 4,701,380, assigned to the assignee of the present invention and hereby incorporated by reference, Narula et al. show that compositions similar to those taught by Blizzard, based on a hydroxy-functional diorganopolysiloxane, can be cured at room temperature to provide a strongly adhering corrosion protective coating when modified with a minor amount of an adhesion promoter selected from a specific group of functional organosilanes. In order to be of commercial value, all of the above mentioned coating compositions are generally applied from an organic solvent solution and they require the further addition of a catalyst so that the time to cure the coating is not excessive.
Although the coating compositions disclosed by Narula et al., cited supra, do provide excellent corrosion protection to ferrous metals when cured thereon, these coating systems have been found to have some inherent drawbacks. Thus, this patent suggests application of the compositions to substrates by a spray method, this coating technique being well appreciated in the art for its relative speed and efficiency. And, even though airless sprayers can handle higher viscosity compositions, commercial applicators strongly prefer to have the added flexibility of using conventional siphon cup spray equipment, wherein viscosity must remain below about 1,000 cP. From a practical standpoint, this means that the above mentioned silicone coating compositions containing a diorganopolysiloxane gum must include a high proportion of organic solvents to have the desired low viscosity. Such a coating composition, further containing a cure catalyst, can be effectively sprayed by conventional equipment but this advantage is overshadowed by its high total volatile organic compounds (VOC) content. The skilled artisan will appreciate the current efforts to reduce total VOC in coating compositions of all types as there has been considerable legislation in the United States toward this end, particularly in the state of California. Furthermore, economic considerations, such as a reduction in coating composition volume and an increased film build per spray pass, provide a strong motivation to use high solids systems, the term "high solids" denoting herein a non-volatile content of 50 to about 100 weight percent or having a total VOC of .ltoreq.420 grams/liter.
An alternative way to achieve the desired low viscosity in the compositions disclosed by Narula et al. is to employ a diorganopolysiloxane having a low molecular weight (i.e., a low viscosity fluid). While a catalyzed high solids coating composition of this type can be sprayed by conventional equipment soon after it is prepared, its viscosity soon climbs out of the preferred range. This short "bath life" (i.e., the maximum time, after being catalyzed, that a batch of the coating composition can be satisfactorily sprayed) severely restricts the batch size which may be used and therefore results in inefficiencies associated with mixing extra batches of the composition and cleaning spray equipment between batches. While not wishing to be bound by any particular theory or mechanism, it is believed that the reduced bath life of such compositions is in large part due to the inherently higher functionality (reactivity) of the low molecular weight diorganopolysiloxane fluids relative to the corresponding gums. It is further believed that the functionality of the diorganopolysiloxane fluid can also react with the functional organosilane adhesion promoter in the presence of moisture. Such a reaction could explain the observed formation of a "skin" at the surface of catalyzed coating compositions prepared according to the disclosure of Narula et al. Although surface skin which is primarily due to solvent evaporation can generally be re-dissolved by mixing it back into the coating composition, it has been found that this is not always possible in the case of sprayable high solids coating systems of Narula et al. When this skin can not be re-dispersed, it tends to clog filters and nozzles in the spray equipment and can result in poor surface quality of the coating. Again, not wishing to be bound by a particular theory, it is believed that the apparently gelled skin results from the interaction of the hydroxy-functional diorganopolysiloxane with the functional organosilane adhesion promoter in the presence of surface moisture.
SUMMARY OF THE INVENTION
It has now been found that silicone compositions prepared according to the disclosure of and Narula et al., cited supra, can be modified by the inclusion of a bath life extender to provide high solids systems which do not exhibit the above mentioned disadvantages and are sprayable in conventional siphon cup spray equipment. Moreover, these modified systems retain the advantages of the compositions of Narula et al. in that they also provide excellent corrosion protection to metals when cured on the surfaces thereof. Additionally, the adhesion of the coatings to a substrate is not compromised, regardless of whether they are cured at room temperature or at elevated temperatures. These advantages are realized when the above mentioned bath life extender is a combination of a trialkyl orthoformate and an organic titanate. That an organic titanate can actually increase the bath life of these compositions is quite surprising since these titanates are generally considered to act as condensation catalysts for such silicone systems. The present invention therefore relates to a curable composition comprising:
(I) from about 10 to about 90 parts by weight of a liquid organopolysiloxane copolymer, prepared by a method comprising (A) forming a homogeneous mixture having an acid number greater than zero and consisting essentially of (a) an organic solvent solution of a resinous copolymeric siloxane containing silicon-bonded hydroxyl radicals and consisting essentially of R.sub.3 SiO.sub.1/2 siloxane units and SiO.sub.4/2 siloxane units wherein the ratio of said R.sub.3 SiO.sub.1/2 units to said SiO.sub.4/2 units has a value of 0.6:1 to 0.9:1 and each R denotes, independently, a monovalent hydrocarbon radical and (b) a liquid organohydrogenpolysiloxane wherein each organic radical is, independently, a monovalent hydrocarbon radical, there being an average of at least one silicon-bonded hydrogen radical per molecule of said organohydrogenpolysiloxane, and (B) heating said homogeneous mixture to remove substantially all of said organic solvent therefrom;
(II) from about 90 to about 10 parts by weight of a hydroxy-functional diorganopolysiloxane having the average formula (HO)R'".sub.2 SiO(R'".sub.2 SiO).sub.c SiR'".sub.2 (OH) wherein R'" is a group selected from alkyl, cycloalkyl, haloalkyl, aromatic or haloaromatic radicals and c has a value sufficient to provide a viscosity of about 1 to about 500 Poise at 25.degree. C. for said diorganopolysiloxane;
(III) from about 1 to about 10 parts by weight, per 100 parts of said component (I) plus component (II), of at least one organosilane having the formula QSi(OR"").sub.3 wherein the group Q is selected from vinyl, 3-glycidoxypropyl, 3-methacryloxypropyl or 3-(N-styrylmethyl-2-aminoethylamino)-propyl hydrochloride groups and R"" is selected from alkyl groups having 1 to 4 carbon atoms, alkoxyalkyl groups having a total of up to 5 carbon atoms or an acetyl group;
(IV) from about 1 to about 10 parts by weight, per 100 parts of said component (I) plus component (II), of a trialkyl orthoformate in which the alkyl groups contain 1-3 carbon atoms;
(V) from about 4 to about 10 parts by weight, per 100 parts of said component (I) plus component (II), of an organic titanate selected from the group consisting of Ti(OR'"").sub.4 and (AcAc)Ti(OR'"").sub.2, in which R'"" is independently selected from alkyl radicals having 3 to 8 carbon atoms and AcAc denotes an acetylacetonate group; and
(VI) a sufficient amount of a condensation catalyst to cure said composition.
This invention further relates to a similar composition to that described above, wherein said component (I) is prepared by simply mixing said components (a) and (b) without subsequent heating and removal of solvent therefrom.
DETAILED DESCRIPTION OF THE INVENTION
Component (I) of the compositions of this invention is a liquid copolymeric organopolysiloxane. It may be prepared by reacting (a) a resinous copolymeric siloxane with (b) a liquid organohydrogenpolysiloxane. Alternatively, component (I) may be prepared by simply blending reactants (a) and (b) and using this mixture directly in the compositions of the present invention.
Component (a) is an organic solvent solution of a resinous copolymeric siloxane consisting essentially of R.sub.3 SiO.sub.1/2 units and SiO.sub.4/2 units which contains from 0.6 to 0.9 R.sub.3 SiO.sub.1/2 units for every SiO.sub.4/2 unit. Each R denotes a monovalent hydrocarbon radical; such as an alkyl radical, such as methyl, ethyl, isopropyl, butyl and hexyl; an alkenyl radical, such as vinyl and allyl; an aryl radical, such as phenyl, tolyl and xylyl; an arylalkyl radical, such as beta-phenylethyl and beta-phenylpropyl; and a cycloaliphatic radical, such as cyclopentyl and cyclohexyl. Preferably all R radicals in component (a) are lower alkyl radicals, although a minor portion of them can be replaced with other monovalent hydrocarbon radicals such as vinyl radical and/or a phenyl radical, to provide additional properties for the resinous copolymer such as the reactivity attendant therewith.
In a preferred curable coating composition of this invention, the resinous copolymeric siloxane portion of component (a) consists essentially of (CH.sub.3).sub.3 SiO.sub.1/2 siloxane units and SiO.sub.4/2 siloxane units in the number ratio of about 0.75:1, respectively.
Component (b) that is used to prepare the liquid copolymeric organopolysiloxane (I) is any liquid organohydrogenpolysiloxane containing an average of at least one silicon-bonded hydrogen radical per molecule and can have a linear, cyclic or branched structure or combinations thereof. An organohydrogenpolysiloxane having the formula
Me.sub.3 SiO[(Me)HSiO].sub.b SiMe.sub.3
wherein Me hereinafter denotes a methyl radical and b has an average value of from 30 to 70 is a highly preferred component (b). It is particularly preferred that b is about 35.
Component (I) preferably consists essentially of a devolatilized reaction product of components (a) and (b). Alternately, it has been found that component (I) may also consist essentially of a blend of components (a) and (b) formed at room temperature wherein the solvent introduced by component (a) is retained when forming the curable silicone compositions of this invention. On a solids basis, the organohydrogenpolysiloxane (i.e.. component b) content of component (I) varies between about 10 and 90 weight percent of the total blend or reaction product. Preferably, the organohydrogenpolysiloxane content of component (I) varies between about 40 and 60 weight percent on a solids basis. Herein, the term "solids basis" denotes the non-volatile content of any composition or component.
Further details dealing with the preparation of component (I) by this method, as well as descriptions of components (a) and (b), may be found in U.S. Pat. No. 4,322,518 to Blizzard, cited supra.
When component (I) is a room temperature blend of components (a) and (b), its preparation simply consists of forming a homogeneous solution between these ingredients. As in the case of the reaction product, described above, an acid number greater than zero is required and an acid number between about 0.1 and 1, on a solids basis, is preferred.
Component (II) of this invention is a polydiorganosiloxane fluid having the general formula
(HO)R'".sub.2 SiO(R'"2SiO).sub.c SiR'".sub.2 (OH)
wherein R'" denotes a monovalent hydrocarbon radical selected from the group of R radicals indicated above for component (I). For the purpose of this invention, at least 95 percent of the R'" radicals are methyl (Me) and it is preferred that all R'" radicals are methyl. Herein, c has a value which is sufficient to provide a viscosity for component (II) of about 1 to 500 P (Poise) at 25.degree. C. Preferably, the viscosity of component (II) is about 150 P at 25.degree. C. Polydiorganosiloxanes which are suitable for use as component (II) are well known in the art and many of these fluids are available commercially. Therefore, further description of methods for the preparation of such materials is not detailed herein.
Component (III) of the present invention is an organosilane having the general formula QSi(OR"").sub.3. The group Q is selected from CH.sub.2 .dbd.CH--, ##STR1## (i.e., 3-glycidoxypropyl), CH.sub.2 .dbd.C(CH.sub.3)C(O)OCH.sub.2 CH.sub.2 CH.sub.2 --(i.e., 3-methacryloxypropyl) or HCl.CH.sub.2 .dbd.CH(C.sub.6 H.sub.4)CH.sub.2 NHCH.sub.2 CH.sub.2 NH(CH.sub.2).sub.3 --(i.e., 3-(N-styrylmethyl-2-aminoethylamino)-propyl hydrochloride). In the above formula, R"" may be an alkyl group having 1 to 4 carbon atoms, an alkoxyalkyl group having a total of up to 5 carbon atoms or an acetyl group. Combinations of different organosilanes are also contemplated for use as component (III) of this invention.
Specific examples of component (III) suitable for use in the present invention are 3-glycidoxypropyltrimethoxysilane, 3-(N-styrylmethyl-2-aminoethylamino)-propyltrimethoxysilane hydrochloride, 3-methacryloxypropyltrimethoxysilane, vinyltrimethoxysilane, vinyltriacetoxysilane and vinyltris(2-methoxyethoxy)silane.
It is preferred that the Q group of component (III) is selected from vinyl or 3-glycidoxypropyl and R"" is selected from methyl or acetyl. Particularly preferred organosilanes are 3-glycidoxypropyltrimethoxysilane and mixtures of 3-glycidoxypropyltrimethoxysilane with vinyltriacetoxysilane, said mixtures being preferably heated for 1-4 hours at about 150.degree. C. and containing approximately equal parts by weight of each silane.
The organosilanes of component (III) are well known in the art and many of them are commercially available, hence further description of methods of preparation will not be addressed herein.
In order to prepare the silicone coating compositions having an extended bath life according to the present invention, from 10 to 90 parts by weight of component (I) are thoroughly mixed with from 90 to 10 parts by weight of component (II), a weight ratio of (I) to (II) of about 45:55 being preferred. With each 100 parts by weight of this mixture of (I) and (II), there is thoroughly mixed from about 1 to about 10 parts by weight, of above described component (III); from about 1 to about 10 parts by weight of (IV) a trialkyl orthoformate; from about 4 to about 10 parts by weight of (V) an organic titanate; and a sufficient amount of (VI) a condensation catalyst to cure said composition. The above proportions are based on a 100% solids system, although various organic solvents which do not contain active hydrogen groups are preferably added to adjust the solids content, and therefore the viscosity and sprayability, of the resulting coating composition. Suitable solvents include methyl isobutyl ketone, methyl amyl ketone, various aliphatic solvents, isobutyl acetate, mineral spirits, various aromatic solvents, such as toluene and xylene, and 1,1,1-trichloroethane.
Component (IV) is selected from trialkyl orthoformates in which the alkyl groups contain 1-3 carbon atoms and is preferably triethyl orthoformate.
Component (V) is an organic titanate selected from the group consisting of Ti(OR'"").sub.4 and (AcAc)Ti(OR'"").sub.2, in which R'"" is independently selected from alkyl radicals having 3 to 8 carbon atoms and AcAc denotes an acetylacetonate group. Preferably, component (V) is tetra(n-butyl) titanate.
These two components (i.e., IV and V) are believed to interact in the compositions of the present invention so as to increase their bath life.
The condensation catalysts (i.e., component VI) suitable for use in this invention include any of the compounds which are known to facilitate the reactions between SiOH groups and between SiOH and SiH groups. For example, the catalysts contemplated may be salts of heavy metals, such as dibutyltin diacetate and stannous octoate, preferably dibutyltin diacetate. The amount of the catalyst needed to effectively cure a given composition will readily be determined by the skilled artisan through routine experimentation. Typically, this component is employed at a level of about 0.1 to about 5 parts by weight, on a solids basis, for each 100 parts by weight of said components (I) plus (II).
Although all of the above named components may be mixed just before application of the resulting coating composition to a substrate, it is preferred that they are separately packaged to provide a storage stable system. It is thus preferred that components (I) and (II) are mixed to form a first part (part A), components (III), (IV) and (VI) are mixed to form a second part (part B) and component (V) forms a third part (part C). These parts are stored separately until ready for use in a given coating operation, whereupon they are blended to form a homogeneous coating composition according to the present invention.
The compositions of this invention can further comprise typical silicone adjuvants such as catalysts, fillers, pigments, dyes, rheology control additives, solvents and cure-control additives, if desired. When solvents are used, it is preferred to add them to part B and/or part C.
The compositions of the present invention find particular utility as coatings for metal substrates, as described in the patent to Narula et al., cited supra. When applied as 100% solids or from solution and cured on such substrates as iron, steel, aluminum, brass or copper, coatings comprising these compositions provide excellent corrosion protection to the metal surfaces. This is particularly true for the case of ferrous metals exposed to moisture and salt. Moreover, the compositions of the present invention can be cured at room temperature and still form strongly adhering coatings on such substrates.
The coating compositions of this invention may be applied to metal surfaces by any of the methods commonly practiced in the coating arts. They find particular utility in conventional spray applications where the extended bath life of the systems typically allows a catalyzed batch to be processed during an entire eight hour work shift.
After coating of the metal substrates with the compositions of this invention, the coatings, which generally should be at least about 1.0 mil in thickness, are cured. This may be done at room temperature (i.e., about 25.degree. C.) or may be carried out at an elevated temperature ranging from 50.degree. to 250.degree. C.

EXAMPLES
The following examples are presented to further illustrate the compositionsof this invention, but are not to be construed as limiting the invention, which is delineated in the appended claims. All parts and percentages in the examples are on a weight basis unless indicated to the contrary.
The following materials were employed in the preparation of the illustrative compositions.
COPOLYMER 1--A liquid organopolysiloxane copolymer was prepared by the methods of U.S. Pat. No. 4,322,518, cited supra. A 70% xylene solution of a siloxane resin copolymer consisting essentially of (CH.sub.3).sub.3 SiO.sub.1/2 units and SiO.sub.2 units in a molar ratio of approximately 0.75:1, was mixed at a level of 68 parts with 32 parts of a liquid organohydrogenpolysiloxane having the average formula ##STR2##wherein Me hereinafter denotes a methyl radical. Using a nitrogen purge, xylene solvent was removed as this mixture was heated under a vacuum of about 100 mm Hg at 150.degree. C. for 2 hours to yield a product containing a 60:40 weight ratio of the siloxane resin copolymer to the organohydrogenpolysiloxane.
COPOLYMER 2--A liquid organopolysiloxane copolymer similar to COPOLYMER 1 but having a 50:50 weight ratio of the siloxane resin copolymer to the organohydrogenpolysiloxane.
FLUID 1--A hydroxy-terminated polydimethylsiloxane having a viscosity of about 2,000 cP at 25.degree. C.
FLUID 2--A hydroxy-terminated polydimethylsiloxane having a viscosity of about 15,000 cP at 25.degree. C.
FLUID 3--A liquid organohydrogenpolysiloxane having the average formula ##STR3##
SILANE 1--A silane blend consisting of a 50:50 mixture of vinyltriacetoxysilane and 3-glycidoxypropyltrimethoxysilane which had beenheated for four hours at about 145.degree. C.
PIGMENT--A homogeneous dispersion of 35% titanium dioxide, 5% black iron oxide in 60% of said FLUID 2.
METHYL RESIN--A 70% xylene solution of a siloxane resin copolymer consisting essentially of (CH.sub.3).sub.3 SiO.sub.1/2 units and SiO.sub.2units in a molar ratio of approximately 0.75:1. PROPYL RESIN--A silicone resin solution consisting essentially of 10% of a hydrolyzate of propyltrichlorosilane in toluene.
IBA--Isobutyl acetate.
MIBK--Methyl isobutyl ketone (4-Methyl-2-pentanone).
MAK--Methyl amyl ketone (2-Heptanone). Isopar G.RTM.--Isoparaffinic solventobtained from Exxon Co., Houston, Tex. Isopar L.RTM.--Isoparaffinic solventobtained from Exxon Co. Kwik-Dri.RTM.--Aliphatic hydrocarbon solvent blend obtained from Ashland Chemical Co., Columbus, Ohio.
TEOF--Triethyl orthoformate (1,1,1'-[Methylidynetris(oxy)]tris[ethane]).
DBTDA--Dibutyltin diacetate catalyst (diacetoxydibutyltin). Bentone SD-2.RTM.--Organic derivative of a montmorillonite clay obtained from Rheox, Inc., Hightstown, N.J.
TBT--Tetra(n-butyl) titanate (Titanium [IV] butoxide).
EXAMPLES 1-4
The coating compositions shown in Table 1 were prepared according to the methods of U.S. Pat. No. 4,701,380, cited supra, wherein heptane solvent was used to adjust the total solids content of each formulation to 65%. Inthe comparative examples, the ingredients were mixed in the order presented. In Example 1, a blend of the first two ingredients (i.e., FLUID2 and COPOLYMER 1) was mixed with a blend of the remaining ingredients.
TABLE 1__________________________________________________________________________ (Comparative) (Comparative) (Comparative)Component Example 1 Example 2 Example 3 Example 4__________________________________________________________________________FLUID 2 65 65 65 65COPOLYMER 1 53.2 53.2 53.2 53.2Heptane 69.2 70 66 73.2TEOF 4 -- 4 --SILANE 1 5.9 5.9 5.9 5.9DBTDA 5.9 5.9 5.9 5.9TBT 5.9 -- -- 5.9__________________________________________________________________________
The viscosity of each catalyzed material was monitored as a function of time with a Brookfield LVF viscometer using a #3 spindle at 60 r.p.m. at atemperature of 75.degree. F. In addition, the compositions were evaluated for sprayability using a Binks Model 62 siphon fed spray gun equipped witha #66 nozzle at an air pressure of 55 p.s.i. These results are presented inTables 2 to 5 for the compositions of Examples 1 to 4, respectively.
TABLE 2______________________________________Viscosity Data for Example 1Time (hours) Viscosity (cP) Comments______________________________________Initial 8001 560 Some skin on sides of beaker2 5803 700 Light skin - removed4 8505 1000 Some skin on sides of beaker/ Still sprayable______________________________________
TABLE 3______________________________________Viscosity Data for (Comparative) Example 2Time (hours) Viscosity (cP) Comments______________________________________Initial 1601 450 Severe skin over2 980 Severe skin over 2.5 2940 Severe skin over/ Too thick to spray______________________________________
TABLE 4______________________________________Viscosity Data for (Comparative) Example 3Time (hours) Viscosity (cP) Comments______________________________________Initial 1401 280 Some skin on sides of beaker; mixed in skin2 500 Some skin on sides of beaker; mixed in skin3 9404 1380 Stopped - too thick to spray______________________________________
TABLE 5______________________________________Viscosity Data for (Comparative) Example 4Time (hours) Viscosity (cP) Comments______________________________________Initial 2401 280 Skin @30 & 60 min - removed skin2 360 Skin @120 min - removed skin3 4004 620 Skin @240 min - removed skin5 1140 Skin @300 min - removed skin Stopped - too thick to spray______________________________________
EXAMPLES 5-8
The following formulated paints were prepared by thoroughly mixing pre-blended parts A and B, shown in Table 6, wherein the values indicate the percentage of each ingredient. In each case, the total solid content of the paint was adjusted to about 61% using Isopar G.RTM. and Kwik-Dri.RTM..
TABLE 6__________________________________________________________________________ (Comparative) (Comparative) (Comparative) Example 5 Example 6 Example 7 Example 8__________________________________________________________________________Part AFLUID 2 23.83 23.83 23.83 23.83COPOLYMER 1 23.98 23.98 23.98 23.98PIGMENT 9.15 9.15 9.15 9.15PROPYL RESIN 0.30 0.30 0.30 0.30Part BIsobutyl acetate 1.6 1.6 1.6 1.6Methyl amyl ketone 2.1 2.1 2.1 2.1Bentone SD-2 .RTM. 0.5 0.5 0.5 0.5Isopar L .RTM. 2.3 2.3 2.3 2.3Isopar G .RTM. 13.84 15.17 15.17 14.29Kwik-Dri .RTM. 13.85 15.17 15.17 14.29Triethyl orthoformate 1.95 1.95 -- --SILANE 1 2.65 2.65 2.65 2.65DBTDA 1.3 1.3 1.3 1.3TBT 2.65 2.65 100.00% 100.00% 100.00% 100.00%__________________________________________________________________________
These catalyzed paints were tested with respect to viscosity increase (at 100.degree. F. in this series) and sprayability, as described above. The results are presented in Tables 7 to 10 for the compositions of Examples 5to 8, respectively.
TABLE 7______________________________________Viscosity Data for Example 5Time (hours) Viscosity (cP) Comments______________________________________Initial 3401 385 No skin observed2 540 No skin observed3 550 No skin observed4 600 No skin observed5 700 No skin observed6 760 No skin observed7 790 No skin observed8 860 No skin observed______________________________________
TABLE 8______________________________________Viscosity Data for (Comparative) Example 6Time (hours) Viscosity (cP) Comments______________________________________Initial 3401 600 Skinning @30 & 60 min - removed2 1380 Skinning @90 & 120 min - removed; No longer sprayable3 Gelled______________________________________
TABLE 9______________________________________Viscosity Data for (Comparative) Example 7Time(hours) Viscosity (cP) Comments______________________________________Initial 3101 620 Skinning @15 & 60 min - removed2 920 Skinning @90 & 120 min - removed 2.5 1040 Skinning @150 & 180 min - removed3 1520 Skinning @210 & 240 min - removed No longer sprayable______________________________________
TABLE 10______________________________________Viscosity Data for (Comparative) Example 8Time(hours) Viscosity (cP) Comments______________________________________Initial 5901 660 Skinning @20 & 60 min - removed2 730 Skinning @90 & 120 min - removed3 900 Skinning @150 & 180 min - removed4 1080 Skinning @210 & 240 min - removed Still Sprayable5 1360 Skinning @270 & 300 min - removed; No longer sprayable______________________________________
EXAMPLES 9-10
The following examples were prepared as above by mixing the pre-blended parts A and B shown in Table 11 and illustrate the use of a lower molecular weight polydimethylsiloxane (i.e., FLUID 1). Again, the total solids content of these compositions was adjusted to about 61% by varying the Isopar G.RTM. and Kwik-Dri.RTM. contents.
TABLE 11______________________________________ (Comparative) Example 9 Example 10______________________________________Part AFLUID 1 24.5 24.5COPOLYMER 1 23.7 23.7PIGMENT 8.4 8.4PROPYL RESIN 0.2 0.2Part BIsobutyl acetate 1.6 1.6MIBK 4.5 4.5Bentone SD-2 .RTM. 0.5 0.5Isopar G .RTM. 16.35 14.05Kwik-Dri .RTM. 16.35 14.05SILANE 1 2.6 2.6DBTDA 1.3 1.3TEOF -- 2.0TBT -- 2.6 100.00 100.00______________________________________
These catalyzed paints were tested with respect to viscosity increase (at 76.degree. F. in this series) and sprayability, as described above. The results are presented in Tables 12 and 13 for the compositions of Examples9 and 10, respectively.
TABLE 12______________________________________Viscosity Data for (Comparative) Example 9Time(hours) Viscosity (cP) Comments______________________________________Initial 801 260 Skinning @15 & 60 min - removed2 390 Skinning @90 & 120 min - removed4 2800 Skinning @150 & 240 min - removed; No longer sprayable______________________________________
TABLE 13______________________________________Viscosity Data for Example 10Time (hours) Viscosity (cP) Comments______________________________________Initial 3001 3002 3103 3204 350 Some skinning on sides--mixed in5 3706 4008 440 Still able to spray______________________________________
EXAMPLES 11-12
Extremely high solids compositions were prepared according to the above methods wherein pre-blended parts A and B were mixed and heptane solvent was used to adjust the total solids content of each formulation to 95%. Table 14 shows the parts by weight of the various ingredients used.
TABLE 14______________________________________ (Comparative) Example 11 Example 12______________________________________Part AFLUID 1 118.0 118.0COPOLYMER 1 98.8 98.8Part BSILANE 1 10.4 10.4DBTDA 5.2 5.2Heptane 7.5 --TEOF -- 8.0TBT -- 10.4______________________________________
These catalyzed coating compositions were tested with respect to viscosity increase (at 76.degree. F. in this series) and sprayability, as described above. The results are presented in Tables 15 and 16 for the compositions of Examples 11 and 12, respectively. Because of the high viscosities, someair was "trapped" in the compositions during mixing.
TABLE 15______________________________________Viscosity Data for (Comparative) Example 11Time (hours) Viscosity (cP) Comments______________________________________Initial 11401 1900 Skinning @20 & 60 min - removed2 4100 Skinning @120 min - removed3 5950 Skinning @180 min - removed4 9000 Skinning @240 min - removed 4.5 Gelled______________________________________
TABLE 16______________________________________Viscosity Data for Example 12Time(hours) Viscosity (cP) Comments______________________________________Initial 56001 3400 Some skinning on sides - trapped air2 3200 Trapped air3 3300 Trapped air4 3400 Skinned over - removed - trapped air5 3600 Trapped air7 4400 Skinned over - removed - trapped air______________________________________
EXAMPLES 13-14
Very high solids paints were formulated according to the above methods wherein pre-blended parts A and B were mixed and heptane and isobutyl acetate solvents were used to adjust the total solids content of each formulation to 96%. Table 17 shows the parts by weight of the various ingredients used.
TABLE 17______________________________________ (Comparative) Example 13 Example 14______________________________________Part AFLUID 1 98.0 98.0COPOLYMER 1 98.8 98.8PIGMENT 33.6 33.6Bentone SD-2 .RTM. 2.0 2.0Isobutyl acetate 7.5 --Part BSILANE 1 10.4 10.4DBTDA 5.2 5.2Heptane 7.5 --TEOF -- 8.0TBT -- 10.4______________________________________
These catalyzed paints were tested with respect to viscosity increase (at 76.degree. F. in this series), as described above. The results are presented in Tables 18 and 19 for the compositions of Examples 13 and 14, respectively.
TABLE 18______________________________________Viscosity Data for (Comparative) Example 13Time (hours) Viscosity (cP) Comments______________________________________Initial 125001 19000 Skinning @20 & 60 min - removed 1.5 Gelled______________________________________
TABLE 19______________________________________Viscosity Data for Example 14Time (hours) Viscosity (cP) Comments______________________________________Initial 90001 5000 Some skinning on sides - removed2 6000 Some skinning on sides - removed3 6000 Some skinning on sides - removed4 6000 Some skinning on sides - removed5 6750 Some skinning on sides - removed6 6750 Some skinning on sides - removed______________________________________
It was noted that, even after 6 hours, the catalyzed paint of Example 14 had a viscosity which could still be sprayed in airless spray equipment orcould be diluted with solvents to be sprayed with conventional equipment. This is a striking contrast to (Comparative) Example 13, which gelled after only 1.5 hours.
EXAMPLES 15-17
The following formulated paints were prepared by thoroughly mixing pre-blended parts A and B and then mixing in part C. These formulations are shown in Table 20, wherein the values indicate the percentage of each ingredient.
TABLE 20______________________________________ Example 15 Example 16 Example 17______________________________________Part AFLUID 2 24.474 24.474 24.474COPOLYMER 1 23.696 -- --COPOLYMER 2 -- 19.192 --FLUID 3 -- -- 9.478PIGMENT 8.446 8.446 8.446Paint Additive #3 0.171 0.171 0.171Part BIsobutyl acetate 1.578 1.578 1.578MIBK 4.458 4.458 4.458Bentone SD-2 .RTM. 0.526 0.526 0.526METHYL RESIN -- 6.514 19.747SILANE 1 2.632 2.632 2.632Isopar G .RTM. 14.053 13.048 11.289Kwik-Dri .RTM. 14.053 13.048 11.288TEOF 1.965 1.965 1.965DBTDA 1.316 1.316 1.316Part CTBT 2.632 2.632 2.632Total 100.000% 100.000% 100.000%______________________________________
These catalyzed paints were tested with respect to viscosity increase (at 75.degree. F. in this series), as described above. The results are presented in Tables 21 to 23 for the compositions of Examples 15 to 17, respectively.
TABLE 21______________________________________Viscosity Data for Example 15Time (hours) Viscosity (cP) Comments______________________________________Initial 9901 820 Light skin; mixed in2 8803 7704 690 Light skin; mixed in5 6906 7407 740 Light skin; mixed in8 810______________________________________
TABLE 22______________________________________Viscosity Data for Example 16Time (hours) Viscosity (cP) Comments______________________________________Initial 4601 3302 4003 510 Light skin; mixed in4 6105 6006 640 Light skin; mixed in7 690 Light skin; mixed in8 720______________________________________
TABLE 23______________________________________Viscosity Data for Example 17Time (hours) Viscosity (cP) Comments______________________________________Initial 3501 2502 2903 2904 3205 3806 3807 4108 420______________________________________
When these paint formulations were applied to substrates and dried at room temperature, they cured to tack free coatings in less than about 30 minutes.

Claims

1. A curable composition comprising:
(I) from about 10 to about 90 parts by weight of a liquid organopolysiloxane copolymer, prepared by a method comprising (A) forming a homogeneous mixture having an acid number greater than zero and consisting essentially of (a) an organic solvent solution of a resinous copolymeric siloxane containing silicon-bonded hydroxyl radicals and consisting essentially of R.sub.3 SiO.sub.1/2 siloxane units and SiO.sub.4/2 siloxane units wherein the ratio of said R.sub.3 SiO.sub.1/2 units to said SiO.sub.4/2 units has a value of 0.6:1 to 0.9:1 and each R denotes, independently, a monovalent hydrocarbon radical and (b) a liquid organohydrogenpolysiloxane wherein each organic radical is, independently, a monovalent hydrocarbon radical, there being an average of at least one silicon-bonded hydrogen radical per molecule of said organohydrogenpolysiloxane, and (B) heating said homogeneous mixture to remove substantially all of said organic solvent therefrom;
(II) from about 90 to about 10 parts by weight of a hydroxy-functional diorganopolysiloxane having the average formula (HO)R'".sub.2 SiO(R'".sub.2 SiO).sub.c SiR'".sub.2 (OH) wherein R'" is a group selected from alkyl, cycloalkyl, haloalkyl, aromatic or haloaromatic radicals and c has a value sufficient to provide a viscosity of about 1 to about 500 Poise at 25.degree. C. for said diorganopolysiloxane;
(III) from about 1 to about 10 parts by weight, per 100 parts of said component (I) plus component (II), of at least one organosilane having the formula QSi(OR"").sub.3 wherein the group Q is selected from vinyl, 3-glycidoxypropyl, 3-methacryloxypropyl or 3-(N-styrylmethyl-2-aminoethylamino)-propyl hydrochloride groups and R"" is selected from alkyl groups having 1 to 4 carbon atoms, alkoxyalkyl groups having a total of up to 5 carbon atoms or an acetyl group;
(IV) from about 1 to about 10 parts by weight, per 100 parts of said component (I) plus component (II), of a trialkyl orthoformate in which the alkyl groups contain 1-3 carbon atoms;
(V) from about 4 to about 10 parts by weight, per 100 parts of said component (I) plus component (II), of an organic titanate selected from the group consisting of Ti(OR'"").sub.4 and (AcAc)Ti(OR'"").sub.2, in which R'"" is an alkyl radical having 3 to 8 carbon atoms and AcAc denotes an acetylacetonate group; and
(VI) a sufficient amount of a condensation catalyst to cure said composition.
2. The composition of claim 1, wherein R and R'" are methyl and said liquid organopolysiloxane copolymer is prepared from a homogeneous mixture having an acid number between 0.1 and 1, on a solids basis.
3. The composition of claim 2, wherein the ratio of R.sub.3 SiO.sub.1/2 units to SiO.sub.4/2 units has a value of about 0.75.
4. The composition of claim 3, wherein said liquid organohydrogenpolysiloxane is represented by the formula ##STR4## in which Me denotes a methyl radical and b has an average value of 30 to 70.
5. The composition of claim 4, wherein said component (IV) is triethyl orthoformate.
6. The composition of claim 5, wherein said component (V) is tetra(n-butyl) titanate.
7. The composition of claim 6, wherein said component (III) is at least one organosilane selected from the group consisting of 3-glycidoxypropyltrimethoxysilane and vinyltriacetoxysilane.
8. The composition of claim 7, wherein said liquid organohydrogenpolysiloxane (b) constitutes from about 40 to 60 weight percent of component (I) and said diorganopolysiloxane (II) has a viscosity of about 150 Poise at 25.degree. C.
9. The composition of claim 8, wherein said condensation catalyst (VI) is dibutyltin diacetate.
10. The composition of claim 1, packaged as a three part system, such that said components (I) and (II) comprise a first part, said components (III), (IV) and ((VI) comprise a second part and said component (V) comprises a third part.
11. The composition of claim 9, packaged as a three part system, such that said components (I) and (II) comprise a first part, said components (III), (IV) and ((VI) comprise a second part and said component (V) comprises a third part.
12. A curable composition comprising:
(I) from about 10 to about 90 parts by weight of a blend, on a solids basis, of (a) an organic solvent solution of a resinous copolymeric siloxane containing silicon-bonded hydroxyl radicals and consisting essentially of R.sub.3 SiO.sub.1/2 siloxane units and SiO.sub.4/2 siloxane units wherein the ratio of said R.sub.3 SiO.sub.1/2 units to said SiO.sub.4/2 units has a value of 0.6:1 to 0.9:1 and each R denotes, independently, a monovalent hydrocarbon radical and (b) a liquid organohydrogenpolysiloxane wherein each organic radical is, independently, a monovalent hydrocarbon radical, there being an average of at least one silicon-bonded hydrogen radical per molecule of said organohydrogenpolysiloxane;
(II) from about 90 to about 10 parts by weight of a hydroxy-functional diorganopolysiloxane having the average formula (HO)R'".sub.2 SiO(R'".sub.2 SiO).sub.c SiR'".sub.2 (OH) wherein R'" is a group selected from alkyl, cycloalkyl, haloalkyl, aromatic or haloaromatic radicals and c has a value sufficient to provide a viscosity of about 1 to about 500 Poise at 25.degree. C. for said diorganopolysiloxane;
(III) from about 1 to 10 parts by weight, per 100 parts of said component (I) plus component (II), of at least one organosilane having the formula QSi(OR"").sub.3 wherein the group Q is selected from vinyl, 3-glycidoxypropyl, 3-methacryloxypropyl or 3-(N-styrylmethyl-2-aminoethylamino)-propyl hydrochloride groups and R"" is selected from alkyl groups having 1 to 4 carbon atoms, alkoxyalkyl groups having a total of up to 5 carbon atoms or an acetyl group;
(IV) from about 1 to about 10 parts by weight, per 100 parts of said component (I) plus component (II), of a trialkyl orthoformate in which the alkyl groups contain 1-3 carbon atoms;
(V) from about 4 to about 10 parts by weight, per 100 parts of said component (I) plus component (II), of an organic titanate selected from the group consisting of Ti(OR'"").sub.4 and (AcAc)Ti(OR'"").sub.2, in which R'"" is an alkyl radical having 3 to 8 carbon atoms and AcAc denotes an acetylacetonate group; and
(VI) a sufficient amount of a condensation catalyst to cure said composition.
13. The composition of claim 12, wherein R and R'" are methyl and said blend (I) is prepared from a homogeneous mixture having an acid number between 0.1 and 1, on a solids basis.
14. The composition of claim 13, wherein the ratio of R.sub.3 SiO.sub.1/2 units to SiO.sub.4/2 units has a value of about 0.75.
15. The composition of claim 14, wherein said liquid organohydrogenpolysiloxane is represented by the formula ##STR5## in which Me denotes a methyl radical and b has an average value of 30 to 70.
16. The composition of claim 15, wherein said component (IV) is triethyl orthoformate.
17. The composition of claim 16, wherein said component (V) is tetra (n-butyl) titanate.
18. The composition of claim 17, wherein said component (III) is at least one organosilane selected from the group consisting of 3-glycidoxypropyltrimethoxysilane and vinyltriacetoxysilane.
19. The composition of claim 18, wherein said liquid organohydrogenpolysiloxane (b) constitutes from about 40 to 60 weight percent of component (I) on a solids basis and said diorganopolysiloxane (II) has a viscosity of about 150 Poise at 25.degree. C.
20. The composition of claim 19, wherein said condensation catalyst (VI) is dibutyltin diacetate.
21. The composition of claim 12, packaged as a three part system, such that said components (I) and (II) comprise a first part, said components (III), (IV) and ((VI) comprise a second part and said component (V) comprises a third part.
22. The composition of claim 20, packaged as a three part system, such that said components (I) and (II) comprise a first part, said components (III), (IV) and ((VI) comprise a second part and said component (V) comprises a third part.
23. A metal substrate coated with the cured composition of claim 1.
24. A metal substrate coated with the cured composition of claim 4.
25. A metal substrate coated with the cured composition of claim 8.
26. A metal substrate coated with the cured composition of claim 12.
27. A metal substrate coated with the cured composition of claim 15.
28. A metal substrate coated with the cured composition of claim 19.

US Referenced Citations (6)

Number	Name	Date
4322518	Blizzard	Mar 1982
4537829	Blizzard	Aug 1985
4701380	Narula et al.	Oct 1987
4808640	Morita et al.	Feb 1989
4824903	Aizawa et al.	Apr 1989
4882377	Sweet et al.	Nov 1989

Silicone corrosion protection coating having extended bath life

Information

Patent Number

Date Filed

Date Issued

Inventors

Original Assignees

Examiners

Agents

CPC

US Classifications

Field of Search

US

International Classifications

Abstract

Description

Claims

US Referenced Citations (6)