Patent Grant
12146034
The present invention generally relates to copolymers and, more specifically, to a silicone-polyester copolymer, methods of preparing the same, and sealants comprising the same.
Sealants are known in the art and are utilized in myriad end use applications and environments. Physical and performance properties of sealants, as well as the particular curing mechanism associated therewith, are generally selected based on the particular end use application and environment in which the sealants are utilized. Sealants can be based on a variety of different chemistries and cure mechanisms. For example, sealants can be silicone-based and include organopolysiloxanes. Alternatively, sealants can be organic and include organic components, e.g. to form urethanes. Increasingly, hybrid materials are utilized in sealants, which can combine the benefits traditionally associated with silicone-based sealants and organic sealants.
A silicone-polyester copolymer having the formula Xg[ZjYo]c is disclosed. Each X is independently a silicone moiety having one of formulas (I) or (II):
each Y is an independently selected polyester moiety, and each Z is an independently selected siloxane moiety having the formula [R1hSiO(4−h)/2]d. In these moieties, each R1 is an independently selected substituted or unsubstituted hydrocarbyl group having from 1 to 18 carbon atoms; each R2 is an independently selected substituted or unsubstituted hydrocarbyl group having from 1 to 18 carbon atoms; each D1 is an independently selected divalent hydrocarbon group having from 2 to 18 carbon atoms; each subscript a is independently from 0 to 2; each subscript b is independently 0 or 1; subscript c is from 1 to 150; each subscript d is from 1 to 1000; each subscript e is independently 1 or 2; each subscript f is independently 0 or 1, with the proviso that within each X, when f is 1, b is 1; subscript g is >1; subscript h is independently selected from 0 to 2 in each moiety indicated by subscript d; each subscript j is independently ≥0 and <2; each subscript o is independently >0 and <2, with the proviso that j+o=2 in each moiety indicated by subscript c; subscript t is ≥0; and subscript u is >0.
A method of preparing the silicone-polyester copolymer is disclosed. The method comprises reacting a polyester compound having on average more than one unsaturated group and an endcapping organosilicon compound in the presence of a hydrosilylation catalyst to give the silicone-polyester copolymer.
A second method of preparing the silicone-polyester copolymer is further disclosed. This second method comprises reacting an organic compound having one terminal unsaturated group and one terminal hydroxyl group with an endcapping organosilicon compound in the presence of a hydrosilylation catalyst to give a hydroxyl-functional intermediate. This second method further comprises reacting the hydroxyl-functional intermediate with a polyisocyanate to give an isocyanate-functional intermediate, and reacting the isocyanate-functional intermediate and a polyester compound having on average more than one hydroxyl group to give the silicone-polyester copolymer.
A sealant is also disclosed. The sealant comprises a condensation reaction catalyst and further comprises the silicone-polyester copolymer.
A cured product is additionally disclosed. The cured product is formed from the sealant. Further, a composite article and a method of preparing the composite article are disclosed. The composite article comprises a substrate and the cured product disposed on the substrate. The method comprising disposing the sealant on the substrate, and curing the sealant to give the cured product on the substrate, thereby preparing the composite article.
A silicone-polyester copolymer has the formula Xg[ZjYo]c, wherein each X is independently a silicone moiety having one of formulas (I) or (II):
each Y is an independently selected polyester moiety, and each Z is an independently selected siloxane moiety having the formula [R1hSiO(4−h)/2]d; where each R1 is an independently selected substituted or unsubstituted hydrocarbyl group having from 1 to 18 carbon atoms; each R2 is an independently selected substituted or unsubstituted hydrocarbyl group having from 1 to 18 carbon atoms; each D1 is an independently selected divalent hydrocarbon group having from 2 to 18 carbon atoms; each subscript a is independently from 0 to 2; each subscript b is independently 0 or 1; subscript c is from 1 to 150; each subscript d is from 1 to 1000; each subscript e is independently 1 or 2; each subscript f is independently 0 or 1, with the proviso that within each X, when f is 1, b is 1; subscript h is independently selected from 0 to 2 in each moiety indicated by subscript d; each subscript j is independently ≥0 and <2; each subscript o is independently >0 and <2, with the proviso that j+o=2 in each moiety indicated by subscript c; subscript t is ≥0; and subscript u is >0.
Each R1 and each R2 is independently selected and may be linear, branched, cyclic, or combinations thereof. Cyclic hydrocarbyl groups encompass aryl groups as well as saturated or non-conjugated cyclic groups. Cyclic hydrocarbyl groups may be monocyclic or polycyclic. Linear and branched hydrocarbyl groups may independently be saturated or unsaturated. One example of a combination of a linear and cyclic hydrocarbyl group is an aralkyl group. By “substituted,” it is meant that one or more hydrogen atoms may be replaced with atoms other than hydrogen (e.g. a halogen atom, such as chlorine, fluorine, bromine, etc.), or a carbon atom within the chain of R1 and/or R2 may be replaced with an atom other than carbon, i.e., R1 and/or R2 may include one or more heteroatoms within the chain, such as oxygen, sulfur, nitrogen, etc. Suitable alkyl groups are exemplified by, but not limited to, methyl, ethyl, propyl (e.g., iso-propyl and/or n-propyl), butyl (e.g., isobutyl, n-butyl, tert-butyl, and/or sec-butyl), pentyl (e.g., isopentyl, neopentyl, and/or tert-pentyl), hexyl, as well as branched saturated hydrocarbon groups of 6 carbon atoms. Suitable aryl groups are exemplified by, but not limited to, phenyl, tolyl, xylyl, naphthyl, benzyl, and dimethyl phenyl. Suitable alkenyl groups include vinyl, allyl, propenyl, isopropenyl, butenyl, isobutenyl, pentenyl, heptenyl, hexenyl, and cyclohexenyl groups. Suitable monovalent halogenated hydrocarbon groups include, but are not limited to, a halogenated alkyl group of 1 to 6 carbon atoms, or a halogenated aryl group of 6 to 10 carbon atoms. Suitable halogenated alkyl groups are exemplified by, but not limited to, the alkyl groups described above where one or more hydrogen atoms is replaced with a halogen atom, such as F or Cl. For example, fluoromethyl, 2-fluoropropyl, 3,3,3-trifluoropropyl, 4,4,4-trifluorobutyl, 4,4,4,3,3-pentafluorobutyl, 5,5,5,4,4,3,3-heptafluoropentyl, 6,6,6,5,5,4,4,3,3-nonafluorohexyl, and 8,8,8,7,7-pentafluorooctyl, 2,2-difluorocyclopropyl, 2,3-difluorocyclobutyl, 3,4-difluorocyclohexyl, and 3,4-difluoro-5-methylcycloheptyl, chloromethyl, chloropropyl, 2-dichlorocyclopropyl, and 2,3-dichlorocyclopentyl are examples of suitable halogenated alkyl groups. Suitable halogenated aryl groups are exemplified by, but not limited to, the aryl groups described above where one or more hydrogen atoms is replaced with a halogen atom, such as F or Cl. For example, chlorobenzyl and fluorobenzyl are suitable halogenated aryl groups.
In certain embodiments, each of R1 and R2 is an independently selected alkyl group. In specific embodiments, R1 and R2 are different from one another. For example, in these embodiments, R2 may include more carbon atoms than R1. In specific embodiments, each R1 is methyl and each R2 is propyl.
With regard to the silicone-polyester copolymer, it is to be understood that the sub-formula [ZjYo]c is not intended to imply a linear structure of the copolymer moieties indicated by ZY. Rather, as understood in the art, the copolymer moieties indicated by ZY may be linear or branched, with each moiety indicated by subscript c being independently selected. As such, the silicone-polyester copolymer comprises c number of copolymer moieties ZY, which each comprise o number of polyester moieties Y and j number of siloxane moieties Z. Additionally, as will be understood in view of the description below, each polyester moiety Y and siloxane moiety Z are independently selected, both within each moiety indicated by subscript c and between such moieties, and also may each be linear or branched. Further, still, because subscript j may be 0, the silicone-polyester copolymer may be free from the siloxane moiety Z, i.e., the backbone of the silicone-polyester copolymer may comprise, alternatively consist essentially of, alternatively consist of, the polyester moiety Y. In such embodiments, the silicone-polyester copolymer has the formula Xg[Y]c, where X, Y, and subscripts g and c are defined above.
Each subscript c is from 1 to 150, such as from 1 to 100, alternatively from 1 to 50, alternatively from 1 to 25, alternatively from 1 to 10, and alternatively from 1 to 5. Subscript g is greater than 1, such as from 1.1 to 10, alternatively from 1.1 to 8, alternatively from 1.1 to 6, alternatively from 1.1 to 4, alternatively from 1.1 to 3, alternatively from 1.1 to 2, alternatively from 1.1 to 1.9, alternatively from 1.2 to 1.8, alternatively from 1.2 to 1.7, alternatively from 1.3 to 1.7, alternatively from 1.4 to 1.7, alternatively of about 1.4, 1.5, 1.6, or 1.7.
Each subscript j is ≥0 and <2, and each subscript o is >0 and <2, with the proviso that j+o=2 in each moiety indicated by subscript c. As such, subscripts j and o may be considered mole fractions, e.g. where j=1 and o=1 equating to a 0.5:0.5 molar ratio of siloxane moiety Z to polyester moiety Y in a moiety indicated by subscript c. For example, when subscript j is >0, the molar ratio of Z:Y may be independently from about 1000:1 to about 1:1000, alternatively from about 100:1 to about 1:100, alternatively from about 10:1 to about 1:10, alternatively from about 5:1 to about 1:5, alternatively from about 2:1 to about 1:2, in each moiety indicated by subscript c. When j is 0, the silicone-polyester copolymer need not require two distinct polyester moieties indicated by subscript o, despite c being 2. The designation of subscripts j and o is merely for mole fraction purposes of the copolymer moieties indicated by ZY.
As described above, the sub-formula [ZjYo]c is not intended to imply a linear structure of the copolymer moieties indicated by ZY. Likewise, the sub-formula does not require a particular structure of any of the copolymer moieties ZY. Rather, depending on the values selected for subscripts j and o, the copolymer moiety indicated by sub-formula [ZjYo]c may comprise siloxane moieties Z and polyester moieties Y in block form (e.g. Z—Y, Y—Z, Y—Z—Y, Z—Y—Z—Y, YY—ZZ, etc.) or random form with subscript j is greater than 0. In particular embodiments, the silicone-polyester copolymer comprises polyester moieties Y and siloxane moieties Z in a 2:1 ratio. In some such embodiments, the polyester moieties Y and siloxane moieties Z are present in the silicone-polyester copolymer in block form, such that the silicone-polyester copolymer has the formula XgY[ZY]c, where subscripts c and g are defined above. In some of these embodiments, the silicone-polyester copolymer comprises linear polyester moieties Y and linear siloxane moieties Z, and is endcapped by silicone moieties X, such that the silicone-polyester copolymer has the formula Xg′Y[ZY]cXg″, where c is defined above, and each of g′ and g″ is ≥0, with the proviso that g′+g″ is >1.
With regard to each X generally, each subscript a is independently from 0 to 2, alternatively from 0 to 1. Typically, subscript a is 0. In some embodiments, each subscript a is 0. In certain embodiments, the silicone-polyester copolymer comprises at least one X where subscript a is 1.
With regard to each X of formula (I), each subscript b is independently 0 or 1. In some embodiments, each subscript b is 0. In other embodiments, each subscript b is 1. In further embodiments, the silicone-polyester copolymer comprises at least one X of formula (I) where subscript b is 0 and at least one X of formula (I) where subscript b is 1. Each subscript e is independently 1 or 2. In some embodiments, each subscript e is 1. In other embodiments, each subscript e is 2. In further embodiments, the silicone-polyester copolymer comprises at least one X of formula (I) where subscript e is 1 and at least one X of formula (I) where subscript e is 2. Each subscript f is independently 0 or 1, with the proviso that within each X, when f is 1, b is 1. In some embodiments, each subscript f is 0. In other embodiments, each subscript f is 1, and thus each b is 1. In further embodiments, the silicone-polyester copolymer comprises at least one X of formula (I) where subscript f is 0 and at least one X of formula (I) where subscript f is 1 and b is 1.
With regard to each X of formula (II), subscript t is ≥0. In certain embodiments, subscript t is from 1 to 100, such as from 0 to 80, alternatively from 0 to 60, alternatively from 0 to 30, alternatively from 0 to 10, alternatively from 0 to 5. Subscript u is >0. In particular embodiments, subscript u is from 1 to 20, such as from 1 to 15, alternatively from 1 to 10, alternatively from 1 to 7, alternatively from 1 to 5, and alternatively from 1 to 3.
Each D1 is an independently selected divalent hydrocarbon group having from 2 to 18 carbon atoms, alternatively from 2 to 16 carbon atoms, alternatively from 2 to 14 carbon atoms, alternatively from 2 to 12 carbon atoms, alternatively from 2 to 10 carbon atoms, alternatively from 2 to 8 carbon atoms, alternatively from 2 to 6 carbon atoms, alternatively from 2 to 4 carbon atoms, alternatively 2 or 3 carbon atoms, alternatively 2 carbon atoms. Each D1 may independently be linear or branched. For example, when D1 has two carbon atoms, D1 has formula C2H4, and may be linear (CH2CH2) or branched (CHCH3). In certain embodiments, D1 is linear. When the silicone-polyester copolymer is prepared in bulk, in certain embodiments, at least 90 mol % of D1 are linear. In specific embodiments, each D1 is C2H4.
Each Y is a polyester moiety. Each Y is independently selected, and may be any polyester moiety including at least one, alternatively at least two, ester moieties. Each Y may be the same as any or each other Y. Alternatively, the silicone-polyester copolymer may comprise at least two Y that are different from each other. Y can be linear or branched. Y may be divalent, trivalent, tetravalent, or have a valency greater than 4. Valency, in the context of the polyester moiety Y, refers to the number of Y—X bonds present in the silicone-polyester copolymer. In certain embodiments, the polyester moiety Y is divalent such that the silicone-polyester copolymer has the formula X—Y—X. In other embodiments, the valency of the polyester moiety may be greater than 2, in which case the polyester moiety Y is typically branched.
Each Y comprises a polyester moiety. The polyester moiety is not limited and may be formed from any polyester compound, as described below in regards to the method of preparing the silicone-polyester copolymer. The term “polyester moiety,” as used herein, means a moiety including at least one ester bond. For example, the polyester moiety may be monomeric, oligomeric, polymeric, aliphatic, aromatic, araliphatic, etc. In addition, the silicone-polyester copolymer may comprise a different polyester moieties, which are independently selected.
Methods of preparing polyesters (and polyester moieties) are known in the art. For example, polyesters may be prepared via a conventional esterification process using a hydroxyl compound (e.g. an aromatic and/or aliphatic alcohol or glycol) and an acid. The hydroxyl compound is typically a polyhydric alcohol.
Specific examples of hydroxyl compounds suitable for preparing polyesters (and polyester moieties) include ethylene glycol, diethylene glycol, propylene glycol, dipropylene glycol, trimethylene glycol, 1,3-propanediol, 1,2-butane diol, 1,3-butanediol, 1,4-butanediol, 1,2-pentanediol, 1,4-pentanediol, neopentyl glycol, 1,5-pentanediol, 1,6-hexanediol, 1,7-heptanediol, glycerol, 1,1,1-trimethylolpropane, 1,1,1-trimethylolethane, 1,2,6-hexanetriol, decanediol, dodecanediol α-methyl glucoside, pentaerythritol, and sorbitol. Also included within the term “polyhydric alcohols” are compounds derived from phenol such as 2,2-bis(4-hydroxylphenyl)propane, commonly known as Bisphenol A
Specific examples of acids suitable for preparing polyesters (and polyester moieties) include polycarboxylic acids, including oxalic acid, malonic acid, succinic acid, glutaric acid, adipic acid, 2-methyl-1,6-hexanoic acid, pimelic acid, suberic acid, azelaic acid, sebacic acid, brassylic acid, maleic acid, fumaric acid, glutaconic acid, α-hydromuconic acid, β-hydromuconic acid, α-butyl-α-ethyl-glutaric acid, α, β-diethylsuccinic acid, isophthalic acid, terephthalic acid, hemimellitic acid, phthalic acid, isophthalic acid and 1,4-cyclohexanedicarboxylic acid.
Other methods of preparing polyesters (and polyester moieties) are also known. For example, polyesters (and polyester moieties) may comprise ring-opened polymers of a cyclic lactone, polycondensation products of a hydroxycarboxylic acid, polycondensation products of a dibasic acid and a polyol, and transesterification of an ester compound with a hydroxyl compound or another ester compound.
The particular polyester moiety Y present in the silicone-polyester copolymer is a function of end use applications of the silicone-polyester copolymer. For example, aliphatic polyester moieties generally provide greater flexibility and lower glass transition temperatures (Tg) than aromatic polyester moieties, which are typically more rigid with higher glass transition temperatures (Tg). Similarly, molecular weight and viscosity may be selectively controlled based on desired properties of the silicone-polyester copolymer. Further still, the selection of the polyester moiety Y can be a function of whether the siloxane moiety Z is present in the silicone-polyester copolymer, or whether Y includes any other moieties other than the polyester moiety, such as an ether moiety.
Each Y typically has a number average molecular weight (Mn) of at least about 100. In certain embodiments, at least one Y has a Mn of at least 100, alternatively at least 125, alternatively at least 150, alternatively at least 200, alternatively at least 250, alternatively at least 300. In these or other embodiments, each Y has a Mn of at least 200, alternatively at least 300, alternatively at least 400, alternatively at least 500, alternatively at least 600, alternatively at least 700, alternatively at least 1,000, alternatively at least 2,000, alternatively at least 4,000, alternatively at least 8,000. In certain embodiments, each Y has a maximum Mn of 100,000, alternatively less than 80,000, alternatively less than 50,000, alternatively less than 35,000, alternatively less than 20,000, alternatively less than 19,000, alternatively less than 18,000, alternatively less than 17,000, alternatively less than 16,000, alternatively less than 15,000. The number average molecular weight may be readily determined using Gel Permeation Chromatography (GPC) techniques based on polystyrene standards.
In certain embodiments, each Y can independently be in the form of a solid or a fluid. When Y is in the form of a fluid, the viscosity of Y is typically greater than 100 centipoise at room temperature. In certain embodiments, Y has a viscosity range of from 1,000 to 100,000 centipoise at 25° C. When Y is in the form of a solid, Y can have a melting point from 20 to 250° C. The selection of melting point is generally matter of matching the need for a specific application. The hydroxyl number is determined by the number of hydroxyl groups on each molecule on average and the average molecular weight, and can be from 1 to 1200 mg KOH/g, alternatively from 5 to 600, alternatively from 10 to 400, alternatively from 15 to 200, alternatively from 20 to 100 mg KOH/g.
Each Z is an independently selected siloxane moiety having the formula [R1hSiO(4−h)/2]d. In each siloxane moiety Z, R1 is as defined above. Each subscript d is from 1 to 1000, such as from 1 to 500, alternatively from 1 to 300, alternatively from 1 to 100, alternatively from 1 to 50, alternatively from 1 to 10. Each subscript h is independently selected from 0 to 2 in each moiety indicated by subscript d, such as 0, 1, or 2. Each siloxane moiety Z may independently comprise a linear siloxane, a branched siloxane, or both. Likewise, any particular siloxane moiety Z may itself comprise linear or branched segments, or comprise both linear and branched segments. As such, Z may be a linear siloxane moiety, a branched siloxane moiety, or a siloxane moiety comprising at least one linear and also at least one branched segment. In certain embodiments, Z is branched (i.e., comprises at least one branched segment).
In certain embodiments, each polyester moiety Y is linear and Z is present, such that the silicone-polyester copolymer may have one of the following structures:
where each X, Y, Z, and subscript c are defined above. Alternatively, each polyester moiety Y may be branched. For example, the silicone-polyester copolymer may have one of the following structures:
where each X, Y, Z, and subscript c are defined above. As shown in these structures, each siloxane moiety Z may be linear or branched. In particular embodiments, both polyester moiety Y and siloxane moiety Z may be branched, such that the silicone-polyester copolymer may have one of the following structures:
where each X, Y, Z, and subscript c are defined above.
In certain embodiments, Y further comprises at least one moiety in addition to and different from the polyester moiety. The at least one moiety may be another polyester moiety different from the polyester moiety Y in any aspect, such as molecular weight, viscosity, structure, etc. Alternatively or in addition, the at least one moiety may be something other than a polyester moiety altogether.
Specific examples of the at least one moiety include an alkylaluminoxane moiety, an alkylgermoxane moiety, a polythioester moiety, a polyester moiety, a polythioether moiety, a polyacrylate moiety, a polyacrylonitrile moiety, a polyacrylamide moiety, a polycarbonate moiety, an epoxy moiety, a polyurethane moiety, a polyurea moiety, a polyacetal moiety, a polyolefin moiety, a polyvinyl alcohol moiety, a polyvinyl ester moiety, a polyvinyl ether moiety, a polyvinyl ketone moiety, a polyisobutylene moiety, a polychloroprene moiety, a polyisoprene moiety, a polybutadiene moiety, a polyvinylidiene moiety, a polyfluorocarbon moiety, a polychlorinated hydrocarbon moiety, a polyalkyne moiety, a polyamide moiety, a polyimide moiety, a polyimidazole moiety, a polyoxazole moiety, a polyoxazine moiety, a polyoxidiazole moiety, a polythiazole moiety, a polysulfone moiety, a polysulfide moiety, a polyketone moiety, a polyesterketone moiety, a polyanhydride moiety, a polyamine moiety, a polyimine moiety, a polyphosphazene moiety, a polysaccharide moiety, a polypeptide moiety, a polyisocyanate moiety, a cellulosic moiety, and combinations thereof. Each Y may independently comprise at least one moiety other than the polyester moiety Y. When there are a plurality of moieties other than the polyester moiety Y, the moieties may be independently selected.
In other embodiments, Y consists essentially of the polyester moiety, alternatively Y consists of the polyester moiety.
In certain embodiments, the silicone-polyester copolymer has the formula: [XA]g[ZjYo]c, wherein each silicone moiety X is bonded to one polyester moiety Y or one siloxane moiety Z, if present, via A, wherein each A is independently selected from a covalent bond, -D2-O—C(═O)—NH—, and -D2-NH—C(═O)—NH—, where D2 is a divalent group. A is typically a covalent bond when X is bonded to Y or Z via hydrosilylation, but may be other than a covalent bond when other reaction mechanisms are utilized to form the silicone-polyester copolymer. When the silicone-polyester copolymer has the formula immediate above, each silicone moiety X is bonded to one polyester moiety Y or one siloxane moiety Z, if present, via A. Each silicone moiety X may be pendent, terminal, or in both locations in the silicone-polyester copolymer. The particular structure associated with A is a function of the method of preparing the silicone-polyester copolymer, as described below. In certain embodiments, each silicone moiety X is bonded to one polyester moiety Y.
When each silicone moiety X is terminal, the siloxane moiety Z is present, and the silicone-polyester polymer is linear, the silicone-polyester may have the following structure:
wherein each X, Y, A, R1, subscript c, and subscript d is defined above.
For example, when each X has formula (I), when each silicone moiety X is terminal, the siloxane moiety Z is present, and the silicone-polyester polymer is linear, the silicone-polyester may have the following structure:
where each Y, R1, R2, D1, subscript a, subscript b, subscript c, subscript d, subscript e, and subscript f are as defined above.
In certain embodiments, X has formula (I), e is 1, each silicone moiety X is terminal, the siloxane moiety Z is present, and the silicone-polyester polymer is linear. In these embodiments, the silicone-polyester copolymer has the following structure:
where each Y, R1, R2, D1, subscript a, subscript b, subscript c, subscript d, and subscript f are as defined above. In some such embodiments, f is 0, and the silicone-polyester copolymer has the following structure:
where each Y, R1, R2, D1, subscript a, subscript b, subscript c, and subscript d are as defined above. In some of these embodiments, b is 0 and the silicone-polyester copolymer has the following structure:
where each Y, R1, R2, D1, subscript a, subscript c, and subscript d are as defined above. In other embodiments, b is 1 and the silicone-polyester copolymer has the following structure:
where each Y, R1, R2, D1, subscript a, subscript c, and subscript d are as defined above. In other embodiments, f is 1 and b is 1 and the silicone-polyester copolymer has the following structure:
where each Y, R1, R2, D1, subscript a, subscript b, subscript c, and subscript d are as defined above.
In some embodiments, X has formula (I), e is 2, each silicone moiety X is terminal, the siloxane moiety Z is present, and the silicone-polyester polymer is linear. In these embodiments, the silicone-polyester copolymer has the following structure:
where each Y, R1, R2, D1, subscript a, subscript b, subscript c, subscript d, and subscript f are as defined above. In some such embodiments, f is 0, and the silicone-polyester copolymer has the following structure:
where each Y, R1, R2, D1, subscript a, subscript b, subscript c, and subscript d are as defined above. In some of these embodiments, b is 1 and the silicone-polyester copolymer has the following structure:
where each Y, R1, R2, D1, subscript a, subscript c, and subscript d are as defined above. In other embodiments, b is 0 and the silicone-polyester copolymer has the following structure:
where each Y, R1, R2, D1, subscript a, subscript c, and subscript d are as defined above. In other embodiments, f is 1 and b is 1 and the silicone-polyester copolymer has the following structure:
where each Y, R1, R2, D1, subscript a, subscript c, and subscript d are as defined above.
When each X has formula (II), the silicone-polyester copolymer has the following structure:
where each Y, R1, D1, subscript a, subscript t, and subscript u are as defined above. In such embodiments, X includes a cyclic moiety. In certain embodiments, (t+u) is from 2 to 14, alternatively from 2 to 9, alternatively from 2 to 6, alternatively from 2 to 5, alternatively 2 to 4.
The exemplary structures above are based on each X, each Y, and/or each Z in the silicone-polyester copolymer being the same. However, each X, each Y, and each Z are independently selected, as described above. As such, one of skill in the art readily understands structures associated with the silicone-polyester copolymer based on the selection of each X, each Y, and/or each Z.
In the specific structures above, Z is present. However, because Z is optional, the silicone-polyester copolymer may have any of the above structures without the presence of Z. One of skill in the art readily understands and envisages such silicone-polyester copolymers in view of the exemplary structures above. For example, when Z is absent, the silicone-polyester copolymer may have the following formula: X-A-Y1-A-X, where X and A are independently selected and defined above and Y1 comprises a polyester moiety. Y1 can be the same as Y, or Y1 can comprise or consist of any combination of different polyester moieties.
A method of preparing the silicone-polyester copolymer is also disclosed. The method comprises reacting a polyester compound having on average more than one unsaturated group, and an endcapping organosilicon compound in the presence of a hydrosilylation catalyst to give the silicone-polyester copolymer.
As will be understood by one of skill in the art in view of the description herein, the polyester compound utilized in the method forms a portion of the silicone-polyester copolymer corresponding to the polyester moiety Y, and the endcapping organosilicon compound utilized in the method forms a portion of the silicone-polyester copolymer corresponding to the silicone moiety X. In certain embodiments, the method further comprises reacting, along with the polyester compound and the endcapping organosilicon compound, at least one of: (i) a chain extending organosilicon compound and (ii) a hybridizing compound having on average more than one unsaturated group. If utilized, the chain extending organosilicon compound utilized in the method forms a portion of the silicone-polyester copolymer corresponding to the siloxane moiety Z. The hybridizing compound, if utilized, becomes part of Y along with the polyester moiety. In certain embodiments, the method is free from the chain extending organosilicon compound and the hybridizing compound. In other embodiments, the method utilizes the chain extending organosilicon compound or the hybridizing compound but not the other. In yet further embodiments, the method utilizes both the chain extending organosilicon compound and the hybridizing compound.
Typically, the polyester compound has the formula: Y[R4]i, where each R4 is an independently selected unsaturated group having from 2 to 14 carbon atoms; subscript i is >1; and Y is polyester moiety comprising at least one polyester group.
Each R4 is an independently selected unsaturated group having from 2 to 14 carbon atoms. Typically, R4 comprises, alternatively is, an alkenyl group or an alkynyl group. Specific examples thereof include H2C═CH—, H2C═CHCH2—, H2C═CHCH2CH2—, H2C═CH(CH2)3—, H2C═CH(CH2)4—, H2C═C(CH3)—, H2C═C(CH3)CH2—, H2C═C(CH3)CH2CH2—, H2C═C(CH3)CH2CH(CH3)—, H2C═C(CH3)CH(CH3)CH2—, H2C═C(CH3)C(CH3)2—, HC≡C—, HC≡CCH2—, HC≡CCH(CH3)—, HC≡CC(CH3)2—, and HC≡CC(CH3)2CH2—.
In certain embodiments, each R4 has the formula CH2C(R3)-[D2]m-, wherein each R3 is independently a hydrocarbyl group having from 1 to 6 carbon atoms, an alkoxy group, a silyl group, or H; each D2 is an independently selected divalent group having from 1 to 6 carbon atoms, and subscript m is 0 or 1. In certain embodiments, R3 is —CH3. In these or other embodiments, D2 is —CH2—. In specific embodiments, each R4 is H2C═C(CH3)CH2—.
Subscript i is >1, such as 2, 3, 4, 5, 6, etc. Generally, the polyester compound comprises an R4 at each terminus of Y, such that subscript i corresponds to the valency of Y, which is at least 2, but may be 3, 4, 5, or higher depending on the branching thereof.
Each Y is a polyester moiety comprising at least one polyester group, such as any of the polyester groups described above, or derivatives thereof. For example, polyesters produced by known methods may be readily functionalized with unsaturated group functionality to give the polyester compound. Such polyesters are commercially available.
As introduced above, the endcapping organosilicon compound utilized in the method forms the silicone moiety X of formulas (I) and (II) above. As such, the endcapping organosilicon compound may be any organosilicon compound suitable for forming the silicone-polyester copolymer, as understood in the art. Typically, the endcapping organosilicon compound is an organohydrogensiloxane compound including at least one silicon-bonded hydrogen atom. The silicon-bonded hydrogen atom of the organohydrogensiloxane compound reacts with the unsaturated group R4 of the polyester compound via a hydrosilylation reaction in the presence of the hydrosilylation catalyst utilized in the method.
In certain embodiments, the endcapping organosilicon compound is an organohydrogensiloxane compound having one of formulas (Ill) and (IV):
wherein each R1, R2, D1, subscript a, subscript b, subscript e, subscript f, subscript t, and subscript u are as defined above.
As readily understood in the art, the organohydrogensiloxane of formula (III) results in the siloxane moieties of formula (I) in the silicone-polyester copolymer, and the organohydrogensiloxane of formula (IV) results in the siloxane moiety of formula (II) in the silicone-polyester copolymer.
Organohydrogensiloxane compounds of formulas (Ill) and (IV)) can be made via any suitable technique. The organohydrogensiloxane may be prepared in accordance with the methods disclosed in U.S. Provisional Pat. Appln. Nos. 62/524,637, 62/524,636, and 62/524,639, the subject matter of which are incorporated by reference herein.
The chain extending organosilicon compound is optional. When utilized, the chain extending organosilicon compound is typically an organohydrogensiloxane having at least 2 terminal silicon-bonded H atoms. However, the chain extending organosilicon compound may be branched, and have 3, 4, or more terminal silicon-bonded H atoms. For example, the chain extending organosilicon compound may have one of the following formulas:
wherein Z′ is a siloxane moiety and each R1 is as defined above. As such, the chain extending organosilicon compound typically comprises a linear silicon hydride functional organosilicon compound, a branched silicon hydride functional organosilicon compound, or both.
In some embodiments, the chain extending organosilicon compound comprises a siloxane moiety Z′ of formula [R1h′SiO(4−h′)/2]d′, wherein subscript d′ is from 1 to 1000, subscript h′ is independently selected from 0 to 2 in each moiety indicated by subscript d′, and R1 is as defined above. In such embodiments, the chain extending organosilicon compound typically comprises hydrides bonded to terminal silicon atoms of the siloxane moiety Z′, terminal silyl groups having silicon-bonded H atoms, or a combination thereof.
In certain embodiments, the siloxane moiety Z′ is linear, and the chain extending organosilicon compound is an organohydrogensiloxane having the formula:
wherein each R1 is as defined above, and subscript d′ is from 1 to 999.
When Y further comprises at least one moiety in addition to and different from the polyester moiety, the method further comprises reacting a hybridizing compound along with the polyester compound, the endcapping organosilicon compound, and optionally the chain extending organosilicon compound. Specific examples of suitable moieties are set forth above. One of skill in the art readily understands the hybridizing compounds which provide the optional moieties described above. In certain embodiments, the method is free from reacting the hybridizing compound along with the polyester compound, the endcapping organosilicon compound, and optionally the chain extending organosilicon compound. In certain embodiments, the polyester moiety Y comprises a polyester moiety and further comprises an additional moiety other than the polyester moiety by copolymerization of an ester forming monomer and a monomer forming the additional moiety.
The polyester compound, the endcapping organosilicon compound, and optionally the chain extending organosilicon compound and/or the hybridizing compound, may be reacted in any order or combination to give the silicone-polyester copolymer, as understood in the art. In certain embodiments including Z, the method comprises reacting the polyester compound and the chain extending organosilicon compound in the presence of the hydrosilylation catalysts to give a siloxane-polyester compound (i.e., a chain-extended silicone-polyester compound), and reacting the siloxane-polyester compound and the endcapping organosilicon compound in the presence of a hydrosilylation catalyst to give the silicone-polyester copolymer. The siloxane-polyester compound may be prepared by any suitable technique. Alternatively, in certain embodiments, the siloxane-polyester copolymer is prepared by reacting the polyester compound having two terminal unsaturated groups and the chain extending organosilicon compound in the presence of a hydrosilylation catalyst to give the siloxane-polyester copolymer.
The siloxane-polyester compound, if formed and utilized in such embodiments, forms a portion of the silicone-polyester copolymer having the formula [ZjYo]c, where Z, Y, subscript c, and subscript j, and subscript o are defined above. For example, when polyester moieties Y and siloxane moieties Z are linear, the siloxane-polyester compound may have the formula:
where each Y, R1, subscript c, and subscript d are as defined above. Thus, the siloxane-polyester compound utilized may be selected based on the desired structure of the silicone-polyester copolymer, e.g. based on molecular weight, the particular structure of (i.e., units within) each Y, the degree of polymerization of the siloxane units represented by subscript d, etc.
In certain embodiments, the siloxane-polyester compound has the formula:
In such embodiments, each Y1 and R1 is as defined above, and subscript c is typically from 1 to 150, such as from 1 to 100, alternatively from 1 to 50, alternatively from 1 to 25, alternatively from 1 to 10, and alternatively from 1 to 5. Typically, each subscript d is from 1 to 1000, such as from 1 to 500, alternatively from 1 to 300, alternatively from 1 to 100, alternatively from 1 to 50, alternatively from 1 to 10, in each moiety indicated by subscript c.
The polyester compound and the chain extending organosilicon compound, if utilized, are typically reacted in a molar ratio of from 1.001:1 to 2:1; alternatively from 1.4:1 to 1.7:1; alternatively from 1.05:1 to 1.5:1; alternatively from 1.1:1 to 1.2:1; alternatively from 1.2:1 to 1.5:1. The siloxane-polyester compound is typically formed by the molar ratio of the polyester compound and the chain extending organosilicon compound to reach a desired value of subscript c.
The silicone-polyester compound and the endcapping organosilicon compound are typically reacted in a molar ratio between unsaturated groups of the silicone-polyester and silicon hydride groups of the endcapping organosilicon compound of from 1.5:1 to 1:2.5, alternatively from 1.4:1 to 1:2, alternatively from 1.3:1 to 1:1.5, alternatively from 1.2:1 to 1:1.2, alternatively from 1.1:1 to 1:1.1, alternatively from 1.1:1 to 1:1. When the silicone-polyester is difunctional, the silicone-polyester copolymer is typically formed by a 1:2 molar ratio of the silicone-polyester compound and the endcapping organosilicon compound, although a molar excess of one relative to the other may be utilized.
In certain embodiments, the method comprises reacting the polyester compound and the endcapping organosilicon compound in the presence of the hydrosilylation catalyst to give an endcapped silicone-polyester compound, and reacting the endcapped silicone-polyester compound and the chain extending organosilicon compound in the presence of the hydrosilylation catalyst to give the silicone-polyester copolymer. In these or other embodiments, the method comprises reacting at least some of the polyester compound and some of the endcapping organosilicon compound to give the endcapped silicone-polyester compound, and also reacting at least some of the polyester compound and some of the chain extending organosilicon compound to give the siloxane-polyester compound, as each described above.
The hydrosilylation-reaction catalyst is not limited and may be any known hydrosilylation-reaction catalyst for catalyzing hydrosilylation reactions. Combinations of different hydrosilylation-reaction catalysts may be utilized.
In certain embodiments, the hydrosilylation-reaction catalyst comprises a Group VIII to Group XI transition metal. Group VIII to Group XI transition metals refer to the modern IUPAC nomenclature. Group VIII transition metals are iron (Fe), ruthenium (Ru), osmium (Os), and hassium (Hs); Group IX transition metals are cobalt (Co), rhodium (Rh), and iridium (Ir); Group X transition metals are nickel (Ni), palladium (Pd), and platinum (Pt); and Group XI transition metals are copper (Cu), silver (Ag), and gold (Au). Combinations thereof, complexes thereof (e.g. organometallic complexes), and other forms of such metals may be utilized as the hydrosilylation-reaction catalyst.
Additional examples of catalysts suitable for the hydrosilylation-reaction catalyst include rhenium (Re), molybdenum (Mo), Group IV transition metals (i.e., titanium (Ti), zirconium (Zr), and/or hafnium (Hf)), lanthanides, actinides, and Group I and II metal complexes (e.g. those comprising calcium (Ca), potassium (K), strontium (Sr), etc.). Combinations thereof, complexes thereof (e.g. organometallic complexes), and other forms of such metals may be utilized as the hydrosilylation-reaction catalyst.
The hydrosilylation-reaction catalyst may be in any suitable form. For example, the hydrosilylation-reaction catalyst may be a solid, examples of which include platinum-based catalysts, palladium-based catalysts, and similar noble metal-based catalysts, and also nickel-based catalysts. Specific examples thereof include nickel, palladium, platinum, rhodium, cobalt, and similar elements, and also platinum-palladium, nickel-copper-chromium, nickel-copper-zinc, nickel-tungsten, nickel-molybdenum, and similar catalysts comprising combinations of a plurality of metals. Additional examples of solid catalysts include Cu—Cr, Cu—Zn, Cu—Si, Cu—Fe—Al, Cu—Zn—Ti, and similar copper-containing catalysts, and the like.
The hydrosilylation-reaction catalyst may be in or on a solid carrier. Examples of carriers include activated carbons, silicas, silica aluminas, aluminas, zeolites and other inorganic powders/particles (e.g. sodium sulphate), and the like. The hydrosilylation-reaction catalyst may also be disposed in a vehicle, e.g. a solvent which solubilizes the hydrosilylation-reaction catalyst, alternatively a vehicle which merely carries, but does not solubilize, the hydrosilylation-reaction catalyst. Such vehicles are known in the art.
In specific embodiments, the hydrosilylation-reaction catalyst comprises platinum. In these embodiments, the hydrosilylation-reaction catalyst is exemplified by, for example, platinum black, compounds such as chloroplatinic acid, chloroplatinic acid hexahydrate, a reaction product of chloroplatinic acid and a monohydric alcohol, platinum bis(ethylacetoacetate), platinum bis(acetylacetonate), platinum chloride, and complexes of such compounds with olefins or organopolysiloxanes, as well as platinum compounds microencapsulated in a matrix or core-shell type compounds. Microencapsulated hydrosilylation catalysts and methods of their preparation are also known in the art, as exemplified in U.S. Pat. Nos. 4,766,176 and 5,017,654, which are incorporated by reference herein in their entireties.
Complexes of platinum with organopolysiloxanes suitable for use as the hydrosilylation-reaction catalyst include 1,3-diethenyl-1,1,3,3-tetramethyldisiloxane complexes with platinum. These complexes may be microencapsulated in a resin matrix. Alternatively, the hydrosilylation-reaction catalyst may comprise 1,3-diethenyl-1,1,3,3-tetramethyldisiloxane complex with platinum. The hydrosilylation-reaction catalyst may be prepared by a method comprising reacting chloroplatinic acid with an aliphatically unsaturated organosilicon compound such as divinyltetramethyldisiloxane, or alkene-platinum-silyl complexes. Alkene-platinum-silyl complexes may be prepared, for example by mixing 0.015 mole (COD)PtCl2 with 0.045 mole COD and 0.0612 moles HMeSiCl2, where COD represents cyclooctadiene.
Additional examples of suitable hydrosilylation catalysts for component are described in, for example, U.S. Pat. Nos. 3,159,601; 3,220,972; 3,296,291; 3,419,593; 3,516,946; 3,814,730; 3,989,668; 4,784,879; 5,036,117; and 5,175,325; the disclosures of which are incorporated herein by reference in their entireties.
The hydrosilylation catalyst may also, or alternatively, be a photoactivatable hydrosilylation catalyst, which may initiate curing via irradiation and/or heat. The photoactivatable hydrosilylation catalyst can be any hydrosilylation catalyst capable of catalyzing the hydrosilylation reaction, particularly upon exposure to radiation having a wavelength of from 150 to 800 nanometers (nm).
A second method of preparing the silicone-polyester copolymer. This second method comprises reacting an organic compound having one terminal unsaturated group and one terminal hydroxyl group with an endcapping organosilicon compound in the presence of a hydrosilylation catalyst to give a hydroxyl-functional intermediate. This second method further comprises reacting the hydroxyl-functional intermediate with a polyisocyanate to give an isocyanate-functional intermediate, and reacting the isocyanate-functional intermediate and a polyester compound having on average more than one hydroxyl group to give the silicone-polyester copolymer.
The organic compound is not limited and may be any organic compound including one terminal unsaturated group and one terminal hydroxyl group. For example, the organic compound may be an unsaturated alcohol such as allyl alcohol, or a polymer such as a polyether, a polyester, a polycarbonate, etc. The organic compound may introduce further polyester moieties into the silicone-polyester copolymer, or may introduce additional hybridizing segments when the organic compound is something other than a polyester. In certain embodiments, the organic compound is a polyether compound.
In certain embodiments, the polyether compound has the average formula R4O(CnH2nO)w′H, wherein R4 is defined above; each subscript n is independently selected from 2 to 4 in each moiety indicated by subscript w′; and subscript w′ is from 1 to 200. Those skilled in the art readily understand that impurities or alternative groups may exist in the polyether compound which do not substantially diminish the utility or properties of the resulting silicone-polyester copolymer formed therewith. Examples of such impurities or alternative groups include certain molecules of the polyether compound having two terminal unsaturated groups.
In certain embodiments, the polyether compound has the formula —R3O(C2H4O)x′(C3H6O)y′(C4H8O)z′H, wherein R3 is defined above; subscript x′ is from 0 to 200; subscript y′ is from 1 to 200; and subscript z′ is from 0 to 200; and wherein units indicated by subscripts x′, y′ and z′ may be in randomized or block form in the polyether compound. Generally, the polyoxyalkylene moieties indicated by subscripts x′, y′, and z′ are nonreactive when forming the silicone-polyester copolymer. Thus, x′ of the polyether compound becomes x of Y; y′ of the polyether compound becomes y of Y; and z′ of the polyether compound becomes z of Y. As with Y, described above, each of the oxyalkylene units indicated by subscripts x′, y′, and z′ may independently be branched or linear.
In specific embodiments, the polyether compound comprises only oxypropylene units (C3H6O). Representative, non-limiting examples of such polyether compounds include: H2C═CHCH2O[C3H6O]y′H, H2C═CHO[C3H6O]y′H, H2C═C(CH3)CH2O[C3H6O]y′H, HC≡CCH2O[C3H6O]y′H, and HC≡CC(CH3)2O[C3H6O]y′H, where y′ is as defined above. Each oxypropylene unit may independently be of formula —CH2CH2CH2O—, —CH2CHCH3O—, or —CHCH3CH2O—.
The polyether compound may be prepared by, for example, the polymerization of ethylene oxide, propylene oxide, butylene oxide, 1,2-epoxyhexane, 1,2-epoxyoctane, and/or cyclic epoxides, such as cyclohexene oxide or exo-2,3-epoxynorborane.
The polyether compound typically has a number average molecular weight (Mn) of at least about 100. In certain embodiments, the polyether compound has a Mn of at least 200, alternatively at least 300, alternatively at least 400, alternatively at least 500, alternatively at least 600, alternatively at least 700, alternatively at least 1,000, alternatively at least 2,000, alternatively at least 3,000, alternatively at least 5,000, alternatively at least 10,000, alternatively at least 20,000, alternatively up to 30,000. In specific embodiments, the polyether compound has a Mn of from 700 to 900. The number average molecular weight may be readily determined using Gel Permeation Chromatography (GPC) techniques based on polystyrene standards or using end group analysis by nuclear magnetic resonance spectroscopy.
The endcapping organosilicon compound utilized in the method forms the silicone moiety of formulas (I) or (II) above. The endcapping organosilicon compound may be any organosilicon compound suitable for forming the silicone-polyester copolymer, as understood in the art. Typically, the endcapping organosilicon compound is an organohydrogensiloxane compound including at least one silicon-bonded hydrogen atom. The silicon-bonded hydrogen atom of the organohydrogensiloxane compound reacts with R4 of the organic compound via a hydrosilylation reaction to give the hydroxy-functional intermediate.
In certain embodiments, the endcapping organosilicon compound is an organohydrogensiloxane compound having one of formulas (Ill) and (IV) above. Specific examples of suitable hydrosilylation catalysts are also set forth above.
The organic compound and the organosilicon compound are typically reacted in a molar ratio of from 5:1 to 1:5; alternatively from 4:1 to 1:4; alternatively from 3:1 to 1:3; alternatively from 2:1 to 1:2; alternatively to 1.1:1 to 1:1.1. The hydroxy-functional intermediate is typically formed by a 1.2:1 molar ratio of the organic compound and the endcapping organosilicon compound, although a different molar excess of one relative to the other may be utilized.
This second method further comprises reacting the hydroxyl-functional intermediate with a polyisocyanate to give an isocyanate-functional intermediate.
The polyisocyanate is not limited and may be an aliphatic, cycloaliphatic, araliphatic and/or aromatic polyisocyanate. The polyisocyanate advantageously contains at least 2.0 isocyanate groups per molecule. A typical isocyanate functionality of the polyisocyanate is from about 2.0 to about 3.0 or from about 2.0 to about 2.5 isocyanate groups per molecule. However, the polyisocyanate may be utilized as a blend. When the polyisocyanate is utilized as a blend, the polyisocyanate typically has a nominal functionality of at least 1.6, alternatively at least 1.7, alternatively at least 1.8.
In certain embodiments, the polyisocyanate is selected from the group of diphenylmethane diisocyanates (MDIs), polymeric diphenylmethane diisocyanates (pMDIs), toluene diisocyanates (TDIs), butanediisocyanate, hexamethylene diisocyanates (HDIs), isophorone diisocyanates (IPDIs), naphthalene diisocyanates (NDIs), and combinations thereof.
Exemplary polyisocyanates include, for example, m-phenylene diisocyanate, 2,4- and/or 2,6-toluene diisocyanate (TDI), the various isomers of diphenylmethanediisocyanate (MDI), hexamethylene-1,6-diisocyanate, tetramethylene-1,4-diisocyanate, cyclohexane-1,4-diisocyanate, hexahydrotoluene diisocyanate, hydrogenated MDI (H12 MDI), naphthylene-1,5-diisocyanate, methoxyphenyl-2,4-diisocyanate, 4,4′-biphenylene diisocyanate, 3,3′-dimethyoxy-4,4′-biphenyl diisocyanate, 3,3′-dimethyldiphenylmethane-4,4′-diisocyanate, 4,4′,4″-triphenylmethane diisocyanate, polymethylene polyphenylisocyanates, hydrogenated polymethylene polyphenyl polyisocyanates, toluene-2,4,6-triisocyanate and 4,4′-dimethyldiphenylmethane-2,2′,5,5′-tetraisocyanate. The polyisocyanate may be modified to include urea, isocyanurate, uretidinedione, allophonate, biuret, carbodiimide, urethane or other linkages.
In certain embodiments, the polyisocyanate comprises a diisocyanate. For example, the diisocyanate may have formula OCN-D′-NCO, wherein D′ is a divalent linking group. When the diisocyanate comprises MDI, D′ is a methylene diphenyl moiety. However, the diisocyanate need not be symmetrical and the isocyanate functional groups need not be terminal. For example, the diisocyanate may have formula (OCN)2-D′, where D′ is defined above. The isocyanate functional groups may be bonded to the same or different atoms within D′.
In certain embodiments, the polyisocyanate is an isocyanate-terminated prepolymer. The isocyanate-terminated prepolymer is a reaction product of an isocyanate and a polyol and/or a polyamine, as understood in the polyurethane art. The polyisocyanate may be any type of polyisocyanate known to those skilled in the polyurethane art, such as one of the polyisocyanates described above. If employed to make the isocyanate-terminated prepolymer, the polyol is typically selected from the group of ethylene glycol, diethylene glycol, propylene glycol, dipropylene glycol, butane diol, glycerol, trimethylolpropane, triethanolamine, pentaerythritol, sorbitol, and combinations thereof. If employed to make the isocyanate-terminated prepolymer, the polyamine is typically selected from the group of ethylene diamine, toluene diamine, diaminodiphenylmethane and polymethylene polyphenylene polyamines, aminoalcohols, and combinations thereof. Examples of suitable aminoalcohols include ethanolamine, diethanolamine, triethanolamine, and combinations thereof. It is to be appreciated that the isocyanate-terminated prepolymer may be formed from a combination of two or more of the aforementioned polyols and/or polyamines.
The hydroxyl-functional intermediate and the polyisocyanate are typically reacted in a molar ratio of from 5:1 to 1:5; alternatively from 4:1 to 1:4; alternatively from 3:1 to 1:3; alternatively from 2:1 to 1:2; alternatively to 1.1:1 to 1:1.1. The isocyanate-functional intermediate is typically formed by a 1:1 molar ratio of the hydroxyl-functional intermediate and the polyisocyanate, although a molar excess of one relative to the other may be utilized.
In certain embodiments, the hydroxyl-functional intermediate and the polyisocyanate are reacted to form the isocyanate-functional intermediate in the presence of a catalyst. Examples of catalysts include tertiary amines; tin carboxylates; organotin compounds; tertiary phosphines; various metal chelates; metal salts of strong acids, such as ferric chloride, stannic chloride, stannous chloride, antimony trichloride, bismuth nitrate and bismuth chloride, and the like. Tertiary amine and tin catalysts are typical.
Exemplary examples of tertiary amine catalysts include trimethylamine, triethylamine, N-methylmorpholine, N-ethylmorpholine, N,N-dimethylbenzylamine, N,N-dimethylethanolamine, N,N,N′,N′-tetramethyl-1,4-butanediamine, N,N-dimethylpiperazine, 1,4-diazobicyclo-2,2,2-octane, bis(dimethylaminoethyl)ether, bis(2-dimethylaminoethyl) ether, morpholine,4,4′-(oxydi-2,1-ethanediyl)bis, triethylenediamine, pentamethyl diethylene triamine, dimethyl cyclohexyl amine, N-cetyl N,N-dimethyl amine, N-coco-morpholine, N,N-dimethyl aminomethyl N-methyl ethanol amine, N,N,N′-trimethyl-N′-hydroxyethyl bis(aminoethyl) ether, N,N-bis(3-dimethylaminopropyl)N-isopropanolamine, (N,N-dimethyl) amino-ethoxy ethanol, N,N,N′,N′-tetramethyl hexane diamine, 1,8-diazabicyclo-5,4,0-undecene-7, N,N-dimorpholinodiethyl ether, N-methyl imidazole, dimethyl aminopropyl dipropanolamine, bis(dimethylaminopropyl)amino-2-propanol, tetramethylamino bis (propylamine), (dimethyl(aminoethoxyethyl))((dimethyl amine)ethyl)ether, tris(dimethylamino propyl) amine, dicyclohexyl methyl amine, bis(N,N-dimethyl-3-aminopropyl) amine, 1,2-ethylene piperidine and methyl-hydroxyethyl piperazine.
Exemplary examples of tin-containing catalysts include stannous octoate, dibutyl tin diacetate, dibutyl tin dilaurate, dibutyl tin dimercaptide, dialkyl tin dialkylmercapto acids, dibutyl tin oxide, dimethyl tin dimercaptide, dimethyl tin diisooctylmercaptoacetate, dimethyltindineodecanoate, and the like.
The second method further comprises reacting the isocyanate-functional intermediate and a polyester compound having on average more than one hydroxyl group to give the silicone-polyester copolymer. When the silicone-polyester copolymer is formed via the second method, A is typically selected from -D2-O—C(═O)—NH—, and -D2-NH—C(═O)—NH—, where D2 is a divalent group.
As will be understood by one of skill in the art in view of the description herein, the polyester compound utilized in the method forms a portion of the silicone-polyester copolymer corresponding to the polyester moiety Y, and the endcapping organosilicon compound utilized in the method forms a portion of the silicone-polyester copolymer corresponding to the silicone moiety X. In certain embodiments, the method further comprises reacting, along with the polyester compound and the endcapping organosilicon compound, at least one of: (i) a chain extending organosilicon compound and (ii) a hybridizing compound having on average more than one hydroxyl group or amino group. If utilized, the chain extending organosilicon compound utilized in the method forms a portion of the silicone-polyester copolymer corresponding to the siloxane moiety Z. The hybridizing compound, if utilized, becomes part of Y along with the polyester moiety. In certain embodiments, the method is free from the chain extending organosilicon compound and the hybridizing compound. In other embodiments, the method utilizes the chain extending organosilicon compound or the hybridizing compound but not the other. In yet further embodiments, the method utilizes both the chain extending organosilicon compound and the hybridizing compound. When the method utilizes the chain extending organosilicon compound the chain extending organosilicon compound may be any of those set forth above with respect to the first method of preparing the silicone-polyester copolymer, with the only difference between any silicon-bonded hydrogen atoms from the first method are instead silicon-bonded hydroxyl groups, alcohol groups, or aminoalkyl groups in the second method.
Typically, the polyester compound has the formula: Y[OH]i, where subscript i is >1; and Y is polyester moiety comprising at least one polyester group.
Subscript i is >1, such as 2, 3, 4, 5, 6, etc. Generally, the polyester compound comprises a hydroxyl group at each terminus of Y, such that subscript i corresponds to the valency of Y, which is at least 2, but may be 3, 4, 5, or higher depending on the branching thereof.
Each Y is a polyester moiety comprising at least one polyester group, such as any of the polyester groups described above, or derivatives thereof. For example, polyesters produced by known methods may be readily functionalized with hydroxyl functionality to give the polyester compound. Such polyesters are commercially available.
Other methods of preparing the silicone-polyester copolymer can be readily envisaged by one of skill in the art based on modifications or replacements of functional groups and reaction schemes.
For example, in one embodiment, the silicone-polyester copolymer can be prepared by reacting a polysiloxane with more than one hydroxyl group and a polyisocyanate to give an isocyanate-functional polysiloxane. The isocyanate-functional polysiloxane can be reacted with the hydroxyl-functional intermediate described above, and the reaction product thereof can be reacted with and then react with a polyester compound with more than one hydroxyl group, optionally in the presence of any further amount of polyisocyanate, hydroxyl functional polysiloxane, or isocyanate-functional polysiloxane.
In a second embodiment, the silicone-polyester copolymer can be prepared by reacting a polysiloxane with more than one hydroxyl group and a polyisocyanate to give an isocyanate-functional polysiloxane. The isocyanate-functional polysiloxane can be reacted with a polyester compound having more than one hydroxyl group and the isocyanate-functional intermediate described above, optionally in the presence of any further amount of polyisocyanate or organic polyhydroxyl compounds.
In a third embodiment, the silicone-polyester copolymer can be prepared by reacting a polysiloxane with more than one hydroxyl group, a hydroxyl-functional polyester compound, and a polyisocyanate to give a isocyanate-functional prepolymer. The isocyanate-functional pre-polymer may be reacted with the hydroxyl-functional intermediate described above.
In a fourth embodiment, the silicone-polyester copolymer can be prepared by reacting a polysiloxane with more than one amino group and a polyisocyanate to give an isocyanate-functional polysiloxane. The isocyanate-functional polysiloxane may be reacted with the hydroxyl-functional intermediate described above to give a further intermediate. The further intermediate can be reacted with a polyester compound having more than one isocyanate-reactive group, optionally in the presence of any further amount of polyisocyanate, amino-functional polysiloxane, or isocyanate-functional polysiloxane.
In a fifth embodiment, the silicone-polyester copolymer can be prepared by reacting a polysiloxane with more than one amino group and a polyisocyanate to give an isocyanate-functional polysiloxane. The isocyanate-functional polysiloxane may be reacted with a polyester compound having more than one isocyanate-reactive group and the isocyanate-functional intermediate described above, optionally in the presence of any further amount of polyisocyanate organic polyhydroxyl compounds.
In a sixth embodiment, the silicone-polyester copolymer can be prepared by mixing an amino-functional polysiloxane and an amino-functional polyester compound to give a mixture. The mixture can be reacted with polyisocyanate to give an isocyanate-functional prepolymer. The isocyanate-functional prepolymer can be reacted with the hydroxyl-functional intermediate described above.
In a seventh embodiment, the silicone-polyester copolymer can be prepared by initiating polymerization of caprolactone via a polysiloxane containing more than one hydroxyl group, optionally in the presence of a catalyst such as an organometal catalyst, an acid, or a base, to give a hydroxyl-functional copolymer. The hydroxyl-functional copolymer can be reacted with the isocyanate-functional intermediate described above.
A sealant comprising the silicone-polyester copolymer is also provided. More specifically, the sealant comprises: (I) a copolymer comprising the silicone-polyester copolymer; and (II) a condensation reaction catalyst.
The (II) condensation reaction catalyst is not limited and, in some embodiments, is exemplified by tin catalysts, titanium catalysts, zirconate catalysts, and zirconium catalysts.
General examples of suitable tin catalysts include organotin compounds where the valence of the tin is either +4 or +2 (e.g. tin (IV) compounds and/or tin (II) compounds). Specific examples of tin (IV) compounds include stannic salts of carboxylic acids such as dibutyl tin dilaurate, dimethyl tin dilaurate, di-(n-butyl)tin bis-ketonate, dibutyl tin diacetate, dibutyl tin maleate, dibutyl tin diacetylacetonate, dibutyl tin dimethoxide, carbomethoxyphenyl tin tris-uberate, dibutyl tin dioctanoate, dibutyl tin diformate, isobutyl tin triceroate, dimethyl tin dibutyrate, dimethyl tin di-neodeconoate, dibutyl tin di-neodeconoate, triethyl tin tartrate, dibutyl tin dibenzoate, butyltintri-2-ethylhexanoate, dioctyl tin diacetate, tin octylate, tin oleate, tin butyrate, tin naphthenate, dimethyl tin dichloride, a combination thereof, and/or a partial hydrolysis product thereof. Additional examples of tin (IV) compounds are known in the art and are commercially available, such as Metatin® 740 and Fascat® 4202 from Acima Specialty Chemicals of Switzerland, Europe, which is a business unit of The Dow Chemical Company, as well as Formrez® UL-28 from Galata Chemicals of Hahnville, La. Specific examples of tin (II) compounds include tin (II) salts of organic carboxylic acids such as tin (II) diacetate, tin (II) dioctanoate, tin (II) diethylhexanoate, tin (II) dilaurate, stannous salts of carboxylic acids such as stannous octoate, stannous oleate, stannous acetate, stannous laurate, stannous stearate, stannous naphthanate, stannous hexanoate, stannous succinate, stannous caprylate, and a combination thereof. Examples of suitable titanium catalysts include titanium esters such as tetra-n-butyltitanate tetraisopropyltitanate, tetra-2-ethylhexyltitanate, tetraphenyltitanate, triethanolamine titanate, organosiloxytitanium compounds, and dicarbonyl titanium compounds, such as titanium ethyl acetoacetate, diisopropoxydi(ethoxyacetoacetyl) titanium and bis(acetoacetonyl)-diisopropoxy titanium (IV). Many of these titanium catalysts are commercially available, such as Tyzor™ DC, Tyzor™ TnBT, and Tyzor™ 9000 from Doft Ketal Specialty Catalysts LLC of Houston, Tex. In certain embodiments, the (II) condensation reaction catalyst is a titanium catalyst, such as one of those exemplified above, e.g. where the sealant is or may be formulated as a room temperature vulcanizing sealant composition. The amount of the (II) condensation reaction catalyst present in the sealant depends on various factors (e.g. the amount and/or type of the (I) copolymer, the types and/or amounts of any additional materials present in the sealant, etc.), and may be readily determined by one of skill in the art. Typically, the sealant comprises the (II) condensation reaction catalyst in an amount of from 0.2 to 6, alternatively from 0.5 to 3, parts by weight based on the total weight of the (I) copolymer present in the sealant.
In some embodiments, the sealant further comprises one or more additives. Examples of suitable additives that may be present in the sealant include fillers, treating agents (e.g. filler treating agents), cross-linkers, adhesion promotors, surface modifiers, drying agents, extenders, biocides, flame retardants, plasticizers, end-blockers, binders, anti-aging additives, water release agents, pigments, rheology modifiers, carriers, tackifying agents, corrosion inhibitors, catalyst inhibitors, viscosity modifiers, UV absorbers, anti-oxidants, light-stabilizers, and the like, as well as combinations thereof.
In certain embodiments, the sealant includes a filler. The filler may be or comprise a reinforcing filler, an extending filler, a conductive filler (e.g., electrically conductive, thermally conductive, or both), or the like, or a combination thereof. Examples of suitable reinforcing fillers include precipitated calcium carbonates and reinforcing silica fillers such as fume silica, silica aerogel, silica xerogel, and precipitated silica. Specific suitable precipitated calcium carbonates include Winnofil® SPM from Solvay and Ultrapflex® and Ultrapflex® 100 from Specialty Minerals, Inc. Examples of fumed silicas are known in the art and are commercially available, such as those sold under the name CAB-O-SIL by Cabot Corporation of Massachusetts, U.S.A. Examples of suitable extending fillers include crushed quartz, aluminum oxide, magnesium oxide, calcium carbonate such as ground calcium carbonate, precipitated calcium carbonate, zinc oxide, talc, diatomaceous earth, iron oxide, clays, mica, chalk, titanium dioxide, zirconia, sand, carbon black, graphite, or a combination thereof. Examples of extending fillers are known in the art and are commercially available, including ground quartz sold under the name MIN-U-SIL by U.S. Silica of Berkeley Springs, W. Va. Other examples of commercially available extending fillers include calcium carbonates sold under the name CS-11 from Imerys, G3T from Huber, Pfinyl 402 from Specialty Minerals, Inc. and Omyacarb 2T from Omya. The amount of the filler present in the sealant depends on various factors (e.g. the amount and/or type of the (I) copolymer, the types and/or amounts of any additional materials present in the sealant, etc.), and may be readily determined by one of skill in the art. The exact amount of the filler employed in a specific implementation of the sealant will also depend on whether more than one type of filler is utilized. Typically, where present, the sealant comprises the filler in an amount of from 0.1 to 95, alternatively from 1 to 60, alternatively from 1 to 20 wt. %, based on the weight of the sealant.
In particular embodiments, the sealant comprises a treating agent. The treating agent is not limited, and may be any treating agent suitable for use in treating (e.g. surface treating) an additive of the sealant, such as the filler and other additives (e.g. physical drying agents, flame retardants, pigments, and/or water release agents) which may be present in the sealant. More specifically, solid and/or particulate additives may be treated with the treating agent before being added to the sealant. Alternatively, or in addition, solid and/or particulate additives may be treated with the treating agent in situ. General examples of suitable treating agents include those comprising an alkoxysilane, an alkoxy-functional oligosiloxane, a cyclic polyorganosiloxane, a hydroxyl-functional oligosiloxane (e.g. dimethyl siloxane or methyl phenyl siloxane), a fatty acid (e.g. a stearate, such as calcium stearate), and the like, as well as combinations thereof. Specific examples of treating agents include alkylthiols, fatty acids, titanates, titanate coupling agents, zirconate coupling agents, and the like, as well as combinations thereof.
In some embodiments, the treating agent is or comprises an organosilicon filler treating agent. Examples of such organosilicon filler treating agents include compositions suitable for treating silica fillers, such as organochlorosilanes, organosiloxanes, organodisilazanes (e.g. hexaalkyl disilazane), and organoalkoxysilanes (e.g. CH3Si(OCH3)3, C6H13Si(OCH3)3, C8H17Si(OC2H5)3, C10H21Si(OCH3)3, C12H25Si(OCH3)3, C14H29Si(OC2H5)3, C6H5CH2CH2Si(OCH3)3, etc.), and the like. In these or other embodiments, the treating agent is or comprises an alkoxysilane having the formula (X): R10ASi(OR11)4−A. In formula (X), subscript A is an integer of from 1 to 3, such as 1, 2, or 3, Each R10 is an independently selected monovalent organic group, such as a monovalent hydrocarbon group having from 1 to 50 carbon atoms, alternatively from 8 to 30 carbon atoms, alternatively from 8 to 18 carbon atoms, alternatively from 1 to 5 carbon atoms. R10 may be saturated or unsaturated, and branched or unbranched. Alternatively, R10 may be saturated and unbranched. R10 is exemplified by alkyl groups such as methyl, ethyl, hexyl, octyl, dodecyl, tetradecyl, hexadecyl, and octadecyl; alkenyl groups such as vinyl; and aromatic groups such as benzyl and phenylethyl. Each R11 is an independently selected saturated hydrocarbon group having from 1 to 4 carbon atoms, alternatively from 1 to 2 carbon atoms. Specific examples of organosilicon filler treating agents also include hexyltrimethoxysilane, octyltriethoxysilane, decyltrimethoxysilane, dodecyltrimethoxysilane, tetradecyltrimethoxysilane, phenylethyltrimethoxysilane, octadecyltrimethoxysilane, octadecyltriethoxysilane, and combinations thereof.
In some embodiments, the treating agent is or comprises an alkoxy-functional oligosiloxanes. Examples of suitable alkoxy-functional oligosiloxanes include those having the general formula (XI): (R12O)BSi(OSiR132R14)(4−B). In formula (XI), subscript B is 1, 2 or 3. In specific embodiments, subscript B is 3. Each R12 is an independently selected alkyl group. Each R13 is an independently selected unsaturated monovalent hydrocarbon group having from 1 to 10 carbon atoms. Each R14 is an independently selected unsaturated monovalent hydrocarbon group having at least 10 carbon atoms.
In certain embodiments, the treating agent is or comprises a polyorganosiloxane capable of hydrogen bonding. Such treating agents utilize multiple hydrogen bonds, which are clustered and/or dispersed, as a means to tether a compatibilization moiety to a surface of the sealant component to be treated (e.g. the filler). Suitable polyorganosiloxanes capable of hydrogen bonding have an average, per molecule, of at least one silicon-bonded group capable of hydrogen bonding, which is typically selected from organic groups having multiple hydroxyl functionalities, organic groups having at least one amino functional group, and combinations thereof. In other words, the polyorganosiloxane capable of hydrogen bonding typically utilizes hydrogen bonding as a primary mode of attachment to the filler. As such, in some embodiments, the polyorganosiloxane is incapable of forming covalent bonds with the filler. The polyorganosiloxane may be free of condensable silyl groups (e.g. silicon bonded alkoxy groups, silazanes, and silanols). Examples of suitable polyorganosiloxanes for use in or as the sealant include saccharide-siloxane polymers, amino-functional polyorganosiloxanes, and a combination thereof. In specific embodiments, the sealant comprises a polyorganosiloxane comprising a saccharide-siloxane polymer.
The amount of the treating agent present in the sealant depends on various factors (e.g. the amount and/or type of the (I) copolymer, the types and/or amounts of any additional materials present in the sealant (such as those treated with the treating agent), etc.), and may be readily determined by one of skill in the art. Typically, the amount of the treating agent varies depending on the type of treating agent selected, the type and/or amount of particulates to be treated, and whether the particulates are treated before being added to the sealant or in situ. Typically, where present, the sealant comprises the treating agent in an amount of from 0.01 to 20, alternatively from 0.1 to 15, alternatively from 0.5 to 5 wt. %, based on the weight of the sealant.
In some embodiments, the sealant comprises a polymer additive, such as crosslinkers, chain extenders, plasticizers, end-blockers, and the like, or combinations thereof. In general, suitable polymer additives include compounds having functional groups that are reactive with functional groups present in the (I) copolymer of the sealant, or with functional groups present in another polymer additive that has been reacted therewith. Certain polymer additives may be named based on an intended function (e.g. to cross-link, to chain-extend, to end-block, etc.). However, it is to be appreciated that there may be overlap in functions between types of polymer additives because certain polymer additives described herein may have more than one function as will be readily appreciated by one of skill in the art. For examples, suitable crosslinkers include those comprising a compound having an average, per molecule, of two or more substituents reactive with alkoxy groups present within the (I) copolymer, and suitable chain extenders include those comprising a compound having an average, per molecule, of two substituents reactive with alkoxy groups present within the (I) copolymer or with groups present within another polymer additive reacted with the (I) copolymer. Accordingly, as is understood by those of skill in the art, various compounds may be used as a cross-linker and/or a chain extender. Similarly, various plasticizers, which are exemplified by the particular plasticizers described below, may also be interchangeably utilized in or as a crosslinker and/or a chain extender of the sealant.
In some embodiments, the sealant comprises a crosslinker. Some examples of suitable crosslinkers include silane crosslinkers having hydrolyzable groups, or partial or full hydrolysis products thereof. Examples of such silane crosslinkers include those including a silicon compound having the general formula (XII): R15CSi(R16)(4−C), where each R15 is an independently selected monovalent hydrocarbon group, such as an alkyl group; each R16 is a hydrolyzable substituent, for example, a halogen atom, an acetamido group, an acyloxy group such as acetoxy, an alkoxy group, an amido group, an amino group, an aminoxy group, a hydroxyl group, an oximo group, a ketoximo group, or a methylacetamido group; and subscript C is 0-3, such as 0, 1, 2, or 3. Typically, subscript C has an average value greater than 2. Alternatively, subscript C may have a value ranging from 3 to 4. Typically, each R16 is independently selected from hydroxyl, alkoxy, acetoxy, amide, or oxime. Specific examples of suitable silane crosslinkers include methyldiacetoxymethoxysilane, methylacetoxydimethoxysilane, vinyldiacetoxymethoxysilane, vinylacetoxydimethoxysilane, methyldiacetoxyethoxysilane, metylacetoxydiethoxysilane, and combinations thereof.
In some embodiments, the crosslinker includes an acyloxysilane, an alkoxysilane, a ketoximosilane, an oximosilane, or the like, or combinations thereof.
Examples of suitable acetoxysilane crosslinkers include tetraacetoxysilanes, organotriacetoxysilanes, diorganodiacetoxysilanes, and combinations thereof. The acetoxysilane may contain alkyl groups such as methyl, ethyl, propyl, isopropyl, butyl, and tertiary butyl; alkenyl groups such as vinyl, allyl, or hexenyl; aryl groups such as phenyl, tolyl, or xylyl; aralkyl groups such as benzyl or 2-phenylethyl; and fluorinated alkyl groups such as 3,3,3-trifluoropropyl. Exemplary acetoxysilanes include tetraacetoxysilane, methyltriacetoxysilane, ethyltriacetoxysilane, vinyltriacetoxysilane, propyltriacetoxysilane, butyltriacetoxysilane, phenyltriacetoxysilane, octyltriacetoxysilane, dimethyldiacetoxysilane, phenylmethyldiacetoxysilane, vinylmethyldiacetoxysilane, diphenyl diacetoxysilane, tetraacetoxysilane, and combinations thereof. In some embodiments, the crosslinker comprises organotriacetoxysilanes, for example mixtures comprising methyltriacetoxysilane and ethyltriacetoxysilane.
Examples of suitable aminofunctional alkoxysilanes suitable for use in or as the crosslinker are exemplified by H2N(CH2)2Si(OCH3)3, H2N(CH2)2Si(OCH2CH3)3, H2N(CH2)3Si(OCH3)3, H2N(CH2)3Si(OCH2CH3)3, CH3NH(CH2)3Si(OCH3)3, CH3NH(CH2)3Si(OCH2CH3)3, CH3NH(CH2)5Si(OCH3)3, CH3NH(CH2)5Si(OCH2CH3)3, H2N(CH2)2NH(CH2)3Si(OCH3)3, H2N(CH2)2NH(CH2)3Si(OCH2CH3)3, CH3NH(CH2)2NH(CH2)3Si(OCH3)3, CH3NH(CH2)2NH(CH2)3Si(OCH2CH3)3, C4H9NH(CH2)2NH(CH2)3Si(OCH3)3, C4H9NH(CH2)2NH(CH2)3Si(OCH2CH3)3, H2N(CH2)2SiCH3(OCH3)2, H2N(CH2)2SiCH3(OCH2CH3)2, H2N(CH2)3SiCH3(OCH3)2, H2N(CH2)3SiCH3(OCH2CH3)2, CH3NH(CH2)3SiCH3(OCH3)2, CH3NH(CH2)3SiCH3(OCH2CH3)2, CH3NH(CH2)5SiCH3(OCH3)2, CH3NH(CH2)5SiCH3(OCH2CH3)2, H2N(CH2)2NH(CH2)3SiCH3(OCH3)2, H2N(CH2)2NH(CH2)3SiCH3(OCH2CH3)2, CH3NH(CH2)2NH(CH2)3SiCH3(OCH3)2, CH3NH(CH2)2NH(CH2)3SiCH3(OCH2CH3)2, C4H9NH(CH2)2NH(CH2)3SiCH3(OCH3)2, C4H9NH(CH2)2NH(CH2)3SiCH3(OCH2CH3)2, and combinations thereof.
Examples of suitable oximosilane crosslinkers include alkyltrioximosilanes such as methyltrioximosilane, ethyltrioximosilane, propyltrioximosilane, and butyltrioximosilane; alkoxytrioximosilanes such as methoxytrioximosilane, ethoxytrioximosilane, and propoxytrioximosilane; or alkenyltrioximosilanes such as propenyltrioximosilane or butenyltrioximosilane; alkenyloximosilanes such as vinyloximosilane; alkenylalkyldioximosilanes such as vinyl methyl dioximosilane, vinyl ethyldioximosilane, vinyl methyldioximosilane, or vinylethyldioximosilane; or combinations thereof.
Examples of suitable ketoximosilanes crosslinkers include methyl tris(dimethylketoximo)silane, methyl tris(methylethylketoximo)silane, methyl tris(methylpropylketoximo)silane, methyl tris(methylisobutylketoximo)silane, ethyl tris(dimethylketoximo)silane, ethyl tris(methylethylketoximo)silane, ethyl tris(methylpropylketoximo)silane, ethyl tris(methylisobutylketoximo)silane, vinyl tris(dimethylketoximo)silane, vinyl tris(methylethylketoximo)silane, vinyl tris(methylpropylketoximo)silane, vinyl tris(methylisobutylketoximo)silane, tetrakis(dimethylketoximo)silane, tetrakis(methylethylketoximo)silane, tetrakis(methylpropylketoximo)silane, tetrakis(methylisobutylketoximo)silane, methylbis(dimethylketoximo)silane, methylbis(cyclohexylketoximo)silane, triethoxy(ethylmethylketoxime)silane, diethoxydi(ethylmethylketoxime)silane, ethoxytri(ethylmethylketoxime)silane, methylvinylbis(methylisobutylketoximo)silane, or a combination thereof.
In certain embodiments, the crosslinker comprises an alkoxysilane exemplified by a dialkoxysilane, such as a dialkyldialkoxysilane; a trialkoxysilane, such as an alkyltrialkoxysilane; a tetraalkoxysilane; partial or full hydrolysis products thereof; or a combination thereof. Examples of suitable trialkoxysilanes include methyltrimethoxysilane, vinyltrimethoxysilane, methyltriethoxysilane, ethyltrimethoxysilane, ethyltriethoxysilane, isobutyltrimethoxysilane, isobutyltriethoxysilane, and combinations thereof. Examples of suitable tetraalkoxysilanes include tetraethoxysilane. In specific embodiments, the crosslinker comprises, alternatively is, methyltrimethoxysilane.
In certain embodiments, the crosslinker is polymeric. For example, the crosslinker may comprise a disilane such as bis(triethoxysilyl)hexane), 1,4-bis[trimethoxysilyl(ethyl)]benzene, bis[3-(triethoxysilyl)propyl] tetrasulfide, bis(trimethoxysilyl)hexane), bis(triethoxysilyl)ethane, bis(trimethoxysilyl)ethane, and combinations thereof. In these or other embodiments, the crosslinker may be one single crosslinker or a combination comprising two or more crosslinkers that differ from one another, e.g. based on hydrolyzable substituents and other organic groups bonded to silicon, and, when a polymeric crosslinker is used, siloxane units, structure, molecular weight, sequence, etc.
The amount of the crosslinker present in the sealant depends on various factors (e.g. the amount and/or type of the (I) copolymer, the types and/or amounts of any additional materials present in the sealant (such as other polymer additives), the type of crosslinker utilized, etc.), and may be readily determined by one of skill in the art. In general, where present, the sealant comprises the crosslinker in an amount of from 0.5 to 15, alternatively from 1 to 10, alternatively from 3 to 10 wt. %, based on the weight of the (I) copolymer.
In some embodiments, the sealant comprises a plasticizer. Examples of suitable plasticizers include organic plasticizers, such as those comprising a carboxylic acid ester (e.g. esters), a phthalate (e.g. phthalates), a carboxylate (e.g. carboxylates), an adipate (e.g. adipates), or a combination thereof. Specific examples of suitable organic plasticizers include bis(2-ethylhexyl)terephthalate, bis(2-ethylhexyl)-1,4-benzenedicarboxylate, 2-ethylhexyl methyl-1,4-benzenedicarboxylate, 1,2 cyclohexanedicarboxylic acid, dinonyl ester (branched and linear), bis(2-propylheptyl)phthalate, diisononyl adipate, and combinations thereof.
In certain embodiments, the plasticizer is an ester having an average, per molecule, of at least one group of formula:
where R17 represents a hydrogen atom or a monovalent organic group (e.g. a branched or linear monovalent hydrocarbon group, such as an alkyl group of 4 to 15 carbon atoms, alternatively 9 to 12 carbon atoms). In these or other embodiments, the plasticizer has an average, per molecule, of at least two groups of the formula above each bonded to carbon atoms in a cyclic hydrocarbon. In such instances, the plasticizer may have general formula:
In this formula, D is a carbocyclic group having 3 or more carbon atoms, alternatively 3 to 15 carbon atoms, which may be unsaturated, saturated, or aromatic. Subscript E is from 1 to 12. Each R18 is independently a branched or linear monovalent hydrocarbon group, such as an alkyl group of 4 to 15 carbon atoms (e.g. an alkyl group such as methyl, ethyl, butyl, etc.). Each R19 is independently a hydrogen atom or a branched or linear, substituted or unsubstituted, monovalent organic group. For example, in some embodiments, at least one R19 is a moiety comprising an ester functional group.
In specific embodiments, the sealant comprises a polymeric plasticizer. Examples of polymeric plasticizers include alkenyl polymers (e.g. those obtained by polymerizing vinyl or allyl monomers via various methods); polyalkylene glycol esters (e.g. diethylene glycol dibenzoates, triethylene glycols, dibenzoate pentaerythritol esters, etc.); polyester plasticizers (e.g. those obtained from dibasic acids such as sebacic acid, adipic acid, azelaic acid, phthalic acid, etc. and dihydric alcohols such as ethylene glycol, diethylene glycol, triethylene glycol, propylene glycol, dipropylene glycol, etc.); polyesters including polyester polyols each having a molecular weight of not less than 500 (e.g. polyethylene glycols, polypropylene glycols, polytetramethylene glycols, etc.); polystyrenes (e.g. polystyrene, poly-alpha-methylstyrene, etc.); polybutenes and polybutadienes (e.g. polyisobutylene, butadiene acrylonitrile, etc.); and polychloroprenes. In various embodiments, a low molecular weight plasticizer and a higher molecular weight polymeric plasticizer may present in the sealant in combination.
Specific plasticizers are known in the art and are commercially available. Such plasticizers may be present in the sealant alone or in combination. For example, the plasticizer may comprise a phthalate, such as: a dialkyl phthalate such as dibutyl phthalate (Eastman™ DBP Plasticizer), diheptyl phthalate, diisononyl phthalate, di(2-ethylhexyl) phthalate, or diisodecyl phthalate (DIDP), bis(2-propylheptyl) phthalate (BASF Palatinol® DPHP), di(2-ethylhexyl) phthalate (Eastman™ DOP Plasticizer), dimethyl phthalate (Eastman™ DMP Plasticizer); diethyl phthalate (Eastman™ DMP Plasticizer); butyl benzyl phthalate, and bis(2-ethylhexyl)terephthalate (Eastman™ 425 Plasticizer); a dicarboxylate such as Benzyl, C7-C9 linear and branched alkyl esters, 1, 2, benzene dicarboxylic acid (Ferro SANTICIZER® 261A), 1,2,4-benzenetricarboxylic acid (BASF Palatinol® TO™-I), bis(2-ethylhexyl)-1,4-benzenedicarboxylate (Eastman™ 168 Plasticizer); 2-ethylhexyl methyl-1,4-benzenedicarboxylate; 1,2 cyclohexanedicarboxylic acid, dinonyl ester, branched and linear (BASF Hexamoll®DINCH); diisononyl adipate; trimellitates such as trioctyl trimellitate (Eastman™ TOTM Plasticizer); triethylene glycol bis(2-ethylhexanoate) (Eastman™ TEG-EH Plasticizer); triacetin (Eastman™ Triacetin); nonaromatic dibasic acid esters such as dioctyl adipate, bis(2-ethylhexyl)adipate (Eastman™ DOA Plasticizer and Eastman™ DOA Plasticizer, Kosher), di-2-ethylhexyladipate (BASF Plastomoll® DOA), dioctyl sebacate, dibutyl sebacate and diisodecyl succinate; aliphatic esters such as butyl oleate and methyl acetyl recinolate; phosphates such as tricresyl phosphate and tributyl phosphate; chlorinated paraffins; hydrocarbon oils such as alkyldiphenyls and partially hydrogenated terphenyls; process oils; epoxy plasticizers such as epoxidized soybean oil and benzyl epoxystearate; tris(2-ethylhexyl)ester; a fatty acid ester; and a combination thereof. Examples of other suitable plasticizers and their commercial sources include BASF Palamoll® 652 and Eastman 168 Xtreme™ Plasticizer.
The amount of the plasticizer present in the sealant depends on various factors (e.g. the amount and/or type of the (I) copolymer, the types and/or amounts of any additional materials present in the sealant (such as other polymer additives), the type of crosslinker utilized, etc.), and may be readily determined by one of skill in the art. In general, where present, the sealant comprises the plasticizer in an amount of from 5 to 150 parts by weight based on the combined weights of all components in the sealant. In specific embodiments, the sealant comprises the plasticizer in an amount of from 0.1 to 10 wt. % based on the total weight of the sealant.
In some embodiments, the sealant comprises an extender. Examples of suitable extenders include non-functional polyorganosiloxanes, such as those comprising difunctional units of the formula R202SiO2/2 and terminal units of the formula R213SiD′-, where each R20 and each R21 are independently a monovalent organic group such as a monovalent hydrocarbon group exemplified by alkyl such as methyl, ethyl, propyl, and butyl; alkenyl such as vinyl, allyl, and hexenyl; aryl such as phenyl, tolyl, xylyl, and naphthyl; and aralkyl groups such as phenylethyl; and D′ is an oxygen atom or a divalent group. Non-functional polyorganosiloxanes are known in the art and are commercially available. Suitable non-functional polyorganosiloxanes are exemplified by, but not limited to, polydimethylsiloxanes. Such polydimethylsiloxanes include DOWSIL® 200 Fluids, which are commercially available from Dow Silicones Corporation of Midland, Mich., U.S.A. and may have viscosity ranging from 5×10−5 to 0.1, alternatively from 5×10−5 to 0.05, and alternatively from 0.0125 to 0.06, m2/s. The amount of the extender present in the sealant depends on various factors (e.g. the amount and/or type of the (I) copolymer, the types and/or amounts of any additional materials present in the sealant (such as other polymer additives), the type of crosslinker utilized, etc.), and may be readily determined by one of skill in the art. In general, where present, the sealant comprises the extender in an amount of from 0.1 to 10 wt. % based on the total weight of the sealant.
In some embodiments, the sealant comprises an end-blocker. Suitable end-blockers comprise an M unit, i.e., a siloxane unit of formula R223SiO1/2, where each R22 independently represents a monovalent organic group, such as a monovalent hydrocarbon group. General examples of such end-blockers include those comprising a polyorganosiloxane (e.g. a polydiorganosiloxane, such as a polydimethylsiloxane) that is end-blocked at one terminus by a triorganosilyl group, e.g. (CH3)3SiO—, and at another terminus by a hydroxyl group. Other examples of suitable end-blockers include polydiorganosiloxanes having both hydroxyl end groups and triorganosilyl end groups, such as those having more than 50%, alternatively more than 75%, of the total end groups as hydroxyl groups. The amount of triorganosilyl group present in such end-blockers may vary, and is typically used to regulate the modulus of the reaction product prepared by condensation reaction of the sealant. Without wishing to be bound by theory, it is thought that higher concentrations of triorganosilyl end groups may provide a lower modulus in certain cured products. In some embodiments, the end-blocker of the sealant comprises a single end-blocking compound. However, in other embodiments, the end-blocker of sealant comprises two or more different end-blocking compounds that differ from one another, e.g. by way of properties including structure, viscosity, average molecular weight, polymer units, sequence, etc., or combinations thereof. The amount of the end-blocker present in the sealant depends on various factors (e.g. the amount and/or type of the (I) copolymer, the types and/or amounts of any additional materials present in the sealant (such as other polymer additives), the type of end-blocker utilized, etc.), and may be readily determined by one of skill in the art. In general, where present, the sealant comprises the end-blocker in an amount of from 0 to 50, alternatively from 0 to 30, alternatively from 0 to 15, wt. %, based on the total weight of the (I) copolymer.
In certain embodiments, the sealant comprises a surface modifier. Suitable surface modifiers include adhesion promoters, release agents, and the like, as well as combinations thereof. Typically, the surface modifier is utilized to change the appearance of the surface of a reaction product of the sealant. For example, the surface modifier may be used to increase gloss of the surface of such a reaction product. Specific examples of suitable surface modifiers include polydiorganosiloxanes with alkyl and aryl groups. For example, DOWSIL® 550 Fluid is a trimethylsiloxy-terminated poly(dimethyl/methylphenyl)siloxane with a viscosity of 0.000125 m2/s that is commercially available from Dow Silicones Corporation. These and other examples of suitable surface modifiers include natural oils (e.g. those obtained from a plant or animal source), such as linseed oil, tung oil, soybean oil, castor oil, fish oil, hempseed oil, cottonseed oil, oiticica oil, rapeseed oil, and the like, as well as combinations thereof.
In some embodiments, the surface modifier is an adhesion promoter. Suitable adhesion promoters may comprise a hydrocarbonoxysilane such as an alkoxysilane, a combination of an alkoxysilane and a hydroxy-functional polyorganosiloxane, an amino functional silane, an epoxy functional silane, a mercaptofunctional silane, or a combination thereof. Adhesion promoters are known in the art and may comprise silanes having the formula R23FR24GSi(OR25)4−(F+G) where each R23 is independently a monovalent organic group having at least 3 carbon atoms; R24 contains at least one SiC bonded substituent having an adhesion-promoting group, such as amino, epoxy, mercapto or acrylate groups; each R25 is independently a monovalent organic group (e.g. methyl, ethyl, propyl, butyl, etc.); subscript F has a value ranging from 0 to 2; subscript G is either 1 or 2; and the sum of (F+G) is not greater than 3. In certain embodiments, the adhesion promoter comprises a partial condensate of the above silane. In these or other embodiments, the adhesion promoter comprises a combination of an alkoxysilane and a hydroxy-functional polyorganosiloxane.
In some embodiments, the adhesion promoter comprises an unsaturated or epoxy-functional compound. In such embodiments, the adhesion promoter may be or comprise an unsaturated or epoxy-functional alkoxysilane such as those having the formula (XIII): R26HSi(OR27)(4−H), where subscript H is 1, 2, or 3, alternatively subscript H is 1. Each R26 is independently a monovalent organic group with the proviso that at least one R26 is an unsaturated organic group or an epoxy-functional organic group. Epoxy-functional organic groups for R26 are exemplified by 3-glycidoxypropyl and (epoxycyclohexyl)ethyl. Unsaturated organic groups for R26 are exemplified by 3-methacryloyloxypropyl, 3-acryloyloxypropyl, and unsaturated monovalent hydrocarbon groups such as vinyl, allyl, hexenyl, undecylenyl. Each R27 is independently a saturated hydrocarbon group of 1 to 4 carbon atoms, alternatively 1 to 2 carbon atoms. R27 is exemplified by methyl, ethyl, propyl, and butyl.
Specific examples of suitable epoxy-functional alkoxysilanes include 3-glycidoxypropyltrimethoxysilane, 3-glycidoxypropyltriethoxysilane, (epoxycyclohexyl)ethyldimethoxysilane, (epoxycyclohexyl)ethyldiethoxysilane and combinations thereof. Examples of suitable unsaturated alkoxysilanes include vinyltrimethoxysilane, allyltrimethoxysilane, allyltriethoxysilane, hexenyltrimethoxysilane, undecylenyltrimethoxysilane, 3-methacryloyloxypropyl trimethoxysilane, 3-methacryloyloxypropyl triethoxysilane, 3-acryloyloxypropyl trimethoxysilane, 3-acryloyloxypropyl triethoxysilane, and combinations thereof.
In some embodiments, the adhesion promoter comprises an epoxy-functional siloxane, such as a reaction product of a hydroxy-terminated polyorganosiloxane with an epoxy-functional alkoxysilane (e.g. such as one of those described above), or a physical blend of the hydroxy-terminated polyorganosiloxane with the epoxy-functional alkoxysilane. The adhesion promoter may comprise a combination of an epoxy-functional alkoxysilane and an epoxy-functional siloxane. For example, the adhesion promoter is exemplified by a mixture of 3-glycidoxypropyltrimethoxysilane and a reaction product of hydroxy-terminated methylvinylsiloxane with 3-glycidoxypropyltrimethoxysilane, or a mixture of 3-glycidoxypropyltrimethoxysilane and a hydroxy-terminated methylvinylsiloxane, or a mixture of 3-glycidoxypropyltrimethoxysilane and a hydroxy-terminated methylvinyl/dimethylsiloxane copolymer.
In certain embodiments, the adhesion promoter comprises an aminofunctional silane, such as an aminofunctional alkoxysilane exemplified by H2N(CH2)2Si(OCH3)3, H2N(CH2)2Si(OCH2CH3)3, H2N(CH2)3Si(OCH3)3, H2N(CH2)3Si(OCH2CH3)3, CH3NH(CH2)3Si(OCH3)3, CH3NH(CH2)3Si(OCH2CH3)3, CH3NH(CH2)5Si(OCH3)3, CH3NH(CH2)5Si(OCH2CH3)3, H2N(CH2)2NH(CH2)3Si(OCH3)3, H2N(CH2)2NH(CH2)3Si(OCH2CH3)3, CH3NH(CH2)2NH(CH2)3Si(OCH3)3, CH3NH(CH2)2NH(CH2)3Si(OCH2CH3)3, C4H9NH(CH2)2NH(CH2)3Si(OCH3)3, C4H9NH(CH2)2NH(CH2)3Si(OCH2CH3)3, H2N(CH2)2SiCH3(OCH3)2, H2N(CH2)2SiCH3(OCH2CH3)2, H2N(CH2)3SiCH3(OCH3)2, H2N(CH2)3SiCH3(OCH2CH3)2, CH3NH(CH2)3SiCH3(OCH3)2, CH3NH(CH2)3SiCH3(OCH2CH3)2, CH3NH(CH2)5SiCH3(OCH3)2, CH3NH(CH2)5SiCH3(OCH2CH3)2, H2N(CH2)2NH(CH2)3SiCH3(OCH3)2, H2N(CH2)2NH(CH2)3SiCH3(OCH2CH3)2, CH3NH(CH2)2NH(CH2)3SiCH3(OCH3)2, CH3NH(CH2)2NH(CH2)3SiCH3(OCH2CH3)2, C4H9NH(CH2)2NH(CH2)3SiCH3(OCH3)2, C4H9NH(CH2)2NH(CH2)3SiCH3(OCH2CH3)2, N-(3-(trimethoxysilyl)propyl)ethylenediamine, and the like, as well as combinations thereof. In these or other embodiments, the adhesion promoter comprises a mercaptofunctional alkoxysilane, such as 3-mercaptopropyltrimethoxysilane or 3-mercaptopropyltriethoxysilane.
Additional examples of surface modifiers include adhesion promoters which are the reaction product of an epoxyalkylalkoxysilane, such as 3-glycidoxypropyltrimethoxysilane, and an amino-substituted alkoxysilane, such as 3-aminopropyltrimethoxysilane, optionally with an alkylalkoxysilane, such as methyltrimethoxysilane.
In some embodiments, the surface modifier comprises, alternatively is, a release agent. Suitable release agents are exemplified by fluorinated compounds, such as fluoro-functional silicones, or fluoro-functional organic compounds. In specific embodiments, the sealant comprises multiple surface modifiers, such as one or more adhesion promoters, one or more release agents, one or more natural oils, or combinations thereof.
The amount of the surface modifier present in the sealant depends on various factors (e.g. the amount and/or type of the (I) copolymer, the types and/or amounts of any additional materials present in the sealant, curing conditions to which the sealant is intended to be exposed, etc.), and may be readily determined by one of skill in the art. In general, where present, the sealant comprises the surface modifier in an amount of from 0.01 to 50, alternatively from 0.01 to 10, alternatively from 0.01 to 5 parts by weight, based on the combined weights of all components in the sealant.
In certain embodiments, the sealant comprises a drying agent, such as physical drying agents (e.g. adsorbents), chemical drying agents, etc. In general, the drying agent binds water and low-molecular weight alcohol from various sources. For example, the drying agent may bind by-products of a condensation reaction involving the (I) copolymer, such as water and alcohols. Physical drying agents typically trap and/or adsorb such water and/or by-products, where chemical drying agents typically binding the water and/or other by-products by chemical means (e.g. via covalent bonding). Examples of suitable drying agents for use in the sealant include adsorbents, such as those comprising inorganic particulates. Such adsorbents typically have a particle size of 10 micrometers or less, alternatively 5 micrometers or less, and an average pore size sufficient to adsorb water and low-molecular weight alcohol alcohols (e.g. an average pore size of 10 Å (Angstroms) or less, alternatively 5 Å or less, alternatively 3 Å or less). Specific examples of such adsorbents include zeolites (e.g. chabasite, mordenite, and analcite) and molecular sieves comprising alkali metal alumino silicates, silica gel, silica-magnesia gel, activated carbon, activated alumina, calcium oxide, and combinations thereof. Examples of commercially available drying agents include dry molecular sieves, such as 3 Å (Angstrom) molecular sieves sold under the trademark SYLOSIV® by Grace Davidson and under the trade name PURMOL by Zeochem of Louisville, Ky., U.S.A., and 4 Å molecular sieves sold under the trade name Doucil zeolite 4A by Ineos Silicas of Warrington, England. Other examples of suitable drying agents include: MOLSIV ADSORBENT TYPE 13X, 3 A, 4 A, and 5 A molecular sieves, all of which are commercially available from UOP of Illinois, U.S.A.; SILIPORITE NK 30AP and 65xP molecular sieves from Atofina of Philadelphia, Pa., U.S.A.; and molecular sieves available from W.R. Grace of Maryland, U.S.A. under various names. Examples of chemical drying agents include silanes, such as those described above with respect to the crosslinker. For example, alkoxysilanes suitable as drying agents include vinyltrimethoxysilane, vinyltriethoxysilane, and combinations thereof. As understood by those of skill in the art, the chemical drying agent may be added to the sealant, or to a part of the sealant (e.g. where the sealant is a multiple-part composition) to keep the sealant or part thereof free from water. As such, the drying agent may be added to a part (e.g. a dry part) of the sealant prior to the sealant being formed, thereby rendering the part shelf stable. Alternatively, or additionally, the drying agent may keep the sealant free from water after formulation (e.g. after the parts of the sealant are combined/mixed together). The amount of the drying agent present in the sealant depends on various factors (e.g. the amount and/or type of the (I) copolymer, the types and/or amounts of any additional materials present in the sealant, curing conditions to which the sealant is intended to be exposed, etc.), and may be readily determined by one of skill in the art. In general, where present, the sealant comprises the drying agent in an amount of from 0.1 to 5 parts by weight, based on the combined weights of all components in the sealant.
In some embodiments, the sealant comprises a biocide. General examples of suitable biocides include fungicides, herbicides, pesticides, antimicrobials, and the like, as well as combinations thereof. For example, in certain embodiments, the biocide comprises, alternatively is, a fungicide. Specific examples of the fungicide include N-substituted benzimidazole carbamates and benzimidazolyl carbamates, such as methyl 2-benzimidazolylcarbamate, ethyl 2-benzimidazolylcarbamate, isopropyl 2-benzimidazolylcarbamate, methyl N-{2-[1-(N,N-dimethylcarbamoyl)benzimidazolyl]}carbamate, methyl N-{2-[1-(N,N-dimethylcarbamoyl)-6-methylbenzimidazolyl]}carbamate, methyl N-{2-[1-(N,N-dimethylcarbamoyl)-5-methylbenzimidazolyl]}carbamate, methyl N-{2-[1-(N-methylcarbamoyl)benzimidazolyl]}carbamate, methyl N-{2-[1-(N-methylcarbamoyl)-6-methylbenzimidazolyl]}carbamate, methyl N-{2-[1-(N-methylcarbamoyl)-5-methylbenzimidazolyl]}carbamate, ethyl N-{2-[1-(N,N-dimethylcarbamoyl)benzimidazolyl]}carbamate, ethyl N-{2-[2-(N-methylcarbamoyl)benzimidazolyl]}carbamate, ethyl N-{2-[1-(N,N-dimethylcarbamoyl)-6-methylbenzimidazolyl]}carbamate, ethyl N-{2-[1-(N-methylcarbamoyl)-6-methylbenzimidazolyl]}carbamate, isopropyl N-{2-[1-(N,N-dimethylcarbamoyl)benzimidazolyl]}carbamate, isopropyl N-{2-[1-(N-methylcarbamoyl)benzimidazolyl]}carbamate, methyl N-{2-[1-(N-propylcarbamoyl)benzimidazolyl]}carbamate, methyl N-{2-[1-(N-butylcarbamoyl)benzimidazolyl]}carbamate, methoxyethyl N-{2-[1-(N-propylcarbamoyl)benzimidazolyl]}carbamate, methoxyethyl N-{2-[1-(N-butylcarbamoyl)benzimidazolyl]}carbamate, ethoxyethyl N-{2-[1-(N-propylcarbamoyl)benzimidazolyl]}carbamate, ethoxyethyl N-{2-[1-(N-butylcarbamoyl)benzimidazolyl]}carbamate, methyl N-{1-(N,N-dimethylcarbamoyloxy)benzimidazolyl]}carbamate, methyl N-{2-[N-methylcarbamoyloxy)benzimidazolyl]}carbamate, methyl N-{2-[1-(N-butylcarbamoyloxy)benzoimidazolyl]}carbamate, ethoxyethyl N-{2-[1-(N-propylcarbamoyl)benzimidazolyl]}carbamate, ethoxyethyl N-{2-[1-(N-butylcarbamoyloxy)benzoimidazolyl]}carbamate, methyl N-{2-[1-(N,N-dimethylcarbamoyl)-6-chlorobenzimidazolyl]}carbamate, and methyl N-{2-[1-(N,N-dimethylcarbamoyl)-6-nitrobenzimidazolyl]}carbamate; 10,10′-oxybisphenoxarsine (trade name: Vinyzene, OBPA); di-iodomethyl-para-tolylsulfone; benzothiophene-2-cyclohexylcarboxamide-S,S-dioxide; N-(fluordichloridemethylthio)phthalimide (trade names: Fluor-Folper, Preventol A3); methyl-benzimideazol-2-ylcarbamate (trade names: Carbendazim, Preventol BCM); Zinc-bis(2-pyridylthio-1-oxide); zinc pyrithione; 2-(4-thiazolyl)-benzimidazol; N-phenyl-iodpropargylcarbamate; N-octyl-4-isothiazolin-3-on; 4,5-dichloride-2-n-octyl-4-isothiazolin-3-on; N-butyl-1,2-benzisothiazolin-3-on; triazolyl-compounds, such as tebuconazol; and the like, as well as combinations thereof. In particular embodiments, such fungicides are utilized in combination with one or more inorganic materials, such as mineral (e.g. zeolites), metals (e.g. copper, silver, platinum, etc.), and combinations thereof.
In particular embodiments, the biocide comprises, alternatively is, an herbicide. Specific examples of the herbicide include amide herbicides such as allidochlor N,N-diallyl-2-chloroacetamide; CDEA 2-chloro-N,N-diethylacetamide; etnipromid (RS)-2-[5-(2,4-dichlorophenoxy)-2-nitrophenoxy]-N-ethylpropionamide; anilide herbicides such as cisanilide cis-2,5-dimethylpyrrolidine-1-carboxanilide; flufenacet 4′-fluoro-N-isopropyl-2-[5-(trifluoromethyl)-1,3,4-thiadiazol-2-yloxy]acetanilide; naproanilide (RS)-α-2-naphthoxypropionanilide; arylalanine herbicides such as benzoylprop N-benzoyl-N-(3,4-dichlorophenyl)-DL-alanine; flamprop-M N-benzoyl-N-(3-chloro-4-fluorophenyl)-D-alanine; chloroacetanilide herbicides such as butachlor N-butoxy methyl-2-chloro-2′,6′-diethylacetanilide; metazachlor 2-chloro-N-(pyrazol-1-ylmethyl)acet-2′,6′-xylidide; prynachlor (RS)-2-chloro-N-(1-methylprop-2-ynyl)acetanilide; sulphonanilide herbicides such as cloransulam 3-chloro-2-(5-ethoxy-7-fluoro[1,2,4]triazolo[1,5-c]pyrimidin-2-ylsulphonamido)benzoic acid; metosulam 2′,6′-dichloro-5,7-dimethoxy-3′-methyl[1,2,4]triazolo[1,5-a]pyrimidine-2-sulphonanilide; antibiotic herbicides such as bilanafos 4-[hydroxy(methyl)phosphinoyl]-L-homoalanyl-L-alanyl-L-alanine; benzoic acid herbicides such as chloramben 3-amino-2,5-dichlorobenzoic acid; 2,3,6-TBA 2,3,6-trichlorobenzoic acid; pyrimidinyloxybenzoic acid herbicides such as bispyribac 2,6-bis(4,6-dimethoxypyrimidin-2-yloxy)benzoic acid; pyrimidinylthiobenzoic acid herbicides such as pyrithiobac 2-chloro-6-(4,6-dimethoxypyrimidin-2-ylthio)benzoic acid; phthalic acid herbicides such as chlorthal tetrachloroterephthalic acid; picolinic acid herbicides such as aminopyralid 4-amino-3,6-dichloropyridine-2-carboxylic acid; quinolinecarboxylic acid herbicides such as quinclorac 3,7-dichloroquinoline-8-carboxylic acid; arsenical herbicides such as CMA calcium bis(hydrogen methylarsonate); MAMA ammonium hydrogen methylarsonate; sodium arsenite; benzoylcyclohexanedione herbicides such as mesotrione 2-(4-mesyl-2-nitrobenzoyl)cyclohexane-1,3-dione; benzofuranyl alkylsulphonate herbicides such as benfuresate 2,3-dihydro-3,3-dimethylbenzofuran-5-yl ethanesulphonate; carbamate herbicides such as carboxazole methyl 5-tert-butyl-1,2-oxazol-3-ylcarbamate; fenasulam methyl 4-[2-(4-chloro-o-tolyloxy)acetamido]phenylsulphonylcarbamate; carbanilate herbicides such as BCPC (RS)-sec-butyl 3-chlorocarbanilate; desmedipham ethyl 3-phenylcarbamoyloxyphenylcarbamate; swep methyl 3,4-dichlorocarbanilate; cyclohexene oxime herbicides such as butroxydim (RS)-(EZ)-5-(3-butyryl-2,4,6-trimethylphenyl)-2-(1-ethoxyiminopropyl)-3-hydroxycyclohex-2-en-1-one; tepraloxydim (RS)-(EZ)-2-{1-[(2E)-3-chloroallyloxyimino]propyl}-3-hydroxy-5-perhydropyran-4-ylcyclohex-2-en-1-one; cyclopropylisoxazole herbicides such as isoxachlortole 4-chloro-2-mesylphenyl 5-cyclopropyl-1,2-oxazol-4-yl ketone; dicarboximide herbicides such as flumezin 2-methyl-4-(α,α,α-trifluoro-m-tolyl)-1,2,4-oxadiazinane-3,5-dione; dinitroaniline herbicides such as ethalfluralin N-ethyl-α,α,α-trifluoro-N-(2-methylallyl)-2,6-dinitro-p-toluidine; prodiamine 5-dipropylamino-α,α,α-trifluoro-4,6-dinitro-o-toluidine; dinitrophenol herbicides such as dinoprop 4,6-dinitro-o-cymen-3-ol; etinofen α-ethoxy-4,6-dinitro-o-cresol; diphenyl ether herbicides such as ethoxyfen O-[2-chloro-5-(2-chloro-α,α,α-trifluoro-p-tolyloxy)benzoyl]-L-lactic acid; nitrophenyl ether herbicides such as aclonifen 2-chloro-6-nitro-3-phenoxyaniline; nitrofen 2,4-dichlorophenyl 4-nitrophenyl ether; dithiocarbamate herbicides such as dazomet 3,5-dimethyl-1,3,5-thiadiazinane-2-thione; halogenated aliphatic herbicides such as dalapon 2,2-dichloropropionic acid; chloroacetic acid; imidazolinone herbicides such as imazapyr (RS)-2-(4-isopropyl-4-methyl-5-oxo-2-imidazolin-2-yl)nicotinic acid; inorganic herbicides such as disodium tetraborate decahydrate; sodium azide; nitrile herbicides such as chloroxynil 3,5-dichloro-4-hydroxybenzonitrile; ioxynil 4-hydroxy-3,5-di-iodobenzonitrile; organophosphorus herbicides such as anilofos S-4-chloro-N-isopropylcarbaniloylmethyl O,O-dimethyl phosphorodithioate; glufosinate 4-[hydroxy(methyl)phosphinoyl]-DL-homoalanine; phenoxy herbicides such as clomeprop (RS)-2-(2,4-dichloro-m-tolyloxy)propionanilide; fenteracol 2-(2,4,5-trichlorophenoxy)ethanol; phenoxyacetic herbicides such as MCPA (4-chloro-2-methylphenoxy)acetic acid; phenoxybutyric herbicides such as MCPB 4-(4-chloro-o-tolyloxy)butyric acid; phenoxypropionic herbicides such as fenoprop (RS)-2-(2,4,5-trichlorophenoxy)propionic acid; aryloxyphenoxypropionic herbicides such as isoxapyrifop (RS)-2-[2-[4-(3,5-dichloro-2-pyridyloxy)phenoxy]propionyl]isoxazolidine; phenylenediamine herbicides such as dinitramine N1,N1-diethyl-2,6-dinitro-4-trifluoromethyl-m-phenylenediamine, pyrazolyloxyacetophenone herbicides such as pyrazoxyfen 2-[4-(2,4-dichlorobenzoyl)-1,3-dimethylpyrazol-5-yloxy]acetophenone; pyrazolylphenyl herbicides such as pyraflufen 2-chloro-5-(4-chloro-5-difluoromethoxy-1-methylpyrazol-3-yl)-4-fluorophenoxyacetic acid; pyridazine herbicides such as pyridafol 6-chloro-3-phenylpyridazin-4-ol; pyridazinone herbicides such as chloridazon 5-amino-4-chloro-2-phenylpyridazin-3(2H)-one; oxapyrazon 5-bromo-1,6-dihydro-6-oxo-1-phenylpyridazin-4-yloxamic acid; pyridine herbicides such as fluoroxypyr 4-amino-3,5-dichloro-6-fluoro-2-pyridyloxyacetic acid; thiazopyr methyl 2-difluoromethyl-5-(4,5-dihydro-1,3-thiazol-2-yl)-4-isobutyl-6-trifluoromethylnicotinate; pyrimidinediamine herbicides such as iprymidam 6-chloro-N4-isopropylpyrimidine-2,4-diamine; quaternary ammonium herbicides such as diethamquat 1,1′-bis(diethylcarbamoylmethyl)-4,4′-bipyridinium; paraquat 1,1′-dimethyl-4,4′-bipyridinium; thiocarbamate herbicides such as cycloate S-ethyl cyclohexyl(ethyl)thiocarbamate; tiocarbazil S-benzyl di-sec-butylthiocarbamate; thiocarbonate herbicides such as EXD O,O-diethyl dithiobis(thioformate); thiourea herbicides such as methiuron 1,1-dimethyl-3-m-tolyl-2-thiourea; triazine herbicides such as triaziflam (RS)-N-[2-(3,5-dimethylphenoxy)-1-methylethyl]-6-(1-fluoro-1-methylethyl)-1,3,5-triazine-2,4-diamine; chlorotriazine herbicides such as cyprazine 6-chloro-N2-cyclopropyl-N4-isopropyl-1,3,5-triazine-2,4-diamine; propazine 6-chloro-A2,N4-di-isopropyl-1,3,5-triazine-2,4-diamine; methoxytriazine herbicides such as prometon N2,N4-di-isopropyl-6-methoxy-1,3,5-triazine-2,4-diamine; methylthiotriazine herbicides such as cyanatryn 2-(4-ethylamino-6-methylthio-1,3,5-triazin-2-ylamino)-2-methylpropionitrile; triazinone herbicides such as hexazinone 3-cyclohexyl-6-dimethylamino-1-methyl-1,3,5-triazine-2,4(1H,3H)-dione; triazole herbicides such as epronaz N-ethyl-N-propyl-3-propylsulphonyl-1H-1,2,4-triazole-1-carboxamide; triazolone herbicides such as carfentrazone (RS)-2-chloro-3-{2-chloro-5-[4-(difluoromethyl)-4,5-dihydro-3-methyl-5-oxo-1H-1,2,4-triazol-1-yl]-4-fluorophenyl}propionic acid; triazolopyrimidine herbicides such as florasulam 2′,6′,8-trifluoro-5-methoxy[1,2,4]triazolo[1,5-c]pyrimidine-2-sulphonanilide; uracil herbicides such as flupropacil isopropyl 2-chloro-5-(1,2,3,6-tetrahydro-3-methyl-2,6-dioxo-4-trifluoromethylpyrimidin-1-yl)benzoate; urea herbicides such as cycluron 3-cyclo-octyl-1,1-dimethylurea; monisouron 1-(5-tert-butyl-1,2-oxazol-3-yl)-3-methylurea; phenylurea herbicides such as chloroxuron 3-[4-(4-chlorophenoxy)phenyl]-1,1-dimethylurea; siduron 1-(2-methylcyclohexyl)-3-phenylurea; pyrimidinylsulphonylurea herbicides such as flazasulphuron 1-(4,6-dimethoxypyrimidin-2-yl)-3-(3-trifluoromethyl-2-pyridylsulphonyl)urea; pyrazosulphuron 5-[(4,6-dimethoxypyrimidin-2-ylcarbamoyl)sulphamoyl]-1-methylpyrazole-4-carboxylic acid; triazinylsulphonylurea herbicides such as thifensulphuron 3-(4-methoxy-6-methyl-1,3,5-triazin-2-ylcarbamoylsulphamoyl)thiophene-2-carboxylic acid; thiadiazolylurea herbicides such as tebuthiuron 1-(5-tert-butyl-1,3,4-thiadiazol-2-yl)-1,3-dimethylurea; and/or unclassified herbicides such as chlorfenac (2,3,6-trichlorophenyl)acetic acid; methazole 2-(3,4-dichlorophenyl)-4-methyl-1,2,4-oxadiazolidine-3,5-dione; tritac (RS)-1-(2,3,6-trichlorobenzyloxy)propan-2-ol; 2,4-D, chlorimuron, and fenoxaprop; and the like, as well as combinations thereof.
In some embodiments, the biocide comprises, alternatively is, a pesticide. General examples of the pesticide include insect repellents such as N,N-diethyl-meta-toluamide, and pyrethroids such as pyrethrin. Specific examples of the pesticide include atrazine, diazinon, and chlorpyrifos. In these or other embodiments, the biocide comprises, alternatively is, an antimicrobial agent. The type and nature of the antimicrobial agent may vary, and can be readily determined by one of skill in the art. In certain embodiments, the biocide comprises, alternatively is, a boron-containing material, such as a boric anhydride, borax, or a disodium octaborate tetrahydrate. In various embodiments, the sealant comprises two or more biocides, which are each independently selected from the fungicide, herbicide pesticide, antimicrobial, and other biocidal components exemplified herein.
The amount of the biocide present in the sealant depends on various factors (e.g. the type of biocide(s) utilized, the amount and/or type of the (I) copolymer, an intended use of the sealant, curing conditions to which the sealant is intended to be exposed, etc.), and may be readily determined by one of skill in the art. In general, where present, the sealant comprises the biocide, or a combination of biocides, in an amount of from 0.01 to 10, alternatively from 0.1 to 5 wt. % based on the total weight of the sealant.
In particular embodiments, the sealant comprises a flame retardant. Examples of suitable flame retardants include organic/carbonaceous flame retardants (e.g. carbon black, etc.), inorganic/mineral-based flame retardants (e.g. hydrated aluminum hydroxide, silicates such as wollastonite, metal complexes of platinum and/or platinum, etc.) and the like, as well as combinations thereof. Additional examples of suitable flame retardants include halogen-based flame retardants, such as decabromodiphenyloxide, octabromordiphenyl oxide, hexabromocyclododecane, decabromobiphenyl oxide, diphenyoxybenzene, ethylene bis-tetrabromophthalmide, pentabromoethyl benzene, pentabromobenzyl acrylate, tribromophenyl maleic imide, tetrabromobisphenyl A, bis-(tribromophenoxy)ethane, bis-(pentabromophenoxy)ethane, polydibomophenylene oxide, tribromophenylallyl ether, bis-dibromopropyl ether, tetrabromophthalic anhydride, dibromoneopentyl gycol, dibromoethyl dibromocyclohexane, pentabromodiphenyl oxide, tribromostyrene, pentabromochlorocyclohexane, tetrabromoxylene, hexabromocyclododecane, brominated polystyrene, tetradecabromodiphenoxybenzene, trifluoropropene, and PVC; phosphorus based flame-retardants, such as (2,3-dibromopropyl)-phosphate, phosphorus, cyclic phosphates, triaryl phosphates, bis-melaminium pentate, pentaerythritol bicyclic phosphate, dimethylmethylphosphate, phosphine oxide diol, triphenyl phosphate, tris-(2-chloroethyl)phosphate, phosphate esters such as tricreyl-, trixylenyl-, isodecyl diphenyl-, ethylhexyl diphenyl-, trioctyl-, tributyl-, and tris-butoxyethyl phosphate esters, and phosphate salts of various amines (e.g. ammonium phosphate); tetraalkyl lead compounds, such as tetraethyl lead; iron pentacarbonyl; manganese methyl cyclopentadienyl tricarbonyl; melamine and derivatives thereof, such as melamine salts; guanidine; dicyandiamide; ammonium sulphamate; alumina trihydrate; magnesium hydroxide alumina trihydrate; and the like, as well as derivatives, modifications, and combinations thereof. The amount of the flame retardant present in the sealant depends on various factors (e.g. the amount and/or type of the (I) copolymer, an intended use of the sealant, curing conditions to which the sealant is intended to be exposed, a presence/absence of a vehicle/solvent, etc.), and may be readily determined by one of skill in the art. In general, where present, the sealant comprises the flame retardant in an amount of from 0.01 to 15, alternatively from 0.1 to 10 wt. % based on the total weight of the sealant.
In certain embodiments, the sealant comprises a binder. Typically, the binder is a non-reactive, elastomeric, organic polymer, i.e., an elastomeric organic polymer that does not react with the (I) copolymer. Additionally, the binder is typically compatible with the (I) copolymer, i.e., the binder does not form a two-phase system when formulated into the sealant with the (I) copolymer. In general, suitable binders have low gas and moisture permeability, and typically comprise a number average molecular weight (Mn) of from 30,000 to 75,000. However, the binder may comprise a blend of various non-reactive, elastomeric, organic polymers (e.g. of such polymers having a high molecular weight with those having a low molecular weight). In such instances, the higher molecular weight polymer(s) typically comprise a Mn of from 100,000 to 600,000, and the lower molecular weight polymer(s) typically comprise a Mn of from 900 to 10,000, alternatively 900 to 3,000. The value for the lower end of the Mn ranges is typically selected such that the binder is compatible with the (I) copolymer and the other ingredients of the sealant, as understood by those of skill in the art. The binder may comprise or be one non-reactive, elastomeric, organic polymer or, alternatively may comprise two or more non-reactive, elastomeric, organic polymers that differ from one another, e.g. on a basis of structure, viscosity, average molecular weight (Mn or Mw), polymer units, sequence, etc., or combinations thereof.
Examples of suitable binders include polyisobutylenes, which are known in the art and are commercially available. Specific examples of polyisobutylenes include those marketed under the trademark OPPANOL® by BASF Corporation of Germany, as well as the various grades of hydrogenated polyisobutene marketed under the trademark PARLEAM® by NOF Corp. of Japan. Additional examples of suitable polyisobutylenes are commercially available from ExxonMobil Chemical Co. of Baytown, Tex., U.S.A. under the trademark VISTANEX®. These include VISTANEX® MML-80, MML-100, MML-120, and MML-140, which are paraffinic hydrocarbon polymers, composed of long, straight-chain macromolecules containing only chain-end olefinic bonds. VISTANEX® MM polyisobutylenes have a viscosity average molecular weight of from 70,000 to 90,000, and VISTANEX® LM polyisobutylenes (e.g. LM-MS) are lower-molecular weight polyisobutylenes having a viscosity average molecular weight of from 8,700 to 10. Additional examples of polyisobutylenes include VISTANEX LM-MH (viscosity average molecular weight of 10,000 to 11,700); Soltex PB-24 (Mn 950), Indopol® H-100 (Mn 910), Indopol® H-1200 (Mn 2100), from Amoco Corp. of Chicago, Ill., U.S.A.; NAPVIS® and HYVIS® (e.g. NAPVIS® 200, D10, and DE3; and HYVIS® 200.) from BP Chemicals of London, England. The NAPVIS® polyisobutylenes typically have a Mn of from 900 to 1300. In addition, or as an alternative, to the polyisobutylene(s), the binder may comprise or be a butyl rubber, a styrene-ethylene/butylene-styrene (SEBS) block copolymer, a styrene-ethylene/propylene-styrene (SEPS) block copolymer, polyolefin plastomer, or combinations thereof. SEBS and SEPS block copolymers are known in the art and are commercially available as Kraton® G polymers from Kraton Polymers U.S. LLC of Houston, Tex., U.S.A., and as Septon polymers from Kuraray America, Inc., New York, N.Y., U.S.A. Polyolefin plastomers are also known in the art and are commercially available as AFFINITY® GA 1900 and AFFINITY® GA 1950 compositions from Dow Chemical Company, Elastomers & Specialty Products Division, Midland, Mich., U.S.A.
The amount of the binder present in the sealant depends on various factors (e.g. the amount and/or type of the (I) copolymer, an intended use of the sealant, curing conditions to which the sealant is intended to be exposed, a presence/absence of a vehicle/solvent, etc.), and may be readily determined by one of skill in the art. In general, where present, the sealant comprises the binder in an amount of from 1 to 50, alternatively from 5 to 40, alternatively from 5 to 35 parts by weight, based on the combined weights of all components in the sealant.
In some embodiments, the sealant comprises an anti-aging additive. Examples of anti-aging additives include antioxidants, UV absorbers, UV and/or light stabilizers, heat stabilizers, and combinations thereof. The anti-aging additive may be or comprise but one anti-aging additive or, alternatively, may comprise two or more different anti-aging additives. Moreover, one particular anti-aging additive may serve multiple functions (e.g. as both a UV absorber and a UV stabilizer, as both an antioxidant and a UV absorber, etc.). Many suitable anti-aging additives are known in the art and are commercially available. For example, suitable antioxidants include phenolic antioxidants (e.g. fully-sterically hindered phenols and partially-hindered phenols) and combinations of phenolic antioxidants with stabilizers (e.g. sterically hindered amines, such as tetramethyl-piperidine derivatives, also known as “hindered amine light stabilizers” (HALS)). Suitable phenolic antioxidants include vitamin E and IRGANOX® 1010 from BASF. IRGANOX®1010 comprises pentaerythritol tetrakis(3-(3,5-di-t-butyl-4-hydroxyphenyl)propionate). Examples of UV absorbers include phenol, 2-(2H-benzotriazol-2-yl)-6-dodecyl-4-methyl-, branched and linear (TINUVIN® 571). Examples of UV stabilizers include bis(1,2,2,6,6-pentamethyl-4-piperidyl) sebacate; methyl 1,2,2,6,6-pentamethyl-4-piperidyl/sebacate; and combinations thereof (TINUVIN® 272). These and other TINUVIN® additives, such as TINUVIN® 765 are commercially available from BASF. Other UV and light stabilizers are commercially available, and are exemplified by LowLite from Chemtura, OnCap from PolyOne, and Light Stabilizer 210 from E. I. du Pont de Nemours and Company of Delaware, U.S.A. Oligomeric (higher molecular weight) stabilizers may also be utilized in or as the anti-aging additive, for example, to minimize potential for migration of the anti-aging additive out of the sealant or a cured product thereof. Example of such oligomeric antioxidant stabilizers include TINUVIN® 622, which is a dimethylester of butanedioic acid copolymerized with 4-hydroxy-2,2,6,6-tetramethyl-1-piperidine ethanol. Examples of heat stabilizers include iron oxides, carbon blacks, iron carboxylate salts, cerium hydrates, barium zirconates, cerium and zirconium octoates, porphyrins, and the like, as well as combinations thereof.
The amount of the anti-aging additive present in the sealant depends on various factors (e.g. the amount and/or type of the (I) copolymer, an intended use of the sealant, curing conditions to which the sealant is intended to be exposed, etc.), and may be readily determined by one of skill in the art. In general, where present, the sealant comprises the anti-aging additive in an amount of from greater than 0 to 5, alternatively from 0.1 to 4, alternatively from 0.5 to 3 wt. %, based on the total weight of the sealant.
In certain embodiments, the sealant comprises a water release agent, i.e., a component that releases water over time (e.g. in response to an applied condition, such as a temperature and/or a pressure). Typically, the water release agent contains an amount of water sufficient to partially, alternatively fully, react the sealant, and is thus selected to release the amount of water when exposed to the applied condition (e.g. a use temperature of the sealant) for a sufficient amount of time. Generally, however the water release agent is selected to sufficiently bind the water to thereby prevent too much water from being released during making and/or storing the sealant. For example, the water release agent typically binds the water sufficiently during compounding/formulating the sealant, such that sufficient water is available for condensation reaction of the (I) copolymer during or after the application process in which the sealant is used. This “controlled release” property also may provide the benefit of preventing too much water from being released and/or water being released too rapidly during the application process, since this may cause bubbling or voiding in the reaction product formed by condensation reaction of the (I) copolymer of the sealant. The particular water release agent selected can depend on various factors, (e.g. the other components of the sealant, the amount/type of the (I) copolymer, the type of the (II) condensation reaction catalyst, the process conditions under which the sealant will be formulated, etc.) and will be readily determined by one of skill in the art. Examples of suitable water release agents are exemplified by metal salt hydrates, hydrated molecular sieves, and precipitated carbonates. Particular examples include the precipitated calcium carbonate available from Solvay under the trademark WINNOFIL® SPM. In certain embodiments, the water release agent is selected to include, alternatively to be, precipitated calcium carbonate. The water release agent may be selected to ensure that not all of the water content is released during compounding, while still releasing a sufficient amount of water for condensation reaction of the (I) copolymer when exposed to the application temperature range for a sufficient period of time. The amount of the water release agent present in the sealant depends on various factors (e.g. the water permeability of the (I) copolymer, a presence/absence of vehicle/solvent, a presence/absence of drying agent, the method by which the sealant is to be formulated/prepared, etc.), and may be readily determined by one of skill in the art. In general, where present, the sealant comprises the water release agent in an amount of from 1 to 50, alternatively from 5 to 40, alternatively from 5 to 30 parts by weight, based on the combined weights of all components in the sealant.
In some embodiments, the sealant comprises a pigment (i.e., a component that imparts color to the sealant and/or a reaction product thereof). Such pigments may comprise any inorganic compounds, for example those of metals such as chromium oxides, titanium oxides, cobalt pigments, as well as those that are not based on such metals, e.g. non-metal inorganic compounds. Examples of suitable pigments include indigos, titanium dioxides, carbon blacks, and combinations thereof, as well as other commercially available pigments such as Stan-Tone 505P01 Green, which is available from PolyOne. In certain embodiments, the pigment comprises a carbon black. Specific examples of carbon blacks include Shawinigan Acetylene black, which is commercially available from Chevron Phillips Chemical Company LP; SUPERJET® Carbon Black (e.g. LB-1011) supplied by Elementis Pigments Inc., of Fairview Heights, Ill. U.S.A.; SR 511 supplied by Sid Richardson Carbon Co, of Akron, Ohio U.S.A.; and N330, N550, N762, N990 (from Degussa Engineered Carbons of Parsippany, N.J., U.S.A.). The amount of the pigment present in the sealant depends on various factors (e.g. the amount and/or type of the (I) copolymer, an intended use of the sealant, a presence/absence of a vehicle/solvent, etc.), and may be readily determined by one of skill in the art. In general, where present, the sealant comprises the pigment in an amount of from greater than 0 to 20, alternatively from 0.001 to 10, alternatively from 0.001 to 5 wt. % based on the total weight of the sealant.
In certain embodiments, the sealant comprises a rheology additive, such as a rheology modifier and/or a viscosity modifier. Examples of suitable rheological additives include waxes; polyamides; polyamide waxes; hydrogenated castor oil derivatives; metal soaps, such as calcium, aluminum, and/or barium stearates; and the like, as well as derivatives, modifications, and combinations thereof. In particular embodiments, the rheology modifier is selected to facilitate incorporation of fillers, compounding, de-airing, and/or mixing of the sealant (e.g. during preparation thereof), as well understood by those of skill in the art. Specific examples of rheological additives include those known in the art which are commercially available. Examples of such rheological additives include Polyvest, which is commercially available from Evonik; Disparlon which is commercially available from King Industries; Kevlar Fibre Pulp, which is commercially available from Du Pont; Rheospan which is commercially available from Nanocor; Ircogel, which is commercially available from Lubrizol; Crayvallac® SLX, which is commercially available from Palmer Holland, and the like, as well as combinations thereof.
In some embodiments, the rheology modifier comprises, alternatively is, a wax (e.g. a paraffin wax, a microcrystalline wax, or a combination thereof). The wax typically comprises non-polar hydrocarbon(s), which may comprise branched structures, cyclic structures, or combinations thereof. Examples of suitable waxes include petroleum microcrystalline waxes available from Strahl & Pitsch, Inc., of West Babylon, N.Y., U.S.A. under the names SP 96 (melting point of from 62 to 69° C.), SP 18 (melting point of from 73 to 80° C.), SP 19 (melting point of from 76 to 83° C.), SP 26 (melting point ranging from 76 to 83° C.), SP 60 (melting point of from 79 to 85° C.), SP 617 (melting point of from 88 to 93° C.), SP 89 (melting point of from 90 to 95° C.), and SP 624 (melting point of from 90 to 95° C.). Further examples of suitable waxes include those marketed under the trademark Multiwax® by Crompton Corporation of Petrolia, Pa., U.S.A. Such waxes include which include Multiwax® 180-W, which comprises saturated branched and cyclic non-polar hydrocarbons and has melting point of from 79 to 87° C.; Multiwax® W-445, which comprises saturated branched and cyclic non-polar hydrocarbons, and has melting point of from 76 to 83° C.; and Multiwax® W-835, which comprises saturated branched and cyclic non-polar hydrocarbons, and has melting point of from 73 to 80° C. In certain embodiments, the wax comprises, alternatively is, a microcrystalline wax that is a solid at room temperature (25° C.). In some embodiments, the wax is selected to have a melting point within a desired application temperature range (i.e., the temperature range within which the sealant is intended to be used/applied). It is thought that the wax, when molten, serves as a process aid, substantially easing the incorporation of filler in the composition during compounding, the compounding process itself, as well as in during a de-airing step, if used. For example, in certain embodiments, the wax has a melt temperature below 100° C. and may facilitate mixing of parts (e.g. when the sealant is a multiple part composition) before application, even in a simple static mixer. In such instances, the wax may also facilitate application of the sealant at temperatures of from 80 to 110° C., alternatively 90 to 100° C., with good rheology.
The amount of the rheological additive present in the sealant depends on various factors (e.g. the amount and/or type of the (I) copolymer, an intended use of the sealant, curing conditions to which the sealant is intended to be exposed, a presence/absence of a vehicle/solvent, etc.), and may be readily determined by one of skill in the art. In general, where present, the sealant comprises the rheological additive in an amount of from greater than 0 to 20, alternatively from 1 to 15, alternatively from 1 to 5, parts by weight, based on the combined weights of all components in the sealant.
In certain embodiments, the sealant comprises a vehicle (e.g. a carrier vehicle, such as a solvent and/or diluent). Depending on a selection of various components of the sealant, the carrier vehicle may be, for example, an oil (e.g. an organic oil and/or a silicone oil), a solvent, water, etc. As will be understood by one of skill in the art, the particular vehicle utilized, if any, is selected to facilitate (e.g. increase) flow of the sealant or a portion thereof (e.g. one or more parts of the sealant when the sealant is a multiple-part composition); as well as the introduction of certain components (e.g. the (I) copolymer, the chainextender, the end-blocker, etc.). As such, suitable vehicles are varied, and generally include those which help fluidize one or more components of the sealant, but essentially do not react with any of such components. Accordingly, the vehicle may be selected based on a solubility of one or more components of the sealant, volatility, or both. In this sense, the solubility refers to the vehicle being sufficient to dissolve and/or disperse the one or more components of the sealant, and the volatility refers to vapor pressure of the vehicle. If the vehicle is too volatile (i.e., has a vapor pressure too high for the intended use), bubbles may form in the sealant at the application temperature, which may lead to cracks and/or otherwise weaken or detrimentally affect properties of the cured product formed from the sealant. However, if the vehicle is not volatile enough (i.e., has a vapor pressure too low for the intended use) the vehicle may remain in the cured product of the sealant and/or function as a plasticizer therein. Examples of suitable vehicles generally include silicone fluids, organic fluids, and combinations thereof.
In some embodiments, the vehicle of the sealant comprises, alternatively is, a silicone fluid. The silicone fluid is typically a low viscosity and/or volatile siloxane. In some embodiments, the silicone fluid is a low viscosity organopolysiloxane, a volatile methyl siloxane, a volatile ethyl siloxane, a volatile methyl ethyl siloxane, or the like, or combinations thereof. Typically, the silicone fluid has a viscosity at 25° C. in the range of 1 to 1,000 mm2/sec. In some embodiments, the silicone fluid comprises a silicone having the general formula (R28R29SiO)I, where each R28 and R29 is independently selected from H and substituted or unsubstituted hydrocarbyl groups, and subscript I is from 3 to 8. Specific examples of suitable silicone fluids include hexamethylcyclotrisiloxane, octamethylcyclotetrasiloxane, decamethylcyclopentasiloxane, dodecamethylcyclohexasiloxane, octamethyltrisiloxane, decamethyltetrasiloxane, dodecamethylpentasiloxane, tetradecamethylhexasiloxane, hexadeamethylheptasiloxane, heptamethyl-3-{(trimethylsilyl)oxy)}trisiloxane, hexamethyl-3,3, bis{(trimethylsilyl)oxy}trisiloxane pentamethyl{(trimethylsilyl)oxy}cyclotrisiloxane as well as polydimethylsiloxanes, polyethylsiloxanes, polymethylethylsiloxanes, polymethylphenylsiloxanes, polydiphenylsiloxanes, caprylyl methicone, hexamethyldisiloxane, heptamethyloctyltrisiloxane, hexyltrimethicone, and the like, as well as derivatives, modifications, and combinations thereof. Additional examples of suitable silicone fluids include polyorganosiloxanes with suitable vapor pressures, such as from 5×10−7 to 1.5×10−6 m2/s, include DOWSIL® 200 Fluids and DOWSIL® OS FLUIDS, which are commercially available from Dow Silicones Corporation of Midland, Mich., U.S.A.
In certain embodiments, the vehicle of the sealant comprises, alternatively is, an organic fluid, which typically comprises an organic oil including a volatile and/or semi-volatile hydrocarbon, ester, and/or ether. General examples of such organic fluids include volatile hydrocarbon oils, such as C6-C16 alkanes, C8-C16 isoalkanes (e.g. isodecane, isododecane, isohexadecane, etc.) C8-C16 branched esters (e.g. isohexyl neopentanoate, isodecyl neopentanoate, etc.), and the like, as well as derivatives, modifications, and combinations thereof. Additional examples of suitable organic fluids include aromatic hydrocarbons, aliphatic hydrocarbons, alcohols having more than 3 carbon atoms, aldehydes, ketones, amines, esters, ethers, glycols, glycol ethers, alkyl halides, aromatic halides, and combinations thereof. Hydrocarbons include isododecane, isohexadecane, Isopar L (C11-C13), Isopar H (C11-C12), hydrogentated polydecene. Ethers and esters include isodecyl neopentanoate, neopentylglycol heptanoate, glycol distearate, dicaprylyl carbonate, diethylhexyl carbonate, propylene glycol n-butyl ether, ethyl-3 ethoxypropionate, propylene glycol methyl ether acetate, tridecyl neopentanoate, propylene glycol methylether acetate (PGMEA), propylene glycol methylether (PGME), octyldodecyl neopentanoate, diisobutyl adipate, diisopropyl adipate, propylene glycol dicaprylate/dicaprate, octyl ether, octyl palmitate, and combinations thereof.
In some embodiments, the vehicle comprises, alternatively is, an organic solvent. Examples of the organic solvent include those comprising an alcohol, such as methanol, ethanol, isopropanol, butanol, and n-propanol; a ketone, such as acetone, methylethyl ketone, and methyl isobutyl ketone; an aromatic hydrocarbon, such as benzene, toluene, and xylene; an aliphatic hydrocarbon, such as heptane, hexane, and octane; a glycol ether, such as propylene glycol methyl ether, dipropylene glycol methyl ether, propylene glycol n-butyl ether, propylene glycol n-propyl ether, and ethylene glycol n-butyl ether; a halogenated hydrocarbon, such as dichloromethane, 1,1,1-trichloroethane and methylene chloride; chloroform; dimethyl sulfoxide; dimethyl formamide, acetonitrile; tetrahydrofuran; white spirits; mineral spirits; naphtha; n-methylpyrrolidone; and the like, as well as derivatives, modifications, and combination thereof.
Other vehicles may also be utilized in the sealant. For example, in some embodiments, the vehicle comprises, alternatively is, an ionic liquid. Examples of ionic liquids include anion-cation combinations. Generally, the anion is selected from alkyl sulfate-based anions, tosylate anions, sulfonate-based anions, bis(trifluoromethanesulfonyl)imide anions, bis(fluorosulfonyl)imide anions, hexafluorophosphate anions, tetrafluoroborate anions, and the like, and the cation is selected from imidazolium-based cations, pyrrolidinium-based cations, pyridinium-based cations, lithium cation, and the like. However, combinations of multiple cations and anions may also be utilized. Specific examples of the ionic liquids typically include 1-butyl-1-methylpyrrolidinium bis(trifluoromethanesulfonyl)imide, 1-methyl-1-propylpyrrolidinium bis-(trifluoromethanesulfonyl)imide, 3-methyl-1-propylpyridinium bis(trifluoromethanesulfonyl)imide, N-butyl-3-methylpyridinium bis(trifluoromethanesulfonyl)imide, 1-methyl-1-propylpyridinium bis(trifluoromethanesulfonyl)imide, diallyldimethylammonium bis(trifluoromethanesulfonyl)imide, methyltrioctylammonium bis(trifluoromethanesulfonyl)imide, 1-butyl-3-methylimidazolium bis(trifluoromethanesulfonyl)imide, 1,2-dimethyl-3-propylimidazolium bis(trifluoromethanesulfonyl)imide, 1-ethyl-3-methylimidazolium bis(trifluoromethanesulfonyl)imide, 1-vinylimidazolium.bis(trifluoromethanesulfonyl)imide, 1-allyl imidazolium bis(trifluoromethanesulfonyl)imide, 1-allyl-3-methylimidazolium bis(trifluoromethanesulfonyl)imide, lithium bis(trifluoromethanesulfonyl)imide, and the like, as well as derivatives, modifications, and combinations thereof.
The amount of the vehicle present in the sealant depends on various factors (e.g. the amount and/or type of the (I) copolymer, the manner by which the sealant was formulated, curing conditions to which the sealant is intended to be exposed, etc.), and may be readily determined by one of skill in the art. In general, where present, the sealant comprises the vehicle in an amount of from 1 to 99, alternatively from 1 to 75, alternatively from 2 to 60, alternatively from 2 to 50 wt. %, based on the total weight of the sealant.
In particular embodiments, the sealant comprises a tackifying agent. General examples of suitable tackifying agents typically include those comprising an aliphatic hydrocarbon resin (e.g. a hydrogenated polyolefin having 6 to 20 carbon atoms), a hydrogenated terpene resin, a rosin ester, a hydrogenated rosin glycerol ester, or a combination thereof. Specific examples of suitable tackifying agents include natural or modified rosins such as gum rosin, wood rosin, tall-oil rosin, distilled rosin, hydrogenated rosin, dimerized rosin, and polymerized rosin; glycerol and pentaerythritol esters of natural or modified rosins, such as glycerol esters of pale wood rosins, glycerol esters of hydrogenated rosins, glycerol esters of polymerized rosins, pentaerythritol esters of hydrogenated rosins, and phenolic-modified pentaerythritol esters of rosin; copolymers and/or terpolymers of natural terpenes, such as styrene/terpene and/or alpha methyl styrene/terpene polymers; polyterpene resins having a softening point, as determined by ASTM method E28, of from 60 to 150° C., such as those produced via the polymerization of terpene hydrocarbons (e.g. pinene) in the presence of Friedel-Crafts catalysts, as well as the hydrogenation products thereof (e.g. hydrogenated polyterpenes); phenolic modified terpene resins and hydrogenated derivatives thereof, such as those produced via acid-mediated condensation of a bicyclic terpene and a phenol; aliphatic petroleum hydrocarbon resins, such as those produced via the polymerization of monomers consisting of primarily of olefins and diolefins, those having a ring and ball softening point of from 60 to 135° C., and also hydrogenated aliphatic petroleum hydrocarbon resins; alicyclic petroleum hydrocarbon resins and hydrogenated derivatives thereof; aliphatic/aromatic or cycloaliphatic/aromatic copolymers and hydrogenated derivatives thereof; and combinations thereof. In some embodiments, the sealant comprises a solid tackifying agent (i.e., a tackifying agent having a ring and ball softening point above 25° C.). Other examples of suitable tackifying agents include commercially available varieties, such as the aliphatic hydrocarbon resins exemplified by ESCOREZ 1102, 1304, 1310, 1315, and 5600 from Exxon Chemical, and Eastotac H-100, H-115E, and H-130L from Eastman; the hydrogenated terpene resins exemplified by Arkon P 100 from Arakawa Chemicals, and Wingtack 95 from Goodyear; the hydrogenated rosin glycerol esters exemplified by Staybelite Ester 10 and Foral from Hercules; the polyterpenes exemplified by Piccolyte A125 from Hercules; the aliphatic/aromatic and/or cycloaliphatic/aromatic resins exemplified by ECR 149B and ECR 179A from Exxon Chemical; and combinations thereof. The amount of the tackifying agent present in the sealant depends on various factors (e.g. the amount and/or type of the (I) copolymer, the type and/or amount of other components of the sealant, an intended use of the sealant, etc.), and may be readily determined by one of skill in the art. In general, where present, the sealant comprises the tackifying agent in an amount of from 1 to 20 parts by weight, based on the combined weights of all components in the sealant.
In certain embodiments, the sealant comprises a corrosion inhibitor. Examples of suitable corrosion inhibitors include benzotriazoles, mercaptabenzotriazoles, and the like, as well as combinations thereof. Specific examples of suitable corrosion inhibitors are known in the art and commercially available, such as CUVAN® 826 (e.g. a 2,5-dimercapto-1,3,4-thiadiazole derivative) and CUVAN® 484 (an alkylthiadiazole), which are available from R. T. Vanderbilt of Norwalk, Conn., U.S.A.
The amount of the corrosion inhibitor present in the sealant depends on various factors (e.g. the amount and/or type of the (I) copolymer, an intended use of the sealant, curing conditions to which the sealant is intended to be exposed, etc.), and may be readily determined by one of skill in the art. In general, where present, the sealant comprises the corrosion inhibitor in an amount of from 0.05 to 0.5 wt. % based on total weight of the sealant.
As introduced in various sections above, various components of the sealant may be utilized for multiple purposes, and thus certain additives may overlap with regard to the components described herein. For example, certain alkoxysilanes may be useful as filler treating agents, as adhesion promoters, and as crosslinkers. Additionally, the sealant may further comprise additional additives not described above, such as catalyst inhibitors, curing promotors, color-change additives, etc. Such additional additives are independently selected, and each utilized in the sealant in an amount selected based on the indented use thereof, as readily determined by one of skill in the art. Typically, where present, the sealant comprises each of such additional additives in an amount of from 0.001 to 10, alternatively from 0.01 to 5, alternatively from 0.1 to 1 wt. % based on total weight of the sealant.
As described above, the sealant may be prepared as a one-part composition, or as a multiple-part composition (e.g. comprising 2, 3, 4, or more parts). For example, in some embodiments, the sealant is prepared as the one-part composition, which may be prepared by combining all components together by any convenient means, such as mixing. Such a one-part composition may be made by optionally combining (e.g. premixing) the (I) copolymer with various additives (e.g. the filler) to form an intermediate mixture, and subsequently combining (e.g. via mixing) the intermediate mixture with a pre-mix comprising the (II) condensation reaction catalyst and other various additives to form a sealant mixture or the sealant. Other additives (e.g. the anti-aging additive, the pigment, etc.) may be added to the sealant at any desired stage, such as via combination with the intermediate mixture, the pre-mix, or the sealant mixture. As such, a final mixing step may be performed (e.g. under substantially anhydrous conditions) to form the sealant, which is typically stored under substantially anhydrous conditions, for example in sealed containers, until ready for use.
In some embodiments, the sealant is prepared as the multiple-part composition (e.g. when the crosslinker is utilized). In such embodiments, the (II) condensation reaction catalyst and the crosslinker are typically stored in separate parts, which are combined shortly before use of the sealant. For example, the sealant may comprise a two part curable composition prepared by combining the (I) copolymer and the crosslinker to form a first (i.e., curing agent) part by any convenient means (e.g. mixing). A second (i.e., base) part may be prepared by combining the (II) condensation reaction catalyst and (I) copolymer by any convenient means (e.g. mixing). The components may be combined at ambient or elevated temperature and under ambient or anhydrous conditions, depending on various factors, e.g. whether a one part or multiple part composition is selected. The base part and curing agent part may then be combined by any convenient means, such as mixing, shortly before use. The base part and curing agent part may be combined in a 1:1 ratio, or in a relative amount of base: curing agent ranging from 1:1 to 10:1.
The equipment used for mixing the components of the sealant is not specifically restricted, and is typically selected depending on the type and amount of each component selected for use in the sealant or a part thereof (collectively, the “sealant compositions”.) For example, agitated batch kettles may be used for relatively low viscosity sealant compositions, such as compositions that would react to form gums or gels. Alternatively, continuous compounding equipment (e.g. extruders, such as twin screw extruders) may be used for more viscous sealant compositions, as well as sealant compositions containing relatively high amounts of particulates. Exemplary methods that can be used to prepare the sealant compositions described herein include those disclosed in, for example, U.S. Patent Publication Nos. 2009/0291238 and 2008/0300358, which portions are herein incorporated by reference.
The sealant compositions made as described above may be stable when stored in containers that reduce or prevent exposure of the sealant compositions to moisture. However, the sealant compositions, may react via condensation reaction when exposed to atmospheric moisture. Additionally, when the water release agent is utilized, the sealant compositions may react via condensation reaction without exposure to atmospheric moisture.
A cured product is also provided. The cured product is formed from the sealant. More specifically, the cured product is formed by curing the sealant, e.g. via the condensation reaction described above.
A composite article comprising the cured product is also provided. More specifically, the composite article comprises a substrate and the cured product disposed on the substrate. The composite article is formed by disposing the sealant on the substrate, and curing the sealant to give the cured product on the substrate, thereby preparing the composite article. The substrate is exemplified by, for example, an exterior building façade.
A method of sealing a space defined between two elements is also disclosed. This method comprises applying the sealant to the space, and curing the sealant in the space, thereby sealing the space.
The terms “comprising” or “comprise” are used herein in their broadest sense to mean and encompass the notions of “including,” “include,” “consist(ing) essentially of,” and “consist(ing) of. The use of “for example,” “e.g.,” “such as,” and “including” to list illustrative examples does not limit to only the listed examples. Thus, “for example” or “such as” means “for example, but not limited to” or “such as, but not limited to” and encompasses other similar or equivalent examples. The term “about” as used herein serves to reasonably encompass or describe minor variations in numerical values measured by instrumental analysis or as a result of sample handling. Such minor variations may be in the order of +0-25, 0-10, 0-5, or +0-2.5, % of the numerical values. Further, The term “about” applies to both numerical values when associated with a range of values. Moreover, the term “about” may apply to numerical values even when not explicitly stated.
Generally, as used herein a hyphen “-” or dash “-” in a range of values is “to” or “through”; a “>” is “above” or “greater-than”; a “≥” is “at least” or “greater-than or equal to”; a “<” is “below” or “less-than”; and a “≤” is “at most” or “less-than or equal to.” On an individual basis, each of the aforementioned applications for patent, patents, and/or patent application publications, is expressly incorporated herein by reference in its entirety in one or more non-limiting embodiments.
It is to be understood that the appended claims are not limited to express and particular compounds, compositions, or methods described in the detailed description, which may vary between particular embodiments which fall within the scope of the appended claims. With respect to any Markush groups relied upon herein for describing particular features or aspects of various embodiments, different, special, and/or unexpected results may be obtained from each member of the respective Markush group independent from all other Markush members. Each member of a Markush group may be relied upon individually and or in combination and provides adequate support for specific embodiments within the scope of the appended claims.
Further, any ranges and subranges relied upon in describing various embodiments of the present invention independently and collectively fall within the scope of the appended claims, and are understood to describe and contemplate all ranges including whole and/or fractional values therein, even if such values are not expressly written herein. One of skill in the art readily recognizes that the enumerated ranges and subranges sufficiently describe and enable various embodiments of the present invention, and such ranges and subranges may be further delineated into relevant halves, thirds, quarters, fifths, and so on. As just one example, a range “of from 0.1 to 0.9” may be further delineated into a lower third, i.e., from 0.1 to 0.3, a middle third, i.e., from 0.4 to 0.6, and an upper third, i.e., from 0.7 to 0.9, which individually and collectively are within the scope of the appended claims, and may be relied upon individually and/or collectively and provide adequate support for specific embodiments within the scope of the appended claims. In addition, with respect to the language which defines or modifies a range, such as “at least,” “greater than,” “less than,” “no more than,” and the like, it is to be understood that such language includes subranges and/or an upper or lower limit. As another example, a range of “at least 10” inherently includes a subrange of from at least 10 to 35, a subrange of from at least 10 to 25, a subrange of from 25 to 35, and so on, and each subrange may be relied upon individually and/or collectively and provides adequate support for specific embodiments within the scope of the appended claims. Finally, an individual number within a disclosed range may be relied upon and provides adequate support for specific embodiments within the scope of the appended claims. For example, a range “of from 1 to 9” includes various individual integers, such as 3, as well as individual numbers including a decimal point (or fraction), such as 4.1, which may be relied upon and provide adequate support for specific embodiments within the scope of the appended claims.
The following examples are intended to illustrate the invention and are not to be viewed in any way as limiting to the scope of the invention. Table 1 below sets forth abbreviations as utilized in the Examples.
Hydroxyl-Functional Intermediate
A dry 4 neck flask is placed into a temperature controlled heating block and fitted with a mechanical stirrer, thermometer, dropping funnel, and reflux condenser. The flask is purged with N2, and an organic compound having one terminal unsaturated group and one terminal hydroxyl group (Polyether Compound, 750.0 g, 0.94 mol) is disposed therein. The flask is heated to and kept at 105° C. for 2-3 hours under vacuum with intermittent N2 purging. The flask is then cooled to 85° C. A hydrosilylation catalyst is added (5 ppm, 1 wt. % solution of 0-0719 dissolved in MM). An endcapping organosilicon compound (ETM, 200.0 g, 0.71 mol) is added drop-wise. An adiabatic exotherm is observed with a 5-10° C. increase in temperature and the reaction temperature is kept at 85° C. by adjusting the addition of the endcapping organosilicon compound accordingly. The flask is heated to and held at 85° C. until the reaction is deemed complete (˜5 hr), i.e., when the detectible SiH concentration (via FTIR or 1H NMR) falls below 2.5 ppm. The contents of the flask are then cooled to room temperature and packaged to a Nalgene-container under N2 flow. The finished material is referred to as the hydroxyl-functional intermediate.
Isocyanate-Functional Intermediate
A dry 4 neck flask is placed into a temperature controlled heating block and fitted with a mechanical stirrer, thermometer, dropping funnel, and reflux condenser. The flask is then charged with the hydroxyl-functional intermediate (369.2 g), a polyisocyanate (IPDI, 75.6 g) used in an amount to target ˜2.5-3.00 wt. % residual NCO upon reaction completion, T-9 (0.02 g) to give a blend, which is then stirred until a uniform mixture is obtained. The mixture is heated to and held at 80° C. until the reaction is deemed complete (2 hr), i.e., when the target % NCO is reached (as measured via IR). The mixture is then cooled to room temperature to give an isocyanate-functional intermediate.
Silicone-Polyester Copolymer
The 4 neck flask containing the isocyanate-functional intermediate (118.1 g) is charged with the polyester compound (85.8 g, dissolved in EtAc) and heated to 40° C. The flask is then charged with T-12 (0.04 g) and heated to and held at 70° C. until the reaction is deemed complete (10 hr), i.e., until no NCO is detectable by FTIR. Once complete, the reaction mixture is cooled, transferred into a one neck round bottom flask, and stripped of volatiles under vacuum (rotary evaporator, 80° C.). The contents of the flask are then cooled to room temperature and packaged to a Nalgene-container under N2 flow. The finished material is referred to as the silicone-polyester copolymer.
The viscosity, Mn (GPC), and Mw (GPC), and polydispersity (PD) of the silicone-polyester copolymer are determined, and set forth in Table 2 below.
Cured Product
30 g of the silicone-polyester copolymer of Example 1, which is a solid at room temperature, are warmed up in a polypropylene dental cup in a 65° C. oven for two hours. Then 0.03 g of DBTDL and 0.15 g Z-6020 are added to give a mixture. The mixture is mixed on a FlackTek Speed Mixer DAC 150.1 FVZ at 3500 rpm for 1 minute. The mixture is then cast into a Teflon mold 15 cm by 15 cm in size and 2 mm deep. The cast plate is then stored in an environmentally controlled room (50% relative humidity and 25° C.) to cure for 7 days.
Tensile Analysis
Dogbone specimens (5 cm total length, 2 cm neck length) are cut (stamped) from the cured product with a carbon steel die for tensile testing. The tensile properties of the dogbone specimens are then analyzed. A MTS testing frame with a load cell of 100 N full capacity is used for the test. The testing speed is 50.8 cm/min. The strain is calculated as the displaced over the length of the narrow neck. Stress at break is calculated by dividing the peak stress with the initial cross-sectional area of the narrow neck region. The dogbone specimens are also aged in a heated air circulating oven at 60° C. or 80° C. for a certain length of time, and tensile tested to gauge the stability thereof.
Differential Scanning Calorimetry (DSC)
Small pieces are cut from the cured product for differential scanning calorimetry (DSC). DSC is performed with a TA Instrument Discovery Series DSC2500. The sample is weighed into Tzero aluminum pans (˜10 mg of sample) and analyzed on the instrument, the temperature is first ramped down to −180° C. (at 10° C./min) and then up to 200° C. (at 10° C./min). The heat needed to keep up with the ramping process is recorded and the Tg is detected as an abrupt change in heat capacity.
Tack Free Time
Tack free time is measured using a Gardco BK six track drying time recorder for coatings according to ASTM D5895, by coating a 150 micrometer thick, 12 mm wide coating layer on an aluminum strip, placing a needle into the coating layer with a weight of 5 g applied on the top of the needle, and dragging the needle through the coating. Observation of the track left behind over a period of time determines the tack free time.
Hardness
Hardness is measured with a Zwick Roell Hardness tester with a 12.5 N force applied and based on the 00 scale. Properties measured from the cured product are listed in Table 3 below.
Example 3 utilizes the silicone-polyester copolymer of Example 1. Prior to compounding, a pre-mix solution of 0. Z-6020 and DBTDL are combined in a one ounce glass vial. This solution is shaken by hand until a clear straw solution is obtained and set aside for later use. The silicone-polyester copolymer is warmed in a 70° C. oven until flowable. At any point during the mixing process, additional mixing steps of 30 seconds at 2000 rpm are performed if the silicone-polyester copolymer started to thicken as the silicone-polyester copolymer cooled. A max 300 long mixing jar designed for use with the DAC 600.2 VAC SpeedMixer is tared on a balance and then the silicone-polyester copolymer, DINP, and VTM are added. This is mixed at 800 rpm for 30 seconds and then 1500 rpm for 30 seconds. CC is then added to the mixing jar and allowed to mix for 30 seconds at 800 rpm, removed from the mixer and the jar scraped by hand, and reinserted to mix for an additional 30 seconds at 1500 rpm. After this mixing step, CS-11 is weighed into the mixing jar and the jar is placed back into the mixer, and allowed to mix for 30 seconds at 1300 rpm. The jar is then removed, hand scraped to re-incorporate any particles of filler, and then placed back into the mixer for 30 seconds at 2000 rpm. After filler incorporation, the pre-mix solution is added to the mixing jar and then allowed to mix for 30 seconds at 1300 rpm after which the jar is removed and hand scraped. Finally, the jar lid is replaced with one with a hole in the center to allow entrapped air or volatiles to escape the mixing jar for the vacuum step. A final mixing step is performed with vacuum according to the following program: 37 seconds of mixing at 800 rpm to 3.5 psi vacuum, 40 seconds of mixing at 1300 rpm holding 3.5 psi vacuum, and 35 seconds of mixing at 800 rpm to break vacuum to ambient laboratory conditions. A sealant mixture is then packaged into a SEMCO cartridge and set aside for testing.
The sealant mixture is set forth below in Table 4. The amount of VTM, Z-6020, and DBTDL are adjusted during compounding.
The physical and curing properties of Example 3 are evaluated in accordance with the following respective procedures:
Tack Free Time: A 100 mil thick slab of the particular sealant is drawn down on a piece of polyethylene terephthalate (PET). A small strip of PET is then lightly pressed onto the surface of the particular sealant to check for cure. When no sealant is transferred to the strip of PET, the sealant is considered tack free.
Extrusion Rate: A SEMCO Nozzle Type 440 is affixed to a 6-oz SEMCO tube. A brief extrusion is performed to fill the extrusion nozzle. Material is then allowed to extrude for 3 seconds at an applied pressure of 90 psi and the material is collected into a tared container to measure the mass extruded. Extrusion rate is then calculated in grams per minute. The extrusion rate is then calculated in grams per minute as an average of the three data points.
The particular sealant is cured at 50% relative humidity and 23° C. for seven days. Durometer is measured by ASTM Method D2240, Type A. Tensile, Elongation, and Modulus are measured by ASTM Method D412. Physical properties are below in Table 5. A 100% modulus value could not be obtained as the maximum elongation was below 100% extension.
The invention has been described in an illustrative manner, and it is to be understood that the terminology which has been used is intended to be in the nature of words of description rather than of limitation. Obviously, many modifications and variations of the present invention are possible in light of the above teachings. The invention may be practiced otherwise than as specifically described.
This application is the National Stage of International Appl. No. PCT/US2019/066556 filed on Dec. 16, 2019, which claims priority to and all advantages of U.S. Provisional Patent Application No. 62/783,697 filed on 21 Dec. 2018, the content of which is incorporated herein by reference.
| Filing Document | Filing Date | Country | Kind |
|---|---|---|---|
| PCT/US2019/066556 | 12/16/2019 | WO |
| Publishing Document | Publishing Date | Country | Kind |
|---|---|---|---|
| WO2020/131705 | 6/25/2020 | WO | A |
| Number | Name | Date | Kind |
|---|---|---|---|
| 3398174 | Barnes, Jr. | Aug 1968 | A |
| 3419635 | Vaughn, Jr. | Dec 1968 | A |
| 3592795 | Ashby | Jul 1971 | A |
| 3971751 | Isayama et al. | Jul 1976 | A |
| 3972751 | Engelhard | Aug 1976 | A |
| 4207071 | Lipowitz et al. | Jun 1980 | A |
| 4242466 | Schilling, Jr. | Dec 1980 | A |
| 4283519 | Pines et al. | Aug 1981 | A |
| 4323488 | Takago et al. | Apr 1982 | A |
| 4345053 | Rizk et al. | Aug 1982 | A |
| 4546146 | Kobashi et al. | Oct 1985 | A |
| 4625012 | Rizk et al. | Nov 1986 | A |
| 4772675 | Klosowski et al. | Sep 1988 | A |
| 4960844 | Singh | Oct 1990 | A |
| 5109064 | Wakabayashi et al. | Apr 1992 | A |
| 5130413 | Asai et al. | Jul 1992 | A |
| 5403881 | Okawa et al. | Apr 1995 | A |
| 5457166 | Yoshikawa et al. | Oct 1995 | A |
| 5552223 | Mikami et al. | Sep 1996 | A |
| 5569691 | Guggenberger et al. | Oct 1996 | A |
| 5623044 | Chiao | Apr 1997 | A |
| 5811566 | Watabe et al. | Sep 1998 | A |
| 5840800 | Joffre et al. | Nov 1998 | A |
| 5852137 | Hsieh et al. | Dec 1998 | A |
| 6132664 | Gutek et al. | Oct 2000 | A |
| 6204350 | Liu et al. | Mar 2001 | B1 |
| 6235832 | Deng et al. | May 2001 | B1 |
| 6258878 | Bahadur et al. | Jul 2001 | B1 |
| 6265518 | Krahnke et al. | Jul 2001 | B1 |
| 6395341 | Arakawa et al. | May 2002 | B1 |
| 6437071 | Odaka et al. | Aug 2002 | B1 |
| 6503995 | Tsuji et al. | Jan 2003 | B2 |
| 6541593 | Jyono et al. | Apr 2003 | B1 |
| 7223817 | Nakagawa et al. | May 2007 | B2 |
| 7279589 | Uehara et al. | Oct 2007 | B2 |
| 7345130 | Zhu et al. | Mar 2008 | B2 |
| 7601428 | Yamane et al. | Oct 2009 | B2 |
| 7625990 | Wakabayashi et al. | Dec 2009 | B2 |
| 7763699 | Odaka et al. | Jul 2010 | B2 |
| 7794843 | Yamane et al. | Sep 2010 | B2 |
| 7829649 | Yamane et al. | Nov 2010 | B2 |
| 7893170 | Wakioka et al. | Feb 2011 | B2 |
| 7960459 | Noro et al. | Jun 2011 | B2 |
| 7973108 | Okamoto et al. | Jul 2011 | B2 |
| 7994262 | Kono | Aug 2011 | B2 |
| 8030427 | Wakabayashi et al. | Oct 2011 | B2 |
| 8084552 | Herzig | Dec 2011 | B2 |
| 8158723 | Lucet et al. | Apr 2012 | B2 |
| 8178645 | Popa et al. | May 2012 | B2 |
| 8450514 | Schubert et al. | May 2013 | B2 |
| 8481640 | Gough et al. | Jul 2013 | B2 |
| 8592545 | Mackinnon et al. | Nov 2013 | B2 |
| 8697815 | Rutz et al. | Apr 2014 | B2 |
| 8822626 | Vyakaranam et al. | Sep 2014 | B2 |
| 8877885 | Vyakaranam et al. | Nov 2014 | B2 |
| 9428617 | Mittal et al. | Aug 2016 | B2 |
| 9598578 | Groote et al. | Mar 2017 | B1 |
| 9617390 | Hinzmann et al. | Apr 2017 | B2 |
| 10358526 | Müller et al. | Jul 2019 | B2 |
| 20020010245 | Enami et al. | Jan 2002 | A1 |
| 20020013427 | Tsuji et al. | Jan 2002 | A1 |
| 20020084030 | Kotani et al. | Jul 2002 | A1 |
| 20030027974 | Tamai et al. | Feb 2003 | A1 |
| 20040138398 | Fujimoto et al. | Jul 2004 | A1 |
| 20050107547 | Ohno et al. | May 2005 | A1 |
| 20050222332 | Nakagawa et al. | Oct 2005 | A1 |
| 20060128919 | Okamoto et al. | Jun 2006 | A1 |
| 20060293480 | Landon et al. | Dec 2006 | A1 |
| 20070037997 | Uehara | Feb 2007 | A1 |
| 20070093628 | Zhu et al. | Apr 2007 | A1 |
| 20070116907 | Landon et al. | May 2007 | A1 |
| 20070173620 | Kono | Jul 2007 | A1 |
| 20070219299 | Okamoto et al. | Sep 2007 | A1 |
| 20070290202 | Matsumoto et al. | Dec 2007 | A1 |
| 20080051547 | Wakabayashi et al. | Feb 2008 | A1 |
| 20080071042 | Yamane et al. | Mar 2008 | A1 |
| 20090182091 | Noro et al. | Jul 2009 | A1 |
| 20100041910 | Schubert et al. | Feb 2010 | A1 |
| 20100168309 | Mackinnon et al. | Jul 2010 | A1 |
| 20100216925 | Yano | Aug 2010 | A1 |
| 20100234518 | Ferrito et al. | Sep 2010 | A1 |
| 20100280148 | Webster et al. | Nov 2010 | A1 |
| 20110040036 | Herzig | Feb 2011 | A1 |
| 20110245144 | Messner et al. | Oct 2011 | A1 |
| 20120135241 | Yasuda et al. | May 2012 | A1 |
| 20120214925 | Gubbels et al. | Aug 2012 | A1 |
| 20120228864 | Gallucci et al. | Nov 2012 | A1 |
| 20130060000 | Zhang et al. | Mar 2013 | A1 |
| 20130096252 | Vyakaranam et al. | Apr 2013 | A1 |
| 20130096274 | Vyakaranam et al. | Apr 2013 | A1 |
| 20140010853 | Williams et al. | Jan 2014 | A1 |
| 20140018485 | Cook et al. | Jan 2014 | A1 |
| 20140024774 | Cook et al. | Jan 2014 | A1 |
| 20140127140 | Ferrito et al. | May 2014 | A1 |
| 20140128539 | Liu | May 2014 | A1 |
| 20140249280 | Kim et al. | Sep 2014 | A1 |
| 20140256888 | Ishikawa et al. | Sep 2014 | A1 |
| 20140302318 | Ferrito et al. | Oct 2014 | A1 |
| 20150087773 | Williams et al. | Mar 2015 | A1 |
| 20150166733 | Nagao et al. | Jun 2015 | A1 |
| 20150183951 | Bhagwagar et al. | Jul 2015 | A1 |
| 20150259581 | Miyafuji | Sep 2015 | A1 |
| 20150353741 | Liao | Dec 2015 | A1 |
| 20160122478 | Ferrito et al. | May 2016 | A1 |
| 20160130402 | Schubert et al. | May 2016 | A1 |
| 20160168175 | Haaf-Kleinhubbert et al. | Jun 2016 | A1 |
| 20160222169 | Hinzmann et al. | Aug 2016 | A1 |
| 20170107374 | Harumashi et al. | Apr 2017 | A1 |
| 20170130096 | Grunlan et al. | May 2017 | A1 |
| 20170306096 | Muthusamy et al. | Oct 2017 | A1 |
| 20170313816 | Muller et al. | Nov 2017 | A1 |
| 20170369648 | Willumstad et al. | Dec 2017 | A1 |
| 20180002491 | Peeters | Jan 2018 | A1 |
| 20210309792 | Stanjek et al. | Oct 2021 | A1 |
| Number | Date | Country |
|---|---|---|
| 1096039 | Dec 1994 | CN |
| 101151329 | Mar 2008 | CN |
| 101959938 | Jan 2011 | CN |
| 102473056 | May 2012 | CN |
| 103534297 | Jan 2014 | CN |
| 103930466 | Jul 2014 | CN |
| 103958573 | Jul 2014 | CN |
| 104395373 | Mar 2015 | CN |
| 104471012 | Mar 2015 | CN |
| 107075063 | Aug 2017 | CN |
| 108350263 | Jul 2018 | CN |
| 0265929 | May 1988 | EP |
| 0352339 | Jan 1990 | EP |
| 0415404 | Mar 1991 | EP |
| 0693513 | Jan 1996 | EP |
| 1153942 | Nov 2001 | EP |
| 1746133 | Jan 2007 | EP |
| S45027718 | Sep 1970 | JP |
| 53139695 | Dec 1978 | JP |
| S53139695 | Dec 1978 | JP |
| S57158226 | Sep 1982 | JP |
| S6088017 | May 1985 | JP |
| 03140316 | Jun 1991 | JP |
| H03140316 | Jun 1991 | JP |
| H04202317 | Jul 1992 | JP |
| H06145359 | May 1994 | JP |
| H06166810 | Jun 1994 | JP |
| H06211922 | Aug 1994 | JP |
| H0753723 | Feb 1995 | JP |
| H0912709 | Jan 1997 | JP |
| H11172003 | Jun 1999 | JP |
| H11255883 | Sep 1999 | JP |
| H11279274 | Oct 1999 | JP |
| 2000327771 | Nov 2000 | JP |
| 2001049113 | Feb 2001 | JP |
| 2002226564 | Aug 2002 | JP |
| 2002533518 | Oct 2002 | JP |
| 2002356613 | Dec 2002 | JP |
| 2004123893 | Apr 2004 | JP |
| 2005008833 | Jan 2005 | JP |
| 2005306891 | Nov 2005 | JP |
| 2006328416 | Dec 2006 | JP |
| 2007091929 | Apr 2007 | JP |
| 2007091930 | Apr 2007 | JP |
| 2008088412 | Apr 2008 | JP |
| 20071974285 | Oct 2012 | JP |
| 2013508493 | Mar 2013 | JP |
| 2013532226 | Aug 2013 | JP |
| 2016530357 | Sep 2016 | JP |
| 2002094938 | Nov 2002 | WO |
| 2004108774 | Dec 2004 | WO |
| 2007075927 | Jul 2007 | WO |
| 2012119940 | Sep 2012 | WO |
| 2012148635 | Nov 2012 | WO |
| 2013003051 | Jan 2013 | WO |
| 2014038656 | Mar 2014 | WO |
| 2014106610 | Jul 2014 | WO |
| 2014112321 | Jul 2014 | WO |
| 2014126599 | Aug 2014 | WO |
| 2015003875 | Jan 2015 | WO |
| 2015023372 | Feb 2015 | WO |
| 2016002907 | Jan 2016 | WO |
| 2016046110 | Mar 2016 | WO |
| 2016114376 | Jul 2016 | WO |
| 2020035154 | Feb 2020 | WO |
| Entry |
|---|
| Machine translation of JP 2005-008833 (no date). |
| Machine translation of JP 03-140316 (no date). |
| Machine translation of JP 53-139695 (no date). |
| Machine assisted English translation of JP2000327771A obtained from https://patents.google.com/patent on May 7, 2023, 9 pages. |
| Machine assisted English translation of JP2007091929A obtained from https://worldwide.espacenet.com/ on May 4, 2023, 26 pages. |
| Machine assisted English translation of JP2006328416A obtained from https://patents.google.com/patent on Mar. 7, 2023, 31 pages. |
| Machine assisted English translation of CN101151329A, obtained from https://patents.google.com/ on Feb. 2, 2022, 20 pages. |
| Machine assisted English translation of JPH06211922A obtained from https://patents.google.com/patent on Feb. 21, 2023, 19 pages. |
| Machine assisted English translation of JPS53139695, obtained from espacenet.com on Sep. 23, 2021, 9 pages. |
| Machine assisted English translation of JPH03140316, obtained from espacenet.com on Sep. 23, 2021, 6 pages. |
| Machine assisted English translation of JP2002226564, obtained from espacenet.com on Sep. 23, 2021, 12 pages. |
| Machine assisted English translation of JP2004123893, obtained from espacenet.com on Sep. 23, 2021, 11 pages. |
| Machine assisted English translation of WO2004108774, obtained from patents.google.com on Sep. 23, 2021, 27 pages. |
| Machine assisted English translation of JPH11172003A obtained from https://patents.google.com/patent on Dec. 14, 2021, 27 pages. |
| Machine assisted English translation of JP2006328416A obtained from https://patents.google.com/patent on Dec. 14, 2021, 20 pages. |
| Machine assisted English translation of JPH0753723A obtained from https://patents.google.com/patent on Dec. 14, 2021, 8 pages. |
| Machine assisted English translation of JPH04202317A obtained from https://worldwide.espacenet.com/patent on Dec. 14, 2021, 5 pages. |
| Machine assisted English translation of JPS57158226A obtained from https://worldwide.espacenet.com/patent on Jun. 7, 2022, 4 pages. |
| Machine assisted English translation of JPH0912709A obtained from https://worldwide.espacenet.com/patent on Jun. 7, 2022, 8 pages. |
| International Search Report for PCT/US2019/066556 dated Aug. 12, 2020, 4 pages. |
| Machine assisted English translation of JPH11255883A obtained from https://patents.google.com/patent on Sep. 20, 2021, 12 pages. |
| Machine assisted English translation of JPH11279274A obtained from https://patents.google.com/patent on Sep. 20, 2021, 26 pages. |
| Machine assisted English translation of JP2007091930A obtained from https://patents.google.com/patent on Sep. 20, 2021, 16 pages. |
| Machine assisted English translation of WO2014112321A1 obtained from https://patents.google.com/patent on Sep. 20, 2021, 12 pages. |
| Number | Date | Country | |
|---|---|---|---|
| 20220041813 A1 | Feb 2022 | US |
| Number | Date | Country | |
|---|---|---|---|
| 62783697 | Dec 2018 | US |