Claims
- 1. A silicone rubber composition for injection molding, which comprises
- (A) 100 parts by weight of a polyorganosiloxane having at least 2 monovalent aliphatic unsaturated hydrocarbon groups bonded to a silicon atom in the molecule;
- (B) a polyorganohydrogensiloxane having at least 3 hydrogen atoms bonded to the silicon atom in the molecule in an amount such that the number of the hydrogen atoms bonded to the silicon atom becomes from 0.5 to 5 per one monovalent aliphatic unsaturated hydrocarbon group in the component (A);
- (C) a platinum type catalyst in an amount of from 1 to 100 ppm by weight converted as a platinum atom based on the weight of the component (A);
- (D) from 20 to 200 parts by weight of a silica fine powder;
- (E) from 0.01 to 1.0 part by weight of azodicarbon amide;
- (F) from 0.5 to 15 parts by weight of carbon black; and
- (G) from 0.1 to 2.0 parts by weight of at least one kind of cerium hydroxide and cerium oxide.
- 2. The composition as claimed in claim 1, wherein the component (A) has a viscosity at 25.degree. C. of from 500 to 500,000 cP.
- 3. The composition as claimed in claim 1, wherein the component (B) is:
- a. A branched polyorganohydrogensiloxane comprising a (CH.sub.3).sub.2 HSiO.sub.2 unit and a SiO.sub.2 unit;
- b. A straight chain polyorganohydrogensiloxane represented by the following formula (1) ##STR4## wherein p represents an integer of from 3 to 100 and q represents an integer of from 0 to 100; or
- c. A straight chain polyorganohydrogensiloxane represented by the following formula (2) ##STR5## wherein p represents an integer of from 1 to 100 and q represents an integer of from 0 to 100.
- 4. The composition as claimed in claim 1, wherein the component (C) is chloroauric acid, a platinum-olefin complex, a platinum-vinylsiloxane complex, or a platinum-phosphine complex.
- 5. The composition as claimed in claim 1, wherein the component (C) is used in an amount of from 2 to 50 ppm by weight calculated as a platinum atom based on the weight of the component (A).
- 6. The composition as claimed in claim 1, wherein the component (D) is fumed silica, precipitated silica, silica aerogel, molten silica, a quartz powder, or diatomaceous earth.
- 7. The composition as claimed in claim 1, wherein the component (D) is used in an amount of form 60 to 120 parts by weight per 100 parts by weight of the component (A).
- 8. The composition as claimed in claim 1, wherein the component (E) is a compound represented by the following formula (3) or (4):
- R.sup.1 --N.dbd.N--R.sup.2 ( 3) ##STR6## wherein R.sup.1 and R.sup.2 each represents a substituted or unsubstituted hydrocarbon group or aminocarbonyl group.
- 9. The composition as claimed in claim 1, wherein the component (E) is used in an amount of from 0.1 to 0.5 part by weight per 100 parts by weight of the component (A).
- 10. The composition as claimed in claim 1, wherein the component (F) is furnace black, thermal black, channel black, acetylene black or ketchen black.
- 11. The composition as claimed in claim 1, wherein the component (F) is used in an amount of from 1 to 5 parts by weight per 100 parts by weight of the component (A).
- 12. The composition as claimed in claim 1, wherein the component (G) is used in an amount of from 0.2 to 1.2 parts by weight per 100 parts by weight of the component (A).
Priority Claims (1)
Number |
Date |
Country |
Kind |
5-212449 |
Aug 1993 |
JPX |
|
Parent Case Info
This is a Continuation of application Ser. No. 08/297,037 filed Aug. 29, 1994 now abandoned.
US Referenced Citations (11)
Foreign Referenced Citations (3)
Number |
Date |
Country |
0037226 |
Oct 1981 |
EPX |
0415180 |
Mar 1991 |
EPX |
0490523 |
Jun 1992 |
EPX |
Continuations (1)
|
Number |
Date |
Country |
Parent |
297037 |
Aug 1994 |
|