Claims
- 1. A foamable silicone rubber sponge composition consisting essentially of
- (A) 100 parts by weight of a polyorganosiloxane having an average degree of polymerization of 3,000 to 300,000
- (B) 1 to 100 parts by weight of a reinforcing silica filler,
- (C) 1 to 30 parts by weight, per 100 parts by weight of the sum of components (A) and (B), of 1,1'-azo-bis(1-acetoxy-1-phenylethane) as a foaming agent which can be decomposed to generate a gas to yield a sponge, and
- (D) at least one member selected from the group consisting of organic peroxides in an amount of 0.05 to 15 parts by weight of the polyorganosiloxane (A) and the reinforcing silica filler (B) and addition reaction type curing agents which will act to cure the sponge composition.
- 2. The foamable silicone rubber sponge composition as claimed in claim 1, wherein the at least one kind of organic peroxides (D) is an acyl type organic peroxide having a half-life period temperature for 1 minute of 100 to 150.degree. C.
- 3. The foamable silicone rubber sponge composition as claimed in claim 1, wherein the component (D) is the addition reaction type curing agents.
- 4. The foamable silicone rubber sponge composition as claimed in claim 1, wherein the component (C) has an average particle diameter of 100 .mu.m or less.
- 5. The foamable silicone rubber sponge composition as claimed in claim 1, wherein the composition further comprises oxides, hydroxides or carbonates of Group I or II metals in the periodic table, or hydrotalcite compounds in an amount of 0.1 to 30 parts by weight per 100 parts by weight of the components (A) and (B).
- 6. A silicone rubber sponge obtained by foaming and curing the silicone rubber sponge composition as claimed in claim 1.
- 7. The silicone rubber sponge as claimed in claim 6, wherein the sponge has a foaming ratio of 2 to 6 times.
- 8. A silicone rubber sponge obtained by foaming and curing the foamable silicone rubber sponge composition as claimed in claim 5.
- 9. The silicone rubber sponge as claimed in claim 8, wherein the sponge has a foaming ratio of 2 to 6 times.
Priority Claims (1)
Number |
Date |
Country |
Kind |
6-271107 |
Nov 1994 |
JPX |
|
CROSS REFERENCE TO THE RELATED APPLICATION
This application is a continuation-in-part application of U.S. patent application Ser. No. 08/551,425, filed Nov. 1, 1995, abandoned, entitled "SILICONE RUBBER SPONGE COMPOSITION AND SILICONE RUBBER SPONGE USING IT".
US Referenced Citations (5)
Foreign Referenced Citations (2)
Number |
Date |
Country |
0073038 |
Mar 1983 |
EPX |
2137630 |
Mar 1984 |
GBX |
Continuation in Parts (1)
|
Number |
Date |
Country |
Parent |
551425 |
Nov 1995 |
|