Silk Coated Fabrics and Products and Methods of Preparing the Same

FIELD OF THE INVENTION

In some embodiments, the invention relates to silk-coated performance materials, apparel, and products for use in home and automotive applications, such as fabrics coated with pure silk fibroin-based proteins or protein fragments thereof.

BACKGROUND OF THE INVENTION

Silk is a natural polymer produced by a variety of insects and spiders, and comprises a filament core protein, silk fibroin, and a glue-like coating consisting of a non-filamentous protein, sericin. Silk fibers are light weight, breathable, and hypoallergenic. Silk is comfortable when worn next to the skin and insulates very well; keeping the wearer warm in cold temperatures and is cooler than many other fabrics in warm temperatures.

SUMMARY OF THE INVENTION

In an embodiment, a method is provided for coating a material with silk fibroin that may include silk-based proteins or fragments thereof to provide a silk fibroin coated material, wherein the silk fibroin coated upon the silk fibroin coated material may be heat resistant to a selected temperature. In some embodiments, the method may include preparing a silk fibroin solution that may include a concentration of one or more of low molecular weight silk fibroin, medium molecular weight silk fibroin, and high molecular weight silk fibroin at less than about 1% by volume (v/v), or less than about by volume (v/v), or less than about 0.01% by volume (v/v), or less than about by volume (v/v). In some embodiments, the method may include, coating a surface of the material with the silk fibroin solution. In some embodiments, the method may include drying the surface of the material that has been coated with the silk fibroin solution to provide the silk fibroin coated material, wherein drying the surface of the material comprises heating the surface of the material without substantially decreasing silk fibroin coating performance.

In an embodiment, a method is provided for coating a textile with a silk fibroin solution that may include silk-based proteins or fragments thereof to provide a silk fibroin coated article, wherein the silk fibroin coated upon the silk fibroin coated article may be heat resistant to a selected temperature. In some embodiments, the method may include preparing the silk fibroin solution with one or more of low molecular weight silk fibroin, medium molecular weight silk fibroin, and high molecular weight silk fibroin. In some embodiments, the method may include acidically adjusting the pH of the silk fibroin solution with an acidic agent. In some embodiments, the method may include coating a surface of the textile with the silk fibroin solution. In some embodiments, the method may include drying the surface of the textile that has been coated with the silk fibroin solution to provide the silk fibroin coated article, wherein drying the surface of the textile comprises heating the surface of the textile without substantially decreasing silk fibroin coating performance.

In some embodiments, a method is provided for manufacturing a silk fibroin coated textile that may include selected fabric properties. In some embodiments, the method may include admixing silk-based proteins or fragments thereof with one or more chemical agents to provide a coating solution, wherein the one or more chemical agents may be selected to modify one or more of a first selected property and second selected property of the silk fibroin coated textile. In some embodiments, the method may include providing the coating solution to a textile to be coated with one or more of a bath coating process, a kiss rolling process, a spray process, and a two-sided rolling process. In some embodiments, the method may include removing excess coating solution from the silk fibroin coated textile. In some embodiments, the method may include heating the silk fibroin coated textile to modify a third selected property of the silk fibroin coated textile. In some embodiments, the first selected property may include one or more of an antimicrobial property, an antiodor property, a water repellant property, an oil repellant property, a flame retardant property, a coloring property, a fabric softening property, a stain repellant property, a pH adjusting property, an anticrocking property, an antipilling property, and an antifelting property. In some embodiments, the second selected property may include one or more of wetting time, absorption rate, spreading speed, accumulative one-way transport, drying rate, and overall moisture management capability. In some embodiments, the third selected property may include one or more of fabric hand, fabric stretch, fabric recovery, fabric stretch and recovery, and drapability.

In an embodiment, a selected property of the SFS coated articles that may be enhanced as compared to non-coated articles may include one or more of dimensional stability to laundering, dimensional stability to dry cleaning, appearance after laundering, appearance after dry cleaning, colorfastness to laundering, colorfastness to dry cleaning, colorfastness to non-chlorine bleach, seam torque/spirality (on knits), colorfastness to crocking, colorfastness to rubbing, colorfastness to water, colorfastness to light, colorfastness to perspiration, colorfastness to chlorinated pool water, colorfastness to sea water, tensile strength, seam slippage, tearing strength, seam breaking strength, abrasion resistance, pilling resistance, stretch recovery, bursting strength, colorfastness to die transfer in storage (labels), colorfastness to ozone, pile retention, bowing and skewing, colorfastness to saliva, snagging resistance, wrinkle resistance (e.g., appearance of apparel, retention of creases in fabrics, smooth appearance of fabrics), water repellency, water resistance, stain repellant (e.g., water repellency, oil repellency, water/alcohol repellency), vertical wicking, water absorption, dry rate, soil release, air permeability, wicking, antimicrobial properties, ultraviolet protection, resistance to torque, malodor resistant, biocompatibility, wetting time, absorption rate, spreading speed, accumulative one-way transport, flame retardant properties, coloring properties, fabric softening properties, a pH adjusting property, an antifelting property, and overall moisture management capability.

In an embodiment, the silk fibroin coated materials of the invention may be coated with one or more of low molecular weight silk, medium molecular weight silk, and high molecular weight silk to provide resulting coated materials having enhanced hydrophobic or hydrophilic properties.

In an embodiment, the silk fibroin coated materials of the invention, for example a fiber, a yarn, or a fabric, may be coated with compositions including one or more of low molecular weight silk, medium molecular weight silk, and high molecular weight silk, to provide resulting coated materials having enhanced hydrophobic or hydrophilic properties. In an embodiment, the silk fibroin coated materials of the invention, for example a fiber, a yarn, or a fabric, may be coated with compositions including low molecular weight silk and medium molecular weight silk. In an embodiment, the silk fibroin coated materials of the invention, for example a fiber, a yarn, or a fabric, may be coated with compositions including low molecular weight silk and high molecular weight silk. In an embodiment, the silk fibroin coated materials of the invention, for example a fiber, a yarn, or a fabric, may be coated with compositions including medium molecular weight silk and high molecular weight silk. In an embodiment, the silk fibroin coated materials of the invention, for example a fiber, a yarn, or a fabric, may be coated with compositions including low molecular weight silk, medium molecular weight silk, and high molecular weight silk.

In and embodiment, materials coated by silk fibroin coatings described herein may include one or more of textiles, woven materials, non-woven materials, knit materials, crochet materials, and leather materials.

In an embodiment, the invention provides an article comprising a fiber or yarn having a coating, wherein the coating comprises silk based proteins or fragments thereof having an average number of amino acid residues of about 1 to 400 residues, or 1 to 300 residues, or 1 to 200 residues, or 1 to 100 residues, or 1 to 50 residues, or 5 to 25 residues, or 10 to 20 residues.

In an embodiment, the invention provides an article comprising a fiber or yarn having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 5 kDa to about 144 kDa, wherein the silk based proteins or fragments thereof comprise silk fibroin-based proteins or protein fragments having about 0.01% (w/w) to about 10% (w/w) sericin.

In an embodiment, the invention provides an article comprising a fiber or yarn having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 5 kDa to about 144 kDa, wherein the silk based proteins or fragments thereof are selected from the group consisting of natural silk based proteins or fragments thereof, recombinant silk based proteins or fragments thereof, and combinations thereof.

In an embodiment, the invention provides an article comprising a fiber or yarn having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 5 kDa to about 144 kDa, wherein the silk based proteins or fragments thereof are selected from the group consisting of natural silk based proteins or fragments thereof, recombinant silk based proteins or fragments thereof, and combinations thereof, wherein the silk based proteins or fragments thereof are natural silk based proteins or fragments thereof that are selected from the group consisting of spider silk based proteins or fragments thereof, silkworm silk based proteins or fragments thereof, and combinations thereof.

In an embodiment, the invention provides an article comprising a fiber or yarn having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 5 kDa to about 144 kDa, wherein the silk based proteins or fragments thereof are selected from the group consisting of natural silk based proteins or fragments thereof, recombinant silk based proteins or fragments thereof, and combinations thereof, wherein the silk based proteins or fragments thereof are natural silk based proteins or fragments thereof that are selected from the group consisting of spider silk based proteins or fragments thereof, silkworm silk based proteins or fragments thereof, and combinations thereof, wherein the natural silk based proteins or fragments are silkworm silk based proteins or fragments thereof, and the silkworm silk based proteins or fragments thereof is Bombyx mori silk based proteins or fragments thereof.

In an embodiment, the invention provides an article comprising a fiber or yarn having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 5 kDa to about 144 kDa, wherein the silk based proteins or protein fragments thereof have an average weight average molecular weight range selected from the group consisting of about 5 to about 10 kDa, about 6 kDa to about 17 kDa, about 17 kDa to about 39 kDa, about 39 kDa to about 80 kDa, about 60 to about 100 kDa, and about 80 kDa to about 144 kDa, wherein the silk based proteins or fragments thereof have a polydispersity of between about 1.5 and about 3.0, and wherein the proteins or protein fragments, prior to coating the fabric, do not spontaneously or gradually gelate and do not visibly change in color or turbidity when in a solution for at least 10 days.

In an embodiment, the invention provides an article comprising a fiber or yarn having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 5 kDa to about 144 kDa, wherein the fiber or yarn is selected from the group consisting of natural fiber or yarn, synthetic fiber or yarn, or combinations thereof.

In an embodiment, the invention provides an article comprising a fiber or yarn having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 5 kDa to about 144 kDa, wherein the fiber or yarn is selected from the group consisting of natural fiber or yarn, synthetic fiber or yarn, or combinations thereof, wherein the fiber or yarn is natural fiber or yarn selected from the group consisting of cotton, silk, alpaca fleece, alpaca wool, lama fleece, lama wool, cotton, cashmere, sheep fleece, sheep wool, and combinations thereof.

In an embodiment, the invention provides an article comprising a fiber or yarn having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 5 kDa to about 144 kDa, wherein the fiber or yarn is selected from the group consisting of natural fiber or yarn, synthetic fiber or yarn, or combinations thereof, wherein the fiber or yarn is synthetic fiber or yarn selected from the group consisting of polyester, nylon, polyester-polyurethane copolymer, acrylic polymer or copolymer, rayon, i.e., semi-synthetic fiber made of modified cellulose, and combinations thereof.

In an embodiment, the invention provides an article comprising a fiber or yarn having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 5 kDa to about 144 kDa, and wherein the coating has a thickness selected from the group consisting of about 5 nm, about 10 nm, about 15 nm, about 20 nm, about 25 nm, about 50 nm, about 100 nm, about 200 nm, about 500 nm, about 1 about 5 about 10 and about 20 μm.

According to aspects illustrated herein, an aqueous solution of pure silk fibroin-based protein fragments of the present disclosure is available for application to a product, including, but not limited to, apparel, padding, shoes, gloves, luggage, furs, jewelry and bags, or for directly spraying on the body of a consumer, to impart desired properties to the product.

Silk performance apparel and methods of preparing the same are disclosed herein. According to aspects illustrated herein, the present disclosure relates to apparel configured to be worn or carried on the body, that is at least partially surface treated with a solution of pure silk fibroin-based protein fragments of the present disclosure so as to result in a silk coating on the product. In some embodiments, the solutions of silk fibroin-based proteins or fragments thereof may be aqueous solutions, organic solutions, or emulsions. In an embodiment, the product is manufactured from a textile material. In an embodiment, the product is manufactured from a non-textile material. In an embodiment, desired additives can be added to an aqueous solution of pure silk fibroin-based protein fragments of the present disclosure so as to result in a silk coating having desired additives.

In an embodiment, a textile comprising a silk coating of the present disclosure is sold to a consumer. In an embodiment, a textile of the present disclosure is used in constructing action sportswear apparel. In an embodiment, a textile of the present disclosure is used in constructing fitness apparel. In an embodiment, a textile of the present disclosure is used in constructing performance apparel. In an embodiment, a textile of the present disclosure is used in constructing golf apparel. In an embodiment, a textile of the present disclosure is used in constructing lingerie. In an embodiment, a silk coating of the present disclosure is positioned on the underlining of action sportswear/apparel. In an embodiment, a silk coating of the present disclosure is positioned on the shell, the lining, or the interlining of action sportswear/apparel. In an embodiment, action sportswear/apparel is partially made from a silk coated textile of the present disclosure and partially made from an uncoated textile. In an embodiment, action sportswear/apparel partially made from a silk coated textile and partially made from an uncoated textile combines an uncoated inert synthetic material with a silk coated inert synthetic material. Examples of inert synthetic material include, but are not limited to, polyester, polyamide, polyaramid, polytetrafluoroethylene, polyethylene, polypropylene, polyurethane, silicone, mixtures of polyurethane and polyethyleneglycol, ultrahigh molecular weight polyethylene, high-performance polyethylene, nylon, LYCRA (polyester-polyurethane copolymer, also known as SPANDEX and elastomer), and mixtures thereof. In an embodiment, action sportswear/apparel partially made from a silk coated textile and partially made from an uncoated textile combines an elastomeric material at least partially covered with a silk coating of the present disclosure. In an embodiment, the percentage of silk to elastomeric material can be varied to achieve desired shrink or wrinkle resistant properties and desired moisture content against the skin surface. In an embodiment, a silk coating of the present disclosure is positioned on an internal layer of a shoe (textile or non-textile based). In an embodiment, a silk coating of the present disclosure positioned on an internal layer of a shoe helps maintain optimal feet microenvironment, such as temperature and humidity while reducing any excessive perspiration.

In an embodiment, a silk coating of the present disclosure is visible. In an embodiment, a silk coating of the present disclosure is transparent. In an embodiment, a silk coating of the present disclosure positioned on action sportswear/apparel helps control skin temperature of a person wearing the apparel. In an embodiment, a silk coating of the present disclosure positioned on action sportswear/apparel helps control fluid transfer away from the skin of a person wearing the apparel. In an embodiment, a silk coating of the present disclosure positioned on action sportswear/apparel has a soft feel against the skin decreasing abrasions from fabric on the skin. In an embodiment, a silk coating of the present disclosure positioned on a textile has properties that confer at least one of wrinkle resistance, shrinkage resistance, or machine washability to the textile. In an embodiment, a silk coated textile of the present disclosure is 100% machine washable and dry cleanable. In an embodiment, a silk coated textile of the present disclosure is 100% waterproof. In an embodiment, a silk coated textile of the present disclosure is wrinkle resistant. In an embodiment, a silk coated textile of the present disclosure is shrink resistant. In an embodiment, a silk coated fabric improves the health of the skin. In an embodiment, healthy skin can be determined by visibly seeing an even skin tone. In an embodiment, healthy skin can be determined by visibly seeing a smooth, glowing complexion. In an embodiment, a silk coated fabric decreases irritation of the skin. In an embodiment, a decrease in irritation of the skin can result in a decrease in skin bumps or sores. In an embodiment, a decrease in irritation of the skin can result in a decrease in scaly or red skin. In an embodiment, a decrease in irritation of the skin can result in a decrease in itchiness or burning. In an embodiment, a silk coated fabric decreases inflammation of the skin. In an embodiment, a silk coated textile of the present disclosure has the qualities of being waterproof, breathable, and elastic and possess a number of other qualities which are highly desirable in action sportswear. In an embodiment, a silk coated textile of the present disclosure manufactured from a silk fabric of the present disclosure further includes LYCRA brand spandex fibers (polyester-polyurethane copolymer).

In an embodiment, a textile at least partially coated with an aqueous solution of pure silk fibroin-based protein fragments of the present disclosure is a breathable fabric. In an embodiment, a textile at least partially coated with an aqueous solution of pure silk fibroin-based protein fragments of the present disclosure is a water-resistant fabric. In an embodiment, a textile at least partially coated with an aqueous solution of pure silk fibroin-based protein fragments of the present disclosure is a shrink-resistant fabric. In an embodiment, a textile at least partially coated with an aqueous solution of pure silk fibroin-based protein fragments of the present disclosure is a machine-washable fabric. In an embodiment, a textile at least partially coated with an aqueous solution of pure silk fibroin-based protein fragments of the present disclosure is a wrinkle resistant fabric. In an embodiment, textile at least partially coated with an aqueous solution of pure silk fibroin-based protein fragments of the present disclosure provides moisture and vitamins to the skin.

In an embodiment, the textile at least partially coated with an aqueous solution of pure silk fibroin-based protein fragments of the present disclosure has an accumulative one-way transport index of greater than 140. In an embodiment, the textile at least partially coated with an aqueous solution of pure silk fibroin-based protein fragments of the present disclosure has an accumulative one-way transport index of greater than 120. In an embodiment, the textile at least partially coated with an aqueous solution of pure silk fibroin-based protein fragments of the present disclosure has an accumulative one-way transport index of greater than 100. In an embodiment, the textile at least partially coated with an aqueous solution of pure silk fibroin-based protein fragments of the present disclosure has an accumulative one-way transport index of greater than 80.

In an embodiment, the textile at least partially coated with an aqueous solution of pure silk fibroin-based protein fragments of the present disclosure has an overall moisture management capability of greater than 0.4. In an embodiment, the textile at least partially coated with an aqueous solution of pure silk fibroin-based protein fragments of the present disclosure has an overall moisture management capability of greater than 0.35. In an embodiment, the textile at least partially coated with an aqueous solution of pure silk fibroin-based protein fragments of the present disclosure has an overall moisture management capability of greater than 0.3. In an embodiment, the textile at least partially coated with an aqueous solution of pure silk fibroin-based protein fragments of the present disclosure has an overall moisture management capability of greater than 0.25.

In an embodiment, the textile at least partially coated with an aqueous solution of pure silk fibroin-based protein fragments of the present disclosure has a wetting time of at least 3 seconds. In an embodiment, the textile at least partially coated with an aqueous solution of pure silk fibroin-based protein fragments of the present disclosure has a wetting time of at least 2.5 seconds. In an embodiment, the textile at least partially coated with an aqueous solution of pure silk fibroin-based protein fragments of the present disclosure has a wetting time of at least 2 seconds. In an embodiment, the textile at least partially coated with an aqueous solution of pure silk fibroin-based protein fragments of the present disclosure has a wetting time of at least 1.5 seconds.

In an embodiment, the textile at least partially coated with an aqueous solution of pure silk fibroin-based protein fragments of the present disclosure has a top absorption time of at least 50 seconds. In an embodiment, the textile at least partially coated with an aqueous solution of pure silk fibroin-based protein fragments of the present disclosure has a top absorption time of at least 40 seconds. In an embodiment, the textile at least partially coated with an aqueous solution of pure silk fibroin-based protein fragments of the present disclosure has a top absorption time of at least 30 seconds. In an embodiment, the textile at least partially coated with an aqueous solution of pure silk fibroin-based protein fragments of the present disclosure has a top absorption time of at least 29 seconds, 28 seconds, 27 seconds, 26 seconds, 25 seconds, 24 seconds, 23 seconds, 22 seconds, 21 seconds, 20 seconds, 19 seconds, 18 seconds, 17 seconds, 16 seconds, 15 seconds, 14 seconds, 13 seconds, 12 seconds, 11 seconds, seconds, 9 seconds, 8 seconds, 7 seconds, 6 seconds, 5 seconds, 4 seconds, 3 seconds, 2 seconds, or 1 second.

In an embodiment, the textile at least partially coated with an aqueous solution of pure silk fibroin-based protein fragments of the present disclosure has a bottom absorption time of at least 80 seconds. In an embodiment, the textile at least partially coated with an aqueous solution of pure silk fibroin-based protein fragments of the present disclosure has a bottom absorption time of at least 70 seconds. In an embodiment, the textile at least partially coated with an aqueous solution of pure silk fibroin-based protein fragments of the present disclosure has a bottom absorption time of at least 60 seconds. In an embodiment, the textile at least partially coated with an aqueous solution of pure silk fibroin-based protein fragments of the present disclosure has a bottom absorption time of at least 50 seconds. In an embodiment, the textile at least partially coated with an aqueous solution of pure silk fibroin-based protein fragments of the present disclosure has a bottom absorption time of at least 40 seconds.

In an embodiment, the textile at least partially coated with an aqueous solution of pure silk fibroin-based protein fragments of the present disclosure has a spreading speed of at least 1.6 mm/second. In an embodiment, the textile at least partially coated with an aqueous solution of pure silk fibroin-based protein fragments of the present disclosure has a spreading speed of at least 1.4 mm/second. In an embodiment, the textile at least partially coated with an aqueous solution of pure silk fibroin-based protein fragments of the present disclosure has a spreading speed of at least 1.2 mm/second. In an embodiment, the textile at least partially coated with an aqueous solution of pure silk fibroin-based protein fragments of the present disclosure has a spreading speed of at least 1.0 mm/second. In an embodiment, the textile at least partially coated with an aqueous solution of pure silk fibroin-based protein fragments of the present disclosure has a spreading speed of at least 0.8 mm/second.

In an embodiment, the textile at least partially coated with an aqueous solution of pure silk fibroin-based protein fragments of the present disclosure shows less than 2000% microbial growth over 24 hours. In an embodiment, the textile at least partially coated with an aqueous solution of pure silk fibroin-based protein fragments of the present disclosure shows less than 1000% microbial growth over 24 hours. In an embodiment, the textile at least partially coated with an aqueous solution of pure silk fibroin-based protein fragments of the present disclosure shows less than 500% microbial growth over 24 hours. In an embodiment, the textile at least partially coated with an aqueous solution of pure silk fibroin-based protein fragments of the present disclosure shows less than 400% microbial growth over 24 hours. In an embodiment, the textile at least partially coated with an aqueous solution of pure silk fibroin-based protein fragments of the present disclosure shows less than 300% microbial growth over 24 hours. In an embodiment, the textile at least partially coated with an aqueous solution of pure silk fibroin-based protein fragments of the present disclosure shows less than 200% microbial growth over 24 hours. In some embodiments, as described herein, the reduction in microbial growth may be measured and provided after one or more wash cycles in non-chlorine bleach. In some embodiments, solutions that include silk fibroin-based protein fragments may include an additional chemical agent, as described herein, that may provide antimicrobial, antifungal, and/or antibacterial properties.

In an embodiment, the textile at least partially coated with an aqueous solution of pure silk fibroin-based protein fragments of the present disclosure shows less than 2000% bacterial growth over 24 hours. In an embodiment, the textile at least partially coated with an aqueous solution of pure silk fibroin-based protein fragments of the present disclosure shows less than 1000% bacterial growth over 24 hours. In an embodiment, the textile at least partially coated with an aqueous solution of pure silk fibroin-based protein fragments of the present disclosure shows less than 500% bacterial growth over 24 hours. In an embodiment, the textile at least partially coated with an aqueous solution of pure silk fibroin-based protein fragments of the present disclosure shows less than 400% bacterial growth over 24 hours. In an embodiment, the textile at least partially coated with an aqueous solution of pure silk fibroin-based protein fragments of the present disclosure shows less than 300% bacterial growth over 24 hours. In an embodiment, the textile at least partially coated with an aqueous solution of pure silk fibroin-based protein fragments of the present disclosure shows less than 200% bacterial growth over 24 hours.

In an embodiment, the textile at least partially coated with an aqueous solution of pure silk fibroin-based protein fragments of the present disclosure shows less than 2000% fungal growth over 24 hours. In an embodiment, the textile at least partially coated with an aqueous solution of pure silk fibroin-based protein fragments of the present disclosure shows less than 1000% fungal growth over 24 hours. In an embodiment, the textile at least partially coated with an aqueous solution of pure silk fibroin-based protein fragments of the present disclosure shows less than 500% fungal growth over 24 hours. In an embodiment, the textile at least partially coated with an aqueous solution of pure silk fibroin-based protein fragments of the present disclosure shows less than 400% fungal growth over 24 hours. In an embodiment, the textile at least partially coated with an aqueous solution of pure silk fibroin-based protein fragments of the present disclosure shows less than 300% fungal growth over 24 hours. In an embodiment, the textile at least partially coated with an aqueous solution of pure silk fibroin-based protein fragments of the present disclosure shows less than 200% fungal growth over 24 hours.

In an embodiment, the textile at least partially coated with an aqueous solution of pure silk fibroin-based protein fragments of the present disclosure shows less than 2000% growth of Staphylococcus aureus over 24 hours. In an embodiment, the textile at least partially coated with an aqueous solution of pure silk fibroin-based protein fragments of the present disclosure shows less than 1000% growth of Staphylococcus aureus over 24 hours. In an embodiment, the textile at least partially coated with an aqueous solution of pure silk fibroin-based protein fragments of the present disclosure shows less than 500% growth of Staphylococcus aureus over 24 hours. In an embodiment, the textile at least partially coated with an aqueous solution of pure silk fibroin-based protein fragments of the present disclosure shows less than 400% growth of Staphylococcus aureus over 24 hours. In an embodiment, the textile at least partially coated with an aqueous solution of pure silk fibroin-based protein fragments of the present disclosure shows less than 300% growth of Staphylococcus aureus over 24 hours. In an embodiment, the textile at least partially coated with an aqueous solution of pure silk fibroin-based protein fragments of the present disclosure shows less than 200% growth of Staphylococcus aureus over 24 hours.

In an embodiment, the textile at least partially coated with an aqueous solution of pure silk fibroin-based protein fragments of the present disclosure shows less than 2000% growth of Klebsiella pneumoniae over 24 hours. In an embodiment, the textile at least partially coated with an aqueous solution of pure silk fibroin-based protein fragments of the present disclosure shows less than 1000% growth of Klebsiella pneumoniae over 24 hours. In an embodiment, the textile at least partially coated with an aqueous solution of pure silk fibroin-based protein fragments of the present disclosure shows less than 500% growth of Klebsiella pneumoniae over 24 hours. In an embodiment, the textile at least partially coated with an aqueous solution of pure silk fibroin-based protein fragments of the present disclosure shows less than 400% growth of Klebsiella pneumoniae over 24 hours. In an embodiment, the textile at least partially coated with an aqueous solution of pure silk fibroin-based protein fragments of the present disclosure shows less than 300% growth of Klebsiella pneumoniae over 24 hours. In an embodiment, the textile at least partially coated with an aqueous solution of pure silk fibroin-based protein fragments of the present disclosure shows less than 200% growth of Klebsiella pneumoniae over 24 hours.

In an embodiment, an aqueous solution of pure silk fibroin-based protein fragments of the present disclosure is used to coat a textile. In an embodiment, the concentration of silk in the solution ranges from about 0.001% to about 20.0%. In an embodiment, the concentration of silk in the solution ranges from about 0.01% to about 15.0%. In an embodiment, the concentration of silk in the solution ranges from about to about 10.0%. In an embodiment, the concentration of silk in the solution ranges from about 1.0% to about 5.0%. In an embodiment, an aqueous solution of pure silk fibroin-based protein fragments of the present disclosure is applied directly to a fabric. Alternatively, silk microsphere and any additives may be used for coating a fabric. In an embodiment, additives can be added to an aqueous solution of pure silk fibroin-based protein fragments of the present disclosure before coating (e.g., alcohols) to further enhance material properties. In an embodiment, a silk coating of the present disclosure can have a pattern to optimize properties of the silk on the fabric. In an embodiment, a coating is applied to a fabric under tension and/or lax to vary penetration in to the fabric.

In an embodiment, a silk coating of the present disclosure can be applied at the yarn level, followed by creation of a fabric once the yarn is coated. In an embodiment, an aqueous solution of pure silk fibroin-based protein fragments of the present disclosure can be spun into fibers to make a silk fabric and/or silk fabric blend with other materials known in the apparel industry.

In an embodiment, a method for silk coating a fabric includes immersion of the fabric in any of the aqueous solutions of pure silk fibroin-based protein fragments of the present disclosure. In an embodiment, a method for silk coating a fabric includes spraying. In an embodiment, a method for silk coating a fabric includes chemical vapor deposition. In an embodiment, a method for silk coating a fabric includes electrochemical coating. In an embodiment, a method for silk coating a fabric includes knife coating to spread any of the aqueous solutions of pure silk fibroin-based protein fragments of the present disclosure onto the fabric. The coated fabric may then be air dried, dried under heat/air flow, or cross-linked to the fabric surface. In an embodiment, a drying process includes curing with additives and/or ambient condition.

According to aspects illustrated herein, methods for preparing aqueous solutions of pure silk fibroin-based protein fragments are disclosed. In an embodiment, at least one pure silk fibroin-based protein fragment (SPF) mixture solution having a specific average weight average molecular weight (MW) range and polydispersity is created. In an embodiment, at least SPF mixture solution having a MW range between about 6 kDa and 17 kDa and a polydispersity range between about 1.5 and about 3.0 is created. In an embodiment, at least one SPF mixture solution having a MW between about 17 kDa and 39 kDa and a polydispersity range between about 1.5 and about 3.0 is created. In an embodiment, at least one SPF mixture solution having a MW range between about 39 kDa and 80 kDa and a polydispersity range between about 1.5 and about 3.0 is created.

In one embodiment, the invention relates to a material including one or more fibers including a protein, wherein a substantial portion of fibers are coated with silk fibroin-based protein fragments. In some embodiments, the material includes one or more of a woven material, a non-woven material, a knit material, and a crochet material. In some embodiments, the material includes fabric, thread, yarn, fiber, or a combination thereof. In some embodiments, the material includes wool. In some embodiments, the material includes cashmere. In some embodiments, the wool includes one or more of natural wool, synthetic wool, alpaca fleece, alpaca wool, lama fleece, lama wool, cashmere, sheep fleece, sheep wool, mohair wool, camel hair, or angora wool. In some embodiments, the silk fibroin-based protein fragments include one or more of low molecular weight silk fibroin-based protein fragments, medium molecular weight silk fibroin-based protein fragments, and high molecular weight silk fibroin-based protein fragments. In some embodiments, the silk fibroin-based protein fragments have an average molecular weight from about 1 kDa to about 350 kDa. In some embodiments, the silk fibroin-based protein fragments have a polydispersity from about 1.0 to about 5.0.

In one embodiment, the invention relates to coating a material including one or more proteinaceous fibers, wherein a substantial portion of the proteinaceous fibers are coated with silk fibroin-based protein fragments. In some embodiments, the proteinaceous fibers include keratin. In some embodiments, the proteinaceous fibers include hair. In some embodiments, the proteinaceous fibers include human hair or animal hair. In some embodiments, the silk fibroin-based protein fragments include one or more of low molecular weight silk fibroin-based protein fragments, medium molecular weight silk fibroin-based protein fragments, and high molecular weight silk fibroin-based protein fragments. In some embodiments, the silk fibroin-based protein fragments have an average molecular weight from about 1 kDa to about 350 kDa. In some embodiments, the silk fibroin-based protein fragments have a polydispersity from about 1.0 to about 5.0.

In one embodiment, the invention relates to a method of making a silk fibroin coated material, the method including preparing a silk fibroin solution including low molecular weight silk fibroin-based protein fragments, coating a surface of the material with the silk fibroin solution, and drying the surface of the material that has been coated with the silk fibroin solution to provide the silk fibroin coated material. In one embodiment, the invention relates to a method of improving hand in a material, the method including preparing a silk fibroin solution including low molecular weight silk fibroin-based protein fragments, coating a surface of the material with the silk fibroin solution, and drying the surface of the material that has been coated with the silk fibroin solution, wherein the resulting coated material has an improved hand compared to the uncoated material. In one embodiment, the invention relates to a method of improving hand retention on laundering in a material, the method including preparing a silk fibroin solution including low molecular weight silk fibroin-based protein fragments, coating a surface of the material with the silk fibroin solution, and drying the surface of the material that has been coated with the silk fibroin solution, wherein upon laundering, the coated material retains a substantial portion of its initial hand prior to laundering. In one embodiment, the invention relates to a method of improving size and/or shape retention on laundering in a material, the method including preparing a silk fibroin solution including low molecular weight silk fibroin-based protein fragments, coating a surface of the material with the silk fibroin solution, and drying the surface of the material that has been coated with the silk fibroin solution, wherein upon laundering, the coated material substantially retains its initial size and/or shape prior to laundering. In one embodiment, the invention relates to a method of improving pilling resistance in a material, the method including preparing a silk fibroin solution including low molecular weight silk fibroin-based protein fragments, coating a surface of the material with the silk fibroin solution, and drying the surface of the material that has been coated with the silk fibroin solution, wherein the coated material has an improved pilling resistance compared to a similar material which was not so coated. In one embodiment, the invention relates to a method of improving water repellency in a material, the method including preparing a silk fibroin solution comprising low molecular weight silk fibroin-based protein fragments, coating a surface of the material with the silk fibroin solution, and drying the surface of the material that has been coated with the silk fibroin solution, wherein the coated material has an improved water repellency compared to a similar material which was not so coated. In some embodiments, the methods further include an additional treatment step. In some embodiments, the additional treatment step is a pre-treatment step (e.g., preparation of an article surface before treatment or coating), a post treatment step, or a final treatment step. In some embodiments, the additional treatment step comprises an acidic treatment or an alcohol treatment. In some embodiments, the silk fibroin solution further includes medium molecular weight silk fibroin-based protein fragments. In some embodiments, the w/w ratio between low molecular weight silk fibroin-based protein fragments and medium molecular weight silk fibroin-based protein fragments is about 90:10, about 80:20, about 75:25, about 70:30, about 66:34, about 60:40, about 50:50, about 40:60, about 34:66, about 30:70, about 25:75, about 20:80, or about 10:90. In some embodiments, the w/w ratio between low molecular weight silk fibroin-based protein fragments and medium molecular weight silk fibroin-based protein fragments is about 3:1. In some embodiments, the silk fibroin solution further includes high molecular weight silk fibroin-based protein fragments. In some embodiments, the silk fibroin solution further includes medium molecular weight silk fibroin-based protein fragments, and high molecular weight silk fibroin-based protein fragments. In some embodiments, drying the surface of the material includes heating the surface of the material without substantially modifying silk fibroin coating performance. In some embodiments, the silk fibroin solution includes silk fibroin-based protein fragments at less than about by volume (v/v), less than about 0.1% v/v, less than about 1% v/v, less than about 2.5% v/v, or less than about 5% v/v. In some embodiments, the silk fibroin solution includes silk fibroin-based protein fragments at about 0.5% by v/v, weight/weight (w/w), or weight/volume (w/v). In some embodiments, the silk fibroin solution includes a Brønsted acid. In some embodiments, the silk fibroin solution includes one or more of citric acid and acetic acid. In some embodiments, the material includes one or more of a woven material, a non-woven material, a knit material, and a crochet material. In some embodiments, the material includes fabric, thread, yarn, fiber, or a combination thereof. In some embodiments, the material includes wool. In some embodiments, the material includes cashmere. In some embodiments, the wool includes one or more of natural wool, synthetic wool, alpaca fleece, alpaca wool, lama fleece, lama wool, cashmere, sheep fleece, sheep wool, mohair wool, camel hair, angora wool.

According to aspects illustrated herein, there is disclosed a composition that includes pure silk fibroin-based protein fragments that are substantially devoid of sericin, wherein the composition has an average weight average molecular weight ranging from about 6 kDa to about 17 kDa, wherein the composition has a polydispersity of between about 1.5 and about 3.0, wherein the composition is substantially homogenous, wherein the composition includes between 0 ppm and about 500 ppm of inorganic residuals, and wherein the composition includes between 0 ppm and about 500 ppm of organic residuals. In an embodiment, the pure silk fibroin-based protein fragments have between about 10 ppm and about 300 ppm of lithium bromide residuals and between about 10 ppm and about 100 ppm of sodium carbonate residuals. In an embodiment, the lithium bromide residuals are measurable using a high-performance liquid chromatography lithium bromide assay, and the sodium carbonate residuals are measurable using a high-performance liquid chromatography sodium carbonate assay. In an embodiment, the composition further includes less than 10% water. In an embodiment, the composition is in the form of a solution. In an embodiment, the composition includes from about 0.01 wt % to about 30.0 wt % pure silk fibroin-based protein fragments. In some embodiments, the pure silk fibroin-based protein fragments are stable in the solution for at least 30 days. In some embodiments, the pure silk fibroin-based protein fragments are stable in the solution for at least 30 days at about 0° C., about 1° C., about 2° C., about 3° C., about 4° C., about 5° C., about 6° C., about 7° C., about 8° C., about 9° C., about 10° C., about 11° C., about 12° C., about 13° C., about 14° C., about 15° C., about 16° C., about 17° C., about 18° C., about 19° C., about 20° C., about 21° C., about 22° C., about 23° C., about 24° C., or about 25° C. In some embodiments, the pure silk fibroin-based protein fragments are stable in the solution for at least 30 days at room temperature. In an embodiment, the term “stable” refers to the absence of spontaneous or gradual gelation, with no visible change in the color or turbidity of the solution. In an embodiment, the term “stable” refers to no aggregation of fragments and therefore no increase in molecular weight over time. In an embodiment, the composition is in the form of an aqueous solution. In an embodiment, the composition is in the form of an organic solution. The composition may be provided in a sealed container. In some embodiments, the composition further includes one or more molecules selected from the group consisting of therapeutic agents, growth factors, antioxidants, proteins, vitamins, carbohydrates, polymers, nucleic acids, salts, acids, bases, biomolecules, glycosamino glycans, polysaccharides, extracellular matrix molecules, metals, metal ion, metal oxide, synthetic molecules, polyanhydrides, cells, fatty acids, fragrance, minerals, plants, plant extracts, preservatives and essential oils. In an embodiment, the added molecule or molecules are stable (i.e., retain activity over time) within the composition and can be released at a desired rate. In an embodiment, the one or more molecules is vitamin C or a derivative thereof. In an embodiment, the composition further includes an alpha hydroxy acid selected from the group consisting of glycolic acid, lactic acid, tartaric acid and citric acid. In an embodiment, the composition further includes hyaluronic acid or its salt form at a concentration of about 0.5% to about 10.0%. In an embodiment, the composition further includes at least one of zinc oxide or titanium dioxide. In an embodiment, the pure silk fibroin-based protein fragments in the composition are hypoallergenic. In an embodiment, the pure silk fibroin-based protein fragments are biocompatible, non-sensitizing, and non-immunogenic.

According to aspects illustrated herein, there is disclosed a composition that includes pure silk fibroin-based protein fragments that are substantially devoid of sericin, wherein the composition has an average weight average molecular weight ranging from about 17 kDa to about 39 kDa, wherein the composition has a polydispersity of between about 1.5 and about 3.0, wherein the composition is substantially homogenous, wherein the composition includes between 0 ppm and about 500 ppm of inorganic residuals, and wherein the composition includes between 0 ppm and about 500 ppm of organic residuals. In an embodiment, the pure silk fibroin-based protein fragments have between about 10 ppm and about 300 ppm of lithium bromide residuals and between about 10 ppm and about 100 ppm of sodium carbonate residuals. In an embodiment, the lithium bromide residuals are measurable using a high-performance liquid chromatography lithium bromide assay, and the sodium carbonate residuals are measurable using a high-performance liquid chromatography sodium carbonate assay. In an embodiment, the composition further includes less than 10% water. In an embodiment, the composition is in the form of a solution. In an embodiment, the composition includes from about 0.01 wt % to about 30.0 wt % pure silk fibroin-based protein fragments. The pure silk fibroin-based protein fragments are stable in the solution for at least 30 days. In an embodiment, the term “stable” refers to the absence of spontaneous or gradual gelation, with no visible change in the color or turbidity of the solution. In an embodiment, the term “stable” refers to no aggregation of fragments and therefore no increase in molecular weight over time. In an embodiment, the composition is in the form of an aqueous solution. In an embodiment, the composition is in the form of an organic solution. The composition may be provided in a sealed container. In some embodiments, the composition further includes one or more molecules selected from the group consisting of therapeutic agents, growth factors, antioxidants, proteins, vitamins, carbohydrates, polymers, nucleic acids, salts, acids, bases, biomolecules, glycosamino glycans, polysaccharides, extracellular matrix molecules, metals, metal ion, metal oxide, synthetic molecules, polyanhydrides, cells, fatty acids, fragrance, minerals, plants, plant extracts, preservatives and essential oils. In an embodiment, the added molecule or molecules are stable (i.e., retain activity over time) within the composition and can be released at a desired rate. In an embodiment, the one or more molecules is vitamin C or a derivative thereof. In an embodiment, the composition further includes an alpha hydroxy acid selected from the group consisting of glycolic acid, lactic acid, tartaric acid and citric acid. In an embodiment, the composition further includes hyaluronic acid or its salt form at a concentration of about to about 10.0%. In an embodiment, the composition further includes at least one of zinc oxide or titanium dioxide. In an embodiment, the pure silk fibroin-based protein fragments in the composition are hypoallergenic. In an embodiment, the pure silk fibroin-based protein fragments are biocompatible, non-sensitizing, and non-immunogenic.

According to aspects illustrated herein, there is disclosed a composition that includes pure silk fibroin-based protein fragments that are substantially devoid of sericin, wherein the composition has an average weight average molecular weight ranging from about 39 kDa to about 80 kDa, wherein the composition has a polydispersity of between about 1.5 and about 3.0, wherein the composition is substantially homogenous, wherein the composition includes between 0 ppm and about 500 ppm of inorganic residuals, and wherein the composition includes between 0 ppm and about 500 ppm of organic residuals. In an embodiment, the pure silk fibroin-based protein fragments have between about 10 ppm and about 300 ppm of lithium bromide residuals and between about 10 ppm and about 100 ppm of sodium carbonate residuals. In an embodiment, the lithium bromide residuals are measurable using a high-performance liquid chromatography lithium bromide assay, and the sodium carbonate residuals are measurable using a high-performance liquid chromatography sodium carbonate assay. In an embodiment, the composition further includes less than 10% water. In an embodiment, the composition is in the form of a solution. In an embodiment, the composition includes from about 0.01 wt % to about 30.0 wt % pure silk fibroin-based protein fragments. The pure silk fibroin-based protein fragments are stable in the solution for at least 30 days. In an embodiment, the term “stable” refers to the absence of spontaneous or gradual gelation, with no visible change in the color or turbidity of the solution. In an embodiment, the term “stable” refers to no aggregation of fragments and therefore no increase in molecular weight over time. In an embodiment, the composition is in the form of an aqueous solution. In an embodiment, the composition is in the form of an organic solution. The composition may be provided in a sealed container. In some embodiments, the composition further includes one or more molecules selected from the group consisting of therapeutic agents, growth factors, antioxidants, proteins, vitamins, carbohydrates, polymers, nucleic acids, salts, acids, bases, biomolecules, glycosamino glycans, polysaccharides, extracellular matrix molecules, metals, metal ion, metal oxide, synthetic molecules, polyanhydrides, cells, fatty acids, fragrance, minerals, plants, plant extracts, preservatives and essential oils. In an embodiment, the added molecule or molecules are stable (i.e., retain activity over time) within the composition and can be released at a desired rate. In an embodiment, the one or more molecules is vitamin C or a derivative thereof. In an embodiment, the composition further includes an alpha hydroxy acid selected from the group consisting of glycolic acid, lactic acid, tartaric acid and citric acid. In an embodiment, the composition further includes hyaluronic acid or its salt form at a concentration of about to about 10.0%. In an embodiment, the composition further includes at least one of zinc oxide or titanium dioxide. In an embodiment, the pure silk fibroin-based protein fragments in the composition are hypoallergenic. In an embodiment, the pure silk fibroin-based protein fragments are biocompatible, non-sensitizing, and non-immunogenic.

According to aspects illustrated herein, there is disclosed a gel that includes pure silk fibroin-based protein fragments substantially devoid of sericin and comprising: an average weight average molecular weight ranging from about 17 kDa to about 39 kDa; and a polydispersity of between about 1.5 and about 3.0; and water from about 20 wt. % to about 99.9 wt. %, wherein the gel includes between 0 ppm and 500 ppm of inorganic residuals, and wherein the gel includes between 0 ppm and 500 ppm of organic residuals. In an embodiment, the gel includes between about 1.0% and about 50.0% crystalline protein domains. In an embodiment, the gel includes from about 0.1 wt. % to about 6.0 wt. % of pure silk fibroin-based protein fragments. In an embodiment, the gel has a pH from about 1.0 to about 7.0. In an embodiment, the gel further includes from about 0.5 wt. % to about 20.0 wt. % of vitamin C or a derivative thereof. In an embodiment, the vitamin C or a derivative thereof remains stable within the gel for a period of from about 5 days to about 5 years. In an embodiment, the vitamin C or a derivative thereof is stable within the gel so as to result in release of the vitamin C in a biologically active form. In an embodiment, the gel further includes an additive selected from the group consisting of vitamin E, rosemary oil, rose oil, lemon juice, lemon grass oil and caffeine. In an embodiment, the gel is packaged in an airtight container. In an embodiment, the pure silk fibroin-based protein fragments are hypoallergenic. In an embodiment, the gel has less than 10 colony forming units per milliliter.

According to aspects illustrated herein, there is disclosed a method for preparing an aqueous solution of pure silk fibroin-based protein fragments having an average weight average molecular weight ranging from about 6 kDa to about 17 kDa, the method including the steps of: degumming a silk source by adding the silk source to a boiling (100° C.) aqueous solution of sodium carbonate for a treatment time of between about 30 minutes to about 60 minutes; removing sericin from the solution to produce a silk fibroin extract comprising non-detectable levels of sericin; draining the solution from the silk fibroin extract; dissolving the silk fibroin extract in a solution of lithium bromide having a starting temperature upon placement of the silk fibroin extract in the lithium bromide solution that ranges from about 60° C. to about 140° C.; maintaining the solution of silk fibroin-lithium bromide in an oven having a temperature of about 140° C. for a period of at least 1 hour; removing the lithium bromide from the silk fibroin extract; and producing an aqueous solution of silk protein fragments, the aqueous solution comprising: fragments having an average weight average molecular weight ranging from about 6 kDa to about 17 kDa, and wherein the aqueous solution of pure silk fibroin-based protein fragments comprises a polydispersity of between about 1.5 and about 3.0. In an embodiment, the method includes the step of drying the silk fibroin extract prior to the dissolving step. In an embodiment, the amount of lithium bromide residuals in the aqueous solution can be measured using a high-performance liquid chromatography lithium bromide assay. In an embodiment, the amount of sodium carbonate residuals in the aqueous solution can be measured using a high-performance liquid chromatography sodium carbonate assay. In an embodiment, the method includes the step of adding a therapeutic agent to the aqueous solution of pure silk fibroin-based protein fragments. In an embodiment, the method includes the step of adding a molecule selected from one of an antioxidant or an enzyme to the aqueous solution of pure silk fibroin-based protein fragments. In an embodiment, the method includes the step of adding a vitamin to the aqueous solution of pure silk fibroin-based protein fragments. In an embodiment, the vitamin is selected from one of vitamin C or a derivative thereof. In an embodiment, the method further includes the step of adding an alpha hydroxy acid to the aqueous solution of pure silk fibroin-based protein fragments. In an embodiment, the alpha hydroxy acid is selected from the group consisting of glycolic acid, lactic acid, tartaric acid and citric acid. In an embodiment, the method further includes the step of adding hyaluronic acid at a concentration of about 0.5% to about 10.0% to the aqueous solution of pure silk fibroin-based protein fragments. In an embodiment, the method further includes the step of adding at least one of zinc oxide or titanium dioxide to the aqueous solution of pure silk fibroin-based protein fragments.

According to aspects illustrated herein, there is disclosed a method for preparing an aqueous solution of pure silk fibroin-based protein fragments having an average weight average molecular weight ranging from about 17 kDa to about 39 kDa, the method including the steps of: adding a silk source to a boiling (100° C.) aqueous solution of sodium carbonate for a treatment time of between about 30 minutes to about minutes so as to result in degumming; removing sericin from the solution to produce a silk fibroin extract comprising non-detectable levels of sericin; draining the solution from the silk fibroin extract; dissolving the silk fibroin extract in a solution of lithium bromide having a starting temperature upon placement of the silk fibroin extract in the lithium bromide solution that ranges from about 80° C. to about 140° C.; maintaining the solution of silk fibroin-lithium bromide in a dry oven having a temperature in the range between about 60° C. to about 100° C. for a period of at least 1 hour; removing the lithium bromide from the silk fibroin extract; and producing an aqueous solution of pure silk fibroin-based protein fragments, wherein the aqueous solution of pure silk fibroin-based protein fragments comprises lithium bromide residuals of between about 10 ppm and about 300 ppm, wherein the aqueous solution of silk protein fragments comprises sodium carbonate residuals of between about 10 ppm and about 100 ppm, wherein the aqueous solution of pure silk fibroin-based protein fragments comprises fragments having an average weight average molecular weight ranging from about 17 kDa to about 39 kDa, and wherein the aqueous solution of pure silk fibroin-based protein fragments comprises a polydispersity of between about 1.5 and about 3.0. In an embodiment, the method includes the step of drying the silk fibroin extract prior to the dissolving step. In an embodiment, the amount of lithium bromide residuals in the aqueous solution can be measured using a high-performance liquid chromatography lithium bromide assay. In an embodiment, the amount of sodium carbonate residuals in the aqueous solution can be measured using a high-performance liquid chromatography sodium carbonate assay. In an embodiment, the method includes the step of adding a therapeutic agent to the aqueous solution of pure silk fibroin-based protein fragments. In an embodiment, the method includes the step of adding a molecule selected from one of an antioxidant or an enzyme to the aqueous solution of pure silk fibroin-based protein fragments. In an embodiment, the method includes the step of adding a vitamin to the aqueous solution of pure silk fibroin-based protein fragments. In an embodiment, the vitamin is selected from one of vitamin C or a derivative thereof. In an embodiment, the method further includes the step of adding an alpha hydroxy acid to the aqueous solution of pure silk fibroin-based protein fragments. In an embodiment, the alpha hydroxy acid is selected from the group consisting of glycolic acid, lactic acid, tartaric acid and citric acid. In an embodiment, the method further includes the step of adding hyaluronic acid at a concentration of about 0.5% to about 10.0% to the aqueous solution of pure silk fibroin-based protein fragments. In an embodiment, the method further includes the step of adding at least one of zinc oxide or titanium dioxide to the aqueous solution of pure silk fibroin-based protein fragments.

According to aspects illustrated herein, there is disclosed a method for preparing an aqueous solution of pure silk fibroin-based protein fragments having an average weight average molecular weight ranging from about 39 kDa to about 80 kDa, the method including the steps of: adding a silk source to a boiling (100° C.) aqueous solution of sodium carbonate for a treatment time of about 30 minutes so as to result in degumming; removing sericin from the solution to produce a silk fibroin extract comprising non-detectable levels of sericin; draining the solution from the silk fibroin extract; dissolving the silk fibroin extract in a solution of lithium bromide having a starting temperature upon placement of the silk fibroin extract in the lithium bromide solution that ranges from about 80° C. to about 140° C.; maintaining the solution of silk fibroin-lithium bromide in a dry oven having a temperature in the range between about ° C. to about 100° C. for a period of at least 1 hour; removing the lithium bromide from the silk fibroin extract; and producing an aqueous solution of pure silk fibroin-based protein fragments, wherein the aqueous solution of pure silk fibroin-based protein fragments comprises lithium bromide residuals of between about 10 ppm and about 300 ppm, sodium carbonate residuals of between about 10 ppm and about 100 ppm, fragments having an average weight average molecular weight ranging from about 40 kDa to about 65 kDa, and wherein the aqueous solution of pure silk fibroin-based protein fragments comprises a polydispersity of between about 1.5 and about 3.0. In an embodiment, the method includes the step of drying the silk fibroin extract prior to the dissolving step. In an embodiment, the amount of lithium bromide residuals in the aqueous solution can be measured using a high-performance liquid chromatography lithium bromide assay. In an embodiment, the amount of sodium carbonate residuals in the aqueous solution can be measured using a high-performance liquid chromatography sodium carbonate assay. In an embodiment, the method includes the step of adding a therapeutic agent to the aqueous solution of pure silk fibroin-based protein fragments. In an embodiment, the method includes the step of adding a molecule selected from one of an antioxidant or an enzyme to the aqueous solution of pure silk fibroin-based protein fragments. In an embodiment, the method includes the step of adding a vitamin to the aqueous solution of pure silk fibroin-based protein fragments. In an embodiment, the vitamin is selected from one of vitamin C or a derivative thereof. In an embodiment, the method further includes the step of adding an alpha hydroxy acid to the aqueous solution of pure silk fibroin-based protein fragments. In an embodiment, the alpha hydroxy acid is selected from the group consisting of glycolic acid, lactic acid, tartaric acid and citric acid. In an embodiment, the method further includes the step of adding hyaluronic acid at a concentration of about 0.5% to about 10.0% to the aqueous solution of pure silk fibroin-based protein fragments. In an embodiment, the method further includes the step of adding at least one of zinc oxide or titanium dioxide to the aqueous solution of pure silk fibroin-based protein fragments.

According to aspects illustrated herein, a method is disclosed for producing silk gels having entrapped molecules or therapeutic agents such as those listed in the following paragraphs. In an embodiment, at least one molecule or therapeutic agent of interest is physically entrapped into a SPF mixture solution of the present disclosure during processing into aqueous gels. An aqueous silk gel of the present disclosure can be used to release at least one molecule or therapeutic agent of interest.

In some embodiments, the w/w ratio between low molecular weight silk and medium molecular weight silk is between about 99:1 to about 1:99, between about 95:5 to about 5:95, between about 90:10 to about 10:90, between about 75:25 to about 25:75, between about 65:35 to about 35:65, or between about 55:45 to about 45:55. In some embodiments, the w/w ratio between low molecular weight silk and medium molecular weight silk is between about 99:1 to about 55:45, between about 95:5 to about 45:55, between about 90:10 to about 35:65, between about 75:25 to about 15:85, between about 65:35 to about 10:90, or between about 55:45 to about 1:99. In an embodiment, the w/w ratio between low molecular weight silk and medium molecular weight silk is about 99:1, about 98:2, about 97:3, about 96:4, about 95:5, about 94:6, about 93:7, about 92:8, about 91:9, about 90:10, about 89:11, about 88:12, about 87:13, about 86:14, about 85:15, about 84:16, about 83:17, about 82:18, about 81:19, about 80:20, about 79:21, about 78:22, about 77:23, about 76:24, about 75:25, about 74:26, about 73:27, about 72:28, about 71:29, about 70:30, about 69:31, about 68:32, about 67:33, about 66:34, about 65:35, about 64:36, about 63:37, about 62:38, about 61:39, about 60:40, about 59:41, about 58:42, about 57:43, about 56:44, about 55:45, about 54:46, about 53:47, about 52:48, about 51:49, about 50:50, about 49:51, about 48:52, about 47:53, about 46:54, about 45:55, about 44:56, about 43:57, about 42:58, about 41:59, about about 39:61, about 38:62, about 37:63, about 36:64, about 35:65, about 34:66, about 33:67, about 32:68, about 31:69, about 30:70, about 29:71, about 28:72, about 27:73, about 26:74, about 25:75, about 24:76, about 23:77, about 22:78, about 21:79, about 20:80, about 19:81, about 18:82, about 17:83, about 16:84, about 15:85, about 14:86, about 13:87, about 12:88, about 11:89, about 10:90, about 9:91, about 8:92, about 7:93, about 6:94, about 5:95, about 4:96, about 3:97, about 2:98, or about 1:99. In an embodiment, the w/w ratio between low molecular weight silk and medium molecular weight silk is about 3:1. In an embodiment, the w/w ratio between low molecular weight silk and medium molecular weight silk is about 1:3.

In some embodiments, the w/w ratio between low molecular weight silk and high molecular weight silk is between about 99:1 to about 1:99, between about 95:5 to about 5:95, between about 90:10 to about 10:90, between about 75:25 to about 25:75, between about 65:35 to about 35:65, or between about 55:45 to about 45:55. In some embodiments, the w/w ratio between low molecular weight silk and high molecular weight silk is between about 99:1 to about 55:45, between about 95:5 to about 45:55, between about 90:10 to about 35:65, between about 75:25 to about 15:85, between about 65:35 to about 10:90, or between about 55:45 to about 1:99. In an embodiment, the w/w ratio between low molecular weight silk and high molecular weight silk is about 99:1, about 98:2, about 97:3, about 96:4, about 95:5, about 94:6, about 93:7, about 92:8, about 91:9, about 90:10, about 89:11, about 88:12, about 87:13, about 86:14, about 85:15, about 84:16, about 83:17, about 82:18, about 81:19, about 80:20, about 79:21, about 78:22, about 77:23, about 76:24, about 75:25, about 74:26, about 73:27, about 72:28, about 71:29, about 70:30, about 69:31, about 68:32, about 67:33, about 66:34, about 65:35, about 64:36, about 63:37, about 62:38, about 61:39, about 60:40, about 59:41, about 58:42, about 57:43, about 56:44, about 55:45, about 54:46, about 53:47, about 52:48, about 51:49, about 50:50, about 49:51, about 48:52, about 47:53, about 46:54, about 45:55, about 44:56, about 43:57, about 42:58, about 41:59, about about 39:61, about 38:62, about 37:63, about 36:64, about 35:65, about 34:66, about 33:67, about 32:68, about 31:69, about 30:70, about 29:71, about 28:72, about 27:73, about 26:74, about 25:75, about 24:76, about 23:77, about 22:78, about 21:79, about 20:80, about 19:81, about 18:82, about 17:83, about 16:84, about 15:85, about 14:86, about 13:87, about 12:88, about 11:89, about 10:90, about 9:91, about 8:92, about 7:93, about 6:94, about 5:95, about 4:96, about 3:97, about 2:98, or about 1:99.

In an embodiment, the silk fibroin coated materials of the invention, for example a fiber, a yarn, or a fabric, may be coated with compositions including medium molecular weight silk and high molecular weight silk. In some embodiments, the w/w ratio between medium molecular weight silk and high molecular weight silk is between about 99:1 to about 1:99, between about 95:5 to about 5:95, between about 90:10 to about 10:90, between about 75:25 to about 25:75, between about 65:35 to about 35:65, or between about 55:45 to about 45:55. In some embodiments, the w/w ratio between medium molecular weight silk and high molecular weight silk is between about 99:1 to about 55:45, between about 95:5 to about 45:55, between about 90:10 to about 35:65, between about 75:25 to about 15:85, between about 65:35 to about 10:90, or between about 55:45 to about 1:99. In an embodiment, the w/w ratio between medium molecular weight silk and high molecular weight silk is about 99:1, about 98:2, about 97:3, about 96:4, about 95:5, about 94:6, about 93:7, about 92:8, about 91:9, about 90:10, about 89:11, about 88:12, about 87:13, about 86:14, about 85:15, about 84:16, about 83:17, about 82:18, about 81:19, about 80:20, about 79:21, about 78:22, about 77:23, about 76:24, about 75:25, about 74:26, about 73:27, about 72:28, about 71:29, about 70:30, about 69:31, about 68:32, about 67:33, about 66:34, about 65:35, about 64:36, about 63:37, about 62:38, about 61:39, about 60:40, about 59:41, about 58:42, about 57:43, about 56:44, about 55:45, about 54:46, about 53:47, about 52:48, about 51:49, about about 49:51, about 48:52, about 47:53, about 46:54, about 45:55, about 44:56, about 43:57, about 42:58, about 41:59, about 40:60, about 39:61, about 38:62, about 37:63, about 36:64, about 35:65, about 34:66, about 33:67, about 32:68, about 31:69, about 30:70, about 29:71, about 28:72, about 27:73, about 26:74, about 25:75, about 24:76, about 23:77, about 22:78, about 21:79, about 20:80, about 19:81, about 18:82, about 17:83, about 16:84, about 15:85, about 14:86, about 13:87, about 12:88, about 11:89, about 10:90, about 9:91, about 8:92, about 7:93, about 6:94, about 5:95, about 4:96, about 3:97, about 2:98, or about 1:99.

According to aspects illustrated herein, pure silk fibroin-based protein fragments from aqueous solutions of the present disclosure can be formed into yarns and fabrics including for example, woven or weaved fabrics, and these fabrics can be used in textiles, as described above.

According to aspects illustrated herein, silk fabric manufactured from SPF mixture solutions of the present disclosure are disclosed. In an embodiment, at least one molecule or therapeutic agent of interest is physically entrapped into a SPF mixture solution of the present disclosure. A silk film of the present disclosure can be used to release at least one molecule or therapeutic agent of interest.

In some embodiments, the invention may include an article having a fiber or yarn having a coating, wherein the coating may include silk based proteins or fragments thereof having a weight average molecular weight range of about 5 kDa to about 144 kDa. In some embodiments, the article may be a fabric. In some embodiments, the silk based proteins or fragments thereof may include silk fibroin-based proteins or protein fragments having about 0.01% (w/w) to about 10% (w/w) sericin.

In some embodiments, the silk based proteins or fragments thereof may be selected from the group consisting of natural silk based proteins or fragments thereof that may be selected from the group consisting of spider silk based proteins or fragments thereof, silkworm silk based proteins or fragments thereof, and combinations thereof.

In some embodiments, the silk based proteins or fragments thereof may be natural silk based proteins or fragments thereof that may be selected from the group consisting of spider silk based proteins or fragments thereof, silkworm silk based proteins or fragments thereof, and combinations thereof.

In some embodiments, the natural silk based proteins or fragments may be silkworm silk based proteins or fragments thereof, and the silkworm silk based proteins or fragments thereof may be Bombyx mori silk based proteins or fragments thereof.

In some embodiments, the silk based proteins or fragments may include silk and a copolymer.

In some embodiments, the silk based proteins or protein fragments thereof may have an average weight average molecular weight range selected from the group consisting of about 5 to about 10 kDa, about 6 kDa to about 17 kDa, about 17 kDa to about 39 kDa, about 39 kDa to about 80 kDa, about 60 to about 100 kDa, and about 80 kDa to about 144 kDa, wherein the silk based proteins or fragments thereof may have a polydispersity of between about 1.5 and about 3

In some embodiments, the silk based proteins or fragments may include silk and a copolymer.

In some embodiments, the silk based proteins or protein fragments thereof may have an average weight average molecular weight range of about 1 kDa to about 350 kDa, wherein the silk based proteins or fragments thereof may have a polydispersity of between about 1.0 and about 5.0, and wherein the proteins or protein fragments, prior to coating the fabric, do not spontaneously or gradually gelate and do not visibly change in color or turbidity when in a solution for at least 10 days.

In some embodiments, the fiber or yarn may be selected from the group consisting of natural fiber or yarn, synthetic fiber or yarn, or combinations thereof.

In some embodiments, the fiber or yarn may be natural fiber or yarn selected from the group consisting of cotton, alpaca fleece, alpaca wool, lama fleece, lama wool, cotton, cashmere, sheep fleece, sheep wool, and combinations thereof. In some embodiments, the fiber or yarn may be natural fiber or yarn comprising wool, and combinations thereof. In some embodiments, the fiber or yarn may be natural fiber or yarn comprising cashmere, and combinations thereof.

In some embodiments, the fiber or yarn may be synthetic fiber or yarn selected from the group consisting of polyester, nylon, polyester-polyurethane copolymer, and combinations thereof.

In some embodiments, the fabric may exhibit an improved property, wherein the improved property may be an accumulative one-way moisture transport index selected from the group consisting of greater than 40%, greater than 60%, greater than 80%, greater than 100%, greater than 120%, greater than 140%, greater than 160%, and greater than 180%.

In some embodiments, the fabric may exhibit an improved property, wherein the improved property may be an accumulative one-way transport capability increase relative to uncoated fabric selected from the group consisting of 1.2 fold, 1.5 fold, 2.0 fold, 3.0 fold, 4.0 fold, 5.0 fold, and 10 fold.

In some embodiments, the fabric may exhibit an improved property, wherein the improved property may be an overall moisture management capability selected from the group consisting of greater than 0.05, greater than 0.10, greater than 0.15, greater than 0.20, greater than 0.25, greater than 0.30, greater than 0.35, greater than 0.40, greater than 0.50, greater than 0.60, greater than 0.70, and greater than 0.80. In some embodiments, the improved property may be determined after a period of machine washing cycles selected from the group consisting of 5 cycles, 10 cycles, 25 cycles, and 50 cycles.

In some embodiments, the fabric may exhibit substantially no increase in microbial growth after a number of machine washing cycles selected from the group consisting of 5 cycles, 10 cycles, 25 cycles, and 50 cycles. In some embodiments, the microbial growth may be microbial growth of a microbe selected from the group consisting of Staphylococcus aureus, Klebsiella pneumoniae, and combinations thereof. In some embodiments, the microbial growth may be reduced by a percentage selected from the group consisting of 50%, 100%, 500%, 1000%, 2000%, and 3000% compared to an uncoated fabric.

In some embodiments, the coating may be applied to the fabric at the fiber level prior to forming the fabric.

In some embodiments, the coating may be applied to the fabric at the fabric level. In some embodiments, the fabric may be bath coated. In some embodiments, the fabric may be spray coated. In some embodiments, the fabric may be coated with a stencil. In some embodiments, the coating may be applied to at least one side of the fabric using a method selected from the group consisting of a bath coating process, a spray coating process, a stencil process, a silk-foam based process, and a roller-based process.

In some embodiments, the coating may have a thickness of about one nanolayer.

In some embodiments, the coating may have a thickness selected from the group consisting of about 5 nm, about 10 nm, about 15 nm, about 20 nm, about 25 nm, about nm, about 100 nm, about 200 nm, about 500 nm, about 1 μm, about 5 μm, about 10 μm, and about 20 μm.

In some embodiments, the coating may be adsorbed on the fabric.

In some embodiments, the coating may be attached to the fabric through chemical, enzymatic, thermal, or irradiative cross-linking.

In some embodiments, the hand of the coated fabric may be improved relative to an uncoated fabric.

In some embodiments, the hand of the coated fabric that may be improved may be selected from the group consisting of softness, crispness, dryness, silkiness, and combinations thereof.

In some embodiments, a flame retardation property of the coated fabric may be improved relative to an uncoated fabric.

In some embodiments, a flame retardation property of an uncoated fabric may not be adversely affected by the coating.

In some embodiments, the abrasion resistance may be improved relative to an uncoated fabric.

In an embodiment, the invention may include an article comprising a textile or leather having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 5 kDa to about 144 kDa, or about 1 kDa to about 350 kDa.

In some embodiments, the silk based proteins or protein fragments thereof have an average weight average molecular weight range of about 1 kDa to about 350 kDa, wherein the silk based proteins or fragments thereof have a polydispersity of between about 1.0 and about 5.0, and wherein the proteins or protein fragments, prior to coating the fabric, do not spontaneously or gradually gelate and do not visibly change in color or turbidity when in a solution for at least 10 days.

In some embodiments, at least one property of the article may be improved, wherein the property that may be improved may be selected from the group consisting of color retention, resistance to microbial growth, resistance to bacterial growth, resistance to fungal growth, resistance to the buildup of static electrical charge, resistance to the growth of mildew, transparency of the coating, resistance to freeze-thaw cycle damage, resistance from abrasion, blocking of ultraviolet (UV) radiation, regulation of the body temperature of a wearer, resistance to tearing, elasticity of the article, rebound dampening, tendency to cause itching in the wearer, thermal insulation of the wearer, wrinkle resistance, stain resistance, stickiness to skin, and flame resistance.

In some embodiments, the article may be a textile used for apparel.

In some embodiments, the article may be fabricated as an item selected from the group consisting of an item of athletic apparel, an item of outdoor gear, a jacket, an overcoat, a shoe, a sneaker, a glove, an umbrella, a chair, a blanket, a towel, a surgical drape, a surgical gown, a laboratory coat, a wound dressing, a sterilization wrap, a surgical face mask, a surgical sleeve, a laboratory sleeve, a retention bandage, a support device, a compression bandage, a shoe cover, and a surgical blanket.

In some embodiments, the article may be a textile used to fabricate an automotive product.

In an embodiment, the invention may include a method of coating a fabric that may include the step of optionally applying a pretreatment selected from the group consisting of a wetting agent, a detergent, a sequestering or dispersing agent, an enzyme, a bleaching agent, an antifoaming agent, an anti-creasing agent, a dye dispersing agent, a dye leveling agent, a dye fixing agent, a dye special resin agent, a dye anti-reducing agent, a pigment dye system anti-migrating agent, a pigment dye system binder, a delave agent, a wrinkle free treatment, a softener, a handle modifier, a waterborne polyurethane dispersion, a finishing resin, an oil or water repellant, a flame retardant, a crosslinker, a thickener for technical finishing, or any combination thereof. In an embodiment, the method may include the step of applying a coating that may include a solution of silk based proteins or fragments thereof that may have an average molecular weight range of about 1 kDa to about 350 kDa, using a process selected from the group consisting of a continuous spray process, a continuous screen or stencil process, a continuous bath process, a batch spray process, a batch screen or stencil process, and a batch bath process. In an embodiment, the method may include the step of drying and optionally curing the coating.

In an embodiment, the silk based proteins or protein fragments thereof may have an average weight average molecular weight range of about 1 kDa to about 350 kDa, wherein the silk based proteins or fragments thereof may have a polydispersity of between about 1.0 and about 5.0, and optionally wherein the proteins or protein fragments, prior to coating the fabric, do not spontaneously or gradually gelate and do not visibly change in color or turbidity when in a solution for at least 10 days.

In one embodiment, the invention relates to a method of making a silk fibroin coated material, the method including preparing a silk fibroin solution comprising low molecular weight silk fibroin-based protein fragments, coating a surface of a material with the silk fibroin solution, and drying the surface of the material that has been coated with the silk fibroin solution to provide the silk fibroin coated material. In some embodiments, the silk fibroin solution further includes medium molecular weight silk fibroin-based protein fragments. In some embodiments, the w/w ratio between low molecular weight silk fibroin-based protein fragments and medium molecular weight silk fibroin-based protein fragments is about 90:10, about 80:20, about 75:25, about about 66:34, about 60:40, about 50:50, about 40:60, about 34:66, about 30:70, about 25:75, about 20:80, or about 10:90. In some embodiments, the w/w ratio between low molecular weight silk fibroin-based protein fragments and medium molecular weight silk fibroin-based protein fragments is about 3:1. In some embodiments, the silk fibroin solution further includes high molecular weight silk fibroin-based protein fragments. In some embodiments, the silk fibroin solution further includes medium molecular weight silk fibroin-based protein fragments, and high molecular weight silk fibroin-based protein fragments. In some embodiments, drying the surface of the material includes heating the surface of the material without substantially modifying silk fibroin coating performance. In some embodiments, the silk fibroin solution includes silk fibroin-based protein fragments between 0.01% and 1% volume (v/v). In some embodiments, the silk fibroin solution includes silk fibroin-based protein fragments at about 0.25% by volume (v/v). In some embodiments, the polydispersity of the silk fibroin-based protein fragments is between 1.5 and 3. In some embodiments, the silk fibroin solution further includes a Brønsted acid. In some embodiments, the silk fibroin solution further includes one or more of citric acid and acetic acid. In some embodiments, the silk fibroin solution has an acidic pH. In some embodiments, the silk fibroin solution has a pH between 4 and 5. In some embodiments, the method further includes coating the material with a silicone solution. In some embodiments, the silicone solution has an acidic pH. In some embodiments, the silk fibroin solution coating precedes the silicone solution coating. In some embodiments, the material includes one or more of a woven material, a non-woven material, a knit material, and a crochet material. In some embodiments, the material includes fabric, thread, yarn, or a combination thereof. In some embodiments, the material includes one or more of polyester, polyamide, polyaramid, polytetrafluoroethylene, polyethylene, polypropylene, polyurethane, silicone, mixtures of polyurethane and polyethyleneglycol, ultrahigh molecular weight polyethylene, high-performance polyethylene, nylon, and/or LYCRA.

In one embodiment, the invention relates to a method of improving hand in a material, the method including coating a surface of the material with a silk fibroin solution including low molecular weight silk fibroin-based protein fragments, drying the material, and coating a surface of the material with a silicone solution, wherein the resulting coated material has an improved hand compared to the uncoated material. In one embodiment, the invention relates to a method of improving hand retention on laundering in a material, the method including coating a surface of the material with a silk fibroin solution including low molecular weight silk fibroin-based protein fragments, drying the material, and coating a surface of the material with a silicone solution, wherein upon laundering, the coated material retains at least about 80% of its initial hand prior to laundering. In one embodiment, the invention relates to a method of improving the water drop absorption time of a material, the method including coating a surface of the material with a silk fibroin solution including low molecular weight silk fibroin-based protein fragments, drying the material, and coating a surface of the material with a silicone solution, wherein the resulting coated material has an improved water drop absorption time compared to the uncoated material. In one embodiment, the invention relates to a method of improving the abrasion resistance of a material, the method including coating a surface of the material with a silk fibroin solution including low molecular weight silk fibroin-based protein fragments, drying the material, and coating a surface of the material with a silicone solution, wherein the resulting coated material has an improved abrasion resistance compared to the uncoated material. In some embodiments, the silk fibroin solution further includes medium molecular weight silk fibroin-based protein fragments. In some embodiments, the w/w ratio between low molecular weight silk fibroin-based protein fragments and medium molecular weight silk fibroin-based protein fragments is about 90:10, about 80:20, about 75:25, about about 66:34, about 60:40, about 50:50, about 40:60, about 34:66, about 30:70, about 25:75, about 20:80, or about 10:90. In some embodiments, the w/w ratio between low molecular weight silk fibroin-based protein fragments and medium molecular weight silk fibroin-based protein fragments is about 3:1. In some embodiments, the silk fibroin solution further includes high molecular weight silk fibroin-based protein fragments. In some embodiments, the silk fibroin solution further includes medium molecular weight silk fibroin-based protein fragments, and high molecular weight silk fibroin-based protein fragments. In some embodiments, drying the surface of the material includes heating the surface of the material without substantially modifying silk fibroin coating performance. In some embodiments, the silk fibroin solution includes silk fibroin-based protein fragments between 0.01% and 1% volume (v/v). In some embodiments, the silk fibroin solution includes silk fibroin-based protein fragments at about 0.25% by volume (v/v). In some embodiments, the polydispersity of the silk fibroin-based protein fragments is between 1.5 and 3. In some embodiments, the silk fibroin solution further includes a Brønsted acid. In some embodiments, the silk fibroin solution further includes one or more of citric acid and acetic acid. In some embodiments, the silk fibroin solution has an acidic pH. In some embodiments, the silk fibroin solution has a pH between 4 and 5. In some embodiments, the silicone solution has an acidic pH. In some embodiments, the silk fibroin solution coating precedes the silicone solution coating. In some embodiments, the material includes one or more of a woven material, a non-woven material, a knit material, and a crochet material. In some embodiments, the material comprises fabric, thread, yarn, or a combination thereof. In some embodiments, the material includes one or more of polyester, polyamide, polyaramid, polytetrafluoroethylene, polyethylene, polypropylene, polyurethane, silicone, mixtures of polyurethane and polyethyleneglycol, ultrahigh molecular weight polyethylene, high-performance polyethylene, nylon, and/or LYCRA.

In an embodiment, the silk fibroin coated materials of the invention, for example a fiber, a yarn, or a fabric, may be coated with compositions including low molecular weight silk and medium molecular weight silk. In some embodiments, the w/w ratio between low molecular weight silk and medium molecular weight silk is between about 99:1 to about 1:99, between about 95:5 to about 5:95, between about 90:10 to about between about 75:25 to about 25:75, between about 65:35 to about 35:65, or between about 55:45 to about 45:55. In some embodiments, the w/w ratio between low molecular weight silk and medium molecular weight silk is between about 99:1 to about between about 95:5 to about 45:55, between about 90:10 to about 35:65, between about 75:25 to about 15:85, between about 65:35 to about 10:90, or between about to about 1:99. In an embodiment, the w/w ratio between low molecular weight silk and medium molecular weight silk is about 99:1, about 98:2, about 97:3, about 96:4, about 95:5, about 94:6, about 93:7, about 92:8, about 91:9, about 90:10, about 89:11, about 88:12, about 87:13, about 86:14, about 85:15, about 84:16, about 83:17, about 82:18, about 81:19, about 80:20, about 79:21, about 78:22, about 77:23, about 76:24, about 75:25, about 74:26, about 73:27, about 72:28, about 71:29, about 70:30, about 69:31, about 68:32, about 67:33, about 66:34, about 65:35, about 64:36, about 63:37, about 62:38, about 61:39, about 60:40, about 59:41, about 58:42, about 57:43, about 56:44, about 55:45, about 54:46, about 53:47, about 52:48, about 51:49, about about 49:51, about 48:52, about 47:53, about 46:54, about 45:55, about 44:56, about 43:57, about 42:58, about 41:59, about 40:60, about 39:61, about 38:62, about 37:63, about 36:64, about 35:65, about 34:66, about 33:67, about 32:68, about 31:69, about 30:70, about 29:71, about 28:72, about 27:73, about 26:74, about 25:75, about 24:76, about 23:77, about 22:78, about 21:79, about 20:80, about 19:81, about 18:82, about 17:83, about 16:84, about 15:85, about 14:86, about 13:87, about 12:88, about 11:89, about 10:90, about 9:91, about 8:92, about 7:93, about 6:94, about 5:95, about 4:96, about 3:97, about 2:98, or about 1:99. In an embodiment, the w/w ratio between low molecular weight silk and medium molecular weight silk is about 3:1. In an embodiment, the w/w ratio between low molecular weight silk and medium molecular weight silk is about 1:3.

In an embodiment, the silk fibroin coated materials of the invention, for example a fiber, a yarn, or a fabric, may be coated with compositions including low molecular weight silk and high molecular weight silk. In some embodiments, the w/w ratio between low molecular weight silk and high molecular weight silk is between about 99:1 to about 1:99, between about 95:5 to about 5:95, between about 90:10 to about between about 75:25 to about 25:75, between about 65:35 to about 35:65, or between about 55:45 to about 45:55. In some embodiments, the w/w ratio between low molecular weight silk and high molecular weight silk is between about 99:1 to about between about 95:5 to about 45:55, between about 90:10 to about 35:65, between about 75:25 to about 15:85, between about 65:35 to about 10:90, or between about to about 1:99. In an embodiment, the w/w ratio between low molecular weight silk and high molecular weight silk is about 99:1, about 98:2, about 97:3, about 96:4, about 95:5, about 94:6, about 93:7, about 92:8, about 91:9, about 90:10, about 89:11, about 88:12, about 87:13, about 86:14, about 85:15, about 84:16, about 83:17, about 82:18, about 81:19, about 80:20, about 79:21, about 78:22, about 77:23, about 76:24, about 75:25, about 74:26, about 73:27, about 72:28, about 71:29, about 70:30, about 69:31, about 68:32, about 67:33, about 66:34, about 65:35, about 64:36, about 63:37, about 62:38, about 61:39, about 60:40, about 59:41, about 58:42, about 57:43, about 56:44, about 55:45, about 54:46, about 53:47, about 52:48, about 51:49, about 50:50, about 49:51, about 48:52, about 47:53, about 46:54, about 45:55, about 44:56, about 43:57, about 42:58, about 41:59, about 40:60, about 39:61, about 38:62, about 37:63, about 36:64, about 35:65, about 34:66, about 33:67, about 32:68, about 31:69, about about 29:71, about 28:72, about 27:73, about 26:74, about 25:75, about 24:76, about 23:77, about 22:78, about 21:79, about 20:80, about 19:81, about 18:82, about 17:83, about 16:84, about 15:85, about 14:86, about 13:87, about 12:88, about 11:89, about 10:90, about 9:91, about 8:92, about 7:93, about 6:94, about 5:95, about 4:96, about 3:97, about 2:98, or about 1:99.

In some embodiments, the fiber or yarn may be selected from the group consisting of synthetic fiber or yarn, or combinations thereof.