Patent Grant
8361617
The present invention provides methods for the production of 3-dimensional porous silk fibroin scaffolds that can be used in tissue engineering. The silk fibroin scaffolds described herein are particularly suited for tissue engineering as the porosity of the scaffold can be adjusted throughout mimicking the gradient of densities found in natural tissue. Methods for producing 3-dimensional tissue using the silk based scaffolds are also provided.
A major goal of tissue engineering is to develop a biological alternative in vitro for regenerative tissue growth in vivo within a defect area. Porous polymer scaffolds play a crucial role in the three-dimensional growth and formation of new tissue in the field of tissue engineering.
In recent years biodegradable polymers such as poly (glycolic acid), poly (L-lactic acid) (PLLA) and their copolymers poly(L-lactic-co-glycolic acid) (PLGA) have been used as scaffold materials in studies of tissue formation. (Sofia et al. Journal of Biomedical materials research 2001, 54, 139-148). The advantages of these polymers is their biocompatibility and degradability. However, PLGA can induce inflammation due to the acid degradation products that result during hydrolysis (Sofia et al. Journal of Biomedical materials research 2001, 54, 139-148). There also are processing difficulties with polyesters that can lead to inconsistent hydrolysis rates and tissue response profiles. Thus, there is a need for polymeric materials that have more controllable features such as hydrolysis rates, structure, and mechanical strength, while also being biodegradable and biocompatible. Biological polymeric materials often demonstrate combinations of properties which are unable to be reproduced by synthetic polymeric materials. (Perez-Rigueiro et al. Science, 1998; 70: 2439-2447; Hutmacher D. Biomaterials 2000. 21, 2529-2543). Bone tissue is one example; scaffolds for bone tissue regeneration require high mechanical strength and porosity along with biodegradability and biocompatibility.
Several studies have shown that BMSCs can differentiate along an osteogenic lineage and form three-dimensional bone-like tissue (Holy et al. J. Biomed. Mater. Res. (2003) 65A:447-453; Karp et al., J. Craniofacial Surgery 14(3): 317-323). However, there are important limitations. Some calcium phosphate scaffolds show limited ability to degrade (Ohgushi et al. 1992. In CRC Handbook of bioactive ceramics. T. Yamamuro, L. L. Hench, and J. Wilson, editors. Boca Raton, Fla.: CRC Press. 235-238), or degradation is too rapid (Petite et al. 2000. Nat Biotechnol 18:959-963.) Polymeric scaffolds used for bone tissue engineering, such as poly(lactic-co-glycolic acid) or poly-L-lactic acid can induce inflammation due to acid hydrolysis products, and processing difficulties can lead to inconsistent hydrolysis rates and tissue response profiles (Athanasiou, et al. 1996. Biomaterials 17:93-102; Hollinger et al. 1996. Clin Orthop: 55-65). Difficulties in matching mechanical properties to support desired function also remain an issue (Harris et al. J Biomed Mater Res 42:396-402).
Studies have also shown that BMSCs can differentiate along chondrogenic lineage and form three-dimensional cartilage-like tissue on biomaterial substrates, such as poly(lactic-co-glycolic acid) or poly-L-lactic acid (Caterson et al. 2001. J Biomed Mater Res 57:394-403; Martin et al. 2001. J Biomed Mater Res 55:229-235). However, the use of these scaffolds for cartilage formation present with the same limitations as observed with their use in bone engineering.
Therefore, in light of the disadvantages in the existing polymers, and even for more diverse options in degradable polymer systems, there exists a need for additional biocompatible polymers, particularly polymers suitable for formation of scaffolds for mechanically robust applications such as bone or cartilage. The fabrication process for such scaffolds should be simple, reproducible, and the variables relatively easy to control in order to consistently modulate mechanical properties and porosity without sacrificing biodegradation.
The present invention relates to a porous silk fibroin material comprising a three-dimensional silk fibroin body having interconnected pores therein. The pores having a diameter of 50 to 1000 microns. The pore density is from 20-200 mg/ml, preferably from 40-150 mg/ml. Porosity ranges from 50-99.5%, preferably 70-99%. Most preferably the porosity is above 80%. The density or porosity can be adjusted depending on the use of material.
Preferably, the material has a compressive modulus of at least 100 kPa. More preferably, the material has a compressive modulus of at least 150 kPa. Even more preferably, the material has a compressive modulus of 200 kPa. Most preferably, the material has a compressive modulus of 250 kPa.
The porous silk fibroin material of the invention can be used, for example, as a scaffold for a engineered tissue or as a drug delivery device. In tissue engineering, the porosity of the scaffold can be adjusted as to mimic the gradient of cellular densities found in natural tissue. As such, an organized three-dimensional tissue with a shape and cellular organization substantially similar to that of the tissue in vivo is produced.
In one preferred embodiment, a porous silk fibroin material is produced by a process comprising the steps of: (a) forming a silk fibroin solution comprising silk fibroin in an aqueous salt solution; (b) removing the salt and water from the fibroin solution to form a silk fibroin substance; (c) forming a polymer solution comprising about 5 to 35% by weight of the silk fibroin substance in a solvent; (d) contacting the polymer solution with water-soluble non-toxic particles that are insoluble in organic solvents and have a diameter between about 50 and about 1000 microns; (e) placing the polymer solution into a form; (f) removing the solvent from the polymer; (g) contacting said polymer solution with an effective amount of an agent to induce β-sheet structure and insolubility in aqueous solution; (h) leaching said polymer with a solvent in which said particles are soluble and polymer is insoluble to remove said particles from said polymer; and (i) drying said polymer.
Preferably, the solvent in step (c) is selected from the group consisting of hexa-fluoro-iso-propanol (HFIP), N-methyl morpholine N-oxide and calcium nitrate-methanol. Most preferably the solvent is hexa-fluoro-iso-propanol (HFIP).
Preferably the solvent is removed from the polymer by sublimination or evaporation.
In another embodiment, the agent to induce β-sheet structure is an alcohol and is selected from the group consisting of methanol, 2-propanol, or 1-butanol, isoamyl alcohol. The agent may also be a solvent such as chloroform or acetone.
In yet another embodiment, the aqueous salt solution comprises lithium bromide, lithium thiocyanate, calcium nitrate or related chemicals that solubilize the silk.
In one embodiment, the particles are selected from the group consisting of alkali metal and alkaline earth metal halides, phosphates and sulfates, sugar crystals, water-soluble polymer microspheres, polysaccharides and protein microspheres.
In a preferred embodiment, the particles are sodium chloride crystals.
In one embodiment, the polymer used in the method is leached with water.
The invention also provides a porous silk fibroin scaffold material prepared by the process for producing a porous silk as outlined above. The porous silk fibroin material may be combined with other biodegradable polymers.
In one embodiment, the pore density or porosity may be different within separate portions of the material. For example, by altering the size of the water-soluble particles placed in different positions in the mold, the pore density of the material can be controlled.
The present invention further provides for methods for the production of tissue both in vivo and ex vivo using the porous silk fibroin scaffolds described herein. Tissues include for example, cartilaginous and bone tissue.
In one embodiment, tissue is produced ex vivo by culturing mammalian cells on a porous silk fibroin scaffold under conditions that are appropriate for inducing the tissue formation. A bioreactor is preferably used.
In another embodiment, a method for producing tissue in vivo is provided. The method comprises seeding mammalian cells on a porous silk fibroin scaffold and implanting said scaffold into a patient.
In one aspect of the invention, the mammalian cells that are used for producing tissue are multipotent cells selected from the group consisting of bone marrow stromal cells and adult or embryonic stem cells. In one preferred embodiment, for production of bone tissue, the cells are bone marrow stromal cells.
In one preferred embodiment, the porous silk fibroin scaffold has a 3-dimensional structure of a predetermined shape such that the tissue produced takes the form of the 3-dimensional structure.
In one embodiment, the porous silk fibroin scaffold used in tissue engineering comprises silk fibroin selected from the group consisting of silks from silkworms, silks from spiders, silks from genetically engineered cells, silks from transgenic plants and animals, silks from cultured cells, native silk, silk from cloned full or partial sequences of native silk genes, and silk from synthetic genes encoding silk or silk-like sequences. Preferably fibroin obtained from Bombyx mori silkworms is used.
In one embodiment, the porous silk fibroin scaffold further comprises an additive. As used herein, an “additive” is any biologically or pharmaceutically active compound. Additives include, but are not limited to, peptides, antibodies, DNA, RNA, modified RNA/protein composites, glycogens or other sugars, and alcohols. In one preferred aspect the additive is a peptide that contains an integrin binding sequence, e.g. RGD. In another preferred aspect the additive is a growth factor.
In another embodiment, the porous silk fibroin scaffold further comprises one or more biodegradable polymers selected from the group consisting of collagens, polylactic acid or its copolymers, polyglycolic acid or its copolymers, polyanhydrides, elastin, glycosaminoclycans and polysaccharides.
In still another embodiment, the porous silk fibroin scaffold further comprises one or more non-biodegradable polymers selected from the group consisting of polyethylene, polystyrene, polymethylmethylcryalte, polyethylene oxide and polyurethanes.
In yet another embodiment, the porous silk fibroin scaffold further comprises an agent that enhances proliferation and/or differentiation of said mammalian cells.
In one embodiment, the cells used for tissue engineering are autologous cells; cells derived from the recipient of the bone or cartilage implant. Autologous cells can be animal cells, e.g. dog, cat, monkey, pig, cow, human, and the like. In one preferred embodiment, the autologous cells are human.
In another embodiment the cells used for tissue engineering are donor cells, derived from a source other than the recipient. In one aspect the donor cells are allogenic cells, i.e. from the same species as the recipient. In another aspect, the donor cells are derived from a different species than the recipient.
The present invention also provides 3-dimensional tissues produced using the porous silk fibroin material of the invention.
In yet another embodiment a method for treating a patient in need of an implant is provided. The method comprises implanting a 3-dimensional porous silk fibroin scaffold of predetermined shape. In one aspect, for example, the 3-dimensional porous silk fibroin scaffold of predetermined shape is implanted as a bone substitute or as a cartilage substitute. The 3-dimensional porous silk fibroin scaffold can be seeded with autologous or donor cells prior to implantation. Alternatively, the 3-dimensional porous silk fibroin scaffold can be implanted without seeding cells.
Unless otherwise defined, all technical and scientific terms used herein have the same meaning as commonly understood by one of ordinary skill in the art. Although methods and materials similar or equivalent to those described herein can be used in the practice or testing of the invention, the preferred methods and materials are described below. All publications, patent applications, patents and other references mentioned herein are incorporated by reference. In addition, the materials, methods and examples are illustrative only and not intended to be limiting. In case of conflict, the present specification, including definitions, controls.
The accompanying figures, which are incorporated in and constitute a part of this specification, illustrate embodiments of the invention and, together with the description, serve to explain the objects, advantages, and principles of the invention.
The invention is based upon a surprising finding that silk proteins processed into 3-dimensional architectures provides for suitable biomaterial and tissue engineering matrices. The present invention provides a porous silk fibroin material comprising a 3-dimensional silk fibroin body having pores with a diameter of 50 to 1000 microns. The pore density can be adjusted depending on the use of material.
The unique properties of silks (mechanical strength, slow biodegradability, biocompatibility, sequence variants to influence properties) provide unique and versatile features from these matrices. The compressive strengths of gas foamed and salt leached porous silk matrices are comparable with various materials used in tissue engineering to make scaffolds as well as with the strength of cortical bone and cartilage. We discovered that salt leached silk scaffolds exhibited the best mechanical properties including that they had a high compressive modulus as well as compressive stress, and they were not brittle. However, the porous silk fibroin material of the present invention is not limited to this method of production.
In a preferred embodiment, scaffold features include high porosity, interconnected pores, biocompatibility, degradability, and pore sizes large enough for cell growth (greater than or equal to about 50-100 μm).
The methods useful for silk scaffold fabrication according to the present invention include (a) gas foaming, and (b) solvent casting/particulate leaching (Freyman et al. Progress in Materials Science 2001; 46:273-282; Mikos et al. Electronic Journal of Biotechnology, Accurate, 2000; 3: No. 2; Thomson et al. Biomaterials, 1998; 19:1935-1943; Widmer et al. Biomaterials, 1998; 19:1945-1955; Zhang R.& Ma P. Journal of Biomedical Material Science, 1999; 44:446-455; Nam et al. Journal of Applied Polymer Science, Vol. 81, 3008-30021, (2001); Agrawal et al. Journal of Biomedical Material resources 2001, 55, 141-150; Harris et al. Journal of Biomedical Material Research 1998, 42, 396-402; Hutmacher D. Journal of biomaterial science polymer science Edn 2001. 12, 107-124). The preferred method for material fabrication is leaching.
In the preferred embodiment, the solvent casting/particulate leaching method involves mixing a water-soluble porogen, for example, NaCl with a viscous silk polymer solution (Freyman et al. Progress in Materials Science 2001; 46:273-282; mikos et al. Electronic Journal of Biotechnology, Accurate, 2000; 3: No. 2; Agrawal et al. Journal of Biomedical Material resources 2001, 55, 141-150; Hutmacher D. Biomaterials 2000. 21, 2529-2543; Hutmacher D. Journal of biomaterial science polymer science Edn 2001. 12, 107-124). The mixture is cast into a Teflon container where the solvent is evaporated. The result is a salt/polymer composite. The composite is immersed in water to leach out the salt, resulting in a porous three-dimensional structure.
The silk proteins suitable for use in the present invention is preferably fibroin or related proteins (i.e., silks from spiders). As used herein, the term “fibroin” includes selected proteins such as silk from spiders. Preferably, fibroin is obtained from a solution containing a dissolved silkworm silk or spider silk. The silkworm silk protein is obtained, for example, from Bombyx mori, and the spider silk is obtained from Nephila clavipes. In the alternative, the silk proteins suitable for use in the present invention can be obtained from a solution containing a genetically engineered silk, such as from bacteria, yeast, mammalian cells, transgenic animals or transgenic plants.
Silk polymer or silk fibroin solution according to the present invention can be prepared by any conventional method known to one skilled in the art. For example, B. mori cocoons are boiled for about 30 minutes in an aqueous solution. Preferably, the aqueous solution is about 0.02M Na2CO3. The cocoons are rinsed, for example with water, to extract the sericin proteins and the extracted silk is dissolved in an aqueous salt solution. Salts useful according to the present invention include, lithium bromide, lithium thiocyanate, calcium nitrate or other chemical capable of solubilizing silk. Preferably, the extracted silk is dissolved in about 9-12 M LiBr solution. The salt is consequently removed using, for example, dialysis. See
The silk polymer solution is formed by mixing about 5% to 35% by weight of the silk fibroin with a solvent. Preferably about 17% (w/v) of silk is used. Solvents useful according to the present invention include hexa-fluoro-iso-propanyl (HFIP), N-methyl morpholine N-oxide and calcium nitrate-methanol. The preferred solvent is HFIP.
The silk polymer/solvent solution of the present invention is placed into a form, or mold, containing water-soluble particles, or porogens, that are insoluble in organic solvents. Alternatively, the porogens are mixed with the silk polymer solution prior to placement in the mold. The diameter of the particles are preferably between about 50-1000 microns. Examples of water-soluble porogens useful according to the present invention include, NaCl, alkali metals, alkali earth metal halides, phosphates, and sulfates, sugar crystals, water-soluble microspheres, polysaccharides and protein microspheres.
The solvent is consequently removed using, for example, sublimation or evaporation. The polymer solution is treated with an effective amount of alcohol to induce β-sheet structure and insolubility in aqueous solution.
The composite or polymer is immersed in water or other solvent in which the particles, or porogens are soluble and polymer is insoluble, to remove the particles, resulting in a porous three-dimensional structure, referred herein to as a “silk fibroin scaffold” or “silk fibroin material.” See
In general, regenerated silk fibroin is soluble in water and requires immersion in an alcohol or other suitable agent to obtain the β-sheet structure so that it will be insoluble (Sofia et al. Journal of Biomedical materials research 2001, 54, 139-148). Therefore, prior to submersion into aqueous solutions the silk scaffolds are first soaked in a β-sheet structure inducing agent, such as alcohol to induce the phase transition to β-sheet structure. The type of a β-sheet structure inducing agent can be used to generate scaffolds with different properties. For example, as shown in the following examples, when methanol and propanol are used to induce β-sheet structure, the resulting scaffolds are stronger but more brittle and therefore suitable in bone regeneration.
The present invention provides porous silk materials that can be used as scaffolds in tissue regeneration. The porous silk of the present invention have strong mechanical properties as well as pore structure and interconnections among the pores, as shown in
The density of the silk fibroin material is expressed as:
d=W/(V2−V3);
where
The porosity of the silk fibroin material (ε) is measured by the following formula:
ε=(V1−V3)/(V2−V3).
The scaffold material of the present invention is relatively easy to fabricate and has a controlled porous architecture to allow for cell in-growth and tissue regeneration. The ability to adjust porosity provides a means by which an organized three-dimensional tissue with a shape and cellular organization substantially similar to that of the tissue in vivo can be produced.
The porous silk scaffolds of the present invention may further include additives. The additives can be covalently coupled to the scaffold by means known to those skilled in the art. Alternatively, the additive can be added to media surrounding the scaffold.
Additives suitable for use with the present invention includes biologically or pharmaceutically active compounds. Examples of biologically active compounds include, but are not limited to: cell attachment mediators, such as collagen, elastin, fibronectin, vitronectin, laminin, proteoglycans, or peptides containing known integrin binding domains e.g. “RGD” integrin binding sequence, or variations thereof, that are known to affect cellular attachment (Schaffner P & Dard 2003 Cell Mol Life Sci. January; 60(1):119-32; Hersel U. et al. 2003 Biomaterials. November; 24(24):4385-415); biologically active ligands; and substances that enhance or exclude particular varieties of cellular or tissue ingrowth. For example, the steps of cellular repopulation of the scaffold matrix preferably are conducted in the presence of growth factors effective to promote proliferation of the cultured cells employed to repopulate the matrix. Agents that promote proliferation will be dependent on the cell type employed. For example, when fibroblast cells are employed, a growth factor for use herein may be fibroblast growth factor (FGF), most preferably basic fibroblast growth factor (bFGF) (Human Recombinant bFGF, UPSTATE Biotechnology, Inc.). Other examples of additive agents that enhance proliferation or differentiation include, but are not limited to, osteoinductive substances, such as bone morphogenic proteins (BMP); cytokines, growth factors such as epidermal growth factor (EGF), platelet-derived growth factor (PDGF), insulin-like growth factor (IGF-I and II) TGF-β, and the like. As used herein, the term additive also encompasses antibodies, DNA, RNA, modified RNA/protein composites, glycogens or other sugars, and alcohols.
The scaffolds can be shaped into articles for tissue engineering and tissue guided regeneration applications, including reconstructive surgery. The structure of the scaffold allows generous cellular ingrowth, eliminating the need for cellular preseeding. The porous polymer scaffolds may also be molded to form external scaffolding for the support of in vitro culturing of cells for the creation of external support organs.
The silk fibroin scaffolds of the present invention may also be mixed with other biocompatible polymers to form mixed polymer scaffolds. Two or more biocompatible polymers can be added to the aqueous solution together with the silk polymer. The biocompatible polymer preferred for use in the present invention is selected from the group comprising polyethylene oxide (PEO), polyethylene glycol (PEG), collagen, fibronectin, keratin, polyaspartic acid, polylysine, alginate, chitosan, chitin, hyaluronic acid, pectin, polycaprolactone, polylactic acid, polyglycolic acid, polyhydroxyalkanoates, dextrans, polyanhydrides, polymer, PLA-PGA, polyanhydride, polyorthoester, polycaprolactone, polyfumarate, collagen, chitosan, alginate, hyaluronic acid and other biocompatible polymers.
The scaffold functions to mimic the extracellular matrices (ECM) of the body. The scaffold serves as both a physical support and an adhesive substrate for isolated cells during in vitro culture and subsequent implantation. As the transplanted cell populations grow and the cells function normally, they begin to secrete their own ECM support.
In the reconstruction of structural tissues like cartilage and bone, tissue shape is integral to function, requiring the molding of the scaffold into articles of varying thickness and shape. Any crevices, apertures or refinements desired in the three-dimensional structure can be created by removing portions of the matrix with scissors, a scalpel, a laser beam or any other cutting instrument. Scaffold applications include the regeneration of tissues such as nervous, musculoskeletal, cartilaginous, tendenous, hepatic, pancreatic, ocular, integumenary, arteriovenous, urinary or any other tissue forming solid or hollow organs.
The scaffold may also be used in transplantation as a matrix for dissociated cells such to create a three-dimensional tissue or organ. Tissues or organs can be produced by methods of the present invention for any species.
A number of different cell types or combinations thereof may be employed in the present invention, depending upon the intended function of the tissue engineered construct being produced. These cell types include, but are not limited to: smooth muscle cells, skeletal muscle cells, cardiac muscle cells, epithelial cells, endothelial cells, urothelial cells, fibroblasts, myoblasts, chondrocytes, chondroblasts, osteoblasts, osteoclasts, keratinocytes, hepatocytes, bile duct cells, pancreatic islet cells, thyroid, parathyroid, adrenal, hypothalamic, pituitary, ovarian, testicular, salivary gland cells, adipocytes, and precursor cells. For example, smooth muscle cells and endothelial cells may be employed for muscular, tubular constructs, e.g., constructs intended as vascular, esophageal, intestinal, rectal, or ureteral constructs; chondrocytes may be employed in cartilaginous constructs; cardiac muscle cells may be employed in heart constructs; hepatocytes and bile duct cells may be employed in liver constructs; epithelial, endothelial, fibroblast, and nerve cells may be employed in constructs intended to function as replacements or enhancements for any of the wide variety of tissue types that contain these cells. In general, any cells may be employed that are found in the natural tissue to which the construct is intended to correspond. In addition, progenitor cells, such as myoblasts or stem cells, may be employed to produce their corresponding differentiated cell types. In some instances it may be preferred to use neonatal cells or tumor cells.
Cells can be obtained from donors (allogenic) or from recipients (autologous). Cells can also be of established cell culture lines, or even cells that have undergone genetic engineering. Pieces of tissue can also be used, which may provide a number of different cell types in the same structure.
Appropriate growth conditions for mammalian cells are well known in the art (Freshney, R. I. (2000) Culture of Animal Cells, a Manual of Basic Technique. Hoboken N.J., John Wiley & Sons; Lanza et al. Principles of Tissue Engineering, Academic Press; 2nd edition May 15, 2000; and Lanza & Atala, Methods of Tissue Engineering Academic Press; 1st edition October 2001). Cell culture media generally include essential nutrients and, optionally, additional elements such as growth factors, salts, minerals, vitamins, etc., that may be selected according to the cell type(s) being cultured. Particular ingredients may be selected to enhance cell growth, differentiation, secretion of specific proteins, etc. In general, standard growth media include Dulbecco's Modified Eagle Medium, low glucose (DMEM), with 110 mg/L pyruvate and glutamine, supplemented with 10-20% fetal bovine serum (FBS) or calf serum and 100 U/ml penicillin are appropriate as are various other standard media well known to those in the art. Growth conditions will vary dependent on the type of mammalian cells in use and tissue desired.
In one embodiment, methods are provided for producing bone or cartilage tissue in vitro comprising culturing multipotent cells on a porous silk fibroin scaffold under conditions appropriate for inducing bone or cartilage formation. Suitable conditions for the generation of bone and cartilage are well known to those skilled in the art. For example, conditions for the growth of cartilage tissue often comprise nonessential amino acids, ascorbic acid-2-phosphate, dexamethasone, insulin, and TGF-β1. In one preferred embodiment, the nonessential amino acids are present at a concentration of 0.1 mM, ascorbic acid-2-phosphate is present at a concentration of 50 ug/ml, dexamethasone is present at a concentration of 10 nM, insulin is present at a concentration of 5 ug/ml and TGF-β1 is present at a concentration of 5 ng/ml. Suitable conditions for the growth of bone often include ascorbic acid-2-phosphate, dexamethasone, β-glycerolphoasphate and BMP-2. In a preferred embodiment, ascorbic acid-2-phosphate is present at a concentration of 50 ug/ml, dexamethasone is present at a concentration of 10 nM, β-glycerolphoasphate is present at a concentration of 7 mM and BMP-2 is present at a concentration of 1 ug/ml.
In general, the length of the growth period will depend on the particular tissue engineered construct being produced. The growth period can be continued until the construct has attained desired properties, e.g., until the construct has reached a particular thickness, size, strength, composition of proteinaceous components, and/or a particular cell density. Methods for assessing these parameters are known to those skilled in the art.
Following a first growth period the construct can be seeded with a second population of cells, which may comprise cells of the same type as used in the first seeding or cells of a different type. The construct can then be maintained for a second growth period which may be different in length from the first growth period and may employ different growth conditions. Multiple rounds of cell seeding with intervening growth periods may be employed.
In one preferred embodiment, tissues and organs are generated for humans. In other embodiments, tissues and organs are generated for animals such as, dogs, cats, horses, monkeys, or any other mammal.
The cells are obtained from any suitable donor, either human or animal, or from the subject into which they are to be implanted. As used herein, the term “host” or “subject” includes mammalian species, including, but not limited to, humans, monkeys, dogs, cows, horses, pigs, sheep, goats, cats, mice, rabbits, rats.
The cells that are used for methods of the present invention should be derived from a source that is compatible with the intended recipient. The cells are dissociated using standard techniques and seeded onto and into the scaffold. In vitro culturing optionally may be performed prior to implantation. Alternatively, the scaffold is implanted into the subject, allowed to vascularize, then cells are injected into the scaffold. Methods and reagents for culturing cells in vitro and implantation of a tissue scaffold are known to those skilled in the art.
Cells can be seeded within the matrix either pre- or post matrix formation, depending on the method of matrix formation. Uniform seeding is preferable. In theory, the number of cells seeded does not limit the final tissue produced, however optimal seeding may increase the rate of generation. The number of seeded cells can be optimized using dynamic seeding (Vunjak-Novakovic et al. Biotechnology Progress 1998; Radisic et al. Biotechnoloy and Bioengineering 2003).
It is another aspect of the invention that the 3-dimensional porous silk scaffold, described herein, can itself be implanted in vivo and serve as tissue substitute (e.g. to substitute for bone or cartilage). Such implants, would require no seeding of cells, but contain an addition e.g., RGD, that attracts cells.
In one embodiment, silk matrix scaffolds are seeded with multipotent cells in the presence of media that induces either bone or cartilage formation. Suitable media for the production of cartilage and bone are well known to those skilled in the art.
As used herein, “multipotent” cells have the ability to differentiate into more than one cell type in response to distinct differentiation signals. Examples of multipotent cells include, but are not limited to, bone marrow stromal cells (BMSC) and adult or embryonic stem cells. In a preferred embodiment BMSCs are used. BMSCs are multipotential cells of the bone marrow which can proliferate in an undifferentiated state and with the appropriate extrinsic signals, differentiate into cells of mesenchymal lineage, such as cartilage, bone, or fat (Friedenstein, A. J. 1976. Int Rev Cytol 47:327-359; Friedenstein et al. 1987. Cell Tissue Kinet 20:263-272; Caplan, A. I. 1994. Clin Plast Surg 21:429-435; Mackay et al. 1998. Tissue Eng 4:415-428; Herzog et al. Blood. 2003 Nov. 15; 102(10):3483-93. Epub 2003 Jul. 31).
The formation of cartilaginous tissue or bone can be monitored by assays well known to those in the art including, but not limited to, histology, immunohistochemistry, and confocal or scanning electron microscopy (Holy et al., J. Biomed. Mater. Res (2003) 65A:447-453).
Using silk based scaffolds, organized tissue with a predetermined form and structure can be produced either in vitro or in vivo. For example, tissue that is produced ex vivo is functional from the start and can be used as an in vivo implant. Alternatively, the silk based structure can be seeded with cells capable of forming either bone or cartilage and then implanted as to promote growth in vivo. Thus, the scaffolds can be designed to form tissue with a “customized fit” that is specifically designed for implantation in a particular patient. For example, cartilaginous tissue or bone tissue produced by methods of the present invention can be used to replace large cartilage or bone defects found in musculoskeletal disorders and degenerative diseases such as osteoarthritis or rheumatism. Engineered bone and cartilage are also suitable for spine and joint replacements such as, elbow, knee, hip or finger joints or can be used in osteochondral implants.
Three fabrication techniques; freeze-drying, salt leaching and gas foaming, were used to form porous three-dimensional silk biomaterial matrices. Matrices were characterized for morphological and functional properties related to processing method and conditions. The porosity of the salt leached scaffolds varied between 84-98% with a compressive strength up to 175±3 KPa and the gas foamed scaffolds had porosities of 87-97% and compressive strength up to 280±4 KPa. The freeze-dried scaffolds were prepared at different freezing temperatures (−80 and −20° C.), and subsequently treated with different concentrations (15 and 25%) and hydrophilicity alcohols. The porosity of these scaffolds was up to 99% and the maximum compressive strength was 30±2 KPa. Changes in silk fibroin structure during processing to form the 3D matrices was determined by FT-IR and XrD. The salt leached and gas foaming techniques produced scaffolds with a useful combination of high compressive strength, interconnected pores and pore sizes greater than 100 microns in diameter.
1. Materials
Cocoons of B. mori silkworm silk were kindly supplied by M Tsukada, Institute of Sericulture, Tsukuba, Japan and Marion Goldsmith, University of Rhode Island, USA. Sodium chloride and ammonium bicarbonate granules were purchased from Sigma. Hexa-fluoro-iso-propanol (HFIP), methanol, 2-propanol, and 1-butanol, were purchased from Aldrich and used without further purification.
Preparation of Regenerated B. mori Silk Fibroin Solutions
B. mori silk fibroin was prepared as follows as a modification of our earlier procedure (Nam & Young, Science 2001, 81, 3008-30021). Cocoons were boiled for 30 min in an aqueous solution of 0.02 M Na2CO3 then rinsed thoroughly with water to extract the glue-like sericin proteins. The degummed silk was then dissolved in 9-12 M LiBr solution at room temperature yielding a 7-8% (w/v) solution. This solution was dialyzed in water using Slide-a-Lyzer dialysis cassettes (Pierce, MWCO 2000). The final concentration of the aqueous silk fibroin solution was about 2-5.8 wt %, which was determined by weighing the remaining solid after drying. The HFIP silk solutions were prepared by dissolving the silk fibroin produced after lyophilizing the aqueous silk solution into the HFIP.
3D Scaffold Fabrication By Gas Foaming or Salt Leaching Using Silk Solution in HFIP
A viscous silk solution was prepared by dissolving 17% (w/v) silk in HFIP (
Scaffold Fabrication By Freeze-Drying Using Aqueous Silk Solutions
A viscous silk precipitate in gel paste form was prepared by adding 15 or 25 vol % of methanol or propanol to an aqueous silk solution (5.8 wt %) with gentle mixing (
Scaffold Characterization
SEM
The surface and cross-section morphologies of the scaffolds and pore distributions, sizes, and interconnectivity were observed with a LEO Gemini 982 Field Emission Gun SEM. Segments of the outer surface and inner area of the scaffold were prepared by fracture of scaffolds in liquid nitrogen. The specimens were sputter coated with gold. The pore sizes were determined by measuring random samples of ten pores from the SEM images using Corel computer software.
Density and Porosity
The density and porosity of the silk scaffolds were measured by liquid displacement, similar to the published methods (Zhang et al. Journal of Biomedical Material Science, 1999; 44:446-455).
Hexane was used as the displacement liquid since it is a non-solvent for silk and is able to easily permeate through the scaffold and not cause swelling or shrinkage, unlike ethanol. A sample of weight W was immersed in known volume (V1) of hexane in a graduated cylinder. The sample was left in the hexane covered for approximately 5 min. In this time the contents in the cylinder underwent an evacuation-repressurization cycle to force the hexane through the pores. The total volume of the hexane and the hexane-impregnated scaffold was V2. The volume difference (V2−V1) is the volume of the polymer scaffold. The hexane-impregnated scaffold was then removed from the cylinder and the residual hexane volume was recorded as V3. The quantity (V1−V3)—volume of hexane within the scaffold—was determined as the void volume of the scaffold. The total volume of the scaffold: V=(V2−V1)+(V1−V3). The density of the foam is expressed as:
d=W/(V2−V3)
and the porosity of the foam (ε) was obtained by:
ε=(V1−V3)/(V2−V3)
Mechanical Properties
The compression modulus of the scaffolds was evaluated at room temperature on an Instron 881 equipped with a 100N load cell. Cross-head speed was set at 2 mm/min. Cylinder-shaped samples measuring 8.7 mm in diameter and ranging between 3.2 and 9.5 mm in height were used, according to a modification based on ASTM method F451-95. The compressive stress and strain were graphed and the average compressive strength as well as the compressive modulus and standard deviation determined. The elastic modulus is the ratio of the stress to strain when deformation is totally elastic; also a measure of stiffness, and the compressive strength is the maximum engineering stress that may be sustained without (Callister et al., 2000 In Materials Science Enginering; An Introduction; John Wiley & Sons, Inc, New York, pp 114-127).
FTIR
The infrared spectra of the silk fibroin structures were measured with a FT-IR (Bruker Equinox 55) spectrophotometer. The samples were cast on a ZnS cell crystal surface directly from silk fibroin solution. The cast films were treated with alcohols directly. Each spectrum for samples was acquired in transmittance mode by accumulation of 256 scans with a resolution of 4 cm−1 and a spectral range of 4000-400 cm−1. The crystallization effect was investigated on the foams by alcohol type; methanol and 2-propanol. X-ray diffraction was used to determine crystal structure in the scaffolds from the freeze-drying method. Wide angle X-ray diffraction (WAXD) experiments were conducted on a Bruker D8 Discover X-ray diffractometer with general area detector diffraction (GADDS) multiwire area detector; 40 KV, 20 mA and 0.5 mm collimator. The distance between the detector and the sample for WAXD was 81.4 mm (CuKα).
Summary of Results and Discussion
Porous silk matrices were formed using three processing methods: freeze-drying, gas foaming, and salt leaching.
Silk fibroin in solution or frozen at low temperature is generally in a random coil structure based on FTIR analysis. Some aggregation occurs during this process. The silk porous matrices formed at −80° C. resulted in similar morphologies, regardless of the freezing rate or alcohol type and concentration used in the processing. Pores were small, ˜10 microns in diameter, and very fine silk aggregates were observed. There was a difference in morphology when comparing the forms formed with methanol versus 2-propanol at −20° C. With 2-propanol a more leaf or sheet like morphology was observed; while with the methanol smaller spherical pores were formed. The methanol formed foams were friable and easily broken, unlike the scaffolds formed from 2-propanol. These results likely reflect differences in miscibility of the two alcohols with water, since 2-propanol is not highly miscible, leading to larger pore features.
The glass transition temperature is important in the formation of pores within the silk fibroin matrix. The glass transition zone of silk in an aqueous solution is, −20 to −34° C. (Li, M. et al. Journal of Applied Polymer Science 2001, 79, 2185-2191; Nam, J et al. Journal of Applied Polymer Science 2001, 81, 3008-30021). The higher the freezing temperature above the glass transition the longer it will take for ice to form and grow. Therefore, the ice particles will have a greater effect on the size of the pores. The longer the freezing time then the larger the pores. Once the temperature is below the glass transition zone, the pore size is no longer dependent on the temperature.
The porogen particles used for the salt leaching and gas foaming techniques were not sieved to obtain a specific porogen size. Therefore, the resulting pores followed a Gaussian distribution. The salt leached scaffolds (
Scaffolds formed by gas foaming were processed using ammonium bicarbonate as the porogen. The gas foamed scaffolds with higher porosity were not as strong and flaked apart. SEM images showed a highly interconnected open pore morphology with diameters in the range of 155±114 μm. The gas foamed process did not leave a skin layer on the surface of the scaffold. Larger pores could also be formed if larger salt particles were used, the process is only limited by the size of the porogen selected.
Porosity
Matrices with up to 99% porosity were formed depending on the processing method: freeze-drying, gas foaming, and salt leaching (Table 1). The scaffolds prepared by freeze-drying resulted in porosities ˜99%, regardless of the variables studied. With salt leaching and gas foaming, and varying the porogen, (salt to silk ratio of 10:1 or 20:1, wt/wt) the porosities were 84±1% to 98±4% for the salt leached scaffolds and 87±2% to 97±3% for the gas foamed scaffolds.
1Porosity
2Density (mg/ml)
3Weight ratio of water in alcohol
Structure
FTIR spectra of silk fibroins immersed in methanol, 2-propanol, and 1-butanol were observed (
Mechanical Properties
The structure of the freeze-dried scaffolds was foam like and very porous. The compressive strength (Table 2) of 15% and 25% methanol treated foams formed at −20° C. were 10±2 and 10±3 KPa, respectively, with a compressive modulus of 20±1 and 10±3 KPa, respectively. The foams processed using 15 and 25% 2-propanol had a compressive strength of 10±2 and 10±3 KPa, respectively, and a compressive modulus of 40±4 and 50±8 KPa, respectively. The structures of the foams treated with propanol were more compact and less porous macroscopically, they did not flake apart easily. The foams processed using methanol were flakier and easily broken.
Methanol is a hydrophilic alcohol, miscible with water, and when it comes into contact with a silk solution it induces the chains of fibroin to interact with each other (Li, M. et al. Journal of Applied Polymer Science 2001, 79, 2185-2191; Li, M et al. Journal of Applied Polymer Science 2001, 79, 2192-2199; Nam, J et al. Journal of Applied Polymer Science 2001, 81, 3008-30021; Magoshi, J. Kobunshi Ronbunshu 1974, 31, 765-770; Magoshi, J. et al. Applied Polymer Symposia 1985, 41, 187-204). The fibroin silk chains are then able to organize into a β-sheet structure. When silk is in the β-sheet structure it is in a crystalline form making it more brittle. 2-Propanol is less hydrophilic than methanol and therefore less miscible with water. When added to the silk fibroin solution there is a phase separation. Since propanol is not as miscible as methanol, less water is drawn from the silk and less β-sheet structure forms when compared to the methanol treated foams (Li, M. et al. Journal of Applied Polymer Science 2001, 79, 2185-2191; Li, M et al. Journal of Applied Polymer Science 2001, 79, 2192-2199; Nam, J et al. Journal of Applied Polymer Science 2001, 81, 3008-30021; Magoshi, J. Kobunshi Ronbunshu 1974, 31, 765-770; Magoshi, J. et al. Applied Polymer Symposia 1985, 41, 187-204). The foams containing 2-propanol are not crystalline and are tougher, therefore with a higher compressive modulus than those processed with methanol. With an increase in the concentration of methanol there is an increase in compressive modulus. This decrease occurs because of the increase in crystallinity. With a higher concentration of methanol, more rapid and extensive chain rearrangements occur leading to a higher content of β-sheets within the foam (Li, M. et al. Journal of Applied Polymer Science 2001, 79, 2185-2191; Li, M et al. Journal of Applied Polymer Science 2001, 79, 2192-2199).
With the scaffolds prepared at −80° C. with alcohol, methanol and 2-propanol, at concentrations of 15 and 25%, there is an increase in the compressive strength and compressive modulus (Table 2).
1100% unless otherwise indicated, weight percent of the alcohol in water.
This increase may be due to the increased freezing rate induced by the temperature decrease. At this point the foams are able to form only small pores, even though the foams are highly porous, and the compressive force may distributed differently within this structure of the foams.
The gas foamed scaffolds were also treated with alcohols before compressive mechanical test. Scaffolds immersed in methanol and propanol had higher compressive strengths and compressive modulus; 280±4 KPa and 900±94 KPa, respectively, and 250±28 and 800±44 KPa, respectively. When mechanically crushed, the scaffolds flaked apart and were not as ductile as those produced by the salt leached method. There was a dramatic difference in compressive stress between the scaffolds with 87% porosity versus 97% porosity. Scaffolds with a high porosity had a lower compressive strength than the low porosity foams (Table 2).
The salt leached scaffolds prepared using a 10:1 salt to silk ratio had compressive strengths from 30 and 150 KPa depending on alcohol treatment (Table 2). Values were higher for the 20:1 samples. These scaffolds were immersed in methanol, 1-butanol, and 2-propanol. The scaffolds with 84% porosity were thin and formed thick skin layers, therefore data were not reliable due to the heterogeneous structure.
The gas foamed scaffolds generated a definite compressive yield point where the scaffold was no longer able to maintain its original features. However, the salt leached scaffolds showed characteristics that were more ductile and sponge-like in behavior. After maximum compression was reached densification occurred and the scaffold was crushed yet did not flake apart. The cells of the scaffold no longer maintained their shape.
The salt leached scaffolds varied in ductility. The pore structure of the salt leached scaffolds was not uniform perhaps due to the evaporation of the organic solvent, HFIP, and the increase in the polymer concentration of the remaining solution entrapped within the salt bed. The outer surface of the salt leached scaffolds formed a dense skin layer; common when highly volatile solvents are evaporated from the interior region of a matrix (Nam, Y. S. et al. Biomaterials 1999, 20, 1783-1790). The evaporation of the organic solvent from the surface forced the formation of a thick film on the scaffold allowing very few pores to form for the rest of the solvent to evaporate. This residual solvent in the matrix function as a plasticizer and makes the polymer more ductile. It often takes up to three days to remove the residual solvent from these silk matrices, due to this dense skin layer, based on weight changes over time.
The gas foamed scaffolds had a higher compressive strength and compressive modulus than the salt leached scaffolds. The reasons for this difference in mechanical properties may be the uniform distribution of the pores within the gas foamed scaffolds which lead to more consistent mechanical properties, and/or the pore sizes themselves. The stress applied to the matrix is concentrated at pore interfaces and if the pore distribution is not uniform then the polymer matrix can typically deform at a lower compressive strength (Harris, L. D et al. Journal of Biomedical Material Research 1998, 42, 396-402; Ehrenstein, G. W. Mechanical Behavior. In Polymeric Materials; Structure, Properties, and Applications; Hanser/Gardener Publications, Inc., Cincinnati, 2001; pp 167-182). Since the salt leached scaffold consists of both open and closed pore structures the distribution of the compressive forces was uneven, causing the scaffold to collapse at lower stress (Harris, L. D. et al. J. Journal of Biomedical Material Research 1998, 42, 396-402).
The mechanical data show the deformation and compression trends of the scaffolds as load is applied. In tissue engineering scaffolds for bone-related applications, matrices are usually designed to hold a load that will allow for 1 to 2% strain (Table 3). The gas foamed scaffolds and the salt leached scaffolds treated with methanol were analyzed. Of the scaffolds prepared and evaluated these are the most likely to be used in bone tissue regeneration, therefore the secant modulus, used to assess stress-strain relationships at a specific load level (Kim, S.; Cho, et al. Fibers and Polymers 2001, 2, 64-70), were determined. Compared to porous biodegradable polymeric scaffolds often considered in bone-related tissue engineering studies, the silk porous scaffolds had similar properties at 1 and 2% strain. The gas foamed scaffolds showed the highest compressive modulus. These data are also comparable to the strength of cortical bone and cartilage (Table 4).
apoly (d,L-lactic-co-glycolic acid) and NaCl particles were compression molded to form PLGA/NaCl composite. 95% porous scaffold processed using salt leaching method (Harris, L. D.; Kim, B.-S.; Mooney, D. J. Journal of Biomedical Material Research 1998, 42, 396-402).
bpoly (D,L-lactic-co-glycolic acid) 95% porous scaffold processed using gas foaming method(Harris, L. D.; Kim, B.-S.; Mooney, D. J. Journal of Biomedical Material Research 1998, 42, 396-402).
cpoly(L-lactic acid) designed using gas foaming method and NH4HCO3 particles as porogen. The weight ratio of NH4HCO3 to PLLA is 10:1 (Nam, Y. S.; Yoon, J. J.; Park, T. G. J. Biomed. Mater. Res. 2000, 53, 1-7).
dpoly(L-lactic acid) designed using gas foaming method and NH4HCO3 particles as porogen. The weight ratio of NH4HCO3 to PLLA is 20:1(Nam, Y. S.; Yoon, J. J.; Park, T. G. J. Biomed. Mater. Res. 2000, 53, 1-7)..
eporous collagen sponge processed by lyophilization (Kim, S et al. Fibers and Polymers 2001, 2, 64-70).
fporous chitosan sponge processed by lyophilization (Kim, S et al. Fibers and Polymers 2001, 2, 64-70).
gporous sponge made of crosslinked collagen/chitosan, processed by lyophilization (Kim, S et al. Fibers and Polymers 2001, 2, 64-70).
Materials
Bovine serum, RPMI 1640 medium, Dulbecco's Modified Eagle Medium, basic fibroblast growth factor (bFGF), transforming growth factor-β1 (TGF-β1), Pen-Strep, Fungizone, non essential amino acids, trypsin were from Gibco (Carlsbad, Calif.). Ascorbic acid phosphate, Histopaque-1077, insulin, and dexamethasone were from Sigma (St. Lois, Mo.). Collagen scaffolds (Ultrafoam) were from Davol (Cranston, R.I.). All other substances were of analytical or pharmaceutical grade and obtained from Sigma. Silkworm cocoons were kindly supplied by M. Tsukada, Institute of Sericulture, Tsukuba, Japan, and Marion Goldsmith, University of Rhode Island).
Scaffold Preparation and Decoration
Cocoons from Bombyx Mori were boiled for 1 hour in an aqueous solution of 0.02M Na2CO3, and rinsed with water to extract sericins. Purified silk was solubilized in 9M LiBr solution and dialyzed (Pierce, MWCO 2000 g/mol) against PBS for 1 day and again against 0.1M MES, 0.5 M NaCl, pH 6 buffer for another day. An aliquot of the silk solution was coupled with GRGDS peptide to obtain RGD-silk. For coupling COOH groups on the silk were activated by reaction with 1-ethyl-3-(dimethylaminopropyl)carbodiimide hydrochloride (EDC)/N-hydroxysuccinimide (NHS) solution for 15 minutes at room temperature (Sofia et al. 2001. J Biomed Mater Res 54:139-148). To quench the EDC, 70 μl/ml β-mercaptoethanol was added. Then 0.5 g/l peptide was added and left for 2 hours at room temperature. The reaction was stopped with 10 mM hydroxylamine. Silk solutions were dialyzed against 0.1 M 2-(N-morpholino)-ethanesulfonic acid buffer, pH 4.5-5 for 1 day. Silk and Silk-RGD solutions were lyophilized and redissolved in hexafluoro-2-propanol (HFIP) to obtain a 17% (w/v) solution. Granular NaCl was weighed in a Teflon container and silk/HFIP solution was added at a ratio of 20:1 (NaCl/silk). HFIP was allowed to evaporate for 2 days and NaCl/silk blocks were immersed in 90% (v/v) methanol for 30 minutes to induce a protein conformational transition to β-sheet (Nazarov et al. 2003. In Department of Biomedical Engineering. Medford: Tufts University). Blocks were removed, dried and NaCl was extracted in water for 2 days. Disk shaped scaffolds (5 mm diameter, 2 mm thick) were prepared using a dermal punch (Miltey, Lake Success, N.Y.), and autoclaved.
For cross-linking, collagen scaffolds were incubated in 0.1M MES, 0.5 M NaCl, pH=6 buffer for 30 min and subsequently crosslinked with 1.713 g EDC and 0.415 g NHS in 100 ml 0.1M MES, 0.5 M NaCl, pH=6 buffer per gram of collagen (van Wachem et al. 2001. J Biomed Mater Res 55:368-378). The reaction was allowed to proceed for 4 hrs under gentle shaking and was stopped by washing for 2 hrs with 0.1 M Na2HPO4. The films were rinsed 4 times for 30 min with water. The whole procedure was carried out aseptically.
Human Bone Marrow Stromal Cell Isolation and Expansion.
Total bone marrow (25 cm3, Clonetics, Santa Rosa, Calif.) was diluted in 100 ml of isolation medium (5% FBS in RPMI 1640 medium). Cells were separated by density gradient centrifugation. Briefly, 20 ml aliquots of bone marrow suspension were overlaid onto a poly-sucrose gradient (8=1,077 g/cm3, Histopaque, Sigma, St. Louis, Mo.) and centrifuged at 800×g for 30 min at room temperature. The cell layer was carefully removed, washed in 10 ml isolation medium, pelleted and contaminating red blood cells were lysed in 5 ml of Pure-Gene Lysis solution. Cells were pelleted and suspended in expansion medium (DMEM, 10% FBS, 1 ng/ml bFGF) and seeded in 75 cm2 flasks at a density of 5×104 cells/cm2. The adherent cells were allowed to reach approximately 80% confluence (12-17 days for the first passage). Cells were trypsinized, replated and passage 2 (P2) cells (80% confluence after 6-8 days), were used for the experiments.
Tissue Culture
Passage 2 mesenchymal stem cells (7×105 cells) were suspended in 40 μl DMEM and the suspension was used to seed scaffolds, which were prewetted overnight in DMEM. Seeded constructs were placed in 6-well Petri dishes and incubated at 37° C. for 2 hours to allow cell attachment. To maintain moisture 30 μl DMEM was added to the scaffolds every 30 minutes. Subsequently, 5 ml of chondrogenic or control medium was added per well. Control medium was DMEM, supplemented with 10% fetal bovine serum and Pen-Strep. Chondrogenic medium included the control medium was further supplemented with 0.1 mM nonessential amino acids, 50 μg/ml ascorbic acid-2-phosphate, 10 nm dexamethasone, 5 μg/ml insulin, 5 ng/ml TGF-β1. Medium was exchanged every 2-3 days and constructs were harvested after 2 and 4 weeks.
Biochemical Analysis and Histology
Constructs were cultured for 6 hours (0 weeks), 1, 2, and 4 weeks in control or chondrogenic medium and processed for biochemical analysis and histology. For DNA analysis, 3-4 constructs per group and time point were disintegrated after 6 hours (0 weeks), 1, 2 and 4 weeks in culture using steel balls and a Microbeater. DNA content (n=3-4) was measured using the PicoGreen assay (Molecular Probes, Eugene, Oreg.), according to the protocol of the manufacturer. Samples were measured fluorometrically at an excitation wavelength of 480 nm and an emission wavelength of 528 nm. For the MTT assay 3-4 constructs were transferred to 2 ml plastic tubes, and 1.5 ml serum free DMEM was added to each well supplemented with MTT (0.5 g/l) and incubated in the dark at 37° C., 5% CO2 for 2 hours. Tubes were centrifuged for 10 minutes at 2000 g and the supernatant was aspirated. Isopropyl alcohol (1.5 ml) was added and constructs were disintegrated using steel balls and a Microbeater. Tubes were centrifuged at 2000 g for 10 minutes and absorption was measured at 570 nm. Sulphated glycosaminoglycan (GAG) deposition (n=5), was assessed as previously described (Martin et al. 1999. Ann Biomed Eng 27:656-662). Briefly, constructs were frozen, lyophilized for 3 days, weighed, and digested for 16 hours at 60° C. with proteinase-K. GAG content was determined colorimetrically by dimethylmethylene blue dye binding and measured spectrophotometrically at 525 nm (Farndale et al. 1986. Biochim Biophys Acta 883:173-177).
RNA Isolation, Real-Time-Reverse Transcription Polymerase Chain Reaction (Real Time RT-PCR)
Fresh constructs (n=3-4 per group) were transferred into 2 ml plastic tubes and 1.5 ml Trizol was added. Constructs were disintegrated using steel balls and a Microbeater. Tubes were centrifuged at 12000 g for 10 minutes and the supernatant was transferred to a new tube. Chloroform (200 μl) was added to the solution and incubated for 5 minutes at room temperature. Tubes were again centrifuged at 12000 g for 15 minutes and the upper aqueous phase was transferred to a new tube. One volume of 70% ethanol (v/v) was added and applied to an RNeasy mini spin column (Quiagen, Hilden, Germany). The RNA was washed and eluted according to the manufacturer's protocol. The RNA samples were reverse transcribed in cDNA using oligo (dT)-selection according to the manufacturer's protocol (Superscript Preamplification System, Life Technologies, Gaithersburg, Md.). Collagen type 2, MMP1, and MMP2 gene expression was quantified using the ABI Prism 7000 Real Time PCR system (Applied Biosystems, Foster City, Calif.). PCR reaction conditions were 2 min at 50° C., 10 min at 95° C., and then 50 cycles at 95° C. for 15 s, and 1 min at 60° C. The expression data were normalized to the expression of the housekeeping gene, glyceraldehyde-3-phosphate-dehydrogenase (GAPDH). Probes were labeled at the 5′ end with fluorescent dye FAM (VIC for GAPDH) and with the quencher dye TAMRA at the 3′ end. Primer sequences for the human collagen type 2 gene were: Forward primer 5′-GGC AAT AGC AGG TTC ACG TAC A-3′ (SEQ ID NO:1), reverse primer 5′-CGA TAA CAG TCT TGC CCC ACT T-3′ (SEQ ID NO:2), probe 5′-CCG GTA TGT TTC GTG CAG CCA TCC T-3′ (SEQ ID NO:3). Primer sequences for the human GAPDH gene were: Forward primer 5′-ATG GGG AAG GTG AAG GTC G-3′ (SEQ ID NO:4), reverse primer 5′-TAA AAG CCC TGG TGA CC-3′ (SEQ ID NO:5), probe 5′-CGC CCA ATA CGA CCA AAT CCG TTG AC-3′ (SEQ ID NO:6). Primers and probes for MMP1 and MMP2 were purchased from Applied Biosciences (Assay on Demand # Hs00233958 ml (MMP1), Hs 00234422 ml (MMP2))
Histology, Immunohistochemistry and Scanning Electron Microscopy
For histology, constructs were dehydrated, embedded in paraffin and cut in 5 μm sections were. To stain for cartilage tissue, sections were treated with eosin for 1 min, fast green for 5 min, and 0.2% aqueous safranin O solution for 5 min, rinsed with distilled water, dehydrated through xylene, mounted, and placed under a coverslip (Rosenberg, L. 1971. J Bone Joint Surg Am 53:69-82).
For immunohistochemistry using a monoclonal antibody against type 2 collagen (2B1.5, dilution 1:100, Neomarkers, Fremont, Calif.), paraffin embedded sections of tissue exposed to films were deparrafinized through a series of graded alcohols, treated with protease 2 for 16 min. The primary antibody was added to each slide and incubated for 32 minutes at room temperature in a humidified chamber. The secondary antibody was applied, carrying horse-raddish peroxidase and developed according to the manufacturer's protocol (BenchMark IHC staining module, Ventana, Tucson, Ariz.). Sections were counterstained using hematoxylin for 2 minutes.
For SEM, constructs were cut and exposed to Karnovsky's fixative (2% paraformaldehye, 2% glutaraldehyde in 0.1M phosphate Buffer). After initial fixation, constructs were again fixed with 1% osmium tetroxide in 0.1M phosphate buffer for 1 hour. After rinsing with PBS for 15 min the constructs were dehydrated using a series of graded ethyl alcohols and dried. Constructs were coated with a thin layer of gold prior to evaluation.
Statistical Analysis
Statistical analysis of data was performed by one-way analysis of variance (ANOVA) and Tukey-Kramer procedure for post hoc comparison. p values less than 0.05 were considered statistically significant.
Proliferation of Human Bone Marrow Stromal Cells on Silk, Silk-RGD, and Collagen Scaffolds
The proliferation of BMSCs on silk 3D matrices, silk matrices decorated with the cell adhesion peptide RGD, and collagen control matrices was assessed over 4 weeks (
A total of 7×105 cells were seeded on each of the matrices, as determined by DNA assay and cell counts. About 4-5×105 cells were found on the matrices 6 hours after seeding (week 0). Cell number dropped approximately 30% for BMSCs cultured on all substrates between week 0 and week 1 (
The MTT assay was used to determine cell viability (
BMSC proliferation resulted in a formation of cell sheets on the surfaces of all scaffolds after 4 weeks in culture (
BMSCs attached to the silk scaffolds via cellular extensions (
Chondrogenesis
The deposition of sulphated glycosaminoglycans (GAG) on collagen, silk, and silk-RGD matrices after 2 and 4 weeks in culture were assessed (
Expression of interstitial collagenase (MMP1) and gelatinase A (MMP2) on collagen and silk scaffolds cultured in chondrogenic medium were assessed and normalized relative to the expression of the respective constructs cultured in control medium. Neither MMP 1 nor MMP2 expression was significantly increased or decreased in chondrogenic medium as compared to control medium.
The hallmark of human cartilage differentiation is the expression of type II collagen. Gene expression of collagen type II by the cells cultured on collagen, silk, and silk-RGD matrices in chondrogenic or control medium was determined after 2 and 4 weeks (
In the presence of chondrogenic medium, round or angular shaped cells resided in cavities or lacunae (
This work demonstrates that relatively large (500-700 μm) and connected pieces of human cartilage can be generated in vitro by culturing bone marrow stromal cells on highly porous and structurally stable silk scaffolds. This is in contrast to the collagen scaffold used in this study, where degradation was observed and the collapsing matrix prevented a similar outcome. At least two scenarios could account to these observations: (i) the production of matrix metalloproteinases (MMP), leading to enzymatic degradation of the newly deposited cartilage components or (ii) the rapid degradation of the collagen matrix. Diseases such as rheumatoid arthritis, are associated with chondrocytes synthesizing MMPs which collectively degrade all components of cartilage (Cawston et al. 1999. Ann NY Acad Sci 878:120-129). In particular, the collagenolytic enzyme, e.g. interstitial collagenase also known as MMP1, has been strongly implicated in cartilage destruction (Shlopov et al. 1997. Arthritis Rheum 40:2065-2074). Our preliminary results suggest that the observed GAG depletion on collagen matrices was not associated with increased MMP1 or MMP2 transcript levels and no over-expression of either enzyme was observed on a RNA level.
The collagen scaffold used in this study was stabilized by physical methods, but its durability could be extended for example by using chemical agents that cross-link the collagen (Carpentier et al. 1969. J Thorac Cardiovasc Surg 58:467-483). To understand the significance of biodegradation on the decline in GAG content on collagen scaffolds after 4 versus 2 weeks, cross linked (CL) collagen scaffolds were prepared, in which biodegradation was reduced. GAG content on CL-collagen was similar as compared to the silks after 4 weeks and much higher than on the untreated collagen (
Human BMSCs were cultivated on highly porous silk scaffolds to facilitate cell seeding and medium exchange. Approximately 60% of the administered BMSCs were seeded onto the matrices (
After 4 weeks significantly more cells were present on silk and silk-RGD scaffolds than on collagen scaffolds determined by DNA content (
Some studies have been performed to study the differentiation of human BMSCs on three-dimensional scaffolds to engineer cartilage has been reported (for a review see (Hunziker, E. B. 2002. Osteoarthritis Cartilage 10:432-463). Two of these studies used poly-L-lactic acid (PLA) or poly(lactic-co-glycolic acid) matrices (Caterson et al. 2001. J Biomed Mater Res 57:394-403; Martin et al. 2001. J Biomed Mater Res 55:229-235). Although these polymers have been widely used in studies with biomaterials, they are known to elicit inflammatory responses mainly due to the release of acidic hydrolysis products (Athanasiou et al. 1996. Biomaterials 17:93-102). Recently, we have demonstrated in vitro and in vivo that the inflammatory response elicited by silk, silk-RGD and collagen is lower than due to PLA films (Meinel et al., 2003). GAG deposition/mg scaffold was approximately an order of magnitude less for all biomaterials used in this study than described for PLA scaffolds (Martin et al. 2001. J Biomed Mater Res 55:229-235). The study describing chondrogenesis on PLA scaffolds (Martin et al. 2001. J Biomed Mater Res 55:229-235) used bovine instead of human BMSCs and twice as much TGF-β1 than used in this study. However deposition of GAG/DNA was similar compared to the PLA study suggesting that the induction of chondrogensis/cell was similar in human and bovine cells. The wet weight for the PLA scaffolds was less than for the silk scaffolds and this could contribute to the higher GAG/mg wet (Martin et al. 2001. J Biomed Mater Res 55:229-235).
Stained areas for GAG were larger on silk and silk-RGD scaffolds likely due to the mechanical stability of the silks. Decoration of silk scaffolds with RGD adhesion sequences resulted in increased levels of DNA (
This study demonstrates by histological evaluation and biochemical and gene expression analysis that chondrogenesis of bone marrow stromal cells can be induced on both collagen and silk scaffolds. However, the biomechanical properties of collagen were insufficient for cartilage tissue engineering, leading to distributed and unconnected patches within the 3D matrices due to premature degradation and collapse. In contrast, connected cartilage-like tissue was formed in and on silk and silk-RGD matrices. When these results are considered in connection with the unique mechanical properties of silk, the induction of cartilage formation on silk-based materials offers new opportunities for bioengineering of cartilage-like tissue in vitro and the treatment of cartilage defects in vivo.
Materials
Bovine serum, RPMI 1640 medium, Dulbecco's Modified Eagle Medium (DMEM), basic fibroblast growth factor (bFGF), transforming growth factor-β1 (TGF-β1) (R&D Systems, Minneapolis, Minn.), Pen-Strep, Fungizone, non essential amino acids, trypsin were from Gibco (Carlsbad, Calif.). Ascorbic acid phosphate, Histopaque-1077, insulin, dexamethasone, β-glycerolphosphate were from Sigma (St. Lois, Mo.). Collagen scaffolds (Ultrafoam) were from Davol (Cranston, R.I.). All other substances were of analytical or pharmaceutical grade and obtained from Sigma. Silkworm cocoons were kindly supplied by M. Tsukada (Institute of Sericulture, Tsukuba, Japan) and Marion Goldsmith (University of Rhode Island, Cranston, R1).
Scaffold Preparation and Decoration
Cocoons from Bombyx Mori (Linne, 1758) were boiled for 1 hour in an aqueous solution of 0.02M Na2CO3, and rinsed with water to extract sericins. Purified silk was solubilized in 9M LiBr solution and dialyzed (Pierce, Woburn, Mass.; MWCO 3500 g/mol) against water for 1 day and again against 0.1M MES (Pierce), 0.5 M NaCl, pH 6 buffer for another day. An aliquot of the silk solution was coupled with glycine-arginine-alanine-aspartate-serine (GRGDS) peptide to obtain RGD-silk. For coupling COOH groups on the silk were activated by reaction with 1-ethyl-3-(dimethylaminopropyl)carbodiimide hydrochloride (EDC)/N-hydroxysuccinimide (NHS) solution for 15 minutes at room temperature (Sofia et al. 2001. J Biomed Mater Res 54:139-148). To quench the EDC, 70 μl/ml β-mercaptoethanol was added. Then 0.5 g/l peptide was added and left for 2 hours at room temperature. The reaction was stopped with 10 mM hydroxylamine. Silk solutions were dialyzed against water for 2 days. Silk and Silk-RGD solutions were lyophilized and redissolved in hexafluoro-2-propanol (HFIP) to obtain a 17% (w/v) solution. Granular NaCl was weighed in a Teflon container and silk/HFIP solution was added at a ratio of 20:1 (NaCl/silk). HFIP was allowed to evaporate for 2 days and NaCl/silk blocks were immersed in 90% (v/v) methanol for 30 minutes to induce a protein conformational transition to β-sheets (Nazarov et al. 2003. In Department of Biomedical Engineering. Medford: Tufts University). Blocks were removed, dried and NaCl was extracted out in water for 2 days. Disk shaped scaffolds (5 mm diameter, 2 mm thick) were prepared using a dermal punch (Miltey, Lake Success, N.Y.), and autoclaved.
For cross-linking, collagen scaffolds were incubated in 0.1M MES, 0.5 M NaCl, pH=6 buffer for 30 min and subsequently crosslinked with 1.713 g EDC and 0.415 g NHS in 100 ml 0.1M MES, 0.5 M NaCl, pH=6 buffer per gram of collagen (van Wachem et al. 2001. J Biomed Mater Res 55:368-378). The reaction was allowed to proceed for 4 hrs under gentle shaking and was stopped by washing for 2 hrs with 0.1 M Na2HPO4. The films were rinsed 4 times for 30 min with water. The whole procedure was carried out aseptically.
Iodiniation of GRYDS peptide
To assess the amount of bound RGD to the scaffolds, GRYDS peptide was iodinated with non radioactive iodine to quantify the amount of bound peptide in the silk film surface by X-ray photoelectron spectrometer (XPS). The procedure involved first flusing of Sep-Pak C18 reverse phase cartridge (Waters) with 10 ml of a 80:20 mix of methanol:water and then flushing with 10 ml of 0.1M PBS 0.5 NaCl pH=6 buffer, as previously described (Sofia et al. 2001. J Biomed Mater Res 54:139-148). Three IODO-BEADS (Pierce) were rinsed once with 1 ml of PBS buffer. Eighty ml of PBS and then 10 μl of 3.75 g/L NaI in PBS were added and the activation was allowed for 5 minutes. Then, 1 ml of 0.1 g/l GRYDS peptide in PBS was added and the reaction was allowed for 15 min. Beads were rinsed with PBS and the peptide solution was injected into the C18 column followed by elution with 0, 20, 40, and 60% methanol in water solutions. Fractions were collected and analyzed at 280 nm. The iodination procedure was repeated with the same peptide through lyophilization of the desired fractions and resolubilizing in buffer to achieve the desired extent of iodination (1 atom of iodine per molecule of GRYDS). Iodinated peptide was coupled to silk matrices as described above for GRGDS.
Human Bone Marrow Stromal Cell Isolation and Expansion
Total bone marrow (25 cm3, Clonetics, Santa Rosa, Calif.) was diluted in 100 ml of isolation medium (5% FBS in RPMI 1640 medium). Cells were separated by density gradient centrifugation. Briefly, 20 ml aliquots of bone marrow suspension were overlaid onto a poly-sucrose gradient (δ=1,077 g/cm3, Histopaque, Sigma, St. Louis, Mo.) and centrifuged at 800×g for 30 min at room temperature. The cell layer was carefully removed, washed in 10 ml isolation medium, pelleted and contaminating red blood cells were lysed in 5 ml of Pure-Gene Lysis solution. Cells were pelleted and suspended in expansion medium (DMEM, 10% FBS, 1 ng/ml bFGF) and seeded in 75 cm2 flasks at a density of 5×104 cells/cm2. The adherent cells were allowed to reach approximately 80% confluence (12-17 days for the first passage). Cells were trypsinized, replated and passage 2 (P2) cells (80% confluence after 6-8 days), were used for the experiments.
Pellet Culture
For pellet culture, 2×105 cells were centrifuged at 300 g for 10 min at 4° C. The medium was aspirated and replaced with osteogenic, chondrogenic, or control medium. Control medium was DMEM supplemented with 10% FBS, Pen-Strep and Fungizone, chondrogenic medium was control medium supplemented with 0.1 mM nonessential amino acids, 50 μg/ml ascorbic acid-2-phosphate, 10 nm dexamethasone, 5 μg/ml insulin, 5 ng/ml TGF β1 and osteogenic medium was control medium supplemented with 50 μg/ml ascorbic acid-2-phosphate, 10 nm dexamethasone, 7 mM β-glycerolphosphate, and 1 μg/ml BMP-2.
Tissue Culture
For cultivation on scaffolds, P2 BMSC (7×105 cells) were suspended in liquid Matrigel® (10 μl) on ice, and the suspension was seeded onto prewetted (DMEM, overnight) scaffolds. Seeded constructs, placed in dishes were placed in an incubator at 37° C. for 15 minutes to allow gel hardening and osteogenic or control medium was added. Half of the medium was replaced every 2-3 days. Control medium was DMEM supplemented with 10% FBS, Pen-Strep and Fungizone, and osteogenic medium was control medium supplemented with 50 μg/ml ascorbic acid-2-phosphate, 10 nm dexamethasone, 7 mM β-glycerolphosphate, and 1 μg/ml BMP-2.
Biochemical Analysis and Histology
Scaffolds were cultured for 2 and 4 weeks in control or osteogenic medium and processed for biochemical analysis and histology. For DNA analysis, 3-4 scaffolds per group and time point were disintegrated using steel balls and a Microbeater. DNA content (n=3-4) was measured using the PicoGreen assay (Molecular Probes, Eugene, Oreg.), according to the protocol of the manufacturer. Samples were measured fluorometrically at an excitation wavelength of 480 nm and an emission wavelength of 528 nm. Sulphated glycosaminoglycan (GAG) deposition for pellet culture (n=5), was assessed as previously described (Martin et al., 1999 Ann Biomed Eng 27:656-662). Briefly, pellets were frozen, lyophilized for 3 days, weighed, and digested for 16 hours at 60° C. with proteinase-K. GAG content was determined colorimetrically by dimethylmethylene blue dye binding and measured spectrophotometrically at 525 nm (Farndale et al. Biochim Biophys Acta 883:173-177). For total calcium content, samples (n=4) were extracted twice with 0.5 ml 5% trichloroacetic acid. Calcium content was determined by a colorimetric assay using o-cresolphthalein complexone (Sigma, St. Louis, Mo.). The calcium complex was measured spectrophotometrically at 575 nm. Alkaline phosphatase activity was measured using a biochemical assay from Sigma (St. Louis, Mo.), based on conversion of p-nitrophenyl phosphate to p-nitrophenol which was measured spectrophotometrically at 410 nm.
RNA Isolation, Real-Time-Reverse Transcription Polymerase Chain Reaction (Real Time RT-PCR)
Fresh scaffolds (n=3-4 per group) were transferred into 2 ml plastic tubes and 1.5 ml Trizol was added. Scaffolds were disintegrated using steel balls and a Microbeater. Tubes were centrifuged at 12000 g for 10 minutes and the supernatant was transferred to a new tube. Chloroform (200 μl) was added to the solution and incubated for 5 minutes at room temperature. Tubes were again centrifuged at 12000 g for 15 minutes and the upper aqueous phase was transferred to a new tube. One volume of 70% ethanol (v/v) was added and applied to an RNeasy mini spin column (Quiagen, Hilden, Germany). The RNA was washed and eluted according to the manufacturer's protocol. The RNA samples were reverse transcribed into cDNA using oligo (dT)-selection according to the manufacturer's protocol (Superscript Preamplification System, Life Technologies, Gaithersburg, Md.). Osteopontin, bone sialoprotein, and bone morphogenic protein 2 gene expression were quantified using the ABI Prism 7000 Real Time PCR system (Applied Biosystems, Foster City, Calif.). PCR reaction conditions were 2 min at 50° C., 10 min at 95° C., and then 50 cycles at 95° C. for 15 s, and 1 min at 60° C. The expression data were normalized to the expression of the housekeeping gene, glyceraldehyde-3-phosphate-dehydrogenase (GAPDH). The GAPDH probe was labelled at the 5′ end with fluorescent dye VIC and with the quencher dye TAMRA at the 3′ end. Primer sequences for the human GAPDH gene were: Forward primer 5′-ATG GGG AAG GTG AAG GTC G-3′ (SEQ ID NO: 4), reverse primer 5′-TAA AAG CCC TGG TGA CC-3′ (SEQ ID NO: 5), probe 5′-CGC CCA ATA CGA CCA AAT CCG TTG AC-3′ (SEQ ID NO: 6). Primers and probes for osteopontin, bone sialoprotein (BSP), and bone morphogenic protein 2 (BMP-2) were purchased from Applied Biosciences (Assay on Demand # Hs00167093 ml (osteopontin), Hs 00173720 ml (BSP), Hs 00214079 ml (BMP-2)).
Histology and Microcomputrized Tomography (μ-CT)
For histology, scaffolds were dehydrated, embedded in paraffin and cut in 5 μm sections were. To stain for cartilage differentiation in the pellet culture (
For the visualization of bone distribution, scaffolds were analyzed using a μCT20 imaging system (Scanco Medical, Bassersdorf, Switzerland) providing a resolution of 34 μm in the face and 250 μm in the cross direction of the scaffold. A constrained Gaussian filter was used to suppress noise. Mineralized tissue was segmented from non-mineralized tissue using a global thresholding procedure. All samples were analyzed using the same filter width (0.7), filter support (Lysaght et al. 1998. Tissue Eng 4:231-238), and threshold (195/190) as previously described (Muller et al. 1994 Phys Med Biol 39:145-164).
X-Ray Diffraction Measurement (XRD)
X-ray diffraction patterns of scaffolds before and after bone formation were obtained by means of Bruker D8 Discover X-ray diffractometer with GADDS multiwire area detector. WAXD (wide angle X-ray dirrfaction) experiments were performed employing CuKa radiation (40 kV and 20 mA) and 0.5 mm collimator. The distance between the detector and the sample was 47 mm.
Statistical Analysis
Statistical analysis of data was performed by one-way analysis of variance (ANOVA) and Tukey-Kramer procedure for post hoc comparison using SigmaStat 3.0 for Windows. p values less than 0.05 were considered statistically significant.
Characterization of Human Bone Marrow Stem Cells
The BMSCs exhibited a spindle shaped and fibroblast-like morphology (
Scaffolds, Biochemical Analysis and Real Time RT-PCR
The porosity of the 3D silk matrices was 98%, compressive stress was 170±20 kPa and compressive modulus 450±170 kPa (Nazarov et al. 2003. In Department of Biomedical Engineering. Medford: Tufts University).
Calcium deposition was analyzed after 2 and 4 weeks in culture (
Alkaline phosphatase (AP) activity was variable among the groups as indicated by large standard deviations and statistically not significant differences (
Gene expression of bone sialoprotein (BSP) was upregulated 2000 fold on the collagen scaffolds cultured in osteogenic medium for 2 weeks when compared to the expression by BMSCs prior to seeding (represented by the baseline). When compared to 4 weeks on collagen scaffolds, significantly more BSP transcript was found on collagen after 2 weeks than after 4 weeks in osteogenic medium (p<0.05) (
Osteopontin was over-expressed on all scaffolds cultured in osteogenic medium and was similar after 2 and 4 weeks in culture, except for silk, where transcript levels increased, however this observation was not statistically significant (
Bone morphogenetic protein 2 (BMP-2) expression was 100-150 fold upregulated after 2 weeks on all scaffolds cultured in osteogenic medium compared to the BMSCs prior to seeding (
Histogenesis of Bone-Like Tissue
After 2 weeks, mineralized spots were observed on the collagen lattice as seen with von Kossa staining. Degradation of the collagen scaffold was advanced and the matrix did not provide a stable lattice. Open areas of the lattice were filled with randomly oriented collagen-like bundles as seen in H&E staining intermingled with fibroblasts. Restricted to certain locations, enlarged cuboidal cells with an osteoblast-like morphology were observed. After 4 weeks, calcification on silk scaffolds was advanced and found adjacent to the scaffold material. Mineralization occurred in locations which coalesced and formed clusters of mineralized matrix (
Mineralization on silk was appositional to the scaffold lattice and occurred in distinct spots (
On silk-RGD matrices, mineralization occurred in a mode similar to the silk matrix, appositional to the scaffold lattice. After 2 weeks in osteogenic medium, the void scaffold area was completely filled with connective tissue, comprised of randomly oriented collagen-like fibres, fibroblasts and cuboidal osteoblast-like cells which were connected via cellular processes. After 4 weeks, mineralization was especially advanced on the silk-RGD scaffolds compared to silk and collagen. Aside from the small areas that do not stain, a calcified matrix covered the entire silk-RGD lattice. The void area between the lattices was completely filled with extracellular matrix, consisting of parallel oriented collagen bundles, osteoblast like cells, and few cells with fibroblast like morphology. The cells seemed to be interconnected via long processes.
Bone deposition was imaged after 4 weeks in osteogenic medium with micro-computerized tomography (μ-CT) of randomly selected collagen and silk-RGD scaffolds (
In recent years substantial progress has been achieved in the tissue engineering of human autologous bone grafts (Petite et al. 2000. Nat Biotechnol 18:959-963; Athanasiou et al. 2000. Tissue Eng 6:361-381; Kale et al. 2000. Nat Biotechnol 18:954-958; Niklason, L. E. 2000. Nat Biotechnol 18:929-930; Schoeters et al. 1992. Cell Prolif 25:587-603). To evaluate the potential of silk as a scaffold for bone tissue engineering mesenchymal stem cells (BMSC) derived from human bone marrow were cultured in three different 3D porous scaffolds (silk, silk-RGD, and collagen) to study osteogenesis under controlled in vitro conditions. BMSCs cultured on the protein scaffolds for up to four weeks formed mineralized bone matrix, and the amount, density, and structure of bone matrix depended on scaffold degradation and scaffold decoration with RGD.
Human mesenchymal stem cells are a source for autologous bone tissue engineering. They proliferate and differentiate in vitro, can be easily isolated from bone marrow aspirates, and have a documented potential for osteogenic and chondrogenic differentiation (Friedenstein, A. J. 1976. Int Rev Cytol 47:327-359; Friedenstein et al. 1987. Cell Tissue Kinet 20:263-272; Caplan, A. I. 1994. Clin Plast Surg 21:429-435; Pittenger et al. 1999. Science 284:143-147). The osteogenic pathway has been proposed to be the default lineage of this population of cells (Banfi et al. 2002. Tissue Eng 8:901-910). The isolated and expanded BMSCs were positive for the putative BMSC marker CD105/endoglin (Barry et al. 1999. Biochem Biophys Res Commun 265:134-139), and had a capacity for selective differentiation into either cartilage- or bone-forming cells (
Scaffold chemistry and surface modification had a significant impact on mineralization of the matrices. Total calcium deposition per scaffold was advanced on collagen scaffolds, but declined after 4 weeks. This effect was correlated with the biodegradation of the collagen scaffold (Meinel et al. 2003. Ann Biomed Eng accepted). Ideally, a scaffold would provide a suitable mechanical match until gradually replaced by the newly deposited bone. Bone deposition was already present after 2 weeks in culture (
The introduction of RGD moieties by covalent decoration of the silk surfaces resulted in significantly increased calcium deposition in comparison to non decorated silk or the collagen (
To characterize the nature of the mineralized tissue, XRD patterns of engineered bone like tissue were compared to poorly crystalline hydroxyapatite (p.c. HA). From early diffraction measurements it was concluded, that bone mineral is a two phase system, one of which was p.c. HA and the other an amorphous calcium phosphate which makes up less than 10% of the mineralized bone (Betts et al. 1975. Proc Natl Acad Sci USA 72:2088-2090). However, more recent studies could not detect amorphous calcium phosphate even in embryonic bone (Bonar et al. 1984. J Ultrastruct Res 86:93-99; Grynpas, M. D., et al. 1984. Calcif Tissue Int 36:291-301). The similarity in XRD patterns between p.c. HA and the engineered tissue suggested the bone like nature of the deposited interconnected trabeculae.
Substantial differences in the organization of the extracellular matrix were observed on the silks between 2 and 4 weeks in osteogenic medium. After 4 weeks dense connective tissue filled the voids of the silk and silk-RGD lattice in which cuboidal osteoblast like cells were in contact with one another via long tapering processes. The intercellular space was occupied with organized bundles of collagens. This was accompanied by strong induction of gene expression for a non-collagenous element of the extracellular matrix, bone sialoprotein (BSP) (
In summary, tissue engineered organized and trabecular bone-like morphologies were obtained by using BMSCs cultured in osteogenic medium on 3D silk scaffolds. This was accompanied by the production of an organized extracellular matrix. The decoration of silk scaffolds with RGD sequences resulted in increased calcification and a more structured extracellular matrix. Collagen scaffolds could not generate similar outcomes due to the rapid rate of degradation. Large tissue engineered bone with an organized geometry on natural non cross linked polymers can be engineered by cultivation of BMSCs seeded on silk-RGD scaffolds in conjunction with bioreactors.
Tissue engineered bone was produced on silk material scaffolds that were prepared as described herein. Several scaffolds were prepared with mean pore sizes of 106 microns, 225 microns, and 425 microns.
Scaffolds were seeded with 5×106 human mesenchymal stem cells and cultured in osteogenic medium as described in Example III for up to 5 weeks in a spinner flask. Use of the spinner flask created a turbulent flow of medium around the scaffolds. Bone growth was monitored by μ-computed tomography, the results of which are shown in
All references cited herein and throughout the specification are herein incorporated by reference in their entirety.
This application is a continuation Application of U.S. non-provisional patent application Ser. No. 10/541,182 filed 14 Jun. 2006, now U.S. Pat. No. 7,842,780 B2, which is a U.S. §371 National entry of International Application number PCT/US04/00255 filed Jan. 7, 2004, which claims the benefit of priority under 35 U.S.C. §119 (e) of U.S. Provisional Application No. 60/438,393 filed Jan. 7, 2003.
This invention was made with United States Government support under Grant No. 1R01 DE13405-01A1 awarded by the National Institutes of Health, and Grant No. DMR-0090384 awarded by the National Science Foundation. The United States Government has certain rights in the invention. The instant application contains a Sequence Listing which has been submitted in ASCII format via EFS-Web and is hereby incorporated by reference in its entirety. Said ASCII copy, created on Jul. 12, 2010, is named 20100715.txt and is 2,254 bytes in size.
| Number | Name | Date | Kind |
|---|---|---|---|
| 5171505 | Lock | Dec 1992 | A |
| 5252285 | Lock | Oct 1993 | A |
| 5736188 | Alcock et al. | Apr 1998 | A |
| 6110590 | Zarkoob et al. | Aug 2000 | A |
| 20040005363 | Tsukada et al. | Jan 2004 | A1 |
| 20040224406 | Altman et al. | Nov 2004 | A1 |
| Number | Date | Country |
|---|---|---|
| 0154667 | Aug 2001 | WO |
| 0180921 | Nov 2001 | WO |
| Entry |
|---|
| Anthanasiou et al., Biomaterials, 17:93-102 (1996). “Sterilization, toxicity, biocompatibility and clinical applications of polylactic acid/polyglocolic acid copolymers.” |
| Asakura, T., Bioindusty, 4(11):36-44 (1987), Translated pp. 1-24. Translated title: “Structural characteristics of silk fibroin and its application to enzyme fixation material.” |
| Bognitzki et al., Adv Mater, 13(1):70-72 (2001). “Nanostructured fibers via electrospinning.” |
| Boland et al., Polymeric Materials: Science & Engineering, 85:51-52 (2001). “Electrospinning of tissue engineering scaffolds.” |
| Caterson et al., Biomed Mater Res, 57:394-403 (2001). “Three-dimensional cartilage formulation by bone marrow-derived cells seeded in polylactide/alginate amalgam.” |
| Dal Pra et al., Tissue Engineering, 9(6):1113-1121 (2003). “Silk fibron-coated three-dimensional polyurethane scaffolds for tissue engineering: interactions with normal human fibroblasts.” |
| Demura et al., Biosensors, 361-372 (1989). “Immobilization of biocatalysts with Bombyx mori silk fibroin by several kinds of physical treatment and its application to glucose sensors.” |
| Doshi et al., Journal of Electrostatics, 35:151-160 (1995). “Electronspinning process and applications of electrospun fibers.” |
| Elcin et al., Artificial Cells Blood Substitutes and Immobilization Biotechnology, 24(3):257-71 (1996). “Controlled release of endothelial cell growth factor from chitosan-albumin microspheres for localized angiogenesis: in vitro and in vivo studies.” |
| Holy et al., J Biomed Mater Res, 65A:447-453 (2003). “Use of a biomimetic strategy to engineer bone.” |
| Hutmacher, Biomaterials, 21:2529-2543 (2000). “Scaffolds in tissue engineering bone and cartilage.” |
| Jin et al., Polymer Preprints (American Chemical Society, Division of Polymer Chemistry) 43(2):743-744 (2002). “Electrospinning Bombyx moral silk with poly(ethylene oxide).” |
| Karp et al., The Journal of Craniofacial Surgery, 14(3):317-323 (2003). “Fabrication of precise cylindrical three-dimensional tissue engineering scaffolds for in vitro and in vivo bone engineering applications.” |
| Li et al., J Appl Polym Sci, 79:2185-2191 (2001). “Study on porous silk fibroin materials. I. Fine structure of freeze dried silk fibroin.” |
| Li et al., Polymer Adv Technology, 13:605-610 (2002). “Study on porous fibroin materials: 3. Influence of repeated free-thawing on the structure and properties of porous silk fibroin materials.” |
| Martin et al., J Biomed Mater Res, 55:229-235 (2001). “Selective differentiation of mammalian bone marrow stromal cells cultured on three-dimensional polymer foams.” |
| Nam et al., J Appl Polym Sci, 81:3008-3021 (2001). “Morphology of regenerated silk fibroin: effects of freezing temperature, alcohol addition, and molecular weight.” |
| Perez-Rigueiro, J Appl Plym Sci, 70:2439-2447 (1998). “Silkworm silk as an engineering material.” |
| Petite et al., Nature Biotechnology, 18:959-963 (2000). “Tissue-engineered bone regeneration.” |
| Sofia et al., J Biomed Mater Res, 54:139-148 (2000). “Functionalized silk-based biomaterials for bone formation.” |
| Stitzel et al., J Biomater Appl, 16:22-23 (2001). “Aterial smooth muscle cell proliferation on a novel biomimicking, biodegradable vascular graft scaffold.” |
| Tsukada et al., Journal of Applied Polymer Science, 54:507-514 (1994). “Preparation and application of porous silk fibroin materials.” |
| Zarkoob, A Dissertation Presented to the Graduate Faculty of the University of Akron, Aug. 1998. “Structure and morphology of regenerated silk nano-fibers produced by electrospinning.” |
| Zarkoob, Polymer Preprints (American Chemical Society, Division of Polymer Chemistry), 39(2):244-245 (1998). “Structure and morphology of nano electrospun silk fibers.” |
| Number | Date | Country | |
|---|---|---|---|
| 20100279112 A1 | Nov 2010 | US |
| Number | Date | Country | |
|---|---|---|---|
| 60438393 | Jan 2003 | US |