1. Field of the Invention
The present invention relates to a silver paste composition and a solar cell using the same, and more particularly, to a silver paste composition for forming a front electrode of a solar cell which may improve uniformity, stability, and adhesive strength of printed patterns when the silver paste composition is applied through screen printing, and the like, and a silicon solar cell using the same.
2. Description of the Related Art
Recently, it is expected that conventional energy sources such as oil or charcoal will be exhausted, and thus, interests in alternative energy are increasing. Among alternative energy, particularly a solar cell has abundant energy sources and does not cause environmental pollution, and thus, it becomes the object of attention.
The solar cell is classified into a solar heat cell that produces vapor required to run a turbine using solar heat, and a solar light cell that converts photons into electrical energy using properties of a semiconductor. Generally, the solar light cell (hereinafter referred to as a solar cell) is represented as a solar cell.
The solar cell largely includes a silicon solar cell, a compound semiconductor solar cell, and a tandem solar cell according to raw material. Among them, the silicon solar cell leads the solar cell market.
When light falls on a solar cell having the above-mentioned structure, electrons and electron holes create in a silicon semiconductor doped with an impurity by the photovoltaic effect. Specifically, electrons create in the emitter layer 102 of an n-type silicon semiconductor as majority carriers, and electron holes create in the substrate 101 of a p-type silicon semiconductor as majority carriers. The electrons and electron holes created by the photovoltaic effect are drawn toward the n-type silicon semiconductor and the p-type silicon semiconductor, and move to a front electrode 103 on the emitter layer 102 and a rear electrode 104 below the substrate 101, respectively. When the front electrode 103 and the rear electrode 104 are connected to each other, electrical current flows.
Conventionally, a silver paste composition is used to form the front electrode 103, and an aluminum paste composition is used to form the rear electrode 104. In particular, the front electrode 103 needs a small pattern width and a large pattern height for a maximum amount of incident light and good electrical connection, and accordingly, a silver paste composition of high viscosity is prepared.
However, when a high viscosity composition is printed, the high viscosity composition does not ensure uniformity of printed patterns, and leaves much residues, which result in shadowing of a front surface of a solar cell.
Accordingly, there is a need to develop a paste composition that ensures uniformity of printed patterns and reduces occurrence of residues, although the paste composition has high viscosity.
Therefore, it is an object of the present invention to provide a silver paste composition for forming a front electrode of a solar cell that may ensure uniformity of printed patterns, reduced occurrence of residues and good preservation, as well as high viscosity, and a silicon solar cell using the same.
To achieve the object, a silver paste composition of the present invention may include silver powder, glass frit powder, an organic binder, and a plasticizer.
The silver paste composition including the plasticizer according to the present invention may have improved processability and flexibility, and thus, may enable improvement in rolling properties, leveling properties and wettability of the paste composition when the silver paste composition is used in forming printed patterns, so that adhesion between a substrate and the printed patterns may be improved.
The plasticizer of the present invention may include, for example, phthalic acid ester, benzoic acid ester, phosphoric acid ester, trimellitic acid ester, polyester, citric acid ester, adipic acid ester, epoxy compound, or mixtures thereof, however the plasticizer is not limited in this regard. The plasticizer may be any solvent capable of providing plasticity.
The content of the platicizer according to the present invention may be 0.01 to 15 parts by weight per 100 parts by weight of the silver paste composition, however the present invention is not limited in this regard.
To form a front electrode of a solar cell and to manufacture a solar cell, the silver paste composition of the present invention may be applied on an anti-reflection film.
According to the present invention, a silver paste composition for forming a front electrode may have improved rolling and leveling properties, and accordingly, the silver paste composition may enable uniform generation of fine patterns and reduced occurrence of residues.
Also, the silver paste composition for forming a front electrode may reduce a difference in thermal expansion between a substrate and printed patterns, and particularly, may reduce curling of the edges, and accordingly, the silver paste composition may improve stability and uniformity of printed patterns.
Other objects and aspects of the present invention will become apparent from the following description of embodiments with reference to the accompanying drawing in which:
Hereinafter, preferred embodiments of the present invention will be described in detail with reference to the accompanying drawings. Prior to the description, it should be understood that the terms used in the specification and the appended claims should not be construed as limited to general and dictionary meanings, but interpreted based on the meanings and concepts corresponding to technical aspects of the present invention on the basis of the principle that the inventor is allowed to define terms appropriately for the best explanation.
As described above, a silver paste composition of the present invention may include silver, glass frit powder, and an organic binder, and in particular, may further include a plasticizer.
The plasticizer may include, for example, phthalic acid ester, benzoic acid ester, phosphoric acid ester, trimellitic acid ester, polyester, citric acid ester, adipic acid ester, epoxy compound, or mixtures thereof, however the plasticizer is not limited in this regard. The plasticizer may be any solvent capable of providing plasticity.
In the silver paste composition of the present invention, the content of the platicizer may be 0.01 to 15 parts by weight per 100 parts by weight of the silver paste-composition, preferably 0.1 to 10 parts by weight, more preferably 1 to 5 parts by weight.
When the content of the platicizer is less than 0.01 parts by weight, the silver paste composition hardly has leveling properties and shows low wettability with a substrate. When the content of the platicizer exceeds 15 parts by weight, a silver paste has a reduction in rolling properties due to a large pattern width and a reduced content of a main binder when being printed, resulting in poor printability.
With regard to the silver powder included in the present invention, silver particles may include, but are not limited to, any silver particles used conventionally in the art. For example, silver particles may include, but are not limited to, any silver particles having an average particle size between 0.5 to 7 μm.
The glass frit powder usable in the silver paste composition of the present invention may include, but are not limited to, any glass frit powder used conventionally in the art. For example, the glass frit powder may include, but are not limited to, lead oxide and/or bismuth oxide. Specifically, the glass frit powder may include, but are not limited to, SiO2—PbO based powder, SiO2—PbO—B2O3 based powder, Bi2O3-B2O3—SiO2 based powder, PbO—Bi2O3-B2O3—SiO2 based powder, or mixtures thereof.
The organic binder may be used to prepare the silver powder, the glass frit powder and the plasticizer in a paste phase. The organic binder used in the present invention may include, but are not limited to, any organic binder used to prepare a silver paste composition in the art. For example, the organic binder may include, but are not limited to, cellulose, butyl carbitol, terpineol, or mixtures thereof.
In the silver paste composition of the present invention, the glass frit powder and the organic binder may be selected depending on a specific usage of the silver paste composition. For example, the content of the glass frit powder may be preferably 1 to 20 parts by weight per 100 parts of weight of the silver paste composition. The content of the organic binder may be 5 to 30 parts by weight per 100 parts of weight of the silver paste composition. The exemplary content ranges may enable easy electrode formation, and ensure viscosity suitable for screen printing and a proper aspect ratio to prevent a paste from flowing after screen printing.
The silver paste composition of the present invention may be prepared by mixing the above components by various methods known in the art so that the components may be uniformly dispersed.
Optionally, the silver paste composition of the present invention may further include an additional agent without departing from the spirit and scope of the invention. For example, the silver paste composition may further include a wetting agent, a thixotropic agent, and the like, according to necessity.
A method for preparing the silver paste composition of the present invention is described below. The silver paste composition may be prepared by putting the silver powder, the glass frit powder, the binder, and the plasticizer at the same time, and mixing them. Preferably, the silver powder, the glass frit powder, and the binder may be first mixed (first mixing), and then the plasticizer may be added and mixed with them (second mixing). In this instance, the components may be uniformly mixed using a 3-roll mill, and the like.
The simultaneous mixing of all components may allow the intended effects of the present invention, however when the plasticizer is mixed with other components at the same time, the plasticizer may be absorbed into the silver powder and the glass frit powder, and may not be uniformly dispersed in the paste. Accordingly, after the silver powder and the glass frit powder is sufficiently wetted with the binder in first mixing, the plasticizer may be added (second mixing) and uniformly dispersed in the paste, so that effects of the plasticizer may be maximized.
Hereinafter, a silicon solar cell using the silver paste composition of the present invention is described below with reference to
Referring to
The substrate 201 may be doped with p-type impurities of group 3 elements in the periodic table, such as B, Ga, In, and the like, and the emitter layer 202 may be doped with n-type impurities of group 5 elements in the periodic table, such as P, As, Sb, and the like. When the substrate 201 and the emitter layer 202 are doped with impurities of opposite conductivity type, a p-n junction may be formed at an interface between the substrate 201 and the emitter layer 202. In this instance, a p-n junction may be formed between the substrate 201 doped with n-type impurities and the emitter layer 202 doped with p-type impurities.
The anti-reflection film 203 may passivate a defect (for example, a dangling bond) existing on the surface of or in the bulk of the emitter layer 202, and may reduce reflectivity of solar rays incident on the front surface of the substrate 201. When the defect existing on/in the emitter layer 202 is passivated, a site where minority carriers are recombinated may be removed, thereby increasing the open-circuit voltage of the solar cell. Also, a reduction in reflectivity of solar rays may increase an amount of light reaching the p-n junction, thereby increasing the short circuit current of the solar cell. Accordingly, increase in open-circuit voltage and short circuit current of the solar cell by the anti-reflection film 203 may contribute to improvement in conversion efficiency of the solar cell.
For example, the anti-reflection film 203 may have a single film structure of any one selected from the group consisting of a silicon nitride film, a silicon nitride film containing hydrogen, a silicon oxide film, a silicon oxynitride film, MgF2, ZnS, MgF2, TiO2 and CeO2, or a multiple film structure of at least two material films, however the present invention is not limited in this regard. Also, the anti-reflection film 203 may be formed by vacuum deposition, chemical vapor deposition, spin coating, screen printing, or spray coating, however a method for forming the anti-reflection film 203 according to the present invention is not limited in this regard.
The front electrode 204 and the rear electrode 205 may be electrodes made from silver and aluminum, respectively. The front electrode 204 may be made from the silver paste composition of the present invention. A silver electrode may have good electrical conductivity, and an aluminum electrode may have good electrical conductivity and high affinity for the silicon semiconductor substrate 201 to enable good connection therebetween.
The front electrode 204 and the rear electrode 205 may be formed by well-known various techniques, however screen printing is preferred. That is, the front electrode 205 is formed by screen-printing the silver paste composition of the present invention at a location where a front electrode is to be formed, followed by thermal treatment. During the thermal treatment, the front electrode 204 may penetrate the anti-reflection film 203 due to a punch-through phenomenon, and may be connected to the emitter layer 202.
Similarly, the rear electrode 205 is formed by printing an aluminum paste composition for forming a rear electrode, containing aluminum, quartz silica, a binder, and the like, on the rear surface of the substrate 201, followed by thermal treatment. During the thermal treatment of the rear electrode, aluminum, that is, one of the components in the rear electrode composition may diffuse through the rear surface of the substrate 201, so that a back surface field (not shown) layer may be formed at an interface between the rear electrode 205 and the substrate 201. The back surface field layer may prevent carriers from moving to the rear surface of the substrate 201 and recombinating. Prevention of carrier recombinatinon may result in increased open-circuit voltage and increased fill factor, thereby improving conversion efficiency of the solar cell.
Hereinafter, the present invention will be described in detail through specific examples. However, the description proposed herein is just a preferable example for the purpose of illustrations only, not intended to limit the scope of the invention, so it should be understood that the examples are provided for a more definite explanation to an ordinary person skilled in the art.
Each silver paste composition was prepared by mixing silver powder, glass frit powder, an organic binder (ethyl cellulose) and an additive (a plasticizer, a wetting agent and a thixotropic agent) according to composition (unit: weight %) shown in the following Table 1, followed by uniform dispersion using a 3-roll mill.
In Table 1, a plasticizer of examples 1 to 4 was dipropyleneglycol dibenzoate (DPD), a plasticizer of example 5 was dioctyl phthalate (DOP), a plasticizer of example 6 was dioctyl adipic acid (DOA), and a plasticizer of example 7 was tricresyl phosphate (TCP).
After the silver paste compositions according to examples 1 to 7 and comparative example 1 were prepared as described above, a viscosity variation was measured. The viscosity variation was measured with a change in number of milling, and was measured over time.
(1) The viscosity variation (Vm) with a change in number of milling was computed from the following Mathematical formula 1, and viscosity was measured within about 200 seconds after a sample was prepared.
where Vm,4 is viscosity measured after milling is performed four times, and is viscosity measured after milling is performed twelve times.
In Table 2, Vm of 10% or less is represented as O, Vm greater than 10% and not greater than 30% is represented as Δ and Vm greater than 30% is represented as X.
(2) The viscosity variation (Vt) over time was computed from the following Mathematical formula 2, and viscosity was measured within about 200 seconds after a sample was prepared at 50° C.
where Vt,0, is viscosity measured immediately after a sample is prepared, and Vt,72 is viscosity measured after a sample is prepared and preserved at 50° C. for 72 hours.
In Table 2, Vt of 10% or less is represented as O, Vt greater than 10% and not greater than 30% is represented as Δ and Vt greater than 30% is represented as X.
As shown in Table 2, the test results show that the comparative example 1 has a large viscosity variation with a change of number of milling, while the examples have almost uniform viscosity regardless of number of milling.
Also, the test results teach that viscosity of the comparative example 1 significantly increases (at least 1.5 times) over time, while viscosity of the examples maintains within an increment of 10% or less.
Accordingly, it is found that the compositions of examples have smaller viscosity variation than the comparative example 1 without a plasticizer, and consequently, the silver paste composition of the present invention has higher stability. Also, it is found that addition of a plasticizer alone improves stability when a paste is preserved, without using any additive.
The compositions prepared according to examples 1 to 7 and comparative example 1 were printed in patterns having a pattern width of 120 μm by screen printing, and were dried at 200° C. The pattern width of the resulting printed patterns was measured.
A ratio of a minimum pattern width to a maximum pattern width was computed each pattern using the measured values. In Table 5, a ratio of 0.95 or more is represented as O, a ratio between 0.93 and 0.95, but not 0.95, is represented as Δ, and a ratio less than 0.93 is represented as X.
Referring to Table 3, it is found that the printed patterns formed from the compositions of the examples have a smaller variation in pattern width than that of comparative example 1.
Among the above printed patterns, a pattern width of the printed patterns formed from the compositions of the example 2 and the comparative example 1 was observed using an optical microscope. The results are shown in
Referring to
Referring to
Number | Date | Country | Kind |
---|---|---|---|
10-2009-0097296 | Oct 2009 | KR | national |
10-2010-0099638 | Oct 2010 | KR | national |
Filing Document | Filing Date | Country | Kind | 371c Date |
---|---|---|---|---|
PCT/KR2010/007001 | 10/13/2010 | WO | 00 | 8/30/2012 |