Patent Application
20200324463
Additive manufacturing has been utilized for printing three-dimensional parts by depositing successive layers of material in an automated manner. Techniques of additive manufacturing include, without limitation, fused deposition modeling (FDM), fused filament fabrication (FFF), Plastic Jet Printing (PJP), extrusion-based techniques, jetting, selective laser sintering, powder/binder jetting, electron-beam melting, and stereolithographic processes. Using these techniques, a material (e.g., a heated and/or pressurized thermoplastic) may pass through a print head. The print head may be moved in a predefined trajectory (e.g., a tool path) as the material discharges from the print head, such that the material is laid down in a particular pattern and shape of overlapping layers. The material, after exiting the print head, may harden into a final form.
The present disclosure provides methods and systems for generating various single-piece (or unitary) objects, such as, for example frames, sporting equipment, appliances, furniture, and containers. Such frames may be configured for use in vehicles, such as, for example, bicycles, airplane (e.g., airplane seats), and automobiles (car seats, bus seats, and motorcycle seats). Such frames may also be configured for use in sporting equipment, such as, for example, rackets (e.g., tennis rackets, badminton rackets, and racket ball rackets), baseball bats, flying disks, cones, and helmets.
The production of the single-piece object may be performed by three-dimensional (3D) printing. The production of the single-piece bicycle frame configuration may be performed by three-dimensional (3D) printing. The 3D printing method may use software that optimizes the custom placement of fibers (e.g., carbon fibers), for example, by adding polymeric or composite materials (e.g., carbon fibers and resin) where and only as much as is needed, which may also reduce the overall weight of the bike frame. The 3D printing method developed may eliminate assembly of the bicycle frame, which in turn reduces the frame weight, complexity, and need for managing tolerances or extra parts, and provides a method to produce a metal-free bicycle frame structure. The single-piece bicycle frame developed provides a route to produce a lighter, stronger, stiffer, and metal-free bicycle frame that is well-suited for bicycle riding.
One aspect described herein is a racket frame comprising a single-piece body formed of a polymeric material or a composite material, wherein the single-piece body comprises a first portion and a second portion, wherein a mass of the first portion is different from a mass of the second portion.
In some embodiments, the single-piece body has a mass from about 250 grams (g) to 350 g. In some embodiments, at least one of the first portion and the second portion is configured to generate a vibration frequency from about 120 Hertz (Hz) to 190 Hz when the at least one of the first portion and the second portion contacts an object. In some embodiments, at least one of the first portion and the second portion has a surface area from about 200 square centimeters (cm2) to 900 cm2. In some embodiments, at least one of the first portion and the second portion has a thickness from about 4 millimeter (mm) to 35 mm. In some embodiments, the single-piece body is formed of the polymeric material. In some embodiments, the polymeric material is polyaryletherketone (PAEK). In some embodiments, the PAEK is polyether etherketone (PEEK). In some embodiments, the PAEK is crystalline. In some embodiments, the PAEK is polycrystalline. In some embodiments, the single-piece body is formed of the composite material. In some embodiments, the composite material comprises PAEK. In some embodiments, the PAEK is PEEK. In some embodiments, the PAEK is crystalline. In some embodiments, the PAEK is polycrystalline. In some embodiments, the composite material comprises one or more types of fibers. In some embodiments, the composite material does not comprise a fiber.
Another aspect described herein is a method for forming a racket frame, comprising generating a single-piece body formed of a polymeric material or a composite material, wherein the single-piece body comprises a first portion and a second portion, wherein a mass of the first portion is different from a mass of the second portion.
In some embodiments, the single-piece body is generated using three-dimensional (3D) printing. In some embodiments, the 3D printing is additive manufacturing. In some embodiments, the 3D printing is fused filament fabrication. In some embodiments, the 3D printing is achieved by direct energy deposition process (DED). In some embodiments, the single-piece body has a mass from about 250 grams (g) to 350 g. In some embodiments, at least one of the first portion and the second portion has a surface area from about 200 square centimeters (cm2) to 900 cm2. In some embodiments, at least one of the first portion and the second portion has a thickness from about 4 millimeter (mm) to 35 mm. In some embodiments, the single-piece body is formed of the polymeric material. In some embodiments, the polymeric material is polyaryletherketone (PAEK). In some embodiments, the PAEK is polyether etherketone (PEEK). In some embodiments, the PAEK is crystalline. In some embodiments, the PAEK is polycrystalline. In some embodiments, the single-piece body is formed of the composite material. In some embodiments, the composite material comprises PAEK. In some embodiments, the PAEK is PEEK. In some embodiments, the PAEK is crystalline. In some embodiments, the PAEK is polycrystalline. In some embodiments, the composite material comprises one or more types of fiber. In some embodiments, the composite material does not comprise fiber.
Another aspect described herein is a bicycle frame comprising a single-piece body formed of a polymeric or composite material, wherein the single-piece body has a weight of at most 8.2 kilograms (Kg) and has a measure of safety in strength and stiffness greater than 1 when subjected to a compressive load of at least 100 Newtons (N) along a load-bearing axis of the bicycle frame. In some embodiments, the weight is at most 6 Kg. In some embodiments, the weight is at most 4 Kg. In some embodiments, the weight is 3.5 Kg. In some embodiments, the weight is at most 3 Kg.
In some embodiments, the measure of safety in strength and stiffness is greater than 1.5 when subjected to a compressive load of at least 100 Newtons (N) along a load-bearing axis of the bicycle frame. In some embodiments, the measure of safety in strength is greater than 1.5 when subjected to a compressive load of at least 200 Newtons (N) along a load-bearing axis of the bicycle frame. In some embodiments, the single-piece body has a measure of safety in stiffness that is greater than 1 when subjected to a compressive load of at least 200 Newtons (N) along a load-bearing axis of the bicycle frame. In some embodiments, the measure of safety in stiffness that is greater than 1 when subjected to a compression load of 2000 Newtons (N) along a load-bearing axis of the bicycle frame. In some embodiments, the measure of safety in stiffness is greater than 2 when subjected to a compression load of at least 200 Newtons (N) along a load-bearing axis of the bicycle frame. In some embodiments, the measure of safety in strength and safety is greater than 1 or greater than 2 when subjected to a compression load of at least 100 or at least 200 Newtons (N) along a load-bearing axis of the bicycle frame.
In some embodiments, the single-piece body is formed of the polymeric material. In some embodiments, the polymeric material is polyaryletherketone (PAEK). In some embodiments, the polymeric material is polyether etherketone (PEEK). In some embodiments, the PAEK is crystalline. In some embodiments, the PAEK is polycrystalline.
In some embodiments, the single-piece body is formed of the composite material. In some embodiments, the composite material comprises (PAEK). In some embodiments, the composite material is polyether etherketone (PEEK). In some embodiments, the PAEK is crystalline. In some embodiments, the PAEK is polycrystalline. In some embodiments, the composite material comprises one or more types of fiber. In some embodiments, the composite material does not comprise fiber.
Another aspect described herein is a method for forming a bicycle frame, comprising generating a single-piece body formed of a polymeric or composite material, wherein the single-piece body has a weight of at most 8.2 kilograms (Kg) and has a measure of safety in strength and stiffness greater than 1 when subjected to a compression load of at least 100 Newtons (N) along a load-bearing axis of the bicycle frame. In some embodiments, the single-piece body is generated using three-dimensional (3D) printing. In some embodiments, the 3D printing is additive manufacturing. In some embodiments, the 3D printing is fused filament fabrication. In some embodiments, the 3D printing is achieved by direct energy deposition process (DED).
In some embodiments, the weight is at most 6 Kg. In some embodiments, the weight is at most 4 Kg. In some embodiments, the weight is 3.5 Kg. In some embodiments, the weight is at most 3 Kg.
In some embodiments, the single-piece body is formed of the polymeric material. In some embodiments, the polymeric material is polyaryletherketone (PAEK). In some embodiments, the polymeric material is polyether etherketone (PEEK). In some embodiments, the PAEK is crystalline. In some embodiments, the PAEK is polycrystalline.
In some embodiments, the single-piece body is formed of the composite material. In some embodiments, the composite material comprises (PAEK). In some embodiments, the composite material is polyether etherketone (PEEK). In some embodiments, the PAEK is crystalline. In some embodiments, the PAEK is polycrystalline. In some embodiments, the composite material comprises one or more types of fiber. In some embodiments, the composite material does not comprise fiber.
Another aspect of the present disclosure provides a non-transitory computer readable medium comprising machine executable code that, upon execution by one or more computer processors, implements any of the methods above or elsewhere herein.
Another aspect of the present disclosure provides a system comprising one or more computer processors and computer memory coupled thereto. The computer memory comprises machine executable code that, upon execution by the one or more computer processors, implements any of the methods above or elsewhere herein.
Additional aspects and advantages of the present disclosure may become readily apparent to those skilled in this art from the following detailed description, wherein only illustrative embodiments of the present disclosure are shown and described. As will be realized, the present disclosure is capable of other and different embodiments, and its several details are capable of modifications in various obvious respects, all without departing from the disclosure. Accordingly, the drawings and description are to be regarded as illustrative in nature, and not as restrictive.
All publications and patent applications mentioned in this specification are herein incorporated by reference to the same extent as if each individual publication or patent application was specifically and individually indicated to be incorporated by reference.
The patent or application file contains at least one photograph executed in color. Copies of this patent or patent application publication with color photographs(s) will be provided by the Office upon request and payment of the necessary fee.
While various embodiments of the disclosure have been shown and described herein, it will be obvious to those skilled in the art that such embodiments are provided by way of example only. Numerous variations, changes, and substitutions may occur to those skilled in the art without departing from the disclosure. It should be understood that various alternatives to the embodiments of the disclosure described herein may be employed.
The term “fiber”, as used herein, generally refers to a natural or synthetic filamentous material that is significantly longer than it is wide. A fiber, as used herein, can be, but is not limited to a reinforcing fiber. A fiber, as used herein, can be, but is not limited to glass, carbon, aramid, paper, wood, asbestos, or basalt. A fiber, as used herein, can be, but is not limited to reducing the weight while improving the physical properties of the polymeric material.
The term “three-dimensional printing” (also “3D printing”), as used herein, generally refers to a process or method for generating a 3D part (or object). For example, 3D printing may refer to sequential addition of material layer or joining of material layers or parts of material layers to form a three-dimensional (3D) part, object, or structure, in a controlled manner (e.g., under automated control). In the 3D printing process, the deposited material can be fused, sintered, melted, bound or otherwise connected to form at least a part of the 3D object. Fusing the material may include melting or sintering the material. Binding can comprise chemical bonding. Chemical bonding can comprise covalent bonding. Examples of 3D printing include additive printing (e.g., layer by layer printing, or additive manufacturing). The 3D printing may further comprise subtractive printing.
The term “part,” as used herein, generally refers to an object. A part may be generated using 3D printing methods and systems of the present disclosure. A part may be a portion of a larger part or object, or an entirety of an object. A part may have various form factors, as may be based on a model of such part. Such form factors may be predetermined. The object or part may be, for example, a frame, a vehicle, sporting equipment, an appliance, furniture, a container, a barrier, hardware, a tool, a utensil, lab equipment, an instrument, or a toy.
The term “composite material,” as used herein, generally refers to a material made from two or more constituent materials with different physical or chemical properties that, when combined, produce a material with characteristics different from the individual components.
The term “fuse”, as used herein, generally refers to binding, agglomerating, or polymerizing. Fusing may include melting, softening or sintering. Binding may comprise chemical binding. Chemical binding may include covalent binding. The energy source resulting in fusion may supply energy by an electromagnetic radiation source (e.g., laser), a microwave source, source for resistive heating, an infrared energy (IR) source, a ultraviolet (UV) energy source, hot fluid (e.g., hot air), a chemical reaction, a plasma source, a microwave source, an electromagnetic source, or an electron beam. Resistive heating may be joule heating. A source for resistive heating may be a power supply. The hot fluid can have a temperature greater than 25 degrees Celsius (° C.), or greater than or equal to about 40° C., 50° C., 60° C., 70° C., 80° C., 90° C., 100° C., 150° C., 200° C., 250° C., 300° C., 350° C., 400° C., 4 50° C., 500° C., or higher. The hot fluid may have a temperature that is selected to soften or melt a material used to print an object. The hot fluid may have a temperature that is at or above a melting point or glass transition point of a polymeric material. The hot fluid can be a gas or a liquid. In some examples, the hot fluid may be air.
The term “adjacent” or “adjacent to,” as used herein, generally refers to ‘on,’ ‘over, ‘next to,’ ‘adjoining,’ ‘in contact with,’ or ‘in proximity to.’ In some instances, adjacent components are separated from one another by one or more intervening layers. The one or more intervening layers may have a thickness less than about 10 micrometers (“microns”), 1 micron, 500 nanometers (“nm”), 100 nm, 50 nm, 10 nm, 1 nm, 0.5 nm or less. For example, a first layer adjacent to a second layer can be on or in direct contact with the second layer. As another example, a first layer adjacent to a second layer can be separated from the second layer by at least a third layer.
The term “single-piece object” or “single-piece body,” as used herein, generally refers to an object, part, or the like that is generated (e.g., printed) as a whole piece. Such an object may have no material discontinuity. Such an object may have no joints.
Whenever the term “at least,” “greater than,” or “greater than or equal to” precedes the first numerical value in a series of two or more numerical values, the term “at least,” “greater than” or “greater than or equal to” applies to each of the numerical values in that series of numerical values. For example, greater than or equal to 1, 2, or 3 is equivalent to greater than or equal to 1, greater than or equal to 2, or greater than or equal to 3.
Whenever the term “no more than,” “less than,” “at most,” or “less than or equal to” precedes the first numerical value in a series of two or more numerical values, the term “no more than,” “less than,” “at most,” or “less than or equal to” applies to each of the numerical values in that series of numerical values. For example, less than or equal to 3, 2, or 1 is equivalent to less than or equal to 3, less than or equal to 2, or less than or equal to 1.
The object may be a single-piece object. Such single-piece objects may have no joints and/or no material discontinuity. The object may be, for example, a frame, a vehicle, sporting equipment, an appliance, furniture, a container, a barrier, hardware, a tool, a utensil, lab equipment, an instrument, or a toy.
The frame may be the structural component of an object. The frame may be, for example, a frame of a vehicle, a window, a door, a couch, a table, a chair, a bike, a unicycle, a tricycle, a tennis racket, a badminton racket, a ping pong racket, a squash racket, a beach tennis racket, a boat, a canoe, a kayak, a computer, glasses, a desk, a picture, a phone case, or a wheel.
The vehicle may be an object that is used to transport people or goods. The object may be a component of a vehicle. The vehicle, or component thereof, may be, for example, a boat, a bicycle, a unicycle, a tricycle, a car, a truck, a canoe, a kayak, a motorcycle, a stroller, a cart, a grocery cart, a wheel, a propeller, a tractor, an airplane, a spaceship, an airplane seat, an engine, a jet engine, a car engine, a steering wheel, a scooter, a visor, a hood, a tailgate, a tailgate liner, a tailpipe, a wing, a spaceship wing, or an airplane wing.
The sporting equipment may be an object that is used to play a sport. The sporting equipment may be, for example, a tennis racket, a skate, an ice skate, a golf club, a surfboard, a ski, a snowboard, a ping pong racket, a squash racket, a beach tennis racket, a badminton racket, a kayak paddle, a rowing paddle, a boat, a canoe, a kayak, a golf club, a hockey stick, a fishing rod, a ping pong ball, a baseball bat, a helmet, a whistle, a basketball hoop, a cleat, a golf ball, or a cricket bat.
The appliance may be a device or piece of equipment used to perform a task. The appliance may, be for example, a microwave, a refrigerator, a pressure cooker, a coffee maker, a washing machine, a dishwasher, a dryer, an air conditioner, a heater, a space heater, a vacuum, a blender, a toaster, a hair dryer, a humidifier, a waffle maker, a sewing machine, an oven, a water purifier, a dehumidifier, a garbage disposal, an iron, a television, or any component thereof.
The container may an object that is used to hold or transport a solid, a liquid or a gas. The container may be, for example, a trash can, a basket, a bucket, a receptacle, a bottle, a storage container, a tank, a cup, a mug, a jug, a box, a barrel, a drum, a tub, a crate, luggage, or a cargo container.
The barrier may be an obstacle that prevents the movement or access. The barrier may be, for example, a gate, a fence, a railing, a barricade, a bar, a wall, a door, a window, a cabinet, or a shelf.
The hardware may be equipment used to complete a task. The hardware may be, for example, a key, a lock, a doorknob, a nut, a screw, a washer, a hinge, a latch, a handle, a wire, a chain, a belt, a pipe, a wedge, a brace, a computer component, or a charger.
The tool may be a device or implement used to carry out a function. The tool may be hardware. The tool may be, for example, a spanner, a wrench, a block plane, caulking gun, a clamp, screwdriver, a hammer, a plier, a paintbrush, a jack, a crowbar, a gimlet, a hole punch, an impact driver, a mallet, a multi-tool, a nut driver, a paint roller, a pincer, a snake, a plunger, a punch, a putty knife, a sledgehammer, an axe, a staple gun, a tire iron, or a tweezer.
The utensil may be an object for household use. The utensil may be, for example, a fork, a spoon, a knife, a chopstick, a tong, a can opener, a spatula, a grater, a press, a ladle, a corkscrew, a whisk, a bottle opener, a pizza cutter, a scissor, a colander, a measuring spoon, a measuring cup, a cutting board, a masher, a bowl, a plate, or a slotted spoon.
The laboratory equipment may be equipment used in a laboratory. The laboratory equipment may be, for example, a laboratory tube, safety goggles, graduated cylinder, tongs, racks, pipettes, droppers, clamps, spatulas, balances, a microscope, a telescope, a spectrometer, or any component thereof.
The instrument may be a musical instrument. The instrument may be a string instrument, a keyboard instrument, a woodwind instrument, a brass instrument, or a percussion instrument. The instrument may be a plano, a keyboard, a cello, a violin, a viola, a bass, a guitar, a ukulele, a mandolin, a banjo, a lute, a fiddle, an organ, a oboe, a saxophone, a bassoon, a flute, a clarinet, a trumpet, a trombone, a horn, a tuba, a drum, or any component thereof
The toy may be an object that is played with. The toy may be, for example, a figurine, a car, a toy block, an interlocking block, a doll, a puzzle, a gun, a bicycle, a tricycle, a ball, a top, or puppet.
The length of the object may be at least about 0.0001 meters (m), 0.001 m, 0.01 m, 0.1 m, 1 m, 10 m, 100 m, or more. The length of the object may be at most about 100 m, 10 m, 1 m, 0.1 m, 0.01 m, 0.001 m, 0.001 m, or less. The length of the object may be from about 0.0001 m to about 100 m, about 0.01 m to about 10 m, about 0.1 m to about 5 m, about 0.1 m to about 1 m, or about 1 m to about 5 m. The surface area of the object may be at least about 0.0001 meters (m2), 0.001 m2, 0.01 m2, 0.1 m2, 1 m2, 10 m2, 100 m2, 1,000 m2, 10,000 m2, or more. The surface area of the object may be at most about 10,000 m2, 1,000 m2, 100 m2, 10 m2, 1 m2, 0.1 m2, 0.01 m2, 0.001 m2, 0.001 m2, or less. The surface area of the object may be from about 0.0001 m2 to about 10,000 m2, about 0.1 m2 to about 100 m2, about 1 m2 to about 10 m2, or about 10 m2 to about 100 m2. The volume of the object may be at least about 0.0001 meters3 (m3), 0.001 m3, 0.01 m3, 0.1 m3, 1 m3, 10 m3, 100 m3, 1,000 m3, or more. The surface area of the object may be at most about 1,000 m3, 100 m3, 10 m3, 1 m3, 0.1 m3, 0.01 m3, 0.001 m3, 0.001 m3, or less. The surface area of the object may be from about 0.0001 m3 to about 1,000 m3, about 0.1 m3 to about 100 m3, about 1 m3 to about 100 m3, or about 10 m3 to about 100 m3.
The mass of the object may be at least about 0.001 grams (g), 0.01 g, 0.1 g, 1 g, 10 g, 100 g, 1,000 g, 10,000 g, 100,000 g, or more. The mass of the object may be at most about 100,000 g, 1,000 g, 100 g, 10 g, 1 g, 0.1 g, 0.01 g, 0.001 g, or less. The mass of the object may be from about 0.001 g to about 100,000, about 1,000 g to about 100,000 g, or about 1,000 g to about 10,000 g.
The shape of the object may be a functional or a predetermined shape set by program. The shape of the object may be a functional shape set by program. The shape of the object may be a predetermined shape set by program. The shape of the object may be a functional and a predetermined shape set by program. The object may have a shape that is, for example, oblong, square, circular, spherical, linear, triangular, rectangular, parallelogrammical, curved, or any combination thereof. The object may be, for example, textured, smooth, colored, opaque, jagged, stiff, bumpy, hard, coarse, firm, or any combination thereof
The object can have a measure of safety in strength, stiffness, or a combination thereof. The measure of safety in strength and stiffness can be greater than 1.5 when subjected to a compressive load of at least 100 Newtons (N) along a load-bearing axis of the object. The measure of safety in strength can be greater than 1.5 when subjected to a compressive load of at least 200 Newtons (N) along a load-bearing axis of the object. The single-piece body may have a measure of safety in stiffness that is greater than 1 when subjected to a compressive load of at least 200 Newtons (N) along a load-bearing axis of the object. The measure of safety in stiffness may be greater than 1 when subjected to a compression load of 2000 Newtons (N) along a load-bearing axis of the object. The measure of safety in stiffness may be greater than 2 when subjected to a compression load of at least 200 Newtons (N) along a load-bearing axis of the object. The measure of safety in strength and safety may be greater than 1 or greater than 2 when subjected to a compression load of at least 100 or at least 200 Newtons (N) along a load-bearing axis of the object. The measure of safety in strength and stiffness may be at most about 2.5, 2.4, 2.3, 2.2, 2.1, 2.0, 1.9, 1.8, 1.7, 1.6, 1.5, 1.4, 1.3, 1.2, 1.1, 1.0, or less when subjected to a compressive load of at least 100 Newtons (N) along a load-bearing axis of the object. The measure of safety in strength may be at least about 1.0, 1.1, 1.2, 1.3, 1.4, 1.5, 1.6, 1.7, 1.8, 1.9, 2.0, 2.1, 2.2, 2.3, 2.4, 2.5, or more when subjected to a compressive load of at least 100 Newtons (N) along a load-bearing axis of the object. The measure of safety in strength and stiffness may be greater than 1.0 when subjected to a compressive load of at least about 100, 200, 300, 400, 500, 600, 700, 800, 900, 1000, 1100, 1200, 1300, 1400, 1500, 1600, 1700, 1800, 1900, 2000, 2100, 2200, 2300, 2400, 2500 Newtons (N), or more along a load-bearing axis of the object. The measure of safety in strength and stiffness can be greater than 1.0 when subjected to a compressive load of at most about 2500, 2400, 2300, 2200, 2100, 2000, 1900, 1800, 1700, 1600, 1500, 1400, 1300, 1200, 1100, 1000, 900, 800, 700, 600, 500, 400, 300, 200, 100 Newtons (N), or less along a load-bearing axis of the object. The measure of safety in strength and stiffness may be at most about 2.5, 2.4, 2.3, 2.2, 2.1, 2.0, 1.9, 1.8, 1.7, 1.6, 1.5, 1.4, 1.3, 1.2, 1.1, 1.0, or less when subjected to a compressive load of at least about 100, 200, 300, 400, 500, 600, 700, 800, 900, 1000, 1100, 1200, 1300, 1400, 1500, 1600, 1700, 1800, 1900, 2000, 2100, 2200, 2300, 2400, 2500 Newtons (N), or more along a load-bearing axis of the object. The measure of safety in strength and stiffness may be at most about 2.5, 2.4, 2.3, 2.2, 2.1, 2.0, 1.9, 1.8, 1.7, 1.6, 1.5, 1.4, 1.3, 1.2, 1.1, 1.0, or less when subjected to a compressive load of at most about 2500, 2400, 2300, 2200, 2100, 2000, 1900, 1800, 1700, 1600, 1500, 1400, 1300, 1200, 1100, 1000, 900, 800, 700, 600, 500, 400, 300, 200, 100 Newtons (N), or less along a load-bearing axis of the object. The measure of safety in strength may be at least about 1.0, 1.1, 1.2, 1.3, 1.4, 1.5, 1.6, 1.7, 1.8, 1.9, 2.0, 2.1, 2.2, 2.3, 2.4, 2.5, or more when subjected to a compressive load of at least about 100, 200, 300, 400, 500, 600, 700, 800, 900, 1000, 1100, 1200, 1300, 1400, 1500, 1600, 1700, 1800, 1900, 2000, 2100, 2200, 2300, 2400, 2500 Newtons (N), or more along a load-bearing axis of the object. The measure of safety in strength may be at most about 1.0, 1.1, 1.2, 1.3, 1.4, 1.5, 1.6, 1.7, 1.8, 1.9, 2.0, 2.1, 2.2, 2.3, 2.4, 2.5, or less when subjected to a compressive load of at most about 2500, 2400, 2300, 2200, 2100, 2000, 1900, 1800,c1700, 1600, 1500, 1400, 1300, 1200, 1100, 1000, 900, 800, 700, 600, 500, 400, 300, 200, 100 Newtons (N), or less along a load-bearing axis of the object.
The object may be formed of the polymeric material. The polymeric material may be polyaryletherketone (PAEK). The polymeric material may be polyetherketone (PEK), polyether etherketone (PEEK), polyetherketoneketone (PEKK), polyetheretherketoneketone (PEEKK), polyetherketoneetherketoneketone (PEKEKK), or a derivative thereof. The polymeric material may be polyether etherketone (PEEK), polyetherketoneketone (PEKK), polyetheretherketoneketone (PEEKK), or a derivative thereof. The polymeric material may be polyether etherketone (PEEK). The PAEK may be crystalline, polycrystalline, or amorphous. The PAEK may be crystalline. The PAEK may be polycrystalline.
The composite material can be polyetherketone (PEK), polyether etherketone (PEEK), polyetherketoneketone (PEKK), polyetheretherketoneketone (PEEKK), polyetherketoneetherketoneketone (PEKEKK), or a derivative thereof. The composite material can be polyether etherketone (PEEK), polyetherketoneketone (PEKK), polyetheretherketoneketone (PEEKK), or a derivative thereof. The composite material can be polyether etherketone (PEEK). The PAEK can be crystalline, polycrystalline, or amorphous. The PAEK can be crystalline. The PAEK can be polycrystalline. The composite material may comprise one or more types of fiber. The composite material may not comprise fiber. The composite material may comprise at most about 99%, 95%, 90%, 85%, 80%, 75%, 70%, 65%, 60%, 55%, 50%, 45%, 40%, 35%, 30%, 25%, 20%, 15%, 10%, 5%, 1%, or less of one or more types of fiber. The composite material may comprise at least about 1%, 5%, 10%, 15%, 20%, 25%, 30%, 35%, 40%, 45%, 50%, 55%, 60%, 65%, 70%, 75%, 80%, 85%, 90%, 95%, 99%, or more of one or more types of fiber.
The present disclosure provides methods and systems for generating various single-piece (or unitary) objects, such as, for example, frames. Such frames may be configured for use in vehicles, such as, for example, bicycles, airplanes (e.g. airplane seats). Such frames may also be configured for use in sporting equipment, such as, for example, tennis rackets, skates, ice skates, golf clubs, surfboards, skis, snowboards, ping pong rackets, squash rackets, beach tennis rackets, badminton rackets, kayak paddles, rowing paddles, boats, canoes, kayaks, golf clubs, hockey sticks, fishing rods, and more. Such single-piece objects may have no joints and/or no material discontinuity. They may be formed according to methods and systems described elsewhere herein.
One aspect described herein is a bicycle frame comprising a single-piece body formed of a polymeric or composite material, wherein the single-piece body may have a mass of at most 8.2 kilograms (Kg) and may have a measure of safety in strength and stiffness greater than 1 when subjected to a compressive load of at least 100 Newtons (N) along a load-bearing axis of the bicycle frame. In some cases, the mass may be at most about 10 Kg, 9 Kg, 8 Kg, 7 Kg, 6 Kg, 5 Kg, 4.5 Kg, 4 Kg, 3.9 Kg, 3.8 Kg, 3.7 Kg, 3.6 Kg, 3.5 Kg, 3.3 Kg, 3.2 Kg, 3.1 Kg, 3 Kg, 2.5 Kg, 2 Kg, 1 Kg, or less. The mass may be at least about 1 Kg, 2 Kg, 3 Kg, 3.1 Kg, 3.2 Kg, 3.3 Kg, 3.4 Kg, 3.5 Kg, 3.6 Kg, 3.7 Kg, 3.8 Kg, 3.9 Kg, 4 Kg, 5 Kg, 6 Kg, 7 Kg, 8 Kg, 9 Kg, 10 Kg, or more. The mass may be at most about 6 Kg. The mass is at most about 4 Kg. The mass may be about 3.5 Kg. The mass may be at most about 3 Kg.
The measure of safety in strength and stiffness can be greater than 1.5 when subjected to a compressive load of at least 100 Newtons (N) along a load-bearing axis of the bicycle frame. The measure of safety in strength can be greater than 1.5 when subjected to a compressive load of at least 200 Newtons (N) along a load-bearing axis of the bicycle frame. The single-piece body may have a measure of safety in stiffness that is greater than 1 when subjected to a compressive load of at least 200 Newtons (N) along a load-bearing axis of the bicycle frame. The measure of safety in stiffness may be greater than 1 when subjected to a compression load of 2000 Newtons (N) along a load-bearing axis of the bicycle frame. The measure of safety in stiffness may be greater than 2 when subjected to a compression load of at least 200 Newtons (N) along a load-bearing axis of the bicycle frame. The measure of safety in strength and safety may be greater than 1 or greater than 2 when subjected to a compression load of at least 100 or at least 200 Newtons (N) along a load-bearing axis of the bicycle frame. The measure of safety in strength and stiffness may be at most about 2.5, 2.4, 2.3, 2.2, 2.1, 2.0, 1.9, 1.8, 1.7, 1.6, 1.5, 1.4, 1.3, 1.2, 1.1, 1.0, or less when subjected to a compressive load of at least 100 Newtons (N) along a load-bearing axis of the bicycle frame. The measure of safety in strength may be at least about 1.0, 1.1, 1.2, 1.3, 1.4, 1.5, 1.6, 1.7, 1.8, 1.9, 2.0, 2.1, 2.2, 2.3, 2.4, 2.5, or more when subjected to a compressive load of at least 100 Newtons (N) along a load-bearing axis of the bicycle frame. The measure of safety in strength and stiffness may be greater than 1.0 when subjected to a compressive load of at least about 100, 200, 300, 400, 500, 600, 700, 800, 900, 1000, 1100, 1200, 1300, 1400, 1500, 1600, 1700, 1800, 1900, 2000, 2100, 2200, 2300, 2400, 2500 Newtons (N), or more along a load-bearing axis of the bicycle frame. The measure of safety in strength and stiffness can be greater than 1.0 when subjected to a compressive load of at most about 2500, 2400, 2300, 2200, 2100, 2000, 1900, 1800, 1700, 1600, 1500, 1400, 1300, 1200, 1100, 1000, 900, 800, 700, 600, 500, 400, 300, 200, 100 Newtons (N), or less along a load-bearing axis of the bicycle frame. The measure of safety in strength and stiffness may be at most about 2.5, 2.4, 2.3, 2.2, 2.1, 2.0, 1.9, 1.8, 1.7, 1.6, 1.5, 1.4, 1.3, 1.2, 1.1, 1.0, or less when subjected to a compressive load of at least about 100, 200, 300, 400, 500, 600, 700, 800, 900, 1000, 1100, 1200, 1300, 1400, 1500, 1600, 1700, 1800, 1900, 2000, 2100, 2200, 2300, 2400, 2500 Newtons (N), or more along a load-bearing axis of the bicycle frame. The measure of safety in strength and stiffness may be at most about 2.5, 2.4, 2.3, 2.2, 2.1, 2.0, 1.9, 1.8, 1.7, 1.6, 1.5, 1.4, 1.3, 1.2, 1.1, 1.0, or less when subjected to a compressive load of at most about 2500, 2400, 2300, 2200, 2100, 2000, 1900, 1800, 1700, 1600, 1500, 1400, 1300, 1200, 1100, 1000, 900, 800, 700, 600, 500, 400, 300, 200, 100 Newtons (N), or less along a load-bearing axis of the bicycle frame. The measure of safety in strength may be at least about 1.0, 1.1, 1.2, 1.3, 1.4, 1.5, 1.6, 1.7, 1.8, 1.9, 2.0, 2.1, 2.2, 2.3, 2.4, 2.5, or more when subjected to a compressive load of at least about 100, 200, 300, 400, 500, 600, 700, 800, 900, 1000, 1100, 1200, 1300, 1400, 1500, 1600, 1700, 1800, 1900, 2000, 2100, 2200, 2300, 2400, 2500 Newtons (N), or more along a load-bearing axis of the bicycle frame. The measure of safety in strength may be at most about 1.0, 1.1, 1.2, 1.3, 1.4, 1.5, 1.6, 1.7, 1.8, 1.9, 2.0, 2.1, 2.2, 2.3, 2.4, 2.5, or less when subjected to a compressive load of at most about 2500, 2400, 2300, 2200, 2100, 2000, 1900, 1800, 1700, 1600, 1500, 1400, 1300, 1200, 1100, 1000, 900, 800, 700, 600, 500, 400, 300, 200, 100 Newtons (N), or less along a load-bearing axis of the bicycle frame.
The single-piece body may be formed of the polymeric material. The polymeric material may be polyaryletherketone (PAEK). The polymeric material may be polyetherketone (PEK), polyether etherketone (PEEK), polyetherketoneketone (PEKK), polyetheretherketoneketone (PEEKK), polyetherketoneetherketoneketone (PEKEKK), or a derivative thereof. The polymeric material may be polyether etherketone (PEEK), polyetherketoneketone (PEKK), polyetheretherketoneketone (PEEKK), or a derivative thereof. The polymeric material may be polyether etherketone (PEEK). The PAEK may be crystalline, polycrystalline, or amorphous. The PAEK may be crystalline. The PAEK may be polycrystalline.
The composite material can be polyetherketone (PEK), polyether etherketone (PEEK), polyetherketoneketone (PEKK), polyetheretherketoneketone (PEEKK), polyetherketoneetherketoneketone (PEKEKK), or a derivative thereof. The composite material can be polyether etherketone (PEEK), polyetherketoneketone (PEKK), polyetheretherketoneketone (PEEKK), or a derivative thereof. The composite material can be polyether etherketone (PEEK). The PAEK can be crystalline, polycrystalline, or amorphous. The PAEK can be crystalline. The PAEK can be polycrystalline. The composite material comprises one or more types of fiber. The composite material does not comprise fiber. The composite material comprises at most about 99%, 95%, 90%, 85%, 80%, 75%, 70%, 65%, 60%, 55%, 50%, 45%, 40%, 35%, 30%, 25%, 20%, 15%, 10%, 5%, 1%, or less of one or more types of fiber. The composite material comprises at least about 1%, 5%, 10%, 15%, 20%, 25%, 30%, 35%, 40%, 45%, 50%, 55%, 60%, 65%, 70%, 75%, 80%, 85%, 90%, 95%, 99%, or more of one or more types of fiber.
One aspect described herein is a method for forming a bicycle frame, comprising generating a single-piece body formed of a polymeric or composite material, wherein the single-piece body has a mass of at most 8.2 kilograms (Kg) and has a measure of safety in strength and stiffness greater than 1 when subjected to a compression load of at least 100 Newtons (N) along a load-bearing axis of the bicycle frame. The single-piece body may be generated using three-dimensional (3D) printing. The 3D printing may be additive manufacturing. The 3D printing may be fused filament fabrication. The 3D printing may be achieved by direct energy deposition process (DED).
The mass can be at most about 10 Kg, 9 Kg, 8 Kg, 7 Kg, 6 Kg, 5 Kg, 4.5 Kg, 4 Kg, 3.9 Kg, 3.8 Kg, 3.7 Kg, 3.6 Kg, 3.5 Kg, 3.3 Kg, 3.2 Kg, 3.1 Kg, 3 Kg, 2.5 Kg, 2 Kg, 1 Kg, or less. The mass can be at least about 1 Kg, 2 Kg, 3 Kg, 3.1 Kg, 3.2 Kg, 3.3 Kg, 3.4 Kg, 3.5 Kg, 3.6 Kg, 3.7 Kg, 3.8 Kg, 3.9 Kg, 4 Kg, 5 Kg, 6 Kg, 7 Kg, 8 Kg, 9 Kg, 10 Kg, or more. The mass can be at most about 6 Kg. The mass can be at most about 4 Kg. The mass can be about 3.5 Kg. The mass can be at most about 3 Kg.
The single-piece body may be formed of the polymeric material. The polymeric material may be polyaryletherketone (PAEK). The polymeric material may be polyetherketone (PEK), polyether etherketone (PEEK), polyetherketoneketone (PEKK), polyetheretherketoneketone (PEEKK), polyetherketoneetherketoneketone (PEKEKK), or a derivative thereof. The polymeric material may be polyether etherketone (PEEK), polyetherketoneketone (PEKK), polyetheretherketoneketone (PEEKK), or a derivative thereof. The polymeric material may be polyether etherketone (PEEK). The PAEK may be crystalline, polycrystalline, or amorphous. The PAEK may be crystalline. The PAEK may be polycrystalline.
The composite material can be polyetherketone (PEK), polyether etherketone (PEEK), polyetherketoneketone (PEKK), polyetheretherketoneketone (PEEKK), polyetherketoneetherketoneketone (PEKEKK), or a derivative thereof. The composite material can be polyether etherketone (PEEK), polyetherketoneketone (PEKK), polyetheretherketoneketone (PEEKK), or a derivative thereof. The composite material can be polyether etherketone (PEEK). The PAEK can be crystalline, polycrystalline, or amorphous. The PAEK can be crystalline. The PAEK can be polycrystalline. The composite material comprises one or more types of fiber. The composite material does not comprise fiber. The composite material comprises at most about 99%, 95%, 90%, 85%, 80%, 75%, 70%, 65%, 60%, 55%, 50%, 45%, 40%, 35%, 30%, 25%, 20%, 15%, 10%, 5%, 1%, or less of one or more types of fiber. The composite material comprises at least about 1%, 5%, 10%, 15%, 20%, 25%, 30%, 35%, 40%, 45%, 50%, 55%, 60%, 65%, 70%, 75%, 80%, 85%, 90%, 95%, 99%, or more of one or more types of fiber.
The estimated mass for the single-piece bicycle frame used to obtain the following strength and stress data is 2.44 Kg. Various parameters for the strength and stiffness for the single-piece bicycle frame of the present disclosure were measured. The strength with vertical seat load force (Fy) equal to 2000 N was FSstatic=2.3 (compression). The strength with impact energy (E) equal to 40 N-m was FSc=1.40 (compression). The strength with vertical fatigue (Fy) equal to 1200 N was FSf=1.9 (compression). The strength with pedal fatigue (Fy) equal to 2×1000 N was FSf=1.14 (compression). The stiffness with vertical stiffness seat load was 6× Trek and 1.02× Blue bike. The stiffness with contact lateral bending was 36% low. The stiffness with lateral bending (Klein method) was 26% low. The stiffness with bottom bracket torsion (Klein) was 3× higher than max.
The experimental strength data for the material used to construct the single-piece bicycle frame before and after wrapping (fatigue limit (105 cycles) approximately 0.50*static allowable) was measured. For instance, prior to wrapping the z-strength of the composite material was S3t=17.7 MPa, but after 2 and 4 layers of wrapping (with each wrap layer being 0.50 mm each) the Szt, Szc z-strength improved to 50.8 MPa and 67.2 MPa, respectively. Additionally, the sheer strength improved from S23=14.5 MPa before wrapping to 28.6 MPa and 35.6 MPa after 2 and 4 layers of wrapping, respectively.
The differences between the original max stress criteria calculations for the composite material with the experimentally measured max stress criteria calculations for the composite material were measured. All the strength data (reported and measured in MPa) for the 50% fiber volume content composite material used to construct the single-piece bicycle frame was measured. A negative percent error between the reported and measured maximum stress values indicated that there is a predicted strength lower than the actual strength.
Another aspect described herein may be a racket frame comprising a single-piece body formed of a polymeric material or a composite material. The single-piece body may comprise a plurality of portions. In some cases, the single-piece body may comprise at least 1, 2, 3, 4, 5, 6, 7, 8, 9, 10, 15, 20, 25, 30, 35, 40, 45, 50, or more portions. In some cases, the single-piece body may comprise at most about 50, 45, 40, 35, 30, 25, 20, 15, 10, 9, 8, 7, 6, 5, 4, 3, 2, or less portions. For example, the single-piece body may comprise a first portion and a second portion. A mass of the first portion may be different from a mass of the second portion.
A mass of the single-piece body may be at least about 200 grams (g), 250 g, 260 g, 270 g, 280 g, 290 g, 300 g, 310 g, 320 g, 330 g, 340 g, 350 g, 400 g, or more. Alternatively, a mass of the single-piece body may be at most about 400 g, 350 g, 340 g, 330 g, 320 g, 310 g, 300 g, 290 g, 280 g, 270 g, 260 g, 250 g, 200 g, or less. The single-piece body may have a mass of any value between the aforementioned values of mass. For example, a mass of the single-piece body may be from about 250 g to about 350 g, from about 270 g to about 310 g, from about 280 g to about 330 g, from about 250 g to about 300 g.
At least one of the plurality of portions can be configured to generate a vibration frequency of at least about 100 Hertz (Hz), 110 Hz, 120 Hz, 122 Hz, 124 Hz, 126 Hz, 128 Hz, 130 Hz, 135 Hz, 140 Hz, 150 Hz, 160 Hz, 170 Hz, 180 Hz, 190 Hz, or more. Alternatively, at least one of the plurality of portions can be configured to generate a vibration frequency of at most about 190 Hz, 180 Hz, 170 Hz, 160 Hz, 150 Hz, 140 Hz, 130 Hz, 120 Hz, 110 Hz, 100 Hz, or less.
At least one of the plurality of portions may have a surface area of at least about 200 centimeters (cm2), 250 cm2, 300 cm2, 350 cm2, 400 cm2, 450 cm2, 500 cm2, 550 cm2, 600 cm2, 650 cm2, 700 cm2, 750 cm2, 800 cm2, 850 cm2, 900 cm2, or more. Alternatively, at least one of the plurality of portions can be configured to generate a vibration frequency of at most about 900 cm2, 850 cm2, 800 cm2, 750 cm2, 700 cm2, 650 cm2, 600 cm2, 550 cm2, 500 cm2, 450 cm2, 400 cm2, 350 cm2, 300 cm2, 250 cm2, 200 cm2, or less.
At least one of the plurality of portions may have a thickness of at least about 2 millimeters (mm), 3 mm, 4 mm, 5 mm, 6 mm, 7 mm, 8 mm, 9 mm, 10 mm, 11 mm, 12 mm, 13 mm, 14 mm, 15 mm, 20 mm, 25 mm, 30 mm, 35 mm, or more. Alternatively, at least one of the plurality of portions may be configured to have a thickness of at most 35 mm, 30 mm, 25 mm, 20 mm, 15 mm, 14 mm, 13 mm, 12 mm, 11 mm, 10 mm, 9 mm, 8 mm, 7 mm, 6 mm, 5 mm, 4 mm, 3 mm, 2 mm, or less.
In some cases, the single-piece body (e.g., of a bicycle, tennis racket, or airplane seat) may be formed of the polymeric material. In some cases, the polymeric material may be polyaryletherketone (PAEK). In some cases, the polymeric material may be polyetherketone (PEK), polyether etherketone (PEEK), polyetherketoneketone (PEKK), polyetheretherketoneketone (PEEKK), polyetherketoneetherketoneketone (PEKEKK), or a derivative thereof. In some cases, the polymeric material may be polyether etherketone (PEEK), polyetherketoneketone (PEKK), polyetheretherketoneketone (PEEKK), or a derivative thereof. In some cases, the polymeric material may be polyether etherketone (PEEK). In some cases, the PAEK may be crystalline, polycrystalline, or amorphous. In some cases, the PAEK may be crystalline. In some cases, the PAEK may be polycrystalline.
In some cases, the composite material may be polyetherketone (PEK), polyether etherketone (PEEK), polyetherketoneketone (PEKK), polyetheretherketoneketone (PEEKK), polyetherketoneetherketoneketone (PEKEKK), or a derivative thereof. In some cases, the composite material may be polyether etherketone (PEEK), polyetherketoneketone (PEKK), polyetheretherketoneketone (PEEKK), or a derivative thereof. In some cases, the composite material may be polyether etherketone (PEEK). In some cases, the PAEK may be crystalline, polycrystalline, or amorphous. In some cases, the PAEK may be crystalline. In some cases, the PAEK may be polycrystalline.
In some cases, the composite material may comprise one or more types of fiber. In some cases, the composite material does not comprise fiber. In some cases, the composite material comprises at most about 99%, 95%, 90%, 85%, 80%, 75%, 70%, 65%, 60%, 55%, 50%, 45%, 40%, 35%, 30%, 25%, 20%, 15%, 10%, 5%, 1%, or less of one or more types of fiber. In some cases, the composite material may comprise at least about 1%, 5%, 10%, 15%, 20%, 25%, 30%, 35%, 40%, 45%, 50%, 55%, 60%, 65%, 70%, 75%, 80%, 85%, 90%, 95%, 99%, or more of one or more types of fiber.
One aspect described herein is a method for forming a racket frame comprising a single-piece body formed of a polymeric material or a composite material. The single-piece body may comprise a plurality of portions. In some cases, the single-piece body may comprise at least 1, 2, 3, 4, 5, 6, 7, 8, 9, 10, 15, 20, 25, 30, 35, 40, 45, 50, or more portions. In some cases, the single-piece body may comprise at most about 50, 45, 40, 35, 30, 25, 20, 15, 10, 9, 8, 7, 6, 5, 4, 3, 2, or less portions. For example, the single-piece body may comprise a first portion and a second portion. A mass of the first portion may be different from a mass of the second portion. In some cases, the single-piece body can be generated using three-dimensional (3D) printing. In some cases, the 3D printing can be additive manufacturing. In some cases, the 3D printing can be fused filament fabrication. In some cases, the 3D printing can be achieved by direct energy deposition process (DED).
In some cases, a mass of the single-piece body may be at least about 200 grams (g), 250 g, 260 g, 270 g, 280 g, 290 g, 300 g, 310 g, 320 g, 330 g, 340 g, 350 g, or more. Alternatively, a mass of the single-piece body may be at most about 400 g, 350 g, 340 g, 330 g, 320 g, 310 g, 300 g, 290 g, 280 g, 270 g, 260 g, 250 g, or less. The single-piece body may have a mass of any value between the aforementioned values. For example, a mass of the single-piece body may be from about 250 g to about 350 g, from about 270 g to about 310 g, from about 280 g to about 330 g, from about 250 g to about 300 g.
In some cases, at least one of the plurality of portions may be configured to have a surface area of at least about 200 centimeters (cm2), 250 cm2, 300 cm2, 350 cm2, 400 cm2, 450 cm2, 500 cm2, 550 cm2, 600 cm2, 650 cm2, 700 cm2, 750 cm2, 800 cm2, 850 cm2, 900 cm2, or more. Alternatively, at least one of the plurality of portions can be configured to generate a vibration frequency of at most about 900 cm2, 850 cm2, 800 cm2, 750 cm2, 700 cm2, 650 cm2, 600 cm2, 550 cm2, 500 cm2, 450 cm2, 400 cm2, 350 cm2, 300 cm2, 250 cm2, 200 cm2, or less.
In some cases at least one of the plurality of portions may have a thickness of at least about 1 millimeters (mm), 3 mm, 4 mm, 5 mm, 6 mm, 7 mm, 8 mm, 9 mm, 10 mm, 11 mm, 12 mm, 13 mm, 14 mm, 15 mm, 20 mm, 25 mm, 30 mm, 35 mm, 40 mm, 45 mm, 50 mm, or more. Alternatively, at least one of the plurality of portions may have a thickness of at most 50 mm, 45 mm, 40 mm, 35 mm, 30 mm, 25 mm, 20 mm, 15 mm, 14 mm, 13 mm, 12 mm, 11 mm, 10 mm, 9 mm, 8 mm, 7 mm, 6 mm, 5 mm, 4 mm, 3 mm, 2 mm, 1 mm, or less.
In some cases, the single-piece body may be formed of the polymeric material. In some cases, the polymeric material may be polyaryletherketone (PAEK). In some cases, the polymeric material may be polyetherketone (PEK), polyether etherketone (PEEK), polyetherketoneketone (PEKK), polyetheretherketoneketone (PEEKK), polyetherketoneetherketoneketone (PEKEKK), or a derivative thereof. In some cases, the polymeric material may be polyether etherketone (PEEK), polyetherketoneketone (PEKK), polyetheretherketoneketone (PEEKK), or a derivative thereof. In some cases, the polymeric material may be polyether etherketone (PEEK). In some cases, the PAEK may be crystalline, polycrystalline, or amorphous. In some cases, the PAEK may be crystalline. In some cases, the PAEK may be polycrystalline.
In some cases, the composite material may be polyetherketone (PEK), polyether etherketone (PEEK), polyetherketoneketone (PEKK), polyetheretherketoneketone (PEEKK), polyetherketoneetherketoneketone (PEKEKK), or a derivative thereof. In some cases, the composite material can be polyether etherketone (PEEK), polyetherketoneketone (PEKK), polyetheretherketoneketone (PEEKK), or a derivative thereof. In some cases, the composite material can be polyether etherketone (PEEK). In some cases, the PAEK can be crystalline, polycrystalline, or amorphous. In some cases, the PAEK can be crystalline. In some cases, the PAEK can be polycrystalline.
In some cases, the composite material may comprise one or more types of fiber. In some cases, the composite material may not comprise fiber. In some cases, the composite material may comprise at most about 99%, 95%, 90%, 85%, 80%, 75%, 70%, 65%, 60%, 55%, 50%, 45%, 40%, 35%, 30%, 25%, 20%, 15%, 10%, 5%, 1%, or less of one or more types of fiber. In some cases, the composite material may comprise at least about 1%, 5%, 10%, 15%, 20%, 25%, 30%, 35%, 40%, 45%, 50%, 55%, 60%, 65%, 70%, 75%, 80%, 85%, 90%, 95%, 99%, or more of one or more types of fiber.
The single-piece body racket frame may be formed by custom placement of fibers (e.g., carbon fibers), for example, by adding polymeric or composite materials (e.g., carbon fibers and resin) where and only as much as is needed, for example a small space in a lower segment (e.g., handle, or racket handle, or tennis racket handle) 1306, a large space in the lower segment 1307 and 1308, in and around (e.g. handle, and throat, and face of the tennis racket) the single-piece body tennis racket 1311.
The single-piece body racket frame may be formed by custom placement of fibers (e.g., carbon fibers), for example, by adding (e.g. printing) polymeric or composite materials (e.g., carbon fibers and resin) in a plurality of directions, for example, horizontally or perpendicular to the long axis of the single-piece body tennis racket shown in the lower segment (e.g., handle, or racket handle, or tennis racket handle) in 1306 and 1307, or angled with respect to the long axis of the single-piece body tennis racket as shown in the lower segment (e.g., handle, or racket handle, or tennis racket handle) 1308 and 1310.
A front view of a computer-generated model of the 3D printed single-piece racket frame is shown in
An angled view of a computer-generated model of the 3D printed single-piece racket frame is shown in
In some cases, the mass of the single-piece body (e.g., tennis racket) may be configured by addition of an external mass (e.g. lead, tungsten, and or other heavy metal tapes) to the single-piece body frame, by printing with heavier materials, and/or by injecting or adding mass into the single-piece body frame (e.g. a handle of a tennis racket).
In some cases, a width of at least one of the portions of the single-piece body frame (e.g. racket frame) can be customized to a range of widths. For example, the width of at least one of the portions of the single-piece body frame (e.g. racket frame) may be the horizontal distance between any two points on the single-piece body tennis frame in
In some cases, at least a plurality of parameters in a single-body frame (e.g. tennis racket) may be customized (e.g. a stiffness, a torsional stability, a stringing load capacity, a symmetry, a center of percussion, a sweet spot location, a number of holes, a distance of holes with respect to one another, a placement of holes with respect to a pattern of stringing the tennis racket).
The present disclosure provides methods and systems for 3D printing. Such methods and systems may be used to form frames of the present disclosure, such as bicycle frames (e.g., single-piece bicycles frames) or racket frames (e.g., single-piece racket frames).
Examples of 3D printing methodologies comprise extrusion, wire, granular, laminated, light polymerization, VAT photopolymerization, material jetting, binder jetting, sheet lamination, directed energy deposition, or power bed and inkjet head 3D printing. Extrusion 3D printing can comprise robo-casting, fused deposition modeling (FDM) or fused filament fabrication (FFF). Wire 3D printing can comprise electron beam freeform fabrication (EBF3). Granular 3D printing can comprise direct metal laser sintering (DMLS), electron beam melting (EBM), selective laser melting (SLM), selective heat sintering (SHS), or selective laser sintering (SLS). Power bed and inkjet head 3D printing can comprise plaster-based 3D printing (PP). Laminated 3D printing can comprise laminated object manufacturing (LOM). Light polymerized 3D printing can comprise stereo-lithography (SLA), digital light processing (DLP) or laminated object manufacturing (LOM).
Examples of methods, systems and materials that may be used to create or generate objects or parts herein are provided in U.S. Patent Publication Nos. 2014/0232035, 2017/0198104, 2017/0096576, 2016/0271880, and U.S. Pat. Nos. 10,421,267, 9,908,978, 9,998,071, 9,592,660, 9,895,845, 10,067,499, each of which is entirely incorporated herein by reference.
Three-dimensional printing may be performed using various materials. The form of the build materials that can be used in embodiments of the disclosure include, without limitation, filaments, sheets, powders, and inks. In some examples, a material that may be used in 3D printing includes a polymeric material, elemental metal, metal alloy, a ceramic, composite material, an allotrope of elemental carbon, or a combination thereof. The allotrope of elemental carbon may comprise amorphous carbon, graphite, graphene, diamond, or fullerene. The fullerene may be selected from the group consisting of a spherical, elliptical, linear, tubular fullerene, and any combination thereof. The fullerene may comprise a buck ball or a carbon nanotube. The material may comprise an organic material, for example, a polymer or a resin. The material may comprise a solid or a liquid. The material may include one or more strands or filaments. The solid material may comprise powder material. The powder material may be coated by a coating (e.g., organic coating such as the organic material (e.g., plastic coating)). The powder material may comprise sand. The material may be in the form of a powder, wire, pellet, or bead. The material may have one or more layers. The material may comprise at least two materials. In some cases, the material may include a reinforcing material (e.g., that forms a fiber). The reinforcing material may comprise a carbon fiber, Kevlar®, Twaron®, ultra-high-molecular-weight polyethylene, or glass fiber.
Prior to printing the part or object, a computer aided design (CAD) model can be optimized based on specified requirements. For example, the CAD model may comprise a geometry “envelop”. A geometry envelop may be an initial shell design of the three-dimensional part comprising design requirements and geometric features. The geometry of the CAD model may be received by way of I/O devices. Design requirements can be selected from the group consisting of strength, structural deflections, stress, strain, tension, shear, load capacity, stiffness, factor-of safety, weight, strength to weight ratio, envelop geometry, minimal print time, thermal performance, electrical performance, porosity, infill, number of shells, layer height, printing temperature, extruder temperature, solid density, melt density, printing speed, print head movement speed, and any combination thereof.
The CAD model may be initially partitioned according to user input and built in tool path generator rules to produce numerical control programming codes of the partitioned computer model. Partitioning can generate one or more parameters for printing the part. The One or more parameters may be selected from the group consisting of filament diameter, layer thickness, infill percentage, infill pattern, raster angle, build orientation, printed material width, extrudate width, layer height, shell number, infill overlap, grid spacing, and any combination thereof. Partitioning can also generate one or more numerical control programming code of the partitioned computer model. The numerical control programming code can comprise G-code files and intermediate files. G-code files may be a numerical control programming language and can be used in computer-aided manufacturing as a way of controlling automated machine tools. The actions controlled by the G-code may comprise rapid movement, controlled feed in an arc or straight line, series of controlled feed movements, switch coordinate systems, and a set of tool information. Intermediate files may comprise supplemental files and tools for a primary build output. Additionally, intermediate files can comprise automatically generated source files or build output from helper tools. The information from the G-code files and the intermediate files may be extracted to determine the geometry of the three-dimensional printed part.
The 3D object may have a 3D solid model created in CAD software. Such 3D object can be sliced using conventional algorithms as are known in the art to generate a series of two dimensional (2D) layers representing individual transverse cross sections of the 3D object, which collectively depict the 3D object. The 2D slice information for the layers may be sent to the controller and stored in memory. Such information can control the process of fusing particles into a dense layer according to the modeling and inputs obtained during the build process.
Prior to printing the three-dimensional object, a model, in computer memory, of the part for three-dimensional printing may be received from a material. The material can comprise a matrix and fiber material. Additionally, in computer memory, one or more properties for the material may be received. Using the model, a print head tool path may be determined for use during the three-dimensional printing of the part. A virtual mesh of analytic elements may be generated within the model of the part and a trajectory of at least one stiffness-contributing portion of the material may be determined based at least in part on the print head tool path, wherein the trajectory of the at least one stiffness-contributing portion is determined through each of the analytic elements in the virtual mesh. Next, one or more computer processors may be used to determine a performance of the part based at least in part on the one or more properties received and the trajectory of the at least one stiffness-contributing portion. The performance of the part may be electronically outputted. The three-dimensional object may then be printed along the print head tool path.
The present disclosure provides ways to improve the mechanical, thermal, and electrical properties of additively manufactured parts. All additive manufacturing approaches build up an object in a layer-by-layer fashion. In other words, the layers of build material are deposited one on top of the next, such that a successive layer of build material is deposited upon a previously deposited/constructed layer that has cooled below its melting temperature. The print head may comprise three or more axes or degrees of freedom so that the print head can move in the +X direction, the −X direction, the +Y direction, the −Y direction, the +Z direction, the −Z direction, or any combination thereof. The print head may be configured as a six-axis robotic arm. Alternatively, the print head may be configured as a seven-axis robotic arm. The print head may be placed at any location in the build volume of the 3D object, from any approach angle.
In accordance with embodiments of the disclosure, a system for additive manufacturing processes provides localized heating to create a “melt pool” in the current layer or segment of deposited build material prior to depositing the next segment or layer. The melt pool can span the entire thickness of the printed segment, thereby increasing the adhesion across segments built in the same layer. The melt pool can span a portion of the thickness of the printed segment. The melt pool may increase the diffusion and mixing of the build material between adjacent layers (across the Z direction) as compared to current methods, which deposit a subsequent layer of build material on top of a layer of build material that is below its melting temperature. The increased diffusion and mixing resulting from the melt pool can increase the chemical chain linkage/bonding and chemical chain interactions between the two layers. This can result in increases in the build-material adhesion in the Z direction, thereby enhancing mechanical, thermal, and electrical properties. The melt pool may also reduce void space and porosity in the build object. Among any other benefits, this decrease in porosity also contributes somewhat to the aforementioned improvement in mechanical, thermal, and electrical properties.
Before depositing a layer of material on an underlying layer in a build object, the portion of the underlying layer on which the subsequent layer is to be deposited may be melted, creating a “melt pool.” The melt pool can be created using an energy source, such as, without limitation, by an electromagnetic radiation source (e.g., laser), a microwave source, a resistive heating source, an infrared energy source, a UV energy source, hot fluid, a chemical reaction, a plasma source, a microwave source, an electromagnetic source, or an electron beam. Resistive heating may be joule heating. A source for resistive heating may be a power supply. The applied energy is primarily a function of the chemical composition of the build material, such as the build material's thermal conductivity, heat capacity, latent heat of fusion, melting point, and melt flow viscosity.
Prior to printing the 3D object, a request for production of a requested 3D object may be received from a customer. The method may comprise packaging the three dimensional object. After printing of the 3D object, the printed three dimensional object may be delivered to the customer.
In an aspect, the present disclosure provides for method for printing at least a portion of a 3D object. In computer memory, a model of the 3D object may be received. Subsequent to receiving the model of the 3D object, at least one filament material may be directed from a source of at least one filament material towards a substrate that is configured to support the 3D object, thereby depositing a first layer corresponding to a portion of the 3D object adjacent to the substrate. The first layer may be deposited in accordance with the model of the 3D object. At least one filament material may be directed from the source to an opening. At least one filament material can be directed from the opening towards the substrate. Next, a second layer of at least a portion of the 3D object may be deposited. The second layer can be deposited in accordance with the model of the 3D object. At least a first energy beam may be used from at least one energy source to selectively melt at least a portion of the first layer and/or the second layer, thereby forming at least a portion of the 3D object. One or more additional layers may be further deposited adjacent to the first layer prior to depositing the second layer. In some cases, fused deposition modeling may be performed when printing the 3D object. In other cases, the 3D object may be printed with extrusion. In some cases, the 3D object may be printed without extrusion.
The layered structure can comprise substantially repetitive layers. The layers may have an average layer size (e.g. layer thickness or layer width) of at least about 0.5 micrometer (μm), 1 μm, 5 μm, 10 μm, 20 μm, 30 μm, 40 μm, 50 μm, 60 μm, 70 μm, 80 μm, 90 μm, 100 μm, 150 μm, 200 μm, 250 μm, 300 μm, 350 μm, 400 μm, 450 μm, 500 μm, 1 mm, 25 mm, 50 mm, 100 mm, 500 mm, or 1 m. The layers may have an average layer size (e.g. layer thickness or layer width) of at most about 50 m, 1 m, 500 mm, 100 mm, 50 mm, 25 mm, 1 mm, 500 μm, 450 μm, 400 μm, 350 μm, 300 μm, 250 μm, 200 μm, 150 μm, 100 μm, 90 μm, 80 μm, 70 μm, 60 μm, 50 μm, 40 μm, 30 μm, 20 μm, or 10 μm. The layers may have an average layer size of any value between the aforementioned values of layer size. For example, the substantially repetitive microstructure may have an average layer size from about 0.5 μm to about 500 mm, from about 15 μm to about 100 μm, from about 5 μm to about 300 μm, from about 20 μm to about 90 μm, or from about 10 μm to about 70 μm. The layered structure can be indicative of layered deposition. The layered structure can be indicative of solidification of melt pools formed during a three-dimensional printing process. The structure indicative of a three dimensional printing process can comprise substantially repetitive variation comprising: variation in grain orientation, variation in material density, variation in the degree of compound segregation to grain boundaries, variation in the degree of element segregation to grain boundaries, variation in material phase, variation in metallurgical phase, variation in material porosity, variation in crystal phase, or variation in crystal structure. The melt pools may be indicative of an additive manufacturing process comprising stereolithography (SLA), selective laser melting (SLM), selective laser sintering (SLS), digital light processing (DLP), electron beam melting (EBM), laminated object manufacturing (LOM), binder jetting (BM), material jetting/wax casting (MJ), direct metal laser sintering (DMLS), or fused deposition modeling (FDM). The melt pools may be indicative of an additive manufacturing process comprising selective energy melting.
The source of at least one filament material may be configured to supply at least one filament material for generating the three-dimensional object. The at least one filament material may be a composite material, such as a continuous fiber composite. The filament material may be nano milled, short, long, continuous, or a combination thereof. The continuous fiber composite may be a continuous core reinforced filament. The continuous core reinforced filament can comprise a towpreg that is substantially void free and includes a polymer that coats or impregnates an internal continuous core. Depending upon the particular embodiment, the core may be a solid core, or it may be a multi-strand core comprising multiple strands. The continuous fiber composite may be selected from the group consisting of glass, carbon, aramid, cotton, silicon carbide, polymer, wool, metal, and any combination thereof.
The filament material may incorporate one or more additional materials, such as resins and polymers. For example, appropriate resins and polymers include, but are not limited to, acrylonitrile butadiene styrene (ABS), epoxy, vinyl, nylon, polyetherimide (PEI), Polyaryletherketone (PAEK), Polyether ether ketone (PEEK), Polyactic Acid (PLA), Liquid Crystal Polymer, polyamide, polyimide, polyphenylene sulfide, polyphenylsulfone, polysulfone, polyether sulfone, polyethylenimine, polytetrafluoroethylene, polyvinylidene, and various other thermoplastics. The core of the continuous fiber composite may be selected to provide any desired property. Appropriate core fiber or strands include those materials which impart a desired property, such as structural, conductive (electrically and/or thermally), insula.tive (electrically and/or thermally), optical and/or fluidic transport. Such materials include, but are not limited to, carbon fibers, aramid fibers, fiberglass, metals (such as copper, silver, gold, tin, and steel), optical fibers, and flexible tubes. The core fiber or strands may be provided in any appropriate size. Further, multiple types of continuous cores may be used in a single continuous core reinforced filament to provide multiple functionalities such as electrical and optical properties. A single material may be used to provide multiple properties for the core reinforced filament. For example, a steel core may be used to provide both structural properties as well as electrical conductivity properties.
Alternatively, the filament material may comprise metal particles infused into a binder matrix. The metal particles may be metal powder. The metal particles may be carbon nanotubes. The binder matrix may include resins or polymers. Additionally, such binder matrix can be used a delivery device for the metal particles. Once the filament material is deposited onto the base, one or more energy sources can heat and melt the binder matrix, leaving the metal particles to melt and fuse into larger metal particles. Such energy sources may be without limitation, by an electromagnetic radiation source (e.g., laser), a microwave source, a resistive heating source, an infrared energy source, a UV energy source, hot fluid, a chemical reaction, a plasma source, a microwave source, an electromagnetic source, or an electron beam. Resistive heating may be joule heating. A source for resistive heating may be a power supply. The at least one filament material may be a metal filament. The at least one filament material may be a metal filament composite. The deposited at least one filament material may be subjected to resistive heating upon flow of an electrical current through the at least one filament material. The resistive heating may be sufficient to melt at least a portion of the deposited at least one filament material. The at least one filament material may be an electrode. The substrate may be another electrode.
The one or more energy sources may also provide localized heating to create a “melt pool” in the current layer or segment of the deposited build material prior to depositing the next segment or layer. The melt pool can increase diffusion and mixing of the build material between adjacent layers (e.g., across a direction orthogonal to the layers) as compared to other methods which deposit a subsequent layer of build material on top of a layer of build material that is below its melting temperature.
The increased diffusion and mixing resulting from the melt pool may increase the chemical chain linkage, bonding, and chemical chain interactions between the two layers. This can result in increasing the build-material adhesion in the Z direction, thereby enhancing mechanical, thermal, and electrical properties of the three-dimensional object. The melt pool can also reduce the void space and porosity in the build object. Among other benefits, this decrease in porosity may also contribute to the aforementioned improvement in mechanical, thermal, and electrical properties.
The at least one filament material may have a cross sectional shape selected from the group consisting of circle, ellipse, parabola, hyperbola, convex polygon, concave polygon, cyclic polygon, equilateral polygon, equiangular polygon, regular convex polygon, regular star polygon, tape-like geometry, and any combination thereof. Such filament material can have a diameter of at most about 0.1 millimeters (mm), at most about 0.2 mm, at most about 0.3 mm, at most about 0.4 mm, at most about 0.5 mm, at most about 0.6 mm, at most about 0.7 mm, at most about 0.8 mm, at most about 0.9 mm, at most about 1 mm, at most about 2 mm, at most about 3 mm, at most about 4 mm, at most about 5 mm, at most about 10 mm, or at most about 20 mm.
Various modifiers within the layers themselves may be used which are selectively printed onto specific regions of the 3D object in order to impart various desirable mechanical, chemical, magnetic, electrical or other properties to the 3D object. Such modifiers may be selected from the group consisting of thermal conductors and insulators, dielectric promoters, electrical conductors and insulators, locally-contained heater traces for multi-zone temperature control, batteries, and sensors. At least one print head can be may be used for printing such modifiers. As desired, such modifiers can be printed before at least a first energy beam is directed onto at least a portion of the first layer and/or second layer. Alternatively, such modifiers may be printed over a layer that has been melted, before filament material for the next layer is deposited.
For example, when printing a polyimide part from commercially available a filament comprising polyimide, an array of electrically conductive traces may be assimilated as an antenna to selectively absorb radiofrequency (RF) radiation within a specific and predetermined frequency range. The 3D object CAD model and software can designate as a sub-part the layer(s) that comprise the traces for modified properties (high electrical conductivity). Alternatively, if these portions of the layer entail different levels of energy for inducing fusion, compared to other regions having only the primary material, the CAD model and design of the 3D object may be adjusted accordingly.
After deposition of a first layer and/or a second layer of at least a portion of the 3D object, and before fusion is induced, the filament material may be preheated to a temperature sufficient to reduce undesirable shrinkage and/or to minimize the laser energy needed to melt the next layer. For example, the preheating may be accomplished using the infrared heater attached to substrate or through other apparatuses of directing thermal energy within an enclosed space around the substrate. Alternatively, the preheating can be accomplished using energy beam melting by defocusing the energy beam and rapidly scanning it over the deposited first layer and or second layer of at least a portion of the 3D object.
At least a first energy beam from at least one energy source may be used to selectively heat and/or melt at least a portion of the first layer and/or the second layer, thereby forming at least a portion of the 3D object. The energy source may be selected from the group consisting of an electromagnetic radiation source (e.g., laser), a microwave source, a resistive heating source, an infrared energy source, a UV energy source, hot fluid, a chemical reaction, a plasma source, a microwave source, an electromagnetic source, an electron beam, or any combination thereof. Resistive heating may be joule heating. A source for resistive heating may be a power supply. The at least one filament material may be a metal filament. The at least one filament material may be a metal filament composite. The deposited at least one filament material may be subjected to resistive heating upon flow of an electrical current through the at least one filament material. The resistive heating may be sufficient to melt at least a portion of the deposited at least one filament material. The at least one filament material may be an electrode. The substrate may be another electrode.
The energy source may be a function of the chemical composition of the build material, such as the build material's thermal conductivity, heat capacity, latent heat of fusion, melting point, and melt flow viscosity. The at least one energy source may be a laser. The laser may be selected from the group consisting of gas lasers, chemical lasers, dye lasers, metal-vapor lasers, solid-state lasers, semiconductor lasers, free electron laser, gas dynamic laser, nickel-like samarium laser, Raman laser, nuclear pump laser, and any combination thereof. Gas lasers may comprise one or more of helium-neon laser, argon laser, krypton laser, xenon ion laser, nitrogen laser, carbon dioxide laser, carbon monoxide laser, and excimer laser. Chemical lasers may be selected from the group consisting of hydrogen fluoride laser, deuterium fluoride laser, chemical oxygen-iodine laser, all gas-phase iodine laser, and any combination thereof. Metal-vapor lasers can comprise one or more of helium-cadmium, helium mercury, helium selenium, helium silver, strontium vapor laser, neon-copper, copper vapor laser, gold vapor laser, and manganese vapor laser. Solid-state lasers may be selected from the group consisting of ruby laser, neodymium-doped yttrium aluminium garnet laser, neodymium and chromium-doped yttrium aluminium garnet laser, erbium-doped yttrium aluminium garnet laser, neodymium-doped yttrium lithium fluoride laser, neodymium doped yttrium othovanadate laser, neodymium doped yttrium calcium oxoborate laser, neodymium glass laser, titanium sapphire laser, thulium yttrium aluminium garnet laser, ytterbium yttrium aluminium garnet laser, ytterbium:2O3 (glass or ceramics) laser, ytterbium doped glass laser (rod, plate/chip, and fiber), holmium yttrium aluminium garnet laser, chromium zinc selenium laser, cerium doped lithium strontium (or calcium) aluminum fluoride laser, Promethium 147 doped phosphate glass solid-state laser, chromium doped chrysoberyl (alexandrite) laser, erbium doped and erbium-ytterbium codoped glass lasers, trivalent uranium doped calcium fluoride solid-state laser, divalent samarium doped calcium fluoride laser, FARBE center laser, and any combination thereof. Semiconductor laser may comprise one or more of semiconductor laser diode laser, gallium nitride laser, indium gallium nitride laser, aluminium gallium indium phosphide laser, aluminium gallium arsenide laser, indium gallium arsenide phosphide laser, lead salt laser, vertical cavity surface emitting laser, quantum cascade laser, and hybrid silicon laser.
The melting temperature of the at least one filament material can be at least about 150 degrees Celsius (° C.), at least about 200° C., at least about 250° C., at least about 300° C., at least about 350° C., at least about 400° C., at least about 450° C. The sintering temperature can be at most about 150° C., at most about 200° C., at most about 250° C., at most about 300° C., at most about 350° C., at most about 400° C. The method may further comprise separating the remainder of the layer that did not fuse and solidify to form at least a portion of the three-dimensional object, from the portion.
The at least one energy beam from the energy source may be directed to the at least one portion of the 3D object adjacent to the substrate. Such energy beams may be sufficient to induce fusion of particles of the filament material within the desired cross-sectional geometry of the at least one portion of the 3D object. As the energy dissipates with cooling, atoms from neighboring particles may fuse together. The at least one energy beam results in the fusion of particles of filament material both within the same layer and in the previously formed and resolidified adjoining layer(s) such that fusion is induced between at least two adjacent layers of the part, such as between at least one filament material in a deposited unfused layer and a previously-fused adjacent layer. This process is then repeated over multiple cycles as each part layer is added, until the full 3D object is formed.
In some cases, to create a melt pool large enough to span the width of the filament material segment, multiple energy sources or a combination of energy sources may be required. When multiple energy sources are used, the energy sources may be the same energy source. Alternatively, the multiple energy sources may be different energy sources. The energy source(s) may be separate from the system for printing at least a portion of the 3D object. In some other embodiments, the energy source(s) may be integrated with such system. For example, in one embodiment, hot fluid may be channeled through the deposition nozzle. Because the material filament can flow in the melt pool, features of the 3D object being built can be altered. The melt pool may be formed within the build object, such that a melt pool is not formed near the perimeters thereof. To accomplish this, the energy source may be turned off when the perimeters of the object are being built. In such embodiments, the geometrical tolerance of the build object may be maintained while the interior of the object has enhanced interlayer bonding. During printing, the filament material may be printed in the X, Y, and Z directions in one segment or layer.
Such filament material may also be directed to at least one freely suspended roller 206, thereby depositing a first layer corresponding to a portion of the 3D object on the substrate. Next, the second layer of at least a portion of the 3D object may be deposited. One or more additional layers can be deposited adjacent to the first layer prior to depositing the second layer. At least a first energy beam from at least one energy source may selectively melt at least a portion of the first layer and/or the second layer, thereby forming at least a portion of the 3D object. The energy beam may be a laser beam. The energy source may be a laser head that is mounted on a robot or similar mechanism that swivels around the vertical axis enabling deposition in any direction in the plane of deposition. At least one filament material may be fed into a nozzle at an angle such that it is fed under at least one freely suspended roller at a nip point 209 as the at least one freely suspended roller presses this filament material exiting from the nozzle. The nip point can be the point where such filament material meets the substrate and is pressed by the at least one freely suspended roller resulting in a compressed cross section 210. The laser may at least heat either the filament being deposited, or the already deposited material, or both.
The compaction unit may comprise at least one freely suspended roller that is supported by one or more idler rollers 205. The at least one freely suspended roller may be designed to control the bend radii of such filament material. At least a portion of the three-dimensional object may be generated from such filament material continuously upon subjecting such deposited filament material to heating along the one or more locations. The system 200 may further comprise a controller operatively coupled to at least one light source.
The at least one energy source may be in optical communication with one or more beam splitters, which one or more beam splitters can split an energy beam from at least one light source into one or more beamlets (or beams) that yields at least the first energy beam.
One or more beam splitters may be selected from the group consisting of prism, glass sheet, plastic sheet, mirror, dielectric mirror, metal-coated mirror, partially reflecting mirror, pellicles, micro-optic beam splitters, waveguide beam splitters, beam splitter cubes, fiber-optic beam splitter, and any combination thereof. One or more optical wedges may be in optical communication with one or more beam splitters, which one or more optical wedges form at least the first light beam. Such optical wedges can form at least the first light beam in a uniform orientation. The one or more beamlets may pass through one or more focusing lenses prior to passing through at least one or more optical wedges. Such beamlets may have an elliptical polarization. The one or more beamlets may comprise a minor axis of at least about 0.5 millimeters (mm), at least about 1 mm, at least about 2 mm, at least about 3 mm, at least about 4 mm, at least about 5 mm, at least about 6 mm, at least about 7 mm, at least about 8 mm, at least about 9 mm, at least about 10 mm, or at least about 15 mm. The one or more beamlets may also comprise a major axis of at least about 5 mm, at least about 10 mm, at least about 15 mm, at least about 20 mm, at least about 25 mm, at least about 30 mm, at least about 35 mm, at least about 40 mm, at least about 45 mm, or at least about 50 mm. Such light beams can cover at least a portion of at least one filament material. The one or more focusing lenses may be used to adjust a ratio of the minor axis to the major axis of the one or more beamlets.
Optical wedges may alter the path of the beam from vertical to any angle for uniform heating of the filament material. The one or more optical wedges can also direct an optical path of at least the first light beam of a given location, direction, or angle normal to the substrate and/or along the substrate among one or more locations, directions, or angles. Such a direction of one or more optical wedges can allow for control of the heat from the light beam along the at least one filament material.
The one or more optical wedges can be used in combination with one or more of dispersive prism, reflective prism, beam-splitting prism, polarizing prism, or deflecting prisms. Dispersive prisms may be used to break up light into its constituent spectral colors because the refractive index depends on frequency. Examples of dispersive prisms include Triangular prism, Abbe prism, Pellin-Broca prism, Amici prism, Compound prism, or Grism prism. Reflective prisms can be used to reflect light, in order to flip, invert, rotate, deviate or displace the light beam. Examples of reflective prisms include Porro prism, Porro-Abbe prism, Amici roof prism, Pentaprism, Roof Pentaprism, Abbe-Koenig prism, Schmidt-Pechan prism, Bauernfeind prism, Dove prism, or Retroreflector prism. Some reflective prisms may be used for splitting a beam into two or more beams. Beam-splitting prisms may be a beam splitter cube or a dichronic prism. Polarizing prisms can split a beam of light into components of varying polarization. Examples of polarizing prisms may be Nicol prism, Wollaston prism, Nomarski prism, Rochon prism, Senarmont prism, Glan-Foucault prism, Glan-Taylor prism, or Glan-Thompson prism. Deflecting prisms may be one or more of a Risley prism pair, Rhomboid prisms, or Deck prisms. Wedge prisms may be used to deflect a beam of light by a fixed angle. A pair of such prisms can be used for beam steering; by rotating the prisms the beam can be deflected into any desired angle. The deflecting prism may be a Risley prism pair. Two wedge prisms can also be used as an anamorphic pair to change the shape of a beam. For example, this may be used to generate a round beam from the elliptical output of a laser diode.
One or more optical wedges can have a refractive index of at least about 0.5, at least about 1, at least about 1.1, at least about 1.2, at least about 1.3, at least about 1.4, at least about 1.5, at least about 1.6, at least about 1.7, at least about 1.8, at least about 1.9, at least about 2.5, at least about 3, at least about 4, or at least about 5. Such optical wedges can have a diameter of at most about 0.1 inches (in), at most about 0.2 in, at most about 0.3 in, at most about 0.4 in, at most about 0.5 in, at most about 0.6 in, at most about 0.7 in, at most about 0.8 in, at most about 0.9 in, at most about 1 in, at most about 2 in, at most about 3 in, at most about 4 in, or at most about 5 in.
At least the first energy beam may be incident on at least one filament material and on the substrate. Such energy beams may be directed along a given angle among one or more angles relative to the dispensing route of at least one filament material. The one or more optical wedges can comprise a first optical wedge and a second optical wedge. The first optical wedge may be the top wedge and the second optical wedge may be the bottom wedge. Through choosing the wedge angle, the energy beams can be made incident on the filament at an angle to the plane of the substrate. By rotating the bottom optical wedge, the incident angle can be varied. By rotating both the optical wedges, the angle of the line beam in the plane of deposition can be varied. For example, the first optical wedge may rotate relative to the second optical wedge to change the direction of at least the first light beam. The first optical wedge and the second optical wedge can be angled in the same direction to increase an angle of at least the first energy beam with respect to a reference. The first optical wedge and the second optical wedge may rotate in opposite directions to allow the at least the first energy beam to pass vertically through the one or more optical wedges. When altering an angle of incidence of the first optical wedge and the second optical wedge, or when altering a direction of the major axis of at least the first energy beam relative to the substrate or at least one filament material, the fluence of at least the first light beam may be altered. The fluence may be a stream of particles crossing a unit area. The fluence may be expressed as the number of particles per second. As a result, such light beams may heat at least one filament material without melting a deposited portion of the at least one filament material. In some instances, at least the first energy beam can heat and melt a deposited portion of at least one filament material at a given location among one or more locations.
At least one filament material may be directed to a compaction unit. Such filament material may be compacted by the compaction unit to form at least one compacted filament material. The compaction unit may comprise a rigid body, one or more idler rollers, at least one freely suspended roller, a coolant unit, or any combination thereof. The at least one freely suspended roller may be a compaction roller. The rigid body and one or more idler rollers may secure the at least one freely suspended roller. Such freely suspended rollers may have a diameter of at most about 1 millimeter (mm), at most about 2 mm, at most about 3 mm, at most about 4 mm, at most about 5 mm, at most about 6 mm, at most about 7 mm, at most about 8 mm, at most about 9 mm, at most about 10 mm, or at most about 15 mm. The coolant may be used to cool the compaction unit so the at least one filament material does not stick to the roller and adheres only to the previously deposited layer of the three-dimensional object.
The system for printing at least a portion of the 3D object may further comprise one or more cooling components. Such cooling components may be in proximity to the deposited filament material layer. Such cooling components can be located between the deposited filament material layer and the energy source. Such cooling components may be movable to or from a location that may be positioned between the filament material and the energy source. Such cooling components may assist in the process of cooling of the fused portion of the filament material layer. Such cooling components may also assist in the cooling of the filament material layer remainder that did not fuse to subsequently form at least a portion of the 3D object. Such cooling components can assist in the cooling of the at least a portion of the 3D object and the remainder at considerably the same rate. Such cooling components may be separated from the filament material layer and/or from the substrate by a gap. The gap may comprise a gas. The gap can have a cross-section that is at most about 0.1 mm, at most about 0.5 mm, at most about 1 mm, at most about 5 mm, or at most about 10 mm. The gap can be adjustable. The controller may be operatively connected to such cooling components and may be able to adjust the gap distance from the substrate. Such cooling components can track an energy that may be applied to the portion of the filament material layer by the energy source. Such cooling components may comprise a heat sink. Such cooling components may be a cooling fan. The controller may be operatively coupled to such cooling components and controls the tracing of such cooling components. Such cooling components may include at least one opening though which at least one energy beam from the energy source can be directed to the portion of the filament layer. The system for printing at least a portion of the 3D object can further comprise an additional energy source that provides energy to a remainder of the filament material layer that did not fuse to subsequently form at least a portion of the 3D object.
During printing of the three-dimensional object, certain parameters may be critical to printing high quality parts. One or more sensors can be used to measure one or more temperature(s) along at least one filament material. Such sensors can control intensities, positions, and/or angles of at least the first energy beam. The one or more sensors may be an optical pyrometer. Optical pyrometers may be aimed the substrate to detect the temperature of the at least one filament materials as they are deposited. Optical pyrometers may be aimed at the nip points and one or more points before and/or after the compaction unit to detect the temperature of the at least one filament materials as they are deposited. The temperature may vary from region to region of the filament material layer. Factors that affect temperature variance can include variable heater irradiance, variations in absorptivity of the composition, substrate temperature, filament material temperature, unfused filament material temperature, and the use of modifiers and additives. Accordingly, image and temperature measurement inputs based upon layer temperature patterns captured by the one or more sensors may be used. The real time temperature inputs and the sintering model may be factors determining an energy requirement pattern for any one or more subsequent layers.
Additionally, the system may comprise a real time simulation program, a sample as shown in
Other parameters critical to printing high quality parts can include substrate temperature, melt zone temperature, as-built geometry, surface roughness and texture and density. Other critical visible or non-visible metrics include characterization of chemistry, bonding or adhesion strength. Measuring one or more structural or internal properties of the part can comprise one or more methods selected from the group consisting of scattered and reflected or absorbed radiation, x-ray imaging, sound waves, scatterometry techniques, ultrasonic techniques, X-ray Photoelectron Spectroscopy (XPS), Four Transform Infrared Spectroscopy (FTIR), Raman Spectroscopy, Laser-Microprobe Mass Spectrometry (LMMS), and any combination thereof. Specific metrology beneficial to the end goals of characterizing the critical process parameters can be used. This in-situ metrology coupled with fast processing of data can enable open or closed loop control of the manufacturing process. Sensors appropriate to the key parameters of interest can be selected and utilized during the part printing process. The sensors may also comprise a camera for detecting light in the infrared or visible portion of the electromagnetic spectrum. Sensors such as IR cameras may be used to measure temperature fields. An image processing algorithm may be used to evaluate data generated by one or more sensors, to extract one or more structural or internal properties of the part. Visual (e.g., high magnification) microscopy from digital camera(s) can be used with proper software processing to detect voids, defects, and surface roughness. In order to utilize this technique, potentially large quantities of data may need to be interrogated using image processing algorithms in order to extract features of interest. Scatterometry techniques may be adapted to provide roughness or other data.
Ultrasonic techniques can be used to measure solid density and fiber and particle density which in turn may be useful in characterizing bond strength and fiber dispersion. The characterization can affect material strength. Ultrasonic techniques can also be used to measure thickness of features. Chemical bonding characterization, which may be useful for understanding fiber and/or matrix adhesion and layer-to-layer bonding, can be performed by multiple techniques such as XPS (X-ray Photoelectron Spectroscopy), FTIR (Four Transform Infrared Spectroscopy) and Raman Spectroscopy and Laser-Microprobe Mass Spectrometry (LMMS). One or more of these techniques may be utilized as part of the in-situ metrology for 3D printing. Ex-situ techniques may also be utilized in order to help provide appropriate calibration data for the in-situ techniques.
Sensors may be positioned on the robot end-effector of the three-dimensional printer in order to provide a sensor moving along with the deposited material. A robot end-effector may be a device positioned at the end of a robotic arm. The robot end-effector may be programmed to interact with its surrounding environment. Sensors may be also located at other various positions. The positions can be on-board the robot, on the effector, or deployed in the environment. Sensors may be in communication with the system. The system can further comprise one or more processors, a communication unit, memory, power supply, and storage. The communications unit can comprise an input and an output. The communication unit can be wired or wireless. The sensor measurements may or may not be stored in a database, and may or may not be used in future simulation and optimization operations. In-situ measurements may also be made using alternative methods with sensors in a cell but not directly attached to the robot end-effector.
In another aspect, the present disclosure provides for method for printing at least a portion of a three-dimensional (3D) object. At least one filament material may be directed from a source of at least one filament material towards a substrate that is configured to support the 3D object, thereby depositing a first layer corresponding to a portion of the 3D object adjacent to the substrate, which first layer is deposited in accordance with the model of the 3D object. At least one filament material from the source may be deposited to an opening. Such filament material may then be directed from the opening towards the substrate. At least a first energy beam from at least one energy source may be used to melt at least a portion of the first layer. A second layer of at least a portion of the 3D object may be deposited, which second layer is deposited in accordance with the model of the 3D object, thereby generating at least a portion of the 3D object. In some embodiments, such method may be repeated one or more times. Prior to directing at least one filament material from a source of the at least one filament material towards a substrate that is configured to support the 3D object, thereby depositing a first layer corresponding to a portion of the 3D object adjacent to the substrate, a model of the 3D object may be received in computer memory. In some cases, fused deposition modeling may be performed when printing the 3D object. In other cases, the 3D object may be printed with extrusion. In some cases, the 3D object may be printed without extrusion.
The layered structure can comprise substantially repetitive layers. The layers may have an average layer size of at least about 0.5 micrometers (μm), 1 μm, 5 μm, 10 μm, 20 μm, 30 μm, 40 μm, 50 μm, 60 μm, 70 μm, 80 μm, 90 μm, 100 μm, 150 μm, 200 μm, 250 μm, 300 μm, 350 μm, 400 μm, 450 μm, 500 μm, 1 mm, 25 mm, 50 mm, 100 mm, 500 mm, or 1 m. The layers may have an average layer size of at most about 50 m, 1 m, 500 mm, 100 mm, 50 mm, 25 mm, 1 mm, 500 μm, 450 μm, 400 μm, 350 μm, 300 μm, 250 μm, 200 μm, 150 μm, 100 μm, 90 μm, 80 μm, 70 μm, 60 μm, 50 μm, 40 μm, 30 μm, 20 μm, or 10 μm. The layers may have an average layer size of any value between the aforementioned values of layer size. For example, the layers may have an average layer size from about 0.5 μm to about 500 mm, from about 15 μm to about 100 μm, from about 5 μm to about 300 μm, from about 20 μm to about 90 μm, or from about 10 μm to about 70 μm. The layered structure can be indicative of layered deposition. The layered structure can be indicative of solidification of melt pools formed during a three-dimensional printing process. The structure indicative of a three dimensional printing process can comprise substantially repetitive variation comprising: variation in grain orientation, variation in material density, variation in the degree of compound segregation to grain boundaries, variation in the degree of element segregation to grain boundaries, variation in material phase, variation in metallurgical phase, variation in material porosity, variation in crystal phase, or variation in crystal structure. The melt pools may be indicative of an additive manufacturing process comprising stereolithography (SLA), selective laser melting (SLM), selective laser sintering (SLS), digital light processing (DLP), electron beam melting (EBM), laminated object manufacturing (LOM), binder jetting (BM), material jetting/wax casting (MJ), direct metal laser sintering (DMLS), or fused deposition modeling (FDM). The melt pools may be indicative of an additive manufacturing process comprising selective energy melting.
The source of at least one filament material may be configured to supply at least one filament material for generating the three-dimensional object. The at least one filament material may be a composite material, such as a continuous fiber composite. The filament material may be nano milled, short, long, continuous, or a combination thereof. The continuous fiber composite may be a continuous core reinforced filament. The continuous core reinforced filament can comprise a towpreg that is substantially void free and includes a polymer that coats or impregnates an internal continuous core. Depending upon the particular embodiment, the core may be a solid core, or it may be a multi-strand core comprising multiple strands. The continuous fiber composite may be selected from the group consisting of glass, carbon, aramid, cotton, silicon carbide, polymer, wool, metal, and any combination thereof.
The filament material may incorporate one or more additional materials, such as resins and polymers. For example, appropriate resins and polymers include, but are not limited to, acrylonitrile butadiene styrene (ABS), epoxy, vinyl, nylon, polyetherimide (PEI), Polyaryletherketone (PAEK), Polyether ether ketone (PEEK), Polyactic Acid (PLA), Liquid Crystal Polymer, polyamide, polyimide, polyphenylene sulfide, polyphenylsulfone, polysulfone, polyether sulfone, polyethylenimine, polytetrafluoroethylene, polyvinylidene, and various other thermoplastics. The core of the continuous fiber composite may be selected to provide any desired property. Appropriate core fiber or strands include those materials which impart a desired property, such as structural, conductive (electrically and/or thermally), insulative (electrically and/or thermally), optical and/or fluidic transport. Such materials include, but are not limited to, carbon fibers, aramid fibers, fiberglass, metals (such as copper, silver, gold, tin, and steel), optical fibers, and flexible tubes. The core fiber or strands may be provided in any appropriate size. Further, multiple types of continuous cores may be used in a single continuous core reinforced filament to provide multiple functionalities such as electrical and optical properties. A single material may be used to provide multiple properties for the core reinforced filament. For example, a steel core may be used to provide both structural properties as well as electrical conductivity properties.
Alternatively, the filament material may comprise metal particles infused into a binder matrix. The metal particles may be metal powder. The binder matrix may include resins or polymers. Additionally, such binder matrix can be used a delivery device for the metal particles. Once the filament material is deposited onto the base, one or more energy sources can heat and melt the binder matrix, leaving the metal particles to melt and fuse into larger metal particles. Such energy sources may be without limitation, by an electromagnetic radiation source (e.g., laser), a microwave source, a resistive heating source, an infrared energy source, a UV energy source, a hot fluid, a chemical reaction, a plasma source, a microwave source, an electromagnetic source, or an electron beam. Resistive heating may be joule heating. A source for resistive heating may be a power supply. The at least one filament material may be a metal filament. The at least one filament material may be a metal filament composite. The deposited at least one filament material may be subjected to resistive heating upon flow of an electrical current through the at least one filament material. The resistive heating may be sufficient to melt at least a portion of the deposited at least one filament material. The at least one filament material may be an electrode. The substrate may be another electrode.
The one or more energy sources may also provide localized heating to create a “melt pool” in the current layer or segment of the deposited build material prior to depositing the next segment or layer. The melt pool can increase diffusion and mixing of the build material between adjacent layers (e.g., across a direction orthogonal to the layers) as compared to other methods which deposit a subsequent layer of build material on top of a layer of build material that is below its melting temperature.
The increased diffusion and mixing resulting from the melt pool may increase the chemical chain linkage, bonding, and chemical chain interactions between the two layers. This can result in increasing the build-material adhesion in the Z direction, thereby enhancing mechanical, thermal, and electrical properties of the three-dimensional object. The melt pool can also reduce the void space and porosity in the build object. Among other benefits, this decrease in porosity may also contribute to the aforementioned improvement in mechanical, thermal, and electrical properties.
The at least one filament material may have a cross sectional shape selected from the group consisting of circle, ellipse, parabola, hyperbola, convex polygon, concave polygon, cyclic polygon, equilateral polygon, equiangular polygon, regular convex polygon, regular star polygon, tape-like geometry, and any combination thereof. Such filament material can have a diameter of at most about 0.1 millimeters (mm), at most about 0.2 mm, at most about 0.3 mm, at most about 0.4 mm, at most about 0.5 mm, at most about 0.6 mm, at most about 0.7 mm, at most about 0.8 mm, at most about 0.9 mm, at most about 1 mm, at most about 2 mm, at most about 3 mm, at most about 4 mm, at most about 5 mm, at most about 10 mm, or at most about 20 mm.
Various modifiers within the layers themselves may be used which are selectively printed onto specific regions of the 3D object in order to impart various desirable mechanical, chemical, magnetic, electrical or other properties to the 3D object. Such modifiers may be selected from the group consisting of thermal conductors and insulators, dielectric promoters, electrical conductors and insulators, locally-contained heater traces for multi-zone temperature control, batteries, and sensors. At least one print head can be may be used for printing such modifiers. As desired, such modifiers can be printed before at least a first energy beam is directed onto at least a portion of the first layer and/or second layer. Alternatively, such modifiers may be printed over a layer that has been melted, before filament material for the next layer is deposited.
For example, when printing a polyimide part from commercially available a filament comprising polyimide, an array of electrically conductive traces may be assimilated as an antenna to selectively absorb radiofrequency (RF) radiation within a specific and predetermined frequency range. The 3D object CAD model and software can designate as a sub-part the layer(s) that comprise the traces for modified properties (high electrical conductivity). Alternatively, if these portions of the layer entail different levels of energy for inducing fusion, compared to other regions having only the primary material, the CAD model and design of the 3D object may be adjusted accordingly.
After deposition of a first layer and/or a second layer of at least a portion of the 3D object, and before fusion is induced, the filament material may be preheated to a temperature sufficient to reduce undesirable shrinkage and/or to minimize the laser energy needed to melt the next layer. For example, the preheating may be accomplished using the infrared heater attached to substrate or through other apparatuses of directing thermal energy within an enclosed space around the substrate. Alternatively, the preheating can be accomplished using energy beam melting by defocusing the energy beam and rapidly scanning it over the deposited first layer and or second layer of at least a portion of the 3D object.
At least a first energy beam from at least one energy source may be used to selectively heat and/or melt at least a portion of the first layer and/or the second layer, thereby forming at least a portion of the 3D object. The energy source may be selected from the group consisting of an electromagnetic radiation source (e.g., laser), a microwave source, a resistive heating source, an infrared energy source, a UV energy source, a hot fluid, a chemical reaction, a plasma source, a microwave source, an electromagnetic source, an electron beam, or any combination thereof. Resistive heating may be joule heating. A source for resistive heating may be a power supply. The at least one filament material may be a metal filament. The at least one filament material may be a metal filament composite. The deposited at least one filament material may be subjected to resistive heating upon flow of an electrical current through the at least one filament material. The resistive heating may be sufficient to melt at least a portion of the deposited at least one filament material. The at least one filament material may be an electrode. The substrate may be another electrode.
The energy source may be a function of the chemical composition of the build material, such as the build material's thermal conductivity, heat capacity, latent heat of fusion, melting point, and melt flow viscosity. The at least one energy source may be a laser. The laser may be selected from the group consisting of gas lasers, chemical lasers, dye lasers, metal-vapor lasers, solid-state lasers, semiconductor lasers, free electron laser, gas dynamic laser, nickel-like samarium laser, Raman laser, nuclear pump laser, and any combination thereof. Gas lasers may comprise one or more of helium-neon laser, argon laser, krypton laser, xenon ion laser, nitrogen laser, carbon dioxide laser, carbon monoxide laser, and excimer laser. Chemical lasers may be selected from the group consisting of hydrogen fluoride laser, deuterium fluoride laser, chemical oxygen-iodine laser, all gas-phase iodine laser, and any combination thereof. Metal-vapor lasers can comprise one or more of helium-cadmium, helium mercury, helium selenium, helium silver, strontium vapor laser, neon-copper, copper vapor laser, gold vapor laser, and manganese vapor laser. Solid-state lasers may be selected from the group consisting of ruby laser, neodymium-doped yttrium aluminium garnet laser, neodymium and chromium-doped yttrium aluminium garnet laser, erbium-doped yttrium aluminium garnet laser, neodymium-doped yttrium lithium fluoride laser, neodymium doped yttrium othovanadate laser, neodymium doped yttrium calcium oxoborate laser, neodymium glass laser, titanium sapphire laser, thulium yttrium aluminium garnet laser, ytterbium yttrium aluminium garnet laser, ytterbium:203 (glass or ceramics) laser, ytterbium doped glass laser (rod, plate/chip, and fiber), holmium yttrium aluminium garnet laser, chromium zinc selenium laser, cerium doped lithium strontium (or calcium) aluminum fluoride laser, Promethium 147 doped phosphate glass solid-state laser, chromium doped chrysoberyl (alexandrite) laser, erbium doped and erbium-ytterbium codoped glass lasers, trivalent uranium doped calcium fluoride solid-state laser, divalent samarium doped calcium fluoride laser, FARBE center laser, and any combination thereof. Semiconductor laser may comprise one or more of semiconductor laser diode laser, gallium nitride laser, indium gallium nitride laser, aluminium gallium indium phosphide laser, aluminium gallium arsenide laser, indium gallium arsenide phosphide laser, lead salt laser, vertical cavity surface emitting laser, quantum cascade laser, and hybrid silicon laser.
The melting temperature of the at least one filament material can be at least about 150 degrees Celsius (° C.), at least about 200° C., at least about 250° C., at least about 300° C., at least about 350° C., at least about 400° C., at least about 450° C. The sintering temperature can be at most about 150° C., at most about 200° C., at most about 250° C., at most about 300° C., at most about 350° C., at most about 400° C. The method may further comprise separating the remainder of the layer that did not fuse and solidify to form at least a portion of the three-dimensional object, from the portion.
The at least one energy beam from the energy source may be directed to the at least one portion of the 3D object adjacent to the substrate. Such energy beams may be sufficient to induce fusion of particles of the filament material within the desired cross-sectional geometry of the at least one portion of the 3D object. As the energy dissipates with cooling, atoms from neighboring particles may fuse together. The at least one energy beam results in the fusion of particles of filament material both within the same layer and in the previously formed and resolidified adjoining layer(s) such that fusion is induced between at least two adjacent layers of the part, such as between at least one filament material in a deposited unfused layer and a previously-fused adjacent layer. This process is then repeated over multiple cycles as each part layer is added, until the full 3D object is formed.
In some cases, to create a melt pool large enough to span the width of the filament material segment, multiple energy sources or a combination of energy sources may be required. When multiple energy sources are used, the energy sources may be the same energy source. Alternatively, the multiple energy sources may be different energy sources. The energy source(s) may be separate from the system for printing at least a portion of the 3D object. In other embodiments, the energy source(s) may be integrated with such system. For example, in one embodiment, a hot fluid (e.g., hot air) may be channeled through the deposition nozzle. Because the material filament can flow in the melt pool, features of the 3D object being built can be altered. The melt pool may be formed within the build object, such that a melt pool is not formed near the perimeters thereof. To accomplish this, the energy source may be turned off when the perimeters of the object are being built. In such embodiments, the geometrical tolerance of the build object may be maintained while the interior of the object has enhanced interlayer bonding. During printing, the filament material may be printed in the X, Y, and Z directions in one segment or layer.
The at least one energy source may be in optical communication with one or more beam splitters, which one or more beam splitters can split an energy beam from at least one light source into one or more beamlets that yields at least the first energy beam. The example optical system in
One or more beam splitters may be selected from the group consisting of prism, glass sheet, plastic sheet, mirror, dielectric mirror, metal-coated mirror, partially reflecting mirror, pellicles, micro-optic beam splitters, waveguide beam splitters, beam splitter cubes, fiber-optic beam splitter, and any combination thereof. One or more optical wedges may be in optical communication with one or more beam splitters, which one or more optical wedges form at least the first light beam. Such optical wedges can form at least the first light beam in a uniform orientation. The one or more beamlets may pass through one or more focusing lenses prior to passing through at least one or more optical wedges. Such beamlets may have an elliptical polarization. The one or more beamlets may comprise a minor axis of at least about 0.5 millimeters (mm), at least about 1 mm, at least about 2 mm, at least about 3 mm, at least about 4 mm, at least about 5 mm, at least about 6 mm, at least about 7 mm, at least about 8 mm, at least about 9 mm, at least about 10 mm, or at least about 15 mm. The one or more beamlets may also comprise a major axis of at least about 5 mm, at least about 10 mm, at least about 15 mm, at least about 20 mm, at least about 25 mm, at least about 30 mm, at least about 35 mm, at least about 40 mm, at least about 45 mm, or at least about 50 mm. Such energy beams can cover at least a portion of at least one filament material. The one or more focusing lenses may be used to adjust a ratio of the minor axis to the major axis of the one or more beamlets.
Optical wedges may alter the path of the beam from vertical to any angle for uniform heating of the filament material. The one or more optical wedges can also direct an optical path of at least the first light beam of a given location, direction, or angle normal to the substrate and/or along the substrate among one or more locations, directions, or angles. Such a direction of one or more optical wedges can allow for control of the heat from the light beam along the at least one filament material.
The one or more optical wedges can be used in combination with one or more of dispersive prism, reflective prism, beam-splitting prism, polarizing prism, or deflecting prisms. Dispersive prisms may be used to break up light into its constituent spectral colors because the refractive index depends on frequency. Examples of dispersive prisms include Triangular prism, Abbe prism, Pellin-Broca prism, Amici prism, Compound prism, or Grism prism. Reflective prisms can be used to reflect light, in order to flip, invert, rotate, deviate or displace the light beam. Examples of reflective prisms include Porro prism, Porro-Abbe prism, Amici roof prism, Pentaprism, Roof Pentaprism, Abbe-Koenig prism, Schmidt-Pechan prism, Bauernfeind prism, Dove prism, or Retroreflector prism. Some reflective prisms may be used for splitting a beam into two or more beams. Beam-splitting prisms may be a beam splitter cube or a dichronic prism. Polarizing prisms can split a beam of light into components of varying polarization. Examples of polarizing prisms may be Nicol prism, Wollaston prism, Nomarski prism, Rochon prism, Senarmont prism, Glan-Foucault prism, Glan-Taylor prism, or Glan-Thompson prism. Deflecting prisms may be one or more of a Risley prism pair, Rhomboid prisms, or Deck prisms. Wedge prisms may be used to deflect a beam of light by a fixed angle. A pair of such prisms can be used for beam steering; by rotating the prisms the beam can be deflected into any desired angle. The deflecting prism may be a Risley prism pair. Two wedge prisms can also be used as an anamorphic pair to change the shape of a beam. For example, this may be used to generate a round beam from the elliptical output of a laser diode.
One or more optical wedges can have a refractive index of at least about 0.5, at least about 1, at least about 1.1, at least about 1.2, at least about 1.3, at least about 1.4, at least about 1.5, at least about 1.6, at least about 1.7, at least about 1.8, at least about 1.9, at least about 2.5, at least about 3, at least about 4, or at least about 5. Such optical wedges can have a diameter of at most about 0.1 inches (in), at most about 0.2 in, at most about 0.3 in, at most about 0.4 in, at most about 0.5 in, at most about 0.6 in, at most about 0.7 in, at most about 0.8 in, at most about 0.9 in, at most about 1 in, at most about 2 in, at most about 3 in, at most about 4 in, or at most about 5 in.
At least the first energy beam may be incident on at least one filament material and on the substrate. Such energy beams may be directed along a given angle among one or more angles relative to the dispensing route of at least one filament material. The one or more optical wedges can comprise a first optical wedge and a second optical wedge. The first optical wedge may be the top wedge and the second optical wedge may be the bottom wedge. Through choosing the wedge angle, the energy beams can be made incident on the filament at an angle to the plane of the substrate. By rotating the bottom optical wedge, the incident angle can be varied. By rotating both the optical wedges, the angle of the line beam in the plane of deposition can be varied. For example, the first optical wedge may rotate relative to the second optical wedge to change the direction of at least the first light beam. The first optical wedge and the second optical wedge can be angled in the same direction to increase an angle of at least the first energy beam with respect to a reference. The energy beam may be a light beam. The first optical wedge and the second optical wedge may rotate in opposite directions to allow the at least the first energy beam to pass vertically through the one or more optical wedges. When altering an angle of incidence of the first optical wedge and the second optical wedge, or when altering a direction of the major axis of at least the first energy beam relative to the substrate or at least one filament material, the fluence of at least the first light beam may be altered. As a result, such light beams may heat at least one filament material without melting a deposited portion of the at least one filament material. In some instances, at least the first energy beam can heat and melt a deposited portion of at least one filament material at a given location among one or more locations.
At least one filament material may be directed to a compaction unit. Such filament material may be compacted by such a compaction unit to form at least one compacted filament material. The compaction unit may comprise a rigid body, one or more idler rollers, at least one freely suspended roller, a coolant unit, or any combination thereof. The at least one freely suspended roller may be a compaction roller. The rigid body and one or more idler rollers may secure the at least one freely suspended roller. Such freely suspended rollers may have a diameter of at most about 1 mm, at most about 2 mm, at most about 3 mm, at most about 4 mm, at most about 5 mm, at most about 6 mm, at most about 7 mm, at most about 8 mm, at most about 9 mm, at most about 10 mm, or at most about 15 mm. The coolant may be used to cool the compaction unit so the at least one filament material does not stick to the roller and adheres only to the previously deposited layer of the three-dimensional object.
The system for printing at least a portion of the 3D object may further comprise one or more cooling components. Such cooling components may be in proximity to the deposited filament material layer. Such cooling components can be located between the deposited filament material layer and the energy source. Such cooling components may be movable to or from a location that may be positioned between the filament material and the energy source. Such cooling components may assist in the process of cooling of the fused portion of the filament material layer. Such cooling components may also assist in the cooling of the filament material layer remainder that did not fuse to subsequently form at least a portion of the 3D object. Such cooling components can assist in the cooling of the at least a portion of the 3D object and the remainder at considerably the same rate. Such cooling components may be separated from the filament material layer and/or from the substrate by a gap. The gap may comprise a gas. The gap can have a cross-section that is at most about 0.1 mm, at most about 0.5 mm, at most about 1 mm, at most about 5 mm, or at most about 10 mm. The gap can be adjustable. The controller may be operatively connected to such cooling components and may be able to adjust the gap distance from the substrate. Such cooling components can track an energy that may be applied to the portion of the filament material layer by the energy source. Such cooling components may comprise a heat sink. Such cooling components may be a cooling fan. The controller may be operatively coupled to such cooling components and controls the tracing of such cooling components. Such cooling components may include at least one opening though which at least one energy beam from the energy source can be directed to the portion of the filament layer. The system for printing at least a portion of the 3D object can further comprise an additional energy source that provides energy to a remainder of the filament material layer that did not fuse to subsequently form at least a portion of the 3D object.
During printing of the three-dimensional object, certain parameters may be critical to printing high quality parts. One or more sensors can be used to measure one or more temperature(s) along at least one filament material. Such sensors can control intensities, positions, and/or angles of at least the first energy beam. The one or more sensors may be an optical pyrometer. Optical pyrometers may be aimed the substrate to detect the temperature of the at least one filament materials as they are deposited. Optical pyrometers may be aimed at the nip points and one or more points before and/or after the compaction unit to detect the temperature of the at least one filament materials as they are deposited. The temperature may vary from region to region of the filament material layer. Factors that affect temperature variance can include variable heater irradiance, variations in absorptivity of the composition, substrate temperature, filament material temperature, unfused filament material temperature, and the use of modifiers and additives. Accordingly, image and temperature measurement inputs based upon layer temperature patterns captured by the one or more sensors may be used. The real time temperature inputs and the sintering model may be factors determining an energy requirement pattern for any one or more subsequent layers.
Additionally, the system may comprise a real time simulation program, a sample as shown in
Other parameters critical to printing high quality parts can include substrate temperature, melt zone temperature, as-built geometry, surface roughness and texture and density. Other critical visible or non-visible metrics include characterization of chemistry, bonding or adhesion strength. Measuring one or more structural or internal properties of the part can comprise one or more methods selected from the group consisting of scattered and reflected or absorbed radiation, x-ray imaging, sound waves, scatterometry techniques, ultrasonic techniques, X-ray Photoelectron Spectroscopy (XPS), Four Transform Infrared Spectroscopy (FTIR), Raman Spectroscopy, Laser-Microprobe Mass Spectrometry (LMMS), and any combination thereof. Specific metrology beneficial to the end goals of characterizing the critical process parameters can be used. This in-situ metrology coupled with fast processing of data can enable open or closed loop control of the manufacturing process. Sensors appropriate to the key parameters of interest can be selected and utilized during the part printing process. The sensors may also comprise a camera for detecting light in the infrared or visible portion of the electromagnetic spectrum. Sensors such as IR cameras may be used to measure temperature fields. An image processing algorithm may be used to evaluate data generated by one or more sensors, to extract one or more structural or internal properties of the part. Visual (e.g., high magnification) microscopy from digital camera(s) can be used with proper software processing to detect voids, defects, and surface roughness. In order to utilize this technique, potentially large quantities of data may need to be interrogated using image processing algorithms in order to extract features of interest. Scatterometry techniques may be adapted to provide roughness or other data.
Ultrasonic techniques can be used to measure solid density and fiber and particle density which in turn may be useful in characterizing bond strength and fiber dispersion. The characterization can affect material strength. Ultrasonic techniques can also be used to measure thickness of features. Chemical bonding characterization, which may be useful for understanding fiber and/or matrix adhesion and layer-to-layer bonding, can be performed by multiple techniques such as XPS (X-ray Photoelectron Spectroscopy), FTIR (Four Transform Infrared Spectroscopy) and Raman Spectroscopy and Laser-Microprobe Mass Spectrometry (LMMS). One or more of these techniques may be utilized as part of the in-situ metrology for 3D printing. Ex-situ techniques may also be utilized in order to help provide appropriate calibration data for the in-situ techniques.
Sensors may be positioned on the robot end-effector of the three-dimensional printer in order to provide a sensor moving along with the deposited material. A robot end-effector may be a device positioned at the end of a robotic arm. The robot end-effector may be programmed to interact with its surrounding environment. Sensors may be also located at other various positions. The positions can be on-board the robot, on the effector, or deployed in the environment. Sensors may be in communication with the system. The system can further comprise one or more processors, a communication unit, memory, power supply, and storage. The communications unit can comprise an input and an output. The communication unit can be wired or wireless. The sensor measurements may or may not be stored in a database, and may or may not be used in future simulation and optimization operations. In-situ measurements may also be made using alternative methods with sensors in a cell but not directly attached to the robot end-effector.
In another aspect, the present disclosure provides a system for printing at least a portion of a three-dimensional (3D) object. The system may comprise a source of at least one filament material that is configured to supply at least one filament material for generating the 3D object. The system may comprise a substrate for supporting at least a portion of the 3D object. The system may additionally comprise at least one energy source configured to deliver at least a first energy beam. The system can comprise a controller operatively coupled to the at least one energy source, wherein the controller is programmed to (i) receive, in computer memory, a model of the 3D object, (ii) subsequent to receiving the model of the 3D object, direct the at least one filament material from the source of the at least one filament material towards the substrate that is configured to support the 3D object, thereby depositing a first layer corresponding to a portion of the 3D object adjacent to the substrate, which first layer is deposited in accordance with the model of the 3D object, (iii) deposit a second layer corresponding to at least a portion of the 3D object, which second layer is deposited in accordance with the model of the 3D object, and (iv) use at least a first energy beam from at least one energy source to selectively melt at least a portion of the first layer and/or the second layer, thereby forming at least a portion of the 3D object.
In some cases, the controller may be programmed to perform fused deposition modeling when printing the 3D object. In other cases, the controller may be programmed to print the 3D object with extrusion. In some cases, the controller may be programmed to print the 3D object without extrusion. The controller can be further programmed to deposit one or more additional layers adjacent to the first layer prior to depositing the second layer. The system may further comprise an opening for (i) receiving at least one filament material, and (ii) directing at least one filament material towards the substrate.
The layered structure can comprise substantially repetitive layers. The layers may have an average layer size of at least about 0.01 micrometers (μm), 0.1 μm, 0.5 μm, 1 μm, 5 μm, 10 μm, 20 μm, 30 μm, 40 μm, 50 μm, 60 μm, 70 μm, 80 μm, 90 μm, 100 μm, 150 μm, 200 μm, 250 μm, 300 μm, 350 μm, 400 μm, 450 μm, 500 μm, 1 mm, 25 mm, 50 mm, 100 mm, 500 mm, or 1 m. The layers may have an average layer size of at most about 50 m, 1 m, 500 mm, 100 mm, 50 mm, 25 mm, 1 mm, 500 μm, 450 μm, 400 μm, 350 μm, 300 μm, 250 μm, 200 μm, 150 μm, 100 μm, 90 μm, 80 μm, 70 μm, 60 μm, 50 μm, 40 μm, 30 μm, 20 μm, or 10 μm. The layers may have an average layer size of any value between the aforementioned values of layer size. For example, the layers may have an average layer size from about 0.5 μm to about 500 mm, from about 15 μm to about 100 μm, from about 5 μm to about 300 μm, from about 20 μm to about 90 μm, or from about 10 μm to about 70 μm. The layered structure can be indicative of layered deposition. The layered structure can be indicative of solidification of melt pools formed during a three-dimensional printing process. The structure indicative of a three dimensional printing process can comprise substantially repetitive variation comprising: variation in grain orientation, variation in material density, variation in the degree of compound segregation to grain boundaries, variation in the degree of element segregation to grain boundaries, variation in material phase, variation in metallurgical phase, variation in material porosity, variation in crystal phase, or variation in crystal structure. The melt pools may be indicative of an additive manufacturing process comprising stereolithography (SLA), selective laser melting (SLM), selective laser sintering (SLS), digital light processing (DLP), electron beam melting (EBM), laminated object manufacturing (LOM), binder jetting (BM), material jetting/wax casting (MJ), direct metal laser sintering (DMLS), or fused deposition modeling (FDM). The melt pools may be indicative of an additive manufacturing process comprising selective energy melting.
The source of at least one filament material may be configured to supply at least one filament material for generating the three-dimensional object. The at least one filament material may be stored on one or more spools or cartridges. The spools and/or cartridges may be replaceable. The at least one filament material may be a composite material, such as a continuous fiber composite. The filament material may be nano milled, short, long, continuous, or a combination thereof. The continuous fiber composite may be a continuous core reinforced filament. The continuous core reinforced filament can comprise a towpreg that is substantially void free and includes a polymer that coats or impregnates an internal continuous core. Depending upon the particular embodiment, the core may be a solid core or it may be a multi-strand core comprising multiple strands. The continuous fiber composite may be selected from the group consisting of glass, carbon, aramid, cotton, silicon carbide, polymer, wool, metal, and any combination thereof.
The filament material may incorporate one or more additional materials, such as resins and polymers. For example, appropriate resins and polymers include, but are not limited to, acrylonitrile butadiene styrene (ABS), epoxy, vinyl, nylon, polyetherimide (PEI), Polyaryletherketone (PAEK), Polyether ether ketone (PEEK), Polyactic Acid (PLA), Liquid Crystal Polymer, polyamide, polyimide, polyphenylene sulfide, polyphenylsulfone, polysulfone, polyether sulfone, polyethylenimine, polytetrafluoroethylene, polyvinylidene, and various other thermoplastics. The core of the continuous fiber composite may be selected to provide any desired property. Appropriate core fiber or strands include those materials which impart a desired property, such as structural, conductive (electrically and/or thermally), insulative (electrically and/or thermally), optical and/or fluidic transport. Such materials include, but are not limited to, carbon fibers, aramid fibers, fiberglass, metals (such as copper, silver, gold, tin, and steel), optical fibers, and flexible tubes. The core fiber or strands may be provided in any appropriate size. Further, multiple types of continuous cores may be used in a single continuous core reinforced filament to provide multiple functionalities such as electrical and optical properties. A single material may be used to provide multiple properties for the core reinforced filament. For example, a steel core may be used to provide both structural properties as well as electrical conductivity properties.
Alternatively, the filament material may comprise metal particles infused into a binder matrix. The metal particles may be metal powder. The binder matrix may include resins or polymers. Additionally, such binder matrix can be used a delivery device for the metal particles. Once the filament material is deposited onto the base, one or more energy sources can heat and melt the binder matrix, leaving the metal particles to melt and fuse into larger metal particles. Such energy sources may be without limitation, by an electromagnetic radiation source (e.g., laser), a microwave source, a resistive heating source, an infrared energy source, a UV energy source, a hot fluid, a chemical reaction, a plasma source, a microwave source, an electromagnetic source, or an electron beam. Resistive heating may be joule heating. A source for resistive heating may be a power supply. The at least one filament material may be a metal filament. The at least one filament material may be a metal filament composite. The deposited at least one filament material may be subjected to resistive heating upon flow of an electrical current through the at least one filament material. The resistive heating may be sufficient to melt at least a portion of the deposited at least one filament material. The at least one filament material may be an electrode. The substrate may be another electrode.
The one or more energy sources may also provide localized heating to create a “melt pool” in the current layer or segment of the deposited build material prior to depositing the next segment or layer. The melt pool can increase diffusion and mixing of the build material between adjacent layers (e.g., across a direction orthogonal to the layers) as compared to other methods which deposit a subsequent layer of build material on top of a layer of build material that is below its melting temperature.
The hot fluid can have a temperature greater than 25 degrees Celsius (° C.), or greater than or equal to about 40° C., 50° C., 60° C., 70° C., 80° C., 90° C., 100° C., 150° C., 200° C., 250° C., 300° C., 350° C., 400° C., 450° C., 500° C., or higher. The hot fluid may have a temperature that is selected to soften or melt a material used to print an object. The hot fluid may have a temperature that is at or above a melting point or glass transition point of a polymeric material. The hot fluid can be a gas or a liquid. In some examples, the hot fluid is air.
The increased diffusion and mixing resulting from the melt pool may increase the chemical chain linkage, bonding, and chemical chain interactions between the two layers. This can result in increasing the build-material adhesion in the Z direction, thereby enhancing mechanical, thermal, and electrical properties of the three-dimensional object. The melt pool can also reduce the void space and porosity in the build object. Among other benefits, this decrease in porosity may also contribute to the aforementioned improvement in mechanical, thermal, and electrical properties.
The at least one filament material may have a cross sectional shape selected from the group consisting of circle, ellipse, parabola, hyperbola, convex polygon, concave polygon, cyclic polygon, equilateral polygon, equiangular polygon, regular convex polygon, regular star polygon, tape-like geometry, and any combination thereof. Such filament material can have a diameter of at most about 0.1 millimeters (mm), at most about 0.2 mm, at most about 0.3 mm, at most about 0.4 mm, at most about 0.5 mm, at most about 0.6 mm, at most about 0.7 mm, at most about 0.8 mm, at most about 0.9 mm, at most about 1 mm, at most about 2 mm, at most about 3 mm, at most about 4 mm, at most about 5 mm, at most about 10 mm, or at most about 20 mm.
Various modifiers within the layers themselves may be used which are selectively printed onto specific regions of the 3D object in order to impart various desirable mechanical, chemical, magnetic, electrical or other properties to the 3D object. Such modifiers may be selected from the group consisting of thermal conductors and insulators, dielectric promoters, electrical conductors and insulators, locally-contained heater traces for multi-zone temperature control, batteries, and sensors. At least one print head can be may be used for printing such modifiers. As desired, such modifiers can be printed before at least a first energy beam is directed onto at least a portion of the first layer and/or second layer. Alternatively, such modifiers may be printed over a layer that has been melted, before filament material for the next layer is deposited.
For example, when printing a polyimide part from commercially available a filament comprising polyimide, an array of electrically conductive traces may be assimilated as an antenna to selectively absorb radiofrequency (RF) radiation within a specific and predetermined frequency range. The 3D object CAD model and software can designate as a sub-part the layer(s) that comprise the traces for modified properties (high electrical conductivity). Alternatively, if these portions of the layer entail different levels of energy for inducing fusion, compared to other regions having only the primary material, the CAD model and design of the 3D object may be adjusted accordingly.
The system for printing at least a portion of a three-dimensional object may comprise at least one print head. The at least one print head may comprise one or more dies for extrusion. The at least one print head also deposit printed material without extrusion.
The system for printing at least a portion of a three-dimensional object may comprise a build plate form. The system may also comprise a substrate. The substrate may be able to withstand high temperatures. The substrate may have high thermal tolerances, and able to withstand high temperatures, such as at least about 50 degrees Celsius (° C.), at least about 100° C., at least about 150° C., at least about 200° C., at least about 250° C., at least about 300° C., at least about 350° C., or at least about 400° C.
The substrate may be a non-removable. The substrate may be a removable plate secured over the build platform. In an embodiment, guiding legs/rails may be used to slide the removable plate into multiple grooves and multiple set screws and fasteners to secure the plate onto the build platform. In another embodiment, the spring/latch quick-release mechanism may be used to secure in place and remove the plate. The method to secure the plate may also be vacuum suction of the plate onto build platform. The method to secure the plate can be magnets and/or electromagnets.
The substrate may be thermally conductive in nature, so that it can be heated. The substrate can be heated from the heated build platform by the temperature control components, such as heater cartridges. Further, the substrate can be made of a material having a low coefficient of thermal expansion (CTE), to avoid expansion of the plate as it is heated up due to the heated build platform. In an embodiment, the material for the substrate may be aluminum, steel, brass, ceramic, glass, or alloys similar with low coefficient of thermal expansion (CTE). Also, the substrate can have a thickness of at most about 0.1 inches (in), at most about 0.2 in, at most about 0.3 in, at most about 0.4 in, at most about 0.5 in, at most about 0.6 in, at most about 0.7 in, at most about 0.8 in, at most about 0.9 in, at most about 1 in, or at most about 5 in. Further, the thickness of the substrate may also depend on the flexural character of the material. The substrate may be thin enough to allow for minor flexing for the removal of the 3D object. Additionally, the substrate may not be too thin such that heating of the substrate results in rippling, bowing, or warping and resulting in a print surface that is uneven or not consistently level. Furthermore, the substrate may be able to withstand high temperatures, such as at least about 50 degrees Celsius (° C.), at least about 100° C., at least about 150° C., at least about 200° C., at least about 250° C., at least about 300° C., at least about 350° C., or at least about 400° C.
A high temperature polymer coating may be applied directly over the surface of the substrate. The high temperature polymer may be selected from the group consisting of polyether ether ketone, polyamide, polyimide, polyphenylene sulfide, polyphenylsulfone, polysulfone, polyether sulfone, polyethylenimine, polyetherimide, polytetrafluoroethylene, polyvinylidene, or any combination thereof. The high temperature used for coating may be a polyimide. In an embodiment, the high temperature polymer coating may be spray coated over the substrate. The thickness of the polymer coating may be at most about 0.005 in, at most about 0.01 in, at most about 0.05 in, at most about 0.1 in, at most about 0.5 in, or at most about 0.1 in. The high temperature polymer coating may not wear away and thus may not need to be replaced after every build under high temperature. Advantageously, the high temperature polymer coating can operate at temperatures of at least about 50 degrees Celsius (° C.), at least about 100° C., at least about 150° C., at least about 200° C., at least about 250° C., at least about 300° C., at least about 350° C., or at least about 400° C. The high temperature polymer coating may additionally be roughened or treated. The surface of the high temperature polymer coating may comprise a regular or an irregular patterned feature. In an embodiment, the surface of the high temperature polymer coating 106 may be roughened at the nano-, micro-, or milli-meter scale using methods like and not limited to sand blasting, bead blasting, and/or metal wire brushing to increase polymer adhesion to the coated surface.
The substrate may possess flexibility owing to the type of material it is made of The flexibility of the substrate may allow for easier dissociation between the 3D object and the substrate upon cooling. Further, this flexibility can also reduce the possibility of damage to the high temperature polymer coating or the 3D object during object removal since a blade or wedge is no longer needed to pry off the object. Once the printing of the 3D object is completed, the 3D object may pop off the substrate when the substrate and 3D object has cooled.
The system for printing at least a portion of a 3D object may comprise one or more heater cartridges with thermal control from PID controllers connected to thermocouples. The heater cartridges may function as a temperature control for the system. The one or more thermocouples can be situated at one or several locations to provide feedback to a controller, such as a PID controller, and hence maintain temperature set points throughout a build. The system may comprise a jacket cover outside of the print head to contain and direct the flow of the hot fluid (e.g., hot air) towards the layers of the deposited portion of the 3D object.
The controller may be configured after deposition of a first layer and/or a second layer of at least a portion of the 3D object, and before fusion is induced, to preheat the filament material to a temperature sufficient to reduce undesirable shrinkage and/or to minimize the laser energy needed to melt the next layer. For example, the preheating may be accomplished using the infrared heater attached to substrate or through other apparatuses of directing thermal energy within an enclosed space around the substrate. Alternatively, the preheating can be accomplished using energy beam melting by defocusing the energy beam and rapidly scanning it over the deposited first layer and or second layer of at least a portion of the 3D object.
The controller may be configured using at least a first energy beam from at least one energy source to selectively heat and/or melt at least a portion of the first layer and/or the second layer, thereby forming at least a portion of the 3D object. The energy source may be selected from the group consisting of an electromagnetic radiation source (e.g., laser), a microwave source, a resistive heating source, an infrared energy source, a UV energy source, a hot fluid, a chemical reaction, a plasma source, a microwave source, an electromagnetic source, an electron beam, or any combination thereof. Resistive heating may be joule heating. A source for resistive heating may be a power supply. The at least one filament material may be a metal filament. The at least one filament material may be a metal filament composite. The deposited at least one filament material may be subjected to resistive heating upon flow of an electrical current through the at least one filament material. The resistive heating may be sufficient to melt at least a portion of the deposited at least one filament material. The at least one filament material may be an electrode. The substrate may be another electrode.
The energy source may be a function of the chemical composition of the build material, such as the build material's thermal conductivity, heat capacity, latent heat of fusion, melting point, and melt flow viscosity. The at least one energy source may be a laser. The laser may be selected from the group consisting of gas lasers, chemical lasers, dye lasers, metal-vapor lasers, solid-state lasers, semiconductor lasers, free electron laser, gas dynamic laser, nickel-like samarium laser, Raman laser, nuclear pump laser, and any combination thereof. Gas lasers may comprise one or more of helium-neon laser, argon laser, krypton laser, xenon ion laser, nitrogen laser, carbon dioxide laser, carbon monoxide laser, and excimer laser. Chemical lasers may be selected from the group consisting of hydrogen fluoride laser, deuterium fluoride laser, chemical oxygen-iodine laser, all gas-phase iodine laser, and any combination thereof. Metal-vapor lasers can comprise one or more of helium-cadmium, helium mercury, helium selenium, helium silver, strontium vapor laser, neon-copper, copper vapor laser, gold vapor laser, and manganese vapor laser. Solid-state lasers may be selected from the group consisting of ruby laser, neodymium-doped yttrium aluminium garnet laser, neodymium and chromium-doped yttrium aluminium garnet laser, erbium-doped yttrium aluminium garnet laser, neodymium-doped yttrium lithium fluoride laser, neodymium doped yttrium othovanadate laser, neodymium doped yttrium calcium oxoborate laser, neodymium glass laser, titanium sapphire laser, thulium yttrium aluminium garnet laser, ytterbium yttrium aluminium garnet laser, ytterbium:203 (glass or ceramics) laser, ytterbium doped glass laser (rod, plate/chip, and fiber), holmium yttrium aluminium garnet laser, chromium zinc selenium laser, cerium doped lithium strontium (or calcium) aluminum fluoride laser, Promethium 147 doped phosphate glass solid-state laser, chromium doped chrysoberyl (alexandrite) laser, erbium doped and erbium-ytterbium codoped glass lasers, trivalent uranium doped calcium fluoride solid-state laser, divalent samarium doped calcium fluoride laser, FARBE center laser, and any combination thereof. Semiconductor laser may comprise one or more of semiconductor laser diode laser, gallium nitride laser, indium gallium nitride laser, aluminium gallium indium phosphide laser, aluminium gallium arsenide laser, indium gallium arsenide phosphide laser, lead salt laser, vertical cavity surface emitting laser, quantum cascade laser, and hybrid silicon laser.
The melting temperature of the at least one filament material can be at least about 150 degrees Celsius (° C.), at least about 200° C., at least about 250° C., at least about 300° C., at least about 350° C., at least about 400° C., at least about 450° C. The sintering temperature can be at most about 150° C., at most about 200° C., at most about 250° C., at most about 300° C., at most about 350° C., at most about 400° C. The controller may further be programmed to separate the remainder of the layer that did not fuse and solidify to form at least a portion of the three dimensional object, from the portion. The controller may be programmed to direct delivery of the three dimensional object to a customer. The controller may be programmed to direct packaging the three dimensional object.
The controller may be programmed to direct at least one energy beam from the energy source may be directed to the at least one portion of the 3D object adjacent to the substrate. Such energy beams may be sufficient to induce fusion of particles of the filament material within the desired cross-sectional geometry of the at least one portion of the 3D object. As the energy dissipates with cooling, atoms from neighboring particles may fuse together. The at least one energy beam results in the fusion of particles of filament material both within the same layer and in the previously formed and resolidified adjoining layer(s) such that fusion is induced between at least two adjacent layers of the part, such as between at least one filament material in a deposited unfused layer and a previously-fused adjacent layer. The controller may be further programmed to repeat such process over multiple cycles as each part layer is added, until the full 3D object is formed.
In some cases, to create a melt pool large enough to span the width of the filament material segment, multiple energy sources or a combination of energy sources may be required. When multiple energy sources are used, the energy sources may be the same energy source. Alternatively, the multiple energy sources may be different energy sources. The energy source(s) may be separate from the system for printing at least a portion of the 3D object. In some other embodiments, the energy source(s) may be integrated with such system. For example, in one embodiment, a hot fluid may be channeled through the deposition nozzle. Because the material filament can flow in the melt pool, features of the 3D object being built can be altered. The melt pool may be formed within the build object, such that a melt pool is not formed near the perimeters thereof. To accomplish this, the energy source may be turned off when the perimeters of the object are being built. In such embodiments, the geometrical tolerance of the build object may be maintained while the interior of the object has enhanced interlayer bonding. During printing, the filament material may be printed in the X, Y, and Z directions in one segment or layer.
The controller may be programmed to direct the processes of optical communication between at least one energy source and one or more beam splitters, which one or more beam splitters can split an energy beam from at least one light source into one or more beamlets that yields at least the first energy beam. The controller can be programmed to direct the example optical system of
One or more beam splitters may be selected from the group consisting of prism, glass sheet, plastic sheet, mirror, dielectric mirror, metal-coated mirror, partially reflecting mirror, pellicles, micro-optic beam splitters, waveguide beam splitters, beam splitter cubes, fiber-optic beam splitter, and any combination thereof. The controller may be programmed so that one or more optical wedges may be in optical communication with one or more beam splitters, which one or more optical wedges form at least the first light beam. Such optical wedges can form at least the first light beam in a uniform orientation. The one or more beamlets may pass through one or more focusing lenses prior to passing through at least one or more optical wedges. Such beamlets may have an elliptical polarization. The one or more beamlets may comprise a minor axis of at least about 0.5 millimeters (mm), at least about 1 mm, at least about 2 mm, at least about 3 mm, at least about 4 mm, at least about 5 mm, at least about 6 mm, at least about 7 mm, at least about 8 mm, at least about 9 mm, at least about 10 mm, or at least about 15 mm. The one or more beamlets may also comprise a major axis of at least about 5 mm, at least about 10 mm, at least about 15 mm, at least about 20 mm, at least about 25 mm, at least about 30 mm, at least about 35 mm, at least about 40 mm, at least about 45 mm, or at least about 50 mm. Such energy beams can cover at least a portion of at least one filament material. The one or more focusing lenses may be used to adjust a ratio of the minor axis to the major axis of the one or more beamlets.
The controller can further be programmed so that the optical wedges may alter the path of the beam from vertical to any angle for uniform heating of the filament material. The controller may be programmed so that one or more optical wedges can further direct an optical path of at least the first light beam of a given location, direction, or angle normal to the substrate and/or along the substrate among one or more locations, directions, or angles. Such a direction of one or more optical wedges can allow for control of the heat from the light beam along the at least one filament material.
The system for printing at least a portion of a three-dimensional (3D) object may further comprise one or more optical wedges in combination with one or more of dispersive prism, reflective prism, beam-splitting prism, polarizing prism, or deflecting prisms. Dispersive prisms may be used to break up light into its constituent spectral colors because the refractive index depends on frequency. Examples of dispersive prisms include Triangular prism, Abbe prism, Pellin-Broca prism, Amici prism, Compound prism, or Grism prism. Reflective prisms can be used to reflect light, in order to flip, invert, rotate, deviate or displace the light beam. Examples of reflective prisms include Porro prism, Porro-Abbe prism, Amici roof prism, Pentaprism, Roof Pentaprism, Abbe-Koenig prism, Schmidt-Pechan prism, Bauernfeind prism, Dove prism, or Retroreflector prism. Some reflective prisms may be used for splitting a beam into two or more beams. Beam-splitting prisms may be a beam splitter cube or a dichronic prism. Polarizing prisms can split a beam of light into components of varying polarization. Examples of polarizing prisms may be Nicol prism, Wollaston prism, Nomarski prism, Rochon prism, Senarmont prism, Glan-Foucault prism, Glan-Taylor prism, or Glan-Thompson prism. Deflecting prisms may be one or more of a Risley prism pair, Rhomboid prisms, or Deck prisms. Wedge prisms may be used to deflect a beam of light by a fixed angle. A pair of such prisms can be used for beam steering; by rotating the prisms the beam can be deflected into any desired angle. The deflecting prism may be a Risley prism pair. Two wedge prisms can also be used as an anamorphic pair to change the shape of a beam. For example, this may be used to generate a round beam from the elliptical output of a laser diode.
The one or more optical wedges can have a refractive index of at least about 0.5, at least about 1, at least about 1.1, at least about 1.2, at least about 1.3, at least about 1.4, at least about 1.5, at least about 1.6, at least about 1.7, at least about 1.8, at least about 1.9, at least about 2.5, at least about 3, at least about 4, or at least about 5. Such optical wedges can have a diameter of at most about 0.1 inches (in), at most about 0.2 in, at most about 0.3 in, at most about 0.4 in, at most about 0.5 in, at most about 0.6 in, at most about 0.7 in, at most about 0.8 in, at most about 0.9 in, at most about 1 in, at most about 2 in, at most about 3 in, at most about 4 in, or at most about 5 in.
The controller can be programmed so that at least the first energy beam may be incident on at least one filament material and on the substrate. Such energy beams may be directed along a given angle among one or more angles relative to the dispensing route of at least one filament material. The one or more optical wedges can comprise a first optical wedge and a second optical wedge. The first optical wedge may be the top wedge and the second optical wedge may be the bottom wedge. Through choosing the wedge angle, the energy beams can be made incident on the filament at an angle to the plane of the substrate. By directing the controller to rotate the bottom optical wedge, the incident angle can be varied. By directing the controller to rotate both the optical wedges, the angle of the line beam in the plane of deposition can be varied. For example, the controller may be programmed to direct the first optical wedge to rotate relative to the second optical wedge to change the direction of at least the first light beam. The controller may direct the first optical wedge and the second optical wedge to be angled in the same direction to increase an angle of at least the first energy beam with respect to a reference. The energy beam may be a light beam. The controller may direct the first optical wedge and the second optical wedge to rotate in opposite directions to allow at least the first energy beam to pass vertically through the one or more optical wedges. When altering an angle of incidence of the first optical wedge and the second optical wedge, or when altering a direction of the major axis of at least the first energy beam relative to the substrate or at least one filament material, the controller may direct the fluence of at least the first light beam to be altered. As a result, such light beams may heat at least one filament material without melting a deposited portion of the at least one filament material. In some instances, the controller may direct the at least the first energy beam to heat and melt a deposited portion of at least one filament material at a given location among one or more locations.
In other instances, the controller may program the at least one filament material to be directed to a compaction unit. Such filament material may be compacted by such a compaction unit to form at least one compacted filament material. The compaction unit may comprise a rigid body, one or more idler rollers, at least one freely suspended roller, a coolant unit, or any combination thereof. The at least one freely suspended roller may be a compaction roller. The controller may direct the rigid body and one or more idler rollers to secure the at least one freely suspended roller. Such freely suspended rollers may have a diameter of at most about 1 millimeters (mm), at most about 2 mm, at most about 3 mm, at most about 4 mm, at most about 5 mm, at most about 6 mm, at most about 7 mm, at most about 8 mm, at most about 9 mm, at most about 10 mm, or at most about 15 mm. The controller may direct the coolant to cool the compaction unit so the at least one filament material does not stick to the roller and adheres to the previously deposited layer of the three-dimensional object.
The system for printing at least a portion of the 3D object may further comprise one or more cooling components. Such cooling components may be in proximity to the deposited filament material layer. Such cooling components can be located between the deposited filament material layer and the energy source. Such cooling components may be movable to or from a location that may be positioned between the filament material and the energy source. Such cooling components may assist in the process of cooling of the fused portion of the filament material layer. Such cooling components may also assist in the cooling of the filament material layer remainder that did not fuse to subsequently form at least a portion of the 3D object. Such cooling components can assist in the cooling of the at least a portion of the 3D object and the remainder at considerably the same rate. Such cooling components may be separated from the filament material layer and/or from the substrate by a gap. The gap may comprise a gas. The gap can have a cross-section that is at most about 0.1 millimeters (mm), at most about 0.5 mm, at most about 1 mm, at most about 5 mm, or at most about 10 mm. The gap can be adjustable. The controller may be operatively connected to such cooling components and may be able to adjust the gap distance from the substrate. Such cooling components can track an energy that may be applied to the portion of the filament material layer by the energy source. Such cooling components may comprise a heat sink. Such cooling components may be a cooling fan. The controller may be operatively coupled to such cooling components and controls the tracing of such cooling components. Such cooling components may include at least one opening though which at least one energy beam from the energy source can be directed to the portion of the filament layer. The system for printing at least a portion of the 3D object can further comprise an additional energy source that provides energy to a remainder of the filament material layer that did not fuse to subsequently form at least a portion of the 3D object.
During printing of the three-dimensional object, certain parameters may be critical to printing high quality parts. One or more sensors can be used to measure one or more temperature(s) along at least one filament material. Such sensors can control intensities, positions, and/or angles of at least the first energy beam. The one or more sensors may be an optical pyrometer. The controller may direct the optical pyrometers to be aimed at the nip points and one or more points before and/or after the compaction unit to detect the temperature of the at least one filament materials as they are deposited. The temperature may vary from region to region of the filament material layer. Factors that affect temperature variance can include variable heater irradiance, variations in absorptivity of the composition, substrate temperature, filament material temperature, unfused filament material temperature, and the use of modifiers and additives. Accordingly, the controller may be programmed so that the image and temperature measurement inputs based upon layer temperature patterns captured by the one or more sensors may be used. The real time temperature inputs and the sintering model may be factors determining an energy requirement pattern for any one or more subsequent layers.
Additionally, the system may comprise a real time simulation program, a sample as shown in
Other parameters critical to printing high quality parts can include substrate temperature, melt zone temperature, as-built geometry, surface roughness and texture and density. Other critical visible or non-visible metrics include characterization of chemistry, bonding or adhesion strength. Measuring one or more structural or internal properties of the part can comprise one or more methods selected from the group consisting of scattered and reflected or absorbed radiation, x-ray imaging, sound waves, scatterometry techniques, ultrasonic techniques, X-ray Photoelectron Spectroscopy (XPS), Four Transform Infrared Spectroscopy (FTIR), Raman Spectroscopy, Laser-Microprobe Mass Spectrometry (LMMS), and any combination thereof. Specific metrology beneficial to the end goals of characterizing the critical process parameters can be used. This in-situ metrology coupled with fast processing of data can enable open or closed loop control of the manufacturing process. Sensors appropriate to the key parameters of interest can be selected and utilized during the part printing process. The sensors may also comprise a camera for detecting light in the infrared or visible portion of the electromagnetic spectrum. Sensors such as IR cameras may be used to measure temperature fields. An image processing algorithm may be used to evaluate data generated by one or more sensors, to extract one or more structural or internal properties of the part. Visual (e.g., high magnification) microscopy from digital camera(s) can be used with proper software processing to detect voids, defects, and surface roughness. In order to utilize this technique, potentially large quantities of data may need to be interrogated using image processing algorithms in order to extract features of interest. Scatterometry techniques may be adapted to provide roughness or other data.
Ultrasonic techniques can be used to measure solid density and fiber and particle density which in turn may be useful in characterizing bond strength and fiber dispersion. The characterization can affect material strength. Ultrasonic techniques can also be used to measure thickness of features. Chemical bonding characterization, which may be useful for understanding fiber and/or matrix adhesion and layer-to-layer bonding, can be performed by multiple techniques such as XPS (X-ray Photoelectron Spectroscopy), FTIR (Four Transform Infrared Spectroscopy) and Raman Spectroscopy and Laser-Microprobe Mass Spectrometry (LMMS). One or more of these techniques may be utilized as part of the in-situ metrology for 3D printing. Ex-situ techniques may also be utilized in order to help provide appropriate calibration data for the in-situ techniques.
Sensors may be positioned on the robot end-effector of the three-dimensional printer in order to provide a sensor moving along with the deposited material. A robot end-effector may be a device positioned at the end of a robotic arm. The robot end-effector may be programmed to interact with its surrounding environment. Sensors may be also located at other various positions. The positions can be on-board the robot, on the effector, or deployed in the environment. Sensors may be in communication with the system. The system can further comprise one or more processors, a communication unit, memory, power supply, and storage. The communications unit can comprise an input and an output. The communication unit can be wired or wireless. The sensor measurements may or may not be stored in a database and may or may not be used in future simulation and optimization operations. In-situ measurements may also be made using alternative methods with sensors in a cell but not directly attached to the robot end-effector.
In another aspect, the present disclosure provides a system for printing at least a portion of a 3D object. The system may comprise a source of at least one filament material that is configured to supply at least one filament material for generating the 3D object. The system may comprise a substrate for supporting at least a portion of the 3D object. The system may additionally comprise at least one energy source configured to deliver at least a first energy beam. The system can comprise a controller operatively coupled to at least one energy source, wherein the controller is programmed to (i) receive, in computer memory, a model of the 3D object, (ii) subsequent to receiving the model of the 3D object, direct at least one filament material from the source of at least one filament material towards the substrate that is configured to support the 3D object, thereby depositing a first layer corresponding to a portion of the 3D object adjacent to the substrate, which first layer is deposited in accordance with the model of the 3D object, (iii) use at least a first energy beam from at least one energy source to melt at least a portion of the first layer, and (iv) deposit a second layer corresponding to at least a portion of the 3D object, which second layer is deposited in accordance with a model of the 3D object, thereby generating at least a portion of the 3D object. In some cases, the controller may be programmed to perform fused deposition modeling when printing the 3D object. In other cases, the controller may be programmed to print the 3D object with extrusion. In some cases, the controller may be programmed to print the 3D object without extrusion. The controller can be further programmed to repeat (ii)-(iv) one or more times.
The system may further comprise an opening for (i) receiving at least one filament material, and (ii) directing at least one filament material towards the substrate.
The layered structure can comprise substantially repetitive layers. The layers may have an average layer size of at least about 0.5 micrometers (μm), 1 μm, 5 μm, 10 μm, 20 μm, 30 μm, 40 μm, 50 μm, 60 μm, 70 μm, 80 μm, 90 μm, 100 μm, 150 μm, 200 μm, 250 μm, 300 μm, 350 μm, 400 μm, 450 μm, 500 μm, 1 mm, 25 mm, 50 mm, 100 mm, 500 mm, or 1 m. The layers may have an average layer size of at most about 50 m, 1 m, 500 mm, 100 mm, 50 mm, 25 mm, 1 mm, 500 μm, 450 μm, 400 μm, 350 μm, 300 μm, 250 μm, 200 μm, 150 μm, 100 μm, 90 μm, 80 μm, 70 μm, 60 μm, 50 μm, 40 μm, 30 μm, 20 μm, or 10 μm. The layers may have an average layer size of any value between the aforementioned values of layer size. For example, the layers may have an average layer size from about 0.5 μm to about 500 mm, from about 15 μm to about 100 μm, from about 5 μm to about 300 μm, from about 20 μm to about 90 μm, or from about 10 μm to about 70 μm. The layered structure can be indicative of layered deposition. The layered structure can be indicative of solidification of melt pools formed during a three-dimensional printing process. The structure indicative of a three dimensional printing process can comprise substantially repetitive variation comprising: variation in grain orientation, variation in material density, variation in the degree of compound segregation to grain boundaries, variation in the degree of element segregation to grain boundaries, variation in material phase, variation in metallurgical phase, variation in material porosity, variation in crystal phase, or variation in crystal structure. The melt pools may be indicative of an additive manufacturing process comprising stereolithography (SLA), selective laser melting (SLM), selective laser sintering (SLS), digital light processing (DLP), electron beam melting (EBM), laminated object manufacturing (LOM), binder jetting (BM), material jetting/wax casting (MJ), direct metal laser sintering (DMLS), or fused deposition modeling (FDM). The melt pools may be indicative of an additive manufacturing process comprising selective energy melting.
The source of at least one filament material may be configured to supply at least one filament material for generating the three-dimensional object. The at least one filament material may be stored on one or more spools or cartridges. The spools and/or cartridges may be replaceable. The at least one filament material may be a composite material, such as a continuous fiber composite. The filament material may be nano milled, short, long, continuous, or a combination thereof. The continuous fiber composite may be a continuous core reinforced filament. The continuous core reinforced filament can comprise a towpreg that is substantially void free and includes a polymer that coats or impregnates an internal continuous core. Depending upon the particular embodiment, the core may be a solid core or it may be a multi-strand core comprising multiple strands. The continuous fiber composite may be selected from the group consisting of glass, carbon, aramid, cotton, silicon carbide, polymer, wool, metal, and any combination thereof.
The filament material may incorporate one or more additional materials, such as resins and polymers. For example, appropriate resins and polymers include, but are not limited to, acrylonitrile butadiene styrene (ABS), epoxy, vinyl, nylon, polyetherimide (PEI), Polyaryletherketone (PAEK), Polyether ether ketone (PEEK), Polyactic Acid (PLA), Liquid Crystal Polymer, polyamide, polyimide, polyphenylene sulfide, polyphenylsulfone, polysulfone, polyether sulfone, polyethylenimine, polytetrafluoroethylene, polyvinylidene, and various other thermoplastics. The core of the continuous fiber composite may be selected to provide any desired property. Appropriate core fiber or strands include those materials which impart a desired property, such as structural, conductive (electrically and/or thermally), insulative (electrically and/or thermally), optical and/or fluidic transport. Such materials include, but are not limited to, carbon fibers, aramid fibers, fiberglass, metals (such as copper, silver, gold, tin, and steel), optical fibers, and flexible tubes. The core fiber or strands may be provided in any appropriate size. Further, multiple types of continuous cores may be used in a single continuous core reinforced filament to provide multiple functionalities such as electrical and optical properties. A single material may be used to provide multiple properties for the core reinforced filament. For example, a steel core may be used to provide both structural properties as well as electrical conductivity properties.
Alternatively, the filament material may comprise metal particles infused into a binder matrix. The metal particles may be metal powder. The binder matrix may include resins or polymers. Additionally, such binder matrix can be used a delivery device for the metal particles. Once the filament material is deposited onto the base, one or more energy sources can heat and melt the binder matrix, leaving the metal particles to melt and fuse into larger metal particles. Such energy sources may be without limitation, an electromagnetic radiation source (e.g., laser), a microwave source, a resistive heating source, an infrared energy source, a UV energy source, a hot fluid, a chemical reaction, a plasma source, a microwave source, an electromagnetic source, or an electron beam. Resistive heating may be joule heating. A source for resistive heating may be a power supply. The at least one filament material may be a metal filament. The at least one filament material may be a metal filament composite. The deposited at least one filament material may be subjected to resistive heating upon flow of an electrical current through the at least one filament material. The resistive heating may be sufficient to melt at least a portion of the deposited at least one filament material. The at least one filament material may be an electrode. The substrate may be another electrode.
The one or more energy sources may also provide localized heating to create a “melt pool” in the current layer or segment of the deposited build material prior to depositing the next segment or layer. The melt pool can increase diffusion and mixing of the build material between adjacent layers (e.g., across a direction orthogonal to the layers) as compared to other methods which deposit a subsequent layer of build material on top of a layer of build material that is below its melting temperature.
The increased diffusion and mixing resulting from the melt pool may increase the chemical chain linkage, bonding, and chemical chain interactions between the two layers. This can result in increasing the build-material adhesion in the Z direction, thereby enhancing mechanical, thermal, and electrical properties of the three-dimensional object. The melt pool can also reduce the void space and porosity in the build object. Among other benefits, this decrease in porosity may also contribute to the aforementioned improvement in mechanical, thermal, and electrical properties.
The at least one filament material may have a cross sectional shape selected from the group consisting of circle, ellipse, parabola, hyperbola, convex polygon, concave polygon, cyclic polygon, equilateral polygon, equiangular polygon, regular convex polygon, regular star polygon, tape-like geometry, and any combination thereof. Such filament material can have a diameter of at most about 0.1 millimeters (mm), at most about 0.2 mm, at most about 0.3 mm, at most about 0.4 mm, at most about 0.5 mm, at most about 0.6 mm, at most about 0.7 mm, at most about 0.8 mm, at most about 0.9 mm, at most about 1 mm, at most about 2 mm, at most about 3 mm, at most about 4 mm, at most about 5 mm, at most about 10 mm, or at most about 20 mm.
Various modifiers within the layers themselves may be used which are selectively printed onto specific regions of the 3D object in order to impart various desirable mechanical, chemical, magnetic, electrical or other properties to the 3D object. Such modifiers may be selected from the group consisting of thermal conductors and insulators, dielectric promoters, electrical conductors and insulators, locally-contained heater traces for multi-zone temperature control, batteries, and sensors. At least one print head can be may be used for printing such modifiers. As desired, such modifiers can be printed before at least a first energy beam is directed onto at least a portion of the first layer and/or second layer. Alternatively, such modifiers may be printed over a layer that has been melted, before filament material for the next layer is deposited.
For example, when printing a polyimide part from commercially available a filament comprising polyimide, an array of electrically conductive traces may be assimilated as an antenna to selectively absorb radiofrequency (RF) radiation within a specific and predetermined frequency range. The 3D object CAD model and software can designate as a sub-part the layer(s) that comprise the traces for modified properties (high electrical conductivity). Alternatively, if these portions of the layer entail different levels of energy for inducing fusion, compared to other regions having only the primary material, the CAD model and design of the 3D object may be adjusted accordingly.
The system for printing at least a portion of a three-dimensional object may comprise at least one print head. The at least one print head may comprise one or more dies for extrusion. The at least one print head also deposit printed material without extrusion.
The system for printing at least a portion of a three-dimensional object may comprise a build plate form. The system may also comprise a substrate. The substrate may be able to withstand high temperatures. The substrate may have high thermal tolerances, and able to withstand high temperatures, such as at least about 50 degrees Celsius (° C.), at least about 100° C., at least about 150° C., at least about 200° C., at least about 250° C., at least about 300° C., at least about 350° C., or at least about 400° C.
The substrate may be a non-removable. The substrate may be a removable plate secured over the build platform. In an embodiment, guiding legs/rails may be used to slide the removable plate into multiple grooves and multiple set screws and fasteners to secure the plate onto the build platform. In another embodiment, the spring/latch quick-release mechanism may be used to secure in place and remove the plate. The method to secure the plate may also be vacuum suction of the plate onto build platform. The method to secure the plate can be magnets and/or electromagnets.
The substrate may be thermally conductive in nature, so that it can be heated. The substrate can be heated from the heated build platform by the temperature control components, such as heater cartridges. Further, the substrate can be made of a material having a low coefficient of thermal expansion (CTE), to avoid expansion of the plate as it is heated up due to the heated build platform. In an embodiment, the material for the substrate may be aluminum, steel, brass, ceramic, glass, or alloys similar with low coefficient of thermal expansion (CTE). Also, the substrate can have a thickness of at most about 0.1 inches (in), at most about 0.2 in, at most about 0.3 in, at most about 0.4 in, at most about 0.5 in, at most about 0.6 in, at most about 0.7 in, at most about 0.8 in, at most about 0.9 in, at most about 1 in, or at most about 5 in. Further, the thickness of the substrate may also depend on the flexural character of the material. The substrate may be thin enough to allow for minor flexing for the removal of the 3D object. Additionally, the substrate may not be too thin such that heating of the substrate results in rippling, bowing, or warping and resulting in a print surface that is uneven or not consistently level. Furthermore, the substrate may be able to withstand high temperatures, such as at least about 50 degrees Celsius (° C.), at least about 100° C., at least about 150° C., at least about 200° C., at least about 250° C., at least about 300° C., at least about 350° C., or at least about 400° C.
A high temperature polymer coating may be applied directly over the surface of the substrate. The high temperature polymer may be selected from the group consisting of polyether ether ketone, polyamide, polyimide, polyphenylene sulfide, polyphenylsulfone, polysulfone, polyether sulfone, polyethylenimine, polyetherimide, polytetrafluoroethylene, polyvinylidene, or any combination thereof. The high temperature used for coating may be a polyimide. In an embodiment, the high temperature polymer coating may be spray coated over the substrate. The thickness of the polymer coating may be at most about 0.005 in, at most about 0.01 in, at most about 0.05 in, at most about 0.1 in, at most about 0.5 in, or at most about 0.1 in. The high temperature polymer coating may not wear away and thus may not need to be replaced after every build under high temperature. Advantageously, the high temperature polymer coating can operate at temperatures of at least about 50° C., at least about 100° C., at least about 150° C., at least about 200° C., at least about 250° C., at least about 300° C., at least about 350° C., or at least about 400° C. The high temperature polymer coating may additionally be roughened or treated. The surface of the high temperature polymer coating may comprise a regular or an irregular patterned feature. In an embodiment, the surface of the high temperature polymer coating 106 may be roughened at the nano-, micro-, or milli-meter scale using methods like and not limited to sand blasting, bead blasting, and/or metal wire brushing to increase polymer adhesion to the coated surface.
The substrate may possess flexibility owing to the type of material it is made of The flexibility of the substrate may allow for easier dissociation between the 3D object and the substrate upon cooling. Further, this flexibility can also reduce the possibility of damage to the high temperature polymer coating or the 3D object during object removal since a blade or wedge is no longer needed to pry off the object. Once the printing of the 3D object is completed, the 3D object may pop off the substrate when the substrate and 3D object has cooled.
The system for printing at least a portion of a 3D object may comprise one or more heater cartridges with thermal control from PID controllers connected to thermocouples. The heater cartridges may function as a temperature control for the system. The one or more thermocouples can be situated at one or several locations to provide feedback to a controller, such as a PID controller, and hence maintain temperature set points throughout a build. The system may comprise a jacket cover outside of the print head to contain and direct the flow of the hot fluid (e.g., hot air) towards the layers of the deposited portion of the 3D object.
The controller may be configured after deposition of a first layer and/or a second layer of at least a portion of the 3D object, and before fusion is induced, to preheat the filament material to a temperature sufficient to reduce undesirable shrinkage and/or to minimize the laser energy needed to melt the next layer. For example, the preheating may be accomplished using the infrared heater attached to substrate or through other apparatuses of directing thermal energy within an enclosed space around the substrate. Alternatively, the preheating can be accomplished using energy beam melting by defocusing the energy beam and rapidly scanning it over the deposited first layer and or second layer of at least a portion of the 3D object.
The controller may be configured using at least a first energy beam from at least one energy source to selectively heat and/or melt at least a portion of the first layer and/or the second layer, thereby forming at least a portion of the 3D object. The energy source may be selected from the group consisting of an electromagnetic radiation source (e.g., laser), a microwave source, a resistive heating source, an infrared energy source, a UV energy source, a hot fluid, a chemical reaction, a plasma source, a microwave source, an electromagnetic source, an electron beam, or any combination thereof. Resistive heating may be joule heating. A source for resistive heating may be a power supply. The at least one filament material may be a metal filament. The at least one filament material may be a metal filament composite. The deposited at least one filament material may be subjected to resistive heating upon flow of an electrical current through the at least one filament material. The resistive heating may be sufficient to melt at least a portion of the deposited at least one filament material. The at least one filament material may be an electrode. The substrate may be another electrode.
The energy source may be a function of the chemical composition of the build material, such as the build material's thermal conductivity, heat capacity, latent heat of fusion, melting point, and melt flow viscosity. The at least one energy source may be an electromagnetic radiation source (e.g., a laser). The laser may be selected from the group consisting of gas lasers, chemical lasers, dye lasers, metal-vapor lasers, solid-state lasers, semiconductor lasers, free electron laser, gas dynamic laser, nickel-like samarium laser, Raman laser, nuclear pump laser, and any combination thereof. Gas lasers may comprise one or more of helium-neon laser, argon laser, krypton laser, xenon ion laser, nitrogen laser, carbon dioxide laser, carbon monoxide laser, and excimer laser. Chemical lasers may be selected from the group consisting of hydrogen fluoride laser, deuterium fluoride laser, chemical oxygen-iodine laser, all gas-phase iodine laser, and any combination thereof. Metal-vapor lasers can comprise one or more of helium-cadmium, helium mercury, helium selenium, helium silver, strontium vapor laser, neon-copper, copper vapor laser, gold vapor laser, and manganese vapor laser. Solid-state lasers may be selected from the group consisting of ruby laser, neodymium-doped yttrium aluminium garnet laser, neodymium and chromium-doped yttrium aluminium garnet laser, erbium-doped yttrium aluminium garnet laser, neodymium-doped yttrium lithium fluoride laser, neodymium doped yttrium othovanadate laser, neodymium doped yttrium calcium oxoborate laser, neodymium glass laser, titanium sapphire laser, thulium yttrium aluminium garnet laser, ytterbium yttrium aluminium garnet laser, ytterbium:2O3 (glass or ceramics) laser, ytterbium doped glass laser (rod, plate/chip, and fiber), holmium yttrium aluminium garnet laser, chromium zinc selenium laser, cerium doped lithium strontium (or calcium) aluminum fluoride laser, Promethium 147 doped phosphate glass solid-state laser, chromium doped chrysoberyl (alexandrite) laser, erbium doped and erbium-ytterbium codoped glass lasers, trivalent uranium doped calcium fluoride solid-state laser, divalent samarium doped calcium fluoride laser, FARBE center laser, and any combination thereof. Semiconductor laser may comprise one or more of semiconductor laser diode laser, gallium nitride laser, indium gallium nitride laser, aluminium gallium indium phosphide laser, aluminium gallium arsenide laser, indium gallium arsenide phosphide laser, lead salt laser, vertical cavity surface emitting laser, quantum cascade laser, and hybrid silicon laser.
The melting temperature of the at least one filament material can be at least about 150 degree Celsius (° C.), at least about 200° C., at least about 250° C., at least about 300° C., at least about 350° C., at least about 400° C., at least about 450° C. The sintering temperature can be at most about 150° C., at most about 200° C., at most about 250° C., at most about 300° C., at most about 350° C., at most about 400° C. The controller may further be programmed to separate the remainder of the layer that did not fuse and solidify to form at least a portion of the three dimensional object, from the portion. The controller may be programmed to direct delivery of the three dimensional object to a customer. The controller may be programmed to direct packaging the three dimensional object.
The controller may be programmed to direct at least one energy beam from the energy source may be directed to the at least one portion of the 3D object adjacent to the substrate. Such energy beams may be sufficient to induce fusion of particles of the filament material within the desired cross-sectional geometry of the at least one portion of the 3D object. As the energy dissipates with cooling, atoms from neighboring particles may fuse together. The at least one energy beam results in the fusion of particles of filament material both within the same layer and in the previously formed and resolidified adjoining layer(s) such that fusion is induced between at least two adjacent layers of the part, such as between at least one filament material in a deposited unfused layer and a previously-fused adjacent layer. The controller may be further programmed to repeat such process over multiple cycles as each part layer is added, until the full 3D object is formed.
In some cases, to create a melt pool large enough to span the width of the filament material segment, multiple energy sources or a combination of energy sources may be required. When multiple energy sources are used, the energy sources may be the same energy source. Alternatively, the multiple energy sources may be different energy sources. The energy source(s) may be separate from the system for printing at least a portion of the 3D object. In some other embodiments, the energy source(s) may be integrated with such system. For example, in one embodiment, a hot fluid may be channeled through the deposition nozzle. Because the material filament can flow in the melt pool, features of the 3D object being built can be altered. The melt pool may be formed within the build object, such that a melt pool is not formed near the perimeters thereof. To accomplish this, the energy source may be turned off when the perimeters of the object are being built. In such embodiments, the geometrical tolerance of the build object may be maintained while the interior of the object has enhanced interlayer bonding. During printing, the filament material may be printed in the X, Y, and Z directions in one segment or layer.
The controller may be programmed to direct the processes of optical communication between at least one energy source and one or more beam splitters, which one or more beam splitters can split an energy beam from at least one light source into one or more beamlets that yields at least the first energy beam. The controller can be programmed to direct the example optical system of
One or more beam splitters may be selected from the group consisting of prism, glass sheet, plastic sheet, mirror, dielectric mirror, metal-coated mirror, partially reflecting mirror, pellicles, micro-optic beam splitters, waveguide beam splitters, beam splitter cubes, fiber-optic beam splitter, and any combination thereof. The controller may be programmed so that one or more optical wedges may be in optical communication with one or more beam splitters, which one or more optical wedges form at least the first light beam. Such optical wedges can form at least the first light beam in a uniform orientation. The one or more beamlets may pass through one or more focusing lenses prior to passing through at least one or more optical wedges. Such beamlets may have an elliptical polarization. The one or more beamlets may comprise a minor axis of at least about 0.5 millimeters (mm), at least about 1 mm, at least about 2 mm, at least about 3 mm, at least about 4 mm, at least about 5 mm, at least about 6 mm, at least about 7 mm, at least about 8 mm, at least about 9 mm, at least about 10 mm, or at least about 15 mm. The one or more beamlets may also comprise a major axis of at least about 5 mm, at least about 10 mm, at least about 15 mm, at least about 20 mm, at least about 25 mm, at least about 30 mm, at least about 35 mm, at least about 40 mm, at least about 45 mm, or at least about 50 mm. Such energy beams can cover at least a portion of at least one filament material. The one or more focusing lenses may be used to adjust a ratio of the minor axis to the major axis of the one or more beamlets.
The controller can further be programmed so that the optical wedges may alter the path of the beam from vertical to any angle for uniform heating of the filament material. The controller may be programmed so that one or more optical wedges can further direct an optical path of at least the first light beam of a given location, direction, or angle normal to the substrate and/or along the substrate among one or more locations, directions, or angles. Such a direction of one or more optical wedges can allow for control of the heat from the light beam along the at least one filament material.
The system for printing at least a portion of a three-dimensional (3D) object may further comprise one or more optical wedges in combination with one or more of dispersive prism, reflective prism, beam-splitting prism, polarizing prism, or deflecting prisms. Dispersive prisms may be used to break up light into its constituent spectral colors because the refractive index depends on frequency. Examples of dispersive prisms include Triangular prism, Abbe prism, Pellin-Broca prism, Amici prism, Compound prism, or Grism prism. Reflective prisms can be used to reflect light, in order to flip, invert, rotate, deviate or displace the light beam. Examples of reflective prisms include Porro prism, Porro-Abbe prism, Amici roof prism, Pentaprism, Roof Pentaprism, Abbe-Koenig prism, Schmidt-Pechan prism, Bauernfeind prism, Dove prism, or Retroreflector prism. Some reflective prisms may be used for splitting a beam into two or more beams. Beam-splitting prisms may be a beam splitter cube or a dichronic prism. Polarizing prisms can split a beam of light into components of varying polarization. Examples of polarizing prisms may be Nicol prism, Wollaston prism, Nomarski prism, Rochon prism, Senarmont prism, Glan-Foucault prism, Glan-Taylor prism, or Glan-Thompson prism. Deflecting prisms may be one or more of a Risley prism pair, Rhomboid prisms, or Deck prisms. Wedge prisms may be used to deflect a beam of light by a fixed angle. A pair of such prisms can be used for beam steering; by rotating the prisms the beam can be deflected into any desired angle. The deflecting prism may be a Risley prism pair. Two wedge prisms can also be used as an anamorphic pair to change the shape of a beam. For example, this may be used to generate a round beam from the elliptical output of a laser diode.
The one or more optical wedges can have a refractive index of at least about 0.5, at least about 1, at least about 1.1, at least about 1.2, at least about 1.3, at least about 1.4, at least about 1.5, at least about 1.6, at least about 1.7, at least about 1.8, at least about 1.9, at least about 2.5, at least about 3, at least about 4, or at least about 5. Such optical wedges can have a diameter of at most about 0.1 inches (in), at most about 0.2 in, at most about 0.3 in, at most about 0.4 in, at most about 0.5 in, at most about 0.6 in, at most about 0.7 in, at most about 0.8 in, at most about 0.9 in, at most about 1 in, at most about 2 in, at most about 3 in, at most about 4 in, or at most about 5 in.
The controller can be programmed so that at least the first energy beam may be incident on at least one filament material and on the substrate. Such energy beams may be directed along a given angle among one or more angles relative to the dispensing route of at least one filament material. The one or more optical wedges can comprise a first optical wedge and a second optical wedge. The first optical wedge may be the top wedge and the second optical wedge may be the bottom wedge. Through choosing the wedge angle, the energy beams can be made incident on the filament at an angle to the plane of the substrate. By directing the controller to rotate the bottom optical wedge, the incident angle can be varied. By directing the controller to rotate both the optical wedges, the angle of the line beam in the plane of deposition can be varied. For example, the controller may be programmed to direct the first optical wedge to rotate relative to the second optical wedge to change the direction of at least the first light beam. The controller may direct the first optical wedge and the second optical wedge to be angled in the same direction to increase an angle of at least the first energy beam with respect to the reference. The energy beam may be a light beam. The controller may direct the first optical wedge and the second optical wedge to rotate in opposite directions to allow at least the first energy beam to pass vertically through the one or more optical wedges. When altering an angle of incidence of the first optical wedge and the second optical wedge, or when altering a direction of the major axis of at least the first energy beam relative to the substrate or at least one filament material, the controller may direct the fluence of at least the first light beam to be altered. As a result, such light beams may heat at least one filament material without melting a deposited portion of the at least one filament material. In some instances, the controller may direct the at least the first energy beam to heat and melt a deposited portion of at least one filament material at a given location among one or more locations.
In other instances, the controller may program the at least one filament material to be directed to a compaction unit. Such filament material may be compacted by such a compaction unit to form at least one compacted filament material. The compaction unit may comprise a rigid body, one or more idler rollers, at least one freely suspended roller, a coolant unit, or any combination thereof. The at least one freely suspended roller may be a compaction roller. The controller may direct the rigid body and one or more idler rollers to secure the at least one freely suspended roller. Such freely suspended rollers may have a diameter of at most about 1 millimeters (mm), at most about 2 mm, at most about 3 mm, at most about 4 mm, at most about 5 mm, at most about 6 mm, at most about 7 mm, at most about 8 mm, at most about 9 mm, at most about 10 mm, or at most about 15 mm. The controller may direct the coolant to cool the compaction unit so the at least one filament material does not stick to the roller and adheres to the previously deposited layer of the three-dimensional object.
The system for printing at least a portion of the 3D object may further comprise one or more cooling components. Such cooling components may be in proximity to the deposited filament material layer. Such cooling components can be located between the deposited filament material layer and the energy source. Such cooling components may be movable to or from a location that may be positioned between the filament material and the energy source. Such cooling components may assist in the process of cooling of the fused portion of the filament material layer. Such cooling components may also assist in the cooling of the filament material layer remainder that did not fuse to subsequently form at least a portion of the 3D object. Such cooling components can assist in the cooling of the at least a portion of the 3D object and the remainder at considerably the same rate. Such cooling components may be separated from the filament material layer and/or from the substrate by a gap. The gap may comprise a gas. The gap can have a cross-section that is at most about 0.1 mm, at most about 0.5 mm, at most about 1 mm, at most about 5 mm, or at most about 10 mm. The gap can be adjustable. The controller may be operatively connected to such cooling components and may be able to adjust the gap distance from the substrate. Such cooling components can track an energy that may be applied to the portion of the filament material layer by the energy source. Such cooling components may comprise a heat sink. Such cooling components may be a cooling fan. The controller may be operatively coupled to such cooling components and controls the tracing of such cooling components. Such cooling components may include at least one opening though which at least one energy beam from the energy source can be directed to the portion of the filament layer. The system for printing at least a portion of the 3D object can further comprise an additional energy source that provides energy to a remainder of the filament material layer that did not fuse to subsequently form at least a portion of the 3D object.
During printing of the three-dimensional object, certain parameters may be critical to printing high quality parts. One or more sensors can be used to measure one or more temperature(s) along at least one filament material. Such sensors can control intensities, positions, and/or angles of at least the first energy beam. The one or more sensors may be an optical pyrometer. The controller may direct the optical pyrometers to be aimed at the nip points and one or more points before and/or after the compaction unit to detect the temperature of the at least one filament materials as they are deposited. The temperature may vary from region to region of the filament material layer. Factors that affect temperature variance can include variable heater irradiance, variations in absorptivity of the composition, substrate temperature, filament material temperature, unfused filament material temperature, and the use of modifiers and additives. Accordingly, the controller may be programmed so that the image and temperature measurement inputs based upon layer temperature patterns captured by the one or more sensors may be used. The real time temperature inputs and the sintering model may be factors determining an energy requirement pattern for any one or more subsequent layers.
Additionally, the system may comprise a real time simulation program, a sample as shown in
Other parameters critical to printing high quality parts can include substrate temperature, melt zone temperature, as-built geometry, surface roughness and texture and density. Other critical visible or non-visible metrics include characterization of chemistry, bonding or adhesion strength. Measuring one or more structural or internal properties of the part can comprise one or more methods selected from the group consisting of scattered and reflected or absorbed radiation, x-ray imaging, sound waves, scatterometry techniques, ultrasonic techniques, X-ray Photoelectron Spectroscopy (XPS), Four Transform Infrared Spectroscopy (FTIR), Raman Spectroscopy, Laser-Microprobe Mass Spectrometry (LMMS), and any combination thereof. Specific metrology beneficial to the end goals of characterizing the critical process parameters can be used. This in-situ metrology coupled with fast processing of data can enable open or closed loop control of the manufacturing process. Sensors appropriate to the key parameters of interest can be selected and utilized during the part printing process. The sensors may also comprise a camera for detecting light in the infrared or visible portion of the electromagnetic spectrum. Sensors such as IR cameras may be used to measure temperature fields. An image processing algorithm may be used to evaluate data generated by one or more sensors, to extract one or more structural or internal properties of the part. Visual (e.g., high magnification) microscopy from digital camera(s) can be used with proper software processing to detect voids, defects, and surface roughness. In order to utilize this technique, potentially large quantities of data may need to be interrogated using image processing algorithms in order to extract features of interest. Scatterometry techniques may be adapted to provide roughness or other data.
Ultrasonic techniques can be used to measure solid density and fiber and particle density which in turn may be useful in characterizing bond strength and fiber dispersion. The characterization can affect material strength. Ultrasonic techniques can also be used to measure thickness of features. Chemical bonding characterization, which may be useful for understanding fiber and/or matrix adhesion and layer-to-layer bonding, can be performed by multiple techniques such as X-ray Photoelectron Spectroscopy (XPS), Four Transform Infrared Spectroscopy (FTIR) and Raman Spectroscopy and Laser-Microprobe Mass Spectrometry (LMMS). One or more of these techniques may be utilized as part of the in-situ metrology for 3D printing. Ex-situ techniques may also be utilized in order to help provide appropriate calibration data for the in-situ techniques.
Sensors may be positioned on the robot end-effector of the three-dimensional printer in order to provide a sensor moving along with the deposited material. A robot end-effector may be a device positioned at the end of a robotic arm. The robot end-effector may be programmed to interact with its surrounding environment. Sensors may be also located at other various positions. The positions can be on-board the robot, on the effector, or deployed in the environment. Sensors may be in communication with the system. The system can further comprise one or more processors, a communication unit, memory, power supply, and storage. The communications unit can comprise an input and an output. The communication unit can be wired or wireless. The sensor measurements may or may not be stored in a database, and may or may not be used in future simulation and optimization operations. In-situ measurements may also be made using alternative methods with sensors in a cell but not directly attached to the robot end-effector.
The present disclosure provides computer control systems that are programmed to implement methods of the disclosure.
The computer system 501 includes a central processing unit (CPU, also “processor” and “computer processor” herein) 505, which can be a single core or multi core processor, or a plurality of processors for parallel processing. The computer system 501 also includes memory or memory location 510 (e.g., random-access memory, read-only memory, flash memory), electronic storage unit 515 (e.g., hard disk), communication interface 520 (e.g., network adapter) for communicating with one or more other systems, and peripheral devices 525, such as cache, other memory, data storage and/or electronic display adapters. The memory 510, storage unit 515, interface 520 and peripheral devices 525 are in communication with the CPU 505 through a communication bus (solid lines), such as a motherboard. The storage unit 515 can be a data storage unit (or data repository) for storing data. The computer system 501 can be operatively coupled to a computer network (“network”) 530 with the aid of the communication interface 520. The network 530 can be the Internet, an internet and/or extranet, or an intranet and/or extranet that is in communication with the Internet. The network 530 in some cases is a telecommunication and/or data network. The network 530 can include one or more computer servers, which can enable distributed computing, such as cloud computing. The network 530, in some cases with the aid of the computer system 501, can implement a peer-to-peer network, which may enable devices coupled to the computer system 501 to behave as a client or a server.
The CPU 505 can execute a sequence of machine-readable instructions, which can be embodied in a program or software. The instructions may be stored in a memory location, such as the memory 510. The instructions can be directed to the CPU 505, which can subsequently program or otherwise configure the CPU 505 to implement methods of the present disclosure. Examples of operations performed by the CPU 505 can include fetch, decode, execute, and writeback.
The CPU 505 can be part of a circuit, such as an integrated circuit. One or more other components of the system 501 can be included in the circuit. In some cases, the circuit is an application specific integrated circuit (ASIC).
The storage unit 515 can store files, such as drivers, libraries and saved programs. The storage unit 515 can store user data, e.g., user preferences and user programs. The computer system 501 in some cases can include one or more additional data storage units that are external to the computer system 501, such as located on a remote server that is in communication with the computer system 501 through an intranet or the Internet.
The computer system 501 can communicate with one or more remote computer systems through the network 530. For instance, the computer system 501 can communicate with a remote computer system of a user (e.g., customer or operator of a 3D printing system). Examples of remote computer systems include personal computers (e.g., portable PC), slate or tablet PC's (e.g., Apple® iPad, Samsung® Galaxy Tab), telephones, Smart phones (e.g., Apple® iPhone, Android-enabled device, Blackberry®), or personal digital assistants. The user can access the computer system 501 via the network 530.
Methods as described herein can be implemented by way of machine (e.g., computer processor) executable code stored on an electronic storage location of the computer system 501, such as, for example, on the memory 510 or electronic storage unit 515. The machine executable or machine readable code can be provided in the form of software. During use, the code can be executed by the processor 505. In some cases, the code can be retrieved from the storage unit 515 and stored on the memory 510 for ready access by the processor 505. In some situations, the electronic storage unit 515 can be precluded, and machine-executable instructions are stored on memory 510.
The code can be pre-compiled and configured for use with a machine having a processer adapted to execute the code, or can be compiled during runtime. The code can be supplied in a programming language that can be selected to enable the code to execute in a pre-compiled or as-compiled fashion.
Aspects of the systems and methods provided herein, such as the computer system 1801, can be embodied in programming. Various aspects of the technology may be thought of as “products” or “articles of manufacture” typically in the form of machine (or processor) executable code and/or associated data that is carried on or embodied in a type of machine readable medium. Machine-executable code can be stored on an electronic storage unit, such as memory (e.g., read-only memory, random-access memory, flash memory) or a hard disk. “Storage” type media can include any or all of the tangible memory of the computers, processors or the like, or associated modules thereof, such as various semiconductor memories, tape drives, disk drives and the like, which may provide non-transitory storage at any time for the software programming. All or portions of the software may at times be communicated through the Internet or various other telecommunication networks. Such communications, for example, may enable loading of the software from one computer or processor into another, for example, from a management server or host computer into the computer platform of an application server. Thus, another type of media that may bear the software elements includes optical, electrical and electromagnetic waves, such as used across physical interfaces between local devices, through wired and optical landline networks and over various air-links. The physical elements that carry such waves, such as wired or wireless links, optical links or the like, also may be considered as media bearing the software. As used herein, unless restricted to non-transitory, tangible “storage” media, terms such as computer or machine “readable medium” refer to any medium that participates in providing instructions to a processor for execution.
Hence, a machine readable medium, such as computer-executable code, may take many forms, including but not limited to, a tangible storage medium, a carrier wave medium or physical transmission medium. Non-volatile storage media include, for example, optical or magnetic disks, such as any of the storage devices in any computer(s) or the like, such as may be used to implement the databases, etc. shown in the drawings. Volatile storage media include dynamic memory, such as main memory of such a computer platform. Tangible transmission media include coaxial cables; copper wire and fiber optics, including the wires that comprise a bus within a computer system. Carrier-wave transmission media may take the form of electric or electromagnetic signals, or acoustic or light waves such as those generated during radio frequency (RF) and infrared (IR) data communications. Common forms of computer-readable media therefore include for example: a floppy disk, a flexible disk, hard disk, magnetic tape, any other magnetic medium, a CD-ROM, DVD or DVD-ROM, any other optical medium, punch cards paper tape, any other physical storage medium with patterns of holes, a RAM, a ROM, a PROM and EPROM, a FLASH-EPROM, any other memory chip or cartridge, a carrier wave transporting data or instructions, cables or links transporting such a carrier wave, or any other medium from which a computer may read programming code and/or data. Many of these forms of computer readable media may be involved in carrying one or more sequences of one or more instructions to a processor for execution.
The computer system 501 can include or be in communication with an electronic display 535 that comprises a user interface (UI) 540 for providing, for example, a print head tool path to a user. Examples of UI's include, without limitation, a graphical user interface (GUI) and web-based user interface.
Methods and systems of the present disclosure can be implemented by way of one or more algorithms. An algorithm can be implemented by way of software upon execution by the central processing unit 505. The algorithm can, for example, partition a computer model of a part and generate a mesh array from the computer model.
The computer system 501 can include a 3D printing system. The 3D printing system may include one or more 3D printers. A 3D printer may be, for example, a fused filament fabrication (FFF) printer. Alternatively or in addition to, the computer system 501 may be in remote communication with the 3D printing system, such as through the network 530.
In an example, prior to printing the 3D object, a request for production of a requested 3D object is received from a user (e.g., customer). At least a portion of a 3D object may be printed without extrusion by first receiving, in computer memory, a model of the 3D object. Next, a composite filament material may be directed from a spool toward a channel of the print head. The filament material may then be directed through a nozzle towards a substrate that is configured to support the 3D object. A first layer may be deposited corresponding to a portion of the 3D object adjacent to the substrate. The first layer in the X and Y direction may be deposited in accordance with the model of the 3D object. Additional layers may be deposited onto the first layer in the Z direction. A final layer of at filament material may be deposited. The system may comprise a heater cartridge with thermal control from PID controllers connected to thermocouples. During deposition, the heater cartridges may control the temperature for the system in accordance with the parameters for building the model of the 3D object. The thermocouples may provide feedback to the PID controller and may maintain temperature set points throughout the build process. An electromagnetic radiation (e.g., laser) beam may then be used to selectively melt several portions of the first and last deposited layer, thereby increasing adherence and fusion between adjacent layers. A part of the modulated electromagnetic radiation (e.g., laser) beam may be focused by the focusing system, angled by a pair of optical wedges, and irradiated along the filament material for three-dimensional printing. The 3D object may be allowed to cool prior to removing the object from the substrate. The 3D object may be packaged and then delivered to the customer.
In an example, prior to printing the 3D object, a request for production of a requested 3D object is received from a user (e.g., customer). At least a portion of a 3D object may be printed without extrusion by first receiving, in computer memory, a model of the 3D object. Next, a composite filament material may be directed from a spool toward a channel of the print head. The filament material may then be directed through a nozzle towards a substrate that is configured to support the 3D object. A first layer may be deposited corresponding to a portion of the 3D object adjacent to the substrate. The first layer in the X and Y direction may be deposited in accordance with the model of the 3D object. Additional layers may be deposited onto the first layer in the Z direction. A final layer of at filament material may be deposited. The system may comprise a heater cartridge with thermal control from PID controllers connected to thermocouples. During deposition, the heater cartridges may control the temperature for the system in accordance with the parameters for building the model of the 3D object. The thermocouples may provide feedback to the PID controller and may maintain temperature set points throughout the build process. A hot fluid may then be used to selectively melt several portions of the first and last deposited layer, thereby increasing adherence and fusion between adjacent layers. The 3D object may be allowed to cool prior to removing the object from the substrate. The 3D object may be packaged and then delivered to the customer.
In an example, prior to printing the 3D object, a request for production of a requested 3D object is received from a user (e.g., customer). At least a portion of a 3D object may be printed without extrusion by first receiving in computer memory, a model of the 3D object. Next, a composite filament material may be directed from a spool toward a channel of the print head. The filament material may then be directed through a nozzle towards a substrate that is configured to support the 3D object. A first layer can be deposited corresponding to a portion of the 3D object adjacent to the substrate, in accordance with the model of the 3D object. An electromagnetic radiation (e.g., laser) beam may then be used to selectively melt several portions of the first layer. Specifically, the electromagnetic radiation (e.g., laser) beam may be directed to the section of the build object where the subsequent segment may be deposited. A part of the modulated electromagnetic radiation (e.g., laser) beam may be focused by the focusing system, angled by a pair of optical wedges, and irradiated along the filament material for three-dimensional printing. The melt pool can span the entire thickness of the printed segment, thereby increasing the adhesion across segments built in the same layer. Next, a second layer of at least a portion of the 3D object may be deposited. This process may be repeated until the 3D object is built. The system may comprise a heater cartridge with thermal control from PID controllers connected to thermocouples. During deposition, the heater cartridges may control the temperature for the system in accordance with the parameters for building the model of the 3D object. The thermocouples may provide feedback to the PID controller and may maintain temperature set points throughout the build process. Upon completion of the build, the 3D object may be allowed to cool prior to removing the object from the substrate. The 3D object may be packaged and then delivered to the customer.
In an example, prior to printing the 3D object, a request for production of a requested 3D object is received from a user (e.g., customer). At least a portion of a 3D object may be printed without extrusion by first receiving in computer memory, a model of the 3D object. Next, a composite filament material may be directed from a spool toward a channel of the print head. The filament material may then be directed through a nozzle towards a substrate that is configured to support the 3D object. A first layer can be deposited corresponding to a portion of the 3D object adjacent to the substrate, in accordance with the model of the 3D object. A convective hot fluid (e.g., hot air) may then be used to selectively melt several portions of the first layer. Specifically, the convective hot fluid may be directed to the section of the build object where the subsequent segment may be deposited. The melt pool can span the entire thickness of the printed segment, thereby increasing the adhesion across segments built in the same layer. Next, a second layer of at least a portion of the 3D object may be deposited. This process may be repeated until the 3D object is built. The system may comprise a heater cartridge with thermal control from PID controllers connected to thermocouples. During deposition, the heater cartridges may control the temperature for the system in accordance with the parameters for building the model of the 3D object. The thermocouples may provide feedback to the PID controller and may maintain temperature set points throughout the build process. Upon completion of the build, the 3D object may be allowed to cool prior to removing the object from the substrate. The 3D object may be packaged and then delivered to the customer.
In an example, prior to printing the 3D object, a request for production of a requested 3D object may be received from a user (e.g., customer). At least a portion of a 3D object may be printed without extrusion by first receiving in computer memory, a model of the 3D object. Next, a composite filament material may be directed from a spool through an extender mechanism toward a channel of the print head. The extender mechanism can include a motor for dispensing at least one filament material. This composite filament material may be directed from the spool to a channel of the print head through a nozzle towards the substrate. Additionally, the substrate can include a drive mechanism for moving the substrate as each layer is deposited onto the substrate.
From the nozzle, the composite filament material may be directed to at least one freely suspended roller, thereby depositing a first layer corresponding to a portion of the 3D object on the substrate. The composite filament may be fed into a nozzle at an angle such that it is fed under at least one freely suspended roller at a nip point as the freely suspended roller presses the filament material exiting from the nozzle. The freely suspended roller may be designed to control the bend radii of the composite filament material.
Next, the second layer of the 3D object may be deposited. One or more additional layers can be deposited adjacent to the first layer prior to depositing the second layer. At least a first energy beam from at least one energy source may be used to selectively melt at least a portion of the first layer and/or the second layer, thereby forming at least a portion of the 3D object. The energy beam may be an electromagnetic radiation (e.g., laser) beam. The energy source may be in optical communication with one or more beam splitters, which one or more beam splitters can split an energy beam from at least one light source into one or more beamlets that yields at least the first energy beam.
The energy source may be an electromagnetic radiation source (e.g., laser) head that is mounted on a robot or similar mechanism that swivels around the vertical axis enabling deposition in any direction in the plane of deposition. During deposition, optical pyrometers may be aimed at the substrate to detect the temperature of the composite filament materials as they are deposited. A real time simulation program (
In an example, prior to printing the 3D object, a request for production of a requested 3D object is received from a user (e.g., customer). At least a portion of a 3D object may be printed with extrusion by first receiving, in computer memory, a model of the 3D object. Next, a composite filament material may be directed from a spool toward a channel of the print head. The filament material may then be directed and extruded through a nozzle towards a substrate that is configured to support the 3D object. A first layer may be deposited corresponding to a portion of the 3D object adjacent to the substrate. The first layer in the X and Y direction may be deposited in accordance with the model of the 3D object. Additional layers may be deposited onto the first layer in the Z direction. A final layer of at filament material may be deposited. The system may comprise a heater cartridge with thermal control from PID controllers connected to thermocouples. During deposition, the heater cartridges may control the temperature for the system in accordance with the parameters for building the model of the 3D object. The thermocouples may provide feedback to the PID controller and may maintain temperature set points throughout the build process. An electromagnetic radiation (e.g., laser) beam may then be used to selectively melt several portions of the first and last deposited layer, thereby increasing adherence and fusion between adjacent layers. A part of the modulated electromagnetic radiation (e.g., laser) beam may be focused by the focusing system, angled by a pair of optical wedges, and irradiated along the filament material for three-dimensional printing. The 3D object may be allowed to cool prior to removing the object from the substrate. The 3D object may be packaged and then delivered to the customer.
In an example, prior to printing the 3D object, a request for production of a requested 3D object is received from a user (e.g., customer). At least a portion of a 3D object may be printed with extrusion by first receiving, in computer memory, a model of the 3D object. Next, a composite filament material may be directed from a spool toward a channel of the print head. The filament material may then be directed and extruded through a nozzle towards a substrate that is configured to support the 3D object. A first layer may be deposited corresponding to a portion of the 3D object adjacent to the substrate. The first layer in the X and Y direction may be deposited in accordance with the model of the 3D object. Additional layers may be deposited onto the first layer in the Z direction. A final layer of at filament material may be deposited. The system may comprise a heater cartridge with thermal control from PID controllers connected to thermocouples. During deposition, the heater cartridges may control the temperature for the system in accordance with the parameters for building the model of the 3D object. The thermocouples may provide feedback to the PID controller and may maintain temperature set points throughout the build process. A hot fluid may then be used to selectively melt several portions of the first and last deposited layer, thereby increasing adherence and fusion between adjacent layers. The 3D object may be allowed to cool prior to removing the object from the substrate. The 3D object may be packaged and then delivered to the customer.
In an example, prior to printing the 3D object, a request for production of a requested 3D object is received from a user (e.g., customer). At least a portion of a 3D object may be printed with extrusion by first receiving in computer memory, a model of the 3D object. Next, a composite filament material may be directed from a spool toward a channel of the print head. The filament material may then be directed and extruded through a nozzle towards a substrate that is configured to support the 3D object. A first layer can be deposited corresponding to a portion of the 3D object adjacent to the substrate, in accordance with the model of the 3D object. An electromagnetic radiation (e.g., laser) beam may then be used to selectively melt several portions of the first layer. Specifically, the electromagnetic radiation (e.g., laser) beam may be directed to the section of the build object where the subsequent segment may be deposited. A part of the modulated electromagnetic radiation (e.g., laser) beam may be focused by the focusing system, angled by a pair of optical wedges, and irradiated along the filament material for three-dimensional printing. The melt pool can span the entire thickness of the printed segment, thereby increasing the adhesion across segments built in the same layer. Next, a second layer of at least a portion of the 3D object may be deposited. This process may be repeated until the 3D object is built. The system may comprise a heater cartridge with thermal control from PID controllers connected to thermocouples. During deposition, the heater cartridges may control the temperature for the system in accordance with the parameters for building the model of the 3D object. The thermocouples may provide feedback to the PID controller and may maintain temperature set points throughout the build process. Upon completion of the build, the 3D object may be allowed to cool prior to removing the object from the substrate. The 3D object may be packaged and then delivered to the customer.
In an example, prior to printing the 3D object, a request for production of a requested 3D object is received from a user (e.g., customer). At least a portion of a 3D object may be printed with extrusion by first receiving in computer memory, a model of the 3D object. Next, a composite filament material may be directed from a spool toward a channel of the print head. The filament material may then be directed and extruded through a nozzle towards a substrate that is configured to support the 3D object. A first layer can be deposited corresponding to a portion of the 3D object adjacent to the substrate, in accordance with the model of the 3D object. A convective hot fluid (e.g., hot air) may then be used to selectively melt several portions of the first layer. Specifically, the convective hot fluid may be directed to the section of the build object where the subsequent segment may be deposited. The melt pool can span the entire thickness of the printed segment, thereby increasing the adhesion across segments built in the same layer. Next, a second layer of at least a portion of the 3D object may be deposited. This process may be repeated until the 3D object is built. The system may comprise a heater cartridge with thermal control from PID controllers connected to thermocouples. During deposition, the heater cartridges may control the temperature for the system in accordance with the parameters for building the model of the 3D object. The thermocouples may provide feedback to the PID controller and may maintain temperature set points throughout the build process. Upon completion of the build, the 3D object may be allowed to cool prior to removing the object from the substrate. The 3D object may be packaged and then delivered to the customer.
In an example, prior to printing the 3D object, a request for production of a requested 3D object may be received from a user (e.g., customer). At least a portion of a 3D object may be printed with extrusion by first receiving in computer memory, a model of the 3D object. Next, a composite filament material may be directed from a spool through an extender mechanism toward a channel of the print head. The composite filament material may be extruded from the nozzle of the print heat. The extender mechanism can include a motor for dispensing at least one filament material. This composite filament material may be directed from the spool to a channel of the print head through a nozzle towards the substrate. Additionally, the substrate can include a drive mechanism for moving the substrate as each layer is deposited onto the substrate.
From the nozzle, the composite filament material may be directed to at least one freely suspended roller, thereby depositing a first layer corresponding to a portion of the 3D object on the substrate. The composite filament may be fed into a nozzle at an angle such that it is fed under at least one freely suspended roller at a nip point as the freely suspended roller presses the filament material exiting from the nozzle. The freely suspended roller may be designed to control the bend radii of the composite filament material.
Next, the second layer of the 3D object may be deposited. One or more additional layers can be deposited adjacent to the first layer prior to depositing the second layer. At least a first energy beam from at least one energy source may be used to selectively melt at least a portion of the first layer and/or the second layer, thereby forming at least a portion of the 3D object. The energy beam may be an electromagnetic radiation (e.g., laser) beam. The energy source may be in optical communication with one or more beam splitters, which one or more beam splitters can split an energy beam from at least one light source into one or more beamlets that yields at least the first energy beam.
The energy source may be an electromagnetic radiation source (e.g., laser) head that is mounted on a robot or similar mechanism that swivels around the vertical axis enabling deposition in any direction in the plane of deposition. During deposition, optical pyrometers may be aimed at the substrate to detect the temperature of the composite filament materials as they are deposited. A real time simulation program (
A prototype bicycle of the three-dimensional (3D) printed single-piece bicycle frame is shown in
A model bicycle of the three-dimensional (3D) printed single-piece bicycle frame is shown in
While preferred embodiments of the present invention have been shown and described herein, it will be obvious to those skilled in the art that such embodiments are provided by way of example only. It is not intended that the invention be limited by the specific examples provided within the specification. While the invention has been described with reference to the aforementioned specification, the descriptions and illustrations of the embodiments herein are not meant to be construed in a limiting sense. Numerous variations, changes, and substitutions will now occur to those skilled in the art without departing from the invention. Furthermore, it shall be understood that all aspects of the invention are not limited to the specific depictions, configurations or relative proportions set forth herein which depend upon a variety of conditions and variables. It should be understood that various alternatives to the embodiments of the invention described herein may be employed in practicing the invention. It is therefore contemplated that the invention shall also cover any such alternatives, modifications, variations or equivalents. It is intended that the following claims define the scope of the invention and that methods and structures within the scope of these claims and their equivalents be covered thereby.
This application claims priority to: i. U.S. Provisional Patent Application No. 62/976,866, filed Feb. 14, 2020, andii. U.S. Provisional Patent Application No. 62/849,748, filed May 17, 2019, andiii. U.S. Provisional Patent Application No. 62/832,817, filed Apr. 11, 2019, each of which is entirely incorporated herein by reference.
| Number | Date | Country | |
|---|---|---|---|
| 62832817 | Apr 2019 | US | |
| 62849748 | May 2019 | US | |
| 62976866 | Feb 2020 | US |