SIO2-LAYERED DOUBLE HYDROXIDE MICROSPHERES AND METHODS OF MAKING THEM

Abstract
Porous particles comprising an active ingredient and a coating exhibiting greater dissolution rate in aqueous media than in alcoholic media are disclosed. A process for the manufacture of the particles is also disclosed, as well as tamper-proof particles and solid dosage forms comprising the coated particles. The differential solubility characteristics of the particle coating allow the particles to be incorporated into abuse-deterrent medicaments.
Description

The present invention relates to new SiO2-layered double hydroxide (LDH) microspheres and to methods of making the same.


Layered double hydroxides (LDHs) are a class of compounds which comprise two or more metal cations and have a layered structure. A review of LDHs is provided in Structure and Bonding; Vol. 119, 2005 Layered Double Hydroxides ed. X Duan and D. G. Evans. The hydrotalcites, perhaps the most well-known examples of LDHs, have been studied for many years. LDHs can intercalate anions between the layers of the structure.


Core shell particles are described in the literature by “core@shell” (for example by Teng et al., Nano Letters, 2003, 3, 261-264, or by “core/shell” (for example J. Am. Chem Soc., 2001, 123, pages 7961-7962). We have adopted the “core@shell” nomenclature as it is emerging as the more commonly accepted abbreviation.


SiO2/LDH core-shell microspheres are described by Shao et al, Chem. Mater. 2012, 24, pages 1192-1197. Prior to treatment with a metal precursor solution, the SiO2 microspheres are primed by dispersing them in an Al(OOH) primer sol for two hours with vigorous agitation followed by centrifuging, washing with ethanol and drying in air for 30 minutes. This priming treatment of the SiO2 microspheres was repeated 10 times before the SiO2 spheres thus coated with a thin Al(OOH) film were autoclaved at 100° C. for 48 hours in a solution of Ni(NO3)2.6H2O and urea. Hollow SiO2—NiAl-LDH microspheres obtained by this process were reported as exhibiting excellent pseudocapacitance performance. Unfortunately, the requirement for the Al(OOH) priming of the SiO2 surface, prior to LDH growth, makes this process unsuitable for use on an industrial scale.


Chen et al, J. Mater. Chem. A, 1, 3877-3880 describes the synthesis of SiO2@MgAl-LDHs having use in the removal of pharmaceutical pollutants from water. The synthesis described comprises coprecipitating LDH from a metal precursor solution containing the SiO2 microspheres followed by ultrasound assisted direct growth of LDH nanosheets on the surface of the SiO2 microspheres. Unfortunately, the reported method does not allow the morphology of the surface LDHs to be tuned and the surface area of the product SiO2@LDHs is not high.


It is an object of the present invention to provide a facile method of making SiO2@LDH microspheres which overcomes drawbacks of the prior art, which in particular does not require a step of initially forming an Al(OOH) film on the SiO2 surface prior to treatment with the metal precursor solution or the requirement for ultrasound assistance in achieving LDH growth on the SiO2 surface. It is also an object of the present invention to provide SiO2@LDHs wherein the thickness, size and morphology of the LDH layer can each be tuned easily for different applications. It is yet a further object of the present invention to provide SiO2@LDHs that have high surface area.


This object is achieved by a method of making silica-layered double hydroxide microspheres having the general formula I





(SiO2)p@{[Mz+(1-x)M′y+x(OH)2]a+(Xn−)a/n.bH2O.c(AMO-solvent)}q  (I)


wherein,


Mz+ and M′y+ are two different charged metal cations;


z=1 or 2;


y=3 or 4;


0<x<0.9;


b is 0 to 10;


c is 0 to 10;


p>0,


q>0;


Xn− is an anion; with n>0 (preferably 1-5)


a=z(1−x)+xy−2; and


the AMO-solvent is an 100% aqueous miscible organic solvent;


which method comprises the steps:

  • (a) contacting silica microspheres and a metal ion containing solution containing metal ions Mz+ and M′y+ in the presence of a base and anion solution;
  • (b) collecting the product; and
  • (c) optionally treating the product with AMO-solvent and recovering the solvent treated material.


According to a further aspect of the invention, there is provided a silica-layered double hydroxide microsphere or a plurality thereof obtained, directly obtained or obtainable by a process defined herein.


A silica-layered double hydroxide microsphere is known to comprise a silica microsphere having solid LDH attached to its surface. Such a material, denoted as SiO2@LDH, may be a core-shell material where the SiO2 microsphere is a solid sphere, a yolk-shell material where the SiO2 microsphere comprises an outer shell and a smaller SiO2 sphere contained within the outer shell wherein there is a hollow portion between the smaller sphere and the inner surface of the outer shell, or a hollow shell material wherein the SiO2 microsphere has a hollow interior.


In an embodiment, the process does not include a step of growing the LDH on the SiO2 surface using ultrasound.


The SiO2 microspheres used in the preparation of the SiO2@LDH microspheres according to the invention may be solid, yolk-shell or hollow microspheres and are commercially-available in a variety of sizes (diameters). However, SiO2 microspheres may be prepared by a modified Stöber process involving ammonia catalysed hydrolysis and condensation of tetraethylorthosilicate using ethanol as solvent and cetyltrimethylammonium bromide as surfactant porogen, as is well known in the art.


In an embodiment, the silica microspheres do not contain any iron.


In another embodiment, the silica microspheres comprise greater than 75% w/w SiO2. Suitably, silica microspheres comprise greater than 85% w/w SiO2. More suitably, the silica microspheres comprise greater than 95% w/w SiO2. Most suitably, the silica microspheres comprise greater than 98% w/w SiO2.


In another embodiment, the silica microspheres consist essentially of SiO2.


In another embodiment, the silica microspheres consist of SiO2.


In another embodiment, the SiO2 microspheres have an average diameter of between 0.15 μm and 8 μm. Suitably, the SiO2 microspheres have an average diameter of between 0.15 μm and 2 μm. More suitably, the SiO2 microspheres have an average diameter of between 0.15 μm and 1 μm. Most suitably, the SiO2 microspheres have an average diameter of between 0.2 μm and 0.8 μm.


The LDH nanosheets grown on the surface of the SiO2 microspheres comprise, and preferably consist of, LDH represented by the general formula I





[Mz+1-xM′y+x(OH)2]a+(Xn−)a/n.bH2O.c(AMO-solvent)  (I),


wherein Mz+ and M′+ are different charged metal cations; z=1 or 2; y=3 or 4; 0<x<0.9; b=0-10; c=0-10, Xn− is an anion, n is the charge on the anion, n>0 (preferably 1-5); a=z(1−x)+xy−2; and AMO-solvent is an 100% aqueous miscible organic solvent.


As stated above, Mz+ and M′y+ are different charged metal cations. Having regard to the fact that z=1 or 2, M will be either a monovalent metal cation or a divalent metal cation. When z=1, M is either a single monovalent metal cation or two or more different monovalent metal cations. When z=2, M is either a single divalent metal cation or two or more different divalent metal cations. In an embodiment, z=2, i.e. M is one or more divalent metal cations. M′, in view of the fact that y=3 or 4, will be a trivalent metal cation or a tetravalent metal cation. When z=3, M′ is either a single trivalent metal cation or two or more different trivalent metal cations. When z=4, M′ is either a single tetravalent metal cation or two or more different tetravalent metal cations. In an embodiment, y=3, i.e. M′ is one or more trivalent metal cations.


A preferred example of a monovalent metal, for M, is Li. Examples of divalent metals, for M, include Ca, Mg, Zn, Fe, Co, Cu and Ni and mixtures of two or more of these. Preferably, the divalent metal M, if present, is Ca, Ni or Mg. Examples of metals, for M′, include Al, Ga, In, Y and Fe. Preferably, M′ is a trivalent cation, for example Al. Preferably, the LDH will be a Li—Al, an Mg—Al or a Ca—Al LDH.


The anion Xn− in the LDH is any appropriate inorganic or organic anion. Examples of anions that may be used, as Xn−, in the LDH include carbonate, hydroxide, nitrate, borate, sulphate, phosphate and halide (F, Cl, Br, I) anions. Preferably, the anion Xn−, is selected from CO32−, NO3 and Cl.


The AMO-solvent is any aqueous miscible organic solvent, i.e. a solvent which is 100% miscible with water. Examples of suitable water-miscible organic solvents for use in the present invention include one or more of acetone, acetonitrile, dimethylformamide, dimethylsulfoxide, dioxane, ethanol, methanol, n-propanol, isopropanol, or tetrahydrofuran. Suitably, the water-miscible organic solvents for use in the present invention is selected from lower (1-3C) alkanols and acetone. Preferably, the AMO-solvent is methanol, ethanol or acetone, especially acetone and ethanol.


According to one preferred embodiment, the layered double hydroxides are those having the general formula I above


in which Mz+ is a divalent metal cation;


M′+ is a trivalent metal cation; and


each of b and c is a number>zero, which gives compounds optionally hydrated with a stoichiometric amount or a non-stoichiometric amount of water and/or an aqueous-miscible organic solvent (AMO-solvent), such as acetone or ethanol.


Preferably, in the LDH of the above formula, M is Mg or Ca and M′ is Al. The counter anion Xn− is typically selected from CO32−, OH, F, Cl, Br, I, SO42−, NO3 and PO43−. In a most preferred embodiment, the LDH will be one wherein M is Mg, M′ is Al and Xn− is CO32−.


In carrying out the method of the invention, preferably the SiO2 microspheres are dispersed in an aqueous solution containing the desired anion salt, for example Na2CO3. A metal precursor solution, i.e. a solution combining the required monovalent or divalent metal cations and the required trivalent cations may then be added, preferably drop-wise, into the dispersion of the SiO2 microspheres. Preferably, the addition of the metal precursor solution is carried out under stirring. The pH of the reaction solution is preferably controlled within the pH range 8 to 12, typically 8-11, more preferably 9 to 10.


In an embodiment, the method of the present invention does not include ammonia.


The structure of the SiO2@LDH microspheres can be controlled by the tendency of SiO2 to dissolve or partially dissolve at higher temperatures and higher pH values. For instance, carrying out the addition of the metal precursor solution to the dispersion of SiO2 microspheres at room temperature and at pH 10 gives solid SiO2@LDH particles although by raising the temperature of the reaction solutions, for instance to 40° C., it is possible to obtain yolk shell SiO2@LDH particles. By carrying out the reaction at room temperature but using a higher solution pH, e.g. pH 11, it is possible to produce hollow shell SiO2@LDH particles.


Typically, NaOH may be used to adjust the pH of the solution.


During the reaction, the LDH produced from the metal precursor solution reaction is formed on the SiO2 surfaces of the microspheres as nanosheets.


It is preferred that the temperature of the metal ion containing solution in step (a) is within a range of from 20 to 150° C. More preferably, from 20 to 80° C.


In a preferred embodiment, the silica-layered double hydroxide microspheres have specific surface area of at least 100 m2/g, preferably at least 177 m2/g, and more preferably at least 200 m2/g, and even more preferably at least 250 m2/g.


Suitably, the silica-layered double hydroxide microspheres comprise solid silica mircrosphere cores and have specific surface area of at least 100 m2/g.


Suitably, the silica-layered double hydroxide microspheres comprise yolk-shell mircrosphere cores and have specific surface area of at least 100 m2/g.


Suitably, the silica-layered double hydroxide microspheres comprise hollow-shell mircrosphere cores and have specific surface area of at least 130 m2/g.


Most preferred, the silica-layered double hydroxide microspheres have at least one structure from hollow-shell, yolk-shell and solid core-shell structures.


In a preferred embodiment, the silica-layered double hydroxide microspheres have a thickness of layered double hydroxide layer larger than 65 nm, preferably larger than 110 nm, more preferably larger than 160 nm.


The obtained solid product is collected from the aqueous medium. Examples of methods of collecting the solid product include centrifugation and filtration. Typically, the collected solid may be re-dispersed in water and then collected again. Preferably, the collection and re-dispersion steps are repeated twice.


The finally-obtained solid material may then be subjected to drying, for instance, in an oven for several hours.


In the event that a product containing AMO-solvent is required, the material obtained after the collection/re-dispersion procedure described above may be washed with, and preferably also re-dispersed in, the desired solvent, for instance acetone or ethanol. If re-dispersion is employed, the dispersion is preferably stirred. Stirring for more than 2 hours in the solvent is preferable. The final product may then be collected from the solvent and then dried, typically in an oven for several hours.


In an embodiment, the LDH layer is formed in situ. Suitably, the LDH is formed and coated onto the silica microspheres in situ.


The growth of LDH nanosheets on the surface of the SiO2 microspheres is “tuneable”. That is to say, by varying the chemistry of the precursor solution, pH of the reaction medium and the rate of addition of the precursor solution to the dispersion of SiO2 microspheres, the extent of, and the length and/or thickness of, the LDH nanosheets formed on the SiO2 surface can be varied.


The production of the SiO2@LDH microspheres according to the invention can be carried out as a batch process or, with appropriate replenishment of reactants, as a continuous process.


The products of the method of the present invention where the SiO2@LDHs are treated with solvent, i.e. the products having the formula I above where c is greater than zero, are a solution to the problem underlying the present invention per se.


Thus, according to a further aspect, the present invention provides silica-layered double hydroxide microspheres having the formula I





(SiO2)p@{[Mz+(1-x)M′y+x(OH)2]a+(Xn−)a/n.bH2O.c(AMO-solvent)}q  (I)


wherein,


Mz+ and M′y+ are two different charged metal cations;


z=1 or 2;


y=3 or 4;


0<x<0.9;


b is 0 to 10;


c is 0 to 10;


p>0,


q>0;


Xn− is an anion; with n>0 (preferably 1-5)


a=z(1−x)+xy−2; and


AMO-solvent is an 100% aqueous miscible organic solvent.


M′ in formula I above is preferably Al.


M in formula I above is preferably Li, Mg, Ga, In, Ni, Co, Cu or Ca, more preferably Mg or Ni.


According to an embodiment, Xn− in formula I above is selected from carbonate, nitrate, borate, sulphate, phosphate, hydroxide and halide anions (F, Cl, Br, I). Preferably, the anion Xn− is selected from CO32−, NO3 and Cl.


According to a particularly preferred embodiment, the SiO2@LDH microspheres of the invention contain LDH having the formula I above in which M is Mg, M′ is Al and Xn− is CO3.


The AMO-solvent in formula I above is one that is miscible in water, especially one that is 100% miscible in water. Examples of solvents that can be used include methanol, ethanol and acetone. According to a preferred embodiment of the invention, the solvent is ethanol or acetone.


SiO2@LDHs according to the present invention may be used as catalysts and/or catalyst supports.


PARTICULARLY PREFERRED EMBODIMENTS

The following represent particular embodiments of the silica-layered double hydroxide:

  • 1.1 The silica-layered double hydroxide microspheres have the general formula I





(SiO2)p@{[Mz+(1-x)M′y+x(OH)2]a+(Xx−)a/n.bH2O.c(AMO-solvent)}q  (I)

    • wherein,
    • Mz+ is selected from Li+, Ca2+, Ni2+ or Mg2+, and M′y+ is Al3+ or Fe3+;
    • 0<x<0.9;
    • b is 0 to 10;
    • c is 0 to 10;
    • p>0,
    • q>0;
    • Xn− is selected from carbonate, hydroxide, nitrate, borate, sulphate, phosphate and halide (F, Cl, Br, I) anions; with n>0 (preferably 1-5) a=z(1−x)+xy−2; and
    • the AMO-solvent is selected from a lower (1-3C) alkanol (e.g. ethanol) or acetone.
  • 1.2 The silica-layered double hydroxide microspheres have the general formula I





(SiO2)p@{[Mz+(1-x)M′y+x(OH)2]a+(Xn−)a/n.bH2O.c(AMO-solvent)}q  (I)

    • wherein,
    • Mz+ is selected from Li+, Ca2+, Ni2+ or Mg2+, and M′y+ is Al3+;
    • 0<x<0.9;
    • b is 0 to 10;
    • c is 0 to 10;
    • p>0,
    • q>0;
    • Xn− is selected from CO32−, NO3 or Cl; with n>0 (preferably 1-5)
    • a=z(1−x)+xy−2; and
    • the AMO-solvent is acetone or ethanol.
  • 1.3 The silica-layered double hydroxide microspheres have the general formula Ia





(SiO2)p@{[Mz+(1-x)Al3+x(OH)2]a+(Xn−)a/n.bH2O.c(AMO-solvent)}q  (Ia)

    • wherein,
    • Mz+ is selected from Li+, Ca2+, Ni2+ or Mg2+;
    • 0<x<0.9;
    • b is 0 to 10;
    • c is 0 to 10;
    • p>0,
    • q>0;
    • Xn− is selected from CO32−, NO3 or Cl; with n>0 (preferably 1-5)
    • a=z(1−x)+xy−2; and
    • the AMO-solvent is acetone or ethanol.
  • 1.4 The silica-layered double hydroxide microspheres have the general formula Ia





(SiO2)p@{[Mg2+(1-x)Al3+x(OH)2]a+(Xn−)a/n.bH2O.c(AMO-solvent)}q  (Ia)

    • wherein,
    • 0<x<0.9;
    • b is 0 to 10;
    • c is 0 to 10;
    • p>0,
    • q>0;
    • Xn− is selected from CO32−, NO3 or Cl; with n>0 (preferably 1-5)
    • a=z(1−x)+xy−2; and
    • the AMO-solvent is acetone or ethanol.
  • 1.5 The silica-layered double hydroxide microspheres have the general formula Ib





(SiO2)p@{[Mg2+(1-x)Al3+x(OH)2]a+(CO32)a/n.bH2O.c(acetone)}q  (Ib)

    • wherein,
    • 0<x<0.9;
    • b is 0 to 10;
    • c is 0 to 10;
    • p>0,
    • q>0;
    • a=z(1−x)+xy−2.
  • 1.6 The silica-layered double hydroxide microspheres have the general formula Ic





(SiO2)0.04@{[Mg0.75Al0.25(OH)2](CO3)0.125.1.34(H2O)}0.05  (Ic)

  • 1.7 The silica-layered double hydroxide microspheres have the general formula Id





(SiO2)0.04@{[Mg0.75Al0.25(OH)2](CO3)0.125.0.29(H2O).0.15(acetone)}0.05  (Id)


Preferred, suitable, and optional features of any one particular aspect of the present invention are also preferred, suitable, and optional features of any other aspect.





FIGURES


FIG. 1. XRD patterns showing three sizes of silica nanoparticles (a) 300 nm, (b) 550 nm and (c) 800 nm.



FIG. 2. TGA curves of differently sized silica nanoparticles (a) 800 nm, (b) 550 nm and (c) 300 nm.



FIG. 3. SEM images of 800 nm silica microspheres prepared via seeded growth.



FIG. 4. XRD patterns of (a) 550 nm silica microspheres, (b) LDH nano-particles and (c) SiO2@LDH microspheres ((b) and (c) were synthesized according to example 1).



FIG. 5. Percentage weight loss of (a) LDH, (b) SiO2@LDH microspheres and (c) silica nanoparticles ((a) and (b) were synthesized according to example 1).



FIG. 6. 29Si Solid-state NMR of (a) silica microspheres and (b) SiO2@LDH microspheres ((b) were synthesized according to example 1).



FIG. 7. XRD patterns of SiO2@LDH microspheres prepared at different pH conditions (a) ammonia method (example 4), (b) pH 9, (c) pH 10 and (d) pH 11 ((b)-(d): example 1).



FIG. 8. TGA of SiO2@LDH microspheres prepared at different pH conditions (a) pH 11, (b) pH 10, (c) ammonia method and (d) pH 9.



FIG. 9. TEM images of SiO2@LDH microspheres synthesized according to example 1 except at different temperatures (a) room temperature (b) 40° C.



FIG. 10. TGA and dTGA curves of SiO2@LDH microspheres prepared according to example 1 except at different temperature (a) room temperature and (b) 40° C., (i) TGA curve, (ii) dTGA curve.



FIG. 11. Solid state NMR (a)29Si (b)27Al. SiO2 @ LDH prepared according to example 1 except at different temperature (i) at room temperature (ii) at 40° C.



FIG. 12. XRD patterns of SiO2@LDH microspheres prepared with different Mg:Al ratios (a) 1:1 (example 2), (b) 3:1 (example 3).



FIG. 13. XRD patterns of SiO2@LDH microspheres prepared according to example 1 (a) conventional water washing (b) acetone washing.



FIG. 14. TGA of SiO2@LDH microspheres prepared according to example 2 (a) conventional water washing (b) acetone washing.



FIG. 15. TEM image of SiO2@LDH microspheres with different ratio of Mg/Al (a) 1:1 (example 2), (b) 2:1 (example 1) and (c) 3:1 (example 3).



FIG. 16. TEM image of SiO2@LDH microspheres according to example 1 except with different size of silica (a) 300 nm, (b) 550 nm and (c) 800 nm.



FIG. 17. TEM image of SiO2@LDH microspheres with different morphology (a) solid (example 1), (b) yolk-shell (example 1 at 40° C.) and (c) hollow (example 1 at pH 11).



FIG. 18. XRD patterns of SiO2@AMO-LDH with an Mg:Al=3:1 (a) pH=10 and room temperature (b) pH=10 and 40° C. (c) pH=11 and 40° C.



FIG. 19. XRD patterns of SiO2@AMO-LDH with Mg:Ni:Al=2.7:0.3:1 (a) pH=10 and room temperature (b) pH=10 and 40° C. (c) pH=11 and 40° C.



FIG. 20. XRD patterns of SiO2@AMO-LDH with an Mg:Al:Fe=3:0.9:0.1 (a) pH=10 and room temperature (b) pH=10 and 40° C. (c) pH=11 and 40° C.;



FIG. 21. TEM image of SiO2@AMO LDH microspheres according to examples 5 and 7 at pH=10 and room temperature (a) Mg:Al=3:1 (b) Mg:Al:Fe=3:0.9:0.1.



FIG. 22. TEM image of SiO2@AMO-LDH with Mg:Ni:Al=2.7:0.3:1 microspheres with different morphology according to example 6 (a) pH=10 and room temperature (b) pH=10 and 40° C. (c) pH=11 and 40° C.





EXPERIMENTAL METHODS
1. General Details
1.1 Powder X-Ray Diffraction

Powder X-ray diffraction (XRD) data were collected on a PANAnalytical X'Pert Pro diffractometer in reflection mode and a PANAnalytical Empyrean Series 2 at 40 kV and 40 mA using Cu Kα radiation (α1=1.54057 Å, α2=1.54433 Å, weighted average=1.54178 Å). Scans were recorded from 5°≤0≤70° with varying scan speeds and slit sizes. Samples were mounted on stainless steel sample holders. The peaks at 43-44° are produced by the XRD sample holder and can be disregarded.


1.2 Thermogravimetric Analysis

Thermogravimetric analysis (TGA) measurements were collected using a Netzsch STA 409 PC instrument. The sample (10-20 mg) was heated in a corundum crucible between 30° C. and 800° C. at a heating rate of 5° C. min-1 under a flowing stream of nitrogen.


1.3 Solid State NMR Spectroscopy


29Si and 27Al MAS NMR spectra were recorded on a Varian Chemagnetics CMX Infinity 200 (4.7 T). Samples were packed in 7.5 mm zirconia rotors. A double resonance MAS probe was used for all measurements and a MAS rate of 4 kHz for 29Si, whereas MAS rate of 6 kHz was used for 27Al. 27Al MAS NMR spectra were acquired with a single pulse excitation applied using a short pulse length (0.7 μs). Each spectrum resulted from 2000 scans separated by 1 s delay. The 27Al chemical shifts are referenced to an aqueous solution of Al(NO3)3 (δ=0 ppm). In order to obtain the quantitative 29Si DPMAS NMR spectra, 5000 transients were typically acquired with an acquisition time of 68 ms (1024 data points zero filled to 16K) and recycle delay of 30 s. All 29Si spectra were externally referenced to kaolinite (taken to be at δ=−91.7 ppm on a scale where δ(TMS)=0 ppm) as a secondary reference.


1.4 Transmission Electron Microscopy

Transmission Electron Microscopy (TEM) analysis was performed on a JEOL 2100 microscope with an accelerating voltage of 200 kV. Particles were dispersed in water or ethanol with sonication and then cast onto copper grids coated with carbon film and left to dry.


1.5 Scanning Electron Microscopy

Scanning Electron Microscopy (SEM) analysis was performed on a JEOL JSM 6610 scanning electron microscope. Particles were dispersed in water and cast onto a clean silica wafer. Before imaging, the samples were coated with a thin platinum layer to prevent charging and to improve the image quality. Energy dispersive X-ray spectroscopy (EDX), also carried out on this instrument, was used to determine the relative quantities of constituent elements on the surface of the sample.


1.6 Brunauer-Emmett-Teller Surface Area Analysis

Brunauer-Emmett-Teller (BET) specific surface areas were measured from the N2 adsorption and desorption isotherms at 77 K collected from a Quantachrome Autosorb surface area and pore size analyser.


Example 1

Silica spheres (100 mg, 550 nm) were dispersed in deionised water (20 mL) using ultrasound treatment. After 30 min., Na2CO3 (0.96 mmol) was added to the solution and a further 5 min of sonication was carried out to form solution A. Next an aqueous solution (19.2 mL) containing Mg(NO3)2.6H2O (0.96 mmol) and Al(NO3)3.9H2O (0.48 mmol) was added at a rate of 60 mL/h to solution A under vigorous stirring at room temperature. The pH of the reaction solution was controlled to be 10 with the addition of 1 M NaOH. The obtained solid was collected with centrifugation at 4000 rpm for 5 min and then re-dispersed in deionised water (40 mL) and stirred for 1 h. The collection and re-dispersion were repeated twice. Afterward, the solid was washed with acetone (40 mL) and then re-dispersed in acetone (40 mL) and left to stir overnight. The solid was then dried under vacuum.


The SiO2@LDH obtained in this Example, before the treatment with acetone, has the formula:—





(SiO2)0.04@{[Mg0.75Al0.25(OH)2](CO3)0.125.1.34(H2O)}0.05


The SiO2@AMO-LDH, obtained after acetone treatment, has the formula:—





(SiO2)0.04@{[Mg0.75Al0.25(OH)2](CO3)0.125.0.29(H2O).0.15(acetone)}0.05


Yolk shell particles were obtained by carrying out the addition of the aqueous solution containing the Mg(NO3)2.6H2O and Al(NO3)3.9H2O at 40° C. and pH10.


Hollow shell particles were obtained by carrying out the addition of the aqueous solution containing Mg(NO3)2.6H2O and Al(NO3)3.9H2O at room temperature but at pH11.


Surface Area Analysis

The solid SiO2@LDH, the yolk shell SiO2@LDH and the hollow shell SiO2@LDH prepared as described above but without acetone treatment were subjected to Brunauer-Emmett-Teller (BET) surface area analysis.


The N2 BET surface areas of the products were:















BET surface area (m2g−1)



















Solid (i.e. core-shell) SiO2@LDH
107



Yolk-shell SiO2@LDH
118



Hollow-shell SiO2@LDH
177










The BET surface areas reported above may be favourably compared to those of SiO2@LDHs prepared according to (A) Shao et a. Chem. Mater. 2012, 24, pages 1192-1197 and to those of SiO2@LDHs prepared according to (B) Chen et a. J. Mater. Chem. A, 1, 3877-3880.


(A) SiO2 Microspheres Pre-Treated with Al(OOH).












Product SiO2@NiAl LDH.









BET surface area (m2g−1)












Solid (i.e. core-shell) SiO2 microspheres
42.3


Yolk-shell SiO2@LDH microspheres
68


Hollow-shell SiO2@LDH microspheres
124









(B) SiO2 Microspheres—No Pre-Treatment—Ammonia Method.












Product SiO2@LDH.









BET surface area (m2g−1)












Solid (i.e. core-shell) SiO2@LDH microspheres
61









Core-shell SiO2@LDHs were prepared according to the procedures described in Example 1 and in the Examples 2 and 3 below having different thicknesses of LDH layer. The ratio of Mg/Al was varied to control the thickness of the LDH layer. A Mg:Al ratio of 1:1 was found to give an LDH layer of thickness 65 nm, a ratio of 2:1 was found to give an LDH layer of thickness 110 nm and a layer of thickness of 160 nm was obtained using a Mg:Al ratio of 3:1. TEM images are shown in FIG. 15. Core-shell SiO2@LDHs were also prepared according to the procedure described in Example 1 above using different sized SiO2 microspheres, 300 nm, 550 nm and 800 nm. TEM images are shown in FIG. 16. TEM images of the SiO2@LDHs produced with different morphology (a) solid (Example 1), (b) yolk shell (Example 1 at 40° C.) and (c) hollow (Example 1 at pH11), as described above, are shown in FIG. 17.


Example 2

In order to obtain a 1:1 Mg:Al LDH, the procedure described above in Example 1 was repeated with the exception that an aqueous solution (19.2 mL) containing Mg(NO3)2.6H2O (0.72 mmol) and Al(NO3)3.9H2O (0.72 mmol) was added at a rate of 60 mL/h to solution A under vigorous stirring.


Example 3

In order to obtain a 3:1 Mg:Al LDH, the procedure described above in Example 1 was repeated with the exception that an aqueous solution (19.2 mL) containing Mg(NO3)2.6H2O (1.08 mmol) and Al(NO3)3.9H2O (0.36 mmol) was added at a rate of 60 mL/h to solution A under vigorous stirring.


The XRD patterns of the SiO2@LDH samples prepared with Mg:Al ratios of 1:1 (Example 2) and 3:1 (Example 3) are shown in FIG. 12.


Example 4

The silica@LDH particles were synthesised via the coprecipation method. Silica spheres (100 mg, 550 nm) were dispersed in deionised water (20 mL) using ultrasound treatment. After 30 min, the anion salt (0.96 mmol), Na2CO3, was added to the solution containing ammonia (0.8 mL, 35%) and a further 5 min of sonication was carried out to form solution A. Next an aqueous solution (19.2 mL) containing Mg(NO3)2.6H2O) (0.96 mmol) and Al(NO3)3.9H2O (0.48 mmol) was added at a rate of 60 mL/h to solution A under vigorous stirring. The obtained solid was collected with centrifugation at 4000 rpm for 5 min and then re-dispersed in deionised water (40 mL) and stirred for 1 h. The collection and re-dispersion were repeated twice. Afterward, the solid was washed with acetone (40 mL) and then re-dispersed in acetone (40 mL) and left to stir overnight. The solid was then dried under vacuum. The suspension was then dried under vacuum for materials characterisation.


The features disclosed in the foregoing description, in the claims as well as in the accompanying drawings, may both separately and in any combination thereof be material for realizing the invention in diverse forms thereof.


Example 5

In order to obtain Silica@AMO-LDHs in Mg:Al=3:1. Synthesise the Silica@LDH particles by using the co-precipitation method, disperse silica spheres (100 mg) in the deionised water (20 mL) by using ultrasound treatment for 30 min, add the anion salt Na2CO3 (0.96 mmol) in the solution and further treat by ultrasound for 5 min, the finally solution named A. Then add an aqueous solution (19.2 mL) containing (1.08 mmol) Mg2+ and (0.36 mmol) Al3+ in the solution A at the rate of 60 mL/h with vigorous stirring. The pH of the reaction solution is controlled with the addition of 1 M NaOH by an autotitrator. And the morphology of Silica@LDH is controlled by pH and temperature. The obtained solid is collected with centrifugation at 5000 rpm for 5 min and then re-dispersed in deionised water (40 mL) and stir for 1 h, the washing need repeated twice. Before final isolation, the solid is washed with acetone (40 mL) and left to stir over night, and the suspension is then dried under vacuum


Example 6

In order to obtain Silica@AMO-LDHs in Mg:Ni:Al=2.7:0.3:1. The Silica@LDH particles will be synthesized by using the co-precipitation method, disperse silica spheres (100 mg) in the deionised water (20 mL) by using ultrasound treatment for 30 min, add the anion salt Na2CO3 (0.96 mmol) in the solution and further treat by ultrasound for 5 min, the finally solution named A. Then add an aqueous solution (19.2 mL) containing (0.972 mmol) Mg2+, (0.108 mmol) Ni2+ and (0.36 mmol) Al3+ in the solution A at the rate of 60 mL/h with vigorous stirring. The pH of the reaction solution is controlled with the addition of 1 M NaOH by an autotitrator. As followed the morphology of Silica@LDH is controlled by pH and temperature. The obtained solid is collected with centrifugation at 5000 rpm for 5 min and then re-dispersed in deionised water (40 mL) and stir for 1 h, the washing need repeated twice. Before final isolation, the solid is washed with acetone (40 mL) and left to stir over night, and the suspension is then dried under vacuum.


Example 7

In order to obtain Silica@AMO-LDHs in Mg:Al:Fe=3:0.9:0.1. The Silica@LDH particles synthesise using the co-precipitation method, disperse silica spheres (100 mg) in the deionised water (20 mL) by using ultrasound treatment for 30 min, add the anion salt Na2CO3 (0.96 mmol) in the solution and further treat by ultrasound for 5 min, the finally solution named A. Then add an aqueous solution (19.2 mL) containing (1.08 mmol) Mg2+, (0.324 mmol) Al3+ and (0.036 mmol) Fe3+ in the solution A at the rate of 60 mL/h with vigorous stirring. The pH of the reaction solution is controlled with the addition of 1 M NaOH by an autotitrator. As followed the morphology of Silica@LDH is controlled by pH and temperature. The obtained solid is collected with centrifugation at 5000 rpm for 5 min and then re-dispersed in deionised water (40 mL) and stir for 1 h, the washing need repeated twice. Before final isolation, the solid is washed with acetone (40 mL) and left to stir over night, and the suspension is then dried under vacuum

Claims
  • 1.-21. (canceled)
  • 22. Silica-layered double hydroxide microspheres having the formula I below (SiO2)p@{[Mz+(1-x)M′y+x(OH)2]a+(Xn−)a/n.bH2O.c(AMO-solvent)}q  (I)wherein,Mz+ and M′y+ are two different charged metal cations;z=1 or 2;y=3 or 4;0<x<0.9;b is 0 to 10;c is 0 to 10;p>0,q>0;Xn− is an anion; with n>0;a=z(1−x)+xy−2; andAMO-solvent is an 100% aqueous miscible organic solvent,wherein the silica-layered double hydroxide microspheres each comprise a SiO2 microsphere having solid layered double hydroxide attached to its surface, and wherein: A. the silica-layered double hydroxide microspheres are core-shell materials wherein the SiO2 microsphere is a solid sphere, and wherein the specific surface area of the core-shell materials is at least 100 m2/g, orB. the silica-layered double hydroxide microspheres are yolk-shell materials wherein the SiO2 microsphere comprises an outer shell and a smaller SiO2 sphere contained within the outer shell, wherein there is a hollow portion between the smaller sphere and the inner surface of the outer shell, and wherein the specific surface area of the yolk-shell materials is at least 100 m2/g, orC. the silica-layered double hydroxide microspheres are hollow shell materials wherein the SiO2 microsphere has a hollow interior, and wherein the hollow shell materials have a specific surface area of at least 130 m2/g;and wherein the silica-layered double hydroxide microspheres have a thickness of layered double hydroxide layer larger than 110 nm.
  • 23. Silica-layered double hydroxide microspheres according to claim 22, wherein M′ is one or more trivalent cations and M is one or more divalent cations.
  • 24. Silica-layered double hydroxide microspheres according to claim 22, wherein M′ is Al or Fe.
  • 25. Silica-layered double hydroxide microspheres according to claim 22, wherein M is Ca, Cu, Ni or Mg.
  • 26. Silica-layered double hydroxide microspheres according to claim 22, wherein Xn− is carbonate, hydroxide, nitrate, borate, sulphate, phosphate, halide or a mixture of two or more thereof.
  • 27. Silica-layered double hydroxide microspheres according to claim 22, wherein Xn− is CO32−, Cl−, NO3− or a mixture of two or more thereof.
  • 28. Silica-layered double hydroxide microspheres according to claim 22, wherein M′ is Al or Fe, M is Ca, Cu, Ni or Mg, and Xn− is CO32−, Cl−, NO3− or a mixture of two or more thereof.
  • 29. Silica-layered double hydroxide microspheres according to claim 22, wherein M is Mg, M′ is Al and Xn− is CO32−.
  • 30. Silica-layered double hydroxide microspheres according to claim 22, wherein the silica microspheres comprise greater than 95% w/w SiO2.
  • 31. Silica-layered double hydroxide microspheres according to claim 30, wherein M′ is Al or Fe, M is Ca, Cu, Ni or Mg, and Xn− is CO32−, Cl−, NO3− or a mixture of two or more thereof.
  • 32. Silica-layered double hydroxide microspheres according to claim 30, wherein M is Mg, M′ is Al and Xn− is CO32−.
  • 33. Silica-layered double hydroxide microspheres according to claim 22, wherein the silica microspheres do not contain iron.
  • 34. Silica-layered double hydroxide microspheres according to claim 33, wherein M′ is Al or Fe, M is Ca, Cu, Ni or Mg, and Xn− is CO32−, Cl−, NO3− or a mixture of two or more thereof.
  • 35. Silica-layered double hydroxide microspheres according to claim 33, wherein M is Mg, M′ is Al and Xn− is CO32−.
  • 36. Silica-layered double hydroxide microspheres according to claim 22, wherein c is greater than zero.
  • 37. Silica-layered double hydroxide microspheres according to claim 36, wherein the AMO-solvent is acetone, ethanol, methanol or a mixture of two or more thereof.
  • 38. Silica-layered double hydroxide microspheres according to claim 37, wherein M′ is Al or Fe, M is Ca, Cu, Ni or Mg, and Xn− is CO32−, Cl−, NO3− or a mixture of two or more thereof.
  • 39. Silica-layered double hydroxide microspheres according to claim 38, wherein the silica microspheres comprise greater than 95% w/w SiO2.
  • 40. Silica-layered double hydroxide microspheres according to claim 37, wherein M is Mg, M′ is Al and Xn− is CO32−.
  • 41. Silica-layered double hydroxide microspheres according to claim 40, wherein the silica microspheres do not contain iron.
Priority Claims (1)
Number Date Country Kind
1500115.9 Jan 2015 GB national
Divisions (1)
Number Date Country
Parent 15541655 Jul 2017 US
Child 16925596 US