SIO.sub.2 -CaO Based low cubically expansive flame-spraying material

Abstract

The present invention provides a flame-spraying material composed of a powder mixture having a particle size not more than 0.5 mm and essentially comprising 85 to 98% by weight of SiO.sub.2 and 2 to 15% by weight of CaO, and also comprising 0.05 to 1.0% by weight of Li.sub.2 O in addition to the above which show a good adhesion rate and high mechanical strength of the flame-spray deposited coating as well as a tendency towards higher anti-spalling due to the reduced melt viscosity and hot linear thermal expansion rate similar to that of silica brick.

Description

BACKGROUND OF THE INVENTION

The present invention relates to a flame-spraying material and in particular a flame-spraying material for repairing, by flame-spraying, any damaged part of a furnace or kiln such as a coke oven and the like where a number of heating-and-cooling cycles are carried out.

Recently, repair of coke ovens by flame-spraying has been effected and outstanding effects have been demonstrated in relation to the repair time, the adhesive strength of the repaired part, durability and the like. It has been known to employ a flame-spraying material comprised of about 70%SiO.sub.2, said flame spraying material having a refractiveness of 1100.degree. C. to 1280.degree. C.

Coke ovens are lined with silica bricks having a coefficient of thermal expansion that rapidly increases between 300.degree. C. and 500.degree. C. and keeps a level without significant increase temperatures in excess of 500.degree. C. For this reason, the silica bricks have a very high resistance to thermal spalling where they are used at temperatures over 500.degree. C. However, if the silica bricks are repaired, once they are damaged, with a flame-spray material comprising approximately 70% by weight of SiO.sub.2, no adequate endurance can be achieved at present as a result of the peeling off of the flame-sprayed coating due to the differences in the hot expansion behavior between the base silica bricks and the flame-sprayed coating which causes significant thermal stress therebetween as the flame-sprayed coating linearly expands thermally, contrary to silica bricks, up to about 1000.degree. C.

SUMMARY OF THE INVENTION

Accordingly, the object of the present invention is to provide a flame-spraying material excellent in anti-spalling properties due to its very low hot thermal expansion rate as well as having hot thermal expansion behavior similar to that of silica bricks.

Broadly, the flame-spraying material according to the present invention essentially comprises either 85 to 98% by weight of SiO.sub.2 and 2 to 15% by weight of CaO or 85 to 98% by weight of SiO.sub.2, 2 to 15% by weight of CaO and further 0.05 to 1.0% by weight of Li.sub.2 O.

In a preferred embodiment, the flame-spraying material comprises a powder mixture having a particle size of not more than 0.5 mm and essentially consisting of 85 to 98% by weight of SiO.sub.2, 2 to 15% by weight of CaO or of 85 to 98% by weight of SiO.sub.2, 2 to 15% by weight of CaO, 0.05 to 1.0% by weight of Li.sub.2 O and the balance, in either case being not more than 5% by weight of incidental impurities, same flame-spraying material being adhered to the walls of a furnace while changing to a semi-molten or molten state in a flame resulting from the combustion of an oxygen-fuel gas mixture.

DETAILED EXPLANATION OF THE INVENTION

The flame-spraying material according to the first embodiment of the invention can be produced by combining silica based material such as silica, silica sand, a silicate mineral or the like and CaO-SiO.sub.2 based material such as Portland cement, wollastonite, dicalcium silicate or the like. As the CaO-SiO.sub.2 type raw material, preference should be given to Portland cement, wollastonite and dicalcium silicate as given above, while CaO cannot flame-sprayed. CaCO.sub.3 and Ca(OH).sub.2 are less preferred due to their high thermal loss resulting from the evolution of gases derived from their decomposition.

The flame-spraying material in a second embodiment according to the invention can be produced by combining silica based material such as silica, silica sand, a silicate mineral or the like, CaO-SiO.sub.2 based material such as Portland cement, wollastonite, dicalcium silicate or the like and a lithium mineral such as spodumene, petalite or the like. As to the silica based material and the CaO-SiO.sub.2 based material preference should be given to those set forth in the first embodiment.

As set forth in the forgoing, the flame-spraying material according to the invention shows a thermal expansion behavior similar to that of silica bricks provided that the material has the compositions defined above. If the CaO content is less than 2% by weight, the viscosity of the fused material during flame-spraying using the oxygen-fuel combustion gas mixture cannot be reduced to an extent such that adequate fuse-adhering can be achieved because of the very high melt-viscosity of the remaining SiO.sub.2, thus resulting in an unsintered flame-sprayed coating, having a very low strength adhered coating, with a lower adhesion proportion. On the other hand, if CaO exceeds 15% by weight the flame-spraying material would more and more show a linearly increasing thermal expansion rate as a result of the gradual disappearance of the thermal expansion properties similar to those of silica bricks, thus showing an adverse propensity to peeling and damage. If the SiO.sub.2 content is less than 85% by weight or in excess of 98% by weight, similar adverse effects give rise to those corresponding to the case where the CaO contents exceeds 15% by weight or it is less than 2% by weight. The addition of Li.sub.2 O permits production a low thermal expansion flame-spray coating. If the addition, however, is less than 0.05% by weight the characterizing properties of the low thermal expansion can hardly be achieved, on the other hand, if it exceeds 1.0% by weight the refractoriness of the flame-sprayed coating is decreased. If incidental impurities exist in excess of 5% by weight, the thermal expansion rate increases linearly which is not preferable as set forth above. Should the particles be larger than 0.5 mm in size, they do not melt in the flame of the oxygen-fuel combustion gas and almost of them are lost as a re-bound loss, responsive to a lower adhering rate.

The flame-spraying material of the present invention have prominent technical significance over the prior art ones in that they show in improved adhesion rate of the flame-sprayed material and improved hot mechanical strength of the flame-sprayed coating due to the reduction of the melt-viscosity of SiO.sub.2 stemming from the addition of CaO and Li.sub.2 O in the specified amount, SiO.sub.2 alone giving too high a melt-viscosity and also a lower adhering rate along with a low mechanical strength deposited coating, and in that they make possible the suppression of peeling and damage to the deposited flame-sprayed coating by retaining a hot expansion behavior similar to that of silica bricks. The flame-spraying material can be used to repair a furnace in operation.

The following Examples are provided to illustrate, but not to limit the present invention.

EXAMPLE I-IV AND COMPARATIVE EXAMPLE I-II

The flame-spray compositions indicated in the following Table 1 were prepared and were flame-sprayed on a silica brick using conventional techniques. The results are shown in Table 1.

TABLE 1______________________________________ Example Prior Art Compara- Present Invention tive Examples ExamplesItems I II III IV I II______________________________________Formulationchamotte 85 70silica 90 80 80 90silicate rock 5white cement 10wollastonite 10 20 10 5sodium silicate 15 30anhydrousChemical CompositionSiO.sub.2 93.4 88.7 85.8 93.7 65 66CaO 4.8 9.7 11.4 2.4impurities 1.8 1.6 2.8 3.9 35 34Test Resultadhesive strength 100 80 75 90 10 6(kg/cm.sup.2)*bending strength 170 150 120 110 15 12(kg/cm.sup.2)*adhesion rate (%) 70 85 80 70 75 80# of cycles until No 45 40 No 20 15peeling occurs peel- peel-under a thermal ing ingcycle test**______________________________________ *values measured at 1000.degree. C. **substrate: silica brick; A cycle consists of changing the temperature between 1200.degree. C. and 300.degree. C. for 15 minutes, such cycles are repeated 50 times.

EXAMPLE V-IX AND COMPARATIVE EXAMPLE III-IV

The flame-spray composition Table II set forth hereinafter were prepared and were flame sprayed on a silica brick using conventional techniques. The results are represented in Table 2.

TABLE 2______________________________________ Example Prior Art Com- Present Invention parative Examples ExamplesItems V VI VII VIII IX III IV______________________________________Formulationchamotte 85 75silica 90 85 80 80 75silicate rock 10white cement 3.5 8wollastonite 5 5 15 12spodumene 5petalite 1.5 15 5 5sodium silicate 15 30anhydrousChemical CompositionSiO.sub.2 94.0 94.0 92.5 90.2 85.6 65 66CaO 2.1 2.3 2.2 6.5 10.4Li.sub.2 O 0.4 0.06 0.6 0.2 0.2impurities 3.5 3.6 4.7 3.1 3.8 35 34Test Resultsadhesive strength 95 85 120 110 140 10 6(kg/cm.sup.2)*bending strength 115 100 135 170 180 15 12(kg/cm.sup.2)*adhesive rate (%) 80 75 90 80 85 75 80# of cycles until No No No No No 20 15peeling occurs peel- peel- peel- peel- peel-under a thermal ing ing ing ing ingcycle test**______________________________________ *values measured at 1000.degree. C. **substrate: silica brick; A cycle consists of changing the temperature between 1200.degree. C. and 300.degree. C. for 15 minutes, such cycles are repeated 50 times.

As seen from above Tables 1 and 2 the flame-spraying materials according to the invention show both better adhesion strength and bending strength over those of the prior art (comparative Example) and also show no peeling from the silica brick substrate in a heating-cooling thermal cycle test, thus showing superior properties over the prior art flame-spraying material.

Claims

1. A flame-spraying material essentially comprising 85 to 98% by weight of SiO.sub.2, 2 to 15% by weight of CaO and 0.05 to 1.0% by weight of Li.sub.2 O.