SITU THERMAL TREATMENT FOR PBF SYSTEMS

Abstract

Apparatuses and methods for in situ thermal treatment for PBF systems are provided. An apparatus for a PBF-based 3-D printer can include a heating element for heating a gas, wherein the heated gas is delivered via at least one port of the 3-D printer to conduct heat treatment on a build piece during printing. A method for thermal treatment in a PBF-based 3-D printer can include heating a gas and delivering it via at least one port of the 3-D printer arranged proximate a build piece to conduct heat treatment during printing. An apparatus for a PBF-based 3-D printer can include a temperature-regulating element for changing a temperature of a gas, at least one channel for delivering the gas to a plurality of ports, and a controller for determining gas temperatures and durations of application of the gas via different ones of the plurality of the ports.

Description

BACKGROUND

Field

The present disclosure relates generally to powder-bed fusion (PBF) systems, and more particularly, to in situ thermal treatment for PBF systems.

Background

PBF systems can produce structures (referred to as build pieces) with geometrically complex shapes, including some shapes that are difficult or impossible to create with conventional manufacturing processes. PBF systems create build pieces layer-by-layer, i.e., slice-by-slice. Each slice can be formed by a process of depositing a layer of powder and applying an energy beam to melt areas of the powder layer that coincide with the cross-section of the build piece in the layer. The melted powder cools and fuses to form a slice of the build piece. The process can be repeated to form the next slice of the build piece, and so on, until the build piece is complete. Because each layer is deposited on top of the previous layer, it can be useful to think of PBF as forming a build piece slice-by-slice from the ground up.

A persisting challenge with PBF systems relates to the residual cracking or distortion that may occur in build pieces as a result of high temperature gradients in the powder bed where the layers are deposited. Practitioners have often implemented additional post-processing heat treatment steps to ameliorate the adverse effects of these temperature gradients. These steps are often marginally successful while resulting in longer overall build times.

SUMMARY

Several aspects of apparatuses and methods for in situ thermal treatment for PBF systems will be described more fully hereinafter.

In various aspects, a thermal treatment apparatus for a PBF-based three-dimensional (3-D) printer can include a heating element for heating a gas, wherein the heated gas is delivered via at least one port of the 3-D printer, the port being positioned to conduct heat treatment on a build piece during printing.

In various aspects, a method for thermal treatment in a PBF-based 3-D printer can include heating a gas and delivering the heated gas via at least one port of the 3-D printer arranged proximate a build piece to conduct heat treatment on the build piece during printing.

In various aspects, a thermal treatment apparatus for a PBF-based 3-D printer can include a temperature-regulating element for changing a temperature of a gas, at least one channel for delivering the gas to a plurality of ports distributed at different vertical regions of the build piece, and a controller for determining gas temperatures and durations of application of the gas via different ones of the plurality of the ports, wherein the temperature-regulating element is directed to variably deliver, during the 3-D print, the gas to different ones of the plurality of ports at different ones of the determined gas temperatures and durations of application to stabilize the thermal properties of the build piece.

Other aspects will become readily apparent to those skilled in the art from the following detailed description, wherein is shown and described only several embodiments by way of illustration. As will be realized by those skilled in the art, concepts herein are capable of other and different embodiments, and several details are capable of modification in various other respects, all without departing from the present disclosure. Accordingly, the drawings and detailed description are to be regarded as illustrative in nature and not as restrictive.

BRIEF DESCRIPTION OF THE DRAWINGS

Various aspects of apparatuses and methods for in situ thermal treatment for PBF systems will now be presented in the detailed description by way of example, and not by way of limitation, in the accompanying drawings, wherein:

FIG. 1A-D illustrate an example PBF system during different stages of operation.

FIG. 2 illustrates an exemplary energy beam source and deflector system.

FIGS. 3A-B illustrate a perspective view of an exemplary powder bed before and after a layer of powder is deposited.

FIG. 4 illustrates an exemplary thermal treatment apparatus system working in conjunction with a PBF-based printer.

FIG. 5 illustrates an exemplary method for thermal treatment in a PBF-based 3-D printer.

DETAILED DESCRIPTION

The detailed description set forth below in connection with the appended drawings is intended to provide a description of various exemplary embodiments of the concepts disclosed herein and is not intended to represent the only embodiments in which the disclosure may be practiced. The term “exemplary” used in this disclosure means “serving as an example, instance, or illustration,” and should not necessarily be construed as preferred or advantageous over other embodiments presented in this disclosure. The detailed description includes specific details for the purpose of providing a thorough and complete disclosure that fully conveys the scope of the concepts to those skilled in the art. However, the disclosure may be practiced without these specific details. In some instances, well-known structures and components may be shown in block diagram form, or omitted entirely, in order to avoid obscuring the various concepts presented throughout this disclosure.

This disclosure is directed to techniques for managing residual stresses, microstructure, and other processing artifacts that occur in build pieces produced via PBF additive manufacturing (AM)-based systems. PBF AM processes are used in the manufacture of metallic structures and components in an increasing number of industries. PBF AM processes cause development of residual stresses in the printed build piece. The extent of these residual stresses may vary depending on factors like the material used and build piece geometry. Generally, these residual stresses originate as a result of a high cooling rate dictated by the temperature differences between the melt pool and the build plate.

While applicable to all PBF systems in general, particularly in laser-based PBF (L-PBF) systems, the temperature gradient between the melt pool and the previous layers deposited in the powder bed continues to increase as additional layers are added onto the build piece. As a result, build pieces in L-PBF systems often require additional post-AM treatment steps including stress relief measures to avoid part distortion upon removal of the build piece from the build plate. Materials that have high thermal conductivity and a low specific heat are generally more prone to such distortion, and may require more significant post-AM attention.

For example, one conventional measure to address this issue is for the manufacturer to pre-calculate the expected stress and anticipated distortion. After 3-D printing, the manufacturer removes the build plate with the build piece from the 3-D printer and places the collective structure into a dedicated oven for applying the pre-calculated heat and for addressing other variables to reduce stress. One disadvantage of this approach is that the parameters of the predicted solution often are difficult to precisely match with the actual results after heat treatment is conducted, and a certain amount of distortion still occurs. This mismatch is often proportional to the complexity of the build piece, with greater mismatches more evident in complex parts.

In addition to residual stress generation and distortion problems, certain materials used in PBF systems require the resulting build piece to undergo post-AM heat treatment operations to obtain the required microstructure and properties. Heat treatment operations are conducted on the build piece as a series of post-processing steps. These steps can add significant additional time to the overall manufacturing process beyond just the AM production of the build piece. The additional time necessary for thermal post-processing can be appreciably longer, for example, than the comparatively short period of time associated with manufacturing the structure using a non-AM technique such as casting, forging, or welding. In PBF AM processes, the 3-D printing time can in many cases be more comparable to the subsequent heat-treatment durations. These post-AM operations may undesirably add a significant amount of time to the overall product build.

The present disclosure addresses the above problems associated with conventional post-processing techniques. An in situ thermal treatment apparatus (“TTA”) for PBF-based systems includes a gas delivery structure that can deliver heated gas used for clearing the plume generated during L-PBF fusion. In various embodiments, TTA is partially or fully integrated with the PBF 3-D printer. In another embodiment, TTA is a separate apparatus that can be retrofitted to or otherwise operably coupled to the 3-D printer. TTA may utilize any suitable heat source. TTA may deliver heated gas not only to the top layer of the print bed, but also to the printed material below the melt pool, e.g., via TTA's internal ports or channels, and above the build plate. Channels that carry heated gas to port(s) used for the thermal treatment processes may be built into the print bed or other portion of the 3-D printer, or may be subsequently added to the 3-D printer by substituting parts, retrofitting structures, and/or by modifying the 3-D printer itself.

In an embodiment, TTA includes a controller, a gas source, a heating element, a plurality of sensors, and a plurality of ports, each acting in concert to perform in situ operations on a 3-D printed part. In an embodiment, TTA includes at least one channel leading to a port arranged on or proximate the build layer of the 3-D printer and one or more channels leading to ports arranged in the lower chamber of the 3-D printer, such as where the manufactured portion of the build piece is lowered as the printing process progresses. Each port may be connected via a channel to a heating apparatus. The heated gas may flow from the heating element via a single channel for efficiency, and thereafter branch off to a plurality of channels, each channel of the plurality leading to a port arranged at a strategic location for conducting heat treatment operations.

The heating element may receive a gas, which may be, for example, an inert gas, from a gas source. The heating element may heat the gas to a desired temperature based on the determined residual stress relief or further heat treatment of the part, and may deliver the gas. The TTA ports may be integrated within existing PBF-based printers.

In an embodiment, the remaining structure of the TTA may constitute an add-on. That is to say, the TTA may itself comprise an additional, self-contained apparatus that is (optionally) separately provided and then connectable to a PBF-based 3-D printer. The TTA ports may include deflector flaps or other structures to direct the heated gas flow and to ensure that the flow is laminar in nature in the PBF apparatus. TTA may include one or more sensors to obtain or otherwise monitor the temperature. The monitored temperature may be sent to the TTA controller. The TTA controller may, as necessary, instruct the TTA to change the temperature. For example, the TTA controller may communicate with and coordinate operation of the one or more sensors to change the temperature at one or more corresponding locations on or within the TTA.

In an embodiment, the temperature of the top layer is increased during the 3-D printing, e.g., by 100 degrees K, in order to reduce the overall temperature gradient between the top layer and the melt pool, which can minimize the amount of additional heat treatment necessary for a part. While 100 degrees K is used for exemplary purposes, other values may be equally suitable based on system parameters.

Additive Manufacturing (AM). AM involves the use of a stored geometrical model for accumulating layered materials on a build plate to produce a three-dimensional (3-D) build piece having features defined by the model. AM techniques are capable of printing complex components using a wide variety of materials. A 3-D object may be fabricated based on a computer aided design (CAD) model. The CAD model can be used to generate a set of instructions or commands that are compatible with a particular 3-D printer. The AM process can create a solid three-dimensional object using the CAD model and print instructions.

An exemplary AM technique is PBF. PBF systems use a controller that executes the appropriate print instructions to create build pieces layer-by-layer. Each layer is formed by depositing a layer of powder and exposing, per controller instructions, designated portions of the powder to an energy beam such as a laser. The energy beam is applied via a deflector to melt areas of the powder layer that coincide with the cross-section of the build piece in the layer. The melted powder cools and fuses to form a slice of the build piece. The process can be repeated to form the next slice of the build piece, and so on. Each layer is deposited on top of the previous layer. The resulting structure is a build piece assembled slice-by-slice from the ground up.

The present disclosure may use PBF-based 3-D printing in an exemplary implementation, but is not limited to this application. FIG. 1A-D illustrate an example PBF system 100 during different stages of operation. PBF system 100 can include a depositor 101 that can deposit each layer of metal powder, an energy beam source 103 that can generate an energy beam, a deflector 105 that can apply the energy beam to fuse the powder material, and a build plate 107 that can support one or more build pieces, such as a build piece 109. PBF system 100 can also include a build floor 111 positioned within a powder bed receptacle. The walls of the powder bed receptacle are shown as powder bed receptacle walls 112. Build floor 111 can lower build plate 107 so that depositor 101 can deposit a next layer and a chamber 113 that can enclose the other components. Depositor 101 can include a hopper 115 that contains a powder 117, such as a metal powder, and a leveler 119 that can level the top of each layer of powder.

Referring specifically to FIG. 1A, this figure shows PBF system 100 after a slice of build piece 109 has been fused, but before the next layer of powder has been deposited. In fact, FIG. 1A illustrates a time at which PBF system 100 has already deposited and fused slices in multiple layers, e.g., 50 layers, to form the current state of build piece 109, e.g., formed of 50 slices. The multiple layers already deposited have created a powder bed 121, which includes powder that was deposited but not fused. PBF system 100 can include a temperature sensor 122 that can sense the temperature in areas of the work area, such as the surface of powder bed, build piece 109, etc. For example, temperature sensor 122 can include a thermal camera directed toward the work area, thermocouples attached to areas near the powder bed, etc.

FIG. 1B shows PBF system 100 at stage in which build floor 111 can lower by a powder layer thickness 123. The lowering of build floor 111 causes build piece 109 and powder bed 121 to drop by powder layer thickness 123, so that the top of the build piece and powder bed are lower than the top of powder bed receptacle wall 112 by the powder layer thickness. In this way, for example, a space of with a consistent thickness equal to powder layer thickness 123 can be created over the tops of build piece 109 and powder bed 121.

FIG. 1C shows PBF system 100 at a stage in which depositor 101 can deposit powder 117 in the space created over the tops of build piece 109 and powder bed 121. In this example, depositor 101 can cross over the space while releasing powder 117 from hopper 115. Leveler 119 can level the released powder to form a powder layer 125 that has a thickness of powder layer thickness 123. It should be noted, that elements of FIGS. 1A-D and the other figures in this disclosure are not necessarily drawn to scale, but may be drawn larger or smaller for the purpose of better illustration of concepts described herein. For example, the illustrated thickness of powder layer 125 (i.e., powder layer thickness 123) is greater than an actual thickness used for the example 50 previously-deposited layers.

FIG. 1D shows PBF system 100 at a stage in which energy beam source 103 can generate an energy beam 127 and deflector 105 can apply the energy beam to fuse the next slice in build piece 109. In various embodiments, energy beam source 103 can be an electron beam source, energy beam 127 can be an electron beam, and deflector 105 can include deflection plates that can generate an electric field that deflects the electron beam to scan across areas to be fused. In various embodiments, energy beam source 103 can be a laser, energy beam 127 can be a laser beam, and deflector 105 can include an optical system that can reflect and/or refract the laser beam to scan across areas to be fused. In various embodiments, energy beam source 103 and/or deflector 105 can modulate the energy beam, e.g., turn the energy beam on and off as the deflector scans so that the energy beam is applied only in the appropriate areas of the powder layer. For example, in various embodiments, the energy beam can be modulated by a digital signal processor (DSP).

FIG. 2 illustrates an exemplary energy beam source and deflector system. In this example, the energy beam is an electron beam. The energy beam source can include an electron grid 201, an electron grid modulator 203, and a focus 205. A controller 206 can control electron grid 201 and electron grid modulator 203 to generate an electron beam 207 and can control focus 205 to focus electron beam 207 into a focused electron beam 209. To provide a clearer view in the figure, connections between controller 206 and other components are not shown. Focused electron beam 209 can be scanned across a powder layer 211 by a deflector 213. Deflector 213 can include two x-deflection plates 215 and two y-deflection plates 217. Controller 206 can control deflector 213 to generate an electric field between x-deflection plates 215 to deflect focused electron beam 209 along the x-direction and to generate an electric field between y-deflection plates 217 to deflect the focused electron beam along the y-direction. In various embodiments, a deflector can include one or more magnetic coils to deflect the electron beam.

A beam sensor 219 can sense the amount of deflection of focused electron beam 209 and can send this information to controller 206. Controller 206 can use this information to adjust the strength of the electric fields in order to achieve the desired amount of deflection. Focused electron beam 209 can be applied to powder layer 211 by scanning the focused electron beam to melt loose powder 221, thus forming fused powder 223.

FIGS. 3A-B illustrate a perspective view of an exemplary powder bed before and after a layer of powder is deposited. FIG. 3A shows a powder bed 301 after a scanning process has occurred. The figure shows a top surface of an nth build piece slice 303, which is a slice formed by an energy beam source/deflector 305 scanning an energy beam to fuse powder in an nth powder layer 307 (where n is the number of the powder layer). FIG. 3B shows a state of powder bed 301 after a next powder layer, i.e., nth+1 powder layer 309, has been deposited. The figure also shows an outline of the next slice to be fused, i.e., an outline of nth+1 slice 311.

TTA. FIG. 4 depicts a conceptual illustration of a TTA system working in conjunction with a PBF-based printer.

The controller 400 may include a processing system having one or more processors and a memory for storing and executing code that conducts the in situ operations. In some embodiments, the controller 400 may be integrated with or part of the central controller of the printer. In other embodiments, the controller 400 may be a dedicated controller, or a controller built within the TTA.

The heating apparatus/element 410 may generate heat to provide a temperature as controlled by the controller 400 via the controlling sensor 420. The monitoring sensor 430 can measure the temperature and report it back to the controller 400. During in situ operations, the heat input (gas) source 440 transfers a stored inert gas or other substance to the heating element 410. The heating element 410 heats the gas to a desired temperature as determined by the controller 400, and delivers the heated gas (or equivalently, a separate delivery structure coupled to the heating element 410 delivers the heated gas) via one or more channels 450, 451, and 452 to ports 460, 461, and 462.

Ports 460, 461, and 462 in this embodiment are strategically positioned at different locations to provide optimal heat treatment to different portions of the build piece. Thus, the port (460, 461, and 462) outlets may be located at different locations on or adjacent the current layer being deposited in the print bed, or above or beneath the build plate 470 of the PBF apparatus, including the lowering chamber, to optimally access the desired portions of the build piece that may necessitate stress relief or heat treatment. These locations may include both the top, side wall, or other surface of the print bed/print chamber as well as areas adjacent the printed material below the print bed surface.

In an embodiment, associated with each port is a deflector flap (e.g., flaps 480, 481, and 482) that steers the gas in a predetermined directional flow (e.g., gas flows 490, 491, and 492) as the gas exits one or more of ports. The above illustration, including the structure of the apparatus and the number of ports, is for exemplary purposes only, and any number and geometry of heating elements, delivery elements, controlling elements and/or ports may be used to enable in situ heat transfers to occur at desired points within the AM process to optimize 3-D print quality.

FIG. 5 is a flowchart of an exemplary method for thermal treatment in a PBF-based 3-D printer. The method includes heating (500) a gas and delivering (510) the heated gas. For example, the heated gas can be delivered via at least one port of the 3-D printer arranged proximate a build piece to conduct heat treatment on the build piece during printing.

Because the heat treatments are conducted in situ during the actual 3-D printing, they advantageously require substantially less, if any, additional thermal processing time after the 3-D printing process is complete. Thus, multiple operations can be conducted contemporaneously within a single 3-D rendering. Application of thermal treatment during the 3-D rendering maximizes manufacturing efficiency and minimizes overall processing time. Using the features of the present disclosure, the benefits of PBF-based 3-D printing can be realized without the corresponding addition of inefficient post-processing thermal management techniques.

Thus, for example, unlike conventional tooling and machining techniques which often require very expensive precision equipment to manufacture a single type of component, 3-D printing can replace (in part or in whole) these conventional subtractive manufacturing techniques, where desired, to create highly-customized and geometrically-sophisticated structures and components from the ground up. Alternatively, TTA can be used in conjunction with certain of these conventional techniques to augment these techniques and increase their efficiency.

Furthermore, because TTA as disclosed herein enables thermal post-processing operations to take place in situ during the printing, no additional time ordinarily need be delegated to conduct thermal operations later, after having finished build pieces. The total post-processing time associated with any given build piece (which may include, for example, removing 3-D print supports) is therefore reduced. A related advantage is that providing heat operations in situ enables the thermal operations to be selectively applied to the build piece prior to the build piece being complete. For example, stress relief operations can provide heat to a larger surface area of a potentially problematic structure, before additional material covers the structure and adds additional forces and or covers materials that otherwise could have been heat treated in an uncovered state (e.g., the top layer). By virtue of its multiple ports, TTA may also deliver heated gas to clear generated plume (in embodiments where desirable) over a greater area.

Thus, because the TTA may have ports that enable dynamic temperature control over different levels of the build piece at different stages in time during (and optionally, immediately after) the 3-D print, the thermal treatment can be more precise than compared with the conventional case of the build piece being removed and the entire heat treatment occurring solely after the print is complete. Using the TTA, overall quality of the finished structure may therefore be increased.

As noted above, in one embodiment the temperature gradient of the top layer is reduced substantially prior to being melted by applying heat to the top layer, e.g., by increasing the temperature of the top layer, during the 3-D print process. This act can substantially decrease the amount of stress placed on the build piece because the temperature gradient between the melt pool and remaining portions of the top layer of the build piece is lower.

Exemplary heat treatment techniques. In an embodiment, in situ stress reduction techniques can be applied to aluminum alloys. For example, aluminum alloys ordinarily have a coefficient of thermal expansion of about 20×10⁻⁶ m/(m K) and, as such, are susceptible to developing residual stresses that result in distortion of the build piece upon separation from the build plate. Based on the known thermal expansion, every 100-degree C. increase in part temperature results in a decrease of 0.002 elastic strain, which translates to an approximately 140 MPa residual stress reduction that can be applied via equalizing the thermal gradients experienced by the alloy using the techniques herein. While a variety of materials can benefit from this procedure, this stress reduction operation is significant in aluminum alloys as it can represent one third to one half of the fatigue strength of the material, in some cases.

In another embodiment, maraging steels are aged at a temperature such that the steel's microstructure includes one-hundred percent (100%) martensite. The martensite is formed upon transformation from austenite, which is hard to maintain during continuous cooling. An ageing operation at a temperature where the austenite is stable over a long period of time is required prior to transformation to martensite. The maraging heat treatment operations may involve sustained heat treatment at comparatively low temperatures (e.g., about 500° C., for example). TTA can be configured to apply in situ thermal treatment to age the material to obtain the martensite phase during 3-D printing. The controller may enable TTA to apply an in situ treatment capable of balancing the temperature and time in accordance with the ageing requirements of the print material.

Unlike in post-processing operations whose capabilities are circumscribed by the completed build piece, in the case with TTA the layers that are printed first can be exposed to the gas at a lower temperature for longer time. Conversely, the subsequently printed layers can be exposed for a shorter time to a higher temperature gas, each according to the Temperature-Time Transformation relation. The result is an optimally-aged material at the conclusion of the 3-D printing process.

For example, the cooling rate of a build chamber can be selectively regulated at different levels during the 3-D print operation by changing the temperature of the gas at different levels at different times. Therefore, the TTA can ensure that during an exemplary ten hour print, the lower layers are at a lower temperature for a longer time and the higher layers are at a higher temperature for a shorter time, thereby equalizing the microstructure changes. To equalize the temperatures and minimize the overall stress to the part, the temperatures and times for that application of temperature can be calculated in advance or on the fly. Equalizing temperatures can thereupon be applied via the gas delivered across the top, bottom and middle portions of the build piece such that lower portions are proportionately heated and higher portions are proportionately cooled.

This in situ selective equalization can enable the overall part to have the same properties. This technique is in contrast to prior approaches, wherein the quenching and ageing of the part take place in time-consuming operations after the print, conventionally resulting in both inefficiency of the overall build and an inherent uncertainty in the quenching and ageing operations to equalize the non-uniform thermal properties of the part. The in situ thermal treatment can be used to replace this conventional process, saving time and minimizing thermal stresses.

The present disclosure is provided to enable any person skilled in the art to practice the various aspects described herein. Various modifications to these exemplary embodiments presented throughout the present disclosure will be readily apparent to those skilled in the art, and the concepts disclosed herein may be applied to other techniques for in-situ thermal treatment for PBF systems. Thus, the claims are not intended to be limited to the exemplary embodiments presented throughout the disclosure, but are to be accorded the full scope consistent with the language claims. All structural and functional equivalents to the elements of the exemplary embodiments described throughout the present disclosure that are known or later come to be known to those of ordinary skill in the art are intended to be encompassed by the claims. Moreover, nothing disclosed herein is intended to be dedicated to the public regardless of whether such disclosure is explicitly recited in the claims. No claim element is to be construed under the provisions of 35 U.S.C. § 112(f), or analogous law in applicable jurisdictions, unless the element is expressly recited using the phrase “means for” or, in the case of a method claim, the element is recited using the phrase “step for.”

Claims

1. A thermal treatment apparatus for a powder bed fusion (PBF)-based three-dimensional (3-D) printer, comprising: a heating element for heating a gas,wherein the heated gas is delivered via at least one port of the 3-D printer, the port being positioned to conduct heat treatment on a build piece during printing.

2. The apparatus of claim 1, wherein the heat treatment comprises residual stress reduction.

3. The apparatus of claim 1, wherein the heat treatment comprises ageing a material in the build piece based on a selected gas temperature and heat treatment duration.

4. The apparatus of claim 1, wherein the at least one port is coupled to a deflector flap to direct a flow of the delivered heated gas relative to the build piece.

5. The apparatus of claim 1, wherein the delivered gas is operable to reduce a temperature difference between a lower portion and an upper portion of the build piece.

6. The apparatus of claim 1, wherein the at least one port is positioned to deliver the heated gas to a top layer of print material deposited in a print bed of the 3-D printer.

7. The apparatus of claim 6, wherein the at least one port comprises one or more ports positioned to deliver the heated gas to printed portions of the build piece beneath a melt pool corresponding to the top layer, and above a build plate of the 3-D printer.

8. The apparatus of claim 1, wherein the 3-D printer comprises a lower chamber into which the build piece is lowered during the printing, andthe at least one port is arranged in the lower chamber.

9. The apparatus of claim 1, further comprising a gas storage element coupled to the heating element and configured to supply the gas.

10. The apparatus of claim 1, further comprising a controller coupled to the heating element for determining one or more of a temperature, duration, and location, relative to the build piece, of the heat treatment.

11. The apparatus of claim 10, further comprising a monitoring sensor coupled to the controller for monitoring a temperature of the heated gas.

12. The apparatus of claim 11, wherein the controller is further configured to receive the monitored temperature from the monitoring sensor and to instruct the heating element to modify the temperature to a new value.

13. The apparatus of claim 10, further comprising one or more channels arranged at an output of the heating element and extending to the at least one port for transporting the heated gas.

14. A method for thermal treatment in a powder bed fusion (PBF)-based three-dimensional (3-D) printer, comprising: heating a gas; anddelivering the heated gas via at least one port of the 3-D printer arranged proximate a build piece to conduct heat treatment on the build piece during printing.

15. The method of claim 14, wherein the heat treatment comprises residual stress reduction.

16. The method of claim 14, further comprising selecting a gas temperature and heat treatment duration, wherein conducting the heat treatment further comprises ageing a material in the build piece based on the selected gas temperature and heat treatment duration.

17. The method of claim 14, further comprising directing a flow of the delivered gas using a deflector flap coupled to the at least one port.

18. The method of claim 14, further comprising using the delivered gas to reduce a temperature gradient between an upper portion and a lower portion of the build piece.

19. The method of claim 14, further comprising delivering the heated gas to a top layer of print material deposited in a print bed of the 3-D printer.

20. The method of claim 14, further comprising delivering the heated gas to printed portions of the build piece beneath a melt pool corresponding to a top layer, and above a build plate of the 3-D printer.

21. The method of claim 14, further comprising delivering the heated gas to a lower chamber of the 3-D printer into which the build piece is lowered during the printing.

22. The method of claim 14, further comprising supplying the gas to a heating element from a gas storage element, the heating element for heating the gas.

23. The method of claim 22, further comprising determining, via a controller coupled to the heating element, one or more of a temperature, duration, and location, relative to the build piece, of the heat treatment.

24. The method of claim 22, further comprising monitoring a temperature of the heated gas using a monitoring sensor coupled to the heating element.

25. The method of claim 22, further comprising: obtaining a temperature of the heated gas via a sensor coupled to the heating element;modifying a temperature of the heated gas using the obtained temperature.

26. The method of claim 22, further comprising delivering the heated gas via one or more channels arranged at an output of the heating element and extending to the at least one port.

27. A thermal treatment apparatus for a powder bed fusion (PBF)-based three-dimensional (3-D) printer, comprising: a temperature-regulating element for changing a temperature of a gas;at least one channel for delivering the gas to a plurality of ports distributed at different vertical regions of a build piece; anda controller for determining gas temperatures and durations of application of the gas via different ones of the plurality of ports,wherein the temperature-regulating element is directed to variably deliver, during printing, the gas to different ones of the plurality of at different ones of the determined gas temperatures and durations of application to stabilize a plurality of thermal properties of the build piece.

28. The apparatus of claim 27, wherein the temperature-regulating element is configured to heat lower portions of the build piece and to cool upper portions of the build piece.