Sliding element with exposed functional surface

Information

  • Patent Grant
  • 8985009
  • Patent Number
    8,985,009
  • Date Filed
    Monday, January 25, 2010
    14 years ago
  • Date Issued
    Tuesday, March 24, 2015
    9 years ago
Abstract
The invention relates to a sliding element, which comprises a support and a coating applied by means of thermal spraying on the support, wherein the coating comprises at least two phases and at least one of the at least two phases is recessed in respect of the other phase of phases.
Description
BACKGROUND OF THE INVENTION

1. Technical Field


The present invention relates to a sliding element, in particular for an internal combustion engine, with a thermally sprayed coating, which comprises an exposed functional surface.


2. Related Art


In the area of the crank drive, great demands are nowadays made on the components thereof in terms of wear properties, thermal conductivity, strength and weight. For this reason, these components are increasingly produced from light metals. Mixed friction up to solid friction occurs at the contact surfaces, which can lead to high frictional losses as well as a high degree of wear (e.g. micro-welding by metal transfer from aluminium surfaces of the contact partners).


The composite structure has thus become the focus of development. To this end, thermal spraying offers excellent possibilities. By means of this process, it is possible to produce cost-effectively functional surfaces which meet these requirements and, moreover, improve the tribological properties of components in contact with one another.


Several thermally sprayed functional surfaces are currently known in technology, fully sprayed liners, thermally sprayed inner coatings and thermally sprayed annular groove reinforcements. So-called pseudo-alloys find application here. These are spray material structures, which comprise two or more different material phases in order to combine the advantages of the individual materials. A material phase usually comprises a light metal, such as for example an aluminium-based alloy, as well as at least one further, usually high-strength phase, such as for example silicon carbide.


It is known to obtain a communicating system, for example on cylinder running paths of internal combustion engines, by honing. Intersecting grooves thereby arise, which are connected to one another at the intersecting regions and thus constitute an open system overall. A drawback here is that an element sliding on the sliding surface, for example a piston ring of a piston of an internal combustion engine, pushes ahead of it the oil present in the grooves, instead of building up a hydrodynamic oil pressure. A mixed friction between the sliding partners involved thus arises at the groove edges.


SUMMARY OF THE INVENTION

The invention involves producing the materials of the contact surfaces as well as the contact surfaces themselves in such a way that optimum tribological properties with correspondingly required physical properties are constituted.


According to a first aspect of the invention, a sliding element is made available, comprising:

    • a support; and
    • a coating applied on the support by means of thermal spraying; wherein
    • the coating comprises at least two phases; and
    • at least one of the at least two phases is recessed with respect to the other phase or phases.


According to an embodiment, the sliding element is a piston ring, a bearing shell, a liner or a piston.


According to an embodiment, the at least two phases have different strengths, and the recessed phase has the lowest strength.


The solution to the problem consists in changing the thermally sprayed running surfaces in such a way that the light metal phase is recessed with respect to the more wear-resistant phase, as a result of which the service life is lengthened. Furthermore, additional micro-chamber pressure systems arise through the recessing, the effect of which is that the share of the hydrodynamic friction can be increased during the operation.


The application of a thermal spray layer, which is partially recessed by additional processes and thereby exposed, leads to the constitution of a new component. The component is constituted for example as a sliding element such as, for example, a piston ring, a liner, a bearing shell or a piston groove reinforcement.


According to an embodiment,

    • the recessed phase comprises a metal-based alloy; and
    • the element most frequently occurring in the recessed phase has an ordinal number <14 from the periodic table.


According to an embodiment, the exposure of the recessed phase takes place mechanically or chemically.


According to an embodiment, the exposure depth, defined over the reduced groove depth Rvk of the recessed phase, amounts to 0.5 μm-6 μm.


According to an embodiment, the sliding element is a piston ring, which is produced from casting material or steel.


According to an embodiment, the sliding element is a piston which is produced from an aluminium-based or magnesium-based alloy.


According to an embodiment, the piston is cast or forged.


According to an embodiment,

    • the piston comprises at least one annular groove; and
    • at least one annular groove is provided with the coating.


According to an embodiment,

    • the piston comprises at least two annular grooves; and
    • the web between the at least two annular grooves is provided with the coating.


According to a second aspect of the invention, a method for producing a sliding element is made available, comprising:

    • making available a support;
    • application, by means of thermal spraying, of a coating on the support, wherein the coating comprises at least two phases; and
    • recessing of at least one of the at least two phases with respect to the other phase or phases.


According to an embodiment, the sliding element is a piston ring, a bearing shell, a liner or a piston.


According to an embodiment, the at least two phases have different strengths, and the recessed phase has the lowest strength.


According to an embodiment,

    • the recessed phase comprises a metal-based alloy; and
    • the element most frequently occurring in the recessed phase has an ordinal number <14 from the periodic table.


According to an embodiment, the exposure of the recessed phase takes place mechanically or chemically.


According to an embodiment, the exposure depth, defined over the reduced groove depth Rvk of the recessed phase, amounts to 0.5 μm-6 μm.


According to an embodiment, the sliding element is a piston ring and is produced from a casting material or steel.


According to an embodiment, the sliding element is a piston and is produced from an aluminium-based or magnesium-based alloy.


According to an embodiment, the piston is cast or forged.


According to an embodiment,

    • at least one annular groove is provided in the piston; and
    • at least one annular groove is provided with the coating.


According to an embodiment,

    • at least two annular grooves are provided in the piston; and
    • the web between the at least two annular grooves is provided with the coating.





BRIEF DESCRIPTION OF THE DRAWING

The invention is described below with the aid of examples of embodiment, making reference to the appended drawing, in which



FIG. 1 shows an exposed thermally sprayed coating according to an embodiment.



FIG. 2 shows a fragmentary view of an exemplary piston including a pair of annular grooves and a web that is disposed between the annular grooves.



FIG. 3 shows a fragmentary, cross-sectional and enlarged view of an exemplary piston including a coating with an exposed but recessed layer and an other layer.





DETAILED DESCRIPTION


FIG. 1 shows a photograph of a thermally sprayed layer for a sliding element after exposure of the aluminium-based matrix. Here, an aluminium matrix has been recessed with respect to an iron matrix. The exposure depth, defined over the reduced groove depth Rvk, amounts to 5 μm.

Claims
  • 1. A sliding element in the form of a piston or piston ring, comprising: a support; anda coating applied on the support by means of thermal spraying; whereinthe coating comprises at least two layers which have different mechanical strengths;one of the at least two layers is recessed with respect to the other layer or layers and exposed, wherein the recessed layer has the lowest strength;the recessed layer comprises a metal-based alloy; andthe element most frequently occurring in the recessed layer has an ordinal number <14 from the periodic table.
  • 2. The sliding element of claim 1, wherein the recessed layer is exposed mechanically or chemically.
  • 3. A sliding element in the form of a piston or piston ring, comprising: a support; anda coating applied on the support by means of thermal spraying; whereinthe coating comprises at least two layers which have different mechanical strengths;one of the at least two layers is recessed with respect to the other layer or layers and exposed, wherein the recessed layer has the lowest strength;the recessed layer is exposed mechanically or chemically; andthe exposure depth, provided over the reduced groove depth Rvk of the recessed layer, is 0.5 μm -6 μm.
  • 4. The sliding element of claim 1, wherein the sliding element is the piston ring and is produced from casting material or steel.
  • 5. The sliding element of claim 1, wherein the sliding element is the piston and is produced from an aluminium-based or magnesium-based alloy.
  • 6. The sliding element of claim 5, wherein the piston is cast or forged.
  • 7. The sliding element of claim 5, wherein the piston comprises at least one annular groove; andat least one annular groove is provided with the coating.
  • 8. The sliding element of claim 7, wherein the piston comprises at least two annular grooves; andthe web between the at least two annular grooves is provided with the coating.
  • 9. A method for producing a sliding element in the form of a piston or piston ring, comprising: providing a support;applying, by means of thermal spraying, a coating on the support, wherein the coating comprises at least two layers which have different mechanical strengths;recessing one of the at least two layers with respect to the other layer or layers, wherein the recessed layer has the lowest strength, and wherein both of said layers are exposed; and whereinthe recessed layer comprises a metal-based alloy; andthe element most frequently occurring in the recessed layer has an ordinal number <14 from the periodic table.
  • 10. The method according to claim 9, wherein the exposure of the recessed layer takes place mechanically or chemically.
  • 11. The method according to claim 9, wherein an exposure depth of the recessed layer, defined over a reduced groove depth Rvk of the recessed layer, amounts is 0.5 μm -6 μm.
  • 12. The method of claim 9, wherein the sliding element is the piston ring and, wherein the piston ring is produced from casting material or steel.
  • 13. The method of claim 9 wherein the sliding element is the piston and, wherein the piston is produced from an aluminum-based or magnesium-based alloy.
  • 14. The method according to claim 13, wherein the piston is cast or forged.
  • 15. The method according to claim 13, wherein at least one annular groove is provided in the piston; andat least one annular groove is provided with the coating.
  • 16. The method according to claim 15, wherein at least two annular grooves are provided in the piston; andthe web between the at least two annular grooves is provided with the coating.
Priority Claims (1)
Number Date Country Kind
10 2009 022 804 May 2009 DE national
PCT Information
Filing Document Filing Date Country Kind 371c Date
PCT/EP2010/050779 1/25/2010 WO 00 9/23/2011
Publishing Document Publishing Date Country Kind
WO2010/136223 12/2/2010 WO A
US Referenced Citations (11)
Number Name Date Kind
2588422 Shepard Mar 1952 A
3911891 Dowell Oct 1975 A
4612256 Neuhauser et al. Sep 1986 A
4798770 Donomoto et al. Jan 1989 A
5305726 Scharman et al. Apr 1994 A
5592927 Zaluzec et al. Jan 1997 A
6361877 Miyai et al. Mar 2002 B1
7332199 Aram Feb 2008 B2
7947372 Dekempeneer May 2011 B2
20070141270 Sherman Jun 2007 A1
20080163751 Subramanian et al. Jul 2008 A1
Foreign Referenced Citations (6)
Number Date Country
19506568 Aug 1996 DE
0411322 Feb 1991 EP
0449356 Oct 1991 EP
0770698 May 1997 EP
9716577 May 1997 WO
9716578 May 1997 WO
Related Publications (1)
Number Date Country
20120067203 A1 Mar 2012 US