The present invention relates to sliding parts suitable for a mechanical seal, a bearing, and other sliding portions for example. In particular, the present invention relates to sliding parts such as a sealing ring or a bearing in which a fluid lies on sealing faces to reduce friction and there is a need for preventing fluid leakage from the sealing faces.
In order to maintain a sealing property for a long time in a mechanical seal serving as one example of sliding parts, contradictory conditions of “sealing” and “lubricity” have to be met at the same time. In recent years especially, there has been an even greater demand for lower friction in order to reduce mechanical loss while preventing leakage of a sealed fluid for environmental measures or the like. Lower friction is to be realized by applying various texturing to a sealing face. For example, there is a known method of arranging dimples on a sealing face as one of the texturing.
For example, in the invention described in JP 11-287329 A (hereinafter, referred to as “Patent Citation 1”), by forming a large number of dimples having different depth on a sealing face, a load capacity due to a fluid bearing pressure generated in a fluid lying between the sealing face and the opposing sealing face at the time of sliding is decreased at part of the dimples in accordance with a change in a fluid temperature but increased at the other dimples. Thus, the load capacity is stabilized and an effect of always maintaining a preferable sliding property can be obtained irrespective of a temperature change.
In the invention described in JP 2000-169266 A (hereinafter, referred to as “Patent Citation 2”), by forming a sealing face by depositing a hard film on a surface of a base member made of a sintered ceramic material and providing a large number of dimples on this sealing face, wear resistance is improved and a liquid lubricating property by the dimples is improved.
Patent Citation 1: JP 11-287329 A
Patent Citation 2: JP 2000-169266 A
However, the invention described in Patent Citation 1 focuses on the depth of the dimples provided on the sealing face for always maintaining a preferable sliding property irrespective of the temperature change but an influence of opening diameters of the dimples on a sliding characteristic (reduction in friction coefficient) has not yet been examined.
The invention described in Patent Citation 2 is to improve the liquid lubricating property by providing the dimples on the sealing face. However, as well as Patent Citation 1, an influence of opening diameters of the dimples on a sliding characteristic (reduction in friction coefficient) has not yet been examined.
An objective of the present invention is to provide sliding parts capable of improving a sliding characteristic in a wide range of a bearing characteristic number on a sealing face by randomly arranging dimples provided on the sealing face.
In order to achieve the foregoing objective, a first aspect of the present invention is a pair of sliding parts in which a plurality of dimples is arranged on at least one of sealing faces that relatively slide on each other characterized in that each of the plurality of dimples is provided independently from the other dimples, and arranged in such a manner that the plurality of dimples having different diameters is randomly distributed.
According to the first aspect, in the wide range of the bearing characteristic number on the sealing face, the sliding characteristic can be improved, that is, the friction coefficient can be reduced.
A second aspect of the sliding parts of the present invention relates to the first aspect, characterized in that the opening diameters of the plurality of dimples are set within a range from 30 to 100 μm.
According to the second aspect, in the wide range of the bearing characteristic number on the sealing face, the sliding characteristic can be furthermore improved.
A third aspect of the sliding parts of the present invention relates to the first or second aspect, characterized in that depth of the plurality of dimples is set within a range from 50 to 1,000 nm.
According to the third aspect, the friction coefficient on the sealing face can be reduced.
A fourth aspect of the sliding parts of the present invention relates to any of the first to third aspects, characterized in that the depth of the plurality of dimples is set within a range from 100 to 200 nm.
According to the fourth aspect, the sliding characteristic at extremely low speed on the sealing face can become preferable.
A fifth aspect of the sliding parts of the present invention relates to any of the first to fourth aspects, characterized in that an area ratio of the plurality of dimples relative to the sealing face is 30 to 50%.
According to the fifth aspect, sealing and lubricity on the sealing face can be obtained at the same time.
The present invention exhibits the following superior effects.
(1) Since each of the plurality of dimples is provided independently from the other dimples, and arranged in such a manner that the plurality of dimples having different diameters is randomly distributed, the sliding characteristic can be improved in the wide range of the bearing characteristic number on the sealing face.
(2) Since the opening diameters of the plurality of dimples are set within a range from 30 to 100 μm, the sliding characteristic can be furthermore improved in the wide range of the bearing characteristic number on the sealing face.
(3) Since the depth of the plurality of dimples is set within a range from 50 to 1,000 nm, the friction coefficient on the sealing face can be reduced.
(4) Since the depth of the plurality of dimples is set within a range from 100 to 200 nm, the sliding characteristic at extremely low speed on the sealing face can become preferable.
(5) Since the area ratio of the plurality of dimples relative to the sealing face is 30 to 50%, the sealing and the lubricity on the sealing face can be obtained at the same time.
Hereinafter, with reference to the drawings, a mode for carrying out the present invention will be described and exemplified based on an embodiment. However, regarding size, material, shape, and relative arrangement of constituent parts described in the embodiment, and the like, there is no intention to limit the scope of the present invention only to those unless specifically and clearly described.
Embodiment
With reference to
As shown in
This sealed fluid can be effectively sealed by using the sliding part 1. For example, this sliding part 1 is used for at least one of a pair of rotating and stationary sealing rings in a mechanical seal device. By closely placing a sealing face of the rotating sealing ring and the opposing sealing face of the stationary sealing ring, a sealed fluid that exists in one of inner and outer peripheries of the sealing faces is sealed.
The sliding part can also be utilized as a sliding part of a bearing that slides on a rotating shaft while sealing lubricating oil on one side in the axial direction of a cylindrical sealing face.
In the present example, a mechanical seal serving as one example of the sliding part will be described as an example. In the description, an outer peripheral side of the sliding part that forms the mechanical seal serves as a high pressure fluid side (sealed fluid side), and an inner peripheral side serves as a low pressure fluid side (atmosphere side). However, the present invention is not limited to this but can also be applied to a case where the high pressure fluid side and the low pressure fluid side are set the other way around. In
In the example shown in the figures, a sectional shape of the sliding part 1 is a convex shape as shown in
In the present example, the case where the dimples 2 are provided in the dimple formation regions 3 arranged equally and independently in the circumferential direction is shown. However, the present invention is not limited to this but the dimples may be provided continuously in the circumferential direction. In the present example, the sliding part 1 is made of silicon carbide (SiC).
In the present invention, the “dimples” are dents formed on the flat sealing face S, and a shape thereof is not particularly limited. For example, a planar shape of the dents includes various shapes such as a circular shape, an oval shape, an oblong shape, or a polygonal shape, and a sectional shape of the dents also includes various shapes such as a bowl shape or a square shape.
A large number of dimples 2 formed on the sealing face S have a function of holding part of a liquid placed between this sealing face S and the opposing sealing face that relatively slides on the above sealing face as a hydrodynamic lubricating liquid film so as to stabilize a lubricating liquid film.
In
One example of a method of processing the dimples on the sealing face will be described as follows.
(1) Decide diameters and positions of holes formed on a metal mask by using random numbers.
(2) Form holes on the metal mask by means of laser processing according to the decided diameters and positions.
(3) Install the metal mask in which the holes are randomly formed on the sealing face of the target sliding part.
(4) Form the dimples on the sealing face by utilizing the holes of the metal mask by irradiation with a femtosecond laser from the upper side of the metal mask, ion etching, or the like. The dimples having different opening diameters are uniformly arranged on the sealing face in predetermined distribution.
In the present example, the opening diameters of the plurality of dimples 2 are distributed within a range from 30 to 100 μm. More dimples 2 having smaller opening diameters are distributed in comparison to the dimples 2 having larger opening diameters.
Random distribution of the opening diameters of the plurality of dimples 2 is set in accordance with a bearing characteristic number G (fluid viscosity×speed/load) of the sealing face or the like.
Specifications of sliding parts used in the embodiment and a comparative example are shown in Table 1 below.
In the embodiment, the mixed dimples in which the opening diameters of the dimples 2 are randomly distributed within a range from 30 to 100 μm are used.
In the comparative example, single dimples in which the opening diameters of the dimples 2 of three types including 50 μm, 75 μm, and 100 μm are uniformly distributed on the sealing face are used.
Further, 100 nm is adopted as depth of the plurality of dimples 2 in both the embodiment and the comparative example since a sliding characteristic at extremely low speed is preferable.
It should be noted that the depth of the plurality of dimples 2 is preferably set within a range from 50 to 100 nm from a viewpoint of reduction in a friction coefficient. However, in a case where importance is attached to the sliding characteristic at extremely low speed, the depth is preferably set within a range from 100 to 200 nm.
In order to obtain both sealing and lubricity at the same time, 40% is adopted as an area ratio of the plurality of dimples relative to the sealing face. However, the present invention is not limited to this but the area ratio may be 30 to 50%.
Test conditions of the embodiment and the comparative example are shown in Table 2 below.
In
In the embodiment in which the opening diameters of the dimples are mixed from φ30 to 100 μm, within a range where the G value exceeds about 6.0×10−8, the friction coefficient is almost the same as that of the diameter of φ100 μm, and within a range of 6.0×10−8 or less, the Gc point is shifted to the lower G side and further the friction coefficient at the Gc point is lowered. It is found that there is an effect on the reduction in the friction coefficient in a wide rotation number range.
It should be noted that during the test, no leakage from the sealing face is generated in the present test.
Next, with reference to
A main body part of the testing machine 10 includes a casing 13 that supports a stationary ring 11 in a non-rotation state via a spring 12, a rotating shaft 14 rotatably inserted in an inner periphery of this casing 13, and a rotating ring 15 supported on an outer periphery of this rotating shaft 14, the rotating ring facing the stationary ring 11 in the axial direction. A sealing target liquid L is enclosed into a sealed space surrounded by the rotating ring 15, the casing 13, and the rotating shaft 14.
As a characteristic of the present testing machine 10, hydrostatic gas bearings are adopted as bearing parts 16 on both sides, so that the sliding torque of the mechanical seal can be measured with high precision. The torque is measured by two kinds of methods including a torque meter 17 and a cantilever type load cell 18, so as to eliminate measuring errors by double-checking.
Operations and effects of the sliding part according to the embodiment of the present invention are as follows.
(1) In the rotation number range in the test, the comparative example in which the opening diameters of the dimples are φ50 μm, φ75 μm, φ100 μm has a tendency that within a range where the value of the bearing characteristic number G exceeds 7.6×10−8, the greater the opening diameters of the dimples are, the more the friction coefficient is lowered, and the smaller the opening diameters of the dimples are, the more the fluid lubricity transition point (hereinafter, referred to as the “Gc point”) is shifted to the lower G side and further the more the friction coefficient at the Gc point is lowered. Meanwhile, in the embodiment in which the opening diameters of the dimples are mixed from φ30 to 100 μm, within a range where the G value exceeds about 6.0×10−8, the friction coefficient is almost the same as that of the diameter of φ100 μm, and within a range of 6.0×10−8 or less, the Gc point is shifted to the lower G side and further the friction coefficient at the Gc point is lowered. There is an effect on the reduction in the friction coefficient in a wide rotation number range.
(2) The depth of the plurality of dimples 2 is preferably set within a range from 50 to 1,000 nm from a viewpoint of the reduction in the friction coefficient. However, by setting the depth within a range from 100 to 200 nm, the sliding characteristic at extremely low speed can become preferable.
(3) By setting the area ratio of the plurality of dimples relative to the sealing face within a range from 30 to 50%, the sealing and the lubricity can be obtained at the same time.
The mode of the present invention is described with the above embodiment. However, specific configurations are not limited to these modes of the embodiment but modifications and additions within a range not departing from the gist of the present invention are also included in the present invention.
For example, the example that the sliding part is used for at least one of the pair of rotating and stationary sealing rings in the mechanical seal device is described in the above embodiment. However, the sliding part can also be utilized as a sliding part of a bearing that slides on a rotating shaft while sealing lubricating oil on one side in the axial direction of a cylindrical sealing face.
For example, the case where the high pressure sealed fluid exists on the outer peripheral side is described in the above embodiment. However, the present invention can also be applied to a case where the high pressure fluid exists on the inner peripheral side. In that case, the dimples are arranged to communicate with the inner peripheral side.
For example, the case where the opening diameters of the plurality of dimples are set within a range from 30 to 100 μm and more dimples having smaller opening diameters are distributed in comparison to the dimples having larger opening diameters is described in the above embodiment. However, these show one preferable example and the present invention is not limited to these. It is important to randomly distribute and mix the plurality of dimples having different opening diameters. A ratio of the distribution may be set to the most relevant value in accordance with the bearing characteristic number G (fluid viscosity×speed/load) of the sealing face.
For example, the case where 100 nm is adopted as the depth of the plurality of dimples is described in the above embodiment. However, the present invention is not limited to this. The depth may be selected from a range from 50 to 1,000 nm. In order to make the sliding characteristic at extremely low speed become preferable, the depth is desirably set within a range from 100 to 200 nm.
For example, the case where 40% is adopted as the area ratio of the plurality of dimples relative to the sealing face from a viewpoint to obtain both the sealing and the lubricity at the same time is described in the above embodiment. However, the present invention is not limited to this but the area ratio may be set within a range from 30 to 50%.
1 Sliding part
2 Dimple
3 Dimple formation region
4 Seal face
10 Testing machine
11 Stationary ring
12 Spring
13 Casing
14 Rotating shaft
15 Rotating ring
16 Bearing part
17 Torque meter
18 Load cell
S Sealing face
Number | Date | Country | Kind |
---|---|---|---|
2013-192868 | Sep 2013 | JP | national |
This application is a divisional of U.S. application Ser. No. 14/900,064, filed Dec. 18, 2015, which in turn claims a priority to the PCT International Patent application Serial No. PCT/JP2014/073136, filed on Sep. 3, 2014, the contents of which are incorporated herein by reference.